AU2015215866B2 - Composition in the form of liquid for maintenance of contact lenses and medical materials - Google Patents

Abstract

COMPOSITION IN THE FORM OF LIQUID FOR MAINTENANCE OF CONTACT LENSES AND MEDICAL MATERIALS Abstract The invention relates to a composition, particularly in the form of liquid to be used externally for rinsing contact lenses, containing a nanocrystalline photocatalyst active in visible light, and optionally hydrogen peroxide.

Description

AUSTRALIA Patents Act 1990 Uniwersytet Jagiellonski COMPLETE SPECIFICATION STANDARD PATENT Invention Title: Composition in the form of liquid for maintenance of contact lenses and medical materials Divisional of Australian Patent Application No 2011245778 The following statement is a full description of this invention, including the best method of performing it known to us: 1 COMPOSITION IN THE FORM OF LIQUID FOR MAINTENANCE OF CONTACT LENSES AND MEDICAL MATERIALS This application is a divisional of Australian patent application No 2011245778, which is the Australian national phase application of PCT/PL2011/050011 filed 23 April 2011, which claims priority from Polish provisional application P.391056 filed 26 April 2010, the entire contents of which are incorporated by cross-reference. Throughout this specification, unless the context requires otherwise, the word "comprise", or variations such as "comprises" or "comprising", will be understood to imply the inclusion of a stated element, integer or step, or group of elements, integers or steps, but not the exclusion of any other element, integer or step, or group of elements, integers or steps. Any discussion of documents, acts, materials, devices, articles or the like which has been included in the present specification is solely for the purpose of providing a context for the present invention. It is not to be taken as an admission that any or all of these matters form part of the prior art base or were common general knowledge in the field relevant to the present invention as it existed before the priority date of each claim of this specification. The subject of the present invention is a composition, especially in the form of a liquid for an external use, for treatment and maintenance of contact lenses, containing nanocrystalline photocatalyst active upon visible light illumination and eventually hydrogen peroxide. The goal of the present invention is to deliver a composition for the production of solutions exhibiting sterilizing properties upon irradiation with visible light and therefore suitable for maintenance of various materials, especially those requiring physiological use, as contact lenses, medical materials (catheters, bandages, syringes, etc.). Unexpectedly, such a defined goal has been achieved by the present invention.

