WO2024000359A1 - Catalyseurs à base d'or pour procédés de conversion inverse de gaz à l'eau - Google Patents
Catalyseurs à base d'or pour procédés de conversion inverse de gaz à l'eau Download PDFInfo
- Publication number
- WO2024000359A1 WO2024000359A1 PCT/CN2022/102685 CN2022102685W WO2024000359A1 WO 2024000359 A1 WO2024000359 A1 WO 2024000359A1 CN 2022102685 W CN2022102685 W CN 2022102685W WO 2024000359 A1 WO2024000359 A1 WO 2024000359A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- catalyst
- oxide
- support
- range
- gold
- Prior art date
Abstract
L'invention concerne un catalyseur de conversion inverse de gaz à l'eau supporté comprenant : un support qui représente un support d'oxyde de cérium, un support d'oxyde de titane, un support d'oxyde d'aluminium, un support d'oxyde de zirconium, ou un support d'oxyde mixte comprenant un mélange d'au moins deux éléments parmi l'oxyde de cérium, l'oxyde de titane, l'oxyde d'aluminium, et l'oxyde de zirconium ; de l'or, présent dans une proportion se situant dans la plage de 0,05 à 10 % en poids du catalyseur, sur la base du poids total du catalyseur ; et du manganèse, présent dans une proportion se situant dans la plage de 0,5 à 20 % en poids du catalyseur, sur la base du poids total du catalyseur.
Priority Applications (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
PCT/CN2022/102685 WO2024000359A1 (fr) | 2022-06-30 | 2022-06-30 | Catalyseurs à base d'or pour procédés de conversion inverse de gaz à l'eau |
PCT/IB2023/056802 WO2024003845A1 (fr) | 2022-06-30 | 2023-06-29 | Catalyseurs à base de palladium, de platine et d'or pour la conversion inverse de gaz à l'eau et procédés de fischer-tropsch intégrés |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
PCT/CN2022/102685 WO2024000359A1 (fr) | 2022-06-30 | 2022-06-30 | Catalyseurs à base d'or pour procédés de conversion inverse de gaz à l'eau |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2024000359A1 true WO2024000359A1 (fr) | 2024-01-04 |
Family
ID=89383549
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/CN2022/102685 WO2024000359A1 (fr) | 2022-06-30 | 2022-06-30 | Catalyseurs à base d'or pour procédés de conversion inverse de gaz à l'eau |
Country Status (1)
Country | Link |
---|---|
WO (1) | WO2024000359A1 (fr) |
Citations (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2003305364A (ja) * | 2002-04-17 | 2003-10-28 | National Institute Of Advanced Industrial & Technology | 水性ガスシフト反応用触媒 |
CN1583257A (zh) * | 2004-05-26 | 2005-02-23 | 长沙卷烟厂 | 一种用于脱除卷烟主流烟中氢氰酸的催化剂及其制备方法和应用 |
JP2006212571A (ja) * | 2005-02-04 | 2006-08-17 | Nippon Shokubai Co Ltd | Au触媒の劣化抑制方法 |
US20080193354A1 (en) * | 2007-02-08 | 2008-08-14 | Tatung Company | Preparation of manganese oxide-cerium oxide-supported nano-gold catalyst and the application thereof |
WO2017122113A1 (fr) * | 2016-01-15 | 2017-07-20 | Sabic Global Technologies B.V. | Procédés de production de gaz de synthèse à partir de dioxyde de carbone |
CN112774673A (zh) * | 2021-02-05 | 2021-05-11 | 西安凯立新材料股份有限公司 | 一种用于丙烯醛空气氧化制备丙烯酸的催化剂及其制备方法与应用 |
-
2022
- 2022-06-30 WO PCT/CN2022/102685 patent/WO2024000359A1/fr unknown
Patent Citations (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2003305364A (ja) * | 2002-04-17 | 2003-10-28 | National Institute Of Advanced Industrial & Technology | 水性ガスシフト反応用触媒 |
