WO2023277118A1 - 発電用複合材料および発電用複合材料の製造方法 - Google Patents

発電用複合材料および発電用複合材料の製造方法 Download PDF

Info

Publication number
WO2023277118A1
WO2023277118A1 PCT/JP2022/026157 JP2022026157W WO2023277118A1 WO 2023277118 A1 WO2023277118 A1 WO 2023277118A1 JP 2022026157 W JP2022026157 W JP 2022026157W WO 2023277118 A1 WO2023277118 A1 WO 2023277118A1
Authority
WO
WIPO (PCT)
Prior art keywords
power generation
composite material
piezoelectric
ceramic
generation according
Prior art date
Application number
PCT/JP2022/026157
Other languages
English (en)
French (fr)
Inventor
真金 王
衡平 丸山
史生 成田
Original Assignee
国立大学法人東北大学
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 国立大学法人東北大学 filed Critical 国立大学法人東北大学
Publication of WO2023277118A1 publication Critical patent/WO2023277118A1/ja

Abstract

【課題】耐久性が高く、比較的優れた圧電特性を有する発電用複合材料および発電用複合材料の製造方法を提供する。 【解決手段】所定の厚みを有する板状を成し、圧電性を有するセラミックと、圧電性を有するポリマーとを含み、厚み方向に沿ってセラミックの含有率が連続的に徐々に変化するよう構成されている。圧電性を有するセラミックと、圧電性を有するポリマーとを含み、セラミックの含有率が異なる複数種類の圧電薄膜を、その厚み方向に沿ってセラミックの含有率が徐々に変化するよう積層した後、熱処理を行うことにより製造される。

Description

発電用複合材料および発電用複合材料の製造方法
　本発明は、発電用複合材料および発電用複合材料の製造方法に関する。
　近年、モノのインターネット（Internet of Things；ＩｏＴ）の普及に伴い、ＩｏＴデバイスへの電力供給源の一つとして、周囲の環境にある熱や風、振動などの微小なエネルギーを電気エネルギーに変えることのできる環境発電デバイスが注目されている。環境発電を行う材料の一つとして、機械エネルギーを電気エネルギーに変えることのできる圧電材料がある。圧電材料は、比較的耐久性が高く、微小なひずみに対して敏感で、高い出力電力密度および出力電圧が期待できる。また、圧電材料は、小さくコンパクトであり、湿度などの環境要因の影響を受けにくいため、ＩｏＴデバイスの電力供給源として最適である。
　優れた圧電特性を有する材料として圧電セラミックスが知られているが、圧電セラミックスは、高周波の繰り返し荷重を受けると疲労き裂の影響を受けやすくなるため、それのみでは使用するのが難しいという問題があった。そこで、この問題を解決するために、従来、金属製の弾性板などの基板の一方の表面または両面に圧電セラミックスを貼り付けた圧電発電ユニットが、多く利用されている（例えば、特許文献１参照）。また、柔軟性を有する高分子にセラミックスを加えた圧電複合材料も開発されている（例えば、非特許文献１乃至３参照）。
　また、曲げ耐性を向上させるために、樹脂と圧電粒子とを有する圧電体層として、２つの第１圧電体層と、各第１圧電体層の間に配された第２圧電体層とを有し、第２圧電体層の圧電粒子の体積パーセント濃度を、各第１圧電体層よりも低くした複合圧電素子も提案されている（例えば、特許文献２参照）。この複合圧電素子では、第２圧電体層の圧電粒子の体積パーセント濃度が低いため、第２圧電体層の曲げ耐性が向上し、圧電粒子の体積パーセント濃度が高い圧電体の単層で構成した場合と比較して、圧電体層全体の曲げ耐性も向上させることができる。しかも、その第２圧電体層を、圧電粒子の体積パーセント濃度が高い２つの第１圧電体層で挟んだ構造をしているため、各第１圧電体層による性能が優先されて、圧電体層全体での圧電性能は大きく低下しないという特徴を有している。
　なお、圧電複合材料の一つとして、セラミックスに濃度勾配を持たせた傾斜機能材料（Functionally Graded Material；ＦＧＭ）の研究も行われており、高強度かつ高靱性であり、高い疲労強度を有することが確認されている（例えば、非特許文献４参照）が、圧電特性についてはまだ確認されていない。
特開２０１１－２５０５３６号公報 特開２０１５－５０４３２号公報
Zhenjin Wang, Fumio Narita, "Corona Poling Conditions for Barium Titanate/Epoxy Composites and their Unsteady Wind Energy Harvesting Potential", Advanced Engineering Materials, 2019, Volume 21, 1900169 Zhenjin Wang, Fumio Narita, "Fabrication of Potassium Sodium Niobate Nano-Particle/Polymer Composites with Piezoelectric Stability and Their Application to Unsteady Wind Energy Harvesters", Journal of Applied Physics, 2019, Volume 126, 224501 Zhenjin