Classifications

• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
  • A61L27/00—Materials for grafts or prostheses or for coating grafts or prostheses
  • A61L27/40—Composite materials, i.e. containing one material dispersed in a matrix of the same or different material
  • A61L27/44—Composite materials, i.e. containing one material dispersed in a matrix of the same or different material having a macromolecular matrix
  • A61L27/46—Composite materials, i.e. containing one material dispersed in a matrix of the same or different material having a macromolecular matrix with phosphorus-containing inorganic fillers
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
  • A61L27/00—Materials for grafts or prostheses or for coating grafts or prostheses
  • A61L27/02—Inorganic materials
  • A61L27/04—Metals or alloys
  • A61L27/06—Titanium or titanium alloys
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
  • A61L27/00—Materials for grafts or prostheses or for coating grafts or prostheses
  • A61L27/28—Materials for coating prostheses
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
  • A61L27/00—Materials for grafts or prostheses or for coating grafts or prostheses
  • A61L27/28—Materials for coating prostheses
  • A61L27/34—Macromolecular materials
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
  • A61L27/00—Materials for grafts or prostheses or for coating grafts or prostheses
  • A61L27/50—Materials characterised by their function or physical properties, e.g. injectable or lubricating compositions, shape-memory materials, surface modified materials
  • A61L27/56—Porous materials, e.g. foams or sponges
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
  • A61L27/00—Materials for grafts or prostheses or for coating grafts or prostheses
  • A61L27/50—Materials characterised by their function or physical properties, e.g. injectable or lubricating compositions, shape-memory materials, surface modified materials
  • A61L27/58—Materials at least partially resorbable by the body
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
  • A61L31/00—Materials for other surgical articles, e.g. stents, stent-grafts, shunts, surgical drapes, guide wires, materials for adhesion prevention, occluding devices, surgical gloves, tissue fixation devices
  • A61L31/02—Inorganic materials
  • A61L31/022—Metals or alloys
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
  • A61L31/00—Materials for other surgical articles, e.g. stents, stent-grafts, shunts, surgical drapes, guide wires, materials for adhesion prevention, occluding devices, surgical gloves, tissue fixation devices
  • A61L31/08—Materials for coatings
  • A61L31/10—Macromolecular materials
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
  • A61L31/00—Materials for other surgical articles, e.g. stents, stent-grafts, shunts, surgical drapes, guide wires, materials for adhesion prevention, occluding devices, surgical gloves, tissue fixation devices
  • A61L31/12—Composite materials, i.e. containing one material dispersed in a matrix of the same or different material
  • A61L31/125—Composite materials, i.e. containing one material dispersed in a matrix of the same or different material having a macromolecular matrix
  • A61L31/127—Composite materials, i.e. containing one material dispersed in a matrix of the same or different material having a macromolecular matrix containing fillers of phosphorus-containing inorganic materials
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
  • A61L31/00—Materials for other surgical articles, e.g. stents, stent-grafts, shunts, surgical drapes, guide wires, materials for adhesion prevention, occluding devices, surgical gloves, tissue fixation devices
  • A61L31/14—Materials characterised by their function or physical properties, e.g. injectable or lubricating compositions, shape-memory materials, surface modified materials
  • A61L31/146—Porous materials, e.g. foams or sponges
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
  • C01B25/00—Phosphorus; Compounds thereof
  • C01B25/16—Oxyacids of phosphorus; Salts thereof
  • C01B25/26—Phosphates
  • C01B25/32—Phosphates of magnesium, calcium, strontium, or barium
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
  • C01B25/00—Phosphorus; Compounds thereof
  • C01B25/16—Oxyacids of phosphorus; Salts thereof
  • C01B25/26—Phosphates
  • C01B25/32—Phosphates of magnesium, calcium, strontium, or barium
  • C01B25/327—After-treatment
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
  • A61L2400/00—Materials characterised by their function or physical properties
  • A61L2400/12—Nanosized materials, e.g. nanofibres, nanoparticles, nanowires, nanotubes; Nanostructured surfaces
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
  • A61L2430/00—Materials or treatment for tissue regeneration
  • A61L2430/02—Materials or treatment for tissue regeneration for reconstruction of bones; weight-bearing implants
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B82—NANOTECHNOLOGY
  • B82Y—SPECIFIC USES OR APPLICATIONS OF NANOSTRUCTURES; MEASUREMENT OR ANALYSIS OF NANOSTRUCTURES; MANUFACTURE OR TREATMENT OF NANOSTRUCTURES
  • B82Y40/00—Manufacture or treatment of nanostructures
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B82—NANOTECHNOLOGY
  • B82Y—SPECIFIC USES OR APPLICATIONS OF NANOSTRUCTURES; MEASUREMENT OR ANALYSIS OF NANOSTRUCTURES; MANUFACTURE OR TREATMENT OF NANOSTRUCTURES
  • B82Y5/00—Nanobiotechnology or nanomedicine, e.g. protein engineering or drug delivery
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
  • C01P2002/00—Crystal-structural characteristics
  • C01P2002/02—Amorphous compounds
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
  • C01P2002/00—Crystal-structural characteristics
  • C01P2002/70—Crystal-structural characteristics defined by measured X-ray, neutron or electron diffraction data
  • C01P2002/72—Crystal-structural characteristics defined by measured X-ray, neutron or electron diffraction data by d-values or two theta-values, e.g. as X-ray diagram
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
  • C01P2004/00—Particle morphology
  • C01P2004/60—Particles characterised by their size
  • C01P2004/64—Nanometer sized, i.e. from 1-100 nanometer
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
  • C01P2006/00—Physical properties of inorganic compounds
  • C01P2006/12—Surface area