la In one aspect, the present invention provides a composition in the form of a liquid comprising colloidal solution, with surface-modified titanium dioxide nanoparticles smaller than 100 nm as a dispersed phase, and a solution of hydrogen peroxide as the dispersing medium, wherein said titanium dioxide nanoparticles are surface-modified with an organic compound selected from the group consisting of: disodium salt of 4,5-dihydroxybenzene-1,3 disulfonic acid, rutin and ascorbic acid, and wherein the composition exhibits stability in aqueous solution with a pH of about 7. The invention disclosed herein broadly relates to a composition containing titanium dioxide TiO 2 modified on its surface with an organic compound selected from a group encompassing: i. a compound described by the general formula: R R R R HO OH (or -COOH) (or -CGGH) where R denotes -H, -NH 2 , -NH 3 * or -SO 3 M, in which M denotes H', K+, Na*, Li+, NH4,, ii. ascorbic acid, iii. a compound described by the formula: 2 OH HO 0 OH 0 OH 0 OHO -0 I;LOH OH OH OH OH and additionally preferably an aqueous solution of hydrogen peroxide. Preferably, the composition according to the invention is in the form of liquid containing a colloidal solution in which the dispersed phase is composed of the surface modified nanoparticles of titanium dioxide characterized by the particle size lower than 100 nm, while the aqueous solution of hydrogen peroxide plays the role of the dispersion medium. Preferably, the composition according to the present invention exhibits visible light absorption as well as photocatalytic activity in a wavelength range (X) no smaller than ca. 400 nm (the arbitrary threshold between ultraviolet and visible light) to about 600 nm, preferably to ca. 700 nm, as well as absorption of ultraviolet light (X < 400 nm). Equally preferably, it exhibits photocatalytic activity upon irradiation with visible light (wavelengths X higher than 400 nm). Equally preferably, it exhibits photocatalytic activity upon irradiation with ultraviolet light (wavelengths X below 400 nm). Preferably, the organic compound is a compound selected from the group encompassing: phthalic acid, 4-sulfophthalic acid, 4-amino-2-hydroxybenzoic acid, 3 hydroxy-2-naphthylic acid, salicylic acid, 6-hydroxysalicylic acid, 5-hydroxysalicylic acid, 5 sulfosalicylic acid, 3,5-dinitrosalicylic acid, disodium salt of 1,4-dihydroxy-1,3 benzenedisulfonic acid, gallic acid, pyrogallol, 2,3-naphthalenediol, 4-methylcatechol, 3,5-di tert-butylcatechol, p-nitrocatechol, 3,4-dihydroxy-L-phenylalanine (DOPA), rutin as well as ascorbic acid. Equally preferably, it exhibits stability in aqueous solutions at pH of about 7, and the compound bound to the surface (modifier) is a compound selected from the group 3 encompassing: disodium salt of 4,5-dihydroxy-1,3-benzenedisulfonic acid, rutin and ascorbic acid. Preferably, the composition according to the invention contains additionally a buffer, preferably isotonic, stabilizing pH value within the acceptable pharmaceutical range. Preferably, the composition according to the invention contains the surface modified nanocrystalline titanium dioxide within the concentration range of 0.02 to 1 g dm- 3 and hydrogen peroxide, preferably in the concentration range of 0.001 to 0.1 g dm 3 . The composition according to the invention can additionally contain pharmaceutical carriers and excipients. As carriers and excipients the known carriers and excipients used in pharmacy, that are compatible with the active substance, can be applied. In an exemplary composition the modified titanium dioxide characterized by particle size not exceeding 100 nm constitutes stable colloidal systems in solution of PBS buffer, retaining its photocatalytic activity. Preferably, the composition according to the invention constitutes a clear, transparent aqueous solution, containing hydrogen peroxide and nanocrystalline titanium dioxide, the surface of which has been modified with rutin, as the active substances, together with NaCl and phosphate buffer. Preferably, the composition according to the invention or the colloidal solution of titanium dioxide nanoparticles is prepared as a concentrate, preferably containing 40-50 times higher concentration of titanium dioxide as compared to its final concentration in the composition. To obtain the final composition, the concentrate should be diluted with water, preferably with aqueous buffer solution, isotonic aqueous solution, hydrogen peroxide and eventually other additives to the final concentration of all ingredients. Preferably, the composition according to the invention is used to the external use as a contact lens cleaning solution. In general, the composition can be used in the production of a preparation for sterilisation or disinfection, preferably in the production of a photosterilising, photobacteriocidal, photomycocidal, or photocatalytic preparation particularly designed for use in one of the following areas: cosmetology, dermatology, ophthalmology, laryngology, urology, gynaecology, rheumatology, oncology, surgery, veterinary medicine, dentistry, in particular for the sterilization of surfaces and glass or plastic elements, particularly contact lenses, medical catheters, glass and/or plastic conduits as well as other surfaces, the sterilization of which is desirable and/or required. The composition according to the present invention exhibits photocatalytic activity upon irradiation with visible light (X> 400 nm; photocatalysis is the result of the absorption 4 of visible light by the titanium surface complex of