Wang, Hiroki Kurita, Hiroaki Nagaoka, Fumio Narita, "Potassium Sodium Niobate Lead-Free Piezoelectric Nanocomposite Generators Based on Carbon-Fiber-Reinforced Polymer Electrodes for Energy-Harvesting Structures", Composites Science and Technology, 2020, Volume 199, 108331 Saurav Sharma, Anuruddh Kumar, Rajeev Kumar, Mohammad Talha, Rahul Vaish, "Geometry Independent Direct and Converse Flexoelectric Effects in Functionally Graded Dielectrics: An Isogeometric Analysis", Mechanics of Materials, 2020, Volume 148, 103456
　特許文献１に記載のような従来の圧電発電ユニットは、圧電セラミックスを接着剤などで基板に貼り付ける必要があり、振動や衝撃が繰り返し加わると剥がれてしまうという課題があった。また、従来の圧電複合材料では、圧電特性が小さいという課題があった。また、特許文献２に記載の複合圧電素子では、圧電体層が、２つの第１圧電体層の間に、圧電粒子の体積パーセント濃度が異なる第２圧電体層を挟んでいるため、圧電体層に曲げ荷重を加えると、各第１圧電体層と第２圧電体層との界面で、ひずみや応力のギャップが発生してしまう。このため、これらの界面で圧電体層が剥がれ、破壊されてしまうという課題があった。
　本発明は、このような課題に着目してなされたもので、耐久性が高く、比較的優れた圧電特性を有する発電用複合材料および発電用複合材料の製造方法を提供することを目的とする。
　上記目的を達成するために、本発明に係る発電用複合材料は、圧電性を有するセラミックと、圧電性を有するポリマーとを含み、所定の方向に沿って前記セラミックの含有率が連続的に徐々に変化するよう構成されていることを特徴とする。
　本発明に係る発電用複合材料の製造方法は、圧電性を有するセラミックと、圧電性を有するポリマーとを含み、前記セラミックの含有率が異なる複数種類の圧電薄膜を、その膜厚方向に沿って前記セラミックの含有率が徐々に変化するよう積層した後、熱処理を行うことを特徴とする。
　本発明に係る発電用複合材料の製造方法は、本発明に係る発電用複合材料を好適に製造することができる。本発明に係る発電用複合材料は、セラミックだけでなく、柔軟性を有するポリマーも含んでいるため、繰り返し荷重に弱いセラミックのみから成る圧電材料と比べて耐久性が高い。また、弾性を有する基板などに貼り付ける必要もないため、振動や衝撃にも強く、優れた耐久性を有している。また、セラミックの含有率が急激に変化する界面などでは割れが発生しやすいが、本発明に係る発電用複合材料は、セラミックの含有率が連続的に徐々に変化するよう構成されており、セラミックの含有率が急激に変化する界面が存在していないため、割れが発生しにくく、耐久性が高い。
　本発明に係る発電用複合材料は、セラミックだけでなく、ポリマーも圧電性を有しているため、セラミックと圧電性を有さない材料との複合材料と比べて、優れた圧電特性を有している。本発明に係る発電用複合材料は、セラミックの含有率が徐々に変化しているため、圧電定数が異なるセラミックとポリマーとを含むことにより、その含有率の値の大きさや含有率の変化の状態によって、様々な特性を有することができる。本発明に係る発電用複合材料は、特に優れた圧電特性を得るために、正の圧電定数を有するセラミックと、負の圧電定数を有するポリマーとを含むことが好ましい。
　本発明に係る発電用複合材料の製造方法は、セラミックの含有率が異なる複数種類の圧電薄膜を積層した後、熱処理を行うことにより、セラミックの含有率が圧電薄膜の境界で急激に変化せず、連続的に徐々に変化するよう構成することができる。これにより、圧電薄膜の境界が、セラミックの含有率が急激に変化する界面にならず、圧電薄膜の境界で割れたり剥がれたりするのを防ぐことができ、耐久性を高めることができる。
　本発明に係る発電用複合材料の製造方法で、前記熱処理は、積層した各圧電薄膜をその膜厚方向に圧縮した状態で加熱してもよく、積層した各圧電薄膜を圧縮せずに加熱してもよい。また、各圧電薄膜の再結晶温度よりも低い温度で加熱することが好ましい。この場合、再結晶による圧電特性の低下を防ぐことができる。熱処理は、積層した各圧電薄膜を圧縮するときには、例えば、ホットプレスにより行うことができる。
　本発明に係る発電用複合材料の製造方法は、溶媒中に前記セラミックと前記ポリマーとを加えて撹拌した混合液を用いて、スピンコート法により各圧電薄膜を作製することが好ましい。この場合、薄く、濃度が均一な圧電薄膜を、比較的容易に作製することができる。なお、圧電薄膜は、スピンコート法以外にも、例えば、溶剤キャスティング法により作製することができる。
　本発明に係る発電用複合材料の製造方法は、各圧電薄膜を作製した後、各圧電薄膜を積層してもよく、製造した圧電薄膜の上に、順次、圧電薄膜を作製していくことにより、各圧電薄膜を積層してもよい。後者の場合には、前者と比べて、作製した各圧電薄膜を積層する工程を省略することができ、比較的短い時間で効率よく製造することができる。
　本発明に係る発電用複合材料は、前記所定の方向に沿って、前記セラミックの含有率が連続的に徐々に増加または減少するよう構成されていてもよい。この場合、本発明に係る発電用複合材料の製造方法において、各圧電薄膜を、その膜厚方向に沿って前記セラミックの含有率が徐々に増加または減少するよう積層した後、前記熱処理を行うことにより製造することができる。本発明に係る発電用複合材料は、一方の表面側の圧電定数と、他方の表面側の圧電定数とが異なっているため、所定の方向（積層方向）に曲げたときの発電効率が高い。このため、例えば、所定の方向への振動を利用した振動発電に、効果的に利用することができる。
