Description

IMPROVED OPERATION AND REGENERATION OF PERMSELECTIVE ION-EXCHANGE MEMBRANES IN BRINE ELECTROLYSIS CELLS

This invention relates to a method for rejuvenating permselective ion-exchange membranes employed as selective barriers between the anolyte and catholyte of brine electrolysis cells.

"Carbon oxide" is used herein to mean carbon dioxide, or carbonic acid, or a carbonate or bicarbonate of an alkali metal or an alkaline earth metal (including magnesium), or a combination of any of these.

"Cathodic protection voltage" is defined herein to mean a cell voltage drop, as measured between the anode to the cathode of a cell, which is just large enough to cause reduction of water to hydrogen and hydroxyl ions at the cathode. Such a cell voltage is, therefore, capable of providing cathodic protection for the cathodes to prevent them from corroding.

The electrolysis of chlorides of monovalent cations (including lithium, sodium, potassium, rubidium, cesium, thallium and tetra methyl ammonium) with cation

OMPI selective membranes is well known for the production of chlorine and the hydroxides of such cations, particularly with respect to the conversion of sodium chloride to chlorine and caustic. Representative of such permselec- tive cation exchange membranes are the perfluorosulfonic acid membranes made and sold by the E. I. duPont de Nemours & Co., Inc., under the tradena e, Nafion, and the perfluorocarboxylic acid membranes of the Asahi Glass Industry Co., Ltd. of Tokyo, Japan. See U.S. Patent 4,065,366 to Oda et al for a description of the latter carboxylic acid type membranes.

In the process of electrolyzing sodium chloride into chlorine and caustic wherein such membranes are used, the membrane divides the cell into anode and cathode compartments. Brine is fed to the anode compart¬ ment and water is fed to the cathode compartment. A voltage impressed across the cell electrodes causes the migration of sodium ions through the membrane into the cathode compartment where they combine with hydroxide ions (created by the splitting of water at the cathode) to form an aqueous sodium hydroxide solution (caustic). Hydrogen gas is formed at the cathode and chlorine gas at the anode unless a depolarized cathode is used. (When a depolarized cathode is used, H₂ gas is not generated- ) The caustic, hydrogen and chlorine may subsequently be converted to other products such as sodium hypochlorite or hydrochloric acid.

It is known that over a long period (>100 days) of use of such membrane-type cells, there occurs an undesirable increase in the cell voltage and electri¬ cal energy consumed per unit (e.g. ton) of product made. The prior art in general has attributed this undesirable increase to the fouling of the membrane by hardness and other multivalent cation impurities contained in the brine feed.¹ The calcium cation in particular has been singled out as the most damaging impurity.

To further prolong the life of these permselec- tive membranes, several techniques for regenerating them in place have been developed. For example, U.S. Patent 4,115,218, by Michael Krumpelt (issued Sept. 19, 1978) teaches that such membranes can be rejuvenated by merely

¹See U.S. Patent 3,793,163 to R. S. Dotson (1974); The Asahi Chemical Membrane Chlor-Alkali Process, page 5 of a paper presented by Maorni Seko of As hi Chemical Industry Co., Ltd., of Tokyo,• Japan, at The Chlorine Institute, Inc., 20th Chlorine Managers Seminar, at New Orleans, Louisiana on February 3, 1977; Effect of Brine Purity on Chlor-Alkali Membrane Cell Performance, a paper originally presented by Charles J. Molnar of E. I. duPont de Nemours & Co., Inc., and Martin M. Dorio of Diamond Shamrock Corporation at The Electro¬ chemical Society Fall Meeting held October, 1977, at Atlanta, Georgia; The Commercial Use of Membrane Cells in Chlorine/Caustic Plants, pages 6-9 of a paper presented by Dale R. Pulver of Diamond Shamrock Corporation at The Chlorine Institute's 21st Plant Manager's Seminar, at Houston, Texas, on February 15, 1978; Nafion® Membranes Structured for High Efficiency Chlor-Alkali Cells, a paper presented by Charles J. Hora of Diamond Shamrock Corporation and Daniel E. Maloney of E. I. duPont de Nemours & Co., Inc., at The Electrochemical Society Fall Meeting, October, 1977, Atlanta, Georgia; U.S. Patent 4,115,218 to Michael Krumpeit (1978); U.S. Patent 4,073,706 to Zoltan Nagy (1978); U.S. Patent 3,988,223 to S. T. Hirozawa (1976); U.S. Patent 4,204,921 to W.E. Britton et al (1980); U.S. Patent 4,202,743 to Oda et al (1980); and U.S. Patent 4,108,742 to Seko et al (1978). — *i— reducing or interrupting the cell current or voltage alone or in combination with a concomitant flushing of the catholyte portion of the cell. This process is limited to the instance where the brine fed to the cell during its normal operation contains a calcium content which is less "than is ordinarily used".

Another example of membrane regeneration is taught in U.S. Patent 3,988,223, by Stanley T. Hirozawa (issued Oct. 26, 1977). This patent teaches unplugging the membrane by a process which comprises maximizing the brine head, adding a chelate or chelate forming agent to the anolyte, shunting the electrical current to the cell, flushing the cell, and removing the shunt.

A third example of membrane regenerating is taught in U.S. Patent 4,040,919, by Jeffrey D. Eng

(issued Aug. 9, 1977) in which the membrane is regenerated by increasing the acidity of the anolyte, diluting the electrolyte located immediately adjacent to the anolyte and separated from the anolyte by a membrane, reducing the current density, and maintaining such conditions during electrolysis for a period sufficiently long to rejuvenate the membrane. Note, usually the electrolyte referred to in this patent can be the catholyte, but it does no have to be. It can be an electrolyte located between two spaced membranes which are both located between an anode and a cathode.