the charge-transfer type), as well as ultraviolet light (X < 400 nm; photocatalysis is the result of the absorption of ultraviolet light by the titanium surface complex of the charge-transfer type or directly by titanium dioxide). The irradiation generates so-called reactive oxygen species (OH', 02'-, H 2 0 2 , 102). Unexpectedly it has been shown, that addition of small amounts of peroxides, e.g. hydrogen peroxide, intensifies the photocatalytic properties of the photocatalyst described above. The electron transfer from the conduction band of titanium dioxide to the peroxide molecule leads to the formation of highly oxidative hydroxyl radicals as a consequence of the peroxide reduction. In the presence of trace amounts of metal ions a catalytic decomposition of H 2 0 2 to OH' may occur; the reaction known as a Fenton process. This process unfavorably influences the stability and durability of the composition, however it can be inhibited by addition of agents complexing metal ions, e.g. EDTA (ethylenediaminetetraacetic acid or its salt), in amounts assuring binding of all transition metal ions present in the composition. Example embodiments of the present invention have been shown in figures, in which Fig. 1 shows UV-vis absorption spectra of a colloidal solution of TiO 2 nanocrystals modified respectively with compound K-i (Table 2) (a), ascorbic acid (b) and rutin (c) (each concentration: 0.4 g dm- 3 ); Fig. 2 shows a TEM image recorded for the material K-I @TiO 2 ; Fig. 3 shows the results of irradiation with visible light (using cut-off filters) of a reaction mixture (bovine albumin with a solution of colloidal TiO 2 nanocrystals modified respectively with compound K-1, ascorbic acid and rutin), in the electrophoretic image: K-i@TiO 2 : (a) k > 400 nm, (b) X > 435 nm, (c) X > 455 nm, KA@TiO 2 : (d) X > 400 nm, (e) X > 420 nm, rutin@TiO 2 : (f) X> 420 nm, (g) X> 455 nm; Fig. 4 shows E. coli viability tests in the presence of a colloidal solution of TiO 2 nanocrystals modified with K-i (grey) and in the absence of the photocatalyst (black) (a) during irradiation with light X> 420 nm and (b) E. coli viability test results in the same system in the dark, as well as E. coli viability tests in the presence of a colloidal solution of TiO 2 nanocrystals modified with ascorbic acid (squares) and in the absence of the photocatalyst (triangles) (c) upon irradiation with light X > 420 nm and (d) E. coli viability test results in the same system in the dark. Figure 5 shows the results described in the Example 5 of the comparative tests of photoactivity of the composition according to the present invention, or its components, in the process of proteins oxidation. Figure 6 shows the results described in the Example 6 of the comparative tests of photoactivity of the composition according to the present invention, or its components, in the 5 process of bacteria inactivation. Figure 7 presents the results of azure B photooxidation proving the unexpected synergy between activity of the photocatalyst and hydrogen peroxide. Example 1. Production of a nanocrystalline photocatalyst active in visible light The initial substrate for the synthesis of the materials in question is an unmodified nanocrystalline TiO 2 , which may be produced according to various known procedures. One of them is proposed by Wang et al. (J. Phys. Chem. B, 2000, 104, 93-104). Particles of titanium dioxide TiO 2 smaller than 100 nm (estimated using imaging with a transmission electron microscope) is modified on its surface directly via chemisorption of an organic compound selected from the group according to the present invention with the formation of charge transfer complexes. Photoinduced electron transfer occurs between the organic compound molecule and the semiconductor particle. A photoactive colloid according to the present invention is characterized by a high degree of dispersion and occurs in the form of a suspension or emulsion. Variant 1. A colloidal aqueous solution of TiO 2 (1.2 g dm 3 ) containing isopropanol (10%) in a nitric acid (HNO 3 ) environment (pH = 2.5) was supplemented with crystalline 4,5 dihydroxy-1,3-benzenedisulfonic acid disodium salt (K-1; Table 2) at a molar ratio of 1:1 (modifier:TiO 2 ). A yellow precipitate was formed. The resulting suspension was alkalized with an NaOH solution to pH = 7 (causing the precipitate to dissolve). The solution was placed in a dialysis tube and dialyzed twice against water or an appropriate buffer (i.e. SSC or PBS) in order to remove alcohol and the excess of modifier not bound with TiO 2 . A yellow, clear colloidal solution was produced, which was used in further experiments. The method described is equally suitable for synthesizing nanocrystalline TiO 2 modified with catechol derivatives or salicylic acid or phthalic acid derivatives (syntheses 2 and 3, Tables 1 and 2). In these cases it proved impossible to obtain stable materials (ones that do not undergo aggregation) at pH ~ 7. Variant 2. A colloidal aqueous solution of TiO 2 (1.2 g dm 3 ) containing isopropanol (10%) in a nitric acid environment (HNO 3 , pH = 2.5) was supplemented with a compound from the group A (A-1:A-2; phthalic acid derivatives) or S (S-1:S-7; salicylic acid derivatives; Table 1) in crystalline form, at a molar ratio of 1:1 (modifier:TiO 2 ). The colloidal solution changed its color. The resulting colloidal solution was alkalized with an NaOH solution to pH = 7. The solution was placed in a dialysis tube and dialyzed twice against water, in order to remove alcohol and any modifier not bound with TiO 2