　また、本発明に係る発電用複合材料は、前記所定の方向に沿った前記セラミックの含有率の分布が、前記所定の方向での中心面に対して面対称を成すよう構成されていてもよい。この場合、本発明に係る発電用複合材料の製造方法において、各圧電薄膜を積層した積層体の積層方向に沿った前記セラミックの含有率が、前記積層体の積層方向での中心面に対して面対称になるよう、各圧電薄膜を積層した後、前記熱処理を行うことにより製造することができる。本発明に係る発電用複合材料は、所定の方向（積層方向）での中心面に対して、圧電定数の分布が面対称になるため、所定の方向に圧縮されたときの発電効率が高い。このため、例えば、所定の方向の衝撃を利用した衝撃発電に、効果的に利用することができる。
　また、本発明に係る発電用複合材料は、前記所定の方向に沿って、前記セラミックの含有率が増加する範囲と減少する範囲とを有するよう構成されていてもよい。この場合、本発明に係る発電用複合材料の製造方法において、各圧電薄膜を積層した積層体の積層方向に沿って、前記セラミックの含有率が増加する範囲と減少する範囲とを有するよう、各圧電薄膜を積層した後、前記熱処理を行うことにより製造することができる。本発明に係る発電用複合材料は、所定の方向（積層方向）に沿って圧電定数が増減する分布を有している。
　本発明に係る発電用複合材料および発電用複合材料の製造方法で、前記セラミックは、例えば、チタン酸バリウム（ＢａＴｉＯ３；ＢＴＯ）、ニオブ酸カリウムナトリウム［(Ｋ,Ｎａ)ＮｂＯ３；ＫＮＮ］、チタン酸ビスマスナトリウム［（Ｂｉ１／２Ｎａ１／２）Ｔｉ３；ＢＮＴ］、ビスマスフェライト（ＢｉＦｅＯ３；ＢＦ）といったペロブスカイト構造を有するものなど、圧電性を有するものであれば、いかなるものから成っていてもよいが、有毒な鉛を含んでいないことが好ましい。ペロブスカイト構造を有するものは、強誘電体であるため、分極することで圧電性を示す。また、前記ポリマーは、例えば、ポリフッ化ビニリデン（ＰＶＤＦ）や、ポリフッ化ビニリデンと三フッ化エチレンとの共重合体であるＰ（ＶＤＦ－ＴｒＦＥ）など、圧電性を有するものであれば、いかなるものから成っていてもよい。Ｐ（ＶＤＦ－ＴｒＦＥ）は、分極を行うことで、水素とフッ素の電気陰性度の差により電荷に偏りが生じ、圧電性を示す。また、ＰＶＤＦは、伸ばした状態で分極を行う必要があるが、Ｐ（ＶＤＦ－ＴｒＦＥ）は、分極の際に、伸ばしておく必要がない。
　本発明に係る発電用複合材料は、板状を成し、厚み方向が前記所定の方向であることが好ましい。本発明に係る発電用複合材料の製造方法では、各圧電薄膜を積層した積層体が板状を成し、厚み方向が前記積層体の積層方向であることが好ましい。また、本発明に係る発電用複合材料は、所定の方向に沿った任意の範囲でのセラミックの含有率が５０％以下であることが好ましい。この場合、本発明に係る発電用複合材料の製造方法において、各圧電薄膜のセラミックの含有率を５０％以下にすることにより製造することができる。セラミックの含有率が５０％以下であるため、繰り返し荷重や振動、衝撃などを受けたときに割れにくく、耐久性が高い。
　本発明に係る発電用複合材料は、セラミックの含有率がほぼ連続的に変化していることが好ましい。例えば、セラミックの含有率が連続的に変化していれば、その変化がある程度急激であってもよい。また、本発明に係る発電用複合材料は、ポリマーとセラミックとの界面に、物理的あるいは化学的処理が施されていてもよい。また、本発明に係る発電用複合材料は、圧電性を有するポリマーおよびセラミックの他に、鉄コバルト（FeCo）や鉄コバルトバナジウム（FeCoV）などの正の磁歪効果を有する合金粉末や、コバルトフェライト（CoFeO）などの負の磁歪効果を有するセラミック粉末を含んでいてもよい。また、本発明に係る発電用複合材料は、強靱化のため、例えば炭素繊維強化プラスチックを用いた電極などに取り付けられてもよい。
　本発明によれば、耐久性が高く、比較的優れた圧電特性を有する発電用複合材料および発電用複合材料の製造方法を提供することができる。
本発明の実施の形態の発電用複合材料の製造方法の、実施例１でのフローを示す斜視図である。 本発明の実施の形態の発電用複合材料の、実施例１の（ａ）比較例であるBTOの体積分率が30 vol.%の試料、（ｂ）BTOの体積分率が徐々に増加する試料（FGM1）、（ｃ）両側の表面から中心面に向かって、BTOの体積分率が徐々に減少する試料（FGM2）、（ｄ）両側の表面から中心面に向かって、BTOの体積分率が徐々に増加する試料（FGM3）を示す斜視図（上図）および側面図（下図）である。 （ａ）図２（ａ）に示す比較例の試料、（ｂ）図２（ｂ）に示すFGM1、（ｃ）図２（ｃ）に示すFGM2、（ｄ）図２（ｄ）に示すFGM3の、断面の走査型電子顕微鏡（SEM）写真である。 本発明の実施の形態の発電用複合材料の、実施例１の比較例であるBTOの体積分率が一定の各試料の、示差走査熱量測定によるDSC曲線を示すグラフである。 本発明の実施の形態の発電用複合材料の、実施例１の各試料の圧電定数ｄ３３を示すグラフである。 本発明の実施の形態の発電用複合材料の、実施例１の衝撃発電試験の試験装置を示す全体構成図である。 本発明の実施の形態の発電用複合材料の、実施例１の比較例であるBTOの体積分率が30 vol.%の試料、FGM1、FGM2、FGM3の、衝撃発電試験による出力電圧（Output voltage）を示すグラフである。 本発明の実施の形態の発電用複合材料の、実施例１の振動発電試験の試験装置の全体構成を示す斜視図である。 本発明の実施の形態の発電用複合材料の、実施例１の比較例であるBTOの体積分率が30 vol.%の試料、FGM1、FGM2、FGM3の、振動発電試験による各周波数での出力電圧（Output voltage）を示すグラフである。 本発明の実施の形態の発電用複合材料の、（ａ）有限要素解析モデルを示す正面図、（ｂ）有限要素解析モデルを示す斜視図および境界条件である。 