CN105174847B - 一种利用黄河泥沙的商品混凝土 - Google Patents
一种利用黄河泥沙的商品混凝土 Download PDFInfo
- Publication number
- CN105174847B CN105174847B CN201510596853.0A CN201510596853A CN105174847B CN 105174847 B CN105174847 B CN 105174847B CN 201510596853 A CN201510596853 A CN 201510596853A CN 105174847 B CN105174847 B CN 105174847B
- Authority
- CN
- China
- Prior art keywords
- yellow river
- river mud
- concrete
- commerical ready
- mixed concrete
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种利用黄河泥沙的商品混凝土,每立方米混凝土由以下原料制备而成:水泥250~280kg、粉煤灰70~100kg、矿渣微粉50~70kg、黄河泥沙700~900kg、石1000~1100kg、减水剂3~6kg、水120~150kg;所述黄河泥沙粒径在40~10目。本发明利用黄河泥沙制备的商品混凝土,以粒径大于0.4mm的经过除杂的黄河泥沙为原料,在经过科学合理的添加其他制备混凝土原材料,制得的商品混凝土28天强度可达到C40以上,并且利用黄河泥沙的可塑性可减少添加粉煤灰导致的混凝土易开裂的问题,同时,使用本发明商品混凝土配方减少了水泥的使用量,节约了成本。
Description
技术领域
本发明属于建筑材料技术领域,具体涉及一种利用黄河泥沙制备的商品混凝土。
背景技术
混凝土材料是建筑工程必不可少的材料,商品混凝土,又称预拌混凝土,简称为商砼,是目前混凝土材料的主要产品,现代建筑施工大部分均使用商品混凝土。商品混凝土强度值是一个重要的指标,目前高强度混凝土应用越来越广,是未来混凝土发展的主要方向之一。
黄河泥沙是一种固体废物,由黄土高原每年输入黄河的泥沙高达16 亿吨,大量黄河泥沙逐年淤积,造成河道阻塞、河床抬高和诸多环保问题。治理黄河泥沙已经成为治理黄河的重点和难点,但其有效利用率仍然很低。近年来关于黄河泥沙利用的研究越来越热,尤其是应用于建筑行业,如专利CN200810014994.7公开了使用黄河泥沙制作免烧砖的技术,专利CN201310563180.X公开了使用黄河沙制备蒸压加气混凝土砌块及制备方法的技术,专利CN200810197323.9公开了使用黄河泥沙制备环保陶瓷清水砖的方法。然而,这些专利对黄河泥沙的使用比较粗放,黄河泥沙利用率低,且均没有达到精选或筛选分级的程度,但是黄河泥沙粒径的不同其矿物成分含量差异较大,不同粒径黄河泥沙应用于建筑材料或其它材料效果肯定有显著的差异,因此现有技术中对黄河泥沙使用存在一定的不科学及不全面性。
发明内容
本发明的目的就在于为解决现有技术的不足而提供一种利用黄河泥沙制备的商品混凝土。
本发明的目的是以下述技术方案实现的。
一种利用黄河泥沙的商品混凝土,每立方米混凝土由以下原料制备而成:水泥250~280kg、粉煤灰70~100kg、矿渣微粉50~70kg、黄河泥沙700~900kg、石1000~1100kg、减水剂3~6kg、水120~150kg;所述黄河泥沙粒径在40~10目。
所述水泥为强度52.5以上硅酸盐水泥或普通硅酸盐水泥。
所述黄河泥沙经磁选、除杂、筛选处理后使用。
所述粉煤灰为II级粉煤灰,矿渣微粉为S95级以上。
所述石为建筑用碎石,压碎指标值不小于20%。
所述减水剂为聚羧酸高效减水剂。
本发明利用黄河泥沙制备的商品混凝土,以粒径大于0.4mm的经过除杂的黄河泥沙为原料,在经过科学合理的添加其他制备混凝土原材料,制得的商品混凝土28天强度可达到C40以上,并且利用黄河泥沙的可塑性可减少添加粉煤灰导致的混凝土易开裂的问题,同时,使用本发明商品混凝土配方减少了水泥的使用量,节约了成本。
具体实施方式
实施例1
一种利用黄河泥沙的商品混凝土,每立方米混凝土由以下原料制备而成:水泥250~280kg、粉煤灰70~100kg、矿渣微粉50~70kg、黄河泥沙700~900kg、石1000~1100kg、减水剂3~6kg、水120~150kg;所述黄河泥沙粒径在40 ~10目,平均粒径大于0.4mm。
