WO2023061782A1 - Procédé de soudage au laser - Google Patents

Procédé de soudage au laser Download PDF

Info

Publication number
WO2023061782A1
WO2023061782A1 PCT/EP2022/077364 EP2022077364W WO2023061782A1 WO 2023061782 A1 WO2023061782 A1 WO 2023061782A1 EP 2022077364 W EP2022077364 W EP 2022077364W WO 2023061782 A1 WO2023061782 A1 WO 2023061782A1
Authority
WO
WIPO (PCT)
Prior art keywords
intensity
laser beam
laser
weld seam
components
Prior art date
Application number
PCT/EP2022/077364
Other languages
German (de)
English (en)
Inventor
Oliver BOCKSROCKER
Nicolai Speker
Tim Hesse
Original Assignee
Trumpf Laser- Und Systemtechnik Gmbh
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Trumpf Laser- Und Systemtechnik Gmbh filed Critical Trumpf Laser- Und Systemtechnik Gmbh
Publication of WO2023061782A1 publication Critical patent/WO2023061782A1/fr

Abstract

L'invention concerne un procédé pour souder au laser deux composants (19, 12), de préférence métalliques. Un faisceau laser pulsé (18) est dirigé sur une surface (20) de l'un des composants (10) de sorte que le matériau des composants (10, 12) est fondu dans la zone d'un cordon de soudure (23) à produire. Le faisceau laser (18) a un profil d'intensité qui a un maximum d'intensité annulaire et un minimum d'intensité locale en son centre, l'intensité dans le minimum d'intensité étant au moins 10 % plus petite que dans le maximum d'intensité (30), et une profondeur (34) du cordon de soudure (23) produit étant au plus aussi grande qu'une largeur (36) du cordon de soudure.
PCT/EP2022/077364 2021-10-15 2022-09-30 Procédé de soudage au laser WO2023061782A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
DE102021126749.8A DE102021126749A1 (de) 2021-10-15 2021-10-15 Laserschweißverfahren
DE102021126749.8 2021-10-15

Publications (1)

Publication Number Publication Date
WO2023061782A1 true WO2023061782A1 (fr) 2023-04-20

Family

ID=84245646

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2022/077364 WO2023061782A1 (fr) 2021-10-15 2022-09-30 Procédé de soudage au laser

Country Status (2)

Country Link
DE (1) DE102021126749A1 (fr)
WO (1) WO2023061782A1 (fr)

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2019150071A1 (fr) 2018-02-02 2019-08-08 Spi Lasers Uk Limited Appareil et procédé de traitement laser d'un matériau
EP3285956B1 (fr) * 2016-07-15 2020-01-15 Corelase OY Appareil et procédé de traitement au laser
US20200254562A1 (en) * 2019-02-13 2020-08-13 Coherent, Inc. Laser welding method

Family Cites Families (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
IT1179064B (it) 1984-08-20 1987-09-16 Fiat Auto Spa Procedimento di saldatura di lamiere
JP2880061B2 (ja) 1994-02-03 1999-04-05 住友重機械工業株式会社 レーザ加工
DE102007035717A1 (de) 2006-12-27 2008-07-03 Robert Bosch Gmbh Laserstrahlschweißvorrichtung sowie Laserstrahlschweißverfahren
DE102010003750A1 (de) 2010-04-08 2011-10-13 Trumpf Laser- Und Systemtechnik Gmbh Verfahren und Anordnung zum Verändern der Strahlprofilcharakteristik eines Laserstrahls mittels einer Mehrfachclad-Faser
GB201513902D0 (en) 2015-08-06 2015-09-23 Spi Lasers Uk Ltd An amplifying optical device
DE102017001658A1 (de) 2017-02-21 2018-08-23 Precitec Gmbh & Co. Kg Vorrichtung zur materialbearbeitung mit einem laserstrahl entlang einer bearbeitungsrichtung und verfahren zur materialbearbeitung mit einem laserstrahl
EP3731991B1 (fr) 2017-12-29 2023-04-26 Corelase OY Appareil et procédé de traitement au laser
KR102578698B1 (ko) 2018-06-22 2023-09-15 후루카와 덴키 고교 가부시키가이샤 용접 방법 및 용접 장치