図１０に示す有限要素解析モデルによる解析結果を示す、（ａ）６つのBTOの体積分率の分布パターンならびに、各パターンでの電位差、（ｂ）６つのBTOの体積分率の分布パターンおよび、各パターンでの電位差である。 本発明の実施の形態の発電用複合材料の製造方法の、実施例３でのフローを示す斜視図である。 本発明の実施の形態の発電用複合材料の製造方法の、実施例３の（ａ）試料AFGC1、（ｂ）試料AFGC2、（ｃ）試料AFGC3の断面の走査型電子顕微鏡（SEM）写真、（ｄ）　（ｂ）の中心部分を拡大したSEM写真、（ｅ）　（ｂ）の中心近傍を拡大したSEM写真である。 本発明の実施の形態の発電用複合材料の、実施例３の試料AFGC1および試料FGM1（図中では、FGC1と記載）の、振動発電試験による各周波数（Vibration frequency）での出力電圧（Output voltage）を示すグラフである。 本発明の実施の形態の発電用複合材料の、実施例３の試料AFGC1の耐久試験による、各経過時間（Time）が（ａ）0～4005 secのとき、（ｂ）4000～8005 secのときの出力電圧（Real-time output voltage）を示すグラフである。
　以下、実施例等に基づいて、本発明の実施の形態について説明する。
　本発明の実施の形態の発電用複合材料は、所定の厚みを有する板状を成している。本発明の実施の形態の発電用複合材料は、圧電性を有するセラミックと、圧電性を有するポリマーとを含み、厚み方向に沿ってセラミックの含有率が連続的に徐々に変化するよう構成されている。
　セラミックは、例えば、チタン酸バリウム（ＢａＴｉＯ３；ＢＴＯ）、ニオブ酸カリウムナトリウム［(Ｋ,Ｎａ)ＮｂＯ３；ＫＮＮ］、チタン酸ビスマスナトリウム［（Ｂｉ１／２Ｎａ１／２）Ｔｉ３；ＢＮＴ］、ビスマスフェライト（ＢｉＦｅＯ３；ＢＦ）などのペロブスカイト構造を有するものから成り、ポリマーは、例えば、ポリフッ化ビニリデン（ＰＶＤＦ）や、ポリフッ化ビニリデンと三フッ化エチレンとの共重合体であるＰ（ＶＤＦ－ＴｒＦＥ）などから成っている。
　また、本発明の実施の形態の発電用複合材料は、例えば、厚み方向に沿って、セラミックの含有率が徐々に増加または減少するよう構成されていてもよく、厚み方向に沿ったセラミックの含有率の分布が、厚み方向の中心面に対して面対称を成すよう構成されていてもよい。
　本発明の実施の形態の発電用複合材料は、本発明の実施の形態の発電用複合材料の製造方法により製造することができる。すなわち、本発明の実施の形態の発電用複合材料の製造方法では、まず、圧電性を有するセラミックと、圧電性を有するポリマーとを含み、セラミックの含有率が異なる複数種類の圧電薄膜を作製する。このとき、薄く、濃度が均一な圧電薄膜を作製可能であれば、いかなる方法で圧電薄膜を作製してもよい。例えば、溶媒中にセラミックとポリマーとを加えて撹拌した混合液を用いて、スピンコート法により各圧電薄膜を作製してもよい。
　圧電薄膜を作製後、その厚み方向に沿ってセラミックの含有率が徐々に変化するよう積層した後、熱処理を行う。このとき、例えば、ホットプレスにより、積層した各圧電薄膜をその厚み方向に圧縮した状態で加熱してもよく、積層した各圧電薄膜を圧縮せずに加熱してもよい。また、各圧電薄膜の再結晶温度よりも低い温度で加熱することにより、再結晶による圧電特性の低下を防ぐことができる。また、熱処理により、セラミックの含有率が圧電薄膜の境界で急激に変化せず、連続的に徐々に変化するよう構成することができる。こうして、本発明の実施の形態の発電用複合材料を製造することができる。
　本発明の実施の形態の発電用複合材料は、セラミックだけでなく、柔軟性を有するポリマーも含んでいるため、繰り返し荷重に弱いセラミックのみから成る圧電材料と比べて耐久性が高い。また、弾性を有する基板などに貼り付ける必要もないため、振動や衝撃にも強く、優れた耐久性を有している。また、セラミックの含有率が急激に変化する界面などでは割れが発生しやすいが、本発明の実施の形態の発電用複合材料は、セラミックの含有率が連続的に徐々に変化するよう構成されており、セラミックの含有率が急激に変化する界面が存在していないため、圧電薄膜の境界などで割れや剥がれが発生しにくく、耐久性が高い。
　本発明の実施の形態の発電用複合材料は、セラミックだけでなく、ポリマーも圧電性を有しているため、セラミックと圧電性を有さない材料との複合材料と比べて、優れた圧電特性を有している。本発明の実施の形態の発電用複合材料は、圧電定数が異なるセラミックとポリマーとを含み、セラミックの含有率が徐々に変化するよう構成されているため、その含有率の値の大きさや含有率の変化の状態によって、様々な特性を有することができる。
　なお、本発明の実施の形態の発電用複合材料の製造方法は、複数種類の圧電薄膜を作製した後、各圧電薄膜を積層するのではなく、製造した圧電薄膜の上に、順次、圧電薄膜を作製していくことにより、複数種類の圧電薄膜を積層してもよい。この場合、作製した各圧電薄膜を積層する工程を省略することができ、比較的短い時間で効率よく製造することができる。また、この場合にも、スピンコート法により各圧電薄膜を作製することができる。
　本発明の実施の形態の発電用複合材料の製造方法により発電用複合材料を製造し、圧電定数の測定および発電試験を行った。
［発電用複合材料の製造］
　発電用複合材料を製造するための原料のうち、圧電性を有するセラミックとして、BaTiO3（BTO、サイズ 1.04μm；日本化学工業株式会社製）を用い、圧電性を有するポリマーとして、ポリフッ化ビニリデン（PVDF）の共重合体であるポリフッ化ビニリデン三フッ化エチレン P(VDF-TrFE)（株式会社イデアルスター製「ispp015-1」）を用いた。BTOは、身体に有毒な鉛を含まず、ペロブスカイト構造を有する強誘電体であり、分極することで圧電性を示す材料である。また、P(VDF-TrFE)は、分極すると、水素の電気陰性度とフッ素の電気陰性度との差により電荷に偏りが生じて、圧電性を示すものである。
