WO2022154698A1 - Cold-curable intumescent silicone fire-retardant composition - Google Patents
Cold-curable intumescent silicone fire-retardant composition Download PDFInfo
- Publication number
- WO2022154698A1 WO2022154698A1 PCT/RU2022/050010 RU2022050010W WO2022154698A1 WO 2022154698 A1 WO2022154698 A1 WO 2022154698A1 RU 2022050010 W RU2022050010 W RU 2022050010W WO 2022154698 A1 WO2022154698 A1 WO 2022154698A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- aminopropyltrimethoxysilane
- gamma
- additive
- total number
- taken
- Prior art date
Abstract
The proposed technical solution relates to fire-retardant coatings of the intumescent type and is intended, for example, for fire-proofing cabling, inter alia in nuclear and thermal power stations, increasing the fire resistance rating of load-bearing metal structures, increasing the fire resistance rating of ventilation ducts, cables and power lines, inter alia in nuclear and thermal power stations, and treating fire-resistant structures on industrial sites and construction sites, inter alia in nuclear and thermal power stations. The claimed invention solves the technical problem of creating a cold-curable fire-retardant intumescent composition for metal structures, which exhibits improved adhesion to metals and various primers and which, when heated, forms foamed coke that exhibits greater mechanical strength in the event of fire by comparison with known compositions.
Description
ВСПУЧИВАЮЩАЯСЯ СИЛИКОНОВАЯ ОГНЕЗАЩИТНАЯ КОМПОЗИЦИЯ ХОЛОДНОГО ОТВЕРЖДЕНИЯ COLD CURING INVOLVING SILICONE FIREPROOF COMPOSITION
[0001 ] ОБЛАСТЬ ТЕХНИКИ [0001] TECHNICAL FIELD
[0002] Предложенное техническое решение относится к огнезащитным покрытиям вспучивающегося типа и предназначено, например, для противопожарной защиты кабельного хозяйства, в том числе на АЭС и ТЭС, повышения предела огнестойкости несущих металлоконструкций, повышения предела огнестойкости вентиляционных коробов, кабелей и кабельных линий, в том числе на АЭС и ТЭС, отделки огнестойких конструкций промышленных и строительных объектов, в том числе на АЭС и ТЭС. [0002] The proposed technical solution relates to intumescent type fire retardant coatings and is intended, for example, for fire protection of cable facilities, including at nuclear power plants and thermal power plants, increasing the fire resistance of load-bearing metal structures, increasing the fire resistance of ventilation ducts, cables and cable lines, including including at nuclear power plants and thermal power plants, finishing of fire-resistant structures of industrial and building facilities, including nuclear power plants and thermal power plants.
[0003] УРОВЕНЬ ТЕХНИКИ [0003] BACKGROUND OF THE INVENTION
[0004] Известна огнезащитная композиция холодного отверждения для покрытия и способ ее получения (патент RU 2492201 С1 , опубликованный 10.09.2013 на 9 л.). Известная огнезащитная композиция холодного отверждения для покрытий содержит низкомолекулярный силоксановый каучук, низкомолекулярные силаны, дибутилоловодиацетат, полифосфат аммония и пентэритрит технический аппретированные при определенных соотношениях. Приготовление упомянутой композиции осуществляют путём объёмного смешения ингредиентов, при этом процесс смешивания дополняется принудительным втиранием сыпучих ингредиентов в жидкий силоксановый каучук в замкнутой ёмкости с рабочим объёмом от 0,1 до 0,5 м3. Втирание происходит между подвижных лопастей и неподвижных ножей, при этом подвижные лопасти принудительно нагнетают композицию в зону перетира, тем самым вызывая нагрев рабочей смеси композиции. [0004] A cold curing fire retardant composition for a coating and a method for producing it are known (patent RU 2492201 C1, published on September 10, 2013, 9 sheets). Known flame retardant cold curing composition for coatings contains low molecular weight siloxane rubber, low molecular weight silanes, dibutyl tin diacetate, ammonium polyphosphate and technical penteritrite finished at certain ratios. The preparation of the said composition is carried out by volumetric mixing of ingredients, while the mixing process is supplemented by forced rubbing of bulk ingredients into liquid silicone rubber in a closed container with a working volume of 0.1 to 0.5 m 3 . Rubbing occurs between the movable blades and fixed knives, while the movable blades force the composition into the grinding zone, thereby causing heating of the working mixture of the composition.
[0005] Известная композиция не обладает достаточной механической прочностью образуемого пенококса при возникновении пожара, а также обладает плохой адгезией к металлам и грунтовочным покрытиям. [0005] The known composition does not have sufficient mechanical strength of the foam coke formed in the event of a fire, and also has poor adhesion to metals and primers.
[0006] РАСКРЫТИЕ ИЗОБРЕТЕНИЯ [0006] SUMMARY
[0007] Технической проблемой, решаемой заявленным изобретением, является создание огнезащитной вспучивающейся композиции холодного отверждения для металлоконструкций, обладающей повышенной адгезией к металлам и различным грунтовочным покрытиям, пенококс, образуемый в процессе нагрева которой, обладает повышенной механической прочностью при возникновении пожара в сравнении с известными композициями.
[0008] Техническим результатом, достигаемым при реализации заявленного изобретения, является повышение механической прочности пенококса, образуемого в процессе нагрева огнезащитной композиции холодного отверждения, а также повышение адгезии композиции к металлу и различным грунтовочным покрытиям. [0007] The technical problem solved by the claimed invention is the creation of a fire-retardant intumescent composition of cold curing for metal structures, which has increased adhesion to metals and various primer coatings, foam coke formed during the heating process of which has increased mechanical strength in the event of a fire in comparison with known compositions . [0008] The technical result achieved in the implementation of the claimed invention is to increase the mechanical strength of foam coke formed during the heating of the cold curing fire-retardant composition, as well as to increase the adhesion of the composition to metal and various primers.
