WO2024005470A1 - Catalyseur pour appliquer une réaction électrochimique et son procédé de préparation - Google Patents

Catalyseur pour appliquer une réaction électrochimique et son procédé de préparation Download PDF

Info

Publication number
WO2024005470A1
WO2024005470A1 PCT/KR2023/008828 KR2023008828W WO2024005470A1 WO 2024005470 A1 WO2024005470 A1 WO 2024005470A1 KR 2023008828 W KR2023008828 W KR 2023008828W WO 2024005470 A1 WO2024005470 A1 WO 2024005470A1
Authority
WO
WIPO (PCT)
Prior art keywords
sad
catalyst
metal
single atom
xps analysis
Prior art date
Application number
PCT/KR2023/008828
Other languages
English (en)
Korean (ko)
Inventor
이효영
쿠마아쉬와니
실람바라산 페루말
Original Assignee
성균관대학교산학협력단
기초과학연구원
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 성균관대학교산학협력단, 기초과학연구원 filed Critical 성균관대학교산학협력단
Publication of WO2024005470A1 publication Critical patent/WO2024005470A1/fr

Abstract

La présente invention est destinée à fournir un catalyseur comprenant un métal à atome unique et son procédé de préparation, le catalyseur comprenant : une matrice de carbone dopée à l'azote ; et un métal à atome unique lié à l'azote dans la matrice de carbone.
PCT/KR2023/008828 2022-06-27 2023-06-26 Catalyseur pour appliquer une réaction électrochimique et son procédé de préparation WO2024005470A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
KR10-2022-0078497 2022-06-27
KR20220078497 2022-06-27

Publications (1)

Publication Number Publication Date
WO2024005470A1 true WO2024005470A1 (fr) 2024-01-04

Family

ID=89380958

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/KR2023/008828 WO2024005470A1 (fr) 2022-06-27 2023-06-26 Catalyseur pour appliquer une réaction électrochimique et son procédé de préparation

Country Status (2)

Country Link
KR (1) KR20240001685A (fr)
WO (1) WO2024005470A1 (fr)

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR20210057653A (ko) * 2019-11-12 2021-05-21 울산과학기술원 지속적인 물 분해를 위해 폐 효모를 이용한 다중 헤테로원자로 도핑된 탄소 촉매, 이를 포함한 물 분해 장치 및 이의 제조 방법
KR20210121697A (ko) * 2020-03-31 2021-10-08 한국과학기술연구원 단일원자 크기의 이종 전이금속 및 질소가 도핑된 탄소 복합체의 제조방법
KR20220039356A (ko) * 2020-09-22 2022-03-29 전남대학교산학협력단 질소 도핑된 탄화 폴리도파민 구조체를 포함하는 수소 발생 반응용 전기 촉매
CN114515552A (zh) * 2022-03-11 2022-05-20 山东大学 一种NiCo合金@氮掺杂石墨烯多级孔气凝胶及其制备方法与在锌-空气电池中的应用

Family Cites Families (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR102182553B1 (ko) 2018-11-08 2020-11-24 한국과학기술연구원 탄소 담체 상에 담지된 단일원자 촉매의 제조방법

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR20210057653A (ko) * 2019-11-12 2021-05-21 울산과학기술원 지속적인 물 분해를 위해 폐 효모를 이용한 다중 헤테로원자로 도핑된 탄소 촉매, 이를 포함한 물 분해 장치 및 이의 제조 방법
KR20210121697A (ko) * 2020-03-31 2021-10-08 한국과학기술연구원 단일원자 크기의 이종 전이금속 및 질소가 도핑된 탄소 복합체의 제조방법
KR20220039356A (ko) * 2020-09-22 2022-03-29 전남대학교산학협력단 질소 도핑된 탄화 폴리도파민 구조체를 포함하는 수소 발생 반응용 전기 촉매
CN114515552A (zh) * 2022-03-11 2022-05-20 山东大学 一种NiCo合金@氮掺杂石墨烯多级孔气凝胶及其制备方法与在锌-空气电池中的应用

Non-Patent Citations (2)

