WO2023180757A1 - Encre d'impression - Google Patents

Encre d'impression Download PDF

Info

Publication number
WO2023180757A1
WO2023180757A1 PCT/GB2023/050750 GB2023050750W WO2023180757A1 WO 2023180757 A1 WO2023180757 A1 WO 2023180757A1 GB 2023050750 W GB2023050750 W GB 2023050750W WO 2023180757 A1 WO2023180757 A1 WO 2023180757A1
Authority
WO
WIPO (PCT)
Prior art keywords
ink
weight
monomer
inkjet
inkjet ink
Prior art date
Application number
PCT/GB2023/050750
Other languages
English (en)
Inventor
Gemma OSBORNE
Original Assignee
Fujifilm Speciality Ink Systems Limited
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fujifilm Speciality Ink Systems Limited filed Critical Fujifilm Speciality Ink Systems Limited
Publication of WO2023180757A1 publication Critical patent/WO2023180757A1/fr

Abstract

La présente invention concerne une encre pour jet d'encre comprenant de l'acrylate de benzyle, du diacrylate de polyéthylène Glycol 600 et un monomère de N-vinyl amide et/ou un monomère de N-(méth)acryloyle amine, l'encre ayant une viscosité inférieure à 15 mPas à 25 °C. La présente invention concerne en outre un procédé d'impression par jet d'encre comprenant l'impression par jet d'encre de l'encre pour jet d'encre sur un substrat et le durcissement de l'encre pour jet d'encre par exposition de l'encre pour jet d'encre à une source de durcissement.
PCT/GB2023/050750 2022-03-25 2023-03-24 Encre d'impression WO2023180757A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
GBGB2204258.4A GB202204258D0 (en) 2022-03-25 2022-03-25 Printing ink
GB2204258.4 2022-03-25

Publications (1)

Publication Number Publication Date
WO2023180757A1 true WO2023180757A1 (fr) 2023-09-28

Family

ID=81449543

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/GB2023/050750 WO2023180757A1 (fr) 2022-03-25 2023-03-24 Encre d'impression

Country Status (2)

Country Link
GB (1) GB202204258D0 (fr)
WO (1) WO2023180757A1 (fr)

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2011021052A2 (fr) 2009-08-21 2011-02-24 Sericol Limited Encre, appareil et procédé d'impression
EP3075753A1 (fr) * 2013-11-29 2016-10-05 Mitsubishi Rayon Co., Ltd. Copolymère (méth)acrylique, composition adhésive le contenant et feuille adhésive
EP3778802A1 (fr) * 2018-04-11 2021-02-17 Sakata INX Corporation Composition d'encre photocurcissable pour impression jet d'encre
WO2022214814A1 (fr) * 2021-04-08 2022-10-13 Fujifilm Speciality Ink Systems Limited Encre d'impression

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2011021052A2 (fr) 2009-08-21 2011-02-24 Sericol Limited Encre, appareil et procédé d'impression
EP3075753A1 (fr) * 2013-11-29 2016-10-05 Mitsubishi Rayon Co., Ltd. Copolymère (méth)acrylique, composition adhésive le contenant et feuille adhésive
EP3778802A1 (fr) * 2018-04-11 2021-02-17 Sakata INX Corporation Composition d'encre photocurcissable pour impression jet d'encre
WO2022214814A1 (fr) * 2021-04-08 2022-10-13 Fujifilm Speciality Ink Systems Limited Encre d'impression

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
CAS, no. 69701-99-1

Also Published As

Publication number Publication date
GB202204258D0 (en) 2022-05-11

Similar Documents

Publication Publication Date Title
WO2019077364A1 (fr) Encre d'impression
WO2018146495A1 (fr) Procédé d'impression et encre
US10144838B2 (en) Printing ink
WO2022090718A1 (fr) Encre d'impression
US10844234B2 (en) Method of printing
GB2593583A (en) A printing ink
WO2021152309A1 (fr) Encre pour jet d'encre
EP4320200A1 (fr) Encre d'impression
EP4334401A1 (fr) Encre d'impression
GB2593582A (en) A printing ink
GB2564485A (en) A printing ink
EP3858634A1 (fr) Procédé d'impression
US20230193063A1 (en) Inkjet ink
GB2594728A (en) A printing ink
WO2023180757A1 (fr) Encre d'impression
WO2023180756A1 (fr) Encre d'impression
WO2019193359A1 (fr) Encre d'impression
WO2023105207A1 (fr) Encre d'impression
WO2023105206A1 (fr) Encre d'impression
WO2023156771A1 (fr) Encre pour jet d'encre
WO2018042194A1 (fr) Procédé d'impression
EP4347727A1 (fr) Encre d'impression
US20230203331A1 (en) Method of inkjet printing
GB2569628A (en) A printing ink
GB2593797A (en) A method of printing

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 23715906

Country of ref document: EP

Kind code of ref document: A1

DPE1 Request for preliminary examination filed after expiration of 19th month from priority date (pct application filed from 20040101)