CN1583257A (zh) * | 2004-05-26 | 2005-02-23 | 长沙卷烟厂 | 一种用于脱除卷烟主流烟中氢氰酸的催化剂及其制备方法和应用 |
JP2006212571A (ja) * | 2005-02-04 | 2006-08-17 | Nippon Shokubai Co Ltd | Au触媒の劣化抑制方法 |
US20080193354A1 (en) * | 2007-02-08 | 2008-08-14 | Tatung Company | Preparation of manganese oxide-cerium oxide-supported nano-gold catalyst and the application thereof |
WO2017122113A1 (fr) * | 2016-01-15 | 2017-07-20 | Sabic Global Technologies B.V. | Procédés de production de gaz de synthèse à partir de dioxyde de carbone |
CN112774673A (zh) * | 2021-02-05 | 2021-05-11 | 西安凯立新材料股份有限公司 | 一种用于丙烯醛空气氧化制备丙烯酸的催化剂及其制备方法与应用 |
Non-Patent Citations (1)
Title |
---|
CHANG, L. ET AL.: "Au/MnO2-TiO2 catalyst for preferential oxidation of carbon monoxide in hydrogen stream", CATALYSIS COMMUNICATIONS, vol. 8, 23 September 2006 (2006-09-23), pages 1702 - 1710, XP022262211, ISSN: 1566-7367, DOI: 10.1016/j.catcom.2006.08.050 * |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
CN101678329B (zh) | 将二氧化碳催化加氢成合成气混合物 | |
US4927857A (en) | Method of methanol production | |
US8834835B2 (en) | Ultra high temperature shift catalyst with low methanation | |
US7718832B1 (en) | Combination catalytic process for producing ethanol from synthesis gas | |
KR100732784B1 (ko) | 탄화수소로부터 디메틸에테르를 제조하는 방법 | |
US8962702B2 (en) | Mixed oxide based catalyst for the conversion of carbon dioxide to syngas and method of preparation and use | |
CA2887713A1 (fr) | Conversion de gaz naturel en composes organiques | |
CN105944751A (zh) | 一种用于合成气直接制备芳香族化合物的催化剂及其制备与应用 | |
WO2005097319A1 (fr) | Catalyseur supporte pour reactions de vaporeformeur de methane et de reformeur autothermique | |
CN102256687A (zh) | 增加合成气混合物中一氧化碳含量的方法 | |
WO2007029862A1 (fr) | Catalyseur pour l’oxydation catalytique partielle d’hydrocarbures et procede de fabrication d’un gaz de synthese | |
US20070183968A1 (en) | Water-gas shift and reforming catalyst and method of reforming alcohol | |
CN100350023C (zh) | 合成气处理工艺和催化剂 | |
KR101453443B1 (ko) | 고발열량의 합성천연가스 생산을 위한 촉매 및 이의 제조방법 | |
WO2024000359A1 (fr) | Catalyseurs à base d'or pour procédés de conversion inverse de gaz à l'eau | |
CN111511882A (zh) | 高热值合成天然气的制备方法及其制备装置 | |
WO2024000370A1 (fr) | Catalyseurs au manganèse pour procédés de conversion inverse de gaz à l'eau | |
WO2024000343A1 (fr) | Catalyseurs au nickel pour procédés de conversion inverse de gaz à l'eau | |
WO2024000468A1 (fr) | Catalyseurs au palladium et au platine pour processus de conversion inverse de gaz à l'eau | |
WO2024000353A1 (fr) | Procédés fischer-tropsch intégrés utilisant des catalyseurs de conversion inverse eau-gaz au manganèse | |
WO2024000381A1 (fr) | Procédés fischer-tropsch intégrés utilisant des catalyseurs de conversion inverse eau-gaz à l'or | |
WO2024000397A1 (fr) | Procédés fischer-tropsch intégrés utilisant des catalyseurs de conversion inverse eau-gaz au nickel | |
WO2024000403A1 (fr) | Procédés fischer-tropsch intégrés utilisant du palladium et des catalyseurs de conversion eau-gaz inverse de platine | |
RU2414954C1 (ru) | Пористая каталитическая мембрана и способ получения водородсодержащего газа в ее присутствии | |
MXPA06007480A (es) | Procedimiento pra la transformacion de un gas de sintesis en hidrocarburos en presencia de sic beta y efluente de ese procedimiento. |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 22948471 Country of ref document: EP Kind code of ref document: A1 |