CN105130225A - 一种抗裂低碱环保型凝胶材料 - Google Patents

一种抗裂低碱环保型凝胶材料 Download PDF

Info

Publication number
CN105130225A
CN105130225A CN201510459075.0A CN201510459075A CN105130225A CN 105130225 A CN105130225 A CN 105130225A CN 201510459075 A CN201510459075 A CN 201510459075A CN 105130225 A CN105130225 A CN 105130225A
Authority
CN
China
Prior art keywords
raw material
wastes
content
gel material
alkali
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510459075.0A
Other languages
English (en)
Inventor
王东
蒋海托
刘�英
汪清
王玉舟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tongling Hai Yuan Ultrafine Powder Co Ltd
Original Assignee
Tongling Hai Yuan Ultrafine Powder Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tongling Hai Yuan Ultrafine Powder Co Ltd filed Critical Tongling Hai Yuan Ultrafine Powder Co Ltd
Priority to CN201510459075.0A priority Critical patent/CN105130225A/zh
Publication of CN105130225A publication Critical patent/CN105130225A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种抗裂低碱环保型凝胶材料，其原料及其重量配比为：石灰质原料50～65％，粘土质原料10～20％，镁质原料7～13％，铝矿废石1.5～5％，铜矿渣4～9％、废钢5～7％、沸石1.5～5％、硅灰0.5～1％和高含氯废弃物5～8％。本发明主要通过高氯废弃物中的CL离子与高碱原料中的K离子结合产生KCL，从而减低原料中K含量的原理。同时本发明采用工业废渣铜矿渣作铁质校正原料，铝矿废石作铝质校正原料，既解决固体废气物对环境的污染，也变废为宝。本发明的凝胶材料具有碱含量低、中等水化、强度高、微膨胀等特性。

Description

一种抗裂低碱环保型凝胶材料
技术领域
本发明涉及凝胶材料领域，尤其涉及一种抗裂低碱环保型凝胶材料。
背景技术
目前，大体积混凝土工程尤其是大坝混凝土，由于水化放热导致其内部温度升高，内部温度过高则可能导致混凝土内外温差过大，从而产生较大的温度应力；当温度应力大于混凝土的抗拉强度时，会导致大体积混凝土的开裂；因此，一般大体积混凝土工程尤其是水电大坝工程，通常采用水化放热相对较少的中热硅酸盐水泥做凝胶材料，然而在应用、研究过程中发现，中热硅酸盐水泥浇筑的混凝土的自生体积变形有微收缩，从而影响了混凝土的抗裂性能。此外，碱集料反应造成的破坏性膨胀也是导致大体积混凝土尤其大坝混凝土产生裂缝的主要原因之一。
随着水电工程对大坝混凝土技术要求的提高，仅仅具有中等水化热的水泥是不能避免大坝建设中混凝土碱集料反应、混凝土干缩等问题引起混凝土开裂的风险。
发明内容
本发明的目的是解决现有技术的不足，提供一种需要碱含量更低并具有微膨胀特性的凝胶材料。
本发明采用的技术方案是：一种抗裂低碱环保型凝胶材料，其原料及其重量配比为：石灰质原料50～65％，粘土质原料10～20％，镁质原料7～13％，铝矿废石1.5～5％，铜矿渣4～9％、废钢5～7％、沸石1.5～5％、硅灰0.5～1％和高含氯废弃物5～8％。
作为本发明的进一步改进，所述高含氯废弃物为垃圾焚烧飞灰。
作为本发明的更进一步改进，石灰质原料为石灰石，粘土质原料为砂岩，镁质原料为白云石。
本发明采用的有益效果是：本发明主要通过高氯废弃物中的CL离子与高碱原料中的K离子结合产生KCL，从而减低原料中K含量的原理。同时本发明采用工业废渣铜矿渣作铁质校正原料，铝矿废石作铝质校正原料，既解决固体废气物对环境的污染，也变废为宝。本发明的凝胶材料具有碱含量低、中等水化、强度高、微膨胀等特性。
具体实施方式
下面结合实施例1，对本发明做进一步的说明。
实施例1，一种抗裂低碱环保型凝胶材料，其原料及其重量配比为:石灰石50％，砂岩10％，白云石10％，铝矿废石4％，铜矿渣8％、废钢6％、沸石4％、硅灰1％和垃圾焚烧飞灰7％。
实施例2，一种抗裂低碱环保型凝胶材料，其原料及其重量配比为:石灰石62％，砂岩10％，白云石7％，铝矿废石2％，铜矿渣5％、废钢5％、沸石1.5％、硅灰0.5％和垃圾焚烧飞灰7％。
将上述实施例的凝胶材料进行化学成分控制分析及常规物理性能测试。其试验结果表明，本发明的凝胶材料具有低碱微膨胀特性，水泥样品碱含量低于0.30％(GB200-2003要求小于等于0.60％)，且28天抗压强度高，水化热低，完全优于标准要求
本发明主要通过高氯废弃物中的CL离子与高碱原料中的K离子结合产生KCL，从而减低原料中K含量的原理。同时本发明采用工业废渣铜矿渣作铁质校正原料，铝矿废石作铝质校正原料，既解决固体废气物对环境的污染，也变废为宝。本发明的凝胶材料具有碱含量低、中等水化、强度高、微膨胀等特性。
本领域技术人员应当知晓，本发明的保护方案不仅限于上述的实施例，还可以在上述实施例的基础上进行各种排列组合与变换，在不违背本发明精神的前提下，对本发明进行的各种变换均落在本发明的保护范围内。

Claims (3)

1.一种抗裂低碱环保型凝胶材料，其特征是其原料及其重量配比为：石灰质原料50～65％，粘土质原料10～20％，镁质原料7～13％，铝矿废石1.5～5％，铜矿渣4～9％、废钢5～7％、沸石1.5～5％、硅灰0.5～1％和高含氯废弃物5～8％。
2.根据权利要求1所述的一种抗裂低碱环保型凝胶材料，其特征是所述高含氯废弃物为垃圾焚烧飞灰。
3.根据权利要求1或2所述的一种抗裂低碱环保型凝胶材料，其特征是石灰质原料为石灰石，粘土质原料为砂岩，镁质原料为白云石。
CN201510459075.0A 2015-07-30 2015-07-30 一种抗裂低碱环保型凝胶材料 Pending CN105130225A (zh)