WO2025183148A1 - イオン液体中の着色成分の除去 - Google Patents

イオン液体中の着色成分の除去

Info

Publication number
WO2025183148A1
WO2025183148A1 PCT/JP2025/007076 JP2025007076W WO2025183148A1 WO 2025183148 A1 WO2025183148 A1 WO 2025183148A1 JP 2025007076 W JP2025007076 W JP 2025007076W WO 2025183148 A1 WO2025183148 A1 WO 2025183148A1
Authority
WO
WIPO (PCT)
Prior art keywords
liquid
membrane
reverse osmosis
osmosis membrane
ionic liquid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
PCT/JP2025/007076
Other languages
English (en)
French (fr)
Inventor
典昭 加藤
秀人 松山
淳 松岡
豊三 浜田
晋佑 岡部
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Daicel Corp
Kobe University NUC
Original Assignee
Daicel Corp
Kobe University NUC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Daicel Corp, Kobe University NUC filed Critical Daicel Corp
Publication of WO2025183148A1 publication Critical patent/WO2025183148A1/ja
Pending legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

イオン液体中の着色成分を除去し、イオン液体を含む液体を効果的に回収するための方法を提供する。　イオン液体及び着色成分を含む着色液体から、イオン液体を含む液体を回収するための方法であって、前記着色液体をナノろ過膜又は逆浸透膜に供することにより、イオン液体を含む前記液体と、前記着色成分とを分離することを含む、方法が開示される。

Description

イオン液体中の着色成分の除去
　本開示は、イオン液体中の着色成分を除去する方法に関する。また、本開示は、イオン液体及び着色成分を含む着色液体から、イオン液体を含む液体と、着色成分とを分離し、イオン液体を含む液体を回収するための方法に関する。また、本開示は、該方法を含むセルロースエステルの製造方法にも関する。
　酢酸セルロースなどのセルロースエステルを合成するための溶媒として、イオン液体を含む液体が使用されている。イオン液体はセルロースに対する溶解性が高く、セルロースエステルを均一に合成させることが可能である。イオン液体を含む液体は、共溶媒を含んでいてもよい。共溶媒は、液体の粘度を下げ、また、イオン液体の使用量を削減することができる。
　イオン液体は高価であるため、工業的規模でセルロースエステルを合成するには、合成に用いたイオン液体及を含む液体を次の合成に再使用することにより、イオン液体をリサイクルすることが望ましい。
　イオン液体を含む液体中で合成されたセルロースエステルは、析出させ、固液分離をすることにより、固相から回収することができる。一方、液相のイオン液体を含む液体には、合成中及び合成後の処理により生じた不純物が含まれる。このような不純物としては、セルロース由来不純物（例えば、未反応のセルロース、置換度が低いセルロースエステル、分子量が比較的小さいセルロースエステルなど）や、合成後の液体を蒸留などの工程において加熱することに生じる着色成分が含まれる。このような不純物を取り除くことは、イオン液体をリサイクルする上で、重要である。
　不純物を除去し、イオン液体をリサイクルする方法として、例えば、特許文献１では、抽出法により不純物を除去する方法が開示されている。特許文献２では、再結晶法により不純物を除去する方法が開示されている。特許文献３では、イオン交換膜を用いて不純物を除去する方法が開示されている。
特開２０１３－１７７３２４号公報 特開２０１２－１４４４４１号公報 特開２０１５－９６２５５号公報
　イオン液体を含む液体を反応溶媒としてセルロースエステルを合成する場合、合成後の反応溶媒には、通常、セルロースをエステル化させるために添加された有機酸無水物由来の有機酸や、セルロースエステルを析出させるために添加された貧溶媒が、含まれる。したがって、セルロースエステルの製造プロセスにおいてイオン液体をリサイクルするには、イオン液体を含む液体を次の合成において再使用する前に、前の合成で混入した有機酸や貧溶媒を十分に除去する必要がある。
　イオン液体を含む液体に混入した有機酸や貧溶媒は、蒸留により効果的に除去することができる。しかしながら、このような蒸留を行うためにイオン液体を含む液体を加熱すると、該液体中に着色成分が生じる。このような着色成分を含むイオン液体を含む液体をセルロースエステルの製造に使用すると、例えば合成するセルロースエステルが着色するなどの好ましくない影響が生じ、良好な品質を有するセルロースエステルを合成することが困難になる。
　本開示は、これらの事情に鑑み、イオン液体及び着色成分を含む液体から着色成分を効果的に除去することにより、イオン液体を効果的に回収する方法を提供することを課題とする。
　本開示では、例えば、イオン液体及び着色成分を含む着色液体から、イオン液体を含む液体を回収するための方法であって、前記着色液体をナノろ過膜又は前記逆浸透膜に供することにより、イオン液体を含む前記液体と、前記着色成分とを分離することを含む、方法が開示される。
　本開示によれば、イオン液体及び着色成分を含む液体から着色成分を効果的に除去することが可能であり、これにより、イオン液体を効果的に回収し、再使用することができる。
図１は、実施例２のナノろ過膜に供給した、イオン液体及び着色成分を含む供給液、並びに該ナノろ過膜を透過した透過液の紫外／可視光スペクトルを示す。 図２は、実施例７で用いた限外ろ過膜の耐溶剤性試験における、（１）破断強度の経時変化、（２）破断伸度の経時変化、及び（３）弾性率の経時変化を示す。
　以下、本開示の一実施形態について詳細に説明するが、本開示の範囲はここで説明する一実施形態に限定されるものではなく、本開示の趣旨を逸脱しない範囲で種々の変更ができる。本明細書に開示された各々の態様は、本明細書に開示された他のいかなる特徴とも組み合わせることができる。また、特定のパラメータについて、複数の上限値及び下限値が記載されている場合、これらの上限値及び下限値の内、任意の上限値と下限値とを組合せて好適な数値範囲とすることができる。また、本開示に記載されている数値範囲の下限値及び／又は上限値は、その数値範囲内の数値であって、実施例で示されている数値に置き換えてもよい。数値範囲を示す「Ｘ～Ｙ」との表現は、「Ｘ以上Ｙ以下」であることを意味している。一実施形態について記載した特定の説明が他の実施形態についても当てはまる場合には、他の実施形態においてはその説明を省略している場合がある。
＜イオン液体を含む液体を回収するための方法＞
　一実施形態において、イオン液体及び着色成分を含む着色液体から、イオン液体を含む液体を回収するための方法であって、前記着色液体をナノろ過膜又は前記逆浸透膜に供することにより、イオン液体を含む前記液体と、前記着色成分とを分離することを含む、方法が開示される。
　この方法は、イオン液体を効果的に回収することが可能である。回収したイオン液体を再使用することにより、高価なイオン液体の使用に係るコストを削減することができる。また、イオン液体の使用量を削減することにより、環境負荷を軽減することができる。
　上述のイオン液体及び着色成分を含む液体は、共溶媒をさらに含んでいてもよい。
　上述のイオン液体及び着色成分を含む液体は、メタノールをさらに含んでいてもよい。
　上述のイオン液体及び着色成分を含む液体、及び／又はナノろ過膜又は逆浸透膜により着色成分を除去した後の上述のイオン液体を含む液体において、イオン液体の含量は、該液体の総重量に対し、該液体が共溶媒を含みメタノールを含まない場合、好ましくは２０～９０重量％、より好ましくは３０～８０％重量であり、共溶媒を含まずメタノールを含む場合、好ましくは２０～８０重量％、より好ましくは３０～７０重量％であり、共溶媒及びメタノールを含む場合、好ましくは２０～８０重量％、より好ましくは３０～７０重量％である。
