WO2023090478A1 - 하이브리드 그래핀 전극 - Google Patents
하이브리드 그래핀 전극 Download PDFInfo
- Publication number
- WO2023090478A1 WO2023090478A1 PCT/KR2021/016913 KR2021016913W WO2023090478A1 WO 2023090478 A1 WO2023090478 A1 WO 2023090478A1 KR 2021016913 W KR2021016913 W KR 2021016913W WO 2023090478 A1 WO2023090478 A1 WO 2023090478A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- graphene
- electrode
- hybrid
- composite
- microparticles
- Prior art date
Abstract
본 발명은 복수 개의 미세입자(Micro Particle)와 다층 그래핀이 혼합된 구조를 가지는 그래핀 복합체를 구성하되, 상기 미세입자는 금속 또는 반도체 입자이며, 상기 다층 그래핀 표면 또는 내부에 결착되며, 일부 미세입자는 상호 결합응고되고,상기 다층 그래핀은 여러 층의 그래핀이 적층되고 임의의 방향으로 굽혀져 있는 3차원 구조를 가지고,상기 미세입자 사이 빈 공간의 일부는 상기 다층 그래핀이 채워져 상호 연결된 구조로,상기 그래핀 복합체를 통하여 전자의 흐름이 발생하는 하이브리드 그래핀 전극에 관한 것이다.
Description
본 발명은 하이브리드 그래핀 전극에 관한 것으로, 보다 자세하게는 미세입자와 그패핀의 가교결합에 의한 3차원 구조 형성 및 이러한 구조적 특징에 의한 높은 전기 전도성 특성으로, 저농도의 항원에 대해 선택성 및 특이성이 우수하고, 특히 치매 특이항원의 검출을 위한 면역센서에 최적화된 치매 특이항원 하이브리드 그래핀 전극에 관한 것이다.
그래핀은 전기적, 기계적, 화학적 특성이 매우 안정적이고 뛰어날 뿐만 아니라 우수한 전도성 물질로서 실리콘 보다 약 100 배 빠르게 전자를 이동시키며 구리보다도 약 100 배 가량 더 많은 전류를 흐르게 할 수 있는 물질로서, 이의 제조 및 응용에 관한 연구가 활발하게 진행되고 있다.
이를 응용한 바이오센서로 항원-항체 결합을 기반으로하는 면역센서에 활용될 수 있다. 면역센서는 바이오마커와 같이 임상진단에서 질병과 관련된 물질을 감지하는데 널리 사용되고 있다. 항원에 대한 항체의 특이결합에 때문에 항체는 특히 바이오마커를 검출하기위해 면역센서의 표면 등에 고정되어 이용된다.
예를 들어 전립선 암 마커(marker)로서 전립선 특이항원(prostate specific anteigen, PSA)는 전립선 암의 스크리닝, 진단 및 치료에 널리 이용된다. 전립선 특이항원은 전립선의 상피세포에서 합성되어 분비되는 효소로서 일반인의 경우 0~4 ng/㎖으로 측정되나 전립선 암 환자에서는 농도가 더 높게 측정된다. 따라서, 전립선 특이항원에 대한 선택성, 특이성 및 민감성 등이 뛰어난 면역센서는 전립선 암의 조기 진단과 예방에 유용하게 이용될 수 있다.
면역센서는 샌드위치형(sandwich-type) 면역센서와 비표지(label-free)면역 센서 두 가지 종류가 있다. 샌드위치형은 기재표면에 항원과 결합할 수 있는 일차(primary)항체가 고정되고, 전립선 특이항원과 결합할 수 있는 표지된 항체(labeled antibody)가 이차(secondary)항체로서 사용된다. 샌드위치형에서는 일차 및 표지된 이차항체를 사용함으로서 항원-항체 결합 효율, 선택성, 민감도 및 신호 증폭 효과를 얻을 수 있다. 이와 달리, 비표지면역 센서는 항원-항체 결합을 바로 측정할 수 있어 편이성, 신속성 및 민감도 등이 뛰어날뿐만 아니라 비용이 절감되어 경제성이 뛰어나 주목할만한 바이오마커 검출 분석 도구이다.
더 좋은 비표지 면역센서의 개발을 위해 생체적합성 및 전자이동이 뛰어난 성질을 가진 그래핀을 이용한 그래핀 기반 복합체가 전극 재질로서 주목받고 있다. 그리하여, 바이오센서 등에 그래핀을 적용하는 연구가 활발히 이루어지고 있고 그래핀이 극히 높은 민감도를 가지는 전기화학적 바이오센서의 개발에 효과적으로 기여할 수 있는 것으로 알려져있다.
