DE202013012788U1 - Removable pressure-sensitive adhesive strip - Google Patents
Removable pressure-sensitive adhesive strip Download PDFInfo
- Publication number
- DE202013012788U1 DE202013012788U1 DE202013012788.0U DE202013012788U DE202013012788U1 DE 202013012788 U1 DE202013012788 U1 DE 202013012788U1 DE 202013012788 U DE202013012788 U DE 202013012788U DE 202013012788 U1 DE202013012788 U1 DE 202013012788U1
- Authority
- DE
- Germany
- Prior art keywords
- pressure
- sensitive adhesive
- film strip
- adhesive film
- strip according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
Haftklebfolienstreifen, der sich durch dehnendes Verstrecken im Wesentlichen in der Verklebungsebene rückstands- und zerstörungsfrei wieder ablösen lässt, mit einem Träger, der beidseitig mit jeweils einer Klebemassenschicht ausgerüstet ist, wobei
• beide Klebemassenschichten auf Basis von Vinylaromatenblockcopolymeren und Klebharzen aufgebaut sind,
• mindestens eine der beiden Klebemassenschichten eine außenliegende Klebemassenschicht ist, bei der zu mindestens 75 % (bezogen auf den Gesamtharzanteil) Klebharz gewählt wird mit einem DACP (diacetone alcohol cloud point) von größer -20 °C, und bei der es sich bei den Klebharzen zu mindestens 75 Gew.% um Kohlenwasserstoffharze oder Terpenharze oder eine Mischung dergleichen handelt, und
• der Träger mindestens eine Schicht aufweist, die aus einem Polyurethan besteht mit einer Reißdehnung von mindestens 100 % und einem Rückstellvermögen von über 50 %.
Pressure-sensitive adhesive film strip, which can be detached again by stretching stretching substantially in the bonding plane residue and non-destructive, with a support which is equipped on both sides with a layer of adhesive composition, in each case
Both adhesive layers are based on vinylaromatic block copolymers and adhesive resins,
At least one of the two adhesive layers is an outer adhesive layer in which at least 75% (based on the total resin content) of the adhesive resin is selected with a DACP (diacetone alcohol cloud point) of greater than -20 ° C., and in the case of the adhesive resins at least 75% by weight of hydrocarbon resins or terpene resins or a mixture thereof, and
The support comprises at least one layer consisting of a polyurethane having an elongation at break of at least 100% and a resilience of more than 50%.
Description
Die Erfindung betrifft einen reißfesten Haftklebestreifen auf der Basis von Styrolblockcopolymeren, welcher zur Schaffung einer durch dehnende Verstreckung in Richtung der Verklebungsebene wieder lösbare Verbindung eingesetzt werden kann.The invention relates to a tear-resistant pressure-sensitive adhesive strip based on styrene block copolymers, which can be used to create a connection which can be released again by stretching in the direction of the bond plane.
Elastisch oder plastisch hochdehnbare Selbstklebebänder, welche sich durch dehnendes Verstrecken in der Verklebungsebene rückstands- und zerstörungsfrei wieder ablösen lassen, sind beispielsweise aus der
Eingesetzt werden solche strippfähigen Selbstklebebänder häufig in Form von ein- oder beidseitig haftklebrigen Klebfolienstreifen, die bevorzugt einen nicht haftklebrigen Anfassbereich aufweisen, von welchem aus der Ablöseprozess eingeleitet wird. Besondere Anwendungen entsprechender Selbstklebebänder finden sich unter anderem in
Bevorzugte Einsatzgebiete vorgenannter strippfähiger Klebfolienstreifen beinhalten insbesondere die rückstands- und zerstörungsfrei wieder ablösbare Fixierung leichter bis mittelschwerer Gegenstände im Wohn-, Arbeits- und Bürobereich. Für den Einsatz im Wohn- und Bürobereich werden im Allgemeinen recht dicke Produkte von über 400 µm eingesetzt.
In der Consumer-Elektronik-Industrie - wie zum Beispiel bei der Herstellung von Mobiltelefonen, Digitalkameras oder Laptops - wird der Wunsch nach einer Möglichkeit, die einzelnen Bauteile nach der Nutzung bei der Entsorgung zu trennen, immer größer. Dann können einige Bauteile wiederverwendet oder aufbereitet werden. Oder es ist zumindest eine getrennte Entsorgung ermöglicht. Daher sind wiederlösbare Klebeverbindungen in dieser Industrie von großem Interesse. Insbesondere Klebebänder, die eine hohe Halteleistung besitzen und auf Wunsch leicht entfernt werden können, bilden hier eine sinnvolle Alternative zu Klebestreifen, die zum Ablösen erst vorbehandelt werden müssen, indem sie zum Beispiel erhitzt werden.
Im Bereich der Consumer-Elektronik sind Klebestreifen bevorzugt, die möglichst dünn sind, da die Endgeräte möglichst dünn sein und daher auch alle einzelnen Komponenten wenig Platz beanspruchen sollen.
Beim Einsatz von sehr dünnen strippfähigen Klebestreifen, die ohne Träger auskommen, kommt es vermehrt zu Reißern (siehe
In the consumer electronics industry - for example, in the manufacture of mobile phones, digital cameras or laptops - the desire for a way to separate the individual components after use in disposal, ever larger. Then some components can be reused or recycled. Or at least a separate disposal is possible. Therefore, repositionable bonds are of great interest in this industry. Adhesive tapes in particular, which have a high holding power and can easily be removed if desired, form a sensible alternative to adhesive strips, which first have to be pretreated for detachment, for example by heating them.
In the field of consumer electronics adhesive strips are preferred, which are as thin as possible, since the terminals should be as thin as possible and therefore should also occupy little space all the individual components.
The use of very thin stripable adhesive strips, which do not require a carrier, causes an increasing number of tearing (see
Die
Elastische Trägerschichten werden zum Beispiel in der
Elastic carrier layers are used in the
Weitere Veröffentlichungen wie die
Ein strippfähiger Klebfolienstreifen mit einem geschäumten, nicht haftklebrigen Folienträger wird in
Aufgabe der Erfindung ist es, einen durch Dehnung in Richtung der Verklebungsebene wiederablösbaren Klebestreifen zu finden mit einer Klebmasse auf Basis von Vinylaromatenblockcopolymeren und einem Träger, der hoch dehnbar und zum großen Teil elastisch ist und in welchen keine der in der Klebeschicht eingesetzten Harze aus der Klebeschicht hinein wandern.The object of the invention is to find an adhesive strip which can be redetached by stretching in the direction of the gluing plane with an adhesive based on vinylaromatic block copolymers and a support which is highly elastic and largely elastic and in which none of the resins used in the adhesive layer form the adhesive layer wander into it.