　上述のイオン液体及び着色成分を含む液体、及び／又はナノろ過膜又は逆浸透膜により着色成分を除去した後の上述のイオン液体を含む液体が、共溶媒を含みメタノールを含まない場合、共溶媒の含量は、該液体の総重量に対し、好ましくは２０～９０重量％、より好ましくは３０～８０重量％であり、該液体が共溶媒及びメタノールを含む場合、好ましくは２０～８０重量％、より好ましくは３０～７０％重量である。
　上述のイオン液体及び着色成分を含む液体、及び／又はナノろ過膜又は逆浸透膜により着色成分を除去した後の上述のイオン液体を含む液体において、メタノールの含量は、該液体の総重量に対し、好ましくは３０～８０重量％、より好ましくは４０～７０重量％である。
　上述のイオン液体及び着色成分を含む液体、及び／又はナノろ過膜又は逆浸透膜により着色成分を除去した後の上述のイオン液体を含む液体が共溶媒を含む場合、共溶媒の含量は、液体の総重量に対し、好ましくは０．１～８０重量％、より好ましくは２０～７０重量である。また、イオン液体と共溶媒との重量比は、好ましくは２０：８０～９９．９：０．１、より好ましくは３０：７０～８０：２０である。
　上述のイオン液体及び着色成分を含む液体、及び／又はナノろ過膜又は逆浸透膜により着色成分を除去した後の上述のイオン液体を含む液体が、共溶媒を含まずメタノールを含む場合、イオン液体とメタノールとの重量比は、好ましくは３０：７０～７０：３０、より好ましくは４０：６０～６０：４０であり、共溶媒及びメタノールを含む場合、イオン液体及び共溶媒の合計と、メタノールとの重量比は、好ましくは３０：７０～７０：３０、より好ましくは４０：６０～６０：４０である。
［ナノろ過膜又は逆浸透膜］
　逆浸透膜（ＲＯ膜）は、水を通しイオンや塩類など水以外の不純物は透過しない性質を有する膜である。本開示に係るナノろ過膜として、本発明の効果が得られる範囲で、任意の逆浸透膜を用いることができる。
　ナノろ過（ＮＦ）膜は、逆浸透膜（ＲＯ膜）と限外ろ過膜（ＵＦ膜）との中間の性能を有する膜であり、典型的には、約１ｎｍサイズの粒子又は分子を透過し、これより大きいサイズの粒子又は分子を透過させない膜である。本開示に係るナノろ過膜として、本発明の効果が得られる範囲で、任意のナノろ過膜を用いることができる。
　限外ろ過（ＵＦ）膜については、後述する。
　ナノろ過膜又は逆浸透膜は、イオン液体を含む液体に含まれる着色成分を効果的に除去することができる。
　着色成分は、イオン液体を含む液体において、例えば蒸留などの加熱を伴う処理により、生じる成分である。
　ナノろ過膜又は逆浸透膜の塩阻止率は、イオン液体を含む液体がメタノールを含まない場合、好ましくは、９５％以上、９６％以上、９７％以上、９８％以上、９８．５％以上、９９％以上、又は９９．５％以上である。また、ナノろ過膜又は逆浸透膜の塩阻止率は、イオン液体を含む液体がメタノールを含む場合、好ましくは、８５％以上、９０％以上、９５％以上、９６％以上、９７％以上、９８％以上、９８．５％以上、９９％以上、又は９９．５％以上である。
　ここで、塩阻止率は、
　数式１：塩阻止率（％）＝（１－Ｃｆｉｌｌ／Ｃｆｅｅｄ）×１００
［数式１において、Ｃｆｅｅｄは、ナノろ過膜又は逆浸透膜にＮａＣｌ水溶液を通液する際に、前記ナノろ過膜又は前記逆浸透膜に供給されるＮａＣｌ水溶液中のＮａＣｌ濃度であり、Ｃｆｉｌｌは、ナノろ過膜又は逆浸透膜にＮａＣｌ水溶液を通液した際に、前記ナノろ過膜又は前記逆浸透膜から排出されるＮａＣｌ水溶液中のＮａＣｌ濃度である］
により算出することができる。
　ナノろ過膜又は逆浸透膜の透水係数は、イオン液体を含む液体がメタノールを含まない場合、好ましくは、１．０Ｌ／ｍ２／ｈ／ｂａｒ未満であり、より好ましくは、０．５～０．９５Ｌ／ｍ２／ｈ／ｂａｒである。また、ナノろ過膜又は逆浸透膜の透水係数は、イオン液体を含む液体がメタノールを含む場合、好ましくは、８．０Ｌ／ｍ２／ｈ／ｂａｒ未満であり、より好ましくは、１．０～８．０Ｌ／ｍ２／ｈ／ｂａｒである。
　透水係数は、１６００ｐｐｍ　ＮａＣｌ水溶液を前記ナノろ過膜に通液する際の透過速度として定義することができる。
　イオン液体を含む液体において、例えば蒸留などの加熱を伴う処理により生じる、上記の着色成分は、紫外領域に吸収ピークをもち、可視光領域に吸光帯が広がっている（図１）。本開示では、ナノろ過膜又は逆浸透膜の通過前及び通過後のイオン液体を含む液体における、３８０～７７０ｎｍの吸光度平均値の変化を着色除去率と定義する。したがって、ナノろ過膜又は逆浸透膜が、イオン液体を含む液体に含まれる着色成分を効果的に除去することは、ナノろ過膜又は逆浸透膜による着色除去率により、評価することができる。
　着色除去率は、
　数式２：着色除去率（％）＝（１－Ａｂｓｆｉｌｌ／Ａｂｓｆｅｅｄ）×１００
［数式２において、Ａｂｓｆｅｅｄは、ナノろ過膜又は逆浸透膜にイオン液体を含む液体を通液する際の、前記ナノろ過膜又は前記逆浸透膜に供給されるイオン液体を含む液体の３８０～７７０ｎｍにおける吸光度の平均であり、Ａｂｓｆｉｌｌは、ナノろ過膜又は逆浸透膜にイオン液体を含む液体を通液する際の、前記ナノろ過膜又は前記逆浸透膜から排出されるイオン液体を含む液体の３８０～７７０ｎｍにおける吸光度の平均である。］
より算出することができる。
　ナノろ過膜又は逆浸透膜による着色除去率は、好ましくは、５０％以上、６０％以上、７０％以上、８０％以上、９０％以上、又は９０％以上である。
　ナノろ過膜又は逆浸透膜は、好ましくは、架橋ポリアミド樹脂を含む活性層を含む。架橋ポリアミド樹脂は、例えば、芳香族系あるいは脂環族系の多官能アミンと多官能アシルハライドとの界面重合により形成されたものである。多官能アミンは、例えばｍ－フェニレンジアミン、ｐ－フェニレンジアミン、キシリレンジアミン、３，５－ジアミノ安息香酸、３－アミノベンジルアミン、４－アミノベンジルアミン、１，２－ジアミノシクロヘキサン、１，４－ジアミノシクロヘキサン、４－アミノピペリジン、ピペラジンなどからなるジアミン群より選択され、多官能アシルハライドは、例えば、トリメシン酸クロライド、１，３，５－シクロヘキサントリカルボン酸トリクロライド、１，２，４－シクロブタントリカルボン酸トリクロライドなどからなる３官能アシルハライド群より選択される。
　ナノろ過膜又は逆浸透膜は、より好ましくは、ポリケトン製又はポリスルホン製の膜の表面にポリアミドを含む活性層を形成させた複合膜である。
　ナノろ過膜又は逆浸透膜は、本発明の効果が得られる範囲で、任意の形状であってよく、例えば中空糸膜であってもよく、平膜であってもよい。
　ナノろ過膜又は逆浸透膜として、本発明の効果が得られる範囲で、市販のナノろ過膜又は逆浸透膜を用いることができる。市販のナノろ過膜の非限定的な例として、Ａｑｕｑｓｏｕｒｃｅ社製ＴｒｉＳｅｐ　ＴＳ８０、日東電工社製ＮＴＲ７２５０等が挙げられる。市販の逆浸透膜の非限定的な例として、日東電工社製ＳＷＣ４等が挙げられる。
［イオン液体］
　イオン液体は、セルロースを溶解することができるイオン性の液体である。
　イオン液体は、カチオン成分及びアニオン成分を含む。
（カチオン成分）
　カチオン成分は、好ましくは、イミダゾリウムカチオン、ピリジニウムカチオン、ピロリジニウムカチオン、ピペリジニウムカチオン、四級アンモニウムカチオン、及び四級ホスホニウムカチオンからなる群から選択される１以上のカチオンである。
　イミダゾリウムカチオンの非限定的な例として、下記の式（１）で表されるカチオンが挙げられる。式（１）で表されるカチオンには、その互変異性体や、式（１）と共鳴関係にある構造式で表されるカチオンも含まれる。
　　式（１）：
 　式（１）中、Ｒ１及びＲ３は、同一又は異なって、置換若しくは非置換のアルキル基、アルケニル基、アルコキシアルキル基、又は置換若しくは非置換のフェニル基であり、Ｒ２、Ｒ４、及びＲ５は、同一又は異なって、水素原子、置換若しくは非置換のアルキル基、アルケニル基、アルコキシアルキル基、又は置換若しくは非置換のフェニル基である。
　Ｒ１～Ｒ５における置換若しくは非置換のアルキル基としては、例えば、メチル基、エチル基、ｎ－プロピル基、イソプロピル基、ブチル基、ヘキシル基、オクチル基等の１～２０個（好ましくは１～１０個、より好ましくは２～６個、さらに好ましくは２～４個）の炭素原子を有する直鎖状又は分岐状のアルキル基が挙げられる。これらのアルキル基の末端には、スルホ基が結合していてもよい。また、アルケニル基としては、ビニル基、１－プロペニル基、２－プロペニル基、１－ブテニル基、２－ブテニル基、１－ペンテニル基、２－ペンテニル基、１－ヘキセニル基、２－ヘキセニル基、１－オクテニル基等の２～２０個（好ましくは２～１０個、より好ましくは２～６個、さらに好ましくは２～４個）の炭素原子を有する直鎖状又は分岐状のアルケニル基が挙げられる。また、アルコキシアルキル基としては、メトキシメチル基、エトキシメチル基、１－メトキシエチル基、２－メトキシエチル基、１－エトキシエチル基、２－エトキシエチル基等の２～２０個（好ましくは２～１０個、より好ましくは２～６個、さらに好ましくは２～４個）の炭素原子を有する直鎖状又は分岐状のアルコキシアルキル基が挙げられる。さらに、置換若しくは非置換のフェニル基としては、水酸基、ハロゲン原子、低級アルコキシ基、低級アルケニル基、メチルスルホニルオキシ基、置換若しくは非置換の低級アルキル基、置換若しくは非置換のアミノ基、置換若しくは非置換のフェニル基、置換若しくは非置換のフェノキシ基及び置換若しくは非置換のピリジル基から選択される１～２個の基で置換されてもよいフェニル基が挙げられる。
