WO2024100566A1 - Film barrière multicouche, procédé de fabrication d'un tel film, et matériau d'emballage à base de papier ou de carton comprenant un tel film - Google Patents

Film barrière multicouche, procédé de fabrication d'un tel film, et matériau d'emballage à base de papier ou de carton comprenant un tel film Download PDF

Info

Publication number
WO2024100566A1
WO2024100566A1 PCT/IB2023/061256 IB2023061256W WO2024100566A1 WO 2024100566 A1 WO2024100566 A1 WO 2024100566A1 IB 2023061256 W IB2023061256 W IB 2023061256W WO 2024100566 A1 WO2024100566 A1 WO 2024100566A1
Authority
WO
WIPO (PCT)
Prior art keywords
barrier film
layer
multilayer barrier
multilayer
furnish
Prior art date
Application number
PCT/IB2023/061256
Other languages
English (en)
Inventor
Anna Kauppi
Juha KORVENNIEMI
Isto Heiskanen
Kaj Backfolk
Original Assignee
Stora Enso Oyj
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Stora Enso Oyj filed Critical Stora Enso Oyj
Publication of WO2024100566A1 publication Critical patent/WO2024100566A1/fr

Abstract

La présente invention concerne un film barrière multicouche pour un matériau d'emballage en papier ou en carton, ledit film barrière comprenant une première couche comprenant une composition comprenant au moins 70 % en poids de cellulose hautement raffinée sur la base de la teneur totale en fibres de la première couche, une seconde couche comprenant une composition comprenant des fibres cellulosiques et moins de 50 % en poids de cellulose hautement raffinée sur la base de la teneur totale en fibres de la seconde couche et plus de 10 % en poids de charge, le film barrière multicouche ayant un indice de déchirure GM supérieur à 4,5. La présente invention concerne en outre un matériau d'emballage à base de papier et de carton comprenant un tel film barrière multicouche et des procédés de fabrication d'un tel film barrière multicouche.
PCT/IB2023/061256 2022-11-11 2023-11-08 Film barrière multicouche, procédé de fabrication d'un tel film, et matériau d'emballage à base de papier ou de carton comprenant un tel film WO2024100566A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
SE2230361-4 2022-11-11
SE2230361 2022-11-11

Publications (1)

Publication Number Publication Date
WO2024100566A1 true WO2024100566A1 (fr) 2024-05-16

Family

ID=91032048

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/IB2023/061256 WO2024100566A1 (fr) 2022-11-11 2023-11-08 Film barrière multicouche, procédé de fabrication d'un tel film, et matériau d'emballage à base de papier ou de carton comprenant un tel film

Country Status (1)

Country Link
WO (1) WO2024100566A1 (fr)

Similar Documents

Publication Publication Date Title
US20230313463A1 (en) Multilayer film comprising mfc
CN115461391A (zh) 包含高度精制的纤维素纤维的多层膜
CN115413288B (zh) 包含高度精制的纤维素纤维的多层膜
WO2022137016A1 (fr) Stratifiés
CA3179407A1 (fr) Processus de production d'un substrat nano-revetu
CA3216689A1 (fr) Procede de fabrication d'un film barriere et film barriere
US20230131315A1 (en) Process for production of nano-coated substrate
WO2024100566A1 (fr) Film barrière multicouche, procédé de fabrication d'un tel film, et matériau d'emballage à base de papier ou de carton comprenant un tel film
WO2024100568A1 (fr) Film barrière multicouche, procédé de fabrication de film barrière multicouche, et matériau d'emballage à base de papier ou de carton comprenant un film barrière multicouche
WO2024100565A1 (fr) Film barrière pour matériau d'emballage
SE544892C2 (en) Method for manufacturing a multilayer film comprising highly refined cellulose fibers, a multilayer film and paperboard comprising said multilayer film
SE545698C2 (en) A method for manufacturing a barrier layer for a paper or paperboard based packaging laminate
US20230349099A1 (en) Method for manufacturing films comprising highly refined cellulose fibers