Die Aufgabe wird mit einem gattungsgemäßen Haftklebfolienstreifen erfindungsgemäß gelöst, wie er im Hauptanspruch niedergelegt ist. Gegenstand der Unteransprüche sind dabei vorteilhafte Weiterbildungen des Haftklebfolienstreifens.The object is achieved with a generic pressure-sensitive adhesive film strip according to the invention, as laid down in the main claim. The subject of the dependent claims are advantageous developments of the pressure-sensitive adhesive film strip.
Demgemäß betrifft die Erfindung einen Haftklebfolienstreifen aus zumindest drei Schichten, der sich durch dehnendes Verstrecken im Wesentlichen in der Verklebungsebene rückstands- und zerstörungsfrei wieder ablösen lässt, mit einem Träger, der beidseitig mit jeweils einer Klebemassenschicht ausgerüstet ist, wobei
- • beide Klebemassenschichten auf Basis von Vinylaromatenblockcopolymeren und Klebharzen aufgebaut sind,
- • mindestens eine der beiden Klebemassenschichten eine außenliegende Klebemassenschicht ist, bei der zu mindestens 75 % (bezogen auf den Gesamtharzanteil) Klebharz gewählt wird mit einem DACP (diacetone alcohol cloud point) von größer -20 °C, bevorzugt größer 0°C, und bei der es sich bei den Klebharzen zu mindestens 75 Gew.% um Kohlenwasserstoffharze oder Terpenharze oder eine Mischung dergleichen handelt, und
- • der Träger mindestens eine Schicht aufweist, die aus einem Polyurethan besteht mit einer Reißdehnung von mindestens 100 % und einem Rückstellvermögen von über 50 %.
- Both adhesive layers are based on vinylaromatic block copolymers and adhesive resins,
- At least one of the two adhesive layers is an outer adhesive layer in which at least 75% (based on the total resin content) of the adhesive resin is selected with a DACP (diacetone alcohol cloud point) of greater than -20 ° C., preferably greater than 0 ° C., and at at least 75% by weight of the adhesive resins are hydrocarbon resins or terpene resins or a mixture thereof, and
- The support comprises at least one layer consisting of a polyurethane having an elongation at break of at least 100% and a resilience of more than 50%.
Vorzugsweise weisen die erste und die zweite Klebemassenschicht eine identische Zusammensetzung auf.Preferably, the first and second adhesive layers have an identical composition.
Bevorzugt ist eine Ausführungsform des Klebfolienstreifens, bei der der Träger nur aus einer einzigen Schicht besteht.Preferred is an embodiment of the adhesive film strip, in which the carrier consists only of a single layer.
Besonders vorteilhaft ist ein Klebfolienstreifen bestehend aus
- • einem einschichtigen Träger aus einem Polyurethan, wobei der Träger eine Reißdehnung von mindestens 100 % und ein Rückstellvermögen von über 50 % aufweist, wobei
- • auf den Träger beidseitig jeweils eine Klebemassenschicht aus einer Klebmasse aufgebracht ist, die auf Basis von Vinylaromatenblockcopolymeren und Klebharzen aufgebaut ist, wobei weiter vorzugsweise die Zusammensetzung der Klebemassen identisch ist.
- A single-layered support of a polyurethane, wherein the support has an elongation at break of at least 100% and a resilience of over 50%, wherein
- On the support on both sides in each case an adhesive layer of an adhesive is applied, which is based on vinylaromatic block copolymers and adhesive resins, wherein more preferably the composition of the adhesives is identical.
Damit einschlägig bekannte strippfähige Klebfolienstreifen leicht und rückstandsfrei wieder abgelöst werden können, müssen sie bestimmte klebtechnische Eigenschaften besitzen: Beim Verstrecken muss die Klebrigkeit der Klebfolienstreifen deutlich sinken. Je niedriger die Klebleistung im verstreckten Zustand ist, umso weniger stark wird der Untergrund beim Ablösen beschädigt.So that relevant well-known stripable adhesive film strips can be easily removed again without residues, they must possess certain adhesive properties: When stretched, the tackiness of the adhesive film strips must drop markedly. The lower the adhesive performance in the stretched state, the less the substrate will be damaged during detachment.
Besonders deutlich ist diese Eigenschaft bei Klebemassen auf Basis von Vinylaromatenblockcopolymeren zu erkennen, bei denen in der Nähe der Streckgrenze die Klebrigkeit auf unter 10 % sinkt.This property is particularly evident in the case of adhesives based on vinylaromatic block copolymers in which the tack drops below 10% in the vicinity of the yield strength.
Damit strippfähige Klebebänder leicht und rückstandsfrei wieder abgelöst werden können, müssen sie neben den oben beschriebenen klebtechnischen auch einige bestimmte mechanische Eigenschaften besitzen.
Besonders vorteilhaft ist das Verhältnis der Reißkraft und der Strippkraft größer als zwei, bevorzugt größer als drei.So that stripable adhesive tapes can be removed easily and residue-free again, in addition to the adhesive technology described above, they must also have some specific mechanical properties.
Particularly advantageously, the ratio of the breaking force and the stripping force is greater than two, preferably greater than three.
Dabei ist die Strippkraft diejenige Kraft, die aufgewendet werden muss, um einen Klebestreifen aus einer Klebfuge durch paralleles Ziehen in Richtung der Verklebungsebene wieder zu lösen. Diese Strippkraft setzt sich aus der Kraft, die wie oben beschrieben für das Ablösen des Klebebandes von den Verklebungsuntergründen nötig ist, und der Kraft, die zur Verformung des Klebebandes aufgewendet werden muss, zusammen. Die zur Verformung des Klebebandes erforderliche Kraft ist abhängig von der Dicke des Klebfolienstreifens.