.

6 Table 1. Phthalic acid and salicylic acid derivatives. Compound symbol Compound name Structural formula COOH A-1 phthalic acid 0 :COOH

SO

3 H A-2 4-sulfophthalic acid OH HO 0 COOH S-1 4-amino-2-hydroxybenzoic acid H2 OH COOH S-2 3-hydroxy-2-naphthylic acid / / OH COOH S-3 salicylic acid OH OH COOH S-4 6-hydroxysalicylic acid OH OH COOH OH S-5 5-hydroxysalicylic acid HO HO3S - COOH S-6 5-sulfosalicylic acid / OH

O

2 N C OOH S-7 3,5-dinitrosalicylic acid / OH N02 Variant 3. A colloidal aqueous solution of TiO 2 (1.2 g dm 3 ) containing isopropanol (10%) in a nitric acid environment (HNO 3 , pH = 2.5) was supplemented with a compound from the group K (K-2:K-8; Table 2) at a molar ratio of 1:1 (modifier:TiO 2 ). The colloidal solution changed its color. The resulting colloidal solution was alkalized with an NaOH solution to pH = 7. The solution was placed in a dialysis tube and dialyzed twice against water, in order to remove alcohol and any modifier not bound with TiO 2

.

7 Table 2. Catechol derivatives. Compound symbol Compound name Structural formula OH OH K-1 disodium salt of 1,4-dihydroxy- OH 1,3-benzenedisulfonic acid NaOS Na COOH K-2 gallic acid HO OH OH K-3 pyrogallol HO -OH OH OH K-4 2,3-naphthalenediol MOH OH K-5 4-methylcatechol OH OH K-6 3,5-di-tert-butylcatechol O OH OH OH K-7 p-nitrocatechol