These membrane regenerating techniques are an improvement over the alternative of replacing the mem¬ branes, but only marginally so in many instances. Generally these techniques produce only a short term improvement, particularly short term improvements

OMPI --X- insofar as are concerned the cell voltage and cell energy requirement (unit of energy used to make a unit of cell product).

It is not certain why these membrane regenerat- ing techniques usually produce only short term improve¬ ments, but it seems in accordance with the discovery of the present invention that these techniques can readily remove some salts from the membrane, but can remove substantial amounts of impregnated calcium carbonate only at the expense of doing considerable damage to the membrane. The method of the present invention provides a solution to the problem of membrane fouling. Membranes have been found to be much better regenerated with less damage done to the membrane using the method of cell operation and rejuvenation of the invention.

This invention relates to a method of operating and regenerating an electrolysis cell which electrolyzes an aqueous alkali metal halide solution (brine) to a halogen at the anode and an alkali metal hydroxide at the cathode, said cell containing a permselective cation exchange membrane disposed between the anode and cathode to form an anolyte and catholyte compartment which method comprises the steps of: feeding to and electrolyzing in said cell a brine which, at least at the time immediately prior to the brine's becoming part of the anolyte, contains no more than about 5 ppm hardness (expressed as ppm calcium) and no more than about 70 ppm "carbon oxide" (expressed as ppm C0₂ ) ; regenerating the membrane by contacting the membrane on at least one of its sides with a solution capable of dissolving the multivalent cation compounds fouling the membrane for a time sufficient to dissolve a substantial

OMPI a ount of said compounds, said solution having a pH lower than the pH of the electrolyte which contacted that side of- the membrane during the normal cell - electrolysis.

Halides are taken to mean their ordinary primary compounds of halogens. Examples are sodium chloride, potassium chloride, sodium bromide and the like.

Preferably the membrane is regenerated in place (in situ) in the cell. In this case reducing the pH during regeneration can be achieved by a number of methods. The current density and/or cell voltage can be significantly reduced or completely cut off. Increasing the flow rate of water to the catholyte - compartment over that rate used during normal cell electrolysis (Step A) will reduce the catholyte pH. Adding more acid to the anolyte compartment or brine being fed to the anolyte compartment will reduce the pH in the anolyte compartment. Other methods of achieving .^*the lowering of pH required during regeneration will readily occur to those skilled in the art if it is kept in mind that the object of reducing the pH is to reduce the pH inside the membrane to dissolve the foreign salts impregnated therein by maintaining a liquid solution in contact with the membrane on one or both sides to receive these salts when dissolved.

A further feature of this invention is the protection of the cathodes from corrosion during the membrane regenerating step. This can be achieved by the addition of corrosion inhibitors to the catholyte compartment and/or reducing the cell voltage to the "cell cathodic protection voltage" defined above. A yet further feature of this invention is that if the membrane is dried after the contaminating salts have been dissolved from it during regeneration the membrane regeneration is further enhanced-

The drawing is a sectional side view of a lab mini-cell which is representative of those used in the Examples given below in the Detailed Description.

This invention is the discovery that better membrane regenerations can be obtained by operating the cell such that the brine fed to the cell's anolyte compartment has no more than about 70 ppm "carbon oxide" (as defined above and expressed as ppm C0₂ ) prior to the brine feed becoming part of the anolyte. In the anolyte virtually all of the "carbon oxide" is or becomes carbon dioxide, and is swept from the cell without harming the membrane. It is theorized that a residual of th *e carbon dioxide close to the membrane in the cell's anolyte chamber is in the form of carbonate anions. It is a further theory that a very small, but significant, part of these residual carbonate anions react with calcium and are deposited on and in the •membrane.

The less "carbon oxide" is present in the cell, the better the cell performs. Thus, brine feed containing less than 10 ppm is preferred and brine containing less than 2 ppm is most preferred. Also brine which has a low hardness content (expressed as ppm calcium) in addition to having a low "carbon oxide" content was discovered to produce even better results. Brine containing less than about 5 ppm hardness is acceptable; and brine containing less than about 1-2 ppm hardness is preferred. The pH of the brine after it becomes anolyte was also found to have a significant effect on cell performance. A pH of less than about 4 is acceptable; a pH of less than 3.0 is preferred; and a pH of about 2.0 is most preferred^".

The low "carbon oxide" content of this brine can be achieved by several methods. One is not to place it there in the first instance, but the most practical method is to remove it after using a conventional brine treatment wherein: (a) sodium carbonate (in molar excess with respect to the calcium present in the brine) is added to the brine to form insoluble forms of calcium carbonate, and sodium hydroxide (in molar excess with respect to the magnesium present in the brine) is added to the brine to form insoluble compounds of magnesium; and (b) these insoluble compounds of calcium and magnesium are substantially all separated from the brine leaving a brine containing the excess amounts of carbonate and hydroxide anions. This conventionally treated brine can then be treated with a sufficient amount of mineral acid, preferably hydrochloric acid, to convert the carbonate anions to carbon dioxide. This carbon dioxide can be removed by allowing it to set for a few days much like an opened bottle of a carbonated soft drink; or it can be removed more rapidly by agitation such as shaking or stirring; or more rapidly by a gas purge with an innocuous gas such as chlorine gas, air, nitrogen, or the like; or even more rapidly by a combination of agitation and gas purge.