[0009] Технический результат достигается за счёт того, что обеспечивается набор для приготовления огнезащитной вспучивающейся композиции холодного отверждения для металлоконструкций и/или грунтовочных покрытий, включающий одну или несколько тарных единиц равного или неравного объёма с основой и одну или несколько тарных единиц равного или неравного объёма с катализатором или катализирующей смесью, причём в сумме тарные единицы содержат следующие исходные компоненты при следующем соотношении исходных компонентов, мае. %: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа, представляющая собой каучук синтетический термостойкий низкомолекулярный марки СКТН-А, или СКТН-Б, или СКТН-В, или СКТН-Г вязкостью от 100 до 20 000 сП или каучук синтетический термостойкий низкомолекулярный марки СКТН-А, или СКТН-Б, или СКТН-В, или СКТН-Г, разбавленной до вязкости от 100 до 20 000 сП низковязким неорганическим полимером с гидроксильной группой, в том числе, силанольной жидкостью, вязкостью от 50 до 120 сП 23,59-40,44; пентаэритрит технический 17, 18-22,00; полифосфат аммония 35, 10-46, 10; структурирующий агент, плавящийся под воздействием тепла, представляющий собой одно из или комбинацию из: кварц, микросфера стеклянная, микросфера алюмосиликатная 3,10-6,17; и или катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объема, представляющая собой смесь гамма- аминопропилтриэтоксилана, трис-бутаноноксим-метилсилана и добавки в виде модификатора вязкости, являющегося пенорегулятором «ПЕНТА®-483», взятых при следующем соотношении компонентов от общего количества компонентов композиции, мае. %: гамма-аминопропилтриэтоксилан 0,49-0,84; трис-бутаноноксим-метилсилан 1 ,89-3,24; пенорегулятор «ПЕНТА®-483» 0,05-0,15;
или катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объема, представляющая собой смесь гамма- аминопропилтриэтоксилана и трис-бутаноноксим-метилсилана, взятых при следующем соотношении компонентов от общего количества компонентов композиции, мае. %: гамма-аминопропилтриэтоксилан 0,49-0,84; трис-бутаноноксим-метилсилан 1 ,89-3,24; и добавка для катализирующей смеси в виде модификатора вязкости, являющегося пенорегулятором «ПЕНТА®-483», фасованная в отдельную тарную единицу в количестве 0,05-0,15 мае. % от общего количества компонентов композиции. [0009] The technical result is achieved due to the fact that a set is provided for the preparation of a fire-retardant intumescent composition of cold curing for metal structures and / or primer coatings, including one or more tare units of equal or unequal volume with the base and one or more tare units of equal or unequal volume with a catalyst or a catalytic mixture, and in total the packaging units contain the following initial components with the following ratio of initial components, May. %: base packaged in one or more tare units of equal or unequal volume: silicone rubber base, which is synthetic heat-resistant low molecular weight rubber grade SKTN-A, or SKTN-B, or SKTN-V, or SKTN-G with a viscosity of 100 to 20 000 cP or synthetic heat-resistant low molecular weight rubber grade SKTN-A, or SKTN-B, or SKTN-V, or SKTN-G, diluted to a viscosity of 100 to 20,000 cP with a low-viscosity inorganic polymer with a hydroxyl group, including silanol liquid, viscosity from 50 to 120 cP 23.59-40.44; technical pentaerythritol 17, 18-22.00; ammonium polyphosphate 35, 10-46, 10; structuring agent, melting under the influence of heat, which is one of or a combination of: quartz, glass microsphere, aluminosilicate microsphere 3.10-6.17; and or a catalyst mixture packaged in one or more container units of equal or unequal volume, which is a mixture of gamma-aminopropyltriethoxylan, tris-butanonoxime-methylsilane and an additive in the form of a viscosity modifier, which is a foam regulator "PENTA®-483", taken in the following ratio of components from the total number of components of the composition, May. %: gamma-aminopropyltriethoxylan 0.49-0.84; tris-butanonoxime-methylsilane 1.89-3.24; foam regulator "PENTA®-483"0.05-0.15; or a catalytic mixture packaged in one or more container units of equal or unequal volume, which is a mixture of gamma-aminopropyltriethoxylan and tris-butanonoxime-methylsilane, taken in the following ratio of components from the total number of components of the composition, May. %: gamma-aminopropyltriethoxylan 0.49-0.84; tris-butanonoxime-methylsilane 1.89-3.24; and an additive for the catalytic mixture in the form of a viscosity modifier, which is a foam regulator "PENTA®-483", packaged in a separate container unit in the amount of 0.05-0.15 May. % of the total number of components of the composition.
[0010] ОСУЩЕСТВЛЕНИЕ ИЗОБРЕТЕНИЯ [0010] CARRYING OUT THE INVENTION
[0011] Далее приводятся варианты осуществления настоящего изобретения, раскрывающие примеры его реализации в частных исполнениях. Тем не менее, само описание не предназначено для ограничения объёма прав, предоставляемых данным патентом. Скорее, следует исходить из того, что заявленное изобретение также может быть осуществлено другими способами таким образом, что будет включать в себя отличающиеся элементы и условия или комбинации элементов и условий, аналогичных элементам и условиям, описанным в данном документе, в сочетании с другими существующими и будущими технологиями. [0011] The following are embodiments of the present invention, revealing examples of its implementation in private executions. However, the description itself is not intended to limit the scope of the rights granted by this patent. Rather, it should be understood that the claimed invention may also be practiced in other ways in a manner that would include differing elements and conditions, or combinations of elements and conditions similar to those described herein, in combination with other existing and future technologies.
