WO2023101052A1 - 해조류를 포함하는 펄프몰드 및 그 제조방법 - Google Patents

해조류를 포함하는 펄프몰드 및 그 제조방법 Download PDF

Info

Publication number
WO2023101052A1
WO2023101052A1 PCT/KR2021/018062 KR2021018062W WO2023101052A1 WO 2023101052 A1 WO2023101052 A1 WO 2023101052A1 KR 2021018062 W KR2021018062 W KR 2021018062W WO 2023101052 A1 WO2023101052 A1 WO 2023101052A1
Authority
WO
WIPO (PCT)
Prior art keywords
seaweed
pulp
raw material
mold
material solution
Prior art date
Application number
PCT/KR2021/018062
Other languages
English (en)
French (fr)
Inventor
차완영
Original Assignee
주식회사 마린이노베이션
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 마린이노베이션 filed Critical 주식회사 마린이노베이션
Priority to US18/257,347 priority Critical patent/US20240011224A1/en
Priority to PCT/KR2021/018062 priority patent/WO2023101052A1/ko
Publication of WO2023101052A1 publication Critical patent/WO2023101052A1/ko

Abstract

본 발명은 해조류 부산물을 포함하는 펄프몰드 및 그 제조방법에 관한 것이다. 본 발명에 따른 해조류 부산물을 포함하는 펄프몰드 및 그 제조방법은 사과박 및/또는 녹차박을 이용하여 펄프몰드를 제조함으로써, 생분해성 친환경 소재인 해조류를 포함하고 사과박 및/또는 녹차박을 첨가하여 천연 항균 및 항충 기능을 가지는 효과가 있다.