　図１に示すように、発電用複合材料の製造では、まず、粉末状のP(VDF-TrFE)を、溶媒のジメチルホルムアミド（DMF、富士フイルム株式会社製）に、P(VDF-TrFE)：DMF＝10：90の重量比で加え、撹拌器（IKA-Werke GmbH & Co. KG社製「C-MAG HS4」）により、60℃で20分間撹拌（Stirring）した。その後、その溶液にBTOのナノ粒子（nanoparticle）を加え、撹拌機により室温で１時間撹拌（Stirring）し、さらに40℃で２時間超音波（Ultrasonic）を照射して撹拌した。撹拌後の混合液を、スピンコーター（ミカサ株式会社製「MS-B150」）により、直径10 mmのシリコンウエハー上に薄く広げ、90℃のホットプレートで加熱して溶媒を蒸発させて、BaTiO3/P(VDF-TrFE)から成る圧電薄膜１１を作製した。このスピンコート法（Spin coating）では、スピンコーターを、1000 rpm/secの回転速度で５秒間回転させた後、-200 rpm/secで減速させた。
　圧電薄膜１１は、P(VDF-TrFE)に対して、BTOの体積分率がそれぞれ、0 vol.%、10 vol.%、20 vol.%、30 vol.%、40 vol.%、50 vol.%の６種類を作製した。各圧電薄膜１１の平均厚さは、それぞれ 0.010 mm、0.012 mm、0.014 mm、0.016 mm、0.018 mm、0.020mmであった。
　作製した各種の圧電薄膜１１を、その厚み方向に沿って複数枚積層（Laminating）し、ホットプレス（Hot press）により、厚み方向に 7.5 MPaで圧縮した状態で、130℃で30秒間加熱した。こうして、複数種類の発電用複合材料の試料１０を製造した。ホットプレス後、各試料１０を、所望の大きさの矩形状に切断した。なお、厚みは、0.15 mmである。
　試料１０は、まず、図２（ａ）に示すように、BTOの体積分率が一定の試料１０（比較例）として、BTOの体積分率が同じ圧電薄膜１１のみを積層したもの、すなわち、0 vol.%、10 vol.%、20 vol.%、30 vol.%、40 vol.%、50 vol.%の６種類を製造した。これらの試料１０では、BTOの体積分率によって圧電薄膜１１の膜厚が異なるため、ホットプレス後の厚さが0.15 mm になるよう、積層させる枚数をそれぞれ18枚、14枚、13枚、12枚、9枚、8枚としている。なお、図２（ａ）には、BTOの体積分率が30 vol.%の試料１０を示している。
　また、図２（ｂ）～（ｄ）に示すように、BTOの体積分率が徐々に変化する試料１０として、積層体の一方の表面から他方の表面に向かって、BTOの体積分率が0 vol.%から50 vol.%まで徐々に増加するよう、圧電薄膜１１を積層したもの（以下、FGM1と呼ぶ）、積層体の厚み方向の中心面に対して面対称になるよう、両側の表面から中心面に向かって、BTOの体積分率が50 vol.%から0 vol.%まで徐々に減少するよう圧電薄膜１１を積層したもの（以下、FGM2と呼ぶ）、積層体の厚み方向の中心面に対して面対称になるよう、両側の表面から中心面に向かって、BTOの体積分率が0 vol.%から50 vol.%まで徐々に増加するよう圧電薄膜１１を積層したもの（以下、FGM3と呼ぶ）の３種類を製造した。これら３種類の試料１０の、BTOの平均体積分率は、30 vol.%である。
　製造した図２（ａ）～（ｄ）に示す各試料１０をエポキシ樹脂で覆い、走査型電子顕微鏡（SEM；株式会社日立ハイテク製「SU-70」）により、断面観察を行った。その結果を、それぞれ図３（ａ）～（ｄ）に示す。図３（ａ）～（ｄ）に示すように、各試料１０とも、積層した圧電薄膜１１の境界が認められず、一体化していることが確認された。特に、図３（ｂ）～（ｄ）に示す各試料１０では、図中の矢印の方向に沿って、BTOの体積分率が徐々に増加している様子が確認された。
　BTOの体積分率が一定の各試料１０に対し、示差走査熱量測定分析装置（ネッチ・ジャパン株式会社製「DSC 404F3」）を用いて、示差走査熱量測定（DSC）を行った。その結果を、図４に示す。図４に示すように、各試料１０の融点は、150℃～155℃であり、BTOの体積分率が大きくなるほど、融点が低くなることが確認された。また、再結晶温度は、140℃であることも確認された。このことから、130℃でのホットプレスは、試料１０の結晶構造に影響を与えていないといえる。
［分極処理］
　製造した各試料１０に圧電性を発現させるために、コロナ放電システム（エレメント有限会社製「ELC-01N」）を用いて、コロナ分極法により分極処理を行った。コロナ分極法では、裏面を接地すると共に、ホットプレートで加熱した状態の各試料１０に対して、各試料１０の表面から離れて設置されたタングステン針に高電圧を印加することにより、各試料１０とタングステン針との間にコロナ放電を起こす。これにより、各試料１０の表面にタングステン針から電荷が吹き付けられるため、各試料１０の表面と裏面との間に電界が発生し、分極することができる。なお、タングステン針に印加する電圧を、7.0 kV、ホットプレートの温度を、65℃とした。
［圧電特性の測定］
　厚み方向に分極した圧電材料では、電界がゼロのとき、厚み方向に応力Ｔを加えたときに発生する電界密度Ｄは、圧電定数ｄ３３を用いて（１）式で表される。また、（１）式から、圧電定数ｄ３３は、（２）式で求められる。
　　　　　Ｄ＝ｄ３３×Ｔ　　　　　　　　　　　　　　　　　　　（１）
　　　　　ｄ３３＝Ｄ／Ｔ＝（Ｑ／Ａ）／（Ｆ／Ａ）＝Ｑ／Ｆ　　　（２）
ここで、Ｑは表面電荷（Ｃ）、Ａは電極面積（ｍ２）、Ｆは印加した交番力（Ｎ）である。
　製造した各試料１０の裏面に交番力Ｆを印加して、各試料１０の表面に取り付けた電極により、発生電荷Ｑを測定し、（２）式により圧電定数ｄ３３を求めた。測定には、圧電ｄ３３メーター（Sinocera Piezotronics INC.製「YE2730A」）を用いた。測定からは、正および負の圧電定数が得られるため、正の圧電定数と負の圧電定数との平均値を、圧電定数ｄ３３とした。求められた各試料１０の圧電定数ｄ３３を、図５に示す。
