WO2019193359A1 - Encre d'impression - Google Patents

Encre d'impression Download PDF

Info

Publication number
WO2019193359A1
WO2019193359A1 PCT/GB2019/050996 GB2019050996W WO2019193359A1 WO 2019193359 A1 WO2019193359 A1 WO 2019193359A1 GB 2019050996 W GB2019050996 W GB 2019050996W WO 2019193359 A1 WO2019193359 A1 WO 2019193359A1
Authority
WO
WIPO (PCT)
Prior art keywords
ink
acrylate
vinyl
meth
jet
Prior art date
Application number
PCT/GB2019/050996
Other languages
English (en)
Inventor
Gemma OSBORNE
Sean Slater
Original Assignee
Fujifilm Speciality Ink Systems Limited
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fujifilm Speciality Ink Systems Limited filed Critical Fujifilm Speciality Ink Systems Limited
Publication of WO2019193359A1 publication Critical patent/WO2019193359A1/fr

Abstract

La présente invention concerne une encre pour jet d'encre comprenant : un N-vinylamide, un monomère de N-acryloylamine et/ou un N-vinylcarbamate ; un isopropylidène-(méth)acrylate de glycérol ; éventuellement un photo-initiateur radicalaire ; et éventuellement un pigment dispersé. L'encre est appropriée pour des applications de viscosité ultra-basse.
PCT/GB2019/050996 2018-04-05 2019-04-05 Encre d'impression WO2019193359A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
GB1805694.5 2018-04-05
GBGB1805694.5A GB201805694D0 (en) 2018-04-05 2018-04-05 Printing ink

Publications (1)

Publication Number Publication Date
WO2019193359A1 true WO2019193359A1 (fr) 2019-10-10

Family

ID=62202891

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/GB2019/050996 WO2019193359A1 (fr) 2018-04-05 2019-04-05 Encre d'impression

Country Status (2)

Country Link
GB (1) GB201805694D0 (fr)
WO (1) WO2019193359A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN115298272A (zh) * 2020-03-31 2022-11-04 阪田油墨股份有限公司 光固化型喷墨印刷用油墨组合物

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2015022228A1 (fr) * 2013-08-12 2015-02-19 Basf Se Encre d'impression par jet d'encre contenant de la n-vinyloxazolidinone
US20150130878A1 (en) * 2013-11-14 2015-05-14 Shizuka KOHZUKI Active energy ray-curable inkjet ink, ink container, and inkjet discharging device
US20160046777A1 (en) * 2013-03-28 2016-02-18 Seiren Co., Ltd. Decorative film for insert molding and decorative insert molded article
EP3067396A1 (fr) * 2015-03-10 2016-09-14 Seiko Epson Corporation Composition durcissable aux ultraviolets et objet enregistré
WO2016193728A1 (fr) * 2015-06-02 2016-12-08 Fujifilm Speciality Ink Systems Limited Encre d'impression
US20170233594A1 (en) * 2016-02-12 2017-08-17 Seiko Epson Corporation Radiation curable ink jet composition and ink jet recording method

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20160046777A1 (en) * 2013-03-28 2016-02-18 Seiren Co., Ltd. Decorative film for insert molding and decorative insert molded article
WO2015022228A1 (fr) * 2013-08-12 2015-02-19 Basf Se Encre d'impression par jet d'encre contenant de la n-vinyloxazolidinone
US20150130878A1 (en) * 2013-11-14 2015-05-14 Shizuka KOHZUKI Active energy ray-curable inkjet ink, ink container, and inkjet discharging device
EP3067396A1 (fr) * 2015-03-10 2016-09-14 Seiko Epson Corporation Composition durcissable aux ultraviolets et objet enregistré
WO2016193728A1 (fr) * 2015-06-02 2016-12-08 Fujifilm Speciality Ink Systems Limited Encre d'impression
US20170233594A1 (en) * 2016-02-12 2017-08-17 Seiko Epson Corporation Radiation curable ink jet composition and ink jet recording method

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN115298272A (zh) * 2020-03-31 2022-11-04 阪田油墨股份有限公司 光固化型喷墨印刷用油墨组合物
CN115298272B (zh) * 2020-03-31 2023-12-22 阪田油墨股份有限公司 光固化型喷墨印刷用油墨组合物

Also Published As

Publication number Publication date
GB201805694D0 (en) 2018-05-23

Similar Documents

Publication Publication Date Title
WO2019077364A1 (fr) Encre d'impression
WO2018146494A1 (fr) Procédé d'impression et encre
WO2018146495A1 (fr) Procédé d'impression et encre
EP3303488B1 (fr) Encre d'impression
GB2562169A (en) Printing ink
GB2561984A (en) Printing ink
US10844234B2 (en) Method of printing
WO2022090718A1 (fr) Encre d'impression
EP3209736B1 (fr) Encre d'impression
GB2573207A (en) A printing ink
US20220389249A1 (en) Printing ink
WO2019193359A1 (fr) Encre d'impression
GB2564485A (en) A printing ink
WO2015140539A1 (fr) Encre d'impression
US20230193063A1 (en) Inkjet ink
WO2022214814A1 (fr) Encre d'impression
GB2594728A (en) A printing ink
GB2569628A (en) A printing ink
US20230203331A1 (en) Method of inkjet printing
WO2018078355A1 (fr) Encre d'impression
WO2018042194A1 (fr) Procédé d'impression
US20220411652A1 (en) Printing ink
GB2609555A (en) Printing ink
WO2023180756A1 (fr) Encre d'impression
WO2023180757A1 (fr) Encre d'impression

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 19717581

Country of ref document: EP

Kind code of ref document: A1

DPE1 Request for preliminary examination filed after expiration of 19th month from priority date (pct application filed from 20040101)
WA Withdrawal of international application
NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 19717581

Country of ref document: EP

Kind code of ref document: A1