ZA200300885B - Preparation of fatty hydroxamate.

Info

Publication number: ZA200300885B
Application number: ZA200300885A
Authority: ZA
Inventors: Terence Charles Hughes
Original assignee: Ausment Ltd
Priority date: 2000-07-28
Filing date: 2003-01-31
Publication date: 2004-02-09
Also published as: AUPQ906800A0

Description

‘PREPARATION OF FATTY HYDROXAMATE

The present invention relates to a method for preparing salts and acids of fatty hydroxamates, to compositions containing salts of fatty hydroxamic acids and to a method of recovery of metals by a flotation process using the compositions.

Background

Fatty hydroxamates are used as reagents in hydrometallurgical operations, particularly in froth flotation of oxidized minerals. The performance of fatty hydroxamates in such procedures is dependent upon the composition of the reagent. There is a need for an efficient method for producing fatty hydroxamates for industrial uses which provides reliable results.

Summary of the Invention

The invention provides a method for preparation of fatty hydroxamic acids and salts thereof including reacting a fatty acid derivative with an aqueous solution of a hydroxylamine. The fatty acid derivative is preferably selected from the group of acid chlorides and esters. More preferably the fatty acid derivative is an ester selected from the group consisting of lower alkanol esters and glyceride esters. Hydroxylamine may be formed in situ from hydroxylamine salts in the presence of an alkaline aqueous solution which is typically an aqueous solution of alkali metal hydroxide. Alternatively hydroxylamine may be generated in situ from nitrosyl chloride or from ammonia in the presence of an oxidizing agent such as hydrogen peroxide.

During the reaction process the fatty hydroxamate which is formed generally produces foam. In the process of the present invention measures are preferably taken to suppress foam formation during the reaction. The reaction mixture may include a defoaming agent such as a lower alkanol or hydrocarbon.

The defoaming agent is generally present in an amount of no more than 20% by weight of the reaction mixture and typically amounts of no more than 5% by weight of the composition are required.

Alternatively we have found that a foam suppressing agent is not required if the reaction is conducted under pressure. The amount of pressure required for effective foam suppression may vary between reaction mixtures and the skilled person will be able to determine the appropriate pressure for any system without undue experimentation. Typically, however a pressure generated during the reaction in the range of from 0.1 to 2 atmospheres may be sufficient.

Foam may be adequately controlled in most instances by conducting the reaction in a sealed vessel. Alternatively a process for continuous preparation may use a tubular reactor kept under controlled pressurized conditions.

Detailed Description of Preferred Embodiments

It is a feature of the invention that the reaction is conducted in the presence of an aqueous solution of hydroxylamine in the presence of a strong base preferably consisting of an alkali metal hydroxide. In contrast to previous methods of preparing fatty hydroxamates the present invention allows the use of large amounts of organic solvent to be avoided and prepares the hydroxamate salt directly in the aqueous phase. Until now it has been regarded as important to use the hydroxylamine in an organic solvent such as aliphatic alcohols as the reaction medium in order to obtain reaction of the hydroxylamine and fatty acid ester.

Hydroxylamine may be used in the form of an amine salt such as hydroxylammonium chloride or hydroxylammonium sulfate. In an alkali metal hydroxide solution the amine salts produce reactive hydroxylamine. It is particularly preferred to use hydroxylammonium sulfate as it is more readily available and preparation of the chloride is generally from the sulfate. The formation of the free hydroxylamine solution is carried-out in glass or inert plastic lined equipment. The free hydroxylamine concentration is maintained at levels below 10% and the reactive hydroxylamine solution is used directly after removal of the precipitated alkali sulfate.

In one embodiment of the invention hydroxylamine or its salts are prepared from nitrosyl chloride in the presence of UV radiation:

0 0

NOCLhv

R—C—O0CH, —— » R —C ——NHOH

MOH

R—C — NOHM'

A further oximation process which generates hydroxylamine in situ involves the oxidation of ammonia using an oxidant, particularly hydrogen peroxide: 0 0

Il NH; - H,0, I

R—C—O0CH, ——» R— C—NHOH catalyst

MOH i

R —C — NOHM wherein M is an alkali metal such as sodium or potassium and R is fatty alkyl.

