WO2026028643A1 - フィルム - Google Patents

フィルム

Info

Publication number
WO2026028643A1
WO2026028643A1 PCT/JP2025/022076 JP2025022076W WO2026028643A1 WO 2026028643 A1 WO2026028643 A1 WO 2026028643A1 JP 2025022076 W JP2025022076 W JP 2025022076W WO 2026028643 A1 WO2026028643 A1 WO 2026028643A1
Authority
WO
WIPO (PCT)
Prior art keywords
film
layer
polystyrene
stress
mpa
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
PCT/JP2025/022076
Other languages
English (en)
French (fr)
Inventor
宗一郎 山中
恒祐 澤井
宏行 野中
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Gunze Ltd
Original Assignee
Gunze Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Gunze Ltd filed Critical Gunze Ltd
Publication of WO2026028643A1 publication Critical patent/WO2026028643A1/ja
Pending legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

フィルムは、歯列矯正用のアライナーに用いられるフィルムである。このフィルムは、少なくとも第１層と第２層とを備える。第１層は、耐衝撃性ポリスチレンを含む第１樹脂原料によって構成されている。第２層は、ポリスチレン系エラストマーを含む第２樹脂原料によって構成されている。

Description

フィルム
　本発明は、フィルムに関し、特に、歯列矯正用のアライナーに用いられるフィルムに関する。
　特表２０２３－５２５４００号公報（特許文献１）は、歯科矯正アライナトレイを開示する。この歯科矯正アライナトレイは、例えば、多層ポリマーフィルムによって構成される（特許文献１参照）。
特表２０２３－５２５４００号公報
　一般的に、歯列矯正用のアライナーの製造には、ＰＥＴＧ（グリコール変性ポリエチレンテレフタレート）によって構成されたフィルムが用いられる。歯列矯正効果を長く得るためには、アライナーにおける応力緩和が緩やかであることが重要である。しかしながら、ＰＥＴＧによって構成されたフィルムの応力緩和は、必ずしも緩やかではない。また、フィルムの曲げ弾性率が高すぎる場合には、アライナーを装着した患者が強い痛みを感じる可能性がある。これらの問題の解決手段が上記特許文献１には開示されていない。
　本発明は、このような問題を解決するためになされたものであって、その目的は、曲げ弾性率が高すぎず、かつ、応力緩和が比較的緩やかなフィルムを提供することである。
　本発明に従うフィルムは、歯列矯正用のアライナーに用いられるフィルムである。このフィルムは、少なくとも第１層と第２層とを備える。第１層は、耐衝撃性ポリスチレンを含む第１樹脂原料によって構成されている。第２層は、ポリスチレン系エラストマーを含む第２樹脂原料によって構成されている。
　本発明者（ら）は、耐衝撃性ポリスチレンを含むフィルムの応力緩和が、ＰＥＴＧによって構成されたフィルムの応力緩和よりも緩やかであることを見出した。このフィルムによれば、耐衝撃性ポリスチレンを含む第１樹脂原料によって構成された第１層がフィルムに含まれているため、ＰＥＴＧによって構成されたフィルムと比較して、応力緩和をより緩やかにすることができる。また、このフィルムによれば、ポリスチレン系エラストマーを含む第２樹脂原料によって構成された第２層がフィルムに含まれているため、耐衝撃性ポリスチレンのみで構成されたフィルムと比較して、曲げ弾性率を抑制することができる。