* Cited by examiner, † Cited by third party
Title
KUMAR ASHWANI, BUI VIET Q., LEE JINSUN, WANG LINGLING, JADHAV AMOL R., LIU XINGHUI, SHAO XIAODONG, LIU YANG, YU JIANMIN, HWANG YOS: "Moving beyond bimetallic-alloy to single-atom dimer atomic-interface for all-pH hydrogen evolution", NATURE COMMUNICATIONS, NATURE PUBLISHING GROUP, UK, vol. 12, no. 1, UK, XP093121551, ISSN: 2041-1723, DOI: 10.1038/s41467-021-27145-3 *
LI RUNZE, WANG DINGSHENG: "Superiority of Dual‐Atom Catalysts in Electrocatalysis: One Step Further Than Single‐Atom Catalysts", ADVANCED ENERGY MATERIALS, WILEY - V C H VERLAG GMBH & CO. KGAA, DE, vol. 12, no. 9, 1 March 2022 (2022-03-01), DE , XP093121546, ISSN: 1614-6832, DOI: 10.1002/aenm.202103564 *

Also Published As

Publication number Publication date
KR20240001685A (ko) 2024-01-03

Similar Documents

Publication Publication Date Title
WO2016089153A1 (fr) Membrane électrolytique polymère
WO2019022268A1 (fr) Photocatalyseur nanocomposite à base de nanoparticules d'oxyde de zinc/oxyde de graphène réduit ayant une forme contrôlée ayant des caractéristiques photocatalytiques élevées, et son procédé de fabrication
WO2020022822A1 (fr) Nanotube de carbone, son procédé de préparation, et cathode pour batterie primaire le comprenant
WO2019221484A1 (fr) Composé organométallique et diode électroluminescente organique le comprenant
WO2021246762A1 (fr) Composition, source de dépôt, dispositif électroluminescent organique la comprenant, et son procédé de fabrication
WO2022265240A1 (fr) Composition de tricyclodécane diméthanol et son procédé de préparation
WO2024005470A1 (fr) Catalyseur pour appliquer une réaction électrochimique et son procédé de préparation
WO2019004781A1 (fr) Cellule solaire en pérovskite
WO2017171290A1 (fr) Polymère séquencé et membrane électrolytique polymère le comprenant
WO2014181986A1 (fr) Élément électronique organique comprenant un dérivé de fullerène
WO2015190900A1 (fr) Composé précurseur pour la formation de film, et procédé de formation de film mince l'utilisant
WO2019125052A1 (fr) Composition d'aérogel et son procédé de préparation
WO2016144097A2 (fr) Polymère et cellule solaire organique le comprenant
WO2020046064A1 (fr) Catalyseur composite de réduction de dioxyde de carbone et procédé de fabrication correspondant
WO2022025675A1 (fr) Catalyseur d'ammoxydation pour propylène, son procédé de fabrication et procédé d'ammoxydation de propylène utilisant ledit catalyseur
WO2017135638A1 (fr) Complexe de métal de transition contenant un groupe sulfonamide ou amide pour double réaction de décomposition d'oléfines et application correspondante
WO2021137632A1 (fr) Catalyseur à double cyanure métallique, son procédé de préparation, et procédé de préparation de polyol
WO2021145639A1 (fr) Polymère et diode électroluminescente organique l'utilisant
WO2019098771A1 (fr) Polymère et séparateur polymère le comprenant
WO2021167432A1 (fr) Structure d'électrode, structure d'électrode pour électrode positive de batterie métal-air la comprenant, et leurs procédés de fabrication
WO2021145649A1 (fr) Nouveau carbène n-hétérocyclique, complexe de métal de transition de celui-ci et procédé pour la préparation de celui-ci
WO2024005308A1 (fr) Copolymère réticulé, membrane polymère le comprenant et membrane échangeuse d'anions comprenant cette membrane polymère
WO2021241874A1 (fr) Catalyseur mixte pour pile à combustible, son procédé de préparation, procédé de formation d'électrode l'utilisant, et ensemble membrane-électrode le comprenant
WO2017052226A1 (fr) Polymère séquencé et membrane électrolytique polymère le comprenant
WO2023282615A1 (fr) Composé précurseur de molybdène, procédé de préparation associé et procédé de dépôt de film mince contenant du molybdène l'utilisant

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 23831830

Country of ref document: EP

Kind code of ref document: A1