The hardness can also be reduced by methods such as contacting the brine with chelating ion exchange beds, or solvent extraction techniques.

PI The anolyte pH can be lowered and controlled by methods such as adding hydrochloric acid and/or flow controlling the brine to the cell.

Better appreciation of the present invention can be obtained by those skilled in the art from a study of the following six examples. The first two examples are examples of prior art while the latter four are examples of the present invention. The two prior art examples both show the inferior regenerative effect obtained by regenerating membranes after they had been fed brine containing relatively normal con¬ centrations of "carbon oxide" during the normal cell electrolysis step preceding the membrane regeneration step. In the first of these prior art examples, the "carbon oxide" was predominately in the form of carbonate anions (C0₃ ), whereas in the second prior art example, the "carbon oxide" was predominately in the form of entrained carbon dioxide gas. The pH of the brine feed determines what forms the "carbon oxide" will take.

Before presenting these examples, however, it is useful to present a set.of definitions of cell performance and a description of the type of cell used in all six examples.

One parameter which is important in considering a cell's energy performance is the strength of the caustic produced, for the more concentrated the caustic produced, the less energy is later required in evaporating water from the caustic after it has left the cell and is being concentrated. The purity of the caustic- soda pro.duct is also important to over-all process economics. Preferably sodium chloride and sodium chlorate in the

OMPI caustic are maintained as low as possible. The actual level of these impurities is a function of cell operating parameters and the characteristics of the membrane. Over the life of a-membrane cell these impurities are preferably maintained at the same level as when the cell was new.

The two other parameters required for a complete energy view of the overall process, particularly over a long period of time, are current efficiency and cell voltage. Cell voltage is defined to be the electri¬ cal potential as measured at the cell's anode connection to the power supply and the cathode connection to the power supply- Cell voltage includes the chemical decomposition voltages and the IR associated with current^'flowing through electrodes, membrane and elec¬ trolytes.

Current efficiency is a measure of the ability of the membrane to prevent migration into the anode compartment of the caustic produced at the cathode. Herein it is also referred to as caustic efficiency and NaOH efficiency. Caustic efficiency is defined as the actual amount of caustic produced divided by the theoret¬ ical amount of caustic that could have been produced at a given current. The most common method- of comparing the performance of an electrolytic process combines both current efficiency and voltage into a single energy term. This energy term is referred to as the cell's "energy requirement", and is defined to be the amount of electrical energy consumed per unit of NaOH produced. It is usually expressed in killowatt hours (KWH) of electricity consumed per metric ton ( t) of NaOH produced. The method of determining this energy

MPI term is the multiplication of voltage by the constant 670 killoampere-hours, and divided by the current efficiency. Lower current efficiency decreases the quantity of NaOH produced (mt), and higher voltage increases the quantity of KWH used; thus the smaller the "energy requirement" value KWH/mt, the better the performance of the cell.

The examples set forth below were run in laboratory size cells like that depicted in the drawing. These cells had an anolyte compartment 10 and a catholyte compartment 12. These two compartments were separated by a vertically disposed, permselective cation exchange membrane 14. The membrane was sealed between anode frame 20 and cathode frame 22 by gaskets (not shown) located on either side of membrane 14. Gasket 6 repre¬ sents the gasket sealing means used between anolyte compartment 10 and catholyte compartment 12. Near membrane 14 was disposed a vertical, parallel, flat- shaped anode 16. On the opposite side of membrane 14 was disposed a vertical, parallel, flat-shaped cathode 18. Anode 16 was an expanded-metal sheet o^": titanium having a Ti0₂ and Ru0₂ coating. Cathode 18 was made of woven-wire mild steel. Of course, other type cathodes can be used such as low overvoltage cathodes. During regeneration, it is very important to protect these low overvoltage cathodes from corrosion such as by the method employed in Example 4 on its 257th day as described below.

The mechanical supports and D.C. electrical connections for anode 16 and cathode 18 are not shown as they would serve more to^' obscure the drawing. Suffice it to say that anode 16 and cathode 18 were mechanically supported by studs which passed through the cell walls and to which were attached D.C. electrical connections necessary to conduct current for electrolysis. The electrical power passed through the cell was capable of being regulated so that a constant current density per unit of electrode geometrical area—i.e. , amperes per square inch (ASI)—could be maintained during normal cell operation.

Also not shown are the flow devices used to control the cell flow rates. The cells were equipped with a glass immersion heater (not shown) in the anolyte compartment in order to maintain the cell at an elevated temperature.

Basically the cell frame was made of two types of materials. The anode frame 20 was made of titanium so as to be resistant to the corrosive condi¬ tions inside the anolyte compartment 10. The cathode frame 22 was made of acrylic plastic so as to be resistant to the corrosive caustic conditions inside the catholyte compartment 12. The necessary entry and exit ports for introducing brine and water and for removing H₂, Cl₂, spent brine, and caustic soda are shown in the drawing.

Anode frame 20 has port 24 for the brine feed to the anolyte chamber 10. Port 26 provided an outlet for the chlorine generated in the anolyte compartment 10, while port 28 provided an exit for spent brine to leave the anolyte compartment^'10 during normal cell operation.

The cathode frame 22 is provided with a port 30 serving as an inlet for water to be supplied to the catholyte compartment 12. Outlet port 32 is provided as an exit for the hydrogen gas generated in the catholyte compartment 12, while port 34 is provided as an exit for liquid caustic generated in the catholyte compartment 12 during normal cell operation.