Die zum Ablösen benötigte Kraft ist dagegen in dem betrachteten Dickenbereich des Klebfolienstreifens (50 µm bis 800 µm) unabhängig von der Dicke der Klebestreifen.The stripping force is the force that has to be expended in order to loosen an adhesive strip from a glued joint by pulling it parallel in the direction of the gluing plane. This stripping force consists of the force required for detaching the adhesive tape from the bonding substrates as described above and the force required to deform the adhesive tape. together. The force required to deform the adhesive tape depends on the thickness of the adhesive film strip.
In contrast, the force required for detachment is independent of the thickness of the adhesive strips in the considered thickness range of the adhesive film strip (50 μm to 800 μm).
Die Zugfähigkeit steigt hingegen proportional zur Dicke der Klebestreifen an. Hieraus folgt, dass für Selbstklebebänder mit einem Einschichtaufbau, wie sie in der
Als Haftklebemassen finden bevorzugt solche auf Basis von Blockcopolymeren enthaltend Polymerblöcke überwiegend gebildet von Vinylaromaten (A-Blöcke), bevorzugt Styrol, und solche überwiegend gebildet durch Polymerisation von 1,3-Dienen (B-Blöcke) wie zum Beispiel Butadien und Isopren oder einem Copolymer aus beidem Anwendung. Dabei können die Produkte auch teilweise oder vollständig im Dien-Block hydriert sein. Blockcopolymere von Vinylaromaten und Isobutylen sind ebenfalls erfindungsgemäß nutzbar.Preferred PSAs are those based on block copolymers comprising polymer blocks predominantly formed from vinylaromatics (A blocks), preferably styrene, and those predominantly formed by polymerization of 1,3-dienes (B blocks) such as butadiene and isoprene or a copolymer from both applications. The products may also be partially or completely hydrogenated in the diene block. Block copolymers of vinylaromatics and isobutylene are likewise usable according to the invention.
Vorzugsweise besitzen die Blockcopolymere der Haftklebmassen Polystyrolendblöcke.The block copolymers of the PSAs preferably have polystyrene endblocks.
Die aus den A- und B-Blöcken resultierenden Blockcopolymere können gleiche oder unterschiedliche B-Blöcke enthalten. Die Blockcopolymere können lineare A-B-A-Strukturen aufweisen. Einsetzbar sind ebenfalls Blockcopolymere von radialer Gestalt sowie sternförmige und lineare Multiblockcopolymere. Als weitere Komponenten können A-B-Zweiblockcopolymere vorhanden sein. Sämtliche der vorgenannten Polymere können alleine oder im Gemisch miteinander genutzt werden.The block copolymers resulting from the A and B blocks may contain the same or different B blocks. The block copolymers may have linear A-B-A structures. It is also possible to use block copolymers of radial form as well as star-shaped and linear multiblock copolymers. As further components, A-B diblock copolymers may be present. All of the aforementioned polymers can be used alone or in admixture with each other.
Anstelle der bevorzugten Polystyrolblöcke können als Vinylaromaten auch Polymerblöcke auf Basis anderer aromatenhaltiger Homo- und Copolymere (bevorzugt C8- bis C12-Aromaten) mit Glasübergangstemperaturen von größer 75 °C genutzt werden wie zum Beispiel α-methylstyrolhaltige Aromatenblöcke. Weiterhin können auch gleiche oder unterschiedliche A-Blöcke enthalten sein.Instead of the preferred polystyrene blocks can also be used as vinyl aromatic polymer blocks based on other aromatic homo- and copolymers (preferably C 8 - to C 12 aromatics) with glass transition temperatures greater than 75 ° C such as α-methylstyrene-containing aromatic blocks. Furthermore, the same or different A blocks may be included.
A-Blöcke werden im Zusammenhang dieser Erfindung auch als „Hartblöcke“ bezeichnet. B-Blöcke werden entsprechend auch „Weichblöcke“ oder „Elastomerblöcke“ genannt. Dies spiegelt die erfindungsgemäße Auswahl der Blöcke entsprechend ihrer Glasübergangstemperaturen (für A-Blöcke mindestens 25 °C insbesondere mindestens 50 °C und für B-Blöcke höchstens 25 °C insbesondere höchstens -25 °C) wider.A blocks are also referred to as "hard blocks" in the context of this invention. B blocks are also called "soft blocks" or "elastomer blocks" accordingly. This reflects the inventive selection of blocks according to their glass transition temperatures (for A blocks at least 25 ° C in particular at least 50 ° C and for B blocks at most 25 ° C, in particular at most -25 ° C).
In einer vorteilhaften Ausführungsform weisen die Blockcopolymere einen Polyvinylaromatenanteil von 10 Gew.-% bis 35 Gew.-% auf, bevorzugt zwischen 20 Gew.-% und 32 Gew.-%.In an advantageous embodiment, the block copolymers have a Polyvinylaromatenanteil of 10 wt .-% to 35 wt .-%, preferably between 20 wt .-% and 32 wt .-%.
In einer weiteren bevorzugten Ausgestaltung beträgt der Anteil der Vinylaromatblockcopolymere, insbesondere Styrolblockcopolymere in Summe bezogen auf die gesamte Haftklebmasse mindestens 20 Gew.-%, vorzugsweise mindestens 30 Gew.-%, weiter bevorzugt mindestens 35 Gew.-%.
Ein zu geringer Anteil an Vinylaromatenblockcopolymeren hat zur Folge, dass die Kohäsion der Haftklebemasse relativ niedrig ist.In a further preferred embodiment, the proportion of Vinylaromatblockcopolymere, in particular styrene block copolymers in total based on the total pressure-sensitive adhesive at least 20 wt .-%, preferably at least 30 wt .-%, more preferably at least 35 wt .-%.
Too low a proportion of vinylaromatic block copolymers has the consequence that the cohesion of the PSA is relatively low.
Der maximale Anteil der Vinylaromatblockcopolymere, insbesondere Styrolblockcopolymere in Summe bezogen auf die gesamte Haftklebmasse beträgt maximal 80 Gew.-%, bevorzugt maximal 65 Gew.-%, ganz besonders bevorzugt maximal 60 Gew.-%.
Ein zu hoher Anteil an Vinylaromatenblockcopolymere hat wiederum zur Folge, dass die Haftklebemasse kaum noch haftklebrig ist.The maximum proportion of Vinylaromatblockcopolymere, in particular styrene block copolymers in total, based on the total pressure-sensitive adhesive is at most 80 wt .-%, preferably at most 65 wt .-%, most preferably at most 60 wt .-%.