　上記フィルムにおいては、第２樹脂原料に含まれるポリスチレン系エラストマーのショア硬度がＡ６０以上であってもよい。
　上記フィルムにおいては、第１層を引張面として測定された曲げ弾性率が１５００ＭＰａ以下であってもよい。
　本発明によれば、曲げ弾性率が高すぎず、かつ、応力緩和が比較的緩やかなフィルムを提供することができる。
フィルムの断面を模式的に示す図である。 アライナー用途におけるＨＩＰＳの有効性等を説明するための図である。
　以下、本発明の一側面に係る実施の形態（以下、「本実施の形態」とも称する。）について、図面を用いて詳細に説明する。なお、図中同一又は相当部分には同一符号を付してその説明は繰り返さない。また、各図面は、理解の容易のために、適宜対象を省略又は誇張して模式的に描かれている。
　［１．フィルムの構成］
　図１は、本実施の形態に従うフィルム１０の断面を模式的に示す図である。図１を参照して、フィルム１０は、第１層１１と、第１層１１に積層された第２層１２とを含んでいる。フィルム１０の厚みは、例えば、４００μｍ以上、１．６ｍｍ以下であり、５００μｍ以上、１．２ｍｍ以下であることが好ましく、６００μｍ以上、９００μｍ以下であることがより好ましい。第１層１１の厚みを第２層１２の厚みで除算した値は、例えば、０．０６７以上、１５以下であり、０．１１以上、９以下であることが好ましく、０．１１以上、７以下であることがより好ましい。
　フィルム１０は、歯列矯正用のアライナーの製造に用いられる。例えば、フィルム１０は、フィルム１０の形状が平面視円形状になるように加工される。予め作製された患者の歯型にフィルム１０が被せられた状態でフィルム１０が加熱されることによって、フィルム１０の形状が歯型に沿った形状に変化する。その後、不要な部分がフィルム１０から切除されることによって、アライナーが完成する。
　第１層１１は、耐衝撃性ポリスチレン（ＨＩＰＳ（High Impact Polystyrene））を含む第１樹脂原料によって構成されている。ＨＩＰＳは、例えば、汎用ポリスチレン（ＧＰＰＳ（General Purpose Polystyrene））と、ゴム成分とを含んでいる。汎用ポリスチレンは、例えば、スチレンの単独重合体である。ゴム成分の一例としては、ブタジエン系ゴム粒子（例えば、スチレン－ブタジエン共重合体）が挙げられる。ＨＩＰＳは、例えば、汎用ポリスチレンによって構成されたマトリックス中にブタジエン系ゴム粒子が分散された海島アロイによって構成される。
　第２層１２は、ポリスチレン系エラストマーを含む第２樹脂原料によって構成されている。ポリスチレン系エラストマーとしては、例えば、スチレン－エチレン－ブチレン－スチレンのブロック共重合体（ＳＥＢＳ）、及び、スチレン－ブチレンのブロック共重合体（ＳＢＣ）が挙げられる。ポリスチレン系エラストマーのショア硬度は、例えば、Ａ６０以上、Ｄ７０以下であり、Ｄ３９以上、Ｄ４２以下であることが好ましい。例えば、ＳＥＢＳのショア硬度はＩＳＯ７６１９に準拠した方法で、ＳＢＣのショア硬度はＩＳＯ０８６８に準拠した方法で測定される。
　このように、フィルム１０においては、第１層１１と第２層１２とが互いに異なる樹脂原料によって構成されている。そのため、第１層１１側が歯に接触するようにフィルム１０が加工される場合と、第２層１２側が歯に接触するようにフィルム１０が加工される場合とで、アライナーによって歯に掛けられる負荷が変わる。歯科医は、例えば、患者の特性（痛みへの耐性等）に応じて、第１層１１側が歯に接触するようにフィルム１０を加工するか、第２層１２側が歯に接触するようにフィルム１０を加工するかを決定することができる。
　［２．アライナー用途におけるＨＩＰＳの有効性等］
　歯列矯正効果を長く得るためには、アライナーにおける応力緩和がある程度緩やかであることが必要である。また、フィルム１０の曲げ弾性率が高すぎる場合には、フィルム１０を用いて製造されたアライナーを装着した患者が強い痛みを感じる可能性がある。したがって、フィルム１０の曲げ弾性率が高すぎず、かつ、フィルム１０の応力緩和が比較的緩やかであることが重要である。
