BR102018068054A2 - WATERPROOFING COMPOSITION - Google Patents
WATERPROOFING COMPOSITION Download PDFInfo
- Publication number
- BR102018068054A2 BR102018068054A2 BR102018068054-4A BR102018068054A BR102018068054A2 BR 102018068054 A2 BR102018068054 A2 BR 102018068054A2 BR 102018068054 A BR102018068054 A BR 102018068054A BR 102018068054 A2 BR102018068054 A2 BR 102018068054A2
- Authority
- BR
- Brazil
- Prior art keywords
- waterproofing
- composition
- water
- fungicide
- replaces
- Prior art date
Abstract
composição impermeabilizante o seguinte resumo para invenção se refere a um impermeabilizante que é capaz de eliminar pequenas fissuras na alvenaria, impermeabiliza superfícies variadas, serve como selante e tinta para pinturas, substitui manta asfáltica, substitui a massa fina deixando a parede lisa e pronta para acabamentos, apresenta características hidrofugante e pode texturizar a parede, cuja composição básica é água de 1.500 até 2.500 ml, amônia de 15 até 25 ml, dispersante de 15 até 25 ml, carboximetilcelulose (cmc) de 40 até 50 g, éter policarboxilato (wa) de 15 até 25 g, resina acrílica ht 5079 de 9.000 até 11.000 g, quartzo 403/030 de 5.000 até 7.000 g, butil glicol de 150 até 250 ml, solvente issol 160/270 de 120 até 140 ml, bactericida de 40 até 60 ml, fungicida de 40 até 60 ml, copolímero acrílico emulsão aquosa er 05 de 10 até 20 ml, antirrespingo de 10 até 20 ml e antiespumante de15 até 25 ml.waterproofing composition the following summary for invention refers to a waterproofing agent that is able to eliminate small cracks in the masonry, waterproofs various surfaces, serves as a sealant and paint for paintings, replaces asphalt mat, replaces the thin putty leaving the wall smooth and ready for finishing , presents water repellent characteristics and can texturize the wall, whose basic composition is water from 1,500 to 2,500 ml, ammonia from 15 to 25 ml, dispersant from 15 to 25 ml, carboxymethylcellulose (cmc) from 40 to 50 g, polycarboxylate ether (wa) from 15 to 25 g, acrylic resin ht 5079 from 9,000 to 11,000 g, quartz 403/030 from 5,000 to 7,000 g, butyl glycol from 150 to 250 ml, issol solvent 160/270 from 120 to 140 ml, bactericide from 40 to 60 ml, fungicide 40 to 60 ml, acrylic copolymer aqueous emulsion er 05 from 10 to 20 ml, anti-splash from 10 to 20 ml and antifoam from 15 to 25 ml.
Description
COMPOSIÇÃO IMPERMEABILIZANTE CAMPO TÉCNICOWATERPROOFING COMPOSITION TECHNICAL FIELD
[001] O seguinte relatório descritivo para invenção se refere à composição impermeabilizante hidrorrepelente, capaz de corrigir imperfeições no reboco podendo substituir a massa fina, deixando a parede uniforme ou texturizada já pintada e selada, eliminando problemas de umidade e infiltrações.[001] The following descriptive report for the invention refers to the water-repellent waterproofing composition, capable of correcting imperfections in the plaster, replacing the thin mass, leaving the uniform or textured wall already painted and sealed, eliminating moisture and infiltration problems.
ESTADO DA ARTESTATE OF ART
[002] Sabe-se da técnica prévia que impermeabilizantes são substâncias que detêm a água, fungos e bactérias (proteção) impedindo suas passagens, muito utilizados no revestimento de peças e objetos que devem ser mantidos secos e livres de contaminantes. Um impermeabilizante age eliminando ou reduzindo a porosidade do material, preenchendo infiltrações e isolando a umidade do meio.[002] It is known from the prior art that waterproofing substances are substances that hold water, fungi and bacteria (protection) preventing their passage, widely used in the coating of parts and objects that must be kept dry and free from contaminants. A waterproofing agent works by eliminating or reducing the porosity of the material, filling infiltrations and isolating moisture from the medium.