NO

2 O OH K-8 3,4-dihydroxy-L-phenylalanine

NH

2 (DOPA) OH OH Variant 4A. A colloidal aqueous solution of TiO 2 (1.2 g dm 3 ) containing isopropanol (10%) in a nitric acid environment (HNO 3 , pH = 2.5) was supplemented with a compound with the formula (rutin): 8 OH HO O OH 00 OH 0 0 O OH O OH OH OH OH at a molar ratio of 1:1 (rutin:TiO 2 ). An orange precipitate was formed. The resulting suspension was alkalized with an NaOH solution to pH = 9 (causing the precipitate to dissolve). The solution was placed in a dialysis tube and dialyzed three times. The first dialysis was performed against an aqueous solution of NaOH, pH = 9. The subsequent two dialyses were performed against distilled water, or appropriate buffer (i.e. SSC or PBS, pH ~ 7) in order to remove alcohol and any modifier not bound with TiO 2 . An orange, clear colloidal solution was obtained which was used in subsequent experiments. Variant 4B. A colloidal aqueous solution of TiO 2 (1.2 g dm 3 ) containing isopropanol (10%) in a nitric acid environment (HNO 3 , pH = 2.5) was supplemented with a crystalline compound with the formula (rutin): OHOH OO OH OHO0 OH at a molar ratio of 1:1 (rutin:TiO 2 ). An orange precipitate appeared. The resulting suspension was centrifuged. The precipitate was rinsed several times with an aqueous HCl solution (pH = 2 to 4) until excess modifier (rutin) was rinsed out, which was confirmed 9 spectrophotometrically. Next, the precipitate was suspended in water or a buffered aqueous solution. A clear, stable colloidal solution was produced. Variant 5. A colloidal aqueous solution of TiO 2 (1.2 g dm 3 ) containing isopropanol (10%) in a nitric acid environment (HNO 3 , pH = 2.5) was supplemented with a crystalline ascorbic acid (KA) in a molar ratio 1:1 (KA:TiO 2 ); appearance of orange color was observed. Then, the resulting sol was adjusted to pH = 7 and placed in a dialysis bag and dialyzed twice against an aqueous solution of ascorbic acid (5 mmol dm , pH =7). Orange, clear, colloidal solution was obtained, which was used in further experiments. Nanocrystals of TiO 2 modified with ascorbic acid (KA@TiO 2 ) were stable (did not undergo aggregation) at pH = 7. TiO 2 nanocrystals modified with ascorbic acid or another organic compound according to the present invention may then be subjected to further modifications consisting of conjugation with a molecule increasing the specificity of their activity (i.e. an antibody, peptide, biotin or vitamins). Example 2 Characteristics of the synthesized materials Within the group of materials synthesized as described in Example 1 TiO 2 nanocrystals modified by modifier K-i (K-i@TiO 2 ), rutin (rutin@TiO 2 ) and ascorbic acid (KA@TiO 2 ) showed stability at pH =7. Other materials underwent aggregation, which was manifested in the precipitation at pH > 3-4. UV-vis spectrum of the K-I @TiO 2 is shown in Fig la. Like other materials (stable in acidic solutions) it shows absorption of visible light up to ca. 500-700 nm. The transmission electron microscope image presented in Figure 2 confirms the homogeneity of the material - separated particles, showing no tendency to aggregate are several to twenty nanometers in size. UV-vis spectrum of the KA@TiO 2 material is shown in Figure lb. Like other materials (stable in acidic solutions) KA@TiO 2 shows absorption of visible light up to ca. 600-700 nm. UV-vis spectrum of the rutin@TiO 2 solution is shown in Fig ic. The material shows absorption of visible light to a wavelength of 600 nm. Example 3. Photocatalytic activity of the materials Photodegradation tests were carried out with bovine serum albumin (as a model protein) upon visible light irradiation in the presence of nanocrystalline TiO 2 modified by organic compound selected from the group according to the present invention. The protein concentration in solution was monitored using semi-quantitative method of polyacrylamide gel electrophoresis under denaturing conditions (SDS-PAGE). The reaction mixtures, irrespective of the modification of nanocrystalline TiO 2 , were prepared as follows: 10 A solution of modified TiO 2 (in an amount to yield a final concentration of 0.4 mg/ml in terms of TiO 2 ) was mixed with bovine albumin (final concentration 0.4 mg/ml) and water to a final volume of 2 ml. Irradiation was performed using a high-pressure mercury lamp, HBO-500, as a light source and filters delivering light at a wavelength in the range 420-800 nm. Tests were performed in a quvette purged with a small stream of air during irradiation to ensure a constant oxygen level in solution. During the experiment, samples were taken and subjected to electrophoresis following denaturation in order to monitor the degree of albumin degradation. The electrophoresis was performed in a Laemmli system using a 10% separating gel and a 4% stacking gel. The results are shown in Fig. 3. Sample 0' corresponds to an image of 2 [tg of protein. The photodegradation assays of protein have confirmed the high level of photocatalytic activity of K-i@TiO 2 upon visible light irradiation. The compiled protein electrophoresis images show protein degradation over the exposure time in a sample containing the protein and modified titanium dioxide in water. In the spectral range of 400 800 nm (Fig. 3a) one can observe a clear decrease of protein concentration during irradiation. In a narrower radiation ranges, 435-800 nm and 455-800 nm, the results are slightly poorer than the initial ones (Fig. 3b and 3c). Protein photodegradation assays have confirmed the high level of photocatalytic activity of KA@TiO 2 upon visible light irradiation. During ifradiation within the spectral ranges 400-800 nm and 420-800 nm (Fig. 3d and 3e, respectively) a clear decrease in protein concentration can be observed within several minutes. Protein photodegradation assays have confirmed the high level of photocatalytic activity of rutin@TiO 2 upon visible light