[0012] В другом из вариантов осуществления настоящего изобретения обеспечивается набор для приготовления огнезащитной вспучивающейся композиции холодного отверждения для металлоконструкций и/или грунтовочных покрытий, включающий одну или несколько тарных единиц равного или неравного объёма с основой и одну или несколько тарных единиц равного или неравного объёма с катализатором или катализирующей смесью, причём в сумме тарные единицы содержат следующие исходные компоненты при следующем соотношении исходных компонентов, мае. %: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа, представляющая собой каучук синтетический термостойкий низкомолекулярный марки СКТН-А, или СКТН-Б, или СКТН-В, или СКТН-Г вязкостью от 100 до 20 000 сП или каучук синтетический термостойкий низкомолекулярный марки СКТН-А, или СКТН-Б, или СКТН-В, или СКТН-Г, разбавленной до вязкости от 100 до 20 000 сП низковязким неорганическим
полимером с гидроксильной группой, в том числе, силанольной жидкостью, вязкостью от 50 до 120 сП 23,59-40,44; пентаэритрит технический 17, 18-22,00; полифосфат аммония 35, 10-46, 10; структурирующий агент, плавящийся под воздействием тепла, представляющий собой одно из или комбинацию из: кварц, микросфера стеклянная, микросфера алюмосиликатная 3,10-6,17; и или катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объема, представляющая собой смесь гамма- аминопропилтриэтоксилана, трис-бутаноноксим-метилсилана и добавки в виде модификатора вязкости, являющегося пенорегулятором «ПЕНТА®-483», взятых при следующем соотношении компонентов от общего количества компонентов композиции, мае. %: гамма-аминопропилтриэтоксилан 0,49-0,84; трис-бутаноноксим-метилсилан 1 ,89-3,24; пенорегулятор «ПЕНТА®-483» 0,05-0,15; или катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объема, представляющая собой смесь гамма- аминопропилтриэтоксилана и трис-бутаноноксим-метилсилана, взятых при следующем соотношении компонентов от общего количества компонентов композиции, мае. %: гамма-аминопропилтриэтоксилан 0,49-0,84; трис-бутаноноксим-метилсилан 1 ,89-3,24; и добавка для катализирующей смеси в виде модификатора вязкости, являющегося пенорегулятором «ПЕНТА®-483», фасованная в отдельную тарную единицу в количестве 0,05-0,15 мае. % от общего количества компонентов композиции; и дополнительно может содержать добавку в виде 10% раствора М(бета- аминоэтил)гамма-аминопропилтриметоксисилана и гамма- аминопропилтриметоксисилана или М-(2-аминоэтил)-3- аминопропилтриметоксисилана в гексане или толуоле, взятого в количестве 0,05- 0,15 мае. % от общего количества упомянутых исходных компонентов. [0012] In another embodiment, the present invention provides a kit for the preparation of a cold curing fire retardant intumescent composition for metal structures and/or primers, comprising one or more equal or unequal volume container units with a base and one or more equal or unequal volume container units with a catalyst or a catalytic mixture, and in total the packaging units contain the following initial components with the following ratio of initial components, May. %: base packaged in one or more tare units of equal or unequal volume: silicone rubber base, which is synthetic heat-resistant low molecular weight rubber grade SKTN-A, or SKTN-B, or SKTN-V, or SKTN-G with a viscosity of 100 to 20 000 cP or synthetic heat-resistant low molecular weight rubber grade SKTN-A, or SKTN-B, or SKTN-V, or SKTN-G, diluted to a viscosity of 100 to 20,000 cP with a low-viscosity inorganic a polymer with a hydroxyl group, including a silanol liquid, with a viscosity of 50 to 120 centipoise 23.59-40.44; technical pentaerythritol 17, 18-22.00; ammonium polyphosphate 35, 10-46, 10; structuring agent, melting under the influence of heat, which is one of or a combination of: quartz, glass microsphere, aluminosilicate microsphere 3.10-6.17; and or a catalyst mixture packaged in one or more container units of equal or unequal volume, which is a mixture of gamma-aminopropyltriethoxylan, tris-butanonoxime-methylsilane and an additive in the form of a viscosity modifier, which is a foam regulator "PENTA®-483", taken in the following ratio of components from the total number of components of the composition, May. %: gamma-aminopropyltriethoxylan 0.49-0.84; tris-butanonoxime-methylsilane 1.89-3.24; foam regulator "PENTA®-483"0.05-0.15; or a catalytic mixture packaged in one or more container units of equal or unequal volume, which is a mixture of gamma-aminopropyltriethoxylan and tris-butanonoxime-methylsilane, taken in the following ratio of components from the total number of components of the composition, May. %: gamma-aminopropyltriethoxylan 0.49-0.84; tris-butanonoxime-methylsilane 1.89-3.24; and an additive for the catalytic mixture in the form of a viscosity modifier, which is a foam regulator "PENTA®-483", packaged in a separate container unit in the amount of 0.05-0.15 May. % of the total number of components of the composition; and additionally may contain an additive in the form of a 10% solution of M(beta-aminoethyl)gamma-aminopropyltrimethoxysilane and gamma-aminopropyltrimethoxysilane or M-(2-aminoethyl)-3-aminopropyltrimethoxysilane in hexane or toluene, taken in an amount of 0.05-0.15 May. % of the total number of mentioned starting components.
[0013] Предпочтительно, не ограничиваясь, такая огнезащитная вспучивающаяся композиция холодного отверждения для металлоконструкций и/или грунтовочных покрытий пригодна для создания огнезащитных покрытий в несколько
слоёв, способных скрыть дефекты конструкций, а также пригодна для нанесения на металлические конструкции и грунтовочные покрытия, например, не ограничиваясь, на алкидной основе, или эпоксидной основе, или полиуретановой основе, или на основе органосиликатных композиций, так как обладает хорошей адгезией к металлу и различным грунтовочным покрытиям. Предпочтительно, не ограничиваясь, 10% раствор М(бета-аминоэтил)гамма-аминопропилтриметоксисилана и гамма- аминопропилтриметоксисилана или М-(2-аминоэтил)-3- аминопропилтриметоксисилана в гексане или толуоле используется в такой огнезащитной композиции для металлоконструкций и/или грунтовочных покрытий в качестве внутреннего промоутера адгезии. [0013] Preferably, but not limited to, such a cold set fire retardant intumescent composition for structural steel and/or primers is suitable for providing fire retardant coatings of several layers that can hide structural defects, and is also suitable for application to metal structures and primer coatings, for example, but not limited to, alkyd-based, or epoxy-based, or polyurethane-based, or based on organosilicate compositions, as it has good adhesion to metal and various primers. Preferably, but not limited to, a 10% solution of M(beta-aminoethyl)gamma-aminopropyltrimethoxysilane and gamma-aminopropyltrimethoxysilane or M-(2-aminoethyl)-3-aminopropyltrimethoxysilane in hexane or toluene is used in such a fire retardant composition for metal structures and/or primers in as an internal adhesion promoter.