Too high a proportion of vinylaromatic block copolymers, in turn, has the consequence that the PSA is barely tacky.
Blockcopolymere mit weichen und harten Blöcken, deren Glasübergangstemperaturen deutlich divergieren, bilden in der Regel bei Raumtemperatur eine Domänenstruktur. Diese wird für Kohäsionserzeugung durch physikalische Vernetzung der Klebemasse genutzt. Die unmodifizierten Blockcopolymere von Styrol-Blöcken und Dien/Butylen/Isobutylen/Ethylen/Propylen-Blöcken sind meist nur bis 85 oder bis 100 °C scherstabil, in diesem Temperaturbereich beginnen je nach Zusammensetzung die Hartblöcke zu erweichen.Block copolymers with soft and hard blocks, whose glass transition temperatures diverge significantly, usually form a domain structure at room temperature. This is used for cohesive generation by physical crosslinking of the adhesive. The unmodified block copolymers of styrene blocks and diene / butylene / isobutylene / ethylene / propylene blocks are usually shear stable only up to 85 or 100 ° C., in this temperature range, depending on the composition, the hard blocks begin to soften.
Erfindungsgemäße Haftklebmassen basieren auf ausgewählten Styrolblockcopolymeren. Die Haftklebrigkeit der Polymerengemische wird durch Zugabe von mit der Elastomerphase mischbaren Klebharzen erreicht. Als weitere Abmischkomponenten können u. a. Alterungsschutzmittel, Verarbeitungshilfsmittel, Farbstoffe, optische Aufheller, Stabilisatoren, Endblockverstärkerharze sowie gegebenenfalls weitere Polymere, welche bevorzugt elastomerer Natur sind, genutzt werden.
Die Art und Menge der Abmischkomponenten kann bedarfsweise ausgewählt werden.Pressure-sensitive adhesives according to the invention are based on selected styrene block copolymers. The pressure-sensitive tackiness of the polymer mixtures is achieved by adding adhesive resins which are miscible with the elastomer phase. Other blending components which may be used include, inter alia, anti-aging agents, processing aids, dyes, optical brighteners, stabilizers, endblocker resins, and optionally other polymers which are preferably of an elastomeric nature.
The type and amount of the blending components can be selected as needed.
Die Haftklebemassen weisen neben dem mindestens einen Vinylaromatenblockcopolymer mindestens ein Klebharz auf, um die Adhäsion in gewünschter Weise zu erhöhen. Das Klebharz sollte mit dem Elastomerblock der Blockcopolymere verträglich sein. Bei erfindungsgemäßen Produktaufbauten umfassend zumindest drei Schichten, von denen zumindest eine eine Trägerschicht und zumindest zwei eine Klebeschicht sind ist, wie bereits einleitend ausgeführt, darauf zu achten, dass Klebharze aus der/den Klebeschichten im Wesentlichen nicht in die Trägerschicht migrieren. Die vorliegende Erfindung macht sich im Gegensatz zum Stand der Technik (Einführung von Sperrschichten oder gezielter Einbau der gleichen Harze in Klebeschicht(en) und Trägerschicht) die Idee zunutze, dass in der Klebeschicht/den Klebeschichten hauptsächlich Klebharze eingesetzt werden, die nicht mit der Trägerschicht kompatibel sind und daher nicht die Tendenz zur Migration in die Trägerschicht aufweisen. Entsprechend dieses erfinderischen Konzepts wird zu mindestens 75 % (bezogen auf den Gesamtharzanteil) ein Harz gewählt mit einem DACP (diacetone alcohol cloud point) von größer -20 °C, bevorzugt größer 0 °C, um eine Wanderung der Harze in die polare Trägerschicht, nämlich die erfindungsgemäße PU-Trägerschicht zu vermeiden.
Zudem handelt es sich bei den Klebharzen zu mindestens 75 Gew.-% (bezogen auf den Gesamtharzanteil) um Kohlenwasserstoffharze oder Terpenharze oder eine Mischung dergleichen.The pressure-sensitive adhesives have, in addition to the at least one vinylaromatic block copolymer, at least one tackifier resin in order to increase the adhesion in the desired manner. The adhesive resin should be compatible with the elastomeric block of the block copolymers. In product constructions according to the invention comprising at least three layers, at least one of which is a carrier layer and at least two an adhesive layer, as already mentioned in the introduction, care must be taken that adhesive resins from the adhesive layer (s) do not essentially migrate into the carrier layer. The present invention, in contrast to the prior art (introduction of barrier layers or targeted incorporation of the same resins in adhesive layer (s) and backing layer), takes advantage of the idea that in the adhesive layer (s) mainly adhesive resins are used which are not compatible with the backing layer are compatible and therefore do not have the tendency to migrate into the carrier layer. According to this inventive concept, at least 75% (based on the total resin content) of a resin is selected with a DACP (diacetone alcohol cloud point) of greater than -20 ° C., preferably greater than 0 ° C., in order to migrate the resins into the polar carrier layer, namely to avoid the PU carrier layer according to the invention.
In addition, the adhesive resins are at least 75% by weight (based on the total resin content) of hydrocarbon resins or terpene resins or a mixture of the like.
Es wurde gefunden, dass als Klebrigmacher für die Haftklebemasse(n) insbesondere unpolare Kohlenwasserstoffharze zum Beispiel hydrierte und nicht hydrierte Polymerisate des Dicyclopentadiens, nicht hydrierte, partiell, selektiv oder vollständig hydrierte Kohlenwasserstoffharze auf Basis von C5-, C5/C9- oder Cg-Monomerströmen, Polyterpenharze auf Basis von α-Pinen und/oder ß-Pinen und/oder δ-Limonen vorteilhaft eingesetzt werden können. Vorgenannte Klebharze können sowohl allein als auch im Gemisch eingesetzt werden. Dabei können sowohl bei Raumtemperatur feste als auch flüssige Harze zum Einsatz kommen. Kolophoniumharze, hydriert oder nicht hydriert sind bis zu einem maximalen Anteil von 25 % bezogen auf die Gesamtmasse der Harze in der Klebmasse vorhanden, damit die Klebmassen nicht zu polar werden.It has been found that the tackifiers used for the PSA (s) are, in particular, nonpolar hydrocarbon resins, for example hydrogenated and nonhydrogenated polymers of dicyclopentadiene, nonhydrogenated, partially, selectively or fully hydrogenated hydrocarbon resins based on C 5 , C 5 / C 9 or Cg monomer streams, polyterpene resins based on α-pinene and / or β-pinene and / or δ-limonene can be used advantageously. The aforementioned adhesive resins can be used both alone and in admixture. Both solid and liquid resins can be used at room temperature. Rosin resins, hydrogenated or non-hydrogenated, are present in the adhesive up to a maximum proportion of 25%, based on the total mass of the resins, so that the adhesives do not become too polar.