Description

해조류를 포함하는 펄프몰드 및 그 제조방법
본 발명은 해조류 부산물에 사과박 또는 녹차박을 포함하는 펄프몰드 및 그제조방법에 관한 것이다.
펄프몰드는 목재펄프 또는 신문지, 골판지 등의 재생펄프를 물에 풀어 균일한 지료를 조성하고 이러한 지료를 상형과 하형의 금형에서 흡수되면서 지료내 펄프섬유들이 일정 구조를 형성하도록 성형하고 이를 건조하여 제조된 친환경 포장재료이다. 생분해성 펄프자원으로 만들어지는 완충성 소재이기 때문에 스티로폼 등의 화석원료 기반 포장소재를 대체할 수 있는 친환경 포장소재로서 그 수요가 지속적으로 증가되고 있다. 실제 온라인 기반 쇼핑확대로 인한 택배물품의 증가와 1~2인의 소가구가 주요 경제주체로 변화면서 소포장의 증대로 친환경적이고 재활용성이 우수한 포장소재에 대한 수요는 더욱 높아질 것으로 기대되고 있다.
일반적으로, 수용 공간을 포함하는 삼차원 형상의 몰드는 목재를 원료로 하는 종이 펄프를 성형함에 따라 제작된다. 그러나, 나무를 원료로 하기 때문에 벌목으로 인한 자연 훼손의 문제가 있다. 이러한 문제점을 해결하기 위하여, 대한민국등록특허공보 제10-1847039호에서 우뭇가사리를 이용한 펄프의 제조방법을 제시하였다. 상기 방법은 우뭇가사리를 사용하여 펄프를 제조하는 것에 있어서는 구체적인 방법을 제시하지만, 몰드를 제조하는 과정에 대해서는 제시하는 바가 없다. 그러나, 일반적인 몰드 제조의 방법으로는 우뭇가사리(해조류) 펄프의 섬유가 수분 흡수율이 높기 때문에 몰드를 제조할 수 없다는 문제점이 발견되었다.
또한 항균, 항바이러스, 항진균성과 같은 기능성 소재에 대한 요구가 증대됨에 따라 기능성을 가지는 친환경 소재의 활용도 주목받고 있다. 대표적으로 귤, 오렌지, 사과 등 과일을 활용할 수 있다. 구체적으로 대한민국 등록특허공보 제10-1442502호와 같이 과일류 껍질을 이용한 종이의 제조방법을 제공하고 있다.
과일류의 착즙 후 대량으로 발생되는 사과박, 감귤박 등의 경우 유기성폐기물로 주로 해양투기 방식으로 처리되었으나 해양투기가 금지된 이후 그 처리방안의 확보에 많은 비용과 어려움이 커지고 있다. 현재 퇴비나 매립하는 방안 등이 적용되고 있으나 발생되는 폐기물의 처리에 한계가 있고 처리비용의 부담이 커지고 있어서 적정한 활용방안의 확보가 시급한 상황이다.
과일박은 착즙과정을 통해 과육쥬스가 만들어진 후 발생되기 때문에 함수율이 약 80~85%인 상태로 배출되며, 착즙되지 않고 남은 즙을 포함하여 섬유상 과육과 과피 등으로 이루어져 있어서, 다양한 과일류의 기능성 성분을 포함하고 있다. 항균제, 항바이러스제, 항진균제 등을 포함할 수 있으며, 처리비용이 증가되면서 기능성 물질을 포함한 사과박의 자원적 가치를 극대화하기 위한 다양한 활용기술들이 개발되고 있다.
또한 녹차박은 차를 내린 후 발생되기 때문에 함수율이 약 80~85%인 상태로 배출되며, 우려지지 않고 남은 즙을 포함한 섬유상에 다양한 기능성 성분을 포함하고 있다. 카테킨과 같은 항균제, 항바이러스제, 항진균제 등을 포함할 수 있으며,처리비용이 증가되면서 기능성 물질을 포함한 녹차박의 자원적 가치를 극대화하기 위한 다양한 활용기술들이 개발되고 있다. 배출되며, 우려지지 않고 남은 즙을 포함한 섬유상에 다양한 기능성 성분을 포함하고 있다. 카테킨과 같은 항균제, 항바이러스제, 항진균제 등을 포함할 수 있으며, 처리비용이 증가되면서 기능성 물질을 포함한 녹차박의 자원적 가치를 극대화하기 위한 다양한 활용기술들이 개발되고 있다.
해조류 펄프의 높은 수분 흡수율과 과일박 또는 녹차박의 항균성을 고려하여 몰드를 제조하는 방법이 요구된다.
본 발명은 상기와 같은 필요를 해결하기 위하여, 해조류 부산물 및 사과박 및/또는 녹차박을 포함하는 펄프몰드 및 그 제조방법을 제공하는 것을 목적으로 한다.
상기 목적을 달성하기 위하여 본 발명은,
해조 슬러지로부터 이물질을 걸러내고 해조류 섬유분 원료액을 준비하는 제1단계;
사과박 섬유분을 분리하여 상기 해조류 섬유분 원료액에 투입하는 제2단계;
상기 사과박 섬유분이 투입된 원료액을 교반하여 펄프화하는 제3단계; 및
상기 펄프화된 펄프를 이용하여 몰드를 제조하는 제4단계;를 포함하는 해조류를 포함하는 펄프몰드 제조방법을 제공한다.
상기 목적을 달성하기 위하여 본 발명은,
해조 슬러지로부터 이물질을 걸러내고 해조류 섬유분 원료액을 준비하는 제1단계;
녹차박 섬유분을 분리하여 상기 해조류 섬유분 원료액에 투입하는 제2단계;
상기 녹차박 섬유분이 투입된 원료액을 교반하여 펄프화하는 제3단계; 및
상기 펄프화된 펄프를 이용하여 몰드를 제조하는 제4단계;를 포함하는 해조류를 포함하는 펄프몰드 제조방법을 제공한다.
상기 목적을 달성하기 위하여 본 발명은,