　Ｒ１及びＲ３は、アルキル基、アルケニル基、又は置換若しくは非置換のフェニル基であることが好ましく、より好ましくは１～６個の炭素原子を有する直鎖状のアルキル基である。また、Ｒ１及びＲ３の一方が１～４個の炭素原子を有する直鎖状のアルキル基であり、他方が２～６個の炭素原子を有する直鎖状のアルキル基であって、これらのアルキル基の炭素原子数が異なることが特に好ましい。Ｒ２、Ｒ４及びＲ５は、水素原子、アルキル基、アルケニル基、又は置換若しくは非置換のフェニル基であることが好ましく、より好ましくは水素原子、又はアルキル基である。
　イミダゾリウムカチオンは、好ましくは、１，３－ジメチルイミダゾリウム、１－エチル－３－メチルイミダゾリウム、１－ブチル－３－メチルイミダゾリウム、１－ヘキシル－３－メチルイミダゾリウム、１－オクチル－３－メチルイミダゾリウム、１－デシル－３－メチルイミダゾリウム、１－テトラデシル－３－メチルイミダゾリウム、１－ヘキサデシル－３－メチルイミダゾリウム、１－オクタデシル－３－メチルイミダゾリウム、１－アリル－３－メチルイミダゾリウム、１－エチル－２，３－ジメチルイミダゾリウム、１－ブチル－２，３－ジメチルイミダゾリウム、及び１－ヘキシル－２，３－ジメチルイミダゾリウムからなる群から選択される１以上のイミダゾリウムのカチオンであってよく、特に好ましくは、１－エチル－３－メチルイミダゾリウムのカチオン（Ｅｍｉｍ＋）であってよい。
　ピリジニウムカチオンの非限定的な例として、下記の式（２）で表されるカチオンが挙げられる。式（２）で表されるカチオンには、その互変異性体や、式（２）と共鳴関係にある構造式で表されるカチオンも含まれる。
　　式（２）：
 　式（２）中、Ｒ６は、アルキル基、アルケニル基、アルコキシアルキル基、又は置換若しくは非置換のフェニル基であり、Ｒ７～Ｒ１１は、同一又は異なって、水素原子、アルキル基、アルケニル基、アルコキシアルキル基、又は置換若しくは非置換のフェニル基である。
　Ｒ６～Ｒ１１におけるアルキル基、アルケニル基、アルコキシアルキル基、及び置換又は非置換のフェニル基としては、式（１）で表されるカチオンのＲ１～Ｒ５として説明したものと同様のものが例示される。
　Ｒ６は、アルキル基であることが好ましく、１～６個の炭素原子を有する直鎖状のアルキル基であることがより好ましい。Ｒ６～Ｒ１１は、水素原子又はアルキル基であることが好ましく、水素原子であることがより好ましい。
　上記ピリジニウムカチオンは、好ましくは、１－エチルピリジニウム、１－ブチルピリジニウム、１－ヘキシルピリジニウム、１－ブチル－４－メチルピリジニウム、１－ブチル－３－メチルピリジニウム、１－ヘキシル－４－メチルピリジニウム、１－ヘキシル－３－メチルピリジニウム、１－オクチル－４－メチルピリジニウム、１－オクチル－３－メチルピリジニウム、１－ブチル－３，４－ジメチルピリジニウム、１－ブチル－３，５－ジメチルピリジニウム等のピリジニウムのカチオンであってよく、特に好ましくは、１－オクチル－４－メチルピリジニウムのカチオンであってよい。
　ピロリジニウムカチオンの非限定的な例として、下記の式（３）で表されるカチオンが挙げられる。式（３）で表されるカチオンには、その互変異性体も含まれる。
　　式（３）：
 　式（３）中、Ｒ１２及びＲ１３は、同一又は異なって、アルキル基、アルケニル基、アルコキシアルキル基、又は置換若しくは非置換のフェニル基であり、Ｒ１４～Ｒ２１は、同一又は異なって、水素原子、アルキル基、アルケニル基、アルコキシアルキル基、又は置換若しくは非置換のフェニル基である。
　Ｒ１２～Ｒ２１におけるアルキル基、アルケニル基、アルコキシアルキル基、及び置換又は非置換のフェニル基としては、式（１）で表されるカチオンのＲ１～Ｒ５として説明したものと同様のものが例示される。
　Ｒ１２及びＲ１３は、アルキル基であることが好ましく、１～６個の炭素原子を有する直鎖状のアルキル基であることがより好ましい。Ｒ１４～Ｒ２１は、水素原子又はアルキル基であることが好ましく、水素原子であることがより好ましい。
　ピロリジニウムカチオンは、好ましくは、１－ブチル－１－メチルピロリジニウムのカチオンであってよい。
　ピペリジニウムカチオンの非限定的な例として、下記の式（４）で表されるカチオンが挙げられる。式（４）で表されるカチオンには、その互変異性体も含まれる。
　　式（４）：
 　式（４）中、Ｒ２２及びＲ２３は、同一又は異なって、アルキル基、アルケニル基、アルコキシアルキル基、又は置換若しくは非置換のフェニル基であり、Ｒ２４～Ｒ３３は、同一又は異なって、水素原子、アルキル基、アルケニル基、アルコキシアルキル基、又は置換若しくは非置換のフェニル基である。
　Ｒ２２～Ｒ３３におけるアルキル基、アルケニル基、アルコキシアルキル基、及び置換又は非置換のフェニル基としては、式（１）で表されるカチオンのＲ１～Ｒ５として説明したものと同様のものが例示される。
　Ｒ２２及びＲ２３は、アルキル基であることが好ましく、１～６個の炭素原子を有する直鎖状のアルキル基であることがより好ましい。Ｒ２４～Ｒ３３は、水素原子又はアルキル基であることが好ましく、水素原子であることがより好ましい。
　ピペリジニウムカチオンは、好ましくは、１－ブチル－１－メチルピペリジニウムのカチオンであってよい。
　四級アンモニウムカチオンの非限定的な例として、下記式（５）で表されるアンモニウムカチオンが挙げられる。式（５）で表されるカチオンには、その互変異性体も含まれる。
　　式（５）：
 　式（５）中、Ｒ３４～Ｒ３７は、同一又は異なって、アルキル基、アルケニル基、アルコキシアルキル基、又は置換若しくは非置換のフェニル基である。
　Ｒ３４～Ｒ３７におけるアルキル基としては、例えば、メチル基、エチル基、ｎ－プロピル基、イソプロピル基、ブチル基、ヘキシル基、オクチル基等の１～２０個（好ましくは１～１０個、より好ましくは２～６個、さらに好ましくは２～４個）の炭素原子を有する直鎖状又は分岐状のアルキル基が挙げられる。また、アルケニル基としては、ビニル基、１－プロペニル基、２－プロペニル基、１－ブテニル基、２－ブテニル基、１－ペンテニル基、２－ペンテニル基、１－ヘキセニル基、２－ヘキセニル基、１－オクテニル基等の２～２０個（好ましくは２～１０個、より好ましくは２～６個、さらに好ましくは２～４個）の炭素原子を有する直鎖状又は分岐状のアルケニル基が挙げられる。また、アルコキシアルキル基としては、メトキシメチル基、エトキシメチル基、１－メトキシエチル基、２－メトキシエチル基、１－エトキシエチル基、２－エトキシエチル基等の２～２０個（好ましくは２～１０個、より好ましくは２～６個、さらに好ましくは２～４個）の炭素原子を有する直鎖状又は分岐状のアルコキシアルキル基が挙げられる。さらに、置換若しくは非置換のフェニル基としては、水酸基、ハロゲン原子、低級アルコキシ基、低級アルケニル基、メチルスルホニルオキシ基、置換若しくは非置換の低級アルキル基、置換若しくは非置換のアミノ基、置換若しくは非置換のフェニル基、置換若しくは非置換のフェノキシ基及び置換若しくは非置換のピリジル基から選択される１～２個の基で置換されてもよいフェニル基が挙げられる。
　Ｒ３４～Ｒ３７は、アルキル基であることが好ましく、１～６個の炭素原子を有する直鎖状のアルキル基であることがより好ましい。
　四級アンモニウムカチオンとしては、好ましくは、トリメチルプロピルアンモニウム、トリメチルブチルアンモニウム、トリエチルメチルアンモニウム、トリオクチルメチルアンモニウム、テトラメチルアンモニウム、テトラエチルアンモニウム、テトラブチルアンモニウム、テトラペンチルアンモニウム、及びテトラヘキシルアンモニウムからなる群から選択される１以上のカチオンであってよい。
　四級ホスホニウムカチオンの非限定的な例として、下記式（６）で表されるホスホニウムカチオンが挙げられる。式（６）で表されるカチオンには、その互変異性体も含まれる。
　　式（６）：
 　式（６）中、Ｒ３８～Ｒ４１は、同一又は異なって、アルキル基、アルケニル基、アルコキシアルキル基、又は置換若しくは非置換のフェニル基である。