The process of oximation of the fatty acid ester using ammonia and peroxide generally uses a catalyst. The catalyst is preferably selected from catalysts containing titanium and silicon. Preferably the catalyst has a zeolite structure.

This oximation process may involve a pre-treatment of the catalyst with hydrogen peroxide.

The fatty hydroxamate is prepared using a fatty acid derivative. The fatty acid derivative may be a fatty acid chloride or an ester such as a lower alkanol ester of glyceride. The glyceride may be a mono-, di- or tri- glyceride.

The fatty hydroxamate is preferably prepared using a lower alkanol ester of fatty acid. The ester is typically a Cy to C4 alkanol ester of a fatty acid having from 6 to 18 carbon atoms. Preferably the alkanol portion of the ester is methyl or ethyl. The fatty acid portion of the fatty acid derivative may include one or more fatty acids. The most preferred fatty acid composition has a high concentration of fatty acids in the Cg to C4 range and most preferably the Cs to Cio range.

The fatty acid component of the ester preferably contains 95% w/w of Cs to Cy4 and preferably at least 80% w/w of Cg to Cy fatty acids. Most preferably at least 95% w/w of the fatty acid component is made up of Cg to Cy, fatty acids or a mixture thereof. Fatty acids in this range may be prepared by fractionation of an oil containing a high proportion of Cg — C4 acids such as coconut oil and palm kernel oil.

The methyl ester of fractionated coconut oil is a preferred material for preparation of “Fatty Hydroxamate’. Coconut methyl ester is preferably enriched with a Cg and Cj fraction in the composition ratio of 60:40 respectively.

Methyl ester of fractionated palm kernel oil can also be converted into a fatty hydroxamate material with characteristic flotation properties. Palm kernel oll contains a Cg to C49 composition similar to coconut oil Straight palm oil comes from a different part of the plant and is a less suitable composition of the Cg and 16 Cy fraction than palm kernel oil.

We have also found that glycerides from coconut or palm kernel oil, like methyl ester, are reactive to free hydroxylamine and lead to the formation of fatty hydroxamate. The advantage of this process is that it allows the use of glyceride feed stocks from fractionated coconut or palm kernel oil into fatty hydroxamate without the intermediate reaction steps of transesterification, or saponification followed by esterification.

The most preferred glycerides are di or tri- glycerides with a high proportion of

Cz and Cy fatty acid chains attached with glycerol site. Most of the fatty acid component is made up of Cg and Cy, fatty acids or a mixture thereof.

Suitable carboxylic acids can also be derived from petrochemical sources. In this case the acids will most likely have a branched carbon chain structure rather than the straight carbon chain in natural fatty acids.

Examples of suitable petrochemical based carboxylic acids are: Cg-cekanoic acid (essentially iso-octanoic acid), 2-ethyl hexanoic acid, Cs-cekanoic acid (essentially 3,5,5-trimethyl hexanoic acid) and neo-decanoic acid (mixture).

Petrochemical ‘derived alkyl (Cs-C1s) hydroxamates have been shown to have similar flotation advantages to that of natural Cs and C+ fatty hydroxamate. 5 Cekanoic acids are short chain aliphatic carboxylic acids produced by Exxon

Mobil using their proprietary “0X0 process”. The cekanoic Cg and C4, product is a mixture of branched isomers whereas the cekanoic Cg acid is essentially - 3,5,5-trimethyl hexanoic acid. lt is found that the reactivity of cekanoic methyl ester especially those having a significant proportion of a-branching are less reactive to hydroxylamine. With derivatisation into acid chloride instead of ester, the reactivity of cekanoic acid toward free hydroxylamine is enhanced. Examples of a-branching fatty acids are Cg-cekanoic, 2-ethyl-hexanoic and neo-decanoic acids which, after conversion into their corresponding acid chloride, react effectively with hydroxylamine to give fatty hydroxamate.