해조 슬러지로부터 이물질을 걸러내고 해조류 섬유분 원료액을 준비하는 제1단계;
사과박 및 녹차박 섬유분을 분리하여 상기 해조류 섬유분 원료액에 투입하는제2단계;
상기 사과박 및 녹차박 섬유분이 투입된 원료액을 교반하여 펄프화하는 제3단계; 및
상기 펄프화된 펄프를 이용하여 몰드를 제조하는 제4단계;를 포함하는 해조류를 포함하는 펄프몰드 제조방법을 제공한다.
또한 본 발명에 따라 제조되는 것을 특징으로 하는 해조류를 포함하는 펄프몰드을 제공한다.
해조류 부산물을 포함하는 펄프몰드 및 그 제조방법은 사과박 및/또는 녹차박을 이용하여 펄프몰드를 제조함으로써, 생분해성 친환경 소재인 해조류를 포함하고 사과박 및/또는 녹차박을 첨가하여 천연 항균 및 항충 기능을 가지는 효과가 있다.
이하 본 발명에 대하여 보다 상세히 설명한다.
본 발명의 일측면에 따르면 해조 슬러지로부터 이물질을 걸러내고 해조류 섬유분 원료액을 준비하는 제1단계; 사과박 섬유분을 분리하여 상기 해조류 섬유분 원료액에 투입하는 제2단계; 상기 사과박 섬유분이 투입된 원료액을 교반하여 펄프화하는 제3단계; 및 상기 펄프화된 펄프를 이용하여 몰드를 제조하는 제4단계;를 포함하는 해조류를 포함하는 펄프몰드 제조방법을 제공한다.
본 발명의 다른 일 측면에 따르면, 해조 슬러지로부터 이물질을 걸러내고 해조류 섬유분 원료액을 준비하는 제1단계; 녹차박 섬유분을 분리하여 상기 해조류 섬유분 원료액에 투입하는 제2단계; 상기 녹차박 섬유분이 투입된 원료액을 교반하여 펄프화하는 제3단계; 및 상기 펄프화된 펄프를 이용하여 몰드를 제조하는 제4단계;를 포함하는 해조류를 포함하는 펄프몰드 제조방법을 제공한다.
본 발명의 또 다른 일 측면에 따르면, 해조 슬러지로부터 이물질을 걸러내고 해조류 섬유분 원료액을 준비하는 제1단계; 사과박 및 녹차박 섬유분을 분리하여 상기 해조류 섬유분 원료액에 투입하는 제2단계; 상기 사과박 및 녹차박 섬유분이 투입된 원료액을 교반하여 펄프화하는 제3단계; 및 상기 펄프화된 펄프를 이용하여 몰드를 제조하는 제4단계;를 포함하는 해조류를 포함하는 펄프몰드 제조방법을 제공한다.
펄프를 준비하는 단계는 슬러지 필터링 공정, 펄프화 공정 및 펄프 필터링 공정을 포함할 수 있다.
본 발명의 해조 슬러지는 우뭇가사리(agar-agar, ceylon moss), 꼬시래기(sea string), 미역, 및 다시마 중 하나 이상을 포함할 수 있다. 해조 슬러지는 연질화를 거친 해조류 원료일 수 있다. 해조 슬러지는 연질화된 해조류 원료로부터 식품으로 쓰이는 추출물이 빠진 나머지일 수 있다. 해조 슬러지는 정제되지 않은 상태임으로 이물질을 포함할 수 있다.
슬러지 필터링 공정은 이물질을 포함하는 해조 슬러지를 필터 장치에서 이물질을 걸러내어 펄프 원료액을 추출할 수 있다. 입자가 큰 이물질들이 걸러내진 펄프 원료액은 자잘한 해조류 원료들(우뭇가사리, 꼬시래기, 미역, 다시마 등등)을 포함할 수 있다. 해조류 원료들은 껍질이 벗겨지지 않은 상태일 수 있다. 슬러지 필터링 공정에서 걸러내어진 펄프 원료액은 펄프화 공정을 위하여 펄프화 장치의 내부에 수용될 수 있다.
본 발명에 따라 투입되는 사과박 또는 녹차박은 조대물질을 분급처리하고 섬유분을 분리하여 투입될 수 있다. 사과박 또는 녹차박을 그대로 펄프몰드로 제조하는 경우 고루 분포되지 못한 덩어리들이 뭉쳐서 나타날 수 있다. 조대한 입자를 가지는 과피, 과육섬유분, 미세입자를 크기별로 분급하는 과정을 포함하여 메쉬를 기준으로 분급하여 기계적 해섬 처리를 실시함이 바람직하다. 해섬처리는 니더, PFI밀(mill), 콜로이드밀, 롤밀, 해쇄기, 리파이너, 제트 분쇄기, 균질화기 등을 적용하여 해섬처리 할 수 있다. 나아가 해섬 전처리와 분급을 통해 얻어진 사과박 섬유분을 일정 무게비로 투입하여 펄프 몰드를 제조함에 따라 공정 문제의 발생을 예방함이 바람직하다.
본 발명의 사과박은 플라보노이드와 같은 성분을 포함하여 항균, 항바이러스, 항진균성을 확보할 수 있다.
본 발명의 녹차박은 항균, 항바이러스, 항진균성을 확보할 수 있다. 녹차(Camellia sinensis)는 동백나무과의 상록관록으로 녹차에는 카테킨(catechin), 플라보노이드(flavonoid), 데아닌(theanine), 카페인(caffeine) 및 타닌(tannin) 등과 각종 비타민(vitamin)이 함유되어 있어 항균, 소취, 산폐 방지 및 미생물 생육 억제 기능을 부여할 수 있다.
본 발명의 펄프 원료액은 해조류, 사과박 외 식물성 부산물을 더 포함할 수 있다. 구체적으로 코코넛 껍질, 곡물 껍질, 커피 가루와 같은 부산물일 수 있고, 곡물은 쌀, 보리, 콩, 팥, 조, 깨, 밀, 중, 옥수수 등일 수 있다.