黄河泥沙选自开封段,其中二氧化硅的含量在61-75%之间,从抽沙船抽出以后经过磁选机、泥沙水筛分设备分级筛选,选取已除杂、脱泥且在40~10目的黄河泥沙作为制备商品混凝土的原材料;所述水泥为强度52.5以上硅酸盐水泥或普通硅酸盐水泥;所述粉煤灰为II级粉煤灰,比表面积为500~600m2/kg;矿渣微粉为S95级以上,比表面积为400~450m2/kg;所述石为建筑用碎石,压碎指标值不小于20%;粒径为10~30mm,连续级配合理;所述减水剂为聚羧酸高效减水剂。
本发明商品混凝土制备方法与现有技术相同,这里不再赘述。
粉煤灰的使用可减少水泥使用量,提高混凝土的耐久性,然而使用粉煤灰较多易导致混凝土出现裂缝,通过使用黄河泥沙可很好的弥补这个问题,同时将黄河泥沙经过筛选后,选取粒径大于0.4mm的使用,可以避免使用“黄河面砂”造成混凝土强度不高、容易开裂的问题;使用聚羧酸高效减水剂可以减少水的使用,减少水灰比,进一步提高混凝土强度,矿渣的使用可以提升商品混凝土质量的稳定性,进一步提高混凝土的耐久性,因此使用本发明制备的商品混凝土性能优异,质量较好。
实施例2
一种利用黄河泥沙的商品混凝土,每立方米混凝土由以下原料制备而成:水泥250kg、粉煤灰80kg、矿渣微粉55kg、黄河泥沙900kg、石1050kg、减水剂4kg、水130kg;所述黄河泥沙粒径在40~10目,其他同实施例1;用此配方生产的混凝土28天强度为48Mpa,在相同生产条件下比使用细度模数为2.3~3.0的中沙生产的混凝土28天强度大7Mpa。
实施例3
一种利用黄河泥沙的商品混凝土,每立方米混凝土由以下原料制备而成:水泥280kg、粉煤灰90kg、矿渣微粉65kg、黄河泥沙800kg、石1100kg、减水剂5kg、水120kg;所述黄河泥沙粒径在40~10目,其他同实施例1;用此配方生产的混凝土28天强度为53Mpa,在相同生产条件下比使用细度模数为2.3~3.0的中沙生产的混凝土28天强度大5Mpa。
实施例4
一种利用黄河泥沙的商品混凝土,每立方米混凝土由以下原料制备而成:水泥270kg、粉煤灰70kg、矿渣微粉60kg、黄河泥沙850kg、石1000kg、减水剂3kg、水140kg;所述黄河泥沙粒径在40~10目,其他同实施例1;用此配方生产的混凝土28天强度为51Mpa,在相同生产条件下比使用细度模数为2.3~3.0的中沙生产的混凝土28天强度大6Mpa。
实施例5
一种利用黄河泥沙的商品混凝土,每立方米混凝土由以下原料制备而成:水泥260kg、粉煤灰100kg、矿渣微粉50kg、黄河泥沙700kg、石1025kg、减水剂6g、水150kg;所述黄河泥沙粒径在40~10目,其他同实施例1。
实施例6
一种利用黄河泥沙的商品混凝土,每立方米混凝土由以下原料制备而成:水泥255kg、粉煤灰70kg、矿渣微粉50kg、黄河泥沙750kg、石1000kg、减水剂3.5g、水125kg;所述黄河泥沙粒径在40~10目,其他同实施例1。
实施例7
一种利用黄河泥沙的商品混凝土,每立方米混凝土由以下原料制备而成:水泥275kg、粉煤灰100kg、矿渣微粉70kg、黄河泥沙700kg、石1100kg、减水剂4.5g、水120kg;所述黄河泥沙粒径在40~10目,其他同实施例1。
实施例8
一种利用黄河泥沙的商品混凝土,每立方米混凝土由以下原料制备而成:水泥250kg、粉煤灰75kg、矿渣微粉70kg、黄河泥沙900kg、石1075kg、减水剂6g、水150kg;所述黄河泥沙粒径在40~10目,其他同实施例1。
实施例9
一种利用黄河泥沙的商品混凝土,每立方米混凝土由以下原料制备而成:水泥280kg、粉煤灰95kg、矿渣微粉60kg、黄河泥沙800kg、石1090kg、减水剂3g、水145kg;所述黄河泥沙粒径在40~10目,其他同实施例1。
Claims (1)
1.一种利用黄河泥沙的商品混凝土,其特征在于每立方米混凝土由以下原料制备而成:水泥250~280kg、粉煤灰70~100kg、矿渣微粉50~70kg、黄河泥沙700~900kg、石1000~1100kg、减水剂3~6kg、水120~150kg;所述黄河泥沙粒径在40~10目;所述水泥为强度52.5以上硅酸盐水泥或普通硅酸盐水泥;所述黄河泥沙经磁选、除杂、筛选处理后使用;所述粉煤灰为II级粉煤灰,矿渣微粉为S95级以上;所述石为建筑用碎石,压碎指标值不小于20%;所述减水剂为聚羧酸高效减水剂。