[0014] Предпочтительно, не ограничиваясь, заявленные огнезащитные вспучивающиеся композиции могут дополнительно содержать ускоритель полимеризации в виде дибутилдиацетата олова (DBTA) или дибутилдилаурата олова (DBTL), взятый в количестве 0,05-0,15 мае. % от общего количества исходных компонентов, используемый в виде добавки к катализирующей смеси. Предпочтительно, не ограничиваясь, для заявленных огнезащитных композиций силиконовая каучуковая основа представляет собой, не ограничиваясь, каучук синтетический термостойкий низкомолекулярный марок СКТН-А, СКТН-Б, СКТН-В, СКТН-Г вязкостью от 100 до 20 000 сП, либо аналогичную силиконовую каучуковую основу, изготавливаемую в соответствии с какими-либо собственными техническими условиями, но соответствующую упомянутым требованиям по вязкости. Альтернативно, не ограничиваясь, силиконовая каучуковая основа представляет собой какой-либо упомянутый каучук, подвергнутый разбавлению до требуемой вязкости силанольной жидкостью (низковязким неорганическим полимером с гидроксильной группой), например, не ограничиваясь, вязкостью от 50 до 120 сП. Предпочтительно, не ограничиваясь, вязкость силиконовой каучуковой основы, используемой в заявленных огнезащитных композициях, составляет 500 сП, однако специалисту в данной области техники, обладающему обычными знаниями, на которого рассчитано настоящее изобретение, должно быть очевидно, что в зависимости от предъявляемых к вспучивающимся огнезащитным композициям требований может быть обеспечен каучук другой требуемой вязкости. В качестве примера, но не ограничения, упомянутый каучук, если разбавлен до требуемой вязкости силанольной жидкостью, то разбавляется в соотношении в зависимости от требуемой вязкости по основе, и таким образом, например, не ограничиваясь, силиконовая каучуковая основа может содержать, например, каучук синтетический
термостойкий низкомолекулярный марки СКТН-А, взятый в количестве 11 ,80 мае. % от общего количества компонентов и силанольную жидкость, взятую примерно в том же количестве; таким образом, специалисту в данной области техники, обладающему обычными знаниями, на которого рассчитано настоящее изобретение, должно быть очевидно, что если используется упомянутый каучук большей вязкости, то либо используется большее количество силанольной жидкости, либо используется меньшее количество более вязкого каучука - в зависимости от требований, предъявляемым к силиконовой каучуковой основе. Предпочтительно, не ограничиваясь, пентаэритрит технический используется в заявленных композициях в качестве антипирена и вспучивающегося агента. Предпочтительно, не ограничиваясь, полифосфат аммония в заявленных композициях используется в качестве антипирена и пенообразующего агента. Предпочтительно, не ограничиваясь, катализирующая смесь для огнезащитной вспучивающейся композиции холодного отверждения для металлоконструкций и/или грунтовочных покрытий содержит в своём составе смешанные гамма-аминопропилтриэтоксилан в качестве сшивающего агента, взятый в количестве от 0,49 до 0,84 мае. % от общего количества компонентов огнезащитной вспучивающейся композиции, и трис- бутаноноксим-метилсилан в качестве нейтрального сшивателя полимеров, взятый в количестве от 1 ,89 до 3,24 мае. % от общего количества компонентов огнезащитной вспучивающейся композиции; при этом для упомянутой огнезащитной композиции для металлоконструкций и/или грунтовочных покрытий катализирующая смесь может дополнительно содержать 0,05-0,15 мае. % от общего количества компонентов огнезащитной вспучивающейся композиции 10% раствора М(бета- аминоэтил)гамма-аминопропилтриметоксисилана и гамма- аминопропилтриметоксисилана или М-(2-аминоэтил)-3- аминопропилтриметоксисилана в гексане или толуоле, который используется в такой огнезащитной композиции для металлоконструкций и/или грунтовочных покрытий в качестве внутреннего промоутера адгезии, и при этом для упомянутой огнезащитной композиции для металлоконструкций и/или грунтовочных покрытий катализирующая смесь может дополнительно содержать 0,05-0,15 мае. % от общего количества компонентов огнезащитной вспучивающейся композиции модификатора вязкости, в качестве которого может быть использован пенорегулятор «ПЕНТА®-483» (оксиалкиленметилсилоксановый блоксополимер) или тому подобное; при этом такая катализирующая смесь для огнезащитной композиции для металлоконструкций и/или грунтовочных покрытий может быть приготовлена на
основе вышеупомянутой катализирующей смеси с добавлением 10% раствора М(бета-аминоэтил)гамма-аминопропилтриметоксисилана и гамма- аминопропилтриметоксисилана или М-(2-аминоэтил)-3- аминопропилтриметоксисилана в гексане или толуоле и упомянутого модификатора вязкости в указанных соотношениях, при этом упомянутый модификатор вязкости может быть выполнен в отдельной тарной единице, а его добавление в вышеупомянутую катализирующую смесь может быть осуществлено перед приготовлением заявленной композиции. Предпочтительно, не ограничиваясь, в качестве плавящегося под воздействием тепла структурирующего агента в заявленных огнезащитных композициях используется одно из или комбинация из: кварц, микросфера стеклянная, микросфера алюмосиликатная. Использование в составе заявленных огнезащитных композиций структурирующего агента, плавящегося под воздействием тепла, позволяет обеспечить следующий эффект. Под термином «тепло» понимаются температуры, способные вызвать плавление структурирующего агента. Как правило, такими температурами являются температуры пожара, а именно - температуры от 600 градусов Цельсия. Под воздействием тепла полифосфат аммония превращается в пенококс, наряду с этим пентаэритрит технический разлагается с выделением газа, увеличивающего образуемый пенококс в объёме. Однако, образуемый таким образом пенококс не обладает механической прочностью. При этом автором было неожиданно обнаружено, что даже в отсутствие предварительного аппретирования структурирующего агента, в составе заявленных композиций температура его плавления будет существенно снижена. Таким образом, при нагревании до температур, близких к температурам пожара, предварительно неаппретированный структурирующий агент плавится, образуя при спекании пластичную структуру в составе образуемого пенококса, увеличивая его механическую прочность. При