Als weitere Additive können typischerweise genutzt werden:
- • Plastifizierungsmittel wie zum Beispiel Weichmacheröle, oder niedermolekulare flüssige Polymere, wie zum Beispiel niedermolekulare Polybutene
- • primäre Antioxidantien wie zum Beispiel sterisch gehinderte Phenole
- • sekundäre Antioxidantien, wie zum Beispiel Phosphite oder Thioether
- • Prozessstabilisatoren wie zum Beispiel C-Radikalfänger
- • Lichtschutzmittel wie zum Beispiel UV-Absorber oder sterisch gehinderte Amine Verarbeitungshilfsmittel
- • Endblockverstärkerharze sowie
- • gegebenenfalls weitere Polymere von bevorzugt elastomerer Natur; entsprechend nutzbare Elastomere beinhalten unter anderem solche auf Basis reiner Kohlenwasserstoffe, zum Beispiel ungesättigte Polydiene wie natürliches oder synthetisch erzeugtes Polyisopren oder Polybutadien, chemisch im wesentlichen gesättigte Elastomere wie zum Beispiel gesättigte Ethylen-Propylen-Copolymere, α-Olefincopolymere, Polyisobutylen, Butylkautschuk, Ethylen-Propylenkautschuk, sowie chemisch funktionalisierte Kohlenwasserstoffe wie zum Beispiel halogenhaltige, acrylathaltige, allyl- oder vinyletherhaltige Polyolefine.
- Plasticizers, such as plasticizer oils, or low molecular weight liquid polymers, such as low molecular weight polybutenes
- • primary antioxidants such as sterically hindered phenols
- • secondary antioxidants, such as phosphites or thioethers
- • Process stabilizers such as C radical scavenger
- • Sunscreens such as UV absorbers or hindered amine processing aids
- • Endblock amplifier resins as well
- Optionally further polymers of preferably elastomeric nature; correspondingly useful elastomers include, but are not limited to, those based on pure hydrocarbons, for example, unsaturated polydienes such as natural or synthetically produced polyisoprene or polybutadiene, chemically substantially saturated elastomers such as saturated ethylene-propylene copolymers, α-olefin copolymers, polyisobutylene, butyl rubber, ethylene Propylene rubber, as well as chemically functionalized hydrocarbons such as halogen-containing, acrylate-containing, allyl or vinyl ether-containing polyolefins.
In einer Ausführungsform der vorliegenden Erfindung enthält die Haftklebemasse auch Füllstoffe, beispielhaft, aber nicht einschränkend erwähnt seien Oxide, Hydroxide, Carbonate, Nitride, Halogenide, Carbide oder gemischte Oxid-/Hydroxid-/Halogenidverbindungen des Aluminiums, Siliciums, Zirkoniums, Titans, Zinns, Zinks, Eisens oder der (Erd)alkalimetalle. Hierbei handelt es sich im Wesentlichen um Tonerden zum Beispiel Aluminiumoxide, Boehmit, Bayerit, Gibbsit, Diaspor und ähnliche. Ganz besonders geeignet sind Schichtsilicate wie beispielsweise Bentonit, Montmorillonit, Hydrotalcit, Hectorit, Kaolinit, Boehmit, Glimmer, Vermiculit oder deren Mischungen. Aber auch Ruße oder weitere Modifikationen des Kohlenstoffs, etwa Kohlenstoffnanoröhrchen, können verwendet werden.In one embodiment of the present invention, the PSA also contains fillers, by way of example but not by way of limitation oxides, hydroxides, carbonates, nitrides, halides, carbides or mixed oxide / hydroxide / halide compounds of aluminum, silicon, zirconium, titanium, tin, Zinc, iron or (alkaline) alkali metals. These are essentially clays such as aluminas, boehmite, bayerite, gibbsite, diaspore and the like. Particularly suitable are layered silicates such as bentonite, montmorillonite, hydrotalcite, hectorite, kaolinite, boehmite, mica, vermiculite or mixtures thereof. But also carbon blacks or other modifications of the carbon, such as carbon nanotubes, can be used.
Die Klebmassen können auch mit Farbstoffen oder Pigmenten eingefärbt sein. Die Klebemassen können weiß, schwarz oder farbig sein.The adhesives may also be colored with dyes or pigments. The adhesives may be white, black or colored.
Die Trägerschicht besteht aus Polyurethanen, die durch ihre Monomerzusammensetzung hoch flexibel und dehnbar eingestellt sind. Es können sowohl Polyesterurethane als auch Polyetherurethane zum Einsatz kommen. Dabei müssen die Träger eine Reißdehnung von mindestens 100 % aufweisen und ein Rückstellvermögen von mindestens 50 %, das heißt, dass der elastische Anteil des Trägermaterials größer ist als der plastische Anteil.
Die Dicke der Trägerschicht liegt dabei im Bereich von 10 bis 200 µm, bevorzugt zwischen 20 und 100 µm.
Die Spannung bei 50 % Dehnung sollte kleiner als 20 N/cm sein, bevorzugt kleiner als 10 N/cm, um ein einfaches Ablösen ohne allzu großen Kraftaufwand zu ermöglichen.The carrier layer consists of polyurethanes, which are adjusted by their monomer composition highly flexible and expansible. Both polyester urethanes and polyether urethanes can be used. The carriers must have an elongation at break of at least 100% and a Resilience of at least 50%, that is, that the elastic portion of the carrier material is greater than the plastic portion.
The thickness of the carrier layer is in the range of 10 to 200 .mu.m, preferably between 20 and 100 microns.
The stress at 50% elongation should be less than 20 N / cm, preferably less than 10 N / cm, to allow easy peeling without too much effort.
