WO2024122812A1 - 트라이베헤닌 고함유 매트 타입 입술용 화장료 조성물 - Google Patents
트라이베헤닌 고함유 매트 타입 입술용 화장료 조성물 Download PDFInfo
- Publication number
- WO2024122812A1 WO2024122812A1 PCT/KR2023/013600 KR2023013600W WO2024122812A1 WO 2024122812 A1 WO2024122812 A1 WO 2024122812A1 KR 2023013600 W KR2023013600 W KR 2023013600W WO 2024122812 A1 WO2024122812 A1 WO 2024122812A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- weight
- tribehenin
- composition
- lips
- cosmetic composition
- Prior art date
Abstract
본 개시는 트라이베헤닌을 고함량으로 포함하는 매트 타입의 입술용 화장료 조성물에 관한 것이다. 본 개시의 입술용 화장료 조성물은 고함량의 트라이베헤닌을 포함하여 매트한 질감을 나타내면서도 경시에 따른 경도 안정화 효과가 현저하게 우수하다.
Description
본 출원은 2022년 12월 8일 출원된 대한민국출원 제10-2022-0170794호에 기초한 우선권을 주장하며, 해당 출원의 명세서 및 도면에 개시된 모든 내용은 본 출원에 원용된다.
본 개시는 트라이베헤닌을 고함량으로 포함하는 매트 타입의 입술용 화장료 조성물에 관한 것이다.
입술용 화장품으로서 매트 타입의 제형은 광이 나지 않으면서 자연스러운 발색이 가능한 장점이 있다. 종래에는 입술용 화장품에 매트한 질감을 부여하기 위해, 파우더 함량을 높게 배합하거나 또는 트라이베헤닌과 같은 장쇄 지방산을 이용하였다. 매트한 화장 효과를 구현하기 위하여 트라이베헤닌을 고함량 함유한 기존의 유분산 매트 제형의 입술용 화장료 조성물의 경우, 시간이 흐름에 따라 왁스 결정화도가 증가하고 경도가 상승하여 초기의 사용감이 유지되지 않는 단점이 있다. 반면, 트라이베헤닌을 함유하지 않고 매트 제형의 입술용 화장료를 제조할 경우, 고온에서 흐름성이 낮아 생산성이 저하되는 문제가 있다.
국내공개특허 제10-2008-0105569호에는 오일 겔화제로 트라이베헤닌을 포함하는 유중수형 유화메이크업 화장료 조성물이 기재되어 있으나, 트리베헤닌의 함량이 4 중량% 이하로 소량 포함되며, 매트한 화장 효과를 나타내는 제형이 아니고, 경도 안정성의 개선에 대해서는 기재되어 있지 않다. 또한, 일본공개특허 제2021-098667호에는 왁스 및 분체를 포함하는 겔형 유성 화장료가 기재되어 있으나, 트라이베헤닌에 해당하는 왁스를 2 중량% 미만으로 제한하고 있으며, 경도 안정성의 개선에 대해서는 기재되어 있지 않다. 따라서, 입술용 화장품에 매트한 질감을 부여하기 위해 트라이베헤닌을 충분한 함량으로 포함하면서, 이에 따른 경시 경도 상승 문제를 해결할 수 있는 새로운 입술용 화장료 조성물의 개발이 필요한 실정이다.
본 개시가 해결하고자 하는 과제는 고함량의 트라이베헤닌을 포함함으로써 매트한 질감을 나타내면서도, 경시에 따른 경도 상승 문제가 발생하지 않는 입술용 화장료 조성물을 제공하는 것이다.
상기 과제를 해결하기 위하여, 본 발명자들은 매트 제형의 입술용 화장료 조성물을 제조하기 위해 고함량의 트라이베헤닌을 포함하는 경우 경시에 따른 경도 상승 문제를 해결하기 위해 예의 연구 노력한 결과, 상기 조성물에 카올린을 추가하는 경우 경시 경도 안정화 효과가 현저하게 상승하는 놀라운 발견을 하여 본 발명을 완성하게 되었다.
본 개시는 트라이베헤닌 및 카올린을 포함하며, 상기 트라이베헤닌을 조성물 총 중량 대비 5 중량% 이상 포함하는 입술용 화장료 조성물을 제공한다. 또한, 본 개시는 트라이베헤닌 및 탤크를 포함하며, 상기 트라이베헤닌을 조성물 총 중량 대비 5 중량% 이상 포함하는 입술용 화장료 조성물을 제공한다. 본 개시의 한 측면에서, 상기 입술용 화장료 조성물은 매트 제형이다. 상기 입술용 화장료 조성물은 트라이베헤닌을 5 중량% 이상의 고함량으로 포함함으로써 매트한 질감을 나타내면서 경시에 따른 경도 상승 문제가 발생하지 않는다.
본 개시의 한 측면에서, 상기 입술용 화장료 조성물은 액상이다. 본 개시의 한 측면에서, 상기 입술용 화장료 조성물은 유분산 제형, 실리콘중수(W/S), 또는 유중수(W/O) 등일 수 있으며, 이를 통해 트라이베헤닌 및 엘라스토머 등의 유상 성분을 조성물 내에 안정하게 분산시켜 경시 경도 안정화 효과를 나타낼 수 있다.