During normal cell operation the cell in each of the following examples electrolyzed brine at a constant current density, a constant temperature, and a constant caustic concentration during the long electrolysis step(s) before (and between) the membrane regeneration step(s). These conditions however, were not the same in each example, nor was the membrane used the same in each example. When concentration percentages are given, they are intended to be weight percentages.

Prior Art Example #1

A lab cell like that described above was operated at 1^0 ASI, 80°C, 12-13 wt. percent NaOH in the catholyte, 18-19 wt. percent NaCl in the anolyte, and at an anolyte pH of about 4.0-4.3. This cell was operated with brine that contained from 0.4-to 0.9 gram/liter (gpl) Na₂C0₃. Use of brine with this high a carbonate ion concentration is representative of prior art operations, but it is not representative of the method of the present invention.

The permselective membrane employed was

Nafion® 324 obtained from E.I. duPont de Nemours & Co. , Inc. This membrane was a composite of two layers of sulfonic acid polymer and a reinforcing scrim. Similar membranes are described in U.S. Patent 3,909,378.

iREAlT

OMPI The sodium chloride brine was obtained from brine wells located near Clute, Texas. This brine was treated so that it was 25.5 wt. percent NaCl and contained 1-2 ppm hardness (calcium and magnesium content expressed as ppm Ca).

This brine was treated by what is referred to as conventional brine treatment, i.e. that type of brine treatment which has conventionally been used in preparing brine for electrolysis in asbestos diaphragm- -type electrolysis cells for the past many years.

Conventional brine treatment comprises adding Na₂C0₃ and NaOH to the brine in amounts such that the Na₂C0₃ is in a stoichiometric excess of at least about 0.4 gpl (grams per liter) with respect to the calcium present in the brine and such that the NaOH is in a stoichiometric excess of at least about 0.2 gpl with respect to the Mg in the brine. Addition of these excesses of Na₂C0₃ and NaOH cause substantially all of the Ca and Mg to form the insolubles, CaC0₃ and Mg(OH)₂. These insolubles are then removed from the brine feed, usually by settling and filtration techniques, leaving in the brine the excesses of Na₂C0₃ and NaOH as well as a small residual of Ca and Mg as hardness. (This small residual of hardness is on the order of from about 1 ppm to about 5 ppm, expressed as ppm Ca).

In this example, the brine was treated by this conventional brine process to reduce the brine hardness to a level of 1-2 ppm expressed as Ca. The procedure followed to obtain this hardness level was as follows: Na₂C0₃ and NaOH were added to the untreated brine at the well-sight. The brine was then settled and filtered to reduce the hardness to about 1-2 ppm Ca. The Na₂C0₃ was added in stoichiometric excess with respect to the Ca present, so that the filtered brine contained about 0.4 to 0.9 gpl (grams per liter) Na₂C0₃. The NaOH was added in stoichiometric excess to the Mg present, so that the filtered brine pH was about pH 10-12. Normal electrolysis was started and continued for about 282 days using this brine.

On the 283rd day after initial start-up, the membrane was regenerated in situ according to the following procedure. Cell voltage was reduced by turning the cell operating current completely off.

Aqueous HCl was added to and mixed with the feed brine to obtain an acidified brine with a pH of 0.1 to 1.0. This acidified-brine was fed to the anolyte compartment of the cell at a flow rate that was the same as that during normal electrolysis (approximately 9 milliliters per minute). The same water flow rate as used during normal cell operation was fed to the catholyte compart¬ ment (approximately 3.75 milliliters per minute). The membrane in this cell was regenerated in this manner for 20 hrs. at a room temperature of 25°C. The cell was then restored to normal operation at 1.0 ASI, 80°C, 12-13 percent NaOH, 18-19 percent NaCl in the anolyte, and an anolyte pH of 4.0-4.3.

The data in Table I summarize the cell perform- ance before and after the membrane regeneration procedure.

In this and the following tables, "DOL" indi¬ cates the number of days on line, which is approximately equivalent to the number of days that the cell was operated. A few times the cells were shut down because of loss of electrical power) and a hurricane evacuation caused a two day shut-down. Thus DOL is not exact.

OMP "Cell Volts", "NaOH Efficiency" and "Energy Requirement" are the same as defined earlier. "Salt in Caustic" is the weight percent NaCl in the caustic soda product expressed on a 100 percent NaOH basis. For example, all the data in this table are at about 12 wt. percent NaOH, and 100 percent NaOH divided by 12 percent NaOH, multiplied by the actual wt. percent NaCl in this 12 percent NaOH equals the wt. percent NaCl on a 100 percent NaOH weight basis.

TABLE I

Cell NaOH Salt in Energy

D L Volts Efficiency Caustic Requirement

20 3.13 88 0.081 2380

280 3.70 90 0.046 2750

283 Membrane Regenerated ^'

288 3.42 88 0.094 2600

350 3.70 89 0.053 2790

Of particular interest in the data of this table is the amount of decrease in NaOH efficiency observed as occurring from just before to just after the membrane regeneration. In this prior art example, the efficiency declined by two percentage points.

Prior Art Example #2

A lab cell like that described in Prior Art Example #1 was operated and the membrane regenerated. Cell operation and membrane regeneration differed from Prior Art Example #1 in the following ways. The membrane was of the same type, but the lot number and date of manufacture were different. This difference alone can

TOREAlr

OMPI account for some small differences in cell performance and should be considered when comparing data from various tables.