　Ｒ３８～Ｒ４１におけるアルキル基としては、例えば、メチル基、エチル基、ｎ－プロピル基、イソプロピル基、ブチル基、ヘキシル基、オクチル基等の１～２０個（好ましくは１～１０個、より好ましくは２～６個、さらに好ましくは２～４個）の炭素原子を有する直鎖状又は分岐状のアルキル基が挙げられる。また、アルケニル基としては、ビニル基、１－プロペニル基、２－プロペニル基、１－ブテニル基、２－ブテニル基、１－ペンテニル基、２－ペンテニル基、１－ヘキセニル基、２－ヘキセニル基、１－オクテニル基等の２～２０個（好ましくは２～１０個、より好ましくは２～６個、さらに好ましくは２～４個）の炭素原子を有する直鎖状又は分岐状のアルケニル基が挙げられる。また、アルコキシアルキル基としては、メトキシメチル基、エトキシメチル基、１－メトキシエチル基、２－メトキシエチル基、１－エトキシエチル基、２－エトキシエチル基等の２～２０個（好ましくは２～１０個、より好ましくは２～６個、さらに好ましくは２～４個）の炭素原子を有する直鎖状又は分岐状のアルコキシアルキル基が挙げられる。さらに、置換若しくは非置換のフェニル基としては、水酸基、ハロゲン原子、低級アルコキシ基、低級アルケニル基、メチルスルホニルオキシ基、置換若しくは非置換の低級アルキル基、置換若しくは非置換のアミノ基、置換若しくは非置換のフェニル基、置換若しくは非置換のフェノキシ基及び置換若しくは非置換のピリジル基から選択される１～２個の基で置換されてもよいフェニル基が挙げられる。
　四級ホスホニウムカチオンは、好ましくは、テトラメチルホスホニウム、テトラエチルホスホニウム、テトラブチルホスホニウム、テトラヘキシルホスホニウム、テトラオクチルホスホニウム、トリエチルメチルホスホニウム、及びトリブチルエチルホスホニウムからなる群から選択される１以上のカチオンであってよい。
（アニオン成分）
　アニオン成分の非限定的な例として、ハロゲンアニオン、擬ハロゲンアニオン、カルボン酸アニオン、リン酸系アニオン、アミノ酸アニオン、フェノラート、ピリミジンオラート、テトラフルオロホウ酸イオン（ＢＦ４－）、サルフォメチルイオン（ＣＨ３ＳＯ３ －）、メチルホスホネート、硫酸イオン、ＰＦ６ －等が挙げられる。
　ハロゲンアニオンの非限定的な例として、フッ化物イオン（Ｆ－）、塩化物イオン（Ｃｌ－）、ヨウ素イオン（Ｉ－）、及び臭化物イオン（Ｂｒ－）等が挙げられる。
　擬ハロゲンアニオンの非限定的な例として、シアンアニオン、チオシアネートアニオン、シアネートアニオン、フルミネートアニオン、アジドアニオン等が挙げられる。
　カルボン酸アニオンの非限定的な例として、炭素数１～１８のモノカルボン酸アニオン又はジカルボン酸アニオン等が挙げられる。カルボン酸アニオンは、好ましくは、ギ酸アニオン、酢酸アニオン、プロピオン酸アニオン、酪酸アニオン、吉草酸アニオン、フマル酸アニオン、シュウ酸アニオン、乳酸アニオン、及びピルビン酸アニオンからなる群から選択される１以上が挙げられる。
　リン酸系アニオンの非限定的な例として、リン酸アニオン、炭素数１～４０のリン酸エステルアニオン等が挙げられる。リン酸エステルアニオンの非限定的な例として、メチルリン酸モノエステルアニオン、オクチルリン酸モノエステルアニオン、オクチルリン酸ジエステルアニオン、ラウリルリン酸モノエステルアニオン、ラウリルリン酸ジエステルアニオン、ステアリルリン酸モノエステルアニオン、ステアリルリン酸ジエステルアニオン、エイコシルリン酸モノエステルアニオン、エイコシルリン酸ジエステルアニオン等が挙げられる。
（カチオン成分とアニオン成分との組合せ）
　イオン液体は、上記カチオン成分と上記アニオン成分とを任意に組み合わせたものである。例えば、カチオン成分として、イミダゾリウムカチオン又は四級アンモニウムカチオンを含むイオン液体が好ましい。また、アニオン成分として、カルボン酸アニオンを含むイオン液体が好ましい。より具体的には、１－エチル－３－メチルイミダゾリウムアセテート（ＥｍｉｍＯＡｃ）、１－エチル－２，３－ジメチルイミダゾリウムアセテート（ＥＤｍｉｍＯＡｃ）、１－ブチル－３－メチルイミダゾリウムアセテート、１－ヘキシル－３－メチルイミダゾリウムアセテート、及びテトラブチルアンモニウムアセテートからなる群から選択される少なくとも１つであることがより好ましい。
　イオン液体は、好ましくは、１－エチル－３－メチルイミダゾリウムアセテート（ＥｍｉｍＯＡｃ）、及び１－エチル－２，３－ジメチルイミダゾリウムアセテート（ＥＤｍｉｍＯＡｃ）からなる群から選ばれた少なくとも１つであってよく、特に好ましくは、１－エチル－３－メチルイミダゾリウムアセテート（ＥｍｉｍＯＡｃ）であってよい。
　イオン液体は、市販品を使用することができる。また、公知の技術により製造することもできる。
［共溶媒］
　共溶媒は、イオン液体を含む液体の粘度を下げ、また、イオン液体の使用量を削減するために添加される。共溶媒は、好ましくは高沸点極性溶媒である。高沸点極性溶媒は、好ましくは、有機酸よりも高い沸点を有する極性溶媒である。例えば、有機酸が酢酸である場合、沸点が１１７．９℃であるので、それよりも高い沸点を有する極性溶媒が好ましい。好ましくは沸点が１２０℃以上、さらに好ましくは沸点が１５０℃以上である。
　共溶媒の非限定的な例として、ジメチルスルホキシド（ＤＭＳＯ）、スルホラン、Ｎ，Ｎ－ジメチルホルムアミド（ＤＭＦ）、Ｎ－メチル－２－ピロリドン（ＮＭＰ）、及びこれらの組合せからなる群から選択される共溶媒が挙げられ、これらから選択される１以上を含んでいてもよい。
＜セルロースエステルの製造方法＞
　一実施形態において、
　セルロースエステルの製造方法であって、
　セルロースをイオン液体及び共溶媒を含む第１の液体に溶解することにより、第２の液体を得る第１工程と、
　前記第２の液体に有機酸無水物を添加することにより、セルロースと有機酸無水物とを反応させ、セルロースエステルを生成させる第２工程と、
　前記第２工程に続き、前記第２の液体にさらに貧溶媒を添加することにより、セルロースエステルを析出させる第３工程と、
　前記第３工程に続き、セルロースエステルを含む固相と、イオン液体、共溶媒、前記有機酸無水物由来の有機酸、及び貧溶媒を含む第３の液体からなる液相とを分離し、前記固相からセルロースエステルを回収し、前記液相から前記第３の液体を回収する第４工程と、
　前記第３の液体を蒸留することにより、前記第３の液体から前記有機酸及び／又は前記貧溶媒を除去し、イオン液体、共溶媒、及び蒸留により生じた着色成分を含む第４の液体を得る第５工程と、
　前記第４の液体をナノろ過膜又は逆浸透膜に供することにより、イオン液体を含む第５の液体と、着色成分とを分離し、前記第５の液体を回収する第６工程と
を含み、
　前記第５の液体の全部又は一部を前記第１の液体の全部又は一部として再使用することにより、前記第１工程から前記第６工程を繰り返すことができる、
製造方法
が提供される。
　このセルロースエステルの製造方法は、イオン液体を含む液体を反応溶媒として用いることにより、セルロースエステルを効果的に製造することができる。
　また、このセルロースエステルの製造方法は、セルロースエステル生成反応に用いたイオン液体を効果的に回収し、次の生成反応に再使用することが可能であり、これにより、高価なイオン液体の使用に係るコストを削減することができる。また、イオン液体の使用量を削減することにより、環境負荷を軽減することができる。
　上述の第６工程は、好ましくは、上述のイオン液体及び共溶媒を含む液体を回収するための方法に従って、実施される。
　この実施形態における、イオン液体、共溶媒、着色成分などは、上述のイオン液体及び共溶媒を含む液体を回収するための方法について説明したものと同様である。また、この実施形態における各液体の組成は、上述のイオン液体を含む液体を回収するための方法について説明した液体と同様であってよい。
［セルロース及びセルロースエステル］
　セルロースは、分子式（Ｃ６Ｈ１０Ｏ５）ｎで表される炭水化物である。セルロースは植物細胞の細胞壁および植物繊維の主成分である。
　セルロースエステルは、セルロースを、有機酸無水物を用いて、エステル化したものである。例えば、酢酸セルロースは、セルロースを、無水酢酸を用いて、エステル化したものである。
　セルロースエステルは、バイオマス素材であり、高い生分解性を有するなど、環境負荷が小さい素材として重要である。
［有機酸無水物］
　有機酸無水物は、セルロースをエステル化し、セルロースエステルを生成させることができる。有機酸無水物の非限定的な例として、好ましくはＣ１－１８カルボン酸、より好ましくはＣ１－１０カルボン酸、さらに好ましくはＣ１－６カルボン酸、特に好ましくはＣ２－４カルボン酸の酸無水物が挙げられ、また、ギ酸、酢酸、プロピオン酸、トリフルオロ酢酸などのカルボン酸の酸無水物が挙げられる。
　有機酸無水物は、合成するセルロースエステルの種類に応じて、適切に選択することができる。例えば、合成するセルロースエステルが酢酸セルロースである場合には、有機酸無水物として、無水酢酸が好適に用いられる。
［有機酸］
　有機酸は、上述の有機酸無水物が加水分解することにより生成される。例えば、有機酸は、上述のセルロースエステルの生成反応において、有機酸無水物によりセルロースがエステル化する際に、副生成物として生成される。また、有機酸は、後述する貧溶媒が水を含む場合、有機酸無水物が水により加水分解される際にも、生成される。有機酸無水物が無水酢酸である場合、生成される有機酸は、酢酸である。