　図５に示すように、BTOの体積分率が一定の各試料１０では、P(VDF-TrFE)が負の圧電定数ｄ３３を有し、BTOが正の圧電定数ｄ３３を有するため、BTOの体積分率が 0 vol.%のときには、圧電定数ｄ３３が負であるが、BTOの体積分率が大きくなるに従って、圧電定数ｄ３３が負から正に大きくなっていく様子が確認された。また、BTOの体積分率が 10 vol.%程度のとき、圧電定数ｄ３３がゼロになることが確認された。
　また、図５に示すように、BTOの体積分率が徐々に変化する各試料（FGM1, FGM2, FGM3）１０では、BTOの平均体積分率が 30 vol.%であるにもかかわらず、圧電定数ｄ３３が負になっていることが確認された。FGM1では、BTOの体積分率が一定の 0 vol.%の試料１０とほぼ同じ大きさの負の圧電定数ｄ３３が得られ、FGM2およびFGM3では、FGM1よりさらに大きい負の圧電定数ｄ３３が得られることが確認された。これは、BTOの体積分率が徐々に変化する試料１０では、ホットプレス時に内部応力が発生することが影響している、すなわち内部応力が圧電セラミックと圧電ポリマーとを分極しやすくしていると考えられる。
　次に、BTOの体積分率が徐々に変化する各試料（FGM1, FGM2, FGM3）の比誘電率εγを、ＬＣＲメーター（株式会社エヌエフ回路設計ブロック社製「ZM2371」）を用いて測定した。その結果、各試料FGM1～3の比誘電率εγは、約17～18であった。
　以上の結果から、各試料FGM1～3の性能指数ＦｏＭ（figure of merit）を求めた。ＦｏＭは、d×g＝d2×εで求めることができる。ここで、dは圧電ひずみ定数、gは圧電電圧定数、εは誘電率である。ＦｏＭは、33モードでの圧電材料のエネルギー生成効率を表しており、ＦｏＭが大きいほど環境発電（エネルギーハーベスティング）効率が高くなる。各試料のＦｏＭは、FGM1が 279、FGM2が 402、FGM3が 551であった。このことから、各試料FGM1～3のうち、FGM3が最も環境発電効率が高いと考えられる。
［衝撃発電試験］
　BTOの体積分率が一定の30 vol.%の試料１０、および、BTOの体積分率が徐々に変化する各試料１０について、衝撃発電試験を行った。図６に示すように、試験では、各試料１０の表面をたたいたときの衝撃による発電量を調べるために、10 mm×20 mmの矩形状に切断した各試料１０を、キーボード１のエンターキー１ａに張り付け、エンターキー１ａを押したときの出力電圧（Output voltage）を、オシロスコープ（横河電機株式会社製「DL850E」）２により測定した。測定は、各試料に対して200回行い、その平均値を測定値とした。測定結果を、図７に示す。
　図７に示すように、BTOの体積分率が徐々に変化する各試料（FGM1, FGM2, FGM3）１０の方が、BTOの体積分率が一定の30 vol.%の試料１０と比べて、出力電圧が大きくなっており、発電量が大きいことが確認された。また、BTOの体積分率が徐々に変化する各試料１０の中でも、FGM3の出力電圧が特に大きく、BTOの体積分率が一定の30 vol.%の試料１０の約２倍の電力が得られることが確認された。
［振動発電試験］
　BTOの体積分率が一定の30 vol.%の試料１０、および、BTOの体積分率が徐々に変化する各試料１０について、振動発電試験を行った。図８に示すように、試験では、まず、40 mm×10 mmの矩形板状に切断した各試料１０の一端を、加振機（Labworks社製「ET-132」）３に取り付け、他端に1.5 gの錘４を取り付けた。ファンクションジェネレーター（株式会社ケンウッド製「FG-281」）５により、所望の周波数で各試料１０を振動させて、データロガー（株式会社キーエンス製「Keyence NR-500」）６により出力電圧を測定した。試験では、振幅を0.9 mmとし、周波数を 0～68 Hzの範囲で変化させて、各周波数での出力電圧（Output voltage）を測定した。測定結果を、図９に示す。
　図９に示すように、各試料１０とも、周波数が大きくなるに従って、出力電圧が大きくなっていることが確認された。例えば、周波数が68 Hzのときの各試料１０の出力電圧は、BTOの体積分率が一定の30 vol.%の試料１０が 0.973 mV、FGM1が 9.024 mV、FGM2が 2.374 mV、FGM3が 1.987 mVであった。また、BTOの体積分率が徐々に変化する試料１０のFGM1の出力電圧が非常に大きく、周波数が約30 Hz以上のとき、他の各試料１０の５～１０倍の電力が得られることが確認された。これは、FGM1では、厚みの中心面に対してBTOの体積分率が非対称であるため、振動したときに一方の表面（例えば、曲げの外側になる面）に発生する電荷と、他方の表面（例えば、曲げの内側になる面）に発生する電荷とが打ち消しあわず、出力電圧が大きくなったと考えられる。これに対し、他の各試料１０では、厚みの中心面に対してBTOの体積分率が対称であるため、振動したときに一方の表面に発生する電荷と、他方の表面に発生する電荷とが打ち消しあい、出力電圧が小さくなったと考えられる。
　本発明の実施の形態の発電用複合材料について、簡易的な有限要素解析モデルを用いて、圧縮応力誘起電圧に関する数値計算を行った。
　図１０（ａ）に示すように、発電用複合材料の有限要素解析モデルは、細長い棒状で、BTOとP(VDF-TrFE)とを含み、両端から中心に向かってBTOの体積分率が徐々に増加するパターン（実施例１のFGM3のパターン）を有しているものとした。また、有限要素解析モデルでは、BTOは球状とし、各位置でのBTOの半径を調節して、所望のBTOの体積分率が得られるようにした。表１乃至３に、有限要素解析に用いたPVDFの材料特性、BTOの材料特性、および、BTOの各体積分率（volume fraction）における半径（radius）をそれぞれ示す。
Figure JPOXMLDOC01-appb-T000001