Cell operation was at an anolyte pH of about 2.0 instead of 4.0-4.3. This difference was obtained by adding aqueous HC1 to and mixing it with some of the same type conventionally treated brine as prepared and described in Prior Art Example #1, and then feeding a combination of some of this acidified-brine and some of the conventionally treated brine to the anolyte chamber. The acidified-brine solution contained a NaCl concen¬ tration of about 25 wt. percent, an HC1 concentration of about 3 wt. percent, a C0₂ content of only about one ppm, and a total hardness of 1-2 ppm as Ca. The acidified-brine made up only about 25 percent of the total brine fed to the cell. Because the resulting combined mixture of acid-brine and conventionally treated brine contained in excess of 100 ppm C0 , this type cell operation is not representative of the present invention.

Normal electrolysis was started and continued for about 227 days using the above described mixture of acid-brine and conventionally treated brine. On the 228th day after initial start-up, the membrane was regenerated in situ according to the following procedure. Cell voltage was reduced by reducing the operating current from 1.0 ASI to 0.03 ASI. Acid-brine similar to the 3 percent HC1 acid-briiie described above, but containing 0.13 wt. percent HC1, was fed to the anolyte compartment at a flow rate slightly higher than the normal brine flow rate used during the days of normal electrolysis. The water feed to the catholyte was

- ΪRE increased above the flow rate used during no^'rmal elec¬ trolysis so as to maintain a caustic concentration of about 0.4 wt. percent NaOH during the membrane regenera¬ tion step. Cell temperature was maintained at about 60°C and air was bubbled into the anolyte compartment to provide mixing. Membrane regeneration was continued in this manner for 20 hours. Then the cell was returned to normal electrolysis conditions of 1.0 ASI, 80°C, 12-13 percent NaOH, 18-19 percent NaCl in the anolyte, and an anolyte pH of about two.

The data in Table II summarize the cell performance before and after the membrane regeneration procedure.

ΓABLE II

Cell NaOH Salt in Chlorate Energy OL Volts Efficiency Caustic in Caustic Requirement

26 3.04 88 0.134 2 ppm 2310 25 3.23 87 0.078 23 2490 28 Membrane Regenerated 31 3.11 86 0.280 43 2420 51 3.25 86 0.160 ^' 12 2530

In the table "DOL", "Cell Volts", "NaOH Effi¬ ciency", and "Energy Requirement" are the same as defined earlier. "Chlorate in Caustic" is the ppm NaC10₃ impurity in the caustic on a 100 percent NaOH weight basis.

In this Prior Art^" Example there was a sub¬ stantial increase in both salt and chlorate impurity in

the caustic after the membrane regeneration step. A salt concentration of 0.28 wt. percent and a NaC10₃ concentration of 43 ppm represent unacceptably high levels of these impurities. Above 0.20 wt. percent NaCl and above 25 ppm NaC10₃ are considered unacceptable. Also as noted in the table, cell voltage returned to an unacceptably high level after only 23 days. The method of the present invention resulted in a significant improvement in long term cell performance, and it also provided the following: less frequent membrane regen¬ eration steps are required to maintain a given level of cell performance and caustic product purity is maintained at acceptable levels after the membrane regeneration step.

Invention Example 1

A lab cell like that described in Prior Art Example #1 was operated and the membrane regenerated as required to maintain acceptable cell performance. The major difference in operation between the cell in Prior Art Example #1 and the cell in this example was the level of'C0₂ ("carbon oxide") in the brine which was fed to the anolyte compartment.

In order to reduce the C0₂ content of the brine solution which was fed to the anolyte compartment of the cell during normal electrolysis, the following procedure was used. The same conventionally treated- brine as used in Prior Art Example #1 was acidified using aqueous HCl. The brine 'was mixed and sparged with nitrogen to aide in the removal of entrained C0₂ for a period of about 16 hours. The resulting acidi¬ fied brine contained about 25.5 wt. percent NaCl, 0.65 wt. percent HCl, about 1 ppm Ca total hardness, and less than 1 ppm C0₂ - This acid-brine was then fed to a cell containing a Nafion® 324 membrane which was operated at 1.0 ASI, 80°C, 12-13 wt. percent NaOH, and 18-19 wt. percent NaCl in the anolyte, and at an anolyte pH of about 1.5-3.0 during normal electrolysis. Normal electrolysis was started and continued for 209 days.

On the 210th day after initial start-up, the membrane was regenerated in situ using a procedure similar to the one in Prior Art Example #1. Cell voltage was reduced by turning the cell operating current completely off. The same acid-brine used during normal electrolysis was fed to the anolyte compartment at the same flow rate as used during normal electrolysis. Water at the same flow rate as used during normal cell operation, was continuously fed to the catholyte compartment. The membrane in this cell was regenerated in this manner for 24 hours and at a room temperat re of 25°C. The cell was then restored to normal electrolysis operation at 1.0 ASI, 80°C, 12-13 percent NaOH, 18-19 percent NaCl in the anolyte, ^: and an anolyte pH of 1.5-3.0.

The following table summarizes the cell performance before and after the membrane regeneration procedure.

- TABLE III

Cell NaOH Salt- in Chlorate Energy OL Volts Efficiency Caustic in Caustic Requirement

5 3.01 88 0.188 1 ppm 2290 09 3.09 88 0.082 3 2350 10 Membrane Regenerated 20 3.02 88 0.141 11 2300 50 2.97 88 0.140 6 2270

By operating a cell according to the present invention, cell voltage was reduced by the membrane regeneration step with essentially no reduction in NaOH efficiency as shown by the data in Table III.

The cell in this example continued to operate and the membrane was regenerated two more times using the same procedure as used in the first regeneration set out above* The table below summarizes the cell performance before and after these two further membrane regeneration steps.