этом отказ от предварительного аппретирования структурирующего агента также позволяет упростить технологию приготовления частей заявленных огнезащитных композиций и ускорить процесс приготовления. [0014] Preferably, without limitation, the claimed flame retardant intumescent compositions may additionally contain a polymerization accelerator in the form of tin dibutyl diacetate (DBTA) or tin dibutyl dilaurate (DBTL), taken in an amount of 0.05-0.15 wt. % of the total amount of starting components, used as an additive to the catalytic mixture. Preferably, without limitation, for the claimed flame retardant compositions, the silicone rubber base is, without limitation, synthetic heat-resistant low molecular weight rubber grades SKTN-A, SKTN-B, SKTN-V, SKTN-G with a viscosity of 100 to 20,000 cP, or a similar silicone rubber a base made according to some of its own specifications, but meeting the viscosity requirements mentioned. Alternatively, but not limited to, the silicone rubber base is any of the mentioned rubber, diluted to the desired viscosity with a silanol fluid (a low viscosity inorganic polymer with a hydroxyl group), for example, but not limited to, a viscosity of 50 to 120 cps. Preferably, but not limited to, the viscosity of the silicone rubber base used in the claimed flame retardant compositions is 500 cP, however, it should be obvious to a person skilled in the art with ordinary knowledge to whom the present invention is intended, that depending on the requirements for intumescent flame retardant compositions requirements, rubber of other required viscosity can be provided. By way of example, and not limitation, said rubber, if diluted to the desired viscosity with silanol fluid, is diluted in a ratio depending on the desired base viscosity, and thus, for example, without being limited, the silicone rubber base may contain, for example, synthetic rubber heat-resistant low-molecular brand SKTN-A, taken in the amount of 11.80 May. % of the total number of components and silanol liquid, taken in approximately the same amount; thus, it should be apparent to those of ordinary skill in the art to whom the present invention is intended that if said higher viscosity rubber is used, then either more silanol fluid is used or less of the more viscous rubber is used, depending on requirements for silicone rubber base. Preferably, without limitation, technical pentaerythritol is used in the claimed compositions as a flame retardant and intumescent agent. Preferably, but not limited to, ammonium polyphosphate in the claimed compositions is used as a fire retardant and foaming agent. Preferably, but not limited to, the catalyst mixture for a cold curing fire retardant intumescent composition for metal structures and/or primers contains mixed gamma-aminopropyltriethoxylan as a crosslinking agent, taken in an amount of from 0.49 to 0.84 wt. % of the total number of components of the fire-retardant intumescent composition, and tris-butanone oxime-methylsilane as a neutral polymer crosslinker, taken in an amount from 1.89 to 3.24 May. % of the total number of components of the fire-retardant intumescent composition; while for the mentioned fire-retardant composition for metal structures and/or primer coatings, the catalytic mixture may additionally contain 0.05-0.15 wt. % of the total components of the flame retardant intumescent composition of a 10% solution of M(beta-aminoethyl)gamma-aminopropyltrimethoxysilane and gamma-aminopropyltrimethoxysilane or M-(2-aminoethyl)-3-aminopropyltrimethoxysilane in hexane or toluene, which is used in such a fire retardant composition for metal structures and /or primer coatings as an internal adhesion promoter, and at the same time for the mentioned fire-retardant composition for metal structures and/or primer coatings, the catalytic mixture may additionally contain 0.05-0.15 wt. % of the total number of components of the flame retardant intumescent composition of the viscosity modifier, which can be used as a foam regulator "PENTA®-483" (oxyalkylenemethylsiloxane block copolymer) or the like; however, such a catalyst mixture for a fire retardant composition for metal structures and/or primers can be prepared on based on the above catalyst mixture with the addition of a 10% solution of M(beta-aminoethyl)gamma-aminopropyltrimethoxysilane and gamma-aminopropyltrimethoxysilane or M-(2-aminoethyl)-3-aminopropyltrimethoxysilane in hexane or toluene and the mentioned viscosity modifier in the indicated ratios, while the mentioned modifier viscosity can be made in a separate container unit, and its addition to the above catalyst mixture can be carried out before preparing the claimed composition. Preferably, without limitation, one of or a combination of: quartz, glass microsphere, aluminosilicate microsphere is used as a heat-melting structuring agent in the claimed flame retardant compositions. The use of a structuring agent that melts under the influence of heat in the composition of the claimed flame retardant compositions makes it possible to provide the following effect. The term "heat" refers to temperatures capable of causing melting of the structurant. As a rule, such temperatures are fire temperatures, namely, temperatures from 600 degrees Celsius. Under the influence of heat, ammonium polyphosphate turns into foam coke, along with this, technical pentaerythritol decomposes with the release of gas, which increases the volume of foam coke formed. However, foam coke formed in this way does not have mechanical strength. At the same time, the author unexpectedly found that even in the absence of preliminary sizing of the structuring agent, in the composition of the claimed compositions, its melting point will be significantly reduced. Thus, when heated to temperatures close to those of a fire, the previously untreated structuring agent melts, forming a plastic structure during sintering in the composition of the formed foam coke, increasing its mechanical strength. At the same time, the rejection of preliminary dressing of the structuring agent also makes it possible to simplify the technology for preparing parts of the claimed flame retardant compositions and speed up the preparation process.