Definitions

• the present invention relates generally to a porous hydrophilic composite which can serve as a scaffold for bone cell growth and to processes to prepare it.
• the composite comprises nanosized calcium phosphate (CaP) and a biodegradable polymer.
• the composite can be applied to a surface, such as an implant surface. The thickness of the composite layer on the implant surface can be controlled.
• Bone scaffold materials contain a structure and composition which will trigger the formation of bone when implanted in the human body, and act as a cultivating substrate for bone cells.
• Bone scaffolds can be of biological origin, for example harvested from the patient’s own bone prior to the surgery (autograft), or from other donors (allograft).
• the bone scaffold may also be produced from animals, such as bovine bone (xenograft).
• Autografts and allografts have an excellent effect on bone tissue growth, but require surgery to remove the bone, and the handling and storage of the graft is complicated.
• a xenograft has the benefit of not requiring any patient surgery for the harvesting, but needs rigorous cleaning and sterilization procedures due to the risk of infection.
• Synthetic bone scaffolds have also been proposed.
• the primary benefits of synthetic scaffolds compared to bone grafts of biological origin are that they can be made in large quantities and with controlled specifications.
• Synthetic bone scaffolds can be in the form of a powder, such as hydroxyapatite (HA) or tricalcium phosphate. Powder based products are successful in restoring bone tissue but are less suitable for load-bearing applications.
• HA hydroxyapatite
• Powder based products are successful in restoring bone tissue but are less suitable for load-bearing applications.
• bone scaffold is the rigid type, which usually consists of porous HA or tricalcium phosphate which has been sintered at high temperatures.
• the primary advantages of rigid bone scaffold products are form stability when implanted and the porosity, which increases the available surface area for the new bone cells to grow on.
• One disadvantage is the brittleness of the structure; a rigid bone scaffold normally contains no flexible substances such as polymers, which may dissipate forces applied to the material and prevent crack formation.
• Polymer/mineral composite materials consist of a polymer, which can be biodegradable, and a mineral with bone regeneration properties, such as HA.
• the polymer makes the composite elastic and crack-resistant, while the mineral induces the formation of endogenous bone.
• HA is a mineral which closely resembles the calcium phosphate mineral found in natural bone.
• nanosized HA is similar to the size and shape as in human bone, i.e. with a particle size of 1-100 nm in length.
• Natural bone consists of rod-shaped calcium phosphate crystals with a length of 20-40 nm, 2 nm thick and 2-4 nm wide, surrounded by a collagen network (H. A. Lowenstam and S. Weiner, On biomineralization, Oxford University Press, New York, 1989).
• Nanocrystalline HA may promote bone remodelling since the body recognizes the nanosized HA as a part of its own bone tissue and starts to grow new bone around the foreign object.
• a coating with nanosized HA will significantly increase the bone cell activity compared to microsized HA.
• the bioactivity as well as the strength is greatly improved with nanosized HA (J. Wei, Y. Li and K. Lau, Composites partB: engineering, 2007, 38, 301-305; H. Ramay and M. Zhang, Biomaterials, 2003, 24, 3293-3302).
• porous PCL and HA composites with different proportions of HA can be manufactured by selective laser sintering.
• the researchers found that the compressive stiffness increased with increasing amount of HA, and the porosity decreased K. Rezwan et al. Biomaterials 200627(18):3413-31).
• Another example is the fabrication of porous PCL/HA composites by precision extrusion, which produced scaffolds with different porosity and pore size. Osteoblasts were cultivated and shown to migrate and proliferate for these scaffolds (L. Shor et al. Biomaterials Volume 28, Issue 35, December 2007, Pages 5291-5297).
• US2010/226956 describes a moldable composite made of polycaprolactone, hydroxyapatite and different bioresorable plasticizers. The ability to shape the composite is controlled by the amount and type of plasticizer used. Once the composite is implanted in the body, the plasticizers are resorbed to leave a porous structure. The composite is made by melt mixing. However, it has been found that the hydrophilic HA does not fully disperse in the hydrophobic polymer during the melt mixing, leading to a composite which contains large domains of pure polymer which render the overall composite hydrophobic (i.e. with a water contact angle >90 °).
• CN102008752A discloses a method of forming a nano-hydroxyapatite coating on a porous biphasic calcium phosphate biological scaffold using chemical precipitation. The result is a porous biphasic calcium phosphate bioscaffold with a nano-hydroxyapatite coating.
• the HA crystals are not dispersed in a polymer matrix.
• EP3785743A presents various ways of producing porous polymer scaffolds with calcium phosphate content, however the calcium phosphate used in the scaffolds is not nanosized.
• CN107823715A discloses a PCL/HA composite porous bone tissue engineering scaffold that is characterized in that the scaffold is composed of polycaprolactone and hydroxyapatite.
• the content of hydroxyapatite is 0.5 to 50% by mass percentage, and the rest is polycaprolactone.
• the porosity is controlled by the use of pore formers such as sodium carbonate, sodium bicarbonate and potassium carbonate, and these compounds are subsequently removed by the use of strong acids, such as hydrochloric acid, sulphuric acid or nitric acid which dissolve the pore forming compounds.
• strong acids such as hydrochloric acid, sulphuric acid or nitric acid which dissolve the pore forming compounds.
• the formation of carbon dioxide during the dissolution creates pores and helps to create an interconnecting porous structure.
• the acids used to dissolve the pore forming agents will also dissolve any HA which is not fully embedded in and protected by the polymer matrix.
• the result will be a polymer/HA composite with little or no HA present on the surface of the polymer, which will decrease the hydrophilicity and biological activity towards bone cell growth. Additionally, since PCL starts to degrade at acidic pH, this method increases the risk of premature degradation of the PCL matrix.
• US6165486A discloses a composition comprising HA, a polycaprolactone (PCL) and a copolymer of poly(lactic) acid and poly(glycolic) acid (PLGA) and molding the blend and bioceramic into an implant.
• the porosity is created by adding NaCl as the pore forming agent, which is removed with water.
• NaCl as the pore forming agent
• Weight loss curves for different composites stored at 37 °C in phosphate-buffered saline (pH 7.4) are shown in Figures 1 and 2 of US6165486A.
• ES2330823A discloses a polymeric scaffold formed by thermally induced phase separation with hydroxyapatite deposition.
• the scaffold consists of a polymer network with a thin coating of HA on the internal surface of the pores in the polymer network.
• CN 100546661 Cjiiscloses a method for preparing an in situ pore-forming self-setting calcium phosphate composite scaffold.
• the porous calcium phosphate scaffold is then filled with a polymer, which may then be cross-linked.
• the resulting product is a dense structure with low porosity and no open cells.
• Bone scaffolds are often used together with a load-bearing, non-degradable structure, such as a spinal fusion cage. This approach is particularly effective when larger volumes of bone need to be built around the implant.
• a spinal fusion cage may be packed with a bone scaffold material, to combine the high mechanical strength of the spinal cage with the bone stimulation properties of the bone scaffold.
• this type of implant is fragile to handle, and requires preparation of the implant with the bone scaffold on site. It would therefore of great benefit to have a scaffold which can be tailor made for the implant.
• a primary object of the present invention is to provide a porous hydrophilic composite, serving as a scaffold for bone cell growth, comprising of nanosized calcium phosphate, such as amorphous calcium phosphate (ACP), beta-TCP, calcium deficient HA (CDHA) or hydroxyapatite (HA), and a biodegradable polymer.
• ACP amorphous calcium phosphate
• beta-TCP beta-TCP
• CDHA calcium deficient HA
• HA hydroxyapatite
• biodegradable polymer a biodegradable polymer.
• Another object of the invention is provision of a method to produce a layer of the composite onto a surface, such as an implant surface, to form an osteoconductive coating on the implant.
• Yet another object of the invention is provision of a method to produce the porous composite in situ within a void of an implant or on the surface of an implant, or within the pores of a porous metal lattice structure, with the ability to control the geometry of the composite.
• porous hydrophilic composite which can serve as a scaffold for bone cell growth.
• the porous hydrophilic composite comprises:
• nanosized calcium phosphate (CaP) homogeneously dispersed throughout the polymer matrix, wherein the CaP has a specific surface area in the range of about 180 to about 380 m 2 /g; with the proviso that the composite does not contain any copolymer(s) of lactic acid and glycolic acid.
• a scaffold for use in bone reconstruction comprising the porous hydrophilic composite of the invention and a substrate, such as an implant.
• the composite may be present as a coating on a surface of the substrate, or the substrate may be wholly or partially surrounded by the composite.
• a first process for the preparation of a porous hydrophilic composite comprising:
• step (b) solidifying the mixture of step (a) to form a gel
• step (c) removing the first and second solvents from the gel of step (b) by washing with a third solvent to leave a porous hydrophilic composite containing the nanosized CaP homogeneously dispersed in a porous polymer matrix.
• a hydrophilic composite for promoting bone growth comprising:
• step (bl) solidifying the mixture of step (a) on a substrate to form a gel; and (cl) removing the first and second solvents from the gel of step (b) by evaporation to leave a layer of a porous hydrophilic composite containing the nanosized CaP dispersed throughout a porous polymer matrix on the surface.
• the dispersion of nanosized calcium phosphate (CaP) in a second solvent may be prepared by mixing a dispersion of a non-phosphate calcium salt such as CaO in a suitable solvent with an aqueous phosphoric acid solution.
• the first and second solvents may be the same or different, but are preferably the same.
• the third solvent used in the first process is different to the first and second solvents.
• the processes of the invention may further comprise (d) immersing the porous hydrophilic composite in a solution comprising a biocompatible organic polyol, (e) removing the porous hydrophilic composite from the solution and (f) drying the porous hydrophilic composite, to further increase the hydrophilicity of the composite structure.
• the CaP used in the above methods preferably has a surface area in the range of about 180 to about 380 m 2 /g.
• a method for the preparation of nanosized CaP comprising mixing a dispersion of a non-phosphate calcium salt in a suitable non- aqueous solvent with an aqueous phosphoric acid solution to form amorphous nanosized CaP, and optionally contacting the amorphous CaP with water to convert it to HA or b-TCP.
• Figure 1 Powder X-ray diffractogram of a nanocrystalline HA sample.
• Figure 2 Powder X-ray diffractogram of a nanosized amorphous HA sample.
• FIG. 1 Schematic of composite production, step 1.
• FIG. 3b Schematic of composite production, step 2.
• FIG 4. A porous composite, prepared according to Example Id, without nanosized HA after immersion in toluidine blue (a) and the same sample cut in two pieces, showing the inside of the sample (b).