［貧溶媒］
　貧溶媒は、セルロースエステルに対する溶解性が低い溶媒である。貧溶媒は、セルロースエステルが溶解した、上記の第２の液体に添加することで、第２の液体からセルロースエステルを析出させることができる。また、貧溶媒は、析出したセルロースエステルを洗浄する用途にも、使用することができる。この場合、析出したセルロースエステルを洗浄するのに使用した貧溶媒は、第２の液体と併せることができる。
　貧溶媒の非限定的な例として、水、メタノール、エタノール、２－オクタノール等のアルコール類、アセトン等のケトン類が挙げられる。
　第２の液体、又は第２の液体において、析出したセルロースエステルを除いた第３の液体は、貧溶媒を、第２の液体又は第３の液体の総重量に対し、好ましくは、３０～９０重量％、より好ましくは、４０～８０重量％含んでいてもよい。
［蒸留］
　蒸留は、不純物を含む液体を蒸発・再凝縮することにより、沸点の違いに基づき、不純物を除去し液体を精製する操作である。蒸留の温度は、液体及び不純物の沸点に応じて、適切に設定される。また、液体が複数の不純物を含む場合、段階的に温度を上昇させた複数回の蒸留を順次実施することにより、該複数の不純物を順次除去することで、液体をより効果的に精製することができる。例えば、上述の第５工程では、有機酸を除去する蒸留と、貧溶媒を除去する蒸留とを、順次に実施することができる。
［メタノールを添加及び／又は除去する追加工程］
　セルロースエステルの製造方法は、上記の第６工程に先立ち、第４の液体に、第４の液体の総重量に対して、好ましくは３０重量％以上、より好ましくは３５重量％以上、あるいは、４０～７０重量％、より好ましくは４５～６０重量％となるように、メタノールを添加することを含んでいてもよい。
　メタノールを添加する追加工程を含むことにより、セルロースエステルの製造方法は、イオン液体を含む液体に含まれる着色成分をより効果的に除去することができる傾向にある。
　メタノールを添加する追加工程を含む場合、セルロースエステルの製造方法は、上記の第６工程の後に、例えば蒸留や抽出により、イオン液体を含む液体からメタノールを除去する工程をさらに含んでいてもよい。
［セルロース由来不純物を除去する追加工程］
　上記の第２工程におけるセルロースエステルの生成反応の副生成物として、セルロースエステル由来不純物が生じることがある。セルロースエステル由来不純物は、上記の第４工程において、第３の液体に溶解又は混入することがある。
　上記のセルロースエステルの製造方法は、セルロースエステル由来不純物を除去する追加工程を含んでいてもよい。セルロースエステル由来不純物を除去する追加工程は、好ましくは、上記の第６工程に先立っての第４の液体を限外ろ過膜に供し、これにより前記第４の液体中のセルロース由来不純物を除去することにより、実施される。
　セルロース由来不純物を含むイオン液体を含む液体をセルロースエステルの合成に再使用する場合、セルロースエステルの合成を効果的に実施することが困難になる傾向にある。セルロースエステルの製造方法は、セルロース由来不純物を除去する追加工程を含むことにより、イオン液体をより効果的に回収し、より効果的に再使用することが可能になる。
（セルロース由来不純物）
　セルロース由来不純物は、典型的には、セルロースをエステル化してセルロースエステルを製造する際に、合成を終了し、製品としてのセルロースエステルを回収した後の反応液に、溶解又は混入している、セルロース由来不純物である。
　セルロース由来不純物には、典型的には、未反応のセルロース、置換度が小さいセルロースエステル、及び分子量が比較的小さいセルロースエステルのうちの１つ以上が含まれる。
　セルロース由来不純物は、イオン液体及び共溶媒を含む液体を次回の合成に再使用する際の不純物となり得る。
　セルロース由来不純物の分子量は、好ましくは１０，０００～１，５００，０００、より好ましくは２０，０００～１，０００，０００である。セルロース由来不純物の分子量は、たとえば、ゲルろ過クロマトグラフィー（ＧＰＣ）により測定することができる。
　セルロース由来不純物として含まれるセルロースエステルの置換度は、好ましくは３.０以下、より好ましくは２．９以下であり、または好ましくは１．５～２．９、より好ましくは２．０～２．９である。セルロースエステルの置換度は、核磁気共鳴分析装置（ＮＭＲ）により測定することができる。
　セルロース由来不純物として含まれるセルロースエステルは、好ましくは、酢酸セルロースである。
（限外ろ過膜）
　限外ろ過（ＵＦ）膜は、特定の分画分子量より大きい分子量を有する分子と、これより小さい分子量を有する分子とをふるいわけることができる膜である。
　限外ろ過膜の分画分子量は、好ましくは１，０００～１，０００，０００、より好ましくは５，０００～１００，０００、さらに好ましくは１０，０００～３０，０００である。分画分子量がこれらの範囲である限外ろ過膜は、イオン液体、共溶媒、及びセルロースエステルを含む液体からセルロースエステルを除くことが容易である傾向にある。
　限外ろ過膜の分画分子量は、例えば、所定の分子量を有するポリエチレングリコール（ＰＥＧ）のＮＭＰ溶液を試験液として用いた、定圧クロスフロー試験により決定することができる。具体的には、例えば、以下のようにして実施することができる。分子量３Ｋ、８Ｋ、１２Ｋ、３５Ｋ、１００Ｋ、及び５００ＫのＰＥＧを、それぞれ０．１％にてＮＭＰに混合溶解し、これを試験対象の限外ろ過膜で構成された中空糸膜モジュールに、例えば９．９ｍｌ／分の流量で、通液する。さらに中空糸膜の入口付近に設けた圧力計と中空糸膜の出口付近に設けた調圧用レギュレーターにより、操作圧を所定の圧力（例えば１ｂａｒ又は４ｂａｒ）に設定することにより、定圧条件で試験を実施する。通液開始の後（例えば６時間後）に、供給液とろ液とを採取する。採取した供給液とろ液とを、それぞれゲルろ過クロマトグラフィー（ＧＰＣ）カラムと示差屈折（ＲＩ）検出器を用いた液体クロマトグラフィーにより分析する。分子量（ＰＥＧ検量線から算出）に対するＲＩピーク強度のクロマトグラムから供給液強度（Ｉｆｅｅｄ）とろ液強度（Ｉｆｉｌｌ）を求め、下記の数式３からＰＥＧの阻止率を算出することにより、限外ろ過膜の分画曲線をプロットし、９０％阻止率となる分子量を分画分子量として決定する。
　　数式３：阻止率（％）＝（１－Ｉｆｉｌｌ／Ｉｆｅｅｄ）×１００
　限外ろ過膜は、ジメチルスルホキシド（ＤＭＳＯ）、スルホラン、Ｎ，Ｎ－ジメチルホルムアミド（ＤＭＦ）、Ｎ－メチル－２－ピロリドン（ＮＭＰ）、ジメチルアセトアミド（ＤＭＡｃ）などの高沸点極性溶媒に対する耐性が高いことが好ましい。高沸点極性溶媒に対する耐性が高いことにより、共溶媒が高沸点極性溶媒である場合でも、限外ろ過膜を安定して使用することが可能になる。
　限外ろ過膜は、親水性が高いことが好ましい。限外ろ過膜に供されるイオン液体、共溶媒、及びセルロースエステルは、いずれも親水性が高い。したがって、限外ろ過膜の親水性が高い場合、限外ろ過膜へのイオン液体、共溶媒、及びセルロースエステルの吸着が抑制されることにより、吸着による透過速度の低下（膜ファウリング）が抑制され、限外ろ過膜が長期間にわたり、安定的に使用することが可能になり易い。
　限外ろ過膜は、好ましくはポリアミド樹脂を含む。ポリアミド樹脂は、例えば、ポリアミド６、ポリアミド６６、ポリアミド４６、ポリアミド６１０、ポリアミド６１２、ポリアミド１１、ポリアミド１、ポリアミドＭＸＤ６、ポリアミド４Ｔ、ポリアミド６Ｔ、ポリアミド９Ｔ、ポリアミド１０Ｔや、これらのポリアミドの共重合体であってよく、また、これらから選択される複数を含むものであってもよい。
　限外ろ過膜のＮＭＰ透過速度は、好ましくは１～５０Ｌ／ｍ２／ｈ／ｂａｒであり、より好ましくは、１０～２０Ｌ／ｍ２／ｈ／ｂａｒである。
　ＮＭＰ透過速度は、例えば、低圧クロスフロー試験により測定することができる。具体的には、例えば、以下のようにして実施することができる。ＮＭＰを試験対象の限外ろ過膜で構成された中空糸膜モジュールに、例えば９．９ｍｌ／分の流量で、通液する。さらに中空糸膜の入口付近に設けた圧力計と中空糸膜の出口付近に設けた調圧用レギュレーターにより、操作圧を所定の圧力（例えば１ｂａｒ又は４ｂａｒ）に設定することにより、定圧条件で試験を実施する。このとき、中空糸膜の出口から排出される、ろ液の透過速度を測定することで、単位時間（ｈ）、単位膜面積（ｍ２）、単位圧力（ｂａｒ）あたりの透過速度（Ｌ／ｍ２／ｈｒ／ｂａｒ）を算出することができる。
　限外ろ過膜の不純物含有液体の透過速度は、好ましくは０．１～１０Ｌ／ｍ２／ｈ／ｂａｒであり、より好ましくは０．２～２Ｌ／ｍ２／ｈ／ｂａｒである。
　限外ろ過膜の不純物含有液体の透過速度は、上述のＮＭＰ透過速度と同様にして、測定することができる。
　限外ろ過膜の、不純物含有液体中の不純物の阻止率は、好ましくは３０～９９％であり、より好ましくは７０～９９％である。