펄프화 공정은 펄프화 장치 내부에 수용된 펄프 원료액을 교반함으로써, 펄프화하여 펄프를 형성할 수 있다. 펄프화는 해조류를 추출한 후 펄프성분인 섬유분원료에 추가로 투입되는 사과박 또는 녹차박의 섬유분을 균일한 농도로 퍼트리며 액상(예를 들어, 물)에 고르게 퍼지도록 할 수 있다.
펄프화 공정에서 펄프 원료액이 펄프화를 촉진시키기 위하여, 펄프 원료액의해조류들을 절단하는 과정이 추가될 수 있다. 구체적으로 해조 슬러지를 5 ~ 20 mm로 절단하여 이용될 수 있다. 종래에 개발된 홍조류(해조류) 펄프는 섬유의 길이가 짧아서 종이를 제조하기에 적합하지 않다. 이에 따라, 하기에 설명된 본원 발명의 해조류를 포함하는 펄프몰드 제조 방법은 해조류 펄프의 섬유의 길이를 조절하기 위한 과정들을 포함하는 점에 특징이 있다. 길이가 5mm보다 짧으면 몰드 공정에서 몰드 형성에 장애가 되고, 20mm보다 길면 원료액을 펄프화하는 속도가 느려지는 문제가 발생할 수 있다.
펄프화를 위하여 펄프 원료액을 교반시키는 프로펠러가 펄프화 장치의 내부에 배치될 수 있다. 펄프 원료액은 운동 에너지를 받아 난류를 형성할 수 있다. 펄프 원료액을 교반 시키는 프로펠러의 회전 속도가 느릴 수록 펄프 원료액의 펄프화 속도가 낮아질 수 있다. 프로펠러의 회전 속도는 20 rpm 내지 50rpm으로 설정될 수 있다. 또한, 펄프화를 촉진하기 위하여, 펄프화 장치의 내부로 열과 압력을 가할 수 있다. 가해지는 열 에너지가 작을수록 펄프 원료액의 펄프화 속도가 낮아질 수 있고, 열 에너지가 클수록 펄프 원료액의 해조류가 절단되는 경우가 증가되어 해조류의 길이가 짧아질 수 있다. 가해지는 압력이 낮을수록 펄프 원료액이 해조류 펄프로 펄프화 되는 속도가 낮아질 수 있고, 가해지는 압력이 높을수록 펄프 원료액의 해조류가 얇아져서 절단되는 경우가 증가되어 해조류의 길이가 짧아질 수 있다. 이를 고려하여, 열과 압력의 범위가 설정함이 바람직하다.
또한 원료액에 화학적 촉매제 등을 가하여 펄프의 형성을 촉진할 수 있다. 화학적 촉매제로 과산화수소 및 가성소다 등을 가할 수 있다. 부가적으로 해조류 펄프를 하얗게 만들기 위한 표백 공정이 추가될 수 있다. 펄프화 공정 및 표백 공정이 다수 회 반복될 수록 하얗고 순수한 펄프를 얻을 수 있으나, 해조류 펄프의 섬유 길이가 짧아질 수 있다.
또한 수분 함량이 높은 해조류를 가공하기 위하여 수분 함유량을 측정하고 조절하는 공정을 더 포함할 수 있다. 펄프액의 농도가 성형되기에 적합한 상태인지를 확인하여 균일한 두께의 몰드나 정교한 형상의 몰드를 구현함이 바람직하다. 펄프액의 적정 수분 함유량은 30 ~ 50%인 것이 바람직하다. 수분 함유량을 조절하기 위하여 장치에 열을 가하여 수분을 증발시키거나 탈수시키거나 펄프액 또는 물을 추가로 가할 수 있다.
이후 펄프는 추가 공정을 통하여 몰드로 제조될 수 있다. 몰드 금형(성형장치)에 펄프액을 체우고 압력을 가하여 펄프몰드를 생성할 수 있다. 성형 장치는 하부 금형 및 상부 금형을 포함할 수 있다. 성형 공정은 습식 성형 공정 및 건식 성형 공정 중 하나 이상을 포함할 수 있다. 습식 성형 공정과 건식 성형 공정은 하부 금형에 펄프액이 채워지는 방식이 서로 상이할 수 있다. 습식 성형 공정은 펄프액이 채워진 액조에 하부 금형이 잠기었다가 수직으로 상승하여 하부 금형에 펄프액을 채울 수 있다. 건식 성형 공정은 하부 금형에 직접 펄프액을 부어 넣을 수 있다.
본 발명의 다른 일측면에 따르면 본 발명에 따라 제조되는 것을 특징으로 하는 해조류를 포함하는 펄프몰드를 제공한다. 본 발명의 해조류를 포함하는 펄프몰드는 친환경 소재를 이용함에 따라 생분해성을 가지고, 펄프화 공정 전 해조 슬러지의 길이, 사과박 또는 녹차박 조대물질의 분급처리에 따라 일정한 표면을 확보할 수 있다. 나아가 수분함유량이 높은 해조류를 포함하여 펄프의 겔화가 방지되어 온전한 형태의 몰드를 형성하고, 사과박 또는 녹차박을 포함하여 항균, 항바이러스 기능을 확보함에 특징이 있다.
전술한 내용은 후술할 발명의 청구범위를 더욱 잘 이해할 수 있도록 본 발명의 특징과 기술적 장점을 다소 폭넓게 상술하였다. 본 발명이 속하는 기술분야의 통상의 지식을 가진 자는 본 발명이 그 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시예들은 모든 면에서 예시적인 것이며 한정적이 아닌 것으로 이해해야만 한다. 본 발명의 범위는 상기 상세한 설명보다는 후술하는 특허청구범위에 의하여 나타내어지며, 특허청구범위 그리고 그 균등 개념으로부터 도출되는 모든 변경 또는 변형된 형태가 본 발명의 범위에 포함되는 것으로 해석되어야 한다.