• Figure 5 Illustration of spinal cage (left images) with a layer of composite, prepared according to Example 6, on the insides of the implant (right images).
• FIG. 1 Images of titanium lattice with in situ formed CaP / PCF foam, prior to immersion in Alizarin Red (a) and (b). Image of different 3D printed titanium samples with different mesh size, after immersion in Alizarin Red (c).
• FIG. 7 Illustration of method to produce a screw coated with a 1 mm layer of composite (a). Photo of screw coated with composite (b).
• FIG. 8 Micro-CT images of sham (a) after 6 weeks, and sham with porous composite in place after 6 weeks (b) placed in the calvaria of rabbits. The site with porous composite is completely overgrown with bone.
• Figure 12a Photograph of the composite of Example lc after soaking in red dye for 30 minutes.
• Figure 12b Photograph of the composite of Example lc after glycerol treatment according to Example 11 and subsequent soaking in red dye for 30 minutes.
• the present invention comprises a porous hydrophilic composite comprising (or consisting essentially of or consisting of) nanosized calcium phosphate (CaP) and a matrix of a biodegradable polymer. Due to the bioactive properties of the nanosized CaP particles, the high surface area of the polymer / CaP composite and its hydrophilicity, the composite may serve as an excellent scaffold for bone cell growth.
• a porous hydrophilic composite comprising (or consisting essentially of or consisting of) nanosized calcium phosphate (CaP) and a matrix of a biodegradable polymer. Due to the bioactive properties of the nanosized CaP particles, the high surface area of the polymer / CaP composite and its hydrophilicity, the composite may serve as an excellent scaffold for bone cell growth.
• nanosized refers to particles with a longest dimension of 1 to 100 nm. Preferred are particles with a longest dimension of 1 to 50 nm, for example 5-40 nm or 10-20 nm.
• the particles may be of any shape, including substantially spherical, of hexagonal cross section or fibre shaped.
• CaP refers to calcium phosphate in any form, including but not limited to amorphous CaP (ACP), beta-tricalcium phosphate (b-TCP), tetracalcium phosphate (TTCP), hydroxyapatite (HA) or calcium deficient HA (CDHA).
• ACP amorphous CaP
• b-TCP beta-tricalcium phosphate
• TTCP tetracalcium phosphate
• HA hydroxyapatite
• CDHA calcium deficient HA
• Amorphous calcium phosphate is non-crystalline and can have a varying Ca/P ratio
• Beta-tricalcium phosphate b-TCP
• the dissolution of the calcium phosphate particles is greatly influenced by their structure and size.
• the resorption speed of calcium phosphate polymorphs in an acidic environment is ACP > b-TCP > TTCP > HA (S.V. Dorozhkin, Biomaterials 31 (2010) 1465-1485), and the dissolution and release of calcium and phosphorus in vivo can be controlled by the choice of CaP compound used.
• the CaP may be amorphous or crystalline.
• nanosized refers to the size of the individual crystals whereas for amorphous CaP it refers to the size of individual particles.
• Nanosized crystalline CaP may also be referred to as “nanocrystalline CaP”.
• amorphous CaP with a Ca/P ratio of 5/3 may undergo conversion to crystalline HA when exposed to bodily fluids in vivo. Since amorphous CaP has a lower mechanical strength compared to crystalline HA, this effect can be used to create a composite which will increase in strength after implantation. In addition, since the transformation from ACP to HA is thermodynamically favourable, it will accelerate the infiltration of body liquids and also increase the adhesion strength between the composite and surrounding bone.
• Nanosized CaP may be available commercially, usually in powder form, or may be synthesised using methods known in the art. For example, methods for the synthesis of nanosized CaP are disclosed in WO2005/123579 and US2010/0226956.
• Nanosized crystalline CaP may synthesized by a method which involves the mixing of (i) a dispersion of a non-phosphate calcium salt in water or a non-aqueous solvent with (ii) an aqueous phosphoric acid solution. This results in a dispersion of nanocrystalline CaP which may be used directly in the first or second method to form a composite as discussed below.
• the method can be used to produce HA or other types of calcium phosphate such as ACP, beta-TCP or CDHA.
• the ratio of non-phosphate calcium salt to phosphoric acid can influence the CaP compound formed.
• the non-phosphate calcium salt should have a low solubility in water or in the solvent used to form the non-aqueous dispersion.
• Preferred non phosphate calcium salts are calcium oxide and calcium hydroxide.
• the invention therefore provides a method for the preparation of amorphous nanosized CaP, the method comprising mixing a dispersion of a non-phosphate calcium salt in a suitable non-aqueous solvent with an aqueous phosphoric acid solution to form amorphous nanosized CaP.
• suitable non-aqueous solvents for use in this method include glycerol and ethylene glycol.
• the non-aqueous solvent is miscible with water.
• the non-aqueous solvent is miscible with acetone or another volatile polar solvent to allow it to readily removed by washing with such a solvent.
• the CaP formed in this method can then be treated by contacting it with water to convert it into a different form of CaP.
• ACP can be produced.
• the ACP can optionally be aged by contact with water at ambient temperature to produce HA.
• contact with water at elevated temperature and pressure, such as in an autoclave can produce b-TCP.
• Autoclaving involves heating the powder in a sealed container (e.g. a stainless steel bomb) in the presence of water. Since this is done at elevated temperatures (e.g. 180-220 °C), the pressure will be above 1 atmosphere, typically between 5 and 15 atmospheres.
• the particle size and surface area of the CaP produced can be controlled by controlling the temperature and duration of the contact with water.
• the specific surface area of the CaP is in the range of about 180 to about 380 m 2 /g as measured by the BET method (S. Brunauer, P.H. Emmet, E. Teller, J. Am. Chem. Soc. 1938, 60, 309-319).
• the specific surface area of the CaP is in the range of about 200 to about 350 m 2 /g, more preferably in the range of about 200 to about 250 m 2 /g.
• Amorphous nanosized CaP will tend to have a higher surface area than nanocrystalline CaP.
• X-ray diffraction may also be used to give a rough measurement of the surface area of CaP in a composite.
• the polymer may be dissolved from the composite using a suitable solvent (for example acetone) and the surface area of the CaP thus obtained may be measured by the BET method.
• the polymer used in the composites should be biodegradable in vivo, preferably degrading over a period of about 3 months to about 3 years, for example about 6 months to about 2 years, preferably over about 3 to about 12 months.
• the polymer used in the composites should also be biocompatible.
• the biodegradable polymer may be synthetic or naturally occurring.
• Suitable biodegradable polymers include synthetic polyesters such as poly(caprolactone) (PCL), poly(lactic acid) (PLA), poly(glycolic acid) (PGL), poly(vinyl alcohol) (PVA), and naturally occurring polymers such as soluble collagen, hyaluronic acid, gelatine and chitosan. These polymers undergo hydrolysis in the human body, producing non-toxic degradation products (L. Nair and C. Laurencin, Progress in polymer science, 2007, 32, 762-798).
• the biodegradable polymer may be water soluble or water insoluble, but water insoluble polymers are preferred. Polyesters such as PCL, PLA and PGL are water insoluble, whilst poly(vinyl alcohol) (PVA), soluble collagen, hyaluronic acid, gelatine and chitosan are water soluble.
• PVA poly(vinyl alcohol)
• the biodegradation speed can be governed by the choice of polymer.
• PCL generally degrades more slowly than PLA or PGA in vivo.
• PCL is the only polymer present in the composite.
• the polymer matrix may consist of PCL.
• PLA and PGL can degrade in vivo to produce acidic degradation products (lactic acid and glycolic acid respectively) which may give rise to undesirable inflammatory reactions.
• the degradation product of PCL in vivo (6-hydroxyhexanoic acid) is less likely to give rise to undesirable inflammatory reactions since it is less acidic; the pKa of lactic acid is 3.86 while the pKa of 6-hydroxyhexanoic acid is 4.75.
• the polymer matrix is formed from a single polymer, although blends may also be used.
• the composites do not include any copolymer(s) of lactic and glycolic acid, such as poly (D,L-lactic-co-glycolic) acid or a copolymer of poly(lactic) acid and poly(glycolic) acid.
• the biodegradable polymer is a homopolymer (i.e. is not a copolymer).
• the composites of the invention do not contain any copolymers.
• the composites of the present invention are porous once formed and before use in vivo.
• the pores in the composite comprise nanopores and micropores, where the nanopores are created by the nanosized CaP particles, and the micropores are created by the polymer network.
• the nanopores have a longest dimension of from about 1 to about 100 nm, and the micropores have the longest dimension of from about 1 to 100 pm.
• the size of the nanopores may be measured using SEM, and/or by nitrogen adsorption and desorption using the Barett-Joyner-Halenda (BJH) method.
• the size of the micropores can be measured using SEM and/or by mercury porosimetry.
• the porous composites of the invention have a porosity in the range of about 20 to about 95%, more preferably in the range of about 50 to about 90 %, and even more preferably in the range of about 60 to about 90%. Whilst high levels of porosity are desirable to promote bone growth in vivo, highly porous composites will have low mechanical strength and will not be suitable for all applications.
• the composite may further comprise additional voids created by removable supports. Such voids may have a longest dimension of about 5 to 40 mm. Voids can be introduced into the composite by solidifying the composite around a removable support, which when removed leaves voids in the composite.
• the composite may be moulded around a removable pin array. Following solidification of the composite, the pin array may be removed, leaving voids in the composite corresponding to the shape and size of the pin array.
• the pins may have any cross-section but cylindrical pins are preferred. Suitable diameters for cylindrical pins are about 0.25 to about 2 mm.
• the removable support may be made of metal, for example stainless steel.
• the surface of the support should be smooth, for example a polished metal surface.
• the presence of millimetre-sized voids in the composite may improve vascularization, i.e. growth of blood vessels, within the composite in vivo, for example when it implanted in a patient.
• the composites of the invention are hydrophilic when manufactured and remain hydrophilic as the polymer matrix biodegrades in vivo.
• hydrophilic is meant they have a contact angle with water of ⁇ 90°. The lower the contact angle, the more hydrophilic the composite is and the better it will be at promoting bone growth in vivo.
• the composites have a contact angle with water of about 70° or below, more preferably of about 60° or below.
• the contact angle of a sample can be measured by placing a drop of Type 1 water (resistivity 18.2 MW/cm) on a flat part of the sample and measure the contact angle between the drop and the surface with a goniometer.
• Type 1 water resistivity 18.2 MW/cm
• the porosity and hydrophilicity of the composites promote rapid infiltration and adsorption of bodily fluids, osteointegration and adherence of new bone cells.
• the polymer of the matrix will biodegrade and the CaP will dissolve, leading to the composite eventually being replaced by new bone tissue.
• the nanosized CaP is homogeneously dispersed throughout the polymer matrix.
• some of the CaP will initially be completely surrounded by polymer (i.e. embedded within the polymer) and some will be exposed at the polymer surface, including at the surface of pores within the polymer matrix.