　図２は、アライナー用途におけるＨＩＰＳの有効性等を説明するための図である。図２を参照して、横軸は時間を示し、縦軸はフィルムの応力を示す。線Ｌ１，Ｌ２，Ｌ３の各々は、ＤＭＡ（動的粘弾性測定装置；日立ハイテクサイエンス製　ＤＭＡ７１００）の両持ち梁曲げモードにて試料（フィルム）に０．２５ｍｍの一定歪みを与えた際の応力を４時間連続で測定した結果の一例を示す。アライナーの製造時にフィルムが加熱されるため、各試料は、同等の条件で加熱（例えば、２２０℃で３０秒）・冷却（空冷）れていた。また、アライナーは人の口内で使用されるため、応力の測定は、試料が３７℃の水中に配置された状態で行なわれた。線Ｌ１は、ＰＥＴＧ単層のフィルムにおける応力の推移の一例を示す。線Ｌ２は、ＨＩＰＳ単層のフィルムにおける応力の推移の一例を示す。線Ｌ３は、フィルム１０における応力の推移の一例を示す。
　線Ｌ１，Ｌ２を比較すると、ＨＩＰＳ単層のフィルムの応力緩和は、ＰＥＴＧ単層のフィルムの応力緩和よりも緩やかである。一方、ＨＩＰＳ単層のフィルムの応力は高く、ＨＩＰＳ単層のフィルムの曲げ弾性率も高い。線Ｌ２，Ｌ３を比較すると、フィルム１０の応力緩和は、ＨＩＰＳ単層のフィルムの応力緩和と比較して、同等又はやや緩やかである。また、フィルム１０の応力はＨＩＰＳ単層のフィルムの応力よりも低く、フィルム１０の曲げ弾性率もＨＩＰＳ単層のフィルムの曲げ弾性率よりも低い。第１層１１を引張面として測定されたフィルム１０の曲げ弾性率は、例えば、６００ＭＰａ以上、２０００ＭＰａ以下であり、７００ＭＰａ以上、１６００ＭＰａ以下であることが好ましく、８００ＭＰａ以上、１５００ＭＰａ以下であることがより好ましく、８００ＭＰａ以上、１１００ＭＰａ以下であることがさらに好ましい。また、第２層１２を引張面として測定されたフィルム１０の曲げ弾性率は、例えば、６００ＭＰａ以上、２０００ＭＰａ以下であり、７００ＭＰａ以上、１７００ＭＰａ以下であることが好ましく、７００ＭＰａ以上、１６００ＭＰａ以下であることがより好ましく、７００ＭＰａ以上、１１００ＭＰａ以下であることがさらに好ましい。
　このように、本発明者（ら）は、耐衝撃性ポリスチレンを含むフィルム１０の応力緩和が、ＰＥＴＧによって構成されたフィルムの応力緩和よりも緩やかであることを見出した。フィルム１０によれば、耐衝撃性ポリスチレンを含む第１樹脂原料によって構成された第１層１１がフィルム１０に含まれているため、ＰＥＴＧによって構成されたフィルムと比較して、応力緩和をより緩やかにすることができる。また、フィルム１０によれば、ポリスチレン系エラストマーを含む第２樹脂原料によって構成された第２層１２がフィルム１０に含まれているため、耐衝撃性ポリスチレンのみで構成されたフィルムと比較して、曲げ弾性率を抑制することができる。すなわち、フィルム１０によれば、曲げ弾性率を適切な範囲に収め、かつ、応力緩和を比較的緩やかにすることができる。
　［３．特徴］
　以上のように、本実施の形態に従うフィルム１０によれば、耐衝撃性ポリスチレンを含む第１樹脂原料によって構成された第１層１１がフィルム１０に含まれているため、ＰＥＴＧによって構成されたフィルムと比較して、応力緩和をより緩やかにすることができる。また、フィルム１０によれば、ポリスチレン系エラストマーを含む第２樹脂原料によって構成された第２層１２がフィルム１０に含まれているため、耐衝撃性ポリスチレンのみで構成されたフィルムと比較して、曲げ弾性率を抑制することができる。
　［４．他の実施の形態］
　上記実施の形態の思想は、以上で説明された実施の形態に限定されない。以下、上記実施の形態の思想を適用できる他の実施の形態の例について説明する。
　上記実施の形態に従うフィルム１０においては、第１層１１及び第２層１２の各々が１層しか含まれていなかった。しかしながら、第１層１１及び第２層１２の数はこれに限定されない。フィルム１０においては、第１層１１及び第２層１２の各々が複数設けられていてもよい。フィルム１０における層構成は、例えば、第１層１１／第２層１２／第２層１２であってもよく、第１層１１／第１層１１／第２層１２であってもよく、第１層１１／第１層１１／第２層１２／第２層１２であってもよく、第１層１１／第２層１２／第２層１２／第２層１２であってもよい。また、フィルム１０に複数の第１層１１が含まれる場合に各第１層１１を構成する原料が互いに異なっていてもよく、フィルム１０に複数の第２層１２が含まれる場合に各第２層１２を構成する原料が互いに異なっていてもよい。