Claims (6)

  1. 해조 슬러지로부터 이물질을 걸러내고 해조류 섬유분 원료액을 준비하는 제1단계;
    사과박 섬유분을 분리하여 상기 해조류 섬유분 원료액에 투입하는 제2단계;
    상기 사과박 섬유분이 투입된 원료액을 교반하여 펄프화하는 제3단계; 및
    상기 펄프화된 펄프를 이용하여 몰드를 제조하는 제4단계;를 포함하는 해조
    류를 포함하는 펄프몰드 제조방법.
  2. 해조 슬러지로부터 이물질을 걸러내고 해조류 섬유분 원료액을 준비하는 제1단계;
    녹차박 섬유분을 분리하여 상기 해조류 섬유분 원료액에 투입하는 제2단계;
    상기 녹차박 섬유분이 투입된 원료액을 교반하여 펄프화하는 제3단계; 및
    상기 펄프화된 펄프를 이용하여 몰드를 제조하는 제4단계;를 포함하는 해조류를 포함하는 펄프몰드 제조방법.
  3. 해조 슬러지로부터 이물질을 걸러내고 해조류 섬유분 원료액을 준비하는 제1단계;
    사과박 및 녹차박 섬유분을 분리하여 상기 해조류 섬유분 원료액에 투입하는 제2단계;
    상기 사과박 및 녹차박 섬유분이 투입된 원료액을 교반하여 펄프화하는 제3단계; 및
    상기 펄프화된 펄프를 이용하여 몰드를 제조하는 제4단계;를 포함하는 해조류를 포함하는 펄프몰드 제조방법.
  4. 제1항 내지 제3항 중 어느 한 항에 있어서,
    상기 해조 슬러지는 우뭇가사리, 꼬시래기, 미역 및 다시마 중 하나 이상을 포함하는 해조류를 포함하는 펄프몰드 제조방법.
  5. 제1항 내지 제3항 중 어느 한 항에 있어서,
    상기 제1단계는 상기 해조 슬러지를 5 ~ 20 mm로 절단하는 단계를 더 포함하는 것을 특징으로 하는 해조류를 포함하는 펄프몰드 제조방법.
  6. 제1항 내지 제3항 중 어느 한 항에 따라 제조되는 것을 특징으로 하는 해조류를 포함하는 펄프몰드.
PCT/KR2021/018062 2021-12-02 2021-12-02 해조류를 포함하는 펄프몰드 및 그 제조방법 WO2023101052A1 (ko)