본 개시의 한 측면에서, 상기 트라이베헤닌은 조성물 총 중량 대비 5 중량% 이상, 바람직하게 5 중량% 내지 20 중량%, 보다 바람직하게 5 중량% 내지 15 중량%, 가장 바람직하게 5 중량% 내지 12 중량%로 포함될 수 있다. 상기 트라이베헤닌이 조성물 총 중량 대비 5 중량% 미만으로 포함되는 경우, 입술용 화장료 조성물 사용시 충분한 경도를 형성하지 못하여 사용시 흘러내리거나 매트한 질감을 충분한 나타내지 못한다. 또한, 상기 트라이베헤닌이 20 중량% 초과하여 포함될 경우, 경도가 지나치게 상승하여 제조 효율성 및 사용감이 감소한다.
본 개시의 한 측면에서, 상기 카올린은 조성물 총 중량 대비 10 중량% 미만, 바람직하게 0.1 중량% 내지 7 중량%, 보다 바람직하게 0.5 중량% 내지 5 중량%로 포함될 수 있다. 상기 카올린이 조성물 총 중량 대비 10 중량% 이상으로 포함되는 경우, 경도가 지나치게 상승하여 제조 효율성 및 사용감이 감소한다. 또한, 상기 카올린이 0.1 중량% 미만으로 포함될 경우, 경시 경도 안정화 효과가 나타나지 않는다.
본 개시의 한 측면에서, 상기 탤크는 조성물 총 중량 대비 10 중량% 미만, 바람직하게 0.1 중량% 내지 7 중량%, 보다 바람직하게 0.5 중량% 내지 5 중량%로 포함될 수 있다. 상기 탤크가 조성물 총 중량 대비 10 중량% 이상으로 포함되는 경우, 경도가 지나치게 상승하여 제조 효율성 및 사용감이 감소한다. 또한, 상기 탤크가 0.1 중량% 미만으로 포함될 경우, 경시 경도 안정화 효과가 나타나지 않는다.
본 개시의 한 측면에서, 상기 트라이베헤닌 및 카올린의 중량비는 1:0.01 내지 3, 바람직하게 1:0.05 내지 2, 더욱 바람직하게 1:0.1 내지 1(트라이베헤닌:카올린)일 수 있다. 상기 두 성분이 상기 중량비 범위로 조성물에 포함될 경우, 입술용 화장료 조성물의 경도가 적절하게 형성되고 매트한 질감을 나타낼 뿐만 아니라, 경시 경도 안정성이 현저하게 우수하다.
본 개시의 한 측면에서, 상기 입술용 화장료 조성물은 추가로 엘라스토머를 포함한다. 상기 엘라스토머는 바람직하게 유기폴리실록산 엘라스토머일 수 있으며, 실리콘 성분으로 이루어진(-Si-O-Si- 결합을 갖는 화합물) 점탄성을 갖는 열가소성의 고분자 탄성 물질일 수 있다. 상기 엘라스토머는 본 발명이 속하는 기술분야에서 상업적으로 판매되거나 알려진 제조 방법에 따라 쉽게 얻을 수 있는 통상적인 엘라스토머일 수 있다. 상기 엘라스토머는 예를 들어 디메치콘, 디메치콘 크로스폴리머, 디메치콘/비닐디메치콘크로스폴리머, 디메치콘 코폴리올 또는 이들의 혼합물, 또는 이들의 코폴리머 등을 포함할 수 있으나, 이에 한정되지 않는다.
상기 엘라스토머는 조성물 총 중량 대비 40 내지 70 중량%, 바람직하게 45 내지 65 중량%, 더욱 바람직하게 50 내지 60 중량%이다. 상기 엘라스토머의 함량이 70 중량%를 초과하는 경우 점탄성이 과도하게 증가되어 제조 효율성이 감소하며, 40 중량% 미만일 경우에는 매트한 화장 효과를 나타내기 어렵다.
본 개시의 한 측면에서, 상기 입술용 화장료 조성물은 분체를 포함하며, 상기 분체는 카올린, 탤크, 또는 이들의 혼합물을 포함한다. 상기 분체는 카올린 또는 탤크 외에 실리카실릴레이트, 실리카디메틸실릴레이트, 실리카, 비닐디메티콘/메티콘실세스퀴옥세인크로스폴리머, 나일론-12, 폴리메틸메타크릴레이트, 에이치디아이/트라이메틸올헥실락톤크로스폴리머 등을 포함할 수 있으나, 이에 한정되지 않는다.
상기 분체는 조성물 총 중량 대비 0.1 내지 20 중량%, 바람직하게 0.5 내지 15 중량%, 더욱 바람직하게 1 내지 10 중량%로 포함될 수 있다. 상기 분체가 조성물 총 중량 대비 0.1 중량% 미만으로 포함되는 경우에는 매트한 화장 효과를 나타내기 어려우며, 20 중량% 초과하여 포함되는 경우에는 제조 효율성이 감소된다.
본 개시의 한 측면에서, 상기 입술용 화장료 조성물에서 분체 및 엘라스토머의 총 함량은 조성물 총 중량 대비 80 중량% 이하, 바람직하게 70 중량% 이하이다. 상기 분체 및 엘라스토머의 총 함량이 80 중량%를 초과하는 경우 제조 효율성이 감소된다.