한국 등록특허 제1400976호에서는 환원된 그래핀 산화물 층에 분자 링커를 연결하고 금속 나노입자 층을 더한 바이오센서를 개시하고 있으나, 수평적 구조로 되어 있어 3차원 구조가 아니며 분자 링커가 제한되고, 한국 등록특허 1339403에서는 환원 그래핀 산화물-금속 나노입자 복합필름을 개시하고 있으나 이를 바이오센서로서 이용할수 있는 가능성 정도만이 제시된 것으로 보인다.
이에 본 발명자는 광화학 및 광열 조사를 이용하여 제조한 3차원 형태의 미세입자-그래핀 복합체를 개발하였으며, 이를 기반으로 한 면역센서는 선택성, 특이성, 경제성뿐만 아니라 높은 민감도를 가지고 재현성이 뛰어난 특징이 있다. 본 발명은 특히 치매 특이항원의 검출에 매우 효과적인 면역센서에 응용될 수 있다.
본 발명의 목적은 미세입자와 그패핀의 가교결합에 의한 3차원 구조 형성 및 이러한 구조적 특징에 의한 높은 전기 전도성 특성을 이용하여, 저농도의 항원에 대해 민감도 및 특이성이 우수하고, 특히 치매 특이항원의 검출을 위한 면역센서에 최적화된 치매 특이항원 면역 센서용 하이브리드 그래핀 전극를 제공하는 데 있다.
상기와 같은 문제를 해결하기 위하여 본 발명은 복수 개의 미세입자(Micro Particle)와 다층 그래핀이 혼합된 구조를 가지는 그래핀 복합체를 구성하되, 상기 미세입자는 금속 또는 반도체 입자이며, 상기 다층 그래핀 표면 또는 내부에 결착되며, 일부 미세입자는 상호 결합응고되고,상기 다층 그래핀은 여러 층의 그래핀이 적층되고 임의의 방향으로 굽혀져 있는 3차원 구조를 가지고,상기 미세입자 사이 빈 공간의 일부는 상기 다층 그래핀이 채워져 상호 연결된 구조로,상기 그래핀 복합체를 통하여 전자의 흐름이 발생하는 하이브리드 그래핀 전극을 제공한다.
또한 본 발명은 상기 미세입자 표면에 그래핀이 코팅된 것에 특징이 있는 하이브리드 그래핀 전극을 제공한다.
또한 본 발명은 상기 그래핀 복합체는 광화학, 광열조사 또는 열처리 공정에 의해 생성되는 것에 특징이 있는 하이브리드 그래핀 전극을 제공한다.
또한 본 발명은 상기 그래핀 복합체를 통하여 외부 전자의 유입 또는 방출이 발생하는 하이브리드 그래핀 전극을 제공한다.
또한 본 발명은 상기 미세입자는 금(Au), 실리콘(Si), 실리콘카바이드(Si2C, SiC 또는 SiC2를 포함하는 SiCX), 산화실리콘(SiO 또는 SiO2를 포함하는 SiOX), 은(Ag), 구리 금속 표면에 은(Ag)으로 코팅된 것에 특징이 있는 하이브리드 그래핀 전극을 제공한다.
또한 본 발명은 상기 그래핀 금속 복합체에서 전기화학 반응을 이용해 특정 타겟 물질을 검출하는 전기화학 센서용 하이브리드 그래핀 전극을 제공한다.
또한 본 발명은 상기 그래핀 복합체에 리튬(Li)이온이 결합 및 분리되어 충전 및 방전이 진행되는 하이브리드 그래핀 전극을 제공한다.
본 발명인 미세입자(Micro Particle)와 그패핀의 가교결합에 의한 3차원 구조의 하이브리드 그래핀 전극은 구조적 특징에 의한 높은 전기 전도성 특성을 이용하여, 저농도의 항원에 대해 민감도가 우수하며, 특히 치매 특이항원의 검출을 위한 면역센서에 최적화된 특징이 있다.
도 1a~1e는 본 발명인 하이브리드 그래핀 전극의 단계별 SEM 사진 및 개념도이다.
도 2는 본 발명인 하이브리드 그래핀 전극(그래핀 금속 복합체)와 금속전극, 그래핀 전극의 전기 전도성 특성을 측정하여 비교한 그래프이다.
도 3은 본 발명인 하이브리드 그래핀 전극, 그래핀 전극, 금속 전극에 대해서 전기화학 측정물질(PAP)의 농도에 따른 측정 전류를 보여주는 그래프이다.
도 4은 본 발명인 그래핀 금속 복합체 전극, 그래핀 전극, 금속 전극에 대해 같은 농도의 PAP에 대해 측정한 전류신호의 차이를 보여주는 도면이다.