　限外ろ過膜の、不純物の阻止率は、例えば、定圧クロスフロー試験により測定することができる。具体的には、例えば、以下のようにして実施することができる。不純物含有液体を試験対象の限外ろ過膜で構成された中空糸膜モジュールに、例えば９．９ｍｌ／分の流量で、通液する。さらに中空糸膜の入口付近に設けた圧力計と中空糸膜の出口付近に設けた調圧用レギュレーターにより、操作圧を所定の圧力（例えば１ｂａｒ又は４ｂａｒ）に設定することにより、定圧条件で試験を実施する。通液開始の後（例えば２４時間後）に、通液開始の２４時間後に、供給液とろ液とそれぞれを採取する。採取した供給液及びろ液について、それぞれ、フェノール硫酸法による糖分析定量により、酢酸セルロースの含有量を定量する。定量は、溶媒による測定値への影響を勘案し、同一溶媒系で作成した検量線を用いて実施することが好ましい、供給液中の酢酸セルロースの含有量（Ｃｆｅｅｄ）、ろ液中の酢酸セルロースの含有量（Ｃｆｉｌｌ）に基づき、下記の数式４により溶媒中の不純物の阻止率を算出することができる。
　　数式４：　阻止率（％）＝（１－Ｃｆｉｌｌ／Ｃｆｅｅｄ）×１００
　限外ろ過膜は、容器に収納された膜モジュールの形態で、複数本使用されるものであってよい。この場合、膜モジュール１本あたりの膜面積は、本発明の効果が得られる範囲で任意であるが、好ましくは１～２００ｍ２であり、より好ましくは１０～１００ｍ２である。限外ろ過膜の表面積は、メーカーカタログ値であってもよく、定法による測定値であってもよい。必要な膜モジュール本数は、処理量と膜の透過速度で決定される。
　限外ろ過膜は、イオン液体及び共溶媒を含む液体に対し、好ましくは３月間、より好ましくは６月間、さらに好ましくは１２月間にわたり、耐性を有する。
　限外ろ過膜の厚さは、好ましくは０．１～５ｍｍであり、より好ましくは０．３～３ｍｍである。
　限外ろ過膜は、本発明の効果が得られる範囲で、任意の形状であってよく、例えば中空糸膜であってもよく、平膜であってもよい。
　限外ろ過膜として、本発明の効果が得られる範囲で、市販の限外ろ過膜を用いることができる。市販の限外ろ過膜の非限定的な例として、ユニチカ製ＵＦ５０、ＵＦ１２０などが挙げられる。また、限外ろ過膜として、公知の方法により製造した限外ろ過膜を使用することもできる。
　限外ろ過膜により除去されるセルロースエステルの分子量は、好ましくは１０，０００～１，５００，０００、より好ましくは２０，０００～１，０００，０００である。
　限外ろ過膜により除去されるセルロースエステルの置換度は、好ましくは３.０以下、より好ましくは２．９以下であり、または好ましくは１．５～２．９、より好ましくは２．０～２．９である。セルロースエステルの置換度は、核磁気共鳴分析装置（ＮＭＲ）により測定することができる。
　本開示の例示的な実施形態及び例示的な実施形態の組み合わせの非限定的なリストを以下に開示する。
　［１］イオン液体及び着色成分を含む着色液体から、イオン液体を含む液体を回収するための方法であって、前記着色液体をナノろ過膜又は逆浸透膜に供することにより、イオン液体を含む前記液体と、前記着色成分とを分離することを含む、方法。
　［２］前記ナノろ過膜又は前記逆浸透膜の塩阻止率が、９５％以上であり、
　前記塩阻止率が、
　数式１：塩阻止率（％）＝（１－Ｃｆｉｌｌ／Ｃｆｅｅｄ）×１００
［数式１において、Ｃｆｅｅｄは、前記ナノろ過膜又は前記逆浸透膜にＮａＣｌ水溶液を通液する際に、前記ナノろ過膜又は前記逆浸透膜に供給されるＮａＣｌ水溶液中のＮａＣｌ濃度であり、Ｃｆｉｌｌは、前記ナノろ過膜又は前記逆浸透膜にＮａＣｌ水溶液を通液した際に、前記ナノろ過膜又は前記逆浸透膜から排出されるＮａＣｌ水溶液中のＮａＣｌ濃度である］
により算出される、
［１］に記載の方法。
　［３］前記ナノろ過膜又は前記逆浸透膜の透水係数が、１．０Ｌ／ｍ２／ｈ／ｂａｒ未満であり、ここで、前記透水係数は、１６００ｐｐｍ　ＮａＣｌ水溶液が前記ナノろ過膜又は前記逆浸透膜を透過する際の、単位時間（ｈ）、単位膜面積（ｍ２）、単位圧力（ｂａｒ）あたりの透過速度として定義される、［１］又は［２］に記載の方法。
　［４］前記着色液体が、前記着色液体の総重量に対し、３０重量％以上のメタノールを含む、［１］から［３］のいずれかに記載の方法。
　［５］前記ナノろ過膜又は前記逆浸透膜の塩阻止率が、８５％以上であり、
　前記塩阻止率が、
　数式１：塩阻止率（％）＝（１－Ｃｆｉｌｌ／Ｃｆｅｅｄ）×１００
［数式１において、Ｃｆｅｅｄは、前記ナノろ過膜又は前記逆浸透膜にＮａＣｌ水溶液を通液した際に、前記ナノろ過膜又は前記逆浸透膜に供給されるＮａＣｌ水溶液中のＮａＣｌ濃度であり、Ｃｆｉｌｌは、前記ナノろ過膜又は前記逆浸透膜にＮａＣｌ水溶液を通液した際に、前記ナノろ過膜又は前記逆浸透膜から排出されるＮａＣｌ水溶液中のＮａＣｌ濃度である］
により算出される、［４］に記載の方法。
　［６］前記ナノろ過膜又は前記逆浸透膜の透水係数が、８．０Ｌ／ｍ２／ｈ／ｂａｒ未満であり、ここで、前記透水係数は、１６００ｐｐｍ　ＮａＣｌ水溶液が前記ナノろ過膜又は前記逆浸透膜を透過する際の、単位時間（ｈ）、単位膜面積（ｍ２）、単位圧力（ｂａｒ）あたりの透過速度として定義される、［４］又は［５］に記載の方法。
　［７］前記ナノろ過膜又は前記逆浸透膜が、ポリアミドを含む活性層を含む、［１］から［６］のいずれかに記載の方法。
　［８］前記イオン液体が、カチオン成分として、イミダゾリウムカチオン又は四級アンモニウムカチオンを含み、アニオン成分としてカルボン酸アニオンを含む、［１］から［７］のいずれかに記載の方法。
　［９］前記イオン液体が、１－エチル－３－メチルイミダゾリウムアセテート（ＥｍｉｍＯＡｃ）、１－エチル－２，３－ジメチルイミダゾリウムアセテート（ＥＤｍｉｍＯＡｃ）、１－ブチル－３－メチルイミダゾリウムアセテート、１－ヘキシル－３－メチルイミダゾリウムアセテート、テトラブチルアンモニウムアセテート、及びこれらの組合せからなる群から選択される、［１］から［８］のいずれかに記載の方法。
　［１０］前記ナノろ過膜又は前記逆浸透膜による着色除去率が、３０％以上である、［１］から［９］のいずれかに記載の方法。
　［１１］前記着色液体が、共溶媒をさらに含む、［１］から［１０］のいずれかに記載の方法。
　［１２］前記共溶媒が、高沸点極性溶媒である、［１１］に記載の方法。
　［１３］前記高沸点極性溶媒がジメチルスルホキシド（ＤＭＳＯ）、スルホラン、Ｎ，Ｎ－ジメチルホルムアミド（ＤＭＦ）、Ｎ－メチル－２－ピロリドン（ＮＭＰ）、及びこれらの組合せからなる群から選択される、［１２］に記載の方法。
　［１４］
　セルロースエステルの製造方法であって、
　セルロースをイオン液体及び共溶媒を含む第１の液体に溶解することにより、第２の液体を得る第１工程と、
　前記第２の液体に有機酸無水物を添加することにより、セルロースと有機酸無水物とを反応させ、セルロースエステルを生成させる第２工程と、
　前記第２工程に続き、前記第２の液体にさらに貧溶媒を添加することにより、セルロースエステルを析出させる第３工程と、
　前記第３工程に続き、セルロースエステルを含む固相と、イオン液体、共溶媒、前記有機酸無水物由来の有機酸、及び貧溶媒を含む第３の液体からなる液相とを分離し、前記固相からセルロースエステルを回収し、前記液相から前記第３の液体を回収する第４工程と、
　前記第３の液体を蒸留することにより、前記第３の液体から前記有機酸及び／又は前記貧溶媒を除去し、イオン液体、共溶媒、及び蒸留により生じた着色成分を含む第４の液体を得る第５工程と、
　前記第４の液体をナノろ過膜又は逆浸透膜に供することにより、イオン液体を含む第５の液体と、着色成分とを分離し、前記第５の液体を回収する第６工程と
を含み、
　前記第５の液体の全部又は一部を前記第１の液体の全部又は一部として再使用することにより、前記第１工程から前記第６工程を繰り返すことができる、
製造方法。
　［１５］前記第６工程に先立ち、前記第４の液体に、前記第４の液体の総重量に対して３０重量％以上となるように、メタノールを添加することを含む、［１４］に記載の製造方法。
　［１６］前記第６工程に先立ち、前記第４の液体を限外ろ過膜に供し、これにより前記第４の液体中のセルロース由来不純物を除去する追加工程を含む、［１４］又は［１５］に記載の方法。
　［１７］
　セルロースエステルの製造方法であって、
　セルロースをイオン液体及び共溶媒を含む第１の液体に溶解することにより、第２の液体を得る第１工程と、
　前記第２の液体に有機酸無水物を添加することにより、セルロースと有機酸無水物とを反応させ、セルロースエステルを生成させる第２工程と、
　前記第２工程に続き、前記第２の液体にさらに貧溶媒を添加することにより、セルロースエステルを析出させる第３工程と、
　前記第３工程に続き、セルロースエステルを含む固相と、イオン液体、共溶媒、前記有機酸無水物由来の有機酸、及び貧溶媒を含む第３の液体からなる液相とを分離し、前記固相からセルロースエステルを回収し、前記液相から前記第３の液体を回収する第４工程と、