• the exposed CaP renders the composite as a whole hydrophilic even when a hydrophobic polymer such as PCL or a polymer with low hydrophilicity such as PLA is used to form the composite.
• the composites of the invention have an open cell structure. This allows infiltration of new bone cells into the matrix to promote growth of new bone.
• the composites of the invention Due to the presence of the dispersed CaP, the composites of the invention have a higher surface area than do similar porous polymer matrices made without incorporation of CaP. This indicates that at least some of the nanosized CaP is exposed on the surface of the polymer matrix and is contributing to the surface area of the composite. Suitable surface areas for the composite are in the range of 5-50 m 2 /g, preferably 7 to 50 m 2 /g.
• the stiffness of the composite may be controlled by controlling the relative amounts of polymer and CaP used. Increasing the amount of CaP relative to the polymer will increase the stiffness of the composite but will tend to make it more brittle. Lowering the amount of CaP relative to the amount of polymer will increase the flexibility but decrease the stiffness of the composite.
• the hydrophilicity of the composite may also be controlled by controlling the relative amounts of polymer and CaP used, with hydrophilicity increasing as the amount of CaP used increases.
• Suitable weight ratios of CaP to polymer include about 1 :4 to about 3:1, preferably 1 :3 to about 1:1, preferably about 1 :2. At ratios above 1 : 1 , for example 2CaP: 1PCL, the composites become brittle and harder to handle.
• the composites of the invention do not contain any NaCl.
• the composite may be ground into particles, preferably of about 0.1 to about 1 mm in diameter, and the particles suspended in a pharmaceutically acceptable solvent.
• a pharmaceutically acceptable solvents for injection include glycerol, water, propylene glycol and PEG- 12.
• Composites containing ratios of CaP to polymer of above 1 : 1 are particularly suitable for grinding into particles.
• a first process for the preparation of a porous hydrophilic composite comprising:
• step (b) solidifying the mixture of step (a) to form a gel
• step (c) removing the first and second solvents from the gel of step (b) by washing with a third solvent to leave a porous hydrophilic composite containing the nanosized CaP dispersed throughout a porous polymer matrix.
• Step (a) involves mixing a solution of a biodegradable polymer in a first solvent with nanosized calcium phosphate (CaP), preferably with a dispersion of nanosized calcium phosphate (CaP) in a second solvent, until the CaP is homogeneously distributed throughout the resulting mixture.
• CaP nanosized calcium phosphate
• the first solvent should be one in which the polymer can be fully dissolved but where the solubility is highly temperature dependent over a convenient temperature range (such as between about 0 °C and 50 °C).
• a convenient temperature range such as between about 0 °C and 50 °C.
• first solvents in which the polymer has limited solubility at temperatures below about 10 °C, such as below about 5 °C.
• the first solvent is one in which the polymer can be fully dissolved in the first solvent at ambient temperate (20 °C) or with warming, for example on warming to 50 °C or less, such as 40-45 °C, within a convenient time period. Dissolution of the polymer can be facilitated by stirring or other agitation of the solvent.
• the minimum volume of first solvent required to dissolve the polymer is used, both for cost reasons and to facilitate later solvent removal.
• the amount of first and second solvents should also not be so high that a gel cannot be formed in step (b).
• the amount of solvent used must however be balanced against the desired degree of porosity of the final product as the total volume of first and second solvents used will influence the porosity of the final composite, with higher solvent volumes tending to lead to more porous composites.
• nanosized CaP particles tend to agglomerate and are difficult to disperse in the polymer solution.
• the CaP is therefore preferably used as a dispersion in a second solvent.
• the nanosized CaP may be synthesised using a method which results directly in formation of a suitable dispersion.
• the dispersion of CaP in the second solvent does not contain anything other than the CaP and the second solvent.
• the first and second solvents may be the same or different, but are preferably the same. If the first and second solvents are different, the second solvent should be miscible with the first and should not adversely influence the solubility of the polymer.
• suitable first solvents include tetrahydrofuran (THF), dioxane, ethyl acetate and acetone, with acetone being preferred.
• suitable second solvents for use when the polymer is water insoluble include THF, dioxane, ethyl acetate, acetone and mixtures thereof, with acetone being preferred.
• poly(vinyl alcohol) PVA
• soluble collagen soluble collagen
• hyaluronic acid soluble collagen
• gelatine gelatine or chitosan
• suitable first and second solvents include water, ethanol, methanol and iso-propyl alcohol (IP A), with water being preferred.
• first and second solvents which are biocompatible, so that any solvent residue remaining in the porous composite does not pose a health risk when the composite is used in vivo. For this reason, acetone is a preferred first and second solvent when water insoluble polymers are used, and water is a preferred first and second solvent when water soluble polymers are used.
• the solution of the biodegradable polymer in the first solvent and the nanosized calcium phosphate (CaP), such as the dispersion of nanosized calcium phosphate (CaP) in the second solvent, should be mixed until the CaP is homogeneously distributed throughout the resulting mixture. This may take about an hour. Homogeneous distribution of the CaP in the mixture may be assessed visually.
• CaP nanosized calcium phosphate
• the mixture may be cooled down until the mixture starts to solidify to form a gel. Conveniently, this can be done by allowing the mixture to cool to room temperature (if required) and then placing it in a refrigerator at about 4-5 °C. Alternatively, the mixture may be placed directly in a refrigerator. Lower temperatures may also be used, for example 0 °C or below, but these are less convenient from a processing standpoint. Alternatively, the mixture may also be cooled by pouring into a mold which is at a lower temperature than the mixture. For example, the mixture may be poured into a pre-cooled mold. Solidification to form a gel may then be completed by placing the filled mold in a refrigerator. Molds may be pre-cooled by placing in a refrigerator or freezer prior to use.
• step (b) of the first method preferably comprises cooling the mixture of step (a) to solidify it.
• the mixture starts to solidify, it forms a gel incorporating the CaP and the first and second solvents.
• the gel that is being formed may be regularly agitated (e.g. by stirring or shaking) to avoid sedimentation of the CaP particles. This helps ensure a homogenous distribution of the CaP in the resulting composite material.
• the entire mixture may be transferred to a filter to facilitate the later washing step (c).
• the resulting gel is washed with a third solvent to remove the first and second solvents. Removal of the first and second solvents from the solidified gel results in pores in the polymer matrix.
• Solidification of the mixture can be assessed by seeing whether or not the mixture will flow when the container holding it is tipped. Alternatively, if small waves form on the surface of the mixture when the side of the container is tapped gently, this indicates that the mixture has not yet solidified.
• the third solvent is different to the first and second solvents.
• the third solvent should be miscible with the first and second solvents, such that they dissolve in the third solvent and are removed by the washing.
• the third solvent should not be a solvent for the polymer.
• suitable third solvents include water, IP A, ethanol and methanol.
• the third solvent is IPA or water, more preferably water.
• suitable third solvents include THF, dioxane, ethyl acetate, ethylene glycol, glycerol and acetone, with acetone being preferred.
• amorphous HA is used as the CaP
• use of water as the third solvent may lead to conversion to crystalline HA.
• methanol is a preferred third solvent when the CaP is amorphous HA.
• washing step (c) may also help promote final solidification of the polymer. Removal of the first and second solvents from the gel in washing step (c) leaves a behind a porous polymer matrix with nanosized CaP distributed throughout.
• the first and second solvents are both acetone and the third solvent is water. More preferably, the polymer is PCL, the first and second solvents are both acetone and the third solvent is water
• the resulting porous solid composite may be washed with a fourth solvent to remove traces of water.
• the fourth solvent should be miscible with but more volatile than water, such that traces of the fourth solvent can be easily removed by drying the resulting composite. It should also not be a solvent for the polymer. Suitable fourth solvents include MeOH, EtOH and iso propyl alcohol (IP A), preferably IPA. IPA is a preferred fourth solvent as it is easy to remove by drying at 40 °C, it is not very toxic if small amounts were to be left in the composite, and it is not very hygroscopic when compared to methanol and ethanol which always contain small amounts of water and so can leave traces of moisture in the structure.
• IPA is a preferred fourth solvent as it is easy to remove by drying at 40 °C, it is not very toxic if small amounts were to be left in the composite, and it is not very hygroscopic when compared to methanol and ethanol which always contain small amounts of water and so can leave traces of moisture in the structure.
• the polymer cooling and solidification step (step (b)) may take place in a mold to control the shape of the resulting composite. Once the polymer has solidified sufficiently, the composite can be removed from the mold and immersed in the third solvent to remove the first and second solvents. If the third solvent is water, the resulting porous solid molded composite may be subsequently immersed in a fourth solvent as defined above to remove traces of water.
• Voids can also be introduced into the composite by solidifying the composite around a removable support, which when removed leaves voids in the composite corresponding to the shape and size of the removable support.
• the composite may be moulded around a removable pin array.
• the pin array may be removed, leaving voids in the composite corresponding to the shape and size of the pin array.
• Such voids may take the form of channels or holes in the composite material have a longest dimension of about 5 to 40 mm and a width or diameter of about 0.25 to 2 mm.
• the processes of the invention have a number of advantages over prior art processes to form bone scaffolds. For example, the use of strong acids which may dissolve the CaP and/or cause polymer degradation is avoided. Heating to melt the polymer is not required, and suitable choice of the first solvent avoids the need for excessive heating to dissolve the polymer. Cooling below 0 °C to form a gel is also not normally necessary.
• the mixture formed in step (a) may also be deposited using a 3D printer. This can allow complex shaped composites to be built up layer by layer.
• the mixture can be ejected from a nozzle which is immersed in water or other suitable third solvent, depending on the nature of the polymer. The movement of the nozzle is controllable in the x-y-z directions, which allows for a controlled layer-by-layer build up of the composite structure.
• the composites of the present invention may be used as scaffolds for the promotion of new bone growth.
• the composite may be combined with a load-bearing, non-degradable structure, which may also be referred to as an implant.