도 5는 본 발명인 하이브리드 그래핀 전극을 이용한 인터디지테이티드 전극(IDA) 을 보여주는 도면이다.
이하 본 발명의 바람직한 실시예를 상세히 설명하기로 한다. 우선, 본 발명을 설명함에 있어, 관련된 공지기능 또는 구성에 대한 구체적인 설명은 본 발명의 요지를 모호하지 않게 하기 위하여 생략한다.
본 명세서에서 사용되는 정도의 용어 '약', '실질적으로' 등은 언급된 의미에 고유한 제조 및 물질 허용오차가 제시될 때 그 수치에서 또는 그 수치에 근접한 의미로 사용되고, 본 발명의 이해를 돕기 위해 정확하거나 절대적인 수치가 언급된 개시 내용을 비양심적인 침해자가 부당하게 이용하는 것을 방지하기 위해 사용된다.
본 발명은 미세입자(Micro Particle)와 그래핀 복합층이 혼합된 구조를 가지는 그래핀 복합체를 구성하고, 상기 그래핀 금속 복합체를 통하여 전자의 흐름이 발생하는 하이브리드 그래핀 전극에 관한 것이다.
도 1a~1e는 본 발명인 하이브리드 그래핀 전극의 단계별 SEM 사진 및 개념도이다. (a)는 본 발명의 일예인 은(Ag)미세입자입자를 보여주는 사진으로 구형 형상의 입자 지름은 약 5 ㎛를 갖는다. (b)는 광화학, 광열조사 또는 열처리 공정을 사용하여 은(Ag)미세입자의 표면이 용융된 상태에서 인접 미세입자와 결합 응고된 사진이다. 일부 미세입자는 연결되지 않아 빈 공간이 형성된 것에 특징이 있다. (c)는 광화학 및 광열반응 후 그래핀(다층 그래핀이 3차원 구조로 굽혀짐)에 관한 사진이다.
그래핀은 탄소의 동소체 중 하나이며 탄소 원자들이 모여 2차원 평면을 이루고 있는 구조이다. 각 탄소 원자들은 육각형의 격자를 이루며 육각형의 꼭짓점에 탄소 원자가 위치하고 있는 모양이다. 나노 사이즈에서는 2차원 평면의 그래핀이 겹치거나 굽힌 구조로 불규칙적인 형상이 특징이다.
상기 미세입자는 금(Au), 실리콘(Si), 실리콘카바이드(Si2C, SiC 또는 SiC2를 포함하는 SiCX), 산화실리콘(SiO 또는 SiO2를 포함하는 SiOX), 은(Ag), 구리 금속 표면에 은(Ag)으로 코팅된 것을 포함한다.
또한 반도체입자는 반도체(semiconductor) 재료에 해당되는 입자로 상온에서 전기 전도율이 구리 같은 도체와 유리 같은 부도체(절연체)의 중간 정도인 물질로써 반도체에 전압이나 열, 빛의 파장 등을 가해주면 전도도가 바뀌는 성질이 있는 모든 물질을 포함한다. 주로 고유 반도체인 실리콘(Si)입자를 말한다. 이외에 비고유 반도체로 인(P), 비소(As), 안티모니(Sb), 비스무트(Bi), 붕소(B), 알루미늄(Al), 인듐(In), 갈륨(Ga) 이 혼합된 것도 포함된다.
상기 그래핀 복합층가 그래핀과 반도체인 실리콘 입자로 형성될 경우에는 리튬이온이 그래핀과 실리콘 입자에 결합 및 분리되는 과정으로 충전 및 방전이 진행되는 배터리 음극재로 활용된다.
(d)는 본 발명의 하이브리드 그래핀 전극의 SEM 사진으로 광화학 또는 광열조사에 의해 미세입자는 상기 그래핀 복합층 표면 또는 내부에 결착될 수 있고, 일부 미세입자는 상호 결합응고될 수 있는 고정된 구조를 보여주고 있다.
(e)는 상기 (d)의 광화학 또는 광열 반응으로 제조된 그래핀이 은(Ag)미세입자의 빈 공간(b)에 위치하여 고정된 구조를 보여주는 개념도이다. 상기 은(Ag)미세입자가 그래핀 복합층 내부 또는 외부에 결착될 수 있으며, 상기 개념도에는 미표시되었지만, 은(Ag)미세입자의 불규칙한 위치에 따라 일부 미세입자는 상호 결합응고될 수 있다.