Suitable carboxylic acids can also be derived from petrochemical sources, in this case the acids will probably have a branched carbon chain structure rather than the straight carbon chain in natural fatty acids. Examples of suitable petrochemically derived carboxylic acids are Cs cekanoic acid (essentially iso- octanoic); ethyl hexanoic acid, neo-decanoic acid (mixture), Cg cekanoic acid (essentially 3.5.5 tri methyl hexanoic acid).

We have found that fatty hydroxamates derived from Cg to Cio fatty acids provide particularly effective froth flotation collectors. They have been found to produce reagents of great flotation selectivity and recovery for oxidised base metals such as, but not exclusively, Cu, Pb, Zn, Ni, Co and Sn such as the sulfides or oxide based ores or the naturally occurring metals Cu, Ag, Au and platinum group metals when these metals occur in ores, tailings or wastes.

Petrochemical derived alkyl (Cs — C4g) hydroxamates have been shown to have similar flotation advantages to the Cg, C1p potassium fatty hydroxamates.

AMENDED SHEET 2004 -0- 20

5a in the preferred embodiment of the invention the alkali metal hydroxide is preferably sodium hydroxide or potassium hydroxide and potassium hydroxide is particularly preferred. The alkali metal hydroxide is generally present in an excess on a molar basis when compared with the amount of hydroxylamine component. Preferably the hydroxylamine component is present in an excess

AMENDED SHEET 2004 -02- 20 on a molar basis when compared with the amount of fatty acid ester. We have found that particularly good results are obtained when the molar ratio of fatty acid ester to hydroxylamine compound is in the range of 4 to 1.1 and preferably from 2.5 to 1.2. The molar ratio of alkali metal hydroxide to fatty acid ester is preferably in the range of from 4 to 1.5 and more preferably from 3.5 to 2.

The aqueous solution of alkali metal hydroxide will typically have a concentration in the range of 5 to 50% by weight and preferably from 10 to 25% by weight.

The method of the invention will preferably include agitating the reaction mixture to produce mixing of aqueous alkaline and fatty ester organic phases. Suitable mixing apparatus such as an impeller or the like may be used to produce mixing of an aqueous alkaline phase comprising the hydroxylamine and a water insoluble fatty acid ester phase. After a period of stirring a homogeneous mixture is generally formed.

Formation of the fatty hydroxamate may be accompanied by the formation of foam which may be maintained at an acceptable level by the antifoaming agent or by conducting the reaction under pressure. When used the antifoaming agent may be a lower alcohol such as methanol, ethanol or isopropanol or hydrocarbon solvent such as turpentine, diesel, kerosene or aviation fuel. The antifoaming agent is preferably present in an amount of less than 5% and most preferably less than 3% by weight of the total composition.

The reaction process is generally carried out at a temperature of from ambient to 90°. Relatively mild temperatures of up to 60°C and more preferably 35 to 55°C are used.

In contrast to many previous processes we have found that the addition of surfactants to the reaction mixture is unnecessary and undesirable. While some method of forming hydroxamate derivatives have been reported using fatty alcohols and/or other surfactant additives we have found that these additives generally suppress flotation performance of the hydroxamates formed in accordance with the present invention. Accordingly the reaction mixture preferably contains less than 0.5% by weight of added surfactant and most preferably is free of added surfactant. The added surfactant component does not include derivatives of the fatty acid ester component which may be formed as a result of the manufacturing process of the fatty acid esters. However it is preferred that the fatty acid ester has a purity at least 98% by weight .

We have found that the formation of the first small amount of fatty hydroxamate during the reaction procedure assists in mixing of the aqueous alkaline and organic phases to provide a homogenous composition and the hydroxamate may act as a surfactant and/or phase transfer agent to enhance faster reaction.

The fatty hydroxamate salt produced in accordance with the invention will typically exhibit absorption at approximately 3213, 1628 and 1554cm™ due to the presence of organic hydroxamate group. In UV visible analysis it typically exhibits strong absorption of 499nm after colour complexation with Fe Ill at pH 2-3.