• a substrate may be dipped into the mixture formed from the biodegradable polymer, the first solvent, the nanosized calcium phosphate (CaP) and the second solvent and then removed.
• a thin layer of the mixture will be left on the surface of the substrate, which after solidification of the polymer and removal of the first and second solvents will result in a thin layer of composite present as a coating on the substrate surface.
• the dipping step may be repeated to build up multiple layers of composite on the substrate surface.
• the solvent removal may be carried out by dipping the coated substrate in the third solvent.
• the first and second solvents may be removed by evaporation.
• step (c) of the first method leads to a high degree of porosity in the resulting composite, such as about 50% to about 90%. If the first and second solvents are instead allowed to evaporate, the voids in the polymer network left by the evaporating solvent(s) tend to collapse such that the polymer chains can aggregate and form a denser structure, for example with a maximum porosity of only 10-20%.
• the thickness and porosity of the layer on the substrate surface may therefore be controlled by choice of the method used to remove the first and second solvents. If the first and second solvents are removed using a third solvent, as in the first method of the invention, a porous layer will result. Alternatively, if the first and second solvents are removed by evaporation, a denser (i.e. less porous) and thinner layer will result.
• a composite layer formed by dipping may be from about 400 nm to about 100 micrometers in thickness, for example 500 nm to 50 micrometers thick.
• a hydrophilic composite for promoting bone growth comprising:
• step (al) mixing a solution of a biodegradable polymer in a first solvent with a dispersion of nanosized calcium phosphate (CaP) in a second solvent until the CaP is homogeneously distributed throughout the resulting mixture; (bl) solidifying the mixture of step (a) on a substrate to form a gel; and (cl) removing the first and second solvents from the gel of step (b) by evaporation to leave a layer of a porous hydrophilic composite containing the nanosized CaP dispersed throughout a polymer matrix on the surface.
• CaP nanosized calcium phosphate
• Pre-cooling of the substrate, for example to 4-5 °C, before the dipping step can help initiate solidification of the polymer onto the substrate surface.
• the first and second solvents are both acetone and the polymer is PCL.
• At least a portion of a substrate may be fully or partially immersed in the mixture formed in step (a) before the polymer solidifies.
• the polymer will then solidify around the substrate.
• a scaffold containing some or all of the substrate embedded within the porous composite will be formed.
• a substrate can be introduced into the mixture in any suitable vessel, for example a mold.
• the substrate may be placed in a mold and the mixture then introduced into the mold. If the substrate is placed in a mold, the overall shape of the resulting scaffold will be controlled by the shape of the mold.
• formation of composite can be directed to surfaces of the substrate which are not in contact with the mold.
• Figure 5b shows the formation of composite on the inner surface of a spinal cage. This was produced by placing the case in a suitably shaped Teflon mold in which the outer surface of the cage was in contact with the mold, thus excluding it from composite formation.
• step (b) of the first method can therefore comprise solidifying the polymer on or around a substrate.
• one or more layers of composite may be deposited on the substrate surface by dipping, before immersion of the coated substrate in the mixture. This may allow formation of layers of composite of different density and porosity depending on the method used for removal of the first and second solvents.
• a denser layer will generally adhere more strongly to the underlying substrate, whereas a more porous layer will better promote bone growth.
• a first layer is formed by allowing the first and second solvents to evaporate and a second and any subsequent layers is/are formed by washing to remove the first and second solvents.
• Suitable substrates for use in the invention include orthopaedic and dental implants, including but not limited to screws, spinal fusion cages, wires, meshes, nails, pins, rods, plates, hip stems, ostomy bag ports, bone anchored hearing aids, and dental implant abutments.
• Suitable substrates include, but are not limited to, substrates made from metals such as titanium and its alloys, zirconium and its alloys, stainless steel, tantalum, NiTi alloys and cobalt-chrome alloys; ceramics such as alumina, zirconia, alumina toughened zirconia, and Si3N4; graphitic material such as graphene and pyrocarbon; and polymers such as polypropylene, polyethylene, polysulfone (PSU), polyether ketone (PEKK), poly(styrene), poly(carbonate), poly(ethylene terephthalate) and PEEK.
• metals such as titanium and its alloys, zirconium and its alloys, stainless steel, tantalum, NiTi alloys and cobalt-chrome alloys
• ceramics such as alumina, zirconia, alumina toughened zirconia, and Si3N4
• graphitic material such as graphene and pyrocarbon
• polymers such as poly
• Preferred substrates include titanium and its alloys, zirconium and its alloys, stainless steel, tantalum, NiTi alloys, cobalt- chrome alloys, alumina, zirconia, alumina toughened zirconia, pyrocarbon, polysulfone (PSU), polyether ketone (PEKK), poly(styrene), poly(carbonate) and PEEK. More preferred substrates include titanium and its alloys, stainless steel, zirconia, alumina toughened zirconia, pyrocarbon, and PEEK, most preferably titanium or PEEK.
• hydrophilicity of the porous hydrophilic composites formed by the above methods may be further increased by treating the composites with a biocompatible organic polyol.
• the processes of the invention may therefore further comprise, after step (c) or step (cl):
• the organic polyol should be biocompatible. Suitable organic polyols include glycerol, propylene glycol, polyvinyl alcohol or low molecular weight polyethylene glycols such as PEG- 12. Suitable polyethylene glycols are those with a molecular weight of about 200-2000 g/mol. A preferred polyol is glycerol.
• the polyol is applied to the composites by immersing the composite in a solution of the polyol in a volatile organic solvent.
• volatile organic solvent is meant a solvent which is more volatile than the polyol. Suitable volatile organic solvents are non-toxic. The solvent should also be completely miscible with the organic polyol. If the polyol is a solid, it should be soluble in the solvent. The solvent should not be a solvent for the polymer in the polymer matrix.
• Suitable volatile organic solvents include isopropanol and ethanol.
• a suitable solution contains about 0.25 - 50 wt. % of the organic polyol, for example about 0.25 to 50 wt.% of glycerol in isopropanol.
• the mixture contains at least 0.5 wt. % glycerol in isopropanol.
• the composite is immersed in the solution for up to 10 minutes, more preferably up to 5 minutes.
• the composite will float in the solution initially and will then sink as solution displaces air and fills the pores in the composite.
• the pores of the composite have been filled with the solution when the composite sinks and there are no longer any visible air bubbles being released from the composite.
• After removal of the composite from the solution it is dried to remove the volatile organic solvent. Drying can involve leaving the composite at room temperature to allow the volatile organic solvent to evaporate.
• the treated composite may also be heated to speed up evaporation of the volatile organic solvent. The heating temperature should not be high enough to evaporate the polyol or damage the polymer matrix.
• Suitable temperatures for such heating are in the range of about 30 to 40 °C, preferably about 35 °C.
• the removal of the volatile solvent can be monitored by weighing the composite during the heating. Once the volatile solvent has been removed, any increase in weight of the treated composite compared to the starting composite before immersion can be attributed to the polyol.
• the polyol is adsorbed on at least a portion of an internal and/or external surface of the composite and/or forms a coating on at least a portion of an internal and/or external surface thereof, thereby increasing the hydrophilicity.
• internal surfaces of the composite is meant the surfaces of any pores or voids within the composite.
• the invention therefore provides a porous hydrophilic composite for promoting bone growth, as described herein, wherein the porous hydrophilic composite further comprises from about 0.5 to 50 wt% of a biocompatible organic polyol.
• the wt.% is based on the total weight of the composite and the biocompatible organic polyol.
• the biocompatible organic polyol may be adsorbed on at least a portion of an internal and/or external surface of the porous hydrophilic composite and/or forms a coating on at least a portion of an internal and/or external surface thereof.
• biocompatible organic polyol will improve the hydrophilicity, and will also make the composite softer and less brittle/friable.
• Embodiment 1 A porous hydrophilic composite for promoting bone growth, the composite comprising:
• nanosized calcium phosphate (CaP) homogeneously dispersed throughout the polymer matrix, wherein the CaP has a specific surface area in the range of about 180 to about 380 m 2 /g; with the proviso that the composite does not contain any copolymer(s) of lactic acid and glycolic acid.
• Embodiment 2 The porous hydrophilic composite of Embodiment 1, wherein the nanosized CaP is amorphous calcium phosphate (ACP), beta-TCP, calcium deficient HA (CDHA) or hydroxyapatite (HA)
• Embodiment 3 The porous hydrophilic composite of Embodiment 1, wherein the CaP is nanocrystalline.
• Embodiment 4 The porous hydrophilic composite of any preceding Embodiment, wherein the CaP is HA.
• Embodiment 5 The porous hydrophilic composite of any of Embodiments 1 to 3, wherein the CaP is ACP.
• Embodiment 6 The porous hydrophilic composite of any preceding Embodiment, wherein the polymer matrix comprises or consists of poly(caprolactone) (PCL), poly(lactic acid) (PLA), poly(glycolic acid) (PGL), poly(vinyl alcohol) (PVA), soluble collagen, hyaluronic acid, gelatine or chitosan.
• PCL poly(caprolactone)
• PLA poly(lactic acid)
• PGL poly(glycolic acid)
• PVA poly(vinyl alcohol)
• soluble collagen hyaluronic acid
• gelatine or chitosan chitosan
• Embodiment 7 The porous hydrophilic composite of any preceding Embodiment, wherein the polymer matrix comprises or consists of s-poly(caprolactone) (PCL).
• PCL s-poly(caprolactone)
• Embodiment 8 The porous hydrophilic composite of any preceding Embodiment, wherein the ratio of CaP to polymer matrix is about 1 :4 to about 3 : 1 by weight.
• Embodiment 9 The porous hydrophilic composite of any preceding Embodiment which comprises nanopores and micropores.
• Embodiment 10 The porous hydrophilic composite of any preceding Embodiment, wherein the CaP has a specific surface area in the range of about 200 to about 350 m 2 /g.
• Embodiment 11 The porous hydrophilic composite of any preceding Embodiment which has a specific surface area in the range of about 5 to about 50 m 2 /g.
• Embodiment 12 The porous hydrophilic composite of any preceding Embodiment further comprising from about 0.5 to 50 wt% of a biocompatible organic polyol, based on the total weight of the composite including the biocompatible organic polyol.
• Embodiment 13 The porous hydrophilic composite of any preceding Embodiment, wherein the organic polyol is adsorbed on at least a portion of an internal and/or external surface thereof and/or forms a coating on at least a portion of an internal and/or external surface thereof.
• Embodiment 14 The porous hydrophilic composite of any preceding claim wherein the organic polyol is glycerol, propylene glycol, polyvinyl alcohol or a polyethylene glycol with a molecular weight in the range of about 200 to about 2,000.