본 개시의 한 측면에서, 상기 입술용 화장료 조성물은 트라이베헤닌 외의 왁스를 실질적으로 포함하지 않는다. 상기 입술용 화장료 조성물은 트라이베헤닌 외의 왁스를 조성물 총 중량 대비 3 중량% 미만, 바람직하게 1 중량% 미만, 더욱 바람직하게 0.1 중량% 미만으로 포함하거나, 또는 전혀 포함하지 않을 수 있다. 이를 통해 상기 입술용 화장료 조성물은 사용시 매트한 질감을 나타냄과 함께 적절한 경도를 형성하여 사용성 및 제조 효율성이 우수하다. 본 개시의 한 측면에서, 트라이베헤닌 외의 왁스를 포함할 경우 조성물의 경도가 지나치게 높아짐에 따라 경시 경도 변화량도 현저하게 증가할 수 있다. 본 개시에 따른 입술용 화장료 조성물은 트라이베헤닌 외의 왁스를 실질적으로 포함하지 않음으로써 경시 경도 안정성을 증가시킬 수 있다.
본 개시의 한 측면에서, 상기 입술용 화장료 조성물의 경도는 30 내지 1500, 바람직하게 40 내지 1200, 더욱 바람직하게 50 내지 1000일 수 있다. 상기 경도는 조성물의 제조 후 7일 이상 경과된 이후의 경도값일 수 있다. 상기 경도의 측정 조건은 FUDOH RHEOMETER 이용, Adapter No.9, 15pi, Range: 500, S.Adj.: 25mm, T Speed: 2cm/min이다. 상기 경도가 30 미만일 경우에는 매트 효과가 현저하게 감소하며, 750 초과일 경우에는 발림성이 현저하게 감소할 수 있다.
본 개시의 한 측면에서, 본 발명에 따른 조성물에 트라이베헤닌의 함량을 증가시킬 경우, 더욱 우수한 매트 질감이 구현 가능하며 경도가 증가되더라도 발림성 측면에서 허용가능한 경도로 얻어질 수 있다. 트라이베헤닌과 함께 카올린 또는 탈크를 특정한 함량으로 추가 배합시킬 경우 트라이베헤닌만을 포함시키는 경우에 비하여 경시 경도 안정성을 현저하게 개선할 수 있어, 제조 과정에서 제품의 품질 관리를 더욱 용이하게 할 수 있다.
본 개시의 한 측면에서, 상기 입술용 화장료 조성물의 광택도는 1 내지 60, 바람직하게 1 내지 40, 더욱 바람직하게 1 내지 20일 수 있다. 상기 광택도의 측정 조건은 Glossmeter를 이용, 측정 각도 75, 시료 두께 120μm이다. 본 개시의 입술용 화장료 조성물은 상기 광택도 범위를 나타냄으로써 매트한 화장 효과를 구현할 수 있다.
본 개시의 한 측면에서, 상기 입술용 화장료 조성물은 오일 성분을 포함할 수 있으며, 상기 오일 성분은 휘발성 오일, 비휘발성 오일, 또는 이들의 혼합물일 수 있다. 상기 휘발성 오일은 이소도데칸, 이소헥사데칸, C7-8이소파라핀, C8-9이소파라핀, C10-11이소파라핀, C10-13이소파라핀, C11-12이소파라핀, C11-13이소파라핀, C13-14이소파라핀, 메칠트리메치콘, 카프릴릴메치콘, 사이클로메치콘, 사이클로테트라실록산, 사이클로펜타실록산 및 사이클로헥사실록산 등으로 이루어진 군으로부터 선택된 어느 하나 이상을 포함할 수 있으나, 이에 한정되는 것은 아니다. 상기 비휘발성 오일은 카프릴릭/카프릭트리글리세라이드, 트리에칠헥사노인, 디이소스테아릴말레이트, 트리데실트리멜리테이트, 펜타에리스리틸테트라이소스테아레이트, 트리이소스테아린, 디글리세릴세바케이트/이소팔미테이트, 피토스테릴/이소스테아릴/세틸/스테아릴/베헤닐다이머디리놀리에이트, 디펜타에리스리틸헥사하이드록시스테아레이트/헥사스테아레이트/헥사로지네이트, 피토스테릴/이소스테아릴/세틸/스테아릴/베헤닐다이머디리놀리에이트, 하이드로제네이티드캐스터오일이소스테아레이트, 디메치콘크로스폴리머, 디메치콘/비닐디메치콘크로스폴리머, 피이지-12디메치콘/피피지-20크로스폴리머 등으로 이루어진 군으로부터 선택된 어느 하나 이상을 포함할 수 있으나, 이에 한정되는 것은 아니다.
본 개시의 한 측면에서, 입술용 화장료 조성물은 피부에 도포될 수 있는 립글로스 또는 립크림 등의 제형으로 제조될 수 있다. 본 개시에 따른 입술용 화장료 조성물은 상기 성분들 외에 소포제, 왁스, 점증제, 분체계 점증제, 산화방지제, 피부연화제, 보습제, 진정제, 윤활제, 방부제, 보습제, 자외선흡수제, 색소 및 향료 등으로 이루어진 군에서 선택된 하나 이상의 첨가제를 추가로 포함할 수 있다.