[0015] Далее представлены конкретные примеры наборов для приготовления огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий и способ приготовления ее основы и, если применимо, катализирующей смеси. В каждом наборе основа и катализатор (катализирующая смесь) хранятся и поставляются в разных ёмкостях. При этом и основа для каждого набора фасована в тарные единицы равного или неравного объёма. При этом
катализирующая смесь для каждого набора фасована в тарные единицы равного или неравного объёма. При этом никакие соотношения компонентов между собой не являются обязательными, а обусловлены лишь количеством компонентов, исходя из общего количества исходных компонентов; например, не ограничиваясь, не обязательно добавки в катализирующую смесь должны быть использованы в соотношении один к одному, так как наличие и количество добавок определяется требованиями, предъявляемыми к самой композиции, а также могут быть обусловлены окружающей средой, в которой композиция будет использоваться; главным образом при этом следует исходить из того, что использование добавок изменяет исходное количество катализирующей смеси как компонента, либо изменяет исходное количество компонентов катализирующей смеси. В сумме тарные единицы, в которых содержатся основа и катализирующая смесь, содержат следующие исходные компоненты при следующем соотношении исходных компонентов, мае. %.: [0015] The following are specific examples of kits for preparing a fire retardant intumescent composition for metal structures and/or primers and a method for preparing its base and, if applicable, the catalyst mixture. In each set, the base and the catalyst (catalyst mixture) are stored and supplied in different containers. At the same time, the basis for each set is packaged in tare units of equal or unequal volume. Wherein the catalytic mixture for each set is packaged in tare units of equal or unequal volume. At the same time, no ratios of components among themselves are mandatory, but are determined only by the number of components, based on the total number of initial components; for example, without limitation, not necessarily additives in the catalytic mixture should be used in a ratio of one to one, since the presence and amount of additives is determined by the requirements for the composition itself, and may also be due to the environment in which the composition will be used; in this case, one should mainly proceed from the fact that the use of additives changes the initial amount of the catalytic mixture as a component, or changes the initial amount of the components of the catalytic mixture. In total, the container units, which contain the base and the catalytic mixture, contain the following initial components with the following ratio of the initial components, May. %.:
[0016] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 1 : основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 23,59; пентаэритрит технический 22,0; полифосфат аммония 46,0; структурирующий агент, плавящийся под воздействием тепла 6,07; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 2,14; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде 10% раствора М(бета- аминоэтил)гамма-аминопропилтриметоксисилана и гамма- аминопропилтриметоксисилана или М-(2-аминоэтил)-3- аминопропилтриметоксисилана в гексане или толуоле, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов. [0016] Fire Retardant Intumescent Composition for Metalwork and/or Primer Coatings No. 1: base packaged in one or more equal or unequal container units: silicone rubber base 23.59; technical pentaerythritol 22.0; ammonium polyphosphate 46.0; heat melting structurant 6.07; catalyst mixture packaged in one or more container units of equal or unequal volume 2.14; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.1 May. % of the total number of mentioned starting components; and contains an additive in the form of a 10% solution of M(beta-aminoethyl)gamma-aminopropyltrimethoxysilane and gamma-aminopropyltrimethoxysilane or M-(2-aminoethyl)-3-aminopropyltrimethoxysilane in hexane or toluene, taken in an amount of 0.1 wt. % of the total number of mentioned starting components.
[0017] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 2: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма:
силиконовая каучуковая основа 30,33; пентаэритрит технический 19,00; полифосфат аммония 42,00; структурирующий агент, плавящийся под воздействием тепла 5,74; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 2,73; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде 10% раствора М(бета- аминоэтил)гамма-аминопропилтриметоксисилана и гамма- аминопропилтриметоксисилана или М-(2-аминоэтил)-3- аминопропилтриметоксисилана в гексане или толуоле, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов. [0017] Fire Retardant Intumescent Composition for Metalwork and/or Primer Coatings No. 2: base packaged in one or more equal or unequal container units: silicone rubber base 30.33; technical pentaerythritol 19.00; ammonium polyphosphate 42.00; heat melting structurant 5.74; catalytic mixture, packaged in one or more container units of equal or unequal volume 2.73; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.1 May. % of the total number of mentioned starting components; and contains an additive in the form of a 10% solution of M(beta-aminoethyl)gamma-aminopropyltrimethoxysilane and gamma-aminopropyltrimethoxysilane or M-(2-aminoethyl)-3-aminopropyltrimethoxysilane in hexane or toluene, taken in an amount of 0.1 wt. % of the total number of mentioned starting components.
[0018] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 3: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 40,44; пентаэритрит технический 17,76; полифосфат аммония 35,00; структурирующий агент, плавящийся под воздействием тепла 3,0; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 3,60; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде 10% раствора М(бета- аминоэтил)гамма-аминопропилтриметоксисилана и гамма- аминопропилтриметоксисилана или М-(2-аминоэтил)-3- аминопропилтриметоксисилана в гексане или толуоле, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов. [0018] Fire Retardant Intumescent Composition for Metalwork and/or Undercoats No. 3: base packaged in one or more equal or unequal container units: silicone rubber base 40.44; technical pentaerythritol 17.76; ammonium polyphosphate 35.00; heat melting structuring agent 3.0; catalytic mixture, packaged in one or more container units of equal or unequal volume 3.60; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.1 May. % of the total number of mentioned starting components; and contains an additive in the form of a 10% solution of M(beta-aminoethyl)gamma-aminopropyltrimethoxysilane and gamma-aminopropyltrimethoxysilane or M-(2-aminoethyl)-3-aminopropyltrimethoxysilane in hexane or toluene, taken in an amount of 0.1 wt. % of the total number of mentioned starting components.
[0019] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 4: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 23,60;
пентаэритрит техническим 21 ,66; полифосфат аммония 46,10; структурирующий агент, плавящийся под воздействием тепла 6,06; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 2,48; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов. [0019] Fire Retardant Intumescent Composition for Metalwork and/or Primer Coatings No. 4: base packaged in one or more equal or unequal container units: silicone rubber base 23.60; technical pentaerythritol 21.66; ammonium polyphosphate 46.10; heat melting structurant 6.06; catalytic mixture, packaged in one or more container units of equal or unequal volume 2.48; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.1 May. % of the total number of mentioned starting components.
[0020] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 5: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 30,34; пентаэритрит технический 18,57; полифосфат аммония 42,10; структурирующий агент, плавящийся под воздействием тепла 5,73; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 3,16; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов. [0020] Set of Fire Retardant Intumescent Composition for Metalwork and/or Primer Coatings No. 5: base packaged in one or more equal or unequal container units: silicone rubber base 30.34; technical pentaerythritol 18.57; ammonium polyphosphate 42.10; heat melting structurant 5.73; catalytic mixture, packaged in one or more container units of equal or unequal volume 3.16; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.1 May. % of the total number of mentioned starting components.
[0021] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 6: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 40,44; пентаэритрит технический 17,18; полифосфат аммония 35,10; структурирующий агент, плавящийся под воздействием тепла 3,0; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 4,18; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов.