또한 상기 은(Ag)미세입자는 광화학 또는 광열 반응으로 표면에 그래핀코팅이 생성될 수 있다. 도 1(e)에서 입자표면에 그물망으로 그래핀 코팅구조가 도시되어 있다.
기존 그래핀의 경우 고온 공정을 비롯해 복잡한 과정이 필요하지만, 광열 또는 광화학 합성 그래핀은 원스텝 공정으로 비교적 간단하게 합성할 수 있다
도 2는 본 발명인 하이브리드 그래핀 전극(그래핀 금속 복합체)와 금속전극, 그래핀 전극의 전기 전도성 특성을 측정하여 비교한 그래프이다. 금(Au) 박막으로 제작된 전극의 경우에 비하여, 그래핀 전극은 측정된 전류 신호가 더 커지게 된다.
이는 다공성 구조로 인하여 전극의 표면적이 넓고 그래핀을 통해 전자의 유입 및 방출이 우수해 전기화학 반응으로 발생하는 전자의 흐름이 더 크기 때문이다.
그래핀 금속 복합체 전극의 경우에는 그래핀 전극의 장점을 모두 가지면서 금속 입자로 인해 전도성이 좋아져서 전극의 저항이 매우 낮아지게 된다.
따라서 3가지 종류의 전극을 이용하여 전기화학 신호를 측정할 때, 그래핀 금속 복합체 전극으로 측정할 때 가장 큰 전류 신호를 발생시키게 된다.
이때, 민감도는 측정 전류 신호(signal)의 절대값이 클수록 우수하다. 따라서 본 발명의 그래핀 금속 복합 전극은 그래핀의 넓은 표면적과 전자의 흡수 및 방출에 의한 전기화학 반응을 더욱 효율적으로 발생시키는 특성과 금속입자의 낮은 저항의 장점이 활용되면 발생되는 신호의 SNR(Signal to Noise Ratio)이 매우 커서, 낮은 농도의 타겟 물질까지 검출할 수 있는 특징이 있다.
이 기술은 광화학 및 광열 반응으로 3D 다공성 그래핀을 얻을 수 있다. 이 기술은 습식 화학 단계없이 3D 그래핀 제조 및 패턴화를 단일 단계로 진행할 수 있는 장점이 있다.
또한 본 발명의 은(Ag)미세입자는 구리 금속 표면에 은(Ag)으로 코팅하여 사용할 수 있다. 은 입자가 전도성이 우수하나 비용등을 고려할 때 코팅으로 사용하여도 입자의 표면이 전도성에 기여도가 큰 것을 감안하면 바람직한 구조일 수 있다.
도 3은 본 발명인 하이브리드 그래핀 전극, 그래핀 전극, 금속 전극에 대해서 전기화학 측정물질(PAP)의 농도에 따른 측정 전류를 보여주는 그래프이다. 각각의 전극에 대해 PAP 농도에 따라 전류 신호의 크기가 점점 커지게 된다. 또한 같은 농도의 PAP에 대해서 금속 전극에 비해 표면적과 전자 유입 및 방출의 장점이 있는 그래핀 전극의 신호가 더 크게 되고, 그래핀 전극 대비 저항이 작은 그래핀 금속 복합전극의 신호가 더 크게 측정됨을 알 수 있다.
본 발명인 하이브리드 그래핀 전극은 그래핀 금속 복합체 소재로 인터디지테이티드 전극(IDA)을 제작할 수 있다. 그래핀 금속 복합체에서 전기화학 반응을 이용해 특정 타겟 물질을 검출하는 전기화학 센서로 사용될 수 있다.
인터디지테이티드 전극(IDA)의 손가락 모양의 두 전극 사이에서 전기화학 반응에 의해 전자가 이동되면서 전류를 만들어 내는 특징이 있다. 인터디지테이티드 전극(IDA)을 이용하여 전기 화학 효소-연결 면역 흡착 분석 (ELISA) 측정을 사용하면 알츠하이머 병의 초 고감도 전기 화학 검출을 할 수 있다.