본 개시의 한 측면에서, 입술용 화장료 조성물은 조성물 총 중량 대비 트라이베헤닌 5 중량% 이상, 카올린 10 중량% 미만, 엘라스토머 40 내지 70 중량%, 및 분체 0.1 내지 20 중량%를 포함하며, 상기 엘라스토머 및 분체의 총 함량은 조성물 총 중량 대비 80 중량% 이하인 매트 제형이다. 상기 각 성분을 특정한 함량으로 포함하는 입술 화장료 조성물은 매트한 화장 효과를 나타냄과 동시에 경시 경도 안정성이 현저하게 우수하다
또한, 본 개시는 상기 입술용 화장료 조성물을 입술에 도포하는 단계를 포함하는 입술 화장 방법을 제공한다. 또한, 본 개시는 트라이베헤닌 및 카올린을 포함하며, 상기 트라이베헤닌을 조성물 총 중량 대비 5 중량% 이상 포함하는 조성물의 입술 화장 용도를 제공한다.
본 개시에 기재된 모든 성분은, 바람직하게는, 한국, 중국, 미국, 유럽, 일본 등의 관련 법규, 규범 (예를 들어, 화장품 안전 기준 등에 관한 규정(한국), 화장품 안전 기술 규범(중국) 등에서 규정한 최대사용치를 초과하지 않는다. 즉, 바람직하게, 본 개시에 따른 화장료 조성물은 각국의 관련 법규, 규범에서 허용되는 함량 한도로 본 개시에 따른 성분들을 포함한다.
본 개시의 입술용 화장료 조성물은 고함량의 트라이베헤닌을 포함하여 매트한 질감을 나타내면서도 경시에 따른 경도 안정화 효과가 현저하게 우수하다.
도 1은 실험예 1에서 트라이베헤닌의 함량에 따른 입술용 화장료 조성물의 경시 경도 변화를 나타낸 그래프이다.
도 2는 실험예 1에서 입술용 화장료 조성물의 도포시 트라이베헤닌의 함량에 따른 광택도를 측정한 결과를 나타낸다.
도 3은 실험예 2에서 카올린의 추가 배합에 따른 입술용 화장료 조성물의 경시 경도 변화를 나타낸 그래프이다.
도 4는 실험예 2에서 입술용 화장료 조성물의 도포시 카올린의 추가 배합에 따른 광택도를 측정한 결과를 나타낸다.
도 5는 실험예 2에서 입술용 화장료 조성물에 카올린을 5 중량% 초과하여 포함하는 경우의 경시 경도 변화를 나타낸 그래프이다.
도 6은 실험예 3에서 분체의 종류에 따른 입술용 화장료 조성물의 경시 경도 변화를 나타낸 그래프이다.
도 7은 실험예 3에서 입술용 화장료 조성물의 도포시 분체의 종류에 따른 광택도를 측정한 결과를 나타낸다.
이하, 본 발명의 이해를 돕기 위하여 실시예 등을 들어 상세하게 설명하기로 한다. 그러나, 본 발명에 따른 실시예들은 여러 가지 다른 형태로 변형될 수 있으며, 본 발명의 범위가 하기 실시예들에 한정되는 것으로 해석되어서는 안 된다. 본 발명의 실시예들은 본 발명이 속한 분야에서 평균적인 지식을 가진 자에게 본 발명을 보다 완전하게 설명하기 위해 제공되는 것이다.
실험예 1: 트라이베헤닌의 함량에 따른 경도 변화 및 매트 효과 비교
① 하기 표 1에 기재된 조성에 따라, 트라이베헤닌과 오일류를 혼합한 후 70℃ 이상으로 가온하여 트라이베헤닌을 완전히 용해시켰다.
② 엘라스토머와 분체 원료를 투입 후 70℃ 이상에서 디스퍼믹서 또는 호모믹서를 이용하여 분산시켰다.
③ 색소를 투입하고 70℃ 이상에서 디스퍼믹스 또는 호모믹서를 이용하여 분산시켰다.
④ 탈포 후 70℃에서 100ml 바이알에 샘플링하고, 25℃ 항온조에서 1시간 보관한 이후 경도를 측정하였다.
* 측정조건: FUDOH RHEOMETER 이용, Adapter No.9, 15pi, Range: 500, S.Adj.: 25mm, T Speed: 2cm/min
| 배합성분 (중량%) | 비교예1 | 실시예1 | 실시예2 |
| 트라이베헤닌 | 3.00 | 7.00 | 11.00 |
| 다이아이소스테아릴말레이트 | to 100 | to 100 | to 100 |
| 폴리글리세릴-2트라이아이소스테아레이트 | 4.00 | 4.00 | 4.00 |
| 세틸피이지/피피지-10/1디메티콘 | 2.00 | 2.00 | 2.00 |
| 소르비탄아이소스테아레이트 | 1.00 | 1.00 | 1.00 |
| 페녹시에탄올 | 1.00 | 1.00 | 1.00 |
| 디메티콘, 디메티콘크로스폴리머 | 53.00 | 53.00 | 53.00 |
| 비닐디메티콘/메티콘실세스퀴옥세인크로스폴리머 | 3.00 | 3.00 | 3.00 |
| 카올린 | - | - | - |
| 색소 베이스 | 10.10 | 10.10 | 10.10 |
| TOTAL | 100.00 | 100.00 | 100.00 |
경시 경도 측정 결과를 하기 표 2 및 도 1에 나타내었다.