The fatty hydroxamates particularly as the K salt may be used to produce froth flotation concentrates from base metal ores and tailings and provide high levels of recovered metal. The fatty hydroxamates can be used alone if only metal oxides or carbonates (eg. SnOj-cassiterite Cu,O-cuprite, Cu(CO3)(OH),- malacite) are present, and are preferably used together with sulfide collectors (eg. xanthates or organo thiophosphates) if a mixture of sulfides and oxidised minerals is present, eg. Cu as chalcopyrite or chalcocite (fresh or oxidised), or as Cu oxides, carbonates, hydroxides or silicates (chryscolla). Metallic Cu, usually tarnished, silver, gold and platinum group metals are also recovered efficiently. A synergistic result appears with the mixed reagents (eg. xanthate plus fatty hydroxamate). For optimum performance and selectivity the fatty hydroxamate is used at pH 8.5 to 10.5 at low dose rates with a standard flotation frother.

The invention further provides a method of froth flotation including combining a fatty hydroxamate in the form of an alkali preferably potassium metal salt with an ore slurry and preferably a frothing agent.

The concentration of the alkali metal hydroxomate is typically in the range of 10 to 1000mg per litre but will depend on the grade and amount of ore and the metals of interest. In terms of the quantity of ore the amount of alkali metal hydroxamate is generally in the range of 0.1 to 500g per tonne but will of course also be highly dependent of these factors.

We have found that the efficiency recovery of particular metals by the flotation method is highly dependent on pH. Recovery of copper and many other metals is enhanced when the pH of the flotation liquor is no lower than 0.5 units less than the pKa of the Bronstead acid corresponding with the fatty hydroxamate.

The pH may be higher than the pKa. The recovery of copper using potassium fatty hydroxamates is enhanced significantly when the pH is at least about 8.5 and more preferably from 8.5 to 10.5. In the case of tin however the optimum pH is typically acidic for example from pH 4 to 5 and this relationship of effectiveness of flotation with pKa is not observed.

The invention will now be demonstrated by, but is in no way limited to, the following examples.

Example 1

Potassium salt of Cs/C1o hydroxamate derivatives from coconut methyl ester.

Hydroxylammonium sulfate (11.6g, 0.14 mole equivalent of NH,OH) was first treated with (16.06g, 0.25 mole) KOH in 50mi distilled water to generate free hydroxylamine reagent. The formation of by-product K»SO4 as precipitate, if necessary, could be easily separated by filtration or slow decantation of liquid reagent. The resulting free hydroxylamine solution in water (7-8%) was immediately reacted with methyl ester of coconut oil (20g, 0.112 mole equivalent of CO,CH3) at 45°C, when agitated by an overhead mechanical stirrer. In order to control the foam rise generated from the reaction, 0.5g of methanol was introduced as an antifoaming agent. After a stirring period of 6 hours the reaction mixture was exposed to air to allow the solvent to gradually evaporate to dryness. The resultant white, crude solid was subjected to an extraction process using warm methanol (4 x 20ml) that allows separation of the hydroxamate salt from K,SO, or any other inorganic impurities. The hydroxamate derivative contained in the methanol extract is finally recovered as a bright white powder by a typical crystallisation process (in other words, by distilling off the methanol as a solvent recycling procedure). After being left on a bench top to dry for 2 to 3 days a 17g yield of white solid was obtained. This product appeared visually identical to the hydroxamate derivative produced when using methanol as a solvent. Its FT-IR spectral characterisation is summarised in Table 1.

Example 2

Sodium salt of Cg-Csp hydroxamate derivatives from coconut methyl ester.

Following the identical procedure of Example 1, NaOH (10.28g, 0.252 mole OH) was used as a base to generate the hydroxylamine reagent. Unlike potassium salt, the sodium salt of hydroxamate appears to be hygroscopic. lts yield of 12 to 15g after crystallisation from methanol falls in the same range as its corresponding potassium salt. Its FT-IR spectral pattern, as seen in Table 1, also displays a close similarity to that seen from the typical hydroxamate derivative produced in a methanol solvent.