[003] Na construção civil, são empregados no isolamento de fundações, pisos, telhados, lajes, paredes, reservatórios e piscinas.[003] In civil construction, they are used to insulate foundations, floors, roofs, slabs, walls, reservoirs and pools.
[004] Podem ter origem natural ou sintética, orgânica ou inorgânica. Dentre as naturais destaca-se a mamona, dentre as sintéticas o petróleo (altamente agressivo ao ambiente orgânico).[004] They can have natural or synthetic, organic or inorganic origin. Among the natural ones, castor oil stands out, among the synthetic oil (highly aggressive to the organic environment).
[005] O documento PI 0603266-4 descreve uma tinta impermeabilizante de superfície, sendo um composto de polímeros de PVC, solventes álcoois, solventes aromáticos, solventes acetatos, pigmentos orgânicos e inorgânicos, dióxido de titânio, cargas minerais e aditivos à base de silicone, monocomponente de multiplicidade no seu uso, apresentada nas formas líquida, de massa e de manta, que cobre o substrato cimentício, madeira, metais ferrosos e não-ferrosos, minerais e outros, com uma película impermeável, elástica, flexível, antitérmica, atóxica e perfeita durabilidade. Quando acrescida de aditivo à base de silicone, transforma-se em desmoldante. Aplicada a frio, em temperaturas e ambientes variadas, sendo resistente aos raios ultravioletas. Por ser atóxica e aplicada a frio diminui riscos no seu manuseio e não agride o meio ambiente.[005] PI 0603266-4 describes a waterproof surface paint, being composed of PVC polymers, alcohol solvents, aromatic solvents, acetate solvents, organic and inorganic pigments, titanium dioxide, mineral fillers and silicone based additives , single component of multiplicity in use, presented in liquid, mass and blanket forms, which covers the cementitious substrate, wood, ferrous and non-ferrous metals, minerals and others, with a waterproof, elastic, flexible, antipyretic, non-toxic film and perfect durability. When added with a silicone-based additive, it becomes a release agent. Applied cold, in different temperatures and environments, being resistant to ultraviolet rays. Because it is non-toxic and applied cold, it reduces risks in its handling and does not harm the environment.
[006] Uma composição de impermeabilizante é descrito no PI 0700744-2, que é destinado a proporcionar um impermeabilizante líquido para aplicação preferencialmente sobre elementos construtivos constituídos de material cerâmico e/ou argamassa de cimento e areia, tais como: blocos, tijolos, placas de revestimento, telhas entre outros, proporcionando-lhes proteção contra a umidade, sendo que, a formulação compreende preferencialmente uma parte de 5% de n.octiltrietoxissilano, mais uma parte de 95% de aguarrás, sendo também consideradas eficientes as misturas de 2,5% de n.octiltrietoxissilano, mais 97,5% de aguarrás, até 15% de n.octiltrietoxissilano, mais 85% de aguarrás.[006] A waterproofing composition is described in PI 0700744-2, which is intended to provide a liquid waterproofing agent for application preferably on construction elements consisting of ceramic material and / or cement and sand mortar, such as: blocks, bricks, slabs coating, tiles, among others, providing them with protection against moisture, and the formulation preferably comprises a 5% part of n.octiltriethoxysilane, plus a 95% part of turpentine, and mixtures of 2, 5% n.octiltriethoxysilane, plus 97.5% turpentine, up to 15% n.octiltriethoxysilane, plus 85% turpentine.
[007] O documento PI 0701417-1 descreve um composto impermeabilizante e hidrofugante, formado por silicone modificado ligado a acrílicos de alto poder de cobertura com aglutinantes amaciantes, que fazem a película interna e superficial perdurarem de forma a criar efeitos estéticos e duradouros ligados a preservantes e conservantes que promovem a estética contínua do próprio produto.[007] PI 0701417-1 describes a waterproofing and water repellent compound, formed by modified silicone bonded to high-coverage acrylics with softening binders, which make the inner and surface film last in order to create aesthetic and lasting effects linked to preservatives and preservatives that promote the continuous aesthetics of the product itself.