　前記第３の液体を蒸留することにより、前記第３の液体から前記有機酸及び／又は前記貧溶媒を除去し、イオン液体、共溶媒、及び蒸留により生じた着色成分を含む第４の液体を得る第５工程と、
　［１］から［１３］のいずれかに記載の方法に従い、前記第４の液体をナノろ過膜又は逆浸透膜に供することにより、イオン液体を含む第５の液体と、着色成分とを分離し、前記第５の液体を回収する第６工程と
を含み、
　前記第５の液体の全部又は一部を前記第１の液体の全部又は一部として再使用することにより、前記第１工程から前記第６工程を繰り返すことができる、
製造方法。
　［１８］
　前記第６工程に先立ち、前記第４の液体に、前記第４の液体の総重量に対して３０重量％以上となるように、メタノールを添加することを含む、［１７］に記載の製造方法。
　［１９］前記第６工程に先立ち、前記第４の液体を限外ろ過膜に供し、これにより前記第４の液体中のセルロース由来不純物を除去する追加工程を含む、［１７］又は［１８］に記載の方法。
　各実施形態における各構成及びそれらの組み合わせ等は、一例であって、本開示の主旨から逸脱しない範囲内で、適宜、構成の付加、省略、置換、及びその他の変更が可能である。
　以下に実施例を示して本開示を更に具体的に説明するが、これらの実施例により本開示の解釈が限定されるものではない。
＜ナノろ過膜又は逆浸透膜による着色成分の除去＞
　本開示に係るナノろ過膜又は逆浸透膜による着色成分の除去について検討した。
　ナノろ過膜又は逆浸透膜として、ポリケトン担体界面重合複合膜及びポリスルホン担体複合膜を用いた。
　ポリケトン担体界面重合複合膜（ＩＰ－ＰＫ膜）としては、非溶媒相分離法により作製した、ポリケトン（Ｈｙｏｓｕｎｇ社製）からなる基材平膜の表面に、ｍ－フェニレンジアミン（ＭＰＤ）又はトリメシン酸クロライド（ＴＭＣ）の各モノマーから構成される、ポリアミドを含む活性層を、公知の方法により重合させた膜（ＩＰ－ＰＫ膜）を用いた。
　ポリスルホン担体複合膜としては、市販の逆浸透膜である日東電工社製ＳＷＣ４）、市販のナノろ過膜であるＡｑｕｑｓｏｕｒｃｅ社製ＴｒｉＳｅｐ　ＴＳ８０、及び日東電工社製ＮＴＲ７２５０を用いた。なお、ＳＷＣ４及びＴｒｉＳｅｐ　ＴＳ８０は、分離活性層がポリアミドを含む界面重合複合膜（ＩＰ－ＰＳ膜）であり、ＮＴＲ７２５０は分離活性層がポリビニルアルコールとポリアミドを含む膜（ＶＡ－ＰＳ膜）である。
　ナノろ過膜又は逆浸透膜に供する液体として、ＥｍｉｍＯＡｃ／ＮＭＰ混合液体、及びｍｉｍＯＡｃ／ＮＭＰ／メタノール混合液体を用い、これを１２０℃にて１４時間加熱することにより、着色成分を生成させたものを用いた。なお、これらの液体の成分は、ＥｍｉｍＯＡｃ（ＩＬｑ）とＮＭＰとの重量比、又はＥｍｉｍＯＡｃ（ＩＬｑ）とＮＭＰとメタノール（Ｍｅ）との重量比で表す。
[膜の塩阻止率と透水係数]
　ナノろ過膜又は逆浸透膜の塩阻止率及び透水係数を、表面積０．０００８ｍ２のナノろ過膜又は逆浸透膜の平膜を用いた定圧クロスフロー試験により測定した。すなわち、ＮａＣｌを１６００ｐｐｍで純水に溶解した液を９．９ｍｌ／分の流量で、ナノろ過膜又は逆浸透膜に通液した。さらにナノろ過膜又は逆浸透膜の入口付近に設けた圧力計とナノろ過膜又は逆浸透膜の出口付近に設けた調圧用レギュレーターにより、操作圧を１０ｂａｒに設定することにより、定圧条件で試験を実施した。通液開始の１時間後に、供給液とろ液とを採取した。電気伝導度計により、供給液におけるＮａＣｌ濃度（Ｃｆｅｅｄ）とろ液におけるＮａＣｌ濃度（Ｃｆｉｌｌ）を測定した。
　塩阻止率は、
　数式１：塩阻止率（％）＝（１－Ｃｆｉｌｌ／Ｃｆｅｅｄ）×１００
［数式１において、Ｃｆｅｅｄは、前記ナノろ過膜又は前記逆浸透膜にＮａＣｌ水溶液を通液した際に、ナノろ過膜又は逆浸透膜に供給されるＮａＣｌ水溶液中のＮａＣｌ濃度であり、Ｃｆｉｌｌは、ナノろ過膜又は逆浸透膜にＮａＣｌ水溶液を通液した際に、ナノろ過膜又は前記逆浸透膜から排出されるＮａＣｌ水溶液中のＮａＣｌ濃度である］
により算出した。
　透水係数は、ＮａＣｌ水溶液をナノろ過膜又は逆浸透膜に通液する際の透過速度として決定された。
［着色除去率］
　各液体について上述と同様に定圧クロスフロー試験を行い、得られた供給液とろ液と試料とし、これらをそれぞれアセトニトリルで２０倍に希釈して３８０～７７０ｎｍにおける吸光度の平均を測定することにより、供給液の吸光度平均値（Ａｂｓｆｅｅｄ）及びろ液の吸光度平均値（Ａｂｓｆｉｌｌ）を求めた。
　着色除去率は、
　数式２：着色除去率（％）＝（１－Ａｂｓｆｉｌｌ／Ａｂｓｆｅｅｄ）×１００
［数式２において、Ａｂｓｆｉｌｌは、ナノろ過膜又は逆浸透膜にイオン液体を含む液体を通液する際の、前記ナノろ過膜又は前記逆浸透膜に供給されるイオン液体を含む液体の３８０～７７０ｎｍにおける吸光度の平均であり、Ａｂｓｆｅｅｄは、ナノろ過膜又は逆浸透膜にイオン液体を含む液体を通液する際の、前記ナノろ過膜又は前記逆浸透膜から排出されるイオン液体を含む液体の３８０～７７０ｎｍにおける吸光度の平均である。］
より算出した。
　なお、図１に示されるように、イオン液体を含む液体において、例えば蒸留などの加熱を伴う処理により生じる着色成分は、紫外領域に吸収ピークをもち、可視光領域に吸光帯が広がっている。したがって、上述のように、着色除去率は、３８０～７７０ｎｍにおける吸光度の平均に基づき、適切に評価することができる。
［イオン液体の回収率］
　イオン液体全体の回収率の評価は、以下の方法で行った。着色成分を除去する操作を行う前後の液体を減圧乾固（１４０℃、５時間）することにより、液体から揮発性溶媒（ＮＭＰ，メタノール）を除去した。残渣としてのイオン液体の重量を、着色成分を除去する操作を行う前後で測定した。着色成分を除去する操作後のイオン液体の重量を、着色成分を除去する操作前のイオン液体の重量で除し、１００を乗じることにより、回収率（％）を算出した。
［活性炭による着色成分の除去］
　着色成分の除去に関する比較例として、活性炭による着色成分の除去について評価した。活性炭として、市販の活性炭である、大阪ガスケミカル社製の白鷺Ａ、白鷺ＡＮＯＸ－１、及びカルボラフィンを用いた。
　活性炭を用いた脱色試験は、液体５０ｇに対し活性炭を１．０ｇ添加（浴比５０）で添加したものを、ボルテックスミキサーで１分間攪拌し、５分間の静置後、遠心分離（３０００ｒｐｍ×１０分）を行い、ろ紙で上澄み液をろ過回収することにより行った。該液体を、活性炭を添加しなかった液体と比較し、各パラメータを上述と同様の方法で決定した。
　ナノろ過膜又は逆浸透膜の着色除去率と、活性炭との比較の着色除去率が、表１に示される。
　表１に示されるように、ナノろ過膜又は逆浸透膜は、良好な着色除去率を示した。一方、活性炭は、良好な着色除去率を示さなかった。
　ナノろ過膜又は逆浸透膜の各パラメータが、表２に示される。
　表２に示されるように、実施例のナノろ過膜又は逆浸透膜は、良好な着色除去率を示した。一方、比較例のナノろ過膜又は逆浸透膜は、良好な着色除去率を示さなかった。
＜限外ろ過膜によるセルロース由来不純物の除去＞
　本開示に係る限外ろ過膜によるセルロース由来不純物の除去について検討するため、限外ろ過膜のＮＭＰ透過速度、分画分子量、並びに不純物含有液体の透過速度及び該溶媒中の不純物の阻止率を測定した。
　限外ろ過膜としては、ナイロン樹脂製の中空糸膜（ユニチカ製ＵＦ５０、ＵＦ１２０）及びポリエーテルサルフォン（ＰＥＳ）製の中空糸膜を使用した。
［ＮＭＰ透過速度］
　ＮＭＰ透過速度は、表面積０．０１２ｍ２の中空糸膜を用いた定圧クロスフロー試験により測定した。まず、ＮＭＰを９．９ｍｌ／分の流量で、中空糸膜に通液した。さらに中空糸膜の入口付近に設けた圧力計と中空糸膜の出口付近に設けた調圧用レギュレーターにより操作圧を１ｂａｒ又は４ｂａｒに設定した。このとき、中空糸膜の出口から排出される、ろ液の透過速度を測定することで、単位時間（ｈ）、単位膜面積（ｍ２）、単位圧力（ｂａｒ）あたりのＮＭＰ透過速度（Ｌ／ｍ２／ｈｒ／ｂａｒ（ＬＭＨ／ｂａｒ））を算出した。
［分画分子量］
　限外ろ過膜の分画分子量は、表面積０．０１２ｍ２の中空糸膜を用いた定圧クロスフロー試験により測定した。すなわち、分子量３Ｋ、８Ｋ、１２Ｋ、３５Ｋ、１００Ｋ、及び５００ＫのＰＥＧを、それぞれ０．１％にてＮＭＰに混合溶解し、これをまず、９．９ｍｌ／分の流量で、中空糸膜に通液した。さらに中空糸膜の入口付近に設けた圧力計と中空糸膜の出口付近に設けた調圧用レギュレーターにより、操作圧を１ｂａｒに設定することにより、定圧条件で試験を実施した。通液開始の６時間後に、供給液とろ液とを採取した。
　採取した供給液とろ液とを、それぞれゲルろ過クロマトグラフィー（ＧＰＣ）カラムと示差屈折（ＲＩ）検出器を用いた液体クロマトグラフィーにより分析した。分子量（ＰＥＧ検量線から算出）に対するＲＩピーク強度のクロマトグラムから供給液強度（Ｉｆｅｅｄ）とろ液強度（Ｉｆｉｌｌ）を求め、下記の数式３からＰＥＧの阻止率を算出することにより、限外ろ過膜の分画曲線をプロットし、９０％阻止率となる分子量を分画分子量として決定した。