irradiation. The compiled protein electrophoresis images show protein degradation over the exposure time in a sample containing the protein and modified titanium dioxide in water. Both in the spectrum range 420-800 nm (Fig. 3f) and in a narrower range of radiation, 455-800 nm (Fig. 3g) one can observe clear decrease in protein concentration throughout the time of exposure. Example 4. Evaluation of the activity of the material in the photoinactivation of bacteria The assays of the ability of the new materials to photoinactivate microorganisms were performed on a model strain of Escherichia coli, and the absence of cytotoxicity in this material to this bacterial strain was demonstrated. The tests assaying the efficiency of the photoinactivation of microorganisms were performed thusly: 11 A suspension of bacteria in water (ca. 106 CFU/ml determined spectrophotometrically) was supplemented with a colloidal solution of nanocrystalline TiO 2 modified with an organic compound selected from the group according to the present invention, to its final concentration of 0.4 mg/ml. The assays were performed under the same irradiation conditions as the protein photodegradation assays (2 ml samples, see above) using a cut-off filter 2 > 420 nm, aerating the sample during irradiation. Small samples were collected in order to evaluate the colony-forming potential of the examined strain. The colony formation ability was determined in dishes through the inoculation of 100 [[1 aliquots of a serial dilution of the bacterial suspension onto minimal medium (DIFCO) and counting the colonies. The results are shown as cell survival fractions S/So. The results obtained for K-i@TiO 2 demonstrate its high activity in the photoinactivation of microorganisms, using the model strain of E. coli (Fig. 4a). At the same time, the cytotoxicity of the tested materials was not observed against this strain (Fig. 4b). Analogous results were obtained for KA@TiO 2 (photoinactivation - Fig. 4c and cytotoxicity - Fig. 4d). Example 5 . Comparison of activity of the composition according to the invention and composition without the additives active towards proteins Photodegradation tests were carried out with bovine serum albumin (a protein as a model substrate) under visible light irradiation in the presence of the composition based on nanocrystalline TiO 2 modified with rutin. The protein concentration in solution was monitored using semi-quantitative method of polyacrylamide gel electrophoresis under denaturing conditions (SDS-PAGE). The reaction mixtures, irrespective of the modification of nanocrystalline TiO 2 , were prepared as follows: The solution of modified TiO 2 (final concentration of 0.32 g dm 3 in terms of TiO 2 ), bovine serum albumin (final concentration of 0.2 g dm 3) and water were mixed together to a final volume of 2 ml. Tests were performed in chambers of 2 ml capacity using LEDs as the light source (Xmax = 470 nm, power of 30 mW). During the experiment, collected samples after protein denaturation were subjected to electrophoretic analysis to determine the extent of albumin degradation. Electrophoresis was performed using Laemni setup with 10% separating gel and 4% stacking gel. The results of measurements are presented in the following figures (sample 0' corresponds to the image of 1 tg of protein): Figure 5a - rutin@TiO 2 in PBS + ifradiation 5 h 12 Figure 5b - rutin@TiO 2 in PBS + 2 mM H 2 0 2 irradiation 5 h Figure 5c - 3% H 2 0 2 (after 5 h in the dark) Example 6. Comparison of activity of the composition according to the invention with composition without active ingredients To a suspension of bacterial strain (Escherichia coli) of various concentrations in PBS a sterile colloidal solution of rutin@TiO 2 (filtered through a sterile syringe filter 0.20 tm) was added (Fig. 6a) or a sterile solution of rutin@TiO 2 with the addition of H 2 0 2 (Fig. 6b) to reach its final concentration of 0.32 g dm 3 (in terms of TiO 2 ). Results were compared to the results obtained for a sterile solution of PBS (Fig. 6c). Tests were performed in chambers of 2 ml capacity using LEDs as the light source (max= 470 nm, power of 30 mW). Suspensions were irradiated for 5 h at ambient temperature. Small volumes of samples were collected to determine the ability of bacteria to form colonies after irradiation. Analogous control experiments were done in the dark. In this case chambers were incubated for 5h in dark at ambient temperature instead of their exposition to irradiation. Colony forming ability was determined by plating the 100 [[1 of serial dilutions of bacterial suspension to the minimum medium (Difco) and counting bacterial colonies after 24 h of bacterial growth on the solid medium at 37 0 C. Results were expressed as survival fraction S/So. The results prove very high activity of tested compositions towards photoinactivation of microorganisms (Fig. 6). No significant cytotoxicity of tested materials to bacterial strains was observed in the dark. Example 7. Synergy of the photocatalyst and hydrogen peroxide The study was performed using a model system in which the decomposition of the dye azur B was monitored. The results are presented in Figure 7. Photodegradation of azur B was observed in the presence of the photocatalyst rutin@TiO 2 at the concentration of 0.32 g dm- 3 (squares), hydrogen peroxide at the concentration of 5 mmol dm- 3 (triangles) and the mixture of the photocatalyst and hydrogen peroxide at the above mentioned concentrations (circles). The experiment was conducted under the following conditions: initial concentration of azur B was 0.8x10-4 mol dm- 3 , irradiation with the high-pressure mercury lamp HBO-500 equipped with the 420 nm cut-off filter (exposure 420 <X < 800 nm). Surprisingly, the activity of the mixture of the photocatalyst and hydrogen peroxide is considerably strengthened as compared to the separate use of the photocatalyst and hydrogen peroxide.

Claims (9)

1. A composition in the form of a liquid comprising colloidal solution, with surface-modified titanium dioxide nanoparticles smaller than 100 nm as a dispersed phase, and a solution of hydrogen peroxide as the dispersing medium, wherein said titanium dioxide nanoparticles are surface-modified with an organic compound selected from the group consisting of: disodium salt of 4,5-dihydroxybenzene-1,3-disulfonic acid, rutin and ascorbic acid, and wherein the composition exhibits stability in aqueous solution with a pH of about 7.

2. The composition according to the claim 1, which shows visible light absorption in the wavelength range (X) of not less than approximately 400 nm to about 700 nm, and ultraviolet light absorption (X < 400 nm).

3. The composition according to claim 2, which shows visible light absorption in the wavelength range (X) of approximately 400 nm to about 600 nm.

4. The composition according to any one of claims 1 to 3, additionally comprising a buffer system to maintain the pH in a pharmaceutically acceptable range.

5. The composition according to claim 4, wherein the buffer system is isotonic.

6. The composition according to the claim 4 or 5, which comprises surface-modified nanocrystalline titanium dioxide within the concentration range of 0.02 g dm- 3 to 1 g dm, hydrogen peroxide, and a stabilizer of hydrogen peroxide.

7. The composition according to claim 6, wherein the concentration of hydrogen peroxide is within the range of 0.001 g dm- 3 to 0.1 g dm.

8. The composition according to claim 7 or 8, wherein the stabilizer of hydrogen peroxide is EDTA.

9. The composition according to any one of claims 4 to 8, further comprising an additive having bacteriocidal and/or mycocidal activity.