[008] Uma composição impermeabilizante, estrutura impermeabilizante, método para impermeabilizar uma estrutura e camada impermeabilizante de uma composição impermeabilizante, que inclui um componente de asfalto emulsificado, mais uma mistura de látex com cloreto de cálcio como a solução de ruptura, é descrita no US 60/809965. A composição impermeabilizante torna-se livre de pegajosidade rapidamente, após aplicação e pode ser aplicada em asfalto, concreto, tijolo, pedra, madeira, metal, vários metais com revestimento base e outras superfícies de substrato. A composição impermeabilizante é aplicada em uma superfície de substrato desejada, depositando-se o componente de asfalto emulsificado mais uma mistura de látex com cloreto de cálcio separadamente, de modo que se misturem entre si durante o processo de aplicação.[008] A waterproofing composition, waterproofing structure, method for waterproofing a waterproofing structure and layer of a waterproofing composition, which includes an emulsified asphalt component, plus a mixture of latex and calcium chloride as the rupture solution, is described in the US 60/809965. The waterproofing composition quickly becomes free of stickiness after application and can be applied to asphalt, concrete, brick, stone, wood, metal, various metals with base coating and other substrate surfaces. The waterproofing composition is applied to a desired substrate surface, depositing the emulsified asphalt component plus a mixture of latex and calcium chloride separately, so that they mix together during the application process.
[009] O documento BR 102012009763-0 descreve processo de fabricação de composto com base em polímeros em suspensão de classificação totalmente acrílica, resistente a agentes externos com características hidrofugantes, vedante, impermeabilizante, bactericida, fungicida, antitérmico e de isolamento acústico que serve como base de tintas e argamassas para a prevenção e reparação de trincas, fissuras, rachaduras, vazamentos e infiltrações e recuperação das deteriorações, ocasionadas pelas variações de temperaturas e umidade. Por ter em sua composição polímeros em suspensão, permite a sua aplicação nos mais variados tipos de materiais e estruturas. Indiferente da composição do material aonde esse venha a ser aplicado, é garantida a elasticidade do composto. Ao ser diluído em veículo líquido, se comporta como substância bloqueadora, podendo ser aplicado ainda em temperaturas variadas, não havendo, durante o processo de aplicação e cura, a liberação de nenhum tipo de resíduo tóxico, tornando-se, portanto, um material ecologicamente correto.[009] The document BR 102012009763-0 describes the manufacturing process of compost based on polymers in suspension of totally acrylic classification, resistant to external agents with water repellent characteristics, sealant, waterproofing, bactericide, fungicide, antipyretic and acoustic insulation that serves as base of paints and mortars for the prevention and repair of cracks, cracks, cracks, leaks and infiltrations and recovery from deteriorations caused by variations in temperatures and humidity. Because it has suspended polymers in its composition, it allows its application in the most varied types of materials and structures. Regardless of the composition of the material where it will be applied, the elasticity of the compound is guaranteed. When diluted in a liquid vehicle, it behaves as a blocking substance and can be applied even at varying temperatures, with no release of any type of toxic waste during the application and curing process, thus becoming an ecologically material right.
[010] Uma tinta impermeabilizante para muros e fachadas é revelada no PI 1102881-5, que tem por objetivo proporcionar um produto para revestimento de muros e fachadas, com aplicação principal voltada para construção civil e indústria, com 10 a 16% de resinas acrílicas, de 20 a 25% de água, de 30 a 40% de cargas minerais, de 0,1 a 2% de pigmentos, e de 5 a 17% de conservantes e aditivos.[010] A waterproofing paint for walls and facades is revealed in PI 1102881-5, which aims to provide a product for wall and facade cladding, with a main application aimed at civil construction and industry, with 10 to 16% acrylic resins , 20 to 25% water, 30 to 40% mineral fillers, 0.1 to 2% pigments, and 5 to 17% preservatives and additives.