[0022] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 7: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 23,59; пентаэритрит технический 22,0; полифосфат аммония 46,0; структурирующий агент, плавящийся под воздействием тепла 6,07; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 2,24; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,05 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде 10% раствора М(бета- аминоэтил)гамма-аминопропилтриметоксисилана и гамма- аминопропилтриметоксисилана или М-(2-аминоэтил)-3- аминопропилтриметоксисилана в гексане или толуоле, взятого в количестве 0,05 мае. % от общего количества упомянутых исходных компонентов. [0021] Fire Retardant Intumescent Composition for Metalwork and/or Primer Coatings No. 6: base packaged in one or more equal or unequal container units: silicone rubber base 40.44; technical pentaerythritol 17.18; ammonium polyphosphate 35.10; heat melting structuring agent 3.0; catalytic mixture, packaged in one or more container units of equal or unequal volume 4.18; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.1 May. % of the total number of mentioned starting components. [0022] Fire Retardant Intumescent Composition for Metalwork and/or Primer Coatings No. 7: base packaged in one or more equal or unequal container units: silicone rubber base 23.59; technical pentaerythritol 22.0; ammonium polyphosphate 46.0; heat melting structurant 6.07; catalytic mixture packaged in one or more container units of equal or unequal volume 2.24; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.05 May. % of the total number of mentioned starting components; and contains an additive in the form of a 10% solution of M(beta-aminoethyl)gamma-aminopropyltrimethoxysilane and gamma-aminopropyltrimethoxysilane or M-(2-aminoethyl)-3-aminopropyltrimethoxysilane in hexane or toluene, taken in an amount of 0.05 wt. % of the total number of mentioned starting components.
[0023] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 8: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 23,59; пентаэритрит технический 22,0; полифосфат аммония 46,0; структурирующий агент, плавящийся под воздействием тепла 6,07; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 2,04; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,15 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде 10% раствора М(бета- аминоэтил)гамма-аминопропилтриметоксисилана и гамма- аминопропилтриметоксисилана или М-(2-аминоэтил)-3- аминопропилтриметоксисилана в гексане или толуоле, взятого в количестве 0,15 мае. % от общего количества упомянутых исходных компонентов.
[0024] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 9: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 23,59; пентаэритрит технический 22,0; полифосфат аммония 46,0; структурирующий агент, плавящийся под воздействием тепла 6,07; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 2,14; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,05 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде 10% раствора М(бета- аминоэтил)гамма-аминопропилтриметоксисилана и гамма- аминопропилтриметоксисилана или М-(2-аминоэтил)-3- аминопропилтриметоксисилана в гексане или толуоле, взятого в количестве 0,15 мае. % от общего количества упомянутых исходных компонентов. [0023] Fire Retardant Intumescent Composition for Metalwork and/or Undercoats No. 8: base packaged in one or more equal or unequal container units: silicone rubber base 23.59; technical pentaerythritol 22.0; ammonium polyphosphate 46.0; heat melting structurant 6.07; catalytic mixture, packaged in one or more container units of equal or unequal volume 2.04; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.15 May. % of the total number of mentioned starting components; and contains an additive in the form of a 10% solution of M(beta-aminoethyl)gamma-aminopropyltrimethoxysilane and gamma-aminopropyltrimethoxysilane or M-(2-aminoethyl)-3-aminopropyltrimethoxysilane in hexane or toluene, taken in an amount of 0.15 wt. % of the total number of mentioned starting components. [0024] Fire Retardant Intumescent Composition for Metalwork and/or Primer Coatings No. 9: base packaged in one or more equal or unequal container units: silicone rubber base 23.59; technical pentaerythritol 22.0; ammonium polyphosphate 46.0; heat melting structurant 6.07; catalyst mixture packaged in one or more container units of equal or unequal volume 2.14; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.05 May. % of the total number of mentioned starting components; and contains an additive in the form of a 10% solution of M(beta-aminoethyl)gamma-aminopropyltrimethoxysilane and gamma-aminopropyltrimethoxysilane or M-(2-aminoethyl)-3-aminopropyltrimethoxysilane in hexane or toluene, taken in an amount of 0.15 wt. % of the total number of mentioned starting components.
[0025] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 10: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 23,59; пентаэритрит технический 22,0; полифосфат аммония 46,0; структурирующий агент, плавящийся под воздействием тепла 6,07; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 2,14; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,15 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде 10% раствора М(бета- аминоэтил)гамма-аминопропилтриметоксисилана и гамма- аминопропилтриметоксисилана или М-(2-аминоэтил)-3- аминопропилтриметоксисилана в гексане или толуоле, взятого в количестве 0,05 мае. % от общего количества упомянутых исходных компонентов.
[0026] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 11 : основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 23,59; пентаэритрит технический 22,0; полифосфат аммония 46,0; структурирующий агент, плавящийся под воздействием тепла 6,07; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 2,09; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде 10% раствора М(бета- аминоэтил)гамма-аминопропилтриметоксисилана и гамма- аминопропилтриметоксисилана или М-(2-аминоэтил)-3- аминопропилтриметоксисилана в гексане или толуоле, взятого в количестве 0,15 мае. % от общего количества упомянутых исходных компонентов. [0025] Set of Fire Retardant Intumescent Composition for Metalwork and/or Primer Coatings No. 10: base packaged in one or more equal or unequal container units: silicone rubber base 23.59; technical pentaerythritol 22.0; ammonium polyphosphate 46.0; heat melting structurant 6.07; catalyst mixture packaged in one or more container units of equal or unequal volume 2.14; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.15 May. % of the total number of mentioned starting components; and contains an additive in the form of a 10% solution of M(beta-aminoethyl)gamma-aminopropyltrimethoxysilane and gamma-aminopropyltrimethoxysilane or M-(2-aminoethyl)-3-aminopropyltrimethoxysilane in hexane or toluene, taken in an amount of 0.05 wt. % of the total number of mentioned starting components. [0026] Fire Retardant Intumescent Composition for Metalwork and/or Primer Coatings No. 11: base packaged in one or more equal or unequal container units: silicone rubber base 23.59; technical pentaerythritol 22.0; ammonium polyphosphate 46.0; heat melting structurant 6.07; catalytic mixture, packaged in one or more container units of equal or unequal volume 2.09; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.1 May. % of the total number of mentioned starting components; and contains an additive in the form of a 10% solution of M(beta-aminoethyl)gamma-aminopropyltrimethoxysilane and gamma-aminopropyltrimethoxysilane or M-(2-aminoethyl)-3-aminopropyltrimethoxysilane in hexane or toluene, taken in an amount of 0.15 wt. % of the total number of mentioned starting components.