Zur besseren Verankerung der Haftklebmassen auf dem Träger können die Träger mit den bekannten Maßnahmen wie Corona, Plasma oder Flammen vorbehandelt werden. Auch die Nutzung eines Primers ist möglich. Idealerweise kann aber auf eine Vorbehandlung verzichtet werden.To better anchor the pressure-sensitive adhesives on the carrier, the carriers can be pretreated with the known measures such as corona, plasma or flames. The use of a primer is possible. Ideally, however, pretreatment can be dispensed with.
Die Herstellung und Verarbeitung der Haftklebemassen kann sowohl aus der Lösung als auch aus der Schmelze erfolgen. Das Aufbringen der Haftklebmassen auf die Trägerschicht kann durch direkte Beschichtung oder durch Laminierung, insbesondere Heißlaminierung erfolgen.The preparation and processing of the PSAs can be carried out both from the solution and from the melt. The application of the pressure-sensitive adhesives to the carrier layer can be effected by direct coating or by lamination, in particular hot lamination.
Typische Konfektionierformen der erfindungsgemäßen Haftklebestreifen sind Klebebandrollen sowie Klebestreifen, wie sie zum Beispiel in Form von Stanzlingen erhalten werden.
Vorzugsweise weisen alle Schichten im Wesentlichen die Form eines Quaders auf. Weiter vorzugsweise sind alle Schichten vollflächig miteinander verbunden.
Optional kann ein nicht haftklebriger Anfasserbereich vorgesehen sein, von welchem aus der Ablöseprozess ausgeführt werden kann.Typical packaging forms of the pressure-sensitive adhesive strips according to the invention are adhesive tape rolls and adhesive strips, as obtained, for example, in the form of diecuts.
Preferably, all layers have substantially the shape of a cuboid. Further preferably, all layers are connected to each other over the entire surface.
Optionally, a non-sticky grip area can be provided, from which the detachment process can be carried out.
Der allgemeine Ausdruck „Klebeband“ umfasst im Sinne dieser Erfindung alle flächigen Gebilde wie in zwei Dimensionen ausgedehnte Folien oder Folienabschnitte, Bänder mit ausgedehnter Länge und begrenzter Breite, Bandabschnitte, Stanzlinge, Etiketten und dergleichen.For the purposes of this invention, the general term "adhesive tape" encompasses all flat structures such as films or film sections which are expanded in two dimensions, tapes of extended length and limited width, tape sections, diecuts, labels and the like.
Der Klebfolienstreifen weist vorzugsweise eine Dicke auf von 50 µm bis 800 µm, weiter vorzugsweise von 100 µm bis 600 µm.
Die erste und/oder zweite Klebemassenschicht weist vorzugsweise eine Dicke auf von 20 µm bis 300 µm, weiter vorzugsweise von 30 µm bis 150 µm.The adhesive film strip preferably has a thickness of from 50 μm to 800 μm, more preferably from 100 μm to 600 μm.
The first and / or second adhesive layer preferably has a thickness of from 20 μm to 300 μm, more preferably from 30 μm to 150 μm.
Bevorzugt ist eine Ausführungsform des Haftklebfolienstreifens, bei dem der Träger eine Dicke zwischen 40 und 60 µm, vorzugsweise 50 µm aufweist und die identischen 50 Klebemassenschichten ebenfalls jeweils eine Dicke zwischen 40 und 60 µm, vorzugsweise 50 µm.An embodiment of the pressure-sensitive adhesive film strip in which the support has a thickness between 40 and 60 μm, preferably 50 μm, and the identical 50 adhesive layers likewise each have a thickness between 40 and 60 μm, preferably 50 μm, is preferred.
Anhand der nachfolgend beschriebenen Figuren sowie Beispielen werden besonders vorteilhafte Ausführungen der Erfindung näher erläutert, ohne damit die Erfindung unnötig einschränken zu wollen.With reference to the figures and examples described below, particularly advantageous embodiments of the invention are explained in more detail, without wishing to unnecessarily limit the invention.
Es zeigen
-
1 einen erfindungsgemäßen dreischichtigen haftklebrigen Klebestreifen, -
2 einen erfindungsgemäßen dreischichtigen haftklebrigen Klebestreifen in einer alternativen Ausführungsform.
-
1 a three-layer pressure-sensitive adhesive strip according to the invention, -
2 a three-layer adhesive pressure-sensitive adhesive strip according to the invention in an alternative embodiment.
In der
Der Streifen besteht aus einem Träger
Auf dem Träger sind beidseitig außenliegende Klebemassenschichten
The strip consists of a
On the support are on both sides outside
Das überstehende Ende der Trägerschicht
In der
Um einen Anfasser zu erzeugen, an dem gezogen wird, um das dehnende Verstrecken insbesondere in der Verklebungsebene zu erzielen, ist das eine Ende des Klebefolienstreifens auf beiden Seiten durch das Aufbringen von bevorzugt silikonisierten Folien- oder Papierstücken
In order to create a grip on which to pull to achieve the stretch stretching, especially in the bonding plane, the one end of the adhesive film strip is on both sides by the application of preferably siliconized pieces of film or paper
Nachfolgend wird die Erfindung durch einige Beispiele näher erläutert. The invention will be explained in more detail by some examples.
Die Bestandteile der Haftklebemassen wurden hierbei 40%ig in Toluol gelöst und mit einem Streichbalken auf eine PET-Folie ausgerüstet mit einem trennenden Silikon ausgestrichen, so dass sie nach einer Trocknung bei 110 °C für 15 min eine Schichtdicke von 50 µm aufwiesen.
Anschließend wurden auf jede Seite der Trägerschicht die Klebmasse laminiert bei Raumtemperatur mit einer Gummirolle.
Durch Ausstanzen wurden Haftklebestreifen der gewünschten Abmessungen erhalten.The components of the PSAs were in this case 40% dissolved in toluene and equipped with a coating bar on a PET film equipped with a separating silicone streaked so that they had a layer thickness of 50 microns after drying at 110 ° C for 15 min.
Subsequently, on each side of the backing layer, the adhesive was laminated at room temperature with a rubber roller.
By punching pressure-sensitive adhesive strips of the desired dimensions were obtained.