| 조건/days | 0 | 3 | 7 | 14 | 28 | 56 | |
| 경도 | 비교예 1 | 15 | 15 | 18 | 17 | 18 | 20 |
| 실시예 1 | 60 | 64 | 90 | 96 | 100 | 121 | |
| 실시예 2 | 84 | 190 | 256 | 215 | 260 | 293 | |
상기 측정 결과를 볼 때, 트라이베헤닌을 5 중량% 이상으로 포함하는 경우, 시간이 흐름에 따라 경도가 현저하게 상승하는 것을 확인하였다.
또한, 상기 비교예 및 실시예들에 대한 광택도를 측정한 후, 측정 결과를 하기 표 3 및 도 2에 나타내었다.
* 측정조건: Glossmeter 이용, 측정 각도 75°, 시료 두께 120μm
| 비교예 1 | 실시예 1 | 실시예 2 | |
| 광택도 | 78.4 | 13.7 | 4 |
상기 측정 결과를 볼 때, 트라이베헤닌을 5 중량% 이상으로 포함하는 경우, 광택도가 현저하게 감소하여 매트한 질감을 나타냄을 확인하였다.
실험예 2: 트라이베헤닌에 카올린 추가 배합시 경시 경도 안정성 평가
트라이베헤닌을 5 중량% 이상 함유할 때 카올린의 추가 배합에 의한 영향을 비교 평가하였다. 엘라스토머와 분체의 총 함량은 70 중량% 이내로 제한하였다.
① 하기 표 4의 조성에 따라 트라이베헤닌 및 오일류를 혼합하여 70℃ 이상으로 가온하여 트라이베헤닌을 완전히 용해시켰다.
② 엘라스토머와 분체 원료를 투입한 후 70℃ 이상에서 디스퍼믹스 또는 호모믹서를 이용하여 분산시켰다.
③ 색소를 투입한 후 70℃ 이상에서 디스퍼믹서 또는 호모믹서를 이용하여 분산시켰다.
④ 탈포 후 70℃에서 100 ml 바이알에 샘플링하여 25℃ 항온조에서 1시간 보관 후 경도를 측정하였다.
* 측정조건: FUDOH RHEOMETER이용, Adapter No.9, 15pi, Range: 500, S.Adj.: 25mm, T Speed: 2cm/min
| 배합성분 (중량%) | 비교예2 | 실시예3 | 실시예4 | 실시예5 | 실시예6 | 실시예7 | 실시예8 |
| 트라이베헤닌 | 8.00 | 8.00 | 8.00 | 8.00 | 8.00 | 8.00 | 8.00 |
| 다이아이소스테아릴말레이트 | to 100 | to 100 | to 100 | to 100 | to 100 | to 100 | to 100 |
| 폴리글리세릴-2트라이아이소스테아레이트 | 4.00 | 4.00 | 4.00 | 4.00 | 4.00 | 4.00 | 4.00 |
| 세틸피이지/피피지-10/1디메티콘 | 2.00 | 2.00 | 2.00 | 2.00 | 2.00 | 2.00 | 2.00 |
| 소르비탄아이소스테아레이트 | 1.00 | 1.00 | 1.00 | 1.00 | 1.00 | 1.00 | 1.00 |
| 페녹시에탄올 | 1.00 | 1.00 | 1.00 | 1.00 | 1.00 | 1.00 | 1.00 |
| 디메티콘, 디메티콘크로스폴리머 | 58.00 | 58.00 | 58.00 | 58.00 | 57.00 | 55.00 | 53.00 |
| 카올린 | 1.00 | 3.00 | 5.00 | 1.00 | 3.00 | 5.00 | |
| 색소베이스 | 10.00 | 10.00 | 10.00 | 10.00 | 10.00 | 10.00 | 10.00 |
| TOTAL | 100.00 | 100.00 | 100.00 | 100.00 | 100.00 | 100.00 | 100.00 |
상기 비교예 및 실시예들에 대한 경시 경도 안정성 실험 결과를 하기 표 5 내지 11 및 도 3에 나타내었다.