FT-IR analysis

Following the standard KBr disc method it was found that samples of both the sodium and potassium salt described above comprised a characteristic hydroxamate functional group. As shown in Table 1, the potassium fatty hydroxamate (AM2) derived from present route (i.e. in water and using hydroxylammonium sulfate salt) produced virtually the same diagnostic signal as AM2 that was made via a methanol solvent route. The amide carbonyl peaks at 1627 and 1554cm™ due to keto-enol tautomers, accompanied with strong hydroxyl (-OH) stretching vibration at 3213cm™, which supports the conclusion that a hydroxamate function (-CONOH'K") is present in the product.

The sodium salt form also shows similar signals, albeit giving a different frequency. This may be partly due to a different counter cation binding effect with conjugate hydroxamate function. It is known that cation size (ionic radii) has an effect on ion-pair stability as shown above structural form. [e) K® o Na®

R-C-NOH R-C-NOH }

Table 1: ester by methanol solvent method "| present method method

Example 3

The procedure of Example 1 was repeated with the exception that the defoaming agent, methanol was omitted and the reaction was carried out in a sealed pressure vessel. The pressure vessel was lined with “Teflon” fluoropolymer and supported by a stainless steel shell and clamp. The pressure vessel was filled to a level of 70% to generate a vapour pressure during the reaction which was found to suppress foam formation during the reaction.

The progress of the reaction may be monitored by FTIR by monitoring the region between 1000 and 4000 cm”. As the reaction progresses the concentration of the ester carbonyl will gradually diminish. This can be . observed by a similar reduction in height of the characteristic ester carbonyl

FTIR peak at wavelength 1739 cm.

The liquid potassium salt of the fatty hydroxamic acid is transformed into a white solid upon cooling and evaporation of the water solvent. The physical and chemical properties closely resemble the product of Example 1

Example 4

Potassium salt of Cg/C1o hydroxamate derivatives from coconut oil. A 7-8% free hydroxylamine reagent was generated by following a procedure similar to than in Example 1. It was then immediately reacted with triglyceride of coconut oil (22.5 g, saponification value 279, 0.112 mole equivalent of glyceride) at 45°C, under agitation. After a stirring period of 12 hours the white, creamy material was transferred to a pyrex bowl and was exposed to air to allow the solvent to gradually evaporate to dryness. The resultant white, paste product was subjected to washing with cold methanol to remove glycerol and other organic 16 materials. The FTIR spectrum of dry white powder (18 g) showed an absorption band similar to that of the potassium salt of CgC1o hydroxamate derivative made in Example 1.

Example 5

Cg-cekanoic hydroxamic acid.

A 7-8% free hydroxylamine reagent, generated by following Example 1, was reacted with methyl ester of Ce-cekanoic acid (19.7 g, 0.112 mole equivalent —

CO,CH3) in a glass reactor using similar reaction conditions as described in

Example 1. Unlike the product of Cs and C1 coconut fatty hydroxamate, the

Cy-cekanoic hydroxamate product appeared as a clear homogeneous liquid.

Upon acidification with 1 M HCI a white precipitate of Cg-cekanoic hydroxamic acid was formed. After filtration, water wash and air dry at 15 g of white powder of cekanoic hydroxamic acid was obtained.

Example 6

A 1kg sample of the mineral feedstock was ground to 80% less than 75um and was subjected to standard flotation methods in a 2 litre laboratory flotation cell.

The fatty hydroxamate was added as required, either as the solid or dispersed in warm water at 0.1 to 500g/tonne at a pH 8 to 10.5 or warm 1% potassium hydroxide solution. Methyl isobutyl carbinol (MIBC) was used as required as a frother (up to 10g/tonne). The composition of the froth concentrate defined is shown in the table below.