• the organic polyol is glycerol, propylene glycol, polyvinyl alcohol or a polyethylene glycol with a molecular weight in the range of about 200 to about 2,000.
• Embodiment 15 The porous hydrophilic composite of any preceding Embodiment, wherein the organic polyol is glycerol.
• Embodiment 16 The porous hydrophilic composite of any preceding Embodiment, which has a porosity of 20-95%.
• Embodiment 17 The porous hydrophilic composite of any preceding Embodiment, which has a porosity of 50-90%.
• Embodiment 18 The porous hydrophilic composite of any preceding Embodiment, which has a porosity of 60-90%.
• Embodiment 19 The porous hydrophilic composite of any preceding Embodiment which has a contact angle with water of 70° or less.
• Embodiment 20 The porous hydrophilic composite of any preceding Embodiment which has a contact angle with water of 60° or less.
• Embodiment 21 A scaffold for use in bone reconstruction, the scaffold comprising a substrate and the porous hydrophilic composite of any preceding Embodiment.
• Embodiment 22 The scaffold of Embodiment 21, wherein the substrate is selected from orthopaedic and dental implants.
• Embodiment 23 The scaffold of Embodiment 22, wherein the substrate is selected from screws, spinal fusion cages, wires, meshes, nails, pins, rods, plates, hip stems, ostomy bag ports, bone anchored hearing aids, and dental implant abutments.
• Embodiment 24 The scaffold of any of Embodiments 21 to 23, wherein the substrate is made from metal, ceramic, graphitic material or a polymer.
• Embodiment 25 The scaffold of any of Embodiments 21 to 24, wherein the substrate is made from titanium and its alloys, zirconium and its alloys, stainless steel, tantalum, NiTi alloys, cobalt-chrome alloys; alumina, zirconia, alumina toughened zirconia, S1 3 N 4 ; graphene, pyrocarbon; polypropylene, polyethylene, polysulfone (PSU), polyether ketone (PEKK), poly(styrene), poly(carbonate), poly( ethylene terephthalate) or PEEK.
• the substrate is made from titanium and its alloys, zirconium and its alloys, stainless steel, tantalum, NiTi alloys, cobalt-chrome alloys; alumina, zirconia, alumina toughened zirconia, S1 3 N 4 ; graphene, pyrocarbon; polypropylene, polyethylene, polysulfone (PSU), polyether ketone (PEKK
• Embodiment 26 The scaffold of any of Embodiments 21 to 25, wherein the substrate is made from titanium and its alloys, zirconium and its alloys, stainless steel, tantalum, NiTi alloys, cobalt-chrome alloys, alumina, zirconia, alumina toughened zirconia, pyrocarbon, polysulfone (PSU), polyether ketone (PEKK), poly( styrene), poly( carbonate) or PEEK.
• the substrate is made from titanium and its alloys, zirconium and its alloys, stainless steel, tantalum, NiTi alloys, cobalt-chrome alloys, alumina, zirconia, alumina toughened zirconia, pyrocarbon, polysulfone (PSU), polyether ketone (PEKK), poly( styrene), poly( carbonate) or PEEK.
• Embodiment 27 The scaffold of any of Embodiments 21 to 26, wherein the substrate is made from titanium and its alloys, stainless steel, zirconia, alumina toughened zirconia, pyrocarbon, or PEEK.
• Embodiment 28 The scaffold of any of Embodiments 21 to 27, wherein the substrate is made from titanium or PEEK.
• Embodiment 29 The scaffold of any of Embodiments 21 to 28, wherein the composite is present as a coating on a surface of the substrate.
• Embodiment 30 The scaffold of any of Embodiments 21 to 28, wherein the substrate is partially or completely embedded in the composite.
• Embodiment 31 The scaffold of Embodiment 29, wherein the coating comprises at least two layers of different porosities.
• Embodiment 32 The scaffold of Embodiment 31, wherein the coating comprises a first layer nearest to the substrate with a porosity below 20% and a second layer on top of the first layer with a porosity greater than 20%, preferably a porosity of 50-90%.
• Embodiment 33 A process for the preparation of a porous hydrophilic composite for promoting bone growth, the process comprising:
• step (b) solidifying the mixture of step (a) to form a gel
• step (c) removing the first and second solvents from the gel of step (b) by washing with a third solvent to leave a porous hydrophilic composite containing the nanosized CaP homogeneously dispersed in a porous polymer matrix.
• Embodiment 34 The process of Embodiment 29 wherein step (a) involves mixing the solution of the biodegradable polymer in a first solvent with a dispersion of nanosized calcium phosphate (CaP) in a second solvent until the CaP is homogeneously distributed throughout the resulting mixture.
• step (a) involves mixing the solution of the biodegradable polymer in a first solvent with a dispersion of nanosized calcium phosphate (CaP) in a second solvent until the CaP is homogeneously distributed throughout the resulting mixture.
• CaP nanosized calcium phosphate
• Embodiment 35 The process of Embodiment 29 or 30, wherein step (b) is carried out in a mold.
• Embodiment 36 The process of Embodiment 29 or 30, wherein steps (b) and (c) comprise printing the mixture of step (a) into a bath of the third solvent.
• Embodiment 37 The process of any of Embodiments 29 to 32, wherein the third solvent is water, iso-propyl alcohol (IP A), ethanol or methanol.
• IP A iso-propyl alcohol
• Embodiment 38 The process of any of Embodiments 29 to 33, wherein the third solvent is IPA or water.
• Embodiment 39 The process of any of Embodiments 29 to 33, wherein the third solvent is water.
• Embodiment 40 The process of any of Embodiments 29 to 32, wherein the third solvent is THF, dioxane or acetone.
• Embodiment 41 The process of any of Embodiments 29 to 32, wherein the third solvent is acetone.
• Embodiment 42 A process for the preparation of a hydrophilic composite, the process comprising:
• step (bl) solidifying the mixture of step (al) on a substrate to form a gel; and (cl) removing the first and second solvents from the gel of step (bl) by evaporation to leave a layer of a porous hydrophilic composite containing the nanosized CaP dispersed throughout a porous polymer matrix on the substrate.
• Embodiment 43 The process of Embodiment 42 wherein step (al) involves mixing the solution of the biodegradable polymer in a first solvent with a dispersion of nanosized calcium phosphate (CaP) in a second solvent until the CaP is homogeneously distributed throughout the resulting mixture.
• step (al) involves mixing the solution of the biodegradable polymer in a first solvent with a dispersion of nanosized calcium phosphate (CaP) in a second solvent until the CaP is homogeneously distributed throughout the resulting mixture.
• CaP nanosized calcium phosphate
• Embodiment 44 The process of Embodiment 42 or 43 further comprising, after step (cl), solidifying additional mixture of step (a) on the layer formed in step (cl) to form a gel; and removing the first and second solvents from the gel by washing with a third solvent to leave a porous polymer matrix containing the nanosized CaP homogeneously dispersed in the polymer matrix on top of the layer, preferably wherein the third solvent is as defined in any of Embodiments 33 to 37.
• Embodiment 45 The process of any of Embodiments 33 to 44, wherein the first and second solvents are the same.
• Embodiment 46 The process of any of Embodiments 33 to 39 or 42 to 45, wherein the first and second solvents are independently selected from THF, dioxane and acetone.
• Embodiment 47 The process of any of Embodiments 33 to 39 or 42 to 45, wherein the first and second solvents are both acetone.
• Embodiment 48 The process of any of any of Embodiments 33 to 36 or 40 to 45, wherein the first and second solvents are independently selected from water, iso-propyl alcohol (IP A), ethanol or methanol.
• IP A iso-propyl alcohol
• ethanol ethanol
• Embodiment 49 The process of any of Embodiments 33 to 36 or 40 to 45, wherein the first and second solvents are independently selected from IPA or water.
• Embodiment 50 The process of any of Embodiments 33 to 36 or 40 to 45, wherein the first and second solvents are both water.
• Embodiment 51 The process of any of Embodiments 33 to 50, wherein the CaP is prepared by mixing a dispersion of a non-phosphate calcium salt in a suitable solvent with an aqueous solution of phosphoric acid.
• Embodiment 52 The process of Embodiment 51, wherein the non-phosphate calcium salt is calcium oxide or calcium hydroxide.
• Embodiment 53 The process of Embodiment 51 or 52, wherein the suitable solvent is water, ethylene glycol or glycerol.
• Embodiment 54 The process of any of Embodiments 33 to 53, wherein step (b) or step (bl) comprises cooling the mixture of step (a).
• Embodiment 55 The process of any of Embodiments 33 to 54, wherein step (b) or step (bl) comprises solidifying the mixture on or around at least a portion of a substrate.
• Embodiment 56 The process of Embodiment 55, wherein the substrate is selected from orthopaedic and dental implants.
• Embodiment 57 The process of Embodiment 56, wherein the substrate is selected from screws, spinal fusion cages, wires, meshes, nails, pins, rods, plates, hip stems, ostomy bag ports, bone anchored hearing aids, and dental implant abutments.
• Embodiment 58 The process of any of Embodiments 54 to 57, wherein the substrate is made from metal, ceramic, graphitic material or a polymer.
• Embodiment 59 The process of any of Embodiments 54 to 58, wherein the substrate is made from titanium and its alloys, zirconium and its alloys, stainless steel, tantalum, NiTi alloys, cobalt-chrome alloys; alumina, zirconia, alumina toughened zirconia, S1 3 N 4 ; graphene, pyrocarbon; polypropylene, polyethylene, polysulfone (PSU), polyether ketone (PEKK), poly(styrene), poly(carbonate), poly( ethylene terephthalate) or PEEK.
• the substrate is made from titanium and its alloys, zirconium and its alloys, stainless steel, tantalum, NiTi alloys, cobalt-chrome alloys; alumina, zirconia, alumina toughened zirconia, S1 3 N 4 ; graphene, pyrocarbon; polypropylene, polyethylene, polysulfone (PSU), polyether ketone
• Embodiment 60 The process of any of Embodiments 54 to 59, wherein the substrate is made from titanium and its alloys, zirconium and its alloys, stainless steel, tantalum, NiTi alloys, cobalt-chrome alloys, alumina, zirconia, alumina toughened zirconia, pyrocarbon, polysulfone (PSU), polyether ketone (PEKK), poly( styrene), poly( carbonate) or PEEK.
• the substrate is made from titanium and its alloys, zirconium and its alloys, stainless steel, tantalum, NiTi alloys, cobalt-chrome alloys, alumina, zirconia, alumina toughened zirconia, pyrocarbon, polysulfone (PSU), polyether ketone (PEKK), poly( styrene), poly( carbonate) or PEEK.
• Embodiment 61 The process of any of Embodiments 54 to 60, wherein the substrate is made from titanium and its alloys, stainless steel, zirconia, alumina toughened zirconia, pyrocarbon, or PEEK.
• Embodiment 62 The process of any of Embodiments 54 to 61, wherein the substrate is made from titanium or PEEK.
• Embodiment 63 The process of any of Embodiments 54 to 62, wherein the process further comprises:
• Embodiment 64 The process of Embodiment 63, wherein the organic polyol is glycerol, propylene glycol, polyvinyl alcohol or a polyethylene glycol with a molecular weight in the range of about 200 to about 2,000.
• the organic polyol is glycerol, propylene glycol, polyvinyl alcohol or a polyethylene glycol with a molecular weight in the range of about 200 to about 2,000.
• Embodiment 65 The process of Embodiments 63 to 64, wherein the organic polyol is glycerol.
• Embodiment 66 The process of any of Embodiments 54 to 65 wherein the CaP has a specific surface area in the range of about 180 to about 380 m 2 /g.
• Embodiment 67 The process of Embodiment 66, wherein the CaP has a specific surface area in the range of about 200 to about 350 m 2 /g.
• Embodiment 68 The process of any of Embodiments 33 to 62, wherein the nanosized CaP is amorphous calcium phosphate (ACP), beta-TCP, calcium deficient HA (CDHA) or hydroxyapatite (HA)
• ACP amorphous calcium phosphate
• beta-TCP beta-TCP
• CDHA calcium deficient HA
• HA hydroxyapatite
• Embodiment 69 The process of any of Embodiments 33 to 63, wherein the CaP is nanocrystalline.