Figure JPOXMLDOC01-appb-T000002
Figure JPOXMLDOC01-appb-T000003
　図１０（ｂ）に示すように、有限要素解析では、モデルの形状を、底面が１ｍｍ×１ｍｍで、高さが１２ｍｍの角柱状とし、モデルの下面（z=0）を固定した。また、x＝0、y＝０の側面に対称条件を用い、z＝0の電位ポテンシャルを0とした。また、有限要素解析では、BTOの体積分率の分布が、図１１（ａ）および（ｂ）に示す６つのパターンのモデルについて、図１０（ｂ）に示すように、各モデルの上面（z=h）に圧縮応力 P0=1 kPaを負荷したときの電位ポテンシャルの分布を求めた。また、その電位ポテンシャルの分布から、１ｋＰａの圧縮応力負荷によって生じる電位差を求めた。各モデルでのBTOの体積分率の分布を図１１（ａ）に、各モデルについて求められた電位差を図１１（ａ）および（ｂ）に示す。
　図１１（ａ）および（ｂ）に示す解析結果から、両端から中心に向かってBTOの体積分率が徐々に増加するパターン（実施例１のFGM3のパターン）であっても、BTOの体積分率の変化の仕方によって、出力電圧が異なることが確認された。例えば、BTOの体積分率を、端部よりも中心部で増加させた方が、発電量が大きくなることが予想される。また、全体的なBTOの体積分率が小さくても、中心に向かって急激にBTOの体積分率を増加させることにより、発電量が大きくなることが予想される。
　本発明の実施の形態の発電用複合材料の製造方法により発電用複合材料を製造し、実施例１と同様に、圧電定数の測定および発電試験を行った。
［発電用複合材料の製造］
　実施例１と同じ材料および装置を用いて、実施例１とは異なる工程で、図２のFGM1～3と同じ構造を有する３つの試料AFGC1～3を製造した。図１２に示すように、まず、粉末状のP(VDF-TrFE)を、溶媒のDMFに、P(VDF-TrFE)：DMF＝10：90の重量比で加え、撹拌器により、60℃で20分間撹拌（Stirring）した。その後、その溶液にBTOのナノ粒子（particle）を加え、撹拌機により室温で２時間撹拌（Stirring）し、さらに40℃で10分間、超音波（Ultrasonic）を照射して撹拌した。撹拌後の混合液を、スピンコート法により、直径４インチ、厚さ300 μmのシリコンウエハー上に薄く広げ、148℃のホットプレートで15分間加熱してDMF溶媒を蒸発させ、最下層の圧電薄膜１１を作製した。また、同様にして、作製した圧電薄膜１１の上に、順次、圧電薄膜１１を作製していくことにより、全部で12枚の圧電薄膜１１を積層した。なお、スピンコート法（Spin coating）では、各圧電薄膜１１の製造毎に、100 rpm/sec で加速させながら、500 rpm/secの回転速度で５秒間、1000 rpm/secの回転速度で５秒間回転させた後、-200 rpm/secで減速させた。
　全ての圧電薄膜１１を積層した後、148℃で４時間の熱処理を行った。熱処理後の各試料を、ウエハーと共に一晩、脱イオン水（Deionized water；ＤＩ水）に浸漬し、ウエハーから各試料を剥がして乾燥させた。こうして、AFGC1～3の各試料１０を製造した。製造された各試料AFGC1～3の厚みを、表４に示す。
Figure JPOXMLDOC01-appb-T000004
　なお、この製造方法では、作製した各圧電薄膜１１を１枚１枚積層する工程を省略することができ、比較的短い時間で効率よく発電用複合材料を製造することができる。また、処理後の各試料を、ウエハーと共に一晩、脱イオン水に浸漬することにより、最下層の圧電薄膜１１の収縮により壊れることなく、各試料１０をウエハーから剥がすことができる。
　表４に示すように、各試料AFGC1～3では、スピンコート法での溶液の蓄積により、端部の方が中央部よりも厚くなっている。このため、各試料AFGC1～3を使用する際には、各試料AFGC1～3の中央部から試験片を切り出した。
　製造した試料AFGC1～3の断面を、走査型電子顕微鏡で観察した結果を、それぞれ図１３（ａ）～（ｅ）に示す。図１３（ａ）～（ｃ）に示すように、各試料AFGC1～3とも、積層した圧電薄膜の境界が認められず、一体化しており、BTOの体積分率が徐々に変化している様子が確認された。また、図１３（ｄ）および（ｅ）に示すように、樹枝状に結晶化したP(VDF-TrFE)結晶の中に、BTOが埋め込まれており、P(VDF-TrFE)とBTOとが接合している様子が確認された。
［分極処理］
　実施例１と同様にして、製造した各試料AFGC1～3に圧電性を発現させるために、コロナ分極法により分極処理を行った。分極処理では、65℃、52 kV/mm2で、各試料の厚み方向に30分間分極した。
［圧電特性の測定］
　実施例１と同様にして、製造した各試料AFGC1～3の圧電定数ｄ３３および比誘電率εγを測定した。測定結果を、表４に示す。表４に示すように、圧電定数ｄ３３では、AFGC1が最も大きい負の値を有し、AFGC2およびAFGC3はほぼ同じ負の値を有していることが確認された。また、各試料AFGC1～3比誘電率εγは、11～14程度であることが確認された。各試料AFGC1～3の圧電定数ｄ３３の値を、図５に示す実施例１の各試料の圧電定数ｄ３３の値と比較すると、AFGC2およびAFGC3は、同じ構造を有するFGM2およびFGM3とほぼ同じ値であるのに対し、AFGC1は、同じ構造を有するFGM1の約1.6倍の値になっていることが確認された。これは、各試料の製造工程の違い、すなわち、ホットプレス工程の有無や、実施例１の試料FGM1の製造時のホットプレスでの熱伝達の均一性によるものと考えられる。
　以上の結果から、実施例１と同様に、各試料AFGC1～3の性能指数ＦｏＭを求めた。各試料のＦｏＭは、AFGC1が 884、AFGC2が 593、AFGC3が 679であった。これらのＦｏＭの値を、実施例１の各試料FGM1～3のＦｏＭの値と比較すると、各試料AFGC1～3の方が、それぞれ対応する構造を有する各試料FGM1～3よりも大きくなっていることが確認された。このことから、各試料AFGC1～3の方が、各試料FGM1～3よりも環境発電効率が高いと考えられる。また、各試料AFGC1～3のうち、AFGC1のＦｏＭが最も大きく、AFGC1が最も環境発電効率が高いと考えられる。