　以上、本発明の実施の形態について例示的に説明した。すなわち、例示的な説明のために、詳細な説明及び添付の図面が開示された。よって、詳細な説明及び添付の図面に記載された構成要素の中には、課題解決のために必須でない構成要素が含まれることがある。したがって、それらの必須でない構成要素が詳細な説明及び添付の図面に記載されているからといって、それらの必須でない構成要素が必須であると直ちに認定されるべきではない。
　また、上記実施の形態は、あらゆる点において本発明の例示にすぎない。上記実施の形態は、本発明の範囲内において、種々の改良や変更が可能である。例えば、いずれかの実施の形態の少なくとも一部の構成と、他のいずれかの実施の形態の少なくとも一部の構成とが組み合わされてもよい。すなわち、本発明の実施にあたっては、実施の形態に応じて具体的構成を適宜採用することができる。
　以下、本発明の実施例について説明する。なお、本発明は以下の実施例に限定されない。
　［１．実施例及び比較例］
　以下の方法で、実施例１－１８及び比較例１－２の各フィルムを製造した。実施例１－１８の各フィルムに関しては、各層を構成する樹脂原料を押出機に供給し、共押出を行なうことによって得た。比較例１－２の各フィルムに関しては、樹脂原料を押出機に供給し、押出成形を行なうことによって得た。得られた各フィルムの総厚みは８００μｍであった。実施例１－１８及び比較例１－２のフィルムにおいては、第１層を構成する樹脂の種類、第２層を構成する樹脂の種類、第１層及び第２層の厚みの比率、及び、第２層を構成するエラストマーのショア硬度の組合せが互いに異なっていた。これらの組合せは、以下の表１に示される通りであった。
　［２．各種測定］
　実施例１－１８及び比較例１－２の各フィルムに関し以下の各種測定を行なった。
　＜２－１．応力緩和＞
　ＤＭＡ（動的粘弾性測定装置　日立ハイテクサイエンス製　ＤＭＡ７１００）の両持ち梁曲げモードにて各フィルムの応力を４時間連続で測定した。各フィルムに関して、第１層側を引張面とした場合、及び、第２層側を引張面とした場合の両方について応力を測定した。各フィルムの変位量は、０．２５ｍｍであった。歪み速度は、１０００００μｍ/分であった。応力測定前に、各フィルムは、２２０℃で３０秒間加熱された。応力の測定は、フィルムが３７℃の水中に配置された状態で行なわれた。１時間毎の応力の変化を確認し、各フィルムの応力緩和特性を確認した。
　＜２－２．曲げ弾性率＞
　原則的にＪＩＳ－Ｋ－７１７１に準拠した方法で各フィルムの曲げ弾性率を測定した。各フィルムの厚みが８００μｍであり、ＪＩＳ－Ｋ－７１７１に準拠すると、支点間距離が極めて短くなるため、支点間距離のみがＪＩＳ－Ｋ－７１７１と異なる基準で決定された。具体的には、支点間距離が２０ｍｍとされた。
　［３．測定結果］
　応力緩和に関する測定結果は、以下の表２に示す通りであった。また、測定開始から１時間後の応力と、測定開始から４時間後の応力との差は、以下の表３に示す通りであった。なお、測定開始から１時間は、他の区間と比較して、応力が大きく低下したため、応力緩和特性としては、測定開始から１時間後の応力と、測定開始から４時間後の応力との差を確認した。表３を参照すると、比較例１－２の各フィルムの応力緩和と比較して、実施例１－１８の各フィルムの応力緩和が緩やかであることが分かった。
　曲げ弾性率の測定結果は、以下の表４に示す通りであった。表４を参照すると、実施例１－１８の各フィルムの曲げ弾性率が適切な範囲に収まっていることが分かった。
　１０　フィルム、１１　第１層、１２　第２層、Ｌ１，Ｌ２，Ｌ３　線。

 

Claims (3)

  1. 　歯列矯正用のアライナーに用いられるフィルムであって、
    　少なくとも第１層と第２層とを備え、
    　前記第１層が耐衝撃性ポリスチレンを含む第１樹脂原料によって構成されており、
    　前記第２層がポリスチレン系エラストマーを含む第２樹脂原料によって構成されている、フィルム。
  2. 　前記第２樹脂原料に含まれるポリスチレン系エラストマーのショア硬度がＡ６０以上である、請求項１に記載のフィルム。
  3. 　前記第１層を引張面として測定された曲げ弾性率が１５００ＭＰａ以下である、請求項１又は請求項２に記載のフィルム。

     
PCT/JP2025/022076 2024-07-30 2025-06-19 フィルム Pending WO2026028643A1 (ja)