BeispieleExamples
Vergleichsbeispiel 1:Comparative Example 1
Einschichtiger Aufbau (150 µm Dicke):
Beispiel 2:Example 2:
Mehrschichtaufbau:
- Trägerschicht 50 µm Platilon 4100D
- Carrier layer 50 μm Platilon 4100D
Äußere Schichten (je 50 µm):
Vergleichsbeispiel 3:Comparative Example 3
Einschichtiger Aufbau (150 µm Dicke):
Beispiel 4:Single-layered construction (150 μm thickness):
Example 4:
Mehrschichtaufbau:Multi-layer structure:
Trägerschicht
50 µm Platilon U073backing
50 μm Platilon U073
Äußere Schichten (je 50 µm):
Eigenschaften der eingesetzten Rohstoffe:
Trägerschichten:
Support layers:
Bestandteile der Klebmasse:
Bei den beispielhaften Haftklebestreifen wurden die folgenden mechanischen und klebtechnischen Daten ermittelt:
Die Vergleichsbeispiele 1 und 3 zeigen, dass mit einem Einschichtaufbau die Anzahl der Reißer beim Strippen in einem Winkel von 30° höher liegt als bei einem Klebestreifen mit einer reißfesten Trägerschicht.
Trotzdem lassen sich die Klebestreifen mit relativ geringer Kraft wieder ablösen. Es kommt auch nicht zu einem Spalten des Verbundes, die Haftklebmassen kleben auch nach dem Ablösen noch an der Trägerschicht.Comparative Examples 1 and 3 show that with a single-layer structure, the number of tears during stripping is at an angle of 30 ° higher than with an adhesive strip with a tear-resistant carrier layer.
Nevertheless, the adhesive strips can be detached again with relatively little force. There is also no cleavage of the composite, the pressure-sensitive adhesives stick to the carrier layer even after detachment.
Die beiden Muster mit Trägerschicht zeigten auch nach 3 Monaten Lagerung bei 40 °C keine geringere Anfassklebrigkeit, die Zugfestigkeiten waren ebenfalls unverändert. Das deutet darauf hin, dass die Klebharze nicht aus der Klebmasse in die Trägerschicht gewandert sind.The two samples with carrier layer showed no lower tack after 3 months of storage at 40 ° C, the tensile strengths were also unchanged. This indicates that the adhesive resins have not migrated from the adhesive into the carrier layer.
PrüfmethodenTest Methods
Alle Messungen wurden, sofern nichts anderes angegeben ist, bei 23 °C und 50 % rel. Luftfeuchtigkeit durchgeführt.All measurements were, unless otherwise stated, at 23 ° C and 50% rel. Humidity carried out.
Die mechanischen und klebtechnischen Daten wurden wie folgt ermittelt:The mechanical and adhesive data were determined as follows:
Rückstellvermögen beziehungsweise Elastizität:Resilience or elasticity:
Zur Messung des Rückstellvermögens wurden die Haftklebestreifen um 100 % gedehnt, in dieser Dehnung für 30 s gehalten und dann entspannt. Nach einer Wartezeit von 1 min wurde erneut die Länge gemessen.To measure the resilience, the pressure-sensitive adhesive strips were stretched by 100%, held in this stretch for 30 s and then relaxed. After a waiting time of 1 min, the length was measured again.
Das Rückstellvermögen berechnet sich nun wie folgt:
- L100 :
- Länge des Klebestreifens nach der Dehnung um 100 %
- L0:
- Länge des Klebestreifens vor der Dehnung
- Lend :
- Länge des Klebestreifens nach der
Relaxation von 1 min.
- L 100 :
- Length of the adhesive strip after stretching by 100%
- L 0 :
- Length of the adhesive strip before stretching
- L end :
- Length of the adhesive strip after the relaxation of 1 min.
Das Rückstellvermögen entspricht dabei der Elastizität.The resilience corresponds to the elasticity.
Reißdehnung, Zugfestigkeit und Spannung bei 50 % DehnungElongation at break, tensile strength and stress at 50% elongation
Die Reißdehnung, die Zugfestigkeit und die Spannung bei 50 % Dehnung wurden in Anlehnung an DIN 53504 unter Verwendung von Schulterstäben der Größe
Ablösekraftpeel force
Die Ablösekraft (Strippkraft beziehungsweise Stripspannung) wurde mit Hilfe einer Klebstofffolie mit den Abmessungen 50 mm Länge x 20 mm Breite mit einem am oberen Ende nicht haftklebrigem Anfasserbereich ermittelt. Die Klebstofffolie wurde zwischen zwei deckungsgleich zueinander angeordneten Stahlplatten mit einer Abmessung von 50 mm x 30 mm mit einem Anpressdruck von jeweils 50 Newton verklebt. Die Stahlplatten haben an ihrem unteren Ende je eine Bohrung zur Aufnahme eines S-förmigen Stahlhakens. Das untere Ende des Stahlhakens trägt eine weitere Stahlplatte, über welche die Prüfanordnung zur Messung in der unteren Klemmbacke einer Zugprüfmaschine fixiert werden kann. Die Verklebungen werden für eine Dauer von 24 Stunden bei +40 °C gelagert. Nach der Rekonditionierung auf Raumtemperatur wird der Klebfolienstreifen mit einer Zuggeschwindigkeit von 1000 mm pro Minute parallel zur Verklebungsebene und kontaktfrei zu den Kantenbereichen der beiden Stahlplatten herausgelöst. Dabei wird die erforderliche Ablösekraft in Newton (N) gemessen. Angegeben wird der Mittelwert der Stripspannungswerte (in N pro mm2), gemessen in dem Bereich, in welchem der Klebestreifen auf einer Verklebungslänge zwischen 10 mm und 40 mm von den Stahluntergründen abgelöst ist.The removal force (stripping force or strip tension) was determined with the aid of an adhesive film with the dimensions 50 mm length × 20 mm width with a grip area which was not adhesive at the upper end. The adhesive film was glued between two congruent steel plates with a dimension of 50 mm x 30 mm with a contact pressure of 50 Newtons each. The steel plates each have at their lower end a bore for receiving an S-shaped steel hook. The lower end of the steel hook carries another steel plate over which the test arrangement can be fixed for measurement in the lower jaw of a tensile testing machine. The bonds are stored for 24 hours at +40 ° C. After reconditioning to room temperature, the adhesive film strip is removed at a pulling speed of 1000 mm per minute parallel to the bond plane and without contact with the edge regions of the two steel plates. The required release force is measured in Newtons (N). The average value of the strip tension values (in N per mm 2 ), measured in the area in which the adhesive strip has detached from the steel substrates at a bond length between 10 mm and 40 mm, is indicated.