Oxidised Cu ore Cu 0.8% Cu 38% 1 atm = 101,325 kPa

AMENDED SHEET 2004 -02- 20

Claims

: PU 1/AUULVUYLY Received 13 May 2002

1. A method for preparing fatty hydroxamic acids and salts thereof comprising forming a two phase system including a water insoluble phase consisting essentially of a lower alkanol ester of a fatty acid and an aqueous phase comprising hydroxylamine and mixing the : phases to provide reaction of the lower alkanol ester of the fatty acid and the hydroxylamine to form said fatty acid hydroxamic acid or salt : thereof. Co : oo oo

2. A method according to claim 1 wherein the two phase system is essentially free of added surfactant.

3. A method according to claim 2 wherein the hydroxylamine formed in situ from hydroxylamine salts in the presence of an alkaline aqueous solution.

4, A method according to claim 2 wherein the hydroxylamine is formed in situ from nitroxyl chloride or ammonia in the presence of an oxidizing agent.

5. A method according to claim 1 wherein the reaction mixture comprises no more than 5% by weight of added lower alkanol defoaming agent.

6. A method according to claim 1 wherein the reaction produces foam under ambient conditions and the method further includes conducting the reaction under a pressure sufficient to suppress foam formation.

7. A method according to claim 6 wherein the reaction is conducted under a © pressure in the range of from 0.1 to 2 atmospheres (10,1 kPa to 202,7 kPa).

8. A method according to claim 6 wherein a continuous or semi continuous reaction is conducted in a tubular reactor.

9. A method according to claim 3 wherein the hydroxylamine is formed in situ from one or more of hydroxylammonium chloride and hydroxylammonium sulfate.

10. A method according to claim 1 wherein the fatty acid derivative is selected from the group consisting of C4 to C, alkyl esters of fatty acids, fatty acid chlorides and mono-di- and tri- glycerides of fatty acids.

11. A method according to claim 1 wherein the fatty acid component of the fatty acid derivative comprises at least 95% by weight of Ce to C14 fatty acids.

12. A method according to claim 1 wherein the fatty acid component of the fatty acid derivative comprises at least 95% by weight of Ce to Cio fatty acids.

13. A method according to claim 3 wherein the hydroxylamine is reacted with the lower alkanol! ester of the fatty acid in the presence of an aqueous alkaline solution selected from sodium hydroxide and potassium hydroxide and the resulting product is a fatty hydroxamic acid salt formed with a counter ion selected from sodium and potassium.

14. A method according to claim 13 wherein the alkali metal is potassium hydroxide.

15. A method according to claim 13 wherein the aqueous alkaline solution comprises a concentration of sodium hydroxide or potassium hydroxide in the range of from 5 to 25% by weight.

16. A method according to claim 1 wherein the reaction is carried out at a temperature in the range of from 35 to 55°C. AMENDED SHEET 2004 -02- 20

17. A method according to claim 1 wherein the fatty acid component of the fatty acid derivative comprises one or more branched fatty acid.

18. A method according to claim 17 wherein the branched fatty acid is a Cs- C16 fatty acid.

19. A method according to claim 18 wherein the fatty acid is selected from the group consisting of iso-octanoic acid, 2-ethyl hexanoic acid, iso- nonanoic acid and neo-decanoic acid.

20. A method according to claim 19 wherein the fatty acid is iso-nonanoic acid.

21. A froth flotation agent comprising a fatty hydroxamic acid compound or salt thereof prepared by the method of claim 1 or claim 17.

22. A froth flotation agent comprising a fatty hydroxamate compounds or sait thereof, comprising a branched carbon chain fatty acid.

23. A froth flotation agent according to claim 22 wherein the branched fatty acid is a Cg-C¢ fatty acid.

24. A froth flotation agent according to claim 23 wherein the fatty acid is selected from the group consisting of iso-octanoic acid, 2-ethyl hexanoic acid, iso-nonanoic acid and neo decanoic acid.

25. A froth flotation agent according to claim 24 wherein the fatty acid is iso- nonanoic acid.

26. A method of froth flotation comprising combining a froth flotation agent according to claim 23 with an ore slurry and a frothing agent to provide separation of metal values in the froth. AMENDED SHEET 7°" -m- 20

27. A method for preparing fatty hydroxamic acids and salts thereof substantially as herein described with reference to any one of the illustrative examples.

AMENDED SHEET 2004 -02- 20