TABLE IV

Cell NaOH Salt in Chlorate Energy OL Volts Efficiency Caustic in Caustic Requirement 50 2.97 88 0.140 6 2270 05 3.06 88 0.117 2 2330 07 Membrane Regenerated 8 3.02 88 0.138^" 2300 8 Membrane Regenerated 0 3.08 88 0.142 1 2345 0 3.06 88 0.145 2 2330

OMPI After more than 400 days of operation long-term cell performance was maintained at an acceptable level of energy increase. At the same time, efficiency was maintained at essentially a constant level of 88 percent and impurities in the caustic were maintained at acceptably low levels.

Invention Example 2

A lab cell like that described in Prior Art Example #1 was operated and the membrane regenerated. The membrane in this cell was an unreinforced sulfon- amide type membrane. Similar membranes are described in U.S. 3,969,285. Membranes of this type with a reinforcing scrim have been sold commercially by E.I. duPont de Nemours and include membranes such as Nafion® 214 and Nafion® 227.

The brine feed to this cell was the same as the brine feed to the cell in Invention Example 1, except for the amount of total hardness. In order to further reduce the hardness of the brine the conven- tionally treated brine of Prior Art Example #1 was further treated by passing this brine through a column containing DOWEX* A-l chelating resin made by The Dow Chemical Company. Next, the brine was acidified and the C0₂ removed. The resulting acidified brine contained about 25.5 wt. percent NaCl, 0.65 wt. percent HCl, only about 0.2 ppm Ca total hardness, and less than 1 ppm C0₂.

This brine was fed to the lab cell containing the sulfonamide membrane described above and this cell

*Trademark of The Dow Chemical Company -was operated at 1.75 ASI, 80°C, 28-31 percent NaOH, 20-21 percent NaCl in/the anolyte, and at an anolyte pH of 3-4 during normal electrolysis. Normal electrolysis was started and was continued for about 194 days.

On the 195th day after initial start-up, the membrane was regenerated in situ using the following procedure. The cell current was turned off and the currrent leads disconnected. Both anolyte and catholyte were drained from the cell. An acid solution of 0.5 wt. percent HCl and water was added to the anolyte compartment. An acid solution of 1.0 wt. percent formic acid and water was added to the catholyte com¬ partment. Each compartment was filled with their respective acid solutions. Mixing of the acid solutions was provided by sparging a stream of nitrogen gas into the bottom of each cell compartment. The acid solutions were heated by an immersion type heater and maintained at a temperature of about 75°C. Following the regeneration procedure the acid solutions were drained from the anolyte and catholyte compartments. Respective, fresh acid solutions as described above were used to refill eaqh compartment. The drain and refill step was repeated three more times during the five hour regeneration procedure. The acid wash solutions removed from the cell were analyzed for. pH and for Mg, Ca, and Fe^content. The results of these analyses are tabulated, in Table V.

OMPI TABLE V •

Sample H ppm Mg ppm Ca ppm Fe Anolyte #1 1.2 114 114 3000 #2 1.3 80 28 5200 #3 1.3 74 22 5000 #4 1.2 44 22 3600 Catholyte #1 4.6 4 26 2600 #2 3.9 5 22 2200 ^• #3 3.8 2 22 2200 #4 3.6 1 22 2000

The cell was then restored to normal operation at 1.75 ASI, 80°C, 28-31 percent NaOH, 20-21 percent NaCl in the anolyte and a pH of 3-4. The data in Table VI summarize the performance of this cell before and after the membrane regeneration procedure.

TABLE VI

Cell NaOH Salt in Energy

DOL Volts Efficiency Caustic Requirement

4 3.48 88 0.034 2650

194 3.54 88 0.027 2700

195 Membrane Regeneration

204 3.34 88 0.072 2540

285 3.40 86 0.052 2650

From the analysis of the anolyte acid solutions in Table V, it was apparent that substantially less Ca than Mg was present in thes.e solutions. This unexpected result was exactly reversed from the normal Ca and Mg content of anolyte acid regeneration solutions for membrane cells operated and regenerated like those described in Prior Art Examples #1 and #2. The fact that the Mg concentration was higher than the Ca concentration may be attributed to the fact that

Mg(OH)₂ is more insoluble than Ca(0H)₂ at the high pH's encountered at the anolyte face of the membrane and within the membrane- Although CaC0₃ is much more insoluble at a high pH than Mg(OH)₂ this calcium precipitate was substantially prevented from forming apparently because essentially all the C0₂ (or other "carbon oxide" forming compounds) in the feed brine had been removed. The present invention takes advantage of these facts, and the result is reduced energy consumption and an improvement in the amount of impurities in the caustic when membrane regeneration becomes necessary in order to maintain and prolong long-term cell performance.

As shown by the data in Table VI, energy consumption at the cell was reduced after the membrane regeneration step, salt in the caustic remained accept¬ ably low, and cell performance after 285 days of operation was essentially equal to the level of per¬ formance that was obtained when the membrane was new.

Also note in Table V, the high concentration of Fe present. This iron was corrosion coming from the cathode, among other Fe sources, as a visual inspection of the cathode showed. Control of this corrosion is shown in Invention Example IV below.

Invention Example 3 A lab cell like that described in Prior Art

Example #1 was operated and the membrane regenerated. The membrane in this cell was Nafion® 324. The acid brine feed to the cell was the same as described in Invention Example #2. The cell was operated at 1.0 ASI, 80°C, 17-18 wt. percent NaOH, 19-20 percent NaCl in the anolyte, and at an anolyte pH of 1.5-3.0.

Normai electrolysis was started and continued for 529 days.