| 조건/days | 0 | 5 | 7 | 14 | 21 |
| 경도 | 53 | 87 | 93 | 116 | 98 |
| 변화수치 | 34 | 40 | 63 | 45 | |
| 변화% | 64.15 | 75.47 | 118.87 | 84.91 | |
| 변화절대값 | 0 | 64.15 | 75.47 | 118.87 | 84.91 |
| 조건/days | 0 | 5 | 7 | 14 | 21 |
| 경도 | 270 | 299 | 293 | 287 | 254 |
| 변화수치 | 29 | 23 | 17 | -16 | |
| 변화% | 10.74 | 8.52 | 6.30 | -5.93 | |
| 변화절대값 | 0 | 10.74 | 8.52 | 6.30 | 5.93 |
| 조건/days | 0 | 5 | 7 | 14 | 21 |
| 경도 | 440 | 400 | 345 | 360 | 328 |
| 변화수치 | -40 | -95 | -80 | -112 | |
| 변화% | -9.09 | -21.59 | -18.18 | -25.45 | |
| 변화절대값 | 0 | 9.09 | 21.59 | 18.18 | 25.45 |
| 조건/days | 0 | 5 | 7 | 14 | 21 |
| 경도 | 560 | 480 | 430 | 371 | 335 |
| 변화수치 | -80 | -130 | -189 | -225 | |
| 변화% | -14.29 | -23.21 | -33.75 | -40.18 | |
| 변화절대값 | 0 | 14.29 | 23.21 | 33.75 | 40.18 |
| 조건/days | 0 | 5 | 7 | 14 | 21 |
| 경도 | 270 | 291 | 289 | 256 | 278 |
| 변화수치 | 21 | 19 | -14 | 8 | |
| 변화% | 7.78 | 7.04 | -5.19 | 2.96 | |
| 변화절대값 | 0 | 7.78 | 7.04 | 5.19 | 2.96 |
| 조건/days | 0 | 5 | 7 | 14 | 21 |
| 경도 | 410 | 379 | 378 | 335 | 352 |
| 변화수치 | -31 | -32 | -75 | -58 | |
| 변화% | -7.56 | -7.80 | -18.29 | -14.15 | |
| 변화절대값 | 0 | 7.56 | 7.80 | 18.29 | 14.15 |
| 조건/days | 0 | 5 | 7 | 14 | 21 |
| 경도 | 530 | 460 | 355 | 321 | 337 |
| 변화수치 | -70 | -175 | -209 | -193 | |
| 변화% | -13.21 | -33.02 | -39.43 | -36.42 | |
| 변화절대값 | 0 | 13.21 | 33.02 | 39.43 | 36.42 |
상기 비교예 2와 같이 카올린을 포함하지 않는 경우, 시간의 흐름에 따른 경도 변화량이 현저하게 증가함을 확인하였다. 반면, 실시예 3 내지 8과 같이 카올린을 5 중량% 이하로 포함하는 경우, 경시 경도 안정성이 현저하게 상승함을 확인하였다.
또한, 상기 실험예 1과 동일한 방법으로 상기 비교예 2 및 실시예 3 내지 8의 광택도를 측정하여, 그 결과를 하기 표 12 및 도 4에 나타내었다.
| 비교예2 | 실시예3 | 실시예4 | 실시예5 | 실시예6 | 실시예7 | 실시예8 |
| 10.6 | 8.7 | 5.1 | 4.6 | 7.4 | 6.9 | 4.8 |
상기 실시예 3 내지 8과 같이, 트라이베헤닌과 함께 5 중량% 이하의 카올린을 포함하는 경우 광택도가 감소하여 매트한 질감을 나타내었다.
추가적으로, 아래 표 13과 같이 카올린을 5 중량% 초과하여 고함량으로 포함하는 비교예 3 및 4를 제조하여, 경시 경도 안정성을 평가한 후, 그 결과를 하기 표 14 및 도 5에 나타내었다.
| 원료명 | 실시예 9 | 비교예 3 | 비교예 4 |
| 트라이베헤닌 | 9.00 | 9.00 | 9.00 |
| 다이아이소스테아릴말레이트 | to 100 | to 100 | to 100 |
| 폴리글리세릴-2트라이아이소스테아레이트 | 4.00 | 4.00 | 4.00 |
| 세틸피이지/피피지-10/1디메티콘 | 2.00 | 2.00 | 2.00 |
| 소르비탄아이소스테아레이트 | 1.00 | 1.00 | 1.00 |
| 페녹시에탄올 | 1.00 | 1.00 | 1.00 |
| 디메티콘, 디메티콘크로스폴리머 | 53.00 | 48.00 | 43.00 |
| 비닐디메티콘/메티콘실세스퀴옥세인크로스폴리머 | 3.00 | 3.00 | 3.00 |
| 카올린 | 5.00 | 10.00 | 15.00 |
| 색소 베이스 | 10.10 | 10.10 | 10.10 |
| TOTAL | 100.00 | 100.00 | 100.00 |
| 조건/days | 0 | 3 | 7 | 14 | 28 | |
| 경도 | 실시예 9 | 1040 | 850 | 880 | 740 | 770 |
| 비교예 3 | 1570 | 940 | 990 | 750 | 690 | |
| 비교예 4 | 2030 | 1330 | 1280 | 870 | 720 | |
카올린을 5 중량% 포함하는 실시예 9에서는 경시 경도 변화량이 크지 않았으나, 상기 비교예 3 및 4와 같이 카올린을 10 중량% 이상으로 포함하는 경우 경시 경도 변화량이 현저하게 상승하는 것을 확인하였다.
실험예 3: 분체 종류에 따른 경시 경도 안정성 평가
카올린 이외의 다른 분체를 적용할 경우에도 경시 경도 안정화 효과가 있는지 확인하였다. 카올린 외 분체의 함량은 3 중량%로 설정하였으며, 추가로 카올린을 1 중량% 적용할 경우 경시 경도 변화에 영향이 있는지 확인하였다.