　　数式３：阻止率（％）＝（１－Ｉｆｉｌｌ／Ｉｆｅｅｄ）×１００
［不純物含有液体の透過速度及び不純物含有液体中の不純物の阻止率］
　不純物含有液体として、分子量５０ｋＤ又は７００ｋＤである酢酸セルロースを１０００ｐ～６４００ｐｐｍ含有する、ＥｍｉｍＯＡｃ／ＮＭＰ混合溶媒（重量比５０：５０）を用いた。酢酸セルロースの分子量及び含有量は、ゲルろ過クロマトグラフィー（ＧＰＣ）により決定した。
　不純物含有液体の透過速度及び該溶媒中の不純物の阻止率は、表面積０．０１２ｍ２の中空糸膜を用いた定圧クロスフロー試験により測定した。すなわち、該溶媒をまず、９．９ｍｌ／分の流量で、中空糸膜に通液した。さらに中空糸膜の入口付近に設けた圧力計と中空糸膜の出口付近に設けた調圧用レギュレーターにより、操作圧を１ｂａｒ又は４ｂａｒに設定することにより、定圧条件で試験を実施した。通液開始の２４時間後に、ろ液の流量を測定した。また、供給液とろ液とを採取した。
　計測したろ液の流量から不純物含有液体の透過速度を求めた。
　また、採取した供給液及びろ液について、それぞれ、フェノール硫酸法による糖分析定量により、酢酸セルロースの含有量を定量した。定量は、溶媒による測定値への影響を勘案し、同一溶媒系で作成した検量線を用いて実施した。定量された、供給液中の酢酸セルロースの含有量（Ｃｆｅｅｄ）、ろ液中の酢酸セルロースの含有量（Ｃｆｉｌｌ）に基づき、下記の数式４により不純物含有液体中の不純物の阻止率を算出した。
　　数式４：　阻止率（％）＝（１－Ｃｆｉｌｌ／Ｃｆｅｅｄ）×１００
　以上の測定の結果が表３に示される。
　表３に示されるように、実施例の限外ろ過膜は、優れたＮＭＰ透過速度、分画分子量、並びに不純物を含む溶媒の透過速度及び該溶媒中の不純物の阻止率を示した。
　一方、比較例の限外ろ過膜は、溶媒に対する耐性がなく、不純物を含む溶媒から不純物を効果的に除去することができなかった。
　この結果は、本発明に係る限外ろ過膜が、不純物を含む溶媒から不純物を効果的に除去できることを示す。
［限外ろ過膜の耐溶媒性］
　限外ろ過膜の溶媒に対する耐性を、上記の実施例８の限外ろ過膜を用い、これをＥｍｉｍＯＡｃ／ＮＭＰ混合溶媒（重量比５０：５０）に、室温で浸漬することにより、検討した。
　中空糸膜を、浸漬の直後、１月後、２月後、及び３月後に取出し、強度の保持率を評価した。すなわち、中空糸膜を混合溶媒から取出した後、ろ紙にて表面の混合溶媒を軽く除く一方、混合溶媒が含浸された状態の中空糸膜を試料として、引張試験の強伸度を、卓上試験機を用いて測定した。
　測定条件は、試料長５ｃｍ、クロスヘッドスピードを１０ｃｍ／分であり、破断強度、破断伸度、及び初期勾配から弾性率を見積もった。図２にその結果が示される。
　図２に示されるように、中空糸膜は、３月間の混合溶媒浸漬にわたり、（１）破断強度の経時変化、（２）破断伸度の経時変化、及び（３）弾性率の経時変化について、有意な変化を示さなかった。
　この結果は、本発明に係る限外ろ過膜が、イオン液体及びセルロースエステルを含む液体に対し耐性を有し、したがって、該液体からイオン液体を含む液体を、効果的に回収できることを示す。
　本開示のイオン液体及び着色成分を含む着色液体から、イオン液体を含む液体を回収するための方法は、原料高分子として広く用いられるセルロースエステルの製造において、好適に用いることが可能であり、産業上の利用可能性を有している。

Claims (15)

  1. 　イオン液体及び着色成分を含む着色液体から、イオン液体を含む液体を回収するための方法であって、前記着色液体をナノろ過膜又は逆浸透膜に供することにより、イオン液体を含む前記液体と、前記着色成分とを分離することを含む、方法。
  2. 　前記ナノろ過膜又は前記逆浸透膜の塩阻止率が、９５％以上であり、
    　前記塩阻止率が、
    　数式１：塩阻止率（％）＝（１－Ｃｆｉｌｌ／Ｃｆｅｅｄ）×１００
    ［数式１において、Ｃｆｅｅｄは、前記ナノろ過膜又は前記逆浸透膜にＮａＣｌ水溶液を通液する際に、前記ナノろ過膜又は前記逆浸透膜に供給されるＮａＣｌ水溶液中のＮａＣｌ濃度であり、Ｃｆｉｌｌは、前記ナノろ過膜又は前記逆浸透膜にＮａＣｌ水溶液を通液した際に、前記ナノろ過膜又は前記逆浸透膜から排出されるＮａＣｌ水溶液中のＮａＣｌ濃度である］
    により算出される、
    請求項１に記載の方法。
  3. 　前記ナノろ過膜又は前記逆浸透膜の透水係数が、１．０Ｌ／ｍ２／ｈ／ｂａｒ未満であり、ここで、前記透水係数は、１６００ｐｐｍ　ＮａＣｌ水溶液が前記ナノろ過膜又は前記逆浸透膜を透過する際の、単位時間（ｈ）、単位膜面積（ｍ２）、単位圧力（ｂａｒ）あたりの透過速度として定義される、請求項１に記載の方法。
  4. 　前記着色液体が、前記着色液体の総重量に対し、３０重量％以上のメタノールを含む、請求項１に記載の方法。
  5. 　前記ナノろ過膜又は前記逆浸透膜の塩阻止率が、８５％以上であり、
    　前記塩阻止率が、
    　数式１：塩阻止率（％）＝（１－Ｃｆｉｌｌ／Ｃｆｅｅｄ）×１００
    ［数式１において、Ｃｆｅｅｄは、前記ナノろ過膜又は前記逆浸透膜にＮａＣｌ水溶液を通液した際に、前記ナノろ過膜又は前記逆浸透膜に供給されるＮａＣｌ水溶液中のＮａＣｌ濃度であり、Ｃｆｉｌｌは、前記ナノろ過膜又は前記逆浸透膜にＮａＣｌ水溶液を通液した際に、前記ナノろ過膜又は前記逆浸透膜から排出されるＮａＣｌ水溶液中のＮａＣｌ濃度である］
    により算出される、請求項４に記載の方法。
  6. 　前記ナノろ過膜又は前記逆浸透膜の透水係数が、８．０Ｌ／ｍ２／ｈ／ｂａｒ未満であり、ここで、前記透水係数は、１６００ｐｐｍ　ＮａＣｌ水溶液が前記ナノろ過膜又は前記逆浸透膜を透過する際の、単位時間（ｈ）、単位膜面積（ｍ２）、単位圧力（ｂａｒ）あたりの透過速度として定義される、請求項４に記載の方法。
  7. 　前記ナノろ過膜又は前記逆浸透膜が、ポリアミド樹脂を含む活性層を含む、請求項１に記載の方法。
  8. 　前記イオン液体が、カチオン成分として、イミダゾリウムカチオン又は四級アンモニウムカチオンを含み、アニオン成分としてカルボン酸アニオンを含む、請求項１に記載の方法。
  9. 　前記イオン液体が、１－エチル－３－メチルイミダゾリウムアセテート（ＥｍｉｍＯＡｃ）、１－エチル－２，３－ジメチルイミダゾリウムアセテート（ＥＤｍｉｍＯＡｃ）、１－ブチル－３－メチルイミダゾリウムアセテート、１－ヘキシル－３－メチルイミダゾリウムアセテート、テトラブチルアンモニウムアセテート、及びこれらの組合せからなる群から選択される、請求項１に記載の方法。
  10. 　前記ナノろ過膜又は前記逆浸透膜による着色除去率が、３０％以上である、請求項１に記載の方法。
  11. 　前記着色液体が、共溶媒をさらに含む、請求項１に記載の方法。
  12. 　前記共溶媒が、高沸点極性溶媒である、請求項１１に記載の方法。
  13. 　前記高沸点極性溶媒がジメチルスルホキシド（ＤＭＳＯ）、スルホラン、Ｎ，Ｎ－ジメチルホルムアミド（ＤＭＦ）、Ｎ－メチル－２－ピロリドン（ＮＭＰ）、及びこれらの組合せからなる群から選択される、請求項１２に記載の方法。
  14. 　セルロースエステルの製造方法であって、
    　セルロースをイオン液体及び共溶媒を含む第１の液体に溶解することにより、第２の液体を得る第１工程と、
    　前記第２の液体に有機酸無水物を添加することにより、セルロースと有機酸無水物とを反応させ、セルロースエステルを生成させる第２工程と、
    　前記第２工程に続き、前記第２の液体にさらに貧溶媒を添加することにより、セルロースエステルを析出させる第３工程と、
    　前記第３工程に続き、セルロースエステルを含む固相と、イオン液体、共溶媒、前記有機酸無水物由来の有機酸、及び貧溶媒を含む第３の液体からなる液相とを分離し、前記固相からセルロースエステルを回収し、前記液相から前記第３の液体を回収する第４工程と、
    　前記第３の液体を蒸留することにより、前記第３の液体から前記有機酸及び／又は前記貧溶媒を除去し、イオン液体、共溶媒、及び蒸留により生じた着色成分を含む第４の液体を得る第５工程と、
    　前記第４の液体をナノろ過膜又は逆浸透膜に供することにより、イオン液体を含む第５の液体と、着色成分とを分離し、前記第５の液体を回収する第６工程と
    を含み、
    　前記第５の液体の全部又は一部を前記第１の液体の全部又は一部として再使用することにより、前記第１工程から前記第６工程を繰り返すことができる、
    製造方法。
  15. 　前記第６工程に先立ち、前記第４の液体に、前記第４の液体の総重量に対して３０重量％以上となるように、メタノールを添加することを含む、請求項１４に記載の製造方法。
PCT/JP2025/007076 2024-03-01 2025-02-28 イオン液体中の着色成分の除去 Pending WO2025183148A1 (ja)