미국 국립노화연구소와 알츠하이머협회(National Institute of Aging and Alzheimer Association, NIA-AA)는 알츠하이머 바이오마커로 뇌와 뇌척수액의 아밀로이드 베타(Amyloid beta, Aβ) Aβ-40 및 Aβ-42와 신경세포 손상을 반영하는 뇌척수액 타우단백질(total tau protein, t-tau)과 인산화 타우단백질(phosphorylated tau protein, p-tau)을 제시하였다. Aß-42 및 Aß-40와 t-tau 및 p-tau를 전기 화학적으로 측정하기 위해, 알칼리성 포스파타제 (AP)는 일반적으로 ELISA에 대한 효소 표지로서 사용된다. AP는 이차 항체에 붙어있어서, 알츠하이머 바이오마커가 많을수록 더 많은 AP 효소가 고정화되어 더 큰 전기화학 신호를 발생한다. 전기 활성 효소-기질 p-아미노 페닐포스페이트 (PAPP)는 효소 생성물과의 화학 반응에서 발생하여 전기 활성 생성물 p-아미노 페놀 (PAP)을 생성한다. PAP는 MHG 인터디지테이티드 전극(IDA) 표면에서 p-퀴논 이민 (PQI)으로 산화 된 다음 PQI가 PAP로 환원되어 PAP의 산화 환원주기를 초래한다. 알츠하이머 바이오마커의 농도가 증가하면, 반응 챔버에 더 많은 AP 효소가 고정되어 전기 화학적 신호를 증가시킨다.
상기와 같은 원리를 이용하여 초기 알츠하이머 진단에서 전기 활성 생성물 p-아미노 페놀 (PAP)의 측정은 중요하여 매우 적은 양을 구분할 수 있는 전극으로 본 발명의 하이브리드 그래핀 전극을 응용할 수 있다.
따라서 하이브리드 그래핀 전극의 미세입자의 형상은 전기 활성 생성물 p-아미노 페놀 (PAP)의 측정의 민감도에 영향을 미치며, 은(Ag)미세입자 입자의 구형 형상이 가장 민감도가 우수함을 알 수 있다.
또한 PAP 분자의 농도가 증가하고, PAP 분자의 산화 환원 주기도 증가하며, 결과적으로 전류는 MHG 인터디지테이티드 전극(IDA)에 의해 측정 된 것과 선형적으로 증가된다.
도 4은 본 발명인 그래핀 금속 복합체 전극, 그래핀 전극, 금속 전극에 대해 같은 농도의 PAP에 대해 측정한 전류신호의 차이를 보여주는 도면이다. 본 발명인 그래핀 금속 복합체 전극의 전류신호가 비교 전극들에 비해 더 큰 신호를 발생시켜서 SNR(Signal to Noise Ration, 신호대 잡음비)이 비교 전극에 비해 더 크다는 것을 알 수 있다.
도 5는 본 발명인 하이브리드 그래핀 전극을 이용한 인터디지테이티드 전극(IDA) 을 보여주는 도면이다.
이상에서 설명한 본 발명은 전술한 실시예 및 첨부된 도면에 의해 한정되는 것이 아니고, 본 발명의 기술적 사상을 벗어나지 않는 범위 내에서 여러 가지 치환, 변형 및 변경이 가능함은 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에게 있어서 명백할 것이다.
Claims (7)
- 복수 개의 미세입자(Micro Particle)와 다층 그래핀이 혼합된 구조를 가지는 그래핀 복합체를 구성하되,상기 미세입자는 금속 또는 반도체 입자이며, 상기 다층 그래핀 표면 또는 내부에 결착되며, 일부 미세입자는 상호 결합응고되고,상기 다층 그래핀은 여러 층의 그래핀이 적층되고 임의의 방향으로 굽혀져 있는 3차원 구조를 가지고,상기 미세입자 사이 빈 공간의 일부는 상기 다층 그래핀이 채워져 상호 연결된 구조로,상기 그래핀 복합체를 통하여 전자의 흐름이 발생하는 하이브리드 그래핀 전극.
- 제1항에 있어서,상기 미세입자 표면에 그래핀이 코팅된 것에 특징이 있는 하이브리드 그래핀 전극.
- 제1항에 있어서,상기 그래핀 복합체는 광화학, 광열조사 또는 열처리 공정에 의해 생성되는 것에 특징이 있는 하이브리드 그래핀 전극.
- 제1항에 있어서,상기 그래핀 복합체를 통하여 외부 전자의 유입 또는 방출이 발생하는 하이브리드 그래핀 전극.
- 제1항에 있어서,상기 미세입자는 금(Au), 실리콘(Si), 실리콘카바이드(Si2C, SiC 또는 SiC2를 포함하는 SiCX), 산화실리콘(SiO 또는 SiO2를 포함하는 SiOX), 은(Ag), 구리 금속 표면에 은(Ag)으로 코팅된 것에 특징이 있는 하이브리드 그래핀 전극.
- 제1항에 있어서,상기 그래핀 금속 복합체에서 전기화학 반응을 이용해 특정 타겟 물질을 검출하는 전기화학 센서용 하이브리드 그래핀 전극.
- 제1항에 있어서,상기 그래핀 복합체에 리튬(Li)이온이 결합 및 분리되어 충전 및 방전이 진행되는 하이브리드 그래핀 전극.