• Embodiment 70 The process of any of Embodiments 33 to 64, wherein the polymer matrix comprises or consists of poly(caprolactone) (PCL), poly(lactic acid) (PLA), poly(glycolic acid) (PGL), poly(vinyl alcohol) (PVA), collagen, hyaluronic acid, chitin or chitosan.
• PCL poly(caprolactone)
• PLA poly(lactic acid)
• PDL poly(glycolic acid)
• PVA poly(vinyl alcohol)
• collagen hyaluronic acid
• chitin or chitosan chitosan
• Embodiment 71 The process of any of Embodiments 33 to 65, wherein the polymer matrix comprises or consists of poly(caprolactone) (PCL).
• PCL poly(caprolactone)
• Embodiment 72 The process of any of Embodiments 33 to 66, wherein the ratio of CaP to polymer is aboutl :4 to about 3: 1 by weight.
• Embodiment 73 The process of any of Embodiments 33 to 72, wherein the CaP has a specific surface area in the range of about 200 to about 350 m 2 /g.
• Embodiment 74 The process of any Embodiments 63 to 65, wherein the solution is a solution of the biocompatible organic polyol in a volatile organic solvent.
• Embodiment 75 The process of Embodiment 74, wherein the volatile organic solvent is isopropanol or ethanol.
• Embodiment 76 A method for the preparation of nanosized CaP, the method comprising mixing a dispersion of a non-phosphate calcium salt in a suitable non-aqueous solvent with an aqueous phosphoric acid solution to form amorphous nanosized CaP, and optionally contacting the amorphous CaP with water to convert it to an alternative form of CaP.
• Embodiment 77 A product obtainable by the process of any of Embodiments 33 to 75.
• Embodiment 78 An injectable formulation comprising a dispersion of particles of the porous hydrophilic composite of any of Embodiments 1-20 or 77 and a pharmaceutically acceptable solvent.
• Embodiment 79 The injectable formulation of Embodiment 78, wherein the pharmaceutically acceptable solvent is selected from glycerol, water for injection, propylene glycol and PEG- 12.
• Embodiment 80 A method for the preparation of nanosized CaP, the method comprising: mixing a dispersion of a non-phosphate calcium salt in a suitable non-aqueous solvent with an aqueous phosphoric acid solution to form amorphous nanosized CaP; and optionally contacting the amorphous nanosized CaP with water to convert it to another form of CaP.
• Embodiment 81 The method of Embodiment 80, wherein the non-aqueous solvent is selected from glycerol and ethylene glycol.
• the invention includes any and all combinations of preferred features and embodiments disclosed herein.
• all the preferred features of the composites are also preferred features of composites and coated substrates obtainable by the methods of the invention.
• Ethylene glycol (anhydrous, 99 %), isopropanol (99.5 %), glycerol (anhydrous, 99%), CaO, H3PO4 (85 %) and poly(caprolactone) 80 000 g/mol (PCL) were obtained from Sigma Aldrich, Sweden.
• a Zeiss FEG-SEM Sigma 300 with Gemini optics was used for the SEM analysis.
• a Bruker D8 instrument with CuKa radiation (1.54 A) was used.
• a Micromeritics TriStar instrument was used for the nitrogen adsorption analysis.
• the acetone / CaP gel (with a total weight of approximately 25 g) prepared in Step la) was transferred to a bottle and 75 ml of acetone was added (to give a total acetone volume of approximately 100 ml). The resulting mixture was stirred for 12 hours.
• 10 g of PCL was mixed with 80 ml of acetone, and the bottle was heated to 42 °C for 12 hours under stirring to dissolve the PCL.
• the PCL / acetone mixture was then added to the acetone / CaP gel mixture and allowed to stir for approximately 1 hour at 42 °C. Stirring was then continued as the mixture was cooled to room temperature.
• a sample of the foam produced in Step 1 c) was sputtered with gold and analysed using SEM.
• a representative image is shown in Figure 10. As seen from this image, the pores of the foam are between 0.25-10 pm in size. It can also be seen that there are no large agglomerates of HA visible and that the HA crystals are evenly dispersed in the polymer matrix.
• a portion of the foam was also analysed with nitrogen adsorption (BET). Analysis of the foam gave a specific surface area of 22.0 m 2 /g.
• BET nitrogen adsorption
• a pure PCL foam was also synthesized. This was done using the procedure described in Step lc), without any addition of CaP/acetone and using a total amount of 160 ml of acetone (an extra amount of 80 ml acetone was added to compensate for the extra amount that would otherwise come from the acetone / CaP gel).
• the pure PCL foam had a specific surface area of 6.2 m 2 /g.
• the acetone / CaP gel prepared in Step 2a) was transferred to a bottle and 75 ml of acetone was added. The resulting mixture was stirred for 12 hours.
• 10 g of PCL was mixed with 80 ml of acetone, and the bottle was heated to 42 °C for 12 hours under stirring to dissolve the PCL.
• the PCL / acetone mixture was then transferred to the acetone / CaP gel mixture and allowed to stir for approximately 1 hour at 42 °C. Stirring was then continued as the mixture was cooled to room temperature. It was then placed in a refrigerator at 4-5 °C for 1 hour, with shaking approximately every 5 minutes.
• the resulting ACP / acetone / PCL gel was placed in a glass filter which had been cooled to 4 °C. Upon pouring the ACP / acetone / PCL gel into the glass filter, the mixture immediately solidified, creating a solid ACP / acetone / PCL foam. After allowing the foam to fully solidify at 4 °C, a process which took approximately 60 minutes, the foam and glass filter was placed on a Biichner flask at room temperature. The foam was washed with 1 L of methanol and subsequently with 1 L of isopropanol. The resulting solid foam was dried at 35 °C for 12 hours.
• the specific surface area as calculated with the BET method, was 320 m 2 /g.
• Step 3a The mixture produced in Step 3a) was processed according to Example 2, Step c) to produce a foam.
• This composite was produced exactly as described in Example 2, but with the ethylene glycol being replaced with glycerol.
• the specific surface area of the ACP powder was measured as 318 m 2 /g.
• Example 5 Production of a HA/PCL coating on a glass surface
• a CaP / acetone / PCL mixture was prepared according to Example la-lc, but instead of cooling the CaP / acetone / PCL mixture to 4 °C, the mixture was kept at 42 °C. Glass slides used for microscopy (O. Kindler GmbH, 26 x 76 mm) were dipped into the mixture and removed. The acetone was then allowed to evaporate from the slides, resulting in a thin and homogenous CaP / PCL film on the surface of the slides.
• the adhesion strength of the CaP / PCL film to the glass surface was assessed using the Scotch® tape test using Scotch® tape (810, 3M). The test was conducted by placing Scotch® tape on CaP / PCL coated microscopy slides, followed by applying a load (1 kg) for approximately 30 seconds, after which the tape was removed and the amount of CaP / PCL film present on the tape as well as on the glass slide was qualitatively evaluated by means of visual inspection. The results showed that the CaP / PCL film was not significantly affected by the Scotch® tape test, i.e. the CaP / PCL film was well adhered to the substrate.
• Example 6 In situ formation of a HA / PCL composite in a PEEK spinal cage implant
• a CaP / acetone / PCL mixture was prepared according to Example la-lc, but instead of cooling the CaP / acetone / PCL mixture to 4 °C, the mixture was kept at 42 °C.
• a PEEK cage (illustrated in Figure 5a) was placed in a Teflon mold which had inserts that were shaped to the same form as the inside channels as the PEEK cage, but with a gap of 2 mm between the mold and PEEK cage channels. The Teflon mold and PEEK cage were cooled down to 4 °C.
• the CaP / acetone / PCL mixture was poured into the gap between the cage and mold, and the mixture was allowed to solidify for 60 minutes.
• the cage and mold were placed in water for 60 minutes, and the mold was carefully removed, leaving a thin layer of composite on the inside channels of the PEEK cage (illustrated in Figure 5b).
• the PEEK cage was flushed with isopropanol and left to dry at room temperature.
• Example 7 In situ formation of a CaP / PCL composite in titanium lattice
• a porous titanium substrate, pre-cooled to 4 °C, with a truss length of 2.5 mm was completely immersed in a mixture of CaP / acetone / PCL (prepared as Example la-lc, but instead of cooling the CaP / acetone / PCL mixture to 4 °C, the mixture was kept at 42 °C) followed by placement at 4 °C in order to induce solidification. After approximately 60 minutes, excess CaP / Acetone / PCL foam surrounding the structure was removed. The acetone was replaced by immersing the substrate in a beaker with 100 ml water for 10 minutes, followed by immersion in a beaker with 100 ml of isopropanol for 10 minutes, and subsequent drying at room temperature. The resulting product was a porous structure with CaP / PCL foam penetrating into the titanium structure and filling the pores in the titanium substrate (see Figures 6a and 6b).
• a CaP / acetone / PCL mixture was prepared according to Example la-lc, but instead of cooling the CaP / acetone / PCL mixture to 4 °C, the mixture was kept at 42 °C instead.
• a pedicle screw for spinal fusion surgery was dipped in the mixture and then placed in water for 10 minutes, which created a thin coating of CaP / PCL foam. The screw was then placed in isopropanol for 10 minutes and allowed to dry in room temperature. An image of the screw is shown in Ligure 7.
• a HA/PCL foam was prepared as described in Example 1. Cylindrical plugs, 5 mm in diameter and 6 mm high, were punched out from the foam using an appropriate tool. The plugs were sterilized using E-Beam radiation (5 KGy). Holes of 6 mm diameter were drilled in into rabbit calvaria. Sterilized foam plugs were then implanted in some of the holes whilst some were left unfilled as a control (sham) in order to assess the ability of the HA / PCL foam composite to induce bone formation. The holes, with and without implants, were allowed to heal for 6 weeks. The animals were then euthanized and the areas were imaged with micro-CT. Samples were subsequently processed for histomorphometry.
• Figure 8 shows a micro-CT image of a control sham (image a) and a hole which had a foam plug inserted (image b).
• image a the composite has been completely overgrown with new bone whereas the sham showed little or no new bone growth.
• Figure 9 shows a histology slide of the sample in Figure 8b. This slide confirms that the composite is overgrown with a thin layer of new bone. Formation of new bone was also observed on the underside of the composite. The irregular shape along the edges of the composite shows that the composite has partially biodegraded during the implantation period.
• a foam was produced according to Example 1 c.
• the foam was then washed with isopropanol, the pin array was removed and the foam was allowed to dry at 35 °C for 12 hours.
• the result was a foam composite with regularly distributed cylindrical channels, each having a diameter of 0.9 mm.
• a foam batch was produced according to Example lc.
• a mixture of 0.5 wt. % glycerol in isopropanol was prepared. Approximately 1 g of foam was immersed in 50 mL glycerol / isopropanol mixture for 30 minutes. The foam piece was then removed from the solution and dried at 35 °C for 12 hours. The foam piece was then immersed in azorubine dye, 1 wt. % in Type-1 water, for 30 minutes, after which a photograph of a cross section of the foam was taken (Figure 12b).
• the dye had completely wetted the whole foam piece ( Figure 12b), indicating that the glycerol treatment had increased the hydrophilicity and hence the wettability of the foam by the dye.
• Foam batches were produced according to Example lc, but with varying CaP /PCF weight ratios, in addition to the 33.3:66.7 CaP / PCF weight ratio which is described in Example lc.
• a qualitative description of the properties of the different composites is as follows:
• CaP / 50 PCF was hard and somewhat brittle. Very hydrophilic. The composite was divided into granules with a scalpel and mixed with water to form a moldable, voluminous putty. The porosity was approximately 80 %.