① 하기 표 15의 조성에 따라 트라이베헤닌 및 오일류를 혼합하여 70℃ 이상으로 가온하여 트라이베헤닌을 완전히 용해시켰다.
② 엘라스토머와 분체 원료를 투입한 후 70℃ 이상에서 디스퍼믹스 또는 호모믹서를 이용하여 분산시켰다.
③ 색소를 투입한 후 70℃ 이상에서 디스퍼믹서 또는 호모믹서를 이용하여 분산시켰다.
④ 탈포 후 70℃에서 100 ml 바이알에 샘플링하여 25℃ 항온조에서 1시간 보관 후 경도를 측정하였다.
* 측정조건: FUDOH RHEOMETER이용, Adapter No.9, 15pi, Range: 500, S.Adj.: 25mm, T Speed: 2cm/min
| 배합성분 (중량%) | 비교예5 | 비교예6 | 비교예7 | 비교예8 | 실시예10 | 실시예11 | 실시예12 | 실시예13 | 실시예14 | 실시예15 |
| 트라이베헤닌 | 8.00 | 8.00 | 8.00 | 8.00 | 8.00 | 8.00 | 8.00 | 8.00 | 8.00 | 8.00 |
| 다이아이소스테아릴말레이트 | to 100 | to 100 | to 100 | to 100 | to 100 | to 100 | to 100 | to 100 | to 100 | to 100 |
| 폴리글리세릴-2트라이아이소스테아레이트 | 4.00 | 4.00 | 4.00 | 4.00 | 4.00 | 4.00 | 4.00 | 4.00 | 4.00 | 4.00 |
| 세틸피이지/피피지-10/1디메티콘 | 2.00 | 2.00 | 2.00 | 2.00 | 2.00 | 2.00 | 2.00 | 2.00 | 2.00 | 2.00 |
| 소르비탄아이소스테아레이트 | 1.00 | 1.00 | 1.00 | 1.00 | 1.00 | 1.00 | 1.00 | 1.00 | 1.00 | 1.00 |
| 페녹시에탄올 | 1.00 | 1.00 | 1.00 | 1.00 | 1.00 | 1.00 | 1.00 | 1.00 | 1.00 | 1.00 |
| 디메티콘, 디메티콘크로스폴리머 | 58.00 | 58.00 | 58.00 | 58.00 | 58.00 | 58.00 | 58.00 | 58.00 | 58.00 | 58.00 |
| 실리카 | 3.00 | - | - | - | - | 3.00 | - | - | - | - |
| 비닐디메티콘/메티콘실세스퀴옥세인크로스폴리머 | - | 3.00 | - | - | - | - | 3.00 | - | - | - |
| 폴리메틸실세스퀴옥세인 | - | - | 3.00 | - | - | - | - | 3.00 | - | - |
| 합성마이카 | - | - | - | 3.00 | - | - | - | - | 3.00 | - |
| 탤크 | - | - | - | - | 3.00 | - | - | - | - | 3.00 |
| 카올린 | - | - | - | - | - | 1.00 | 1.00 | 1.00 | 1.00 | 1.00 |
| 색소베이스 | 10.00 | 10.00 | 10.00 | 10.00 | 10.00 | 10.00 | 10.00 | 10.00 | 10.00 | 10.00 |
| TOTAL | 100.00 | 100.00 | 100.00 | 100.00 | 100.00 | 100.00 | 100.00 | 100.00 | 100.00 | 100.00 |
상기 비교예 및 실시예들에 대한 경시 경도 안정성 실험 결과를 하기 표 16 내지 25 및 도 6에 나타내었다.