[011] Um impermeabilizante acrílico com formulação diferenciada, totalmente solúvel em água, assegurando durabilidade em paredes de alvenaria, fachadas, telhas e tijolos à vista, isento de solventes orgânicos, não agredindo a natureza, obtendo maior brilho que os produtos base água do mercado, maior rendimento, não sendo necessário a aplicação de fundos (seladores), sendo praticamente inodoro e por consequência ecologicamente correto, causando o mínimo de desconforto na aplicação, que apresenta teor de sólidos (resina) de 40% da formulação, tanto nos coloridos como nos incolores, o que diferencia de 12 a 50% do teor de sólidos dos impermeabilizantes convencionais. Com este teor de sólidos (resinas) podem encontrar uma maior espessura da película e fechar mais os poros do substrato, em consequência deste fato, bem como, do tipo de emulsão utilizada a base monômeros acrílicos e modificantes químicos, se terá um produto com excelentes características impermeabilizantes, que dispensa o uso de qualquer tipo de fundo e economicamente interessante por apresentar menor custo e facilidade de aplicação.[011] An acrylic waterproofing agent with differentiated formulation, totally soluble in water, ensuring durability in masonry walls, facades, tiles and exposed bricks, free from organic solvents, not harming nature, obtaining greater shine than the water-based products on the market , higher yield, with no need for the application of bottoms (sealers), being practically odorless and therefore ecologically correct, causing the minimum discomfort in the application, which has a solids (resin) content of 40% of the formulation, both in colored and in colorless, which differs from 12 to 50% of the solids content of conventional waterproofing. With this content of solids (resins) they can find a greater thickness of the film and close the pores of the substrate more, as a result of this fact, as well as, of the type of emulsion used based on acrylic monomers and chemical modifiers, you will have a product with excellent waterproofing characteristics, which dispenses with the use of any type of fund and is economically interesting because it has lower cost and ease of application.
PROBLEMAS DA TÉCNICAPROBLEMS OF THE TECHNIQUE
[012] Os impermeabilizantes conhecidos da arte são substâncias que detêm a água, fungos e bactérias (proteção) impedindo suas passagens, muito utilizados no revestimento de peças e objetos que devem ser mantidos secos e livres de contaminantes. No entanto, estes produtos não se destinam a correções de imperfeições ou texturizar paredes.[012] Waterproofing agents known in the art are substances that stop water, fungi and bacteria (protection) preventing their passage, widely used in the coating of parts and objects that must be kept dry and free from contaminants. However, these products are not intended to correct imperfections or to texture walls.
SOLUÇÃO PROPOSTAPROPOSED SOLUTION
[013] Assim, devido às considerações pertinentes ao estado da arte anteriormente discutido, é um dos objetivos da presente invenção desenvolver um impermeabilizante que apresente as seguintes características: é capaz de eliminar pequenas fissuras na alvenaria, impermeabiliza superfícies variadas, serve como selante e tinta para pinturas, substitui manta asfáltica, substitui a massa fina deixando a parede lisa e pronta para acabamentos, apresenta características hidrofugante e pode texturizar a parede.[013] Thus, due to the considerations pertinent to the state of the art previously discussed, it is one of the objectives of the present invention to develop a waterproofing material that has the following characteristics: it is able to eliminate small cracks in the masonry, waterproofs various surfaces, serves as a sealant and paint for paintings, it replaces asphalt blanket, it replaces the thin mass leaving the wall smooth and ready for finishing, it presents water repellent characteristics and can texture the wall.
DESCRIÇÃODESCRIPTION
[014] A caracterização da invenção proposta nesse relatório é conseguida mediante a descrição das quantidades necessárias para a composição em questão, que são necessárias para a realização da presente aplicação, de tal modo que se possa reproduzi-la integralmente por técnica adequada, permitindo plena caracterização da funcionalidade da patente pleiteada.[014] The characterization of the invention proposed in this report is achieved by describing the quantities necessary for the composition in question, which are necessary for the realization of the present application, in such a way that it can be reproduced in its entirety by appropriate technique, allowing full characterization of the functionality of the patent applied for.
[015] A partir da descrição das quantidades em peso e volume dos constituintes individuais que compõem o produto, se fundamenta a parte descritiva do relatório esclarecendo aspectos que possam ter ficado subentendidos, de modo a determinar claramente a proteção ora solicitada.[015] Based on the description of the quantities by weight and volume of the individual constituents that make up the product, the descriptive part of the report is based, clarifying aspects that may have been implied, in order to clearly determine the protection now requested.
[016] Essas quantidades podem apresentar variações, desde que não se fuja do inicialmente requerido.[016] These quantities may vary, as long as you do not deviate from what was initially required.
[017] Neste caso tem-se que o produto pode ser gerado por diferentes operações.[017] In this case, the product can be generated by different operations.