[0027] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 12: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 23,59; пентаэритрит технический 22,0; полифосфат аммония 46,0; структурирующий агент, плавящийся под воздействием тепла 6,07; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 2,09; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,15 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде 10% раствора М(бета- аминоэтил)гамма-аминопропилтриметоксисилана и гамма- аминопропилтриметоксисилана или М-(2-аминоэтил)-3- аминопропилтриметоксисилана в гексане или толуоле, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов.
[0028] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 13: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 30,33; пентаэритрит технический 19,00; полифосфат аммония 42,00; структурирующий агент, плавящийся под воздействием тепла 5,74; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 2,83; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,05 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде 10% раствора М(бета- аминоэтил)гамма-аминопропилтриметоксисилана и гамма- аминопропилтриметоксисилана или М-(2-аминоэтил)-3- аминопропилтриметоксисилана в гексане или толуоле, взятого в количестве 0,05 мае. % от общего количества упомянутых исходных компонентов. [0027] Set of Fire Retardant Intumescent Composition for Metalwork and/or Primer Coatings No. 12: base packaged in one or more equal or unequal container units: silicone rubber base 23.59; technical pentaerythritol 22.0; ammonium polyphosphate 46.0; heat melting structurant 6.07; catalytic mixture, packaged in one or more container units of equal or unequal volume 2.09; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.15 May. % of the total number of mentioned starting components; and contains an additive in the form of a 10% solution of M(beta-aminoethyl)gamma-aminopropyltrimethoxysilane and gamma-aminopropyltrimethoxysilane or M-(2-aminoethyl)-3-aminopropyltrimethoxysilane in hexane or toluene, taken in an amount of 0.1 wt. % of the total number of mentioned starting components. [0028] Set of Fire Retardant Intumescent Composition for Metalwork and/or Primer Coatings No. 13: base packaged in one or more equal or unequal container units: silicone rubber base 30.33; technical pentaerythritol 19.00; ammonium polyphosphate 42.00; heat melting structurant 5.74; catalytic mixture, packaged in one or more container units of equal or unequal volume 2.83; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.05 May. % of the total number of mentioned starting components; and contains an additive in the form of a 10% solution of M(beta-aminoethyl)gamma-aminopropyltrimethoxysilane and gamma-aminopropyltrimethoxysilane or M-(2-aminoethyl)-3-aminopropyltrimethoxysilane in hexane or toluene, taken in an amount of 0.05 wt. % of the total number of mentioned starting components.
[0029] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 14: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 30,33; пентаэритрит технический 19,00; полифосфат аммония 42,00; структурирующий агент, плавящийся под воздействием тепла 5,74; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 2,63; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,15 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде 10% раствора М(бета- аминоэтил)гамма-аминопропилтриметоксисилана и гамма- аминопропилтриметоксисилана или М-(2-аминоэтил)-3- аминопропилтриметоксисилана в гексане или толуоле, взятого в количестве 0,15 мае. % от общего количества упомянутых исходных компонентов.
[0030] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 14: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 30,33; пентаэритрит технический 19,00; полифосфат аммония 42,00; структурирующий агент, плавящийся под воздействием тепла 5,74; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 2,73; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,15 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде 10% раствора М(бета- аминоэтил)гамма-аминопропилтриметоксисилана и гамма- аминопропилтриметоксисилана или М-(2-аминоэтил)-3- аминопропилтриметоксисилана в гексане или толуоле, взятого в количестве 0,05 мае. % от общего количества упомянутых исходных компонентов. [0029] Fire Retardant Intumescent Composition for Metalwork and/or Primer Coatings No. 14: base packaged in one or more equal or unequal container units: silicone rubber base 30.33; technical pentaerythritol 19.00; ammonium polyphosphate 42.00; heat melting structurant 5.74; catalytic mixture, packaged in one or more container units of equal or unequal volume 2.63; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.15 May. % of the total number of mentioned starting components; and contains an additive in the form of a 10% solution of M(beta-aminoethyl)gamma-aminopropyltrimethoxysilane and gamma-aminopropyltrimethoxysilane or M-(2-aminoethyl)-3-aminopropyltrimethoxysilane in hexane or toluene, taken in an amount of 0.15 wt. % of the total number of mentioned starting components. [0030] Fire Retardant Intumescent Composition for Metalwork and/or Primer Coatings No. 14: base packaged in one or more equal or unequal container units: silicone rubber base 30.33; technical pentaerythritol 19.00; ammonium polyphosphate 42.00; heat melting structurant 5.74; catalytic mixture, packaged in one or more container units of equal or unequal volume 2.73; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.15 May. % of the total number of mentioned starting components; and contains an additive in the form of a 10% solution of M(beta-aminoethyl)gamma-aminopropyltrimethoxysilane and gamma-aminopropyltrimethoxysilane or M-(2-aminoethyl)-3-aminopropyltrimethoxysilane in hexane or toluene, taken in an amount of 0.05 wt. % of the total number of mentioned starting components.
[0031] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 15: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 30,33; пентаэритрит технический 19,00; полифосфат аммония 42,00; структурирующий агент, плавящийся под воздействием тепла 5,74; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 2,73; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,05 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде 10% раствора М(бета- аминоэтил)гамма-аминопропилтриметоксисилана и гамма- аминопропилтриметоксисилана или М-(2-аминоэтил)-3- аминопропилтриметоксисилана в гексане или толуоле, взятого в количестве 0,15 мае. % от общего количества упомянутых исходных компонентов.
[0032] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 16: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 30,33; пентаэритрит технический 19,00; полифосфат аммония 42,00; структурирующий агент, плавящийся под воздействием тепла 5,74; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 2,68; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде 10% раствора М(бета- аминоэтил)гамма-аминопропилтриметоксисилана и гамма- аминопропилтриметоксисилана или М-(2-аминоэтил)-3- аминопропилтриметоксисилана в гексане или толуоле, взятого в количестве 0,15 мае. % от общего количества упомянутых исходных компонентов. [0031] Fire Retardant Intumescent Composition for Metalwork and/or Primer Coatings No. 15: base