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP3285956B1 (fr) * 2016-07-15 2020-01-15 Corelase OY Appareil et procédé de traitement au laser
WO2019150071A1 (fr) 2018-02-02 2019-08-08 Spi Lasers Uk Limited Appareil et procédé de traitement laser d'un matériau
US20200254562A1 (en) * 2019-02-13 2020-08-13 Coherent, Inc. Laser welding method

Also Published As

Publication number Publication date
DE102021126749A1 (de) 2023-04-20

Similar Documents

Publication Publication Date Title
EP2160266B1 (fr) Procédé d'assemblage par soudure de pièces métalliques à parois épaisses
DE102015104411B4 (de) Laserstrahlfügeverfahren und Laserbearbeitungsoptik
EP3429795B1 (fr) Soudage d'acier au laser avec modulation de puissance pour éviter la fissuration à chaud
EP1604772B1 (fr) Procédé pour souder une feuille métallique à une tige métallique cylindrique
WO2021005061A1 (fr) Appareil optique et procédé de soudage au laser d'une pièce, comprenant plusieurs faisceaux partiels présentant une zone centrale et une zone annulaire dans le profil de faisceau
DE102016222357A1 (de) Verfahren zum Tiefschweißen eines Werkstücks, mit Einstrahlen eines Laserstrahls in die von einem anderen Laserstrahl erzeugte Kapillaröffnung
DE102011089146A1 (de) Laser-Überlappschweißverfahren
EP2226146A1 (fr) Procédé d'assemblage de deux pièces métalliques, notamment symétriques de révolution, par soudage TIG et appareil pour la mise en oeuvre d'un tel procédé
DE102019218398A1 (de) Laserschweißen von Stromschienen mit Strahlformung
WO2021019052A1 (fr) Procédé de soudage laser d'une liaison cuivre-aluminium
DE102021113834A1 (de) Bipolarplatte für eine Brennstoffzelle und Verfahren zum Schweißen einer Bipolarplatte
DE102016220067B4 (de) Verfahren zum Tiefschweißen eines Werkstücks, wobei eine verkippte Dampfkapillare mittels zweier Laserstrahlen erzeugt wird
WO2023061782A1 (fr) Procédé de soudage au laser
DE102016205262A1 (de) Verfahren zur Herstellung eines Drahts aus einem spröden Werkstoff und Verwendung desselben zur generativen Herstellung eines Bauteils
DE3708011A1 (de) Duennblechschweissverfahren und anlage fuer dessen durchfuehrung
DE102015115183A1 (de) Verfahren und eine Vorrichtung zum Herstellen einer Fügeverbindung
WO2021175555A1 (fr) Procédé de soudage laser de deux pièces revêtues
WO2020015921A1 (fr) Procédé de fabrication d'une pièce de véhicule au moyen d'un élément auxiliaire d'assemblage
DE102022002630B4 (de) Laserschweißverfahren
DE102021126754A1 (de) Verfahren zum Laserschweißen eines Werkstücks mit schnellem Wechsel zwischen Schweißzonen mit unterschiedlichen zu schweißenden Materialien
DE102022101094A1 (de) Verfahren zum Laserbohren einer Bohrung in ein Werkstück sowie Laserbohrvorrichtung
EP3266549B1 (fr) Procédé de soudage selon le principe de l'arc tiré à l'aide d'un faisceau de lumière à déplacement magnétique et élément de soudure
DE102019123503A1 (de) Laserpunktschweißverfahren
DE102022121052A1 (de) Verfahren zum Schweißen von Blechen mit Beschichtungen, die eine Legierung aus Aluminium und Silizium umfassen
DE102022121053A1 (de) Verfahren zum Schweißen von zinkbeschichteten Blechen

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 22800143

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE