AT15781B - Process for plating steel or iron with copper or aluminum. - Google Patents

Process for plating steel or iron with copper or aluminum.

Info

Publication number
AT15781B
AT15781B AT15781DA AT15781B AT 15781 B AT15781 B AT 15781B AT 15781D A AT15781D A AT 15781DA AT 15781 B AT15781 B AT 15781B
Authority
AT
Austria
Prior art keywords
aluminum
iron
copper
steel
plating steel
Prior art date
Application number
Other languages
German (de)
Inventor
Heinrich Wachwitz
Moritz Duenkelsbuehler
Original Assignee
Heinrich Wachwitz
Moritz Duenkelsbuehler
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Heinrich Wachwitz, Moritz Duenkelsbuehler filed Critical Heinrich Wachwitz
Application granted granted Critical
Publication of AT15781B publication Critical patent/AT15781B/en

Description

  

   <Desc/Clms Page number 1> 
 



   Österreichische PATENTSCHRIFT   Nr 15781.   



    HEINRICH   WACHWITZ UND MORITZ   DÜNKELSBÜHLER  
IN NÜRNBERG. 



  Verfahren zum Plattieren von Stahl oder Eisen mit Kupfer oder Aluminium. 



   Den Gegenstand der Erfindung bildet ein Verfahren, um voneinander verschiedene   Unedelmetallo   durch Erhitzung und Druck auf einem einfacheren Wege als bisher mit- 
 EMI1.1 
 hitzung, welche bis zur Schweisstemperatur des Aluminiums erfolgt,   bezweckt xunächst   eine Vorverbindung der zu verbindenden Metalle zu schaffen, um bei dem späteren Erhitzen der zu verbindenden Metalle bis nahezu auf deren Schmelztemperatur eine schädliche   Oxydation der Vorbundnächon   zu verhüten. Erst bei der zweiten   Erhitzung erfolgt die     endgiltigo Verbindung der Metalle.   
 EMI1.2 
 nicht vorschieben können und bringt sie in einen mässig erwärmten Ofen, in   welchem   diese auf zirka 400  C (Schweisstemperatur des   Aiuminiums) erhitzt werden.   



   Bei dieser   Erhitzung,   bei welcher der Stahl nicht oxydiert, hat das Aluminium die Eigenschaft, unter Druck mit den zu verbindenden Metallen eine   Vorverbindung   einzugehen, 
 EMI1.3 
 Walze erhaltene   Verbundstück   kommt in einen zweiten, stärker erwärmten Ofen, in   welchem   es nahezu bis zum Schmelzpunkte des aufzuplattierendenj Kupferbleches (zika 900  C) erhitzt und dann ausgewalzt wird. Soll Aluminium aufplattiert werden, so wird das   Verbundstück   beim zweiten Erhitzen bis nahezu dem Schmelzpunkte des Aluminiums, d. i. zirka    < 00" ('   erwärmt. 



   Im ersten Ofen   bezw.   bei der Borverbindung   kann ein mässiger Erhitzungsgrad   
 EMI1.4 
 Eisen oder Stahl noch nicht zundert, sondern nur anläuft. Dieses   Anlaufen   des Eisens   bezw.   Stahles hindert jedoch die Vorverbindung nicht. 

**WARNUNG** Ende DESC Feld kannt Anfang CLMS uberlappen**.



   <Desc / Clms Page number 1>
 



   Austrian PATENT LETTER No. 15781.



    HEINRICH WACHWITZ AND MORITZ DÜNKELSBUEHLER
IN NUREMBERG.



  Process for plating steel or iron with copper or aluminum.



   The subject matter of the invention is a method to use different base metals by heating and pressure in a simpler way than before.
 EMI1.1
 Heating, which takes place up to the welding temperature of the aluminum, is initially intended to create a pre-connection of the metals to be connected in order to prevent harmful oxidation of the pre-bundle joints when the metals to be connected are subsequently heated to almost their melting temperature. The final connection of the metals does not take place until the second heating.
 EMI1.2
 and puts them in a moderately heated furnace, in which they are heated to around 400 C (welding temperature of the aluminum).



   With this heating, during which the steel does not oxidize, the aluminum has the property of entering into a pre-connection under pressure with the metals to be connected,
 EMI1.3
 The composite piece obtained from the roller is placed in a second, more heated furnace, in which it is heated almost to the melting point of the copper sheet to be plated (zika 900 C) and then rolled out. If aluminum is to be plated on, the composite piece is heated to almost the melting point of the aluminum during the second heating, i.e. i. approx. <00 "('heated.



   In the first oven respectively. the boron compound can have a moderate degree of heating
 EMI1.4
 Iron or steel does not scale yet, only tarnishes. This tarnishing of the iron BEZW. However, steel does not prevent the pre-connection.

** WARNING ** End of DESC field may overlap beginning of CLMS **.

Claims (1)

PATENT-ANSPRUCH : Verfahren zum Plattieren von Stahl oder Eisen mit Kupfer oder Aluminium, dadurch gekennzeichnet, dass das mit Aluminium überzogene Kupfer oder reine Aluminiumblech auf die gereinigte Ohern cho der Stahl- bezw. Eisenplatte oder dicke Barren gelegt und zunächst nur bis zur Schweisstemporatur des Aluminiums (zirka 400 C) erhitzt und durch geeigneten Druck zu einem Stück verbunden wird und dass erst hierauf das Ganze nahezu EMI1.5 **WARNUNG** Ende CLMS Feld Kannt Anfang DESC uberlappen**. PATENT CLAIM: Method for plating steel or iron with copper or aluminum, characterized in that the aluminum-coated copper or pure aluminum sheet on the cleaned Ohern cho the steel or. Iron plate or thick bars are placed and initially only heated up to the welding temperature of the aluminum (approx. 400 C) and connected to one piece by means of suitable pressure, and only then the whole is almost completely EMI1.5 ** WARNING ** End of CLMS field may overlap beginning of DESC **.
AT15781D 1903-01-21 1903-01-21 Process for plating steel or iron with copper or aluminum. AT15781B (en)