［振動発電試験］
　実施例１と同様にして、試料AFGC1について、振動発電試験を行った。試験は、試料AFGC1の長さを30 mmとした以外は、図８と同様の装置で行った。試験では、振幅が0.9 mm、周波数が 10～50 Hzの正弦波振動を用い、各周波数での出力電圧（Output voltage）を測定した。なお、実施例１で作製した試料FGM1についても、同様に測定を行った。測定結果を、図１４に示す。
　図１４に示すように、各試料AFGC1、FGM1（図中では、FGC1と記載）とも、出力電圧のピークが認められ、そのときの共振周波数がいずれも約23 Hzであることが確認された。また、共振周波数での出力電圧が、試料AFGC1では約91 mVであり、試料FGM1の出力電圧（約9 mV）の約10倍であることが確認された。これは、各試料AFGC1、FGM1の製造方法の違いによるものと考えられ、試料AFGC1では、試料FGM1よりも、各圧電薄膜１１が強固に接合され、分極が容易であり、圧電性が改善されたためであると考えられる。
　試料AFGC1の耐久性を調べるために、振動発電試験の装置を用い、振幅0.9 mm、周波数25 Hzで振動させて、200000サイクルまで、50000サイクル（2000秒）毎に５秒間（125サイクル）、出力電圧（Real-time output voltage）の測定を行った。測定結果を、図１５（ａ）および（ｂ）に示す。図１５に示すように、200000サイクル後であっても、出力電圧が低下していないことが確認された。このことから、試料AFGC1は、優れた耐久性を有しているといえる。
　　１　キーボード
　　　１ａ　エンターキー
　　２　オシロスコープ
　　３　加振機
　　４　錘
　　５　ファンクションジェネレーター
　　６　データロガー
 
　　１０　（発電用複合材料の）試料
　　１１　圧電薄膜

 

Claims (15)

  1. 　圧電性を有するセラミックと、圧電性を有するポリマーとを含み、所定の方向に沿って前記セラミックの含有率が連続的に徐々に変化するよう構成されていることを特徴とする発電用複合材料。
  2. 　前記所定の方向に沿って、前記セラミックの含有率が連続的に徐々に増加または減少するよう構成されていることを特徴とする請求項１記載の発電用複合材料。
  3. 　前記所定の方向に沿った前記セラミックの含有率の分布が、前記所定の方向での中心面に対して面対称を成すよう構成されていることを特徴とする請求項１記載の発電用複合材料。
  4. 　前記所定の方向に沿って、前記セラミックの含有率が増加する範囲と減少する範囲とを有するよう構成されていることを特徴とする請求項１記載の発電用複合材料。
  5. 　前記セラミックは、ペロブスカイト構造を有していることを特徴とする請求項１乃至４のいずれか１項に記載の発電用複合材料。
  6. 　前記セラミックは、チタン酸バリウム（ＢａＴｉＯ３；ＢＴＯ）、ニオブ酸カリウムナトリウム［(Ｋ,Ｎａ)ＮｂＯ３；ＫＮＮ］、チタン酸ビスマスナトリウム［（Ｂｉ１／２Ｎａ１／２）Ｔｉ３；ＢＮＴ］、および、ビスマスフェライト（ＢｉＦｅＯ３；ＢＦ）のうちの少なくとも１つ以上を含み、
    　前記ポリマーは、ポリフッ化ビニリデン（ＰＶＤＦ）、および、ポリフッ化ビニリデンと三フッ化エチレンとの共重合体であるＰ（ＶＤＦ－ＴｒＦＥ）のうち少なくともいずれか一方を含むことを
    　特徴とする請求項１乃至４のいずれか１項に記載の発電用複合材料。
  7. 　板状を成し、厚み方向が前記所定の方向であることを特徴とする請求項１乃至４のいずれか１項に記載の発電用複合材料。
  8. 　圧電性を有するセラミックと、圧電性を有するポリマーとを含み、前記セラミックの含有率が異なる複数種類の圧電薄膜を、その膜厚方向に沿って前記セラミックの含有率が徐々に変化するよう積層した後、熱処理を行うことを特徴とする発電用複合材料の製造方法。
  9. 　前記熱処理は、積層した各圧電薄膜をその膜厚方向に圧縮した状態で、各圧電薄膜の再結晶温度よりも低い温度で加熱することを特徴とする請求項８記載の発電用複合材料の製造方法。
  10. 　溶媒中に前記セラミックと前記ポリマーとを加えて撹拌した混合液を用いて、スピンコート法により各圧電薄膜を作製することを特徴とする請求項８記載の発電用複合材料の製造方法。
  11. 　各圧電薄膜を作製した後、各圧電薄膜を積層することを特徴とする請求項８乃至１０のいずれか１項に記載の発電用複合材料の製造方法。
  12. 　製造した圧電薄膜の上に、順次、圧電薄膜を作製していくことにより、各圧電薄膜を積層することを特徴とする請求項８乃至１０のいずれか１項に記載の発電用複合材料の製造方法。
  13. 　前記セラミックは、ペロブスカイト構造を有していることを特徴とする請求項８乃至１０のいずれか１項に記載の発電用複合材料の製造方法。
  14. 　前記セラミックは、チタン酸バリウム（ＢａＴｉＯ３；ＢＴＯ）、ニオブ酸カリウムナトリウム［(Ｋ,Ｎａ)ＮｂＯ３；ＫＮＮ］、チタン酸ビスマスナトリウム［（Ｂｉ１／２Ｎａ１／２）Ｔｉ３；ＢＮＴ］、および、ビスマスフェライト（ＢｉＦｅＯ３；ＢＦ）のうちの少なくとも１つ以上を含み、
    　前記ポリマーは、ポリフッ化ビニリデン（ＰＶＤＦ）、および、ポリフッ化ビニリデンと三フッ化エチレンとの共重合体であるＰ（ＶＤＦ－ＴｒＦＥ）のうち少なくともいずれか一方を含むことを
    　特徴とする請求項８乃至１０のいずれか１項に記載の発電用複合材料の製造方法。
  15. 　各圧電薄膜を積層した積層体が板状を成し、厚み方向が前記積層体の積層方向であることを特徴とする請求項８乃至１０のいずれか１項に記載の発電用複合材料の製造方法。
     
PCT/JP2022/026157 2021-07-02 2022-06-30 発電用複合材料および発電用複合材料の製造方法 WO2023277118A1 (ja)