[018] Uma composição básica para o impermeabilizante descrita na presente invenção se destina ao padrão para um volume de 16 litros ou 19 quilogramas de massa de produto.[018] A basic composition for the waterproofing agent described in the present invention is intended for the standard for a volume of 16 liters or 19 kilograms of product mass.
[019] Para tal, se consegue obter a composição básica do impermeabilizante proposto, através das seguintes quantidades estabelecidas: [020] - água...............................1.500 até 2.500 ml;[019] For this, it is possible to obtain the basic composition of the proposed waterproofing material, through the following established quantities: [020] - water ....................... ........ 1,500 to 2,500 ml;
[021] - amônia.......................................15 até 25 ml;[021] - ammonia ....................................... 15 to 25 ml;
[022] - dispersante..................................15 até 25 ml;[022] - dispersant .................................. 15 to 25 ml;
[023] - carboximetilcelulose (CMC)...................40 até 50 g;[023] - carboxymethylcellulose (CMC) ................... 40 to 50 g;
[024] - éter policarboxilato (WA)....................15 até 25 g;[024] - polycarboxylate ether (WA) .................... 15 to 25 g;
[025] - resina acrílica HT 5079...............9.000 até 11.000 g;[025] - HT 5079 acrylic resin ............... 9,000 to 11,000 g;
[026] - quartzo 403/030....................... 5.000 até 7.000 g;[026] - 403/030 quartz ....................... 5,000 to 7,000 g;
[027] - butil glicol..............................150 até 250 ml;[027] - butyl glycol .............................. 150 to 250 ml;
[028] - solvente ISSO 160/270.....................120 até 140 ml;[028] - solvent ISSO 160/270 ..................... 120 to 140 ml;
[029] - bactericida.....................................40 até 60 ml;[029] - bactericidal ..................................... 40 to 60 ml;
[030] - fungicida.......................................40 até 60 ml;[030] - fungicide ....................................... 40 to 60 ml;
[031] - copolímero acrílico emulsão aquosa ER 05..10 até 20 ml;[031] - acrylic copolymer aqueous emulsion ER 05..10 up to 20 ml;
[032] - antirrespingo...................................10 até 20 ml;[032] - anti-splash ................................... 10 to 20 ml;
[033] - antiespumante...................................15 até 25 ml.[033] - defoamer ................................... 15 to 25 ml.
[034] Preferencialmente, se consegue obter a composição básica do impermeabilizante proposto, através das seguintes quantidades estabelecidas: [035] - água...................................... 2.000 ml;[034] Preferably, it is possible to obtain the basic composition of the proposed waterproofing material, through the following established quantities: [035] - water ........................ .............. 2,000 ml;
[036] - amônia........................................20 ml;[036] - ammonia ........................................ 20 ml;
[037] - dispersante...................................20 ml;[037] - dispersant ................................... 20 ml;
[038] - carboximetilcelulose (CMC)....................45 g;[038] - carboxymethylcellulose (CMC) .................... 45 g;
[039] - éter policarboxilato (WA).....................20 g;[039] - polycarboxylate ether (WA) ..................... 20 g;
[040] - resina acrílica HT 5079...................10.000 g;[040] - acrylic resin HT 5079 ................... 10,000 g;
[041] - quartzo 403/030...........................6.000 g;[041] - quartz 403/030 ........................... 6,000 g;
[042] - butil glicol.................................200 ml;[042] - butyl glycol ................................. 200 ml;
[043] - solvente ISSOL 160/270.......................133 ml;[043] - ISSOL 160/270 solvent ....................... 133 ml;
[044] - bactericida...................................50 ml;[044] - bactericidal ................................... 50 ml;
[045] - fungicida.....................................50 ml;[045] - fungicide ..................................... 50 ml;
[046] - copolímero acrílico emulsão aquosa ER 05......15 ml;[046] - acrylic copolymer aqueous emulsion ER 05 ...... 15 ml;
[047] - antirrespingo..............................15 ml;[047] - anti-splash .............................. 15 ml;
[048] - antiespumante..............................20 ml. REIVINDICAÇÕES:[048] - defoamer .............................. 20 ml. CLAIMS:
Claims (2)