On the 530th day after initial start-up, the membrane was regenerated in situ using the following procedure. The cell was turned off and was then flushed with conventionally treated brine of the same type as described in Prior Art Example #1. This was done to remove the strong caustic from the catholyte and the acid-brine solution from the anolyte compartment. Both cell compartments were then drained. The anolyte compartment was then filled with a 0.5 wt. percent HCl and water solution. The cathode compartment was filled with a 1.0 wt₄ percent HCl and water solution which also contained 1000 ppm of ANCOR® 0W®-1 corrosion inhibitor, 1000 ppm isopropyl alcohol, and 220 ppm TRITONS- X-100 wetting agent. ANCOR® OW®-l is a registered trademark of Air Products and Chemicals, Incorporated, and ANCOR® OW®-l corrosion inhibitor is a commercial product available from that company. It is composed of a group of acetylic alcohols, a major portion of which is l-hexyn-3-ol. TRITON is a trademark of Rohm and Haas Company, and TRITON X-100 is a commercial product available from that company. TRITON X-100 is a cogeneric mixture of isooctyl phenoxy polyethoxy ethanols.

The corrosion inhibitor and wetting agent were added in order to protect the cathode.from corrosion during the regeneration procedure. Actually this cor¬ rosion technique did not work as well as the cathodic protection method described in the next example, Inven¬ tion Example 4.

Mixing of the acid solutions in their separate chambers 10 and 12 was provided by sparging a stream of N₂ gas into the bottom of both cell compartments. The acid solutions were heated by an immersion type heater and maintained at 75-80°C. .During the regeneration procedure the respective acid solutions were added to each cell compartment in 75 ml aliquots. This adding of additional fresh acid was repeated four times during the 4^*% hour regeneration procedure. Before restoring the cell to normal operation both acid solutions were drained from the cell, and then the membrane was substan¬ tially dried by heating with the immersion heater described previously. The drying step was carried out at a temperature of between 100°C to 200°C and required about ten minutes. The cell was then restored to normal electrolysis operation.

Cell performance data obtained before and after the regeneration procedure are tabulated in Table VII.

TABLE VII

Cell NaOH Salt in Energy OL Volts Efficiency Caustic Requirement

5 3.02 84 0.130 2410 26 3.18 84 0.031 2540 30 Membrane Regenerated 35 3.12 89 0.029 2350 75 3.15 88 0.027 2400

The data in Table VII shows that after the regeneration procedure, energy consumption was reduced, efficiency was increased by a surprising amount, voltage was reduced, and salt impurity in the caustic remained constant. Being able to use a membrane cell for 575 days and still have cell performance of this quantity is not to be expected by those skilled in the art. Even more unexpected is being able to continue.

The cell in this example continued to be operated, and a second and third regeneration were used at later dates according to the following procedure. The cell voltage was reduced to about 2.1 volts. In this way the cathode potential was maintained at slightly above the cathode decomposition voltage (defined above as the "cathodic protection voltage"); therefore, corrosion of the cathode was substantially prevented. Normal acid-brine feed was fed to the anolyte compartment at the flow rate normally used during cell electrolysis. H₂0 was added to the catholyte at an increased rate in order to reduce the catholyte pH to about pH 8-9. The me brane was regenerated in this manner at room tempera¬ ture for 25 hours during the 2nd regeneration and for 6 hours during the 3rd regeneration. A summary of cell performance before and after these regeneration procedures is given in Table VIII.

TABLE VIII

Cell NaOH Salt in Energy

DOL Volts Efficiency Caustic Requirement

575 3.15 88 0.027 2400

578 3.19 88 0.015 2430

585 Membrane Regenerated 2nd Time

591 3.05 87 0.064 2350

625 3.16 90 0.026 2350

636 Membrane Regenerated 3rd Time

638 3.03 87 0.064 2330

790 3.13 87 0.052 2410

The*»data in Table VIII indicate that long term cell performance was maintained for almost 800 days with essentially the same energy consumption and product purity as when the membrane was new. This is, indeed, unexpected.

Invention Example 4

A lab cell like that described in Prior Art

Example #1 was operated and the membrane regenerated using two different procedures. The membrane in this cell was Nafion® 324 and the acid-brine feed was the same as the acid-brine used in Invention Example #1.

The cell was operated at 1.0 ASI, 80°C, 12-13 percent

NaOH, 18-19 wt. percent NaCl in the anolyte, and at an anolyte pH of 1.5-3.0. Normal electrolysis was started and continued for 166 days. On the 167th day after initial start-up, the membrane was regenerated in situ using the following procedure. The electric current to the cell was turned completely off. The current leads were disconnected from the anode and cathode, and the cell remained elec¬ trically isolated from ground potential. The same type acid-brine used during normal electrolysis was fed into the anolyte compartment. Water was fed into the catholyte compartment. The flow rates of both the acid brine and the water were the same as what they had been during normal cell operation. Samples of anolyte and catholyte were taken periodically during this procedure. The membrane was regenerated in this manner at a room •temperature of 23°C for 23 hours. The cell was then restored to normal cell operation and continued to be operated up to the 256th day after initial start-up.

On the 257th day the membrane was again regenerated using the same procedure as was used during the first regeneration except for the following changes. Cell current and voltage were reduced and cell voltage was then maintained at 2.1 volts by passing a small current through the cell during the entire regeneration procedure. This step was done in order to maintain the cathode potential at slightly above the decomposition voltage in order to substantially prevent corrosion of the cathode. Additional water flow to the catholyte compartment was also used in order to further reduce the catholyte pH. After about 10 minutes into the regeneration procedure the rate of water addition was reduced to the same flow as used during normal elec¬ trolysis. Samples of the anolyte and catholyte were taken periodically during the regeneration procedure. A summary of the analyses of the electrolyte samples taken during the 1st and 2nd membrane regeneration procedures are given in Tables IX and X, respectively. A summary of cell electrolysis performance before and after each regeneration is given in Table XI.