Landscapes

• Health & Medical Sciences (AREA)
• Chemical & Material Sciences (AREA)
• Life Sciences & Earth Sciences (AREA)
• Epidemiology (AREA)
• Veterinary Medicine (AREA)
• Animal Behavior & Ethology (AREA)
• General Health & Medical Sciences (AREA)
• Public Health (AREA)
• Dermatology (AREA)
• Medicinal Chemistry (AREA)
• Oral & Maxillofacial Surgery (AREA)
• Transplantation (AREA)
• Inorganic Chemistry (AREA)
• Heart & Thoracic Surgery (AREA)
• Surgery (AREA)
• Vascular Medicine (AREA)
• Organic Chemistry (AREA)
• Dispersion Chemistry (AREA)
• Engineering & Computer Science (AREA)
• Composite Materials (AREA)
• Materials Engineering (AREA)
• Geology (AREA)
• General Life Sciences & Earth Sciences (AREA)
• Environmental & Geological Engineering (AREA)
• Materials For Medical Uses (AREA)

Priority Applications (8)

Applications Claiming Priority (2)

Publications (1)

Family

ID=77651217

Family Applications (1)

Country Status (10)

Families Citing this family (2)

Citations (9)

• 2021
  • 2021-07-30 GB GBGB2111039.0A patent/GB202111039D0/en not_active Ceased
• 2022
  • 2022-07-29 WO PCT/EP2022/071400 patent/WO2023006969A1/en not_active Ceased
  • 2022-07-29 KR KR1020247005787A patent/KR20240079206A/ko active Pending
  • 2022-07-29 CN CN202280052668.3A patent/CN117769444A/zh active Pending
  • 2022-07-29 EP EP22760682.9A patent/EP4376906B1/en active Active
  • 2022-07-29 US US18/292,355 patent/US20240374791A1/en active Pending
  • 2022-07-29 CA CA3226126A patent/CA3226126A1/en active Pending
  • 2022-07-29 AU AU2022317280A patent/AU2022317280A1/en active Pending
  • 2022-07-29 MX MX2024000964A patent/MX2024000964A/es unknown
  • 2022-07-29 JP JP2024530057A patent/JP2024529562A/ja active Pending

Patent Citations (9)

Non-Patent Citations (12)

Also Published As

Similar Documents

Legal Events