ReißeranfälligkeitCrushers of vulnerability
Um die Reißeranfälligkeit zu testen, wurden jeweils 20 Klebestreifen der Abmessungen 20 mm x 50 mm, versehen mit einem Anfasser wie bei der Messungen der Stripspannung beschrieben, auf eine Glasplatte verklebt. Anschließend wurde den Anfasser aus der Klebfuge herausstehen lassend eine Polystyrolplatte der Abmessungen 40 mm x 40 mm auf den Klebestreifen geklebt und mit einer Kraft von 100 N angedrückt. Nach einer Aufziehzeit von 10 Tagen bei 40 °C wurden die Klebestreifen durch Ziehen gelöst, wobei in einem Winkel von 30° gezogen wurde. Notiert wurde die Anzahl der abgerissenen Klebestreifen.In order to test the susceptibility to breakage, 20 strips of 20 mm x 50 mm each, provided with a handle as described for measuring the strip tension, were glued to a glass plate. Then the handle was left out of the glued joint and a 40 mm x 40 mm polystyrene plate was glued to the adhesive strip and pressed with a force of 100 N. After a peeling time of 10 days at 40 ° C, the adhesive strips were released by pulling, being pulled at an angle of 30 °. The number of torn off adhesive strips was noted.
KlebharzerweichungstemperaturKlebharzerweichungstemperatur
Die Klebharzerweichungstemperatur wird nach der einschlägigen Methodik durchgeführt, die als Ring & Ball bekannt ist und nach ASTM E28 standardisiert ist.The adhesive resin softening temperature is carried out according to the relevant methodology known as Ring & Ball and standardized according to ASTM E28.
DACPDACP
Der DACP ist der Diaceton-Trübungspunkt und wird durch Abkühlen einer erhitzten Lösung von 5 g Harz, 5 g Xylol und 5 g Diacetonalkohol bis zu dem Punkt bestimmt, bei welchem die Lösung trübe wird.The DACP is the diacetone cloud point and is determined by cooling a heated solution of 5 g of resin, 5 g of xylene and 5 g of diacetone alcohol to the point where the solution becomes cloudy.
ZITATE ENTHALTEN IN DER BESCHREIBUNG QUOTES INCLUDE IN THE DESCRIPTION
Diese Liste der vom Anmelder aufgeführten Dokumente wurde automatisiert erzeugt und ist ausschließlich zur besseren Information des Lesers aufgenommen. Die Liste ist nicht Bestandteil der deutschen Patent- bzw. Gebrauchsmusteranmeldung. Das DPMA übernimmt keinerlei Haftung für etwaige Fehler oder Auslassungen.This list of the documents listed by the applicant has been generated automatically and is included solely for the better information of the reader. The list is not part of the German patent or utility model application. The DPMA assumes no liability for any errors or omissions.
Zitierte PatentliteraturCited patent literature
- US 4024312 A [0002]US 4024312 A [0002]
- DE 3331016 C2 [0002, 0004, 0018]DE 3331016 C2 [0002, 0004, 0018]
- WO 9211332 A1 [0002, 0005]WO 92/33232 A1 [0002, 0005]
- WO 9211333 A1 [0002, 0005]WO 92/1333 A1 [0002, 0005]
- DE 4222849 C1 [0002]DE 4222849 C1 [0002]
- WO 9506691 A1 [0002, 0007]WO 9506691 A1 [0002, 0007]
- DE 19531696 A1 [0002]DE 19531696 A1 [0002]
- DE 19626870 A1 [0002]DE 19626870 A1 [0002]
- DE 19649727 A1 [0002, 0007]DE 19649727 A1 [0002, 0007]
- DE 19649728 A1 [0002, 0007]DE 19649728 A1 [0002, 0007]
- DE 19649729 A1 [0002, 0007]DE 19649729 A1 [0002, 0007]
- DE 19708364 A1 [0002]DE 19708364 A1 [0002]
- DE 19720145 A1 [0002]DE 19720145 A1 [0002]
- DE 19820858 A1 [0002, 0007]DE 19820858 A1 [0002, 0007]
- WO 9937729 A1 [0002, 0003]WO 9937729 A1 [0002, 0003]
- DE 10003318 A1 [0002]DE 10003318 A1 [0002]
- DE 4233872 C1 [0003]DE 4233872 C1 [0003]
- DE 19511288 C1 [0003]DE 19511288 C1 [0003]
- US 5507464 B1 [0003]US 5507464 B1 [0003]
- US 5672402 B1 [0003]US 5672402 B1 [0003]
- WO 9421157 A1 [0003]WO 9421157 A1 [0003]
- DE 4428587 C1 [0003]DE 4428587 C1 [0003]
- DE 4431914 C1 [0003]DE 4431914 C1 [0003]
- WO 9707172 A1 [0003]WO 9707172 A1 [0003]
- DE 19627400 A1 [0003]DE 19627400 A1 [0003]
- WO 9803601 A1 [0003]WO 9803601 A1 [0003]
- DE 19649636 A1 [0003]DE 19649636 A1 [0003]
- DE 19720526 A1 [0003]DE 19720526 A1 [0003]
- DE 19723177 A1 [0003]DE 19723177 A1 [0003]
- DE 19723198 A1 [0003]DE 19723198 A1 [0003]
- DE 19726375 A1 [0003]DE 19726375 A1 [0003]
- DE 19756084 C1 [0003]DE 19756084 C1 [0003]
- DE 19756816 A1 [0003]DE 19756816 A1 [0003]
- DE 19842864 A1 [0003]DE 19842864 A1 [0003]
- DE 19842865 A1 [0003]DE 19842865 A1 [0003]
- WO 9931193 A1 [0003]WO 9931193 A1 [0003]
- WO 9963018 A1 [0003]WO 9963018 A1 [0003]
- WO 0012644 A1 [0003]WO 0012644 A1 [0003]
- DE 19938693 A1 [0003]DE 19938693 A1 [0003]
- DE 19708366 A1 [0005]DE 19708366 A1 [0005]
- DE 2728346 A1 [0005]DE 2728346 A1 [0005]
- WO 2010/141248 A1 [0006]WO 2010/141248 A1 [0006]
Claims (37)