TABLE IX . 1st REGENERATION

Hours Regeneration ppm ppm ppm

Samp.le in Progress Mg Ca Fe pH

Anolyte #1 1 <2 <2 <2 1.7

II #2 3 6.4 <2 4.4 0

11 #3 5 6.7 <2 2.6 0 fl #4 6 6.8 <2 77 0

II #5 6- ■22 composite 4.9 <2 97 0

11 #6 23 3.0 <2 87 0

Catholyte #1 1 <4 <4 <4 14

II #2 3 <4 <4 <4 13.8

II #3 5 <4 <4 <4 12.4

II #4 - 6 <4 <4 58 4.2

II #5 6τ 22 composite <4 <4 55 —

II #6 23 <4 <4 58 4.0

TABLE X

2nd : REGENERATION

Hours Regeneration ppm ppm ppm

Sample in Progress Ca Fe EM

Anolyte #1 1 20 5.8 <1 1.2

" #2 3 11 9.7 4.7 0

#3 6 7.5 2.4 2.3 0

#4 23 7.3 2.2 1.2 0

Catholyte #1 1 <1 <1 <1 12.8

#2 3 <1 <1 <1 —

#3 6 <1 <1 <1 4.0

#4 23 Fl 2 Fl 8.1

TABLE XI

•*

Cell NaOH Salt in Energy

DOL Volts Efficiencv Caustic Requirement

12 3.04 88 0.190 2310

128 3.01 88 0-183 2290

165 3.11 88 0.085 2370

167 Membrane Regenerated 1st Time

171 3.06 88 0.168 2330

214 3.03 89 0.126 2280

256 3.18 90 0.053 2370

257 Membrane Regenerated 2nd Time

260 3.02 89 0.13-2 2270

The results of the analyses of samples taken dμring the membrane regeneration procedures confirm that by using the 2nd regeneration method, essentially no corrosion of the cathode occurred. The data in Table XI demonstrate that long term cell performance and acceptable caustic purity can be maintained by using brine containing only low amounts of CO- ("carbon oxide") and suitable membrane regeneration procedures.

Claims (11)

1. A method of operating and regenerating an electrolysis cell which-electrolyzes- an aqueous alkali metal halide solution (brine) to a halogen at the anode and an alkali metal hydroxide at the cathode, said cell containing a permselective cation exchange membrane disposed between the anode and cathode to form an anolyte and catholyte compartment which method comprises the steps of: feeding to and electrolyzing in said cell a brine which, at least at the time immediately prior to the brine's becoming part of the anolyte, contains no more than about 5 ppm hardness (expressed as ppm calcium) and no more than about 70 ppm "carbon oxide" (expressed as ppm CO-); regenerating the membrane by contacting the membrane on at least one ;of its sides with a solution capable of dissolving the multivalent cation compounds fouling the membrane for a time suffi¬ cient to dissolve a substantial amount of said compounds, said solution having a pH lower than the pH of the electrolyte which contacted that side of the membrane during the normal cell electrolysis.

2. The method of Claim -1 wherein the brine fed to the cell contains less than about 50 ppm carbon oxide during at least 50 percent of the normal elec¬ trolysis operation of the cell.

3. The method of Claim 1 which further comprises drying the membrane after regeneration.

4. The method of Claim 1 wherein the membrane is regenerated in place in' the cell and both compartments contain liquid solutions.

5. The method of Claim 4 wherein the membrane is regenerated after it has become fouled with compounds of multivalent cations accumulated from the brine fed to the cell during the normal cell electrolysis and reducing the cell voltage to less than about 80 percent of the normal electrolysis voltage employed in the cell.

6. The method of Claim 4 or 5 wherein the cell voltage is reduced to the cathodic protection voltage of the cell so that the cathode is afforded cathodic protection during membrane regeneration.

7. The method of Claim 4, 5 or 6 wherein the pH of the solution in the anolyte chamber is decreased to less than 2.0 during membrane regeneration.

8. The method of any one of Claims 4 to 7. wherein the solution in the catholyte chamber is main¬ tained at a pH below 10 during membrane regeneration.

9. The method of any one of Claims 4 to 8 wherein regeneration of the membrane is carried out for at least one hour.

10. The method of Claim 4 wherein the amount of carbon oxide employed in the brine feed of normal cell operation is less than about 2 ppm; wherein during membrane regeneration the voltage is reduced to the cathodic protection voltage of the cell; the pH of the solution in the anolyte compartment is maintained in a range of from 0.5 to about 2.0 during substantially most of the time required for membrane regeneration to be accomplished; wherein the pH of the solution in the catholyte compartment is maintained at a level below about pH 8 for at least half of the time during which membrane regeneration is carried out; and wherein membrane regeneration is carried out for at least ten hours.

11. The method of Claim 4, wherein the alkali metal halide solution is an aqueous sodium chloride solution, wherein the brine fed to the cell contains less than about 2 ppm carbon oxide, wherein during membrane regeneration, the cell voltage is reduced or turned off and the membrane is contacted with an anolyte solution having a decreased pH range of from 0.5 to 2.0 and a catholyte solution having a pH of less than 8, and wherein regeneration of the membrane is carried out for at least one hour.