WO2022170109A1 - Agent durcissant - Google Patents

Agent durcissant Download PDF

Info

Publication number
WO2022170109A1
WO2022170109A1 PCT/US2022/015331 US2022015331W WO2022170109A1 WO 2022170109 A1 WO2022170109 A1 WO 2022170109A1 US 2022015331 W US2022015331 W US 2022015331W WO 2022170109 A1 WO2022170109 A1 WO 2022170109A1
Authority
WO
WIPO (PCT)
Prior art keywords
crosslinked
linkages
glass transition
transition temperature
hydroxyester
Prior art date
Application number
PCT/US2022/015331
Other languages
English (en)
Inventor
Aaron Kenneth AMSTUTZ
Luke Michael HAVERHALS
Isaiah Amstutz
Skylar Clement
Shang-Min Li
Original Assignee
Natural Fiber Welding, Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Natural Fiber Welding, Inc. filed Critical Natural Fiber Welding, Inc.
Priority to CN202280026208.3A priority Critical patent/CN117136100A/zh
Priority to CA3209003A priority patent/CA3209003A1/fr
Priority to EP22750474.3A priority patent/EP4288212A1/fr
Publication of WO2022170109A1 publication Critical patent/WO2022170109A1/fr
Priority to DO2023000153A priority patent/DOP2023000153A/es

Abstract

L'invention concerne un agent durcissant pour huiles végétales époxydées et caoutchouc naturel époxydé qui est créé par réaction entre un acide polyfonctionnel d'origine naturelle et une huile végétale époxydée. L'agent durcissant peut être utilisé pour produire au moins un matériau parmi six matériaux différents, chaque type de matériau pouvant être conçu sous la forme d'un élastomère thermodurcissable qui est réticulé avec des liaisons β-hydroxyester. Les matériaux peuvent être conçus sous la forme d'un matériau de type cuir, d'un matériau en mousse, d'un élastomère moulé, d'un revêtement, d'un adhésif et/ou d'un matériau rigide ou semi-rigide. Des articles donnés à titre d'exemple fabriqués à partir de n'importe quelle combinaison des six matériaux peuvent être recyclés à l'aide d'un procédé mécano-chimique pour déréticuler l'élastomère thermodurcissable.
PCT/US2022/015331 2021-02-04 2022-02-04 Agent durcissant WO2022170109A1 (fr)

Priority Applications (4)

Application Number Priority Date Filing Date Title
CN202280026208.3A CN117136100A (zh) 2021-02-04 2022-02-04 固化剂
CA3209003A CA3209003A1 (fr) 2021-02-04 2022-02-04 Agent durcissant
EP22750474.3A EP4288212A1 (fr) 2021-02-04 2022-02-04 Agent durcissant
DO2023000153A DOP2023000153A (es) 2021-02-04 2023-08-02 Curativo

Applications Claiming Priority (6)

Application Number Priority Date Filing Date Title
US202163145939P 2021-02-04 2021-02-04
US63/145,939 2021-02-04
US202163274443P 2021-11-01 2021-11-01
US63/274,443 2021-11-01
US202263297569P 2022-01-07 2022-01-07
US63/297,569 2022-01-07

Publications (1)

Publication Number Publication Date
WO2022170109A1 true WO2022170109A1 (fr) 2022-08-11

Family

ID=82741807

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2022/015331 WO2022170109A1 (fr) 2021-02-04 2022-02-04 Agent durcissant

Country Status (5)

Country Link
EP (1) EP4288212A1 (fr)
CA (1) CA3209003A1 (fr)
DO (1) DOP2023000153A (fr)
TW (1) TW202302345A (fr)
WO (1) WO2022170109A1 (fr)

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5108798A (en) * 1989-06-08 1992-04-28 American Cyanamid Company Water soluble binder compositions containing beta-hydroxy urethanes and polyfunctional carboxylic acids
US20150038605A1 (en) * 2013-08-02 2015-02-05 Nike, Inc. Low density foam, midsole, footwear, and methods for making low density foam
US20160060386A1 (en) * 2013-04-26 2016-03-03 Xyleco, Inc. Processing hydroxy-carboxylic acids to polymers
US20190365028A1 (en) * 2018-06-04 2019-12-05 Nike, Inc. Two part sole structures and uses thereof
US20200332057A1 (en) * 2018-04-21 2020-10-22 Natural Fiber Welding, Inc. Curative & Method

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5108798A (en) * 1989-06-08 1992-04-28 American Cyanamid Company Water soluble binder compositions containing beta-hydroxy urethanes and polyfunctional carboxylic acids
US20160060386A1 (en) * 2013-04-26 2016-03-03 Xyleco, Inc. Processing hydroxy-carboxylic acids to polymers
US20150038605A1 (en) * 2013-08-02 2015-02-05 Nike, Inc. Low density foam, midsole, footwear, and methods for making low density foam
US20200332057A1 (en) * 2018-04-21 2020-10-22 Natural Fiber Welding, Inc. Curative & Method
US20190365028A1 (en) * 2018-06-04 2019-12-05 Nike, Inc. Two part sole structures and uses thereof

Also Published As

Publication number Publication date
EP4288212A1 (fr) 2023-12-13
TW202302345A (zh) 2023-01-16
CA3209003A1 (fr) 2022-08-11
DOP2023000153A (es) 2023-12-29

Similar Documents

Publication Publication Date Title
US11542365B2 (en) Curative
US11760835B2 (en) Curative and method
AU2019256523B2 (en) Curative
WO2022170109A1 (fr) Agent durcissant
US20230034643A1 (en) Curative
AU2020299589B2 (en) Curative and method
WO2023004190A1 (fr) Agent de vulcanisation
US11760836B2 (en) Curative
NZ784581B2 (en) Curative & method
CN117136100A (zh) 固化剂

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 22750474

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 3209003

Country of ref document: CA

WWE Wipo information: entry into national phase

Ref document number: MX/A/2023/009057

Country of ref document: MX

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 2022750474

Country of ref document: EP

Effective date: 20230904