| 조건/days | 0 | 3 | 7 | 14 |
| 경도 | 77 | 118 | 162 | 168 |
| 변화수치 | 41 | 85 | 91 | |
| 변화% | 53.25 | 110.39 | 118.18 | |
| 변화절대값 | 0 | 53.25 | 110.39 | 118.18 |
| 조건/days | 0 | 3 | 7 | 14 |
| 경도 | 97 | 147 | 199 | 193 |
| 변화수치 | 50 | 102 | 96 | |
| 변화% | 51.55 | 105.15 | 98.97 | |
| 변화절대값 | 0 | 51.55 | 105.15 | 98.97 |
| 조건/days | 0 | 3 | 7 | 14 |
| 경도 | 64 | 85 | 148 | 154 |
| 변화수치 | 21 | 84 | 90 | |
| 변화% | 32.81 | 131.25 | 140.63 | |
| 변화절대값 | 0 | 32.81 | 131.25 | 140.63 |
| 조건/days | 0 | 3 | 7 | 14 |
| 경도 | 61 | 72 | 129 | 137 |
| 변화수치 | 11 | 68 | 76 | |
| 변화% | 18.03 | 111.48 | 124.59 | |
| 변화절대값 | 0 | 18.03 | 111.48 | 124.59 |
| 조건/days | 0 | 3 | 7 | 14 |
| 경도 | 322 | 298 | 344 | 311 |
| 변화수치 | -24 | 22 | -11 | |
| 변화% | -7.45 | 6.83 | -3.42 | |
| 변화절대값 | 0 | 7.45 | 6.83 | 3.42 |
| 조건/days | 0 | 3 | 7 | 14 |
| 경도 | 402 | 343 | 398 | 444 |
| 변화수치 | -59 | -4 | 42 | |
| 변화% | -14.68 | -1.00 | 10.45 | |
| 변화절대값 | 0 | 14.68 | 1.00 | 10.45 |
| 조건/days | 0 | 3 | 7 | 14 |
| 경도 | 464 | 460 | 481 | 472 |
| 변화수치 | -4 | 17 | 8 | |
| 변화% | -0.86 | 3.66 | 1.72 | |
| 변화절대값 | 0 | 0.86 | 3.66 | 1.72 |
| 조건/days | 0 | 3 | 7 | 14 |
| 경도 | 464 | 349 | 413 | 407 |
| 변화수치 | -115 | -51 | -57 | |
| 변화% | -24.78 | -10.99 | -12.28 | |
| 변화절대값 | 0 | 24.78 | 10.99 | 12.28 |
| 조건/days | 0 | 3 | 7 | 14 |
| 경도 | 463 | 376 | 445 | 362 |
| 변화수치 | -87 | -18 | -101 | |
| 변화% | -18.79 | -3.89 | -21.81 | |
| 변화절대값 | 0 | 18.79 | 3.89 | 21.81 |
| 조건/days | 0 | 3 | 7 | 14 |
| 경도 | 470 | 352 | 420 | 369 |
| 변화수치 | -118 | -50 | -101 | |
| 변화% | -25.11 | -10.64 | -21.49 | |
| 변화절대값 | 0 | 25.11 | 10.64 | 21.49 |
상기 비교예 5 내지 8과 같이 카올린을 포함하지 않는 경우, 시간의 흐름에 따른 경도 변화량이 현저하게 증가함을 확인하였다. 반면, 실시예 11 내지 15와 같이 분체 성분으로 카올린을 1 중량% 포함하는 경우, 경시 경도 안정성이 현저하게 상승함을 확인하였다.
또한, 상기 실험예 1과 동일한 방법으로 상기 비교예 5 내지 8 및 실시예 10 내지 15의 광택도를 측정하여, 그 결과를 하기 표 26 및 도 7에 나타내었다.
| 비교예5 | 비교예6 | 비교예7 | 비교예8 | 실시예10 | 실시예11 | 실시예12 | 실시예13 | 실시예14 | 실시예15 |
| 3.3 | 3.7 | 3.5 | 5.4 | 3.8 | 2.2 | 1.8 | 2.3 | 2.1 | 2.6 |
비교예 5 내지 8과 같이 카올린 외의 분체를 포함하는 경우에 비해, 상기 실시예 10 내지 15와 같이 카올린 또는 탤크를 분체 성분으로 포함하는 경우 광택도가 감소하여 매트한 질감을 나타내었다.
Claims (11)
- 트라이베헤닌 및 카올린을 포함하며,상기 트라이베헤닌을 조성물 총 중량 대비 5 중량% 이상으로 포함하는 입술용 화장료 조성물.
- 트라이베헤닌 및 탤크를 포함하며,상기 트라이베헤닌을 조성물 총 중량 대비 5 중량% 이상으로 포함하는 입술용 화장료 조성물.
- 제1항 또는 제2항에 있어서, 상기 입술용 화장료 조성물은 매트 제형인 입술용 화장료 조성물.
- 제1항에 있어서, 상기 카올린은 조성물 총 중량 대비 10 중량% 미만으로 포함되는 입술용 화장료 조성물.
- 제1항에 있어서, 상기 트라이베헤닌 및 카올린의 중량비는 1:0.01 내지 3(트라이베헤닌:카올린)인 입술용 화장료 조성물.
- 제1항 또는 제2항에 있어서, 상기 조성물은 엘라스토머를 추가적으로 포함하는 입술용 화장료 조성물.
- 제6항에 있어서, 상기 조성물에서 분체 및 엘라스토머의 총 함량은 조성물 총 중량 대비 80 중량% 이하인 입술용 화장료 조성물.
- 제1항 또는 제2항에 있어서, 상기 조성물은 트라이베헤닌 외의 왁스를 실질적으로 포함하지 않는 입술용 화장료 조성물.
- 제1항 또는 제2항에 있어서, 상기 조성물은 FUDOH RHEOMETER 이용, Adapter No.9, 15pi, Range: 500, S.Adj.: 25mm, T Speed: 2cm/min의 경도 측정 조건에서, 경도가 30 내지 1500인 입술용 화장료 조성물.
- 제1항 또는 제2항에 있어서, 상기 조성물은 Glossmeter 이용, 측정 각도 75, 시료 두께 120μm의 광택도 측정 조건에서, 광택도가 1 내지 60인 입술용 화장료 조성물.
- 조성물 총 중량 대비 트라이베헤닌 5 중량% 이상, 카올린 10 중량% 미만, 엘라스토머 40 내지 70 중량%, 및 분체 0.1 내지 20 중량%를 포함하며, 상기 엘라스토머 및 분체의 총 함량은 조성물 총 중량 대비 80 중량% 이하인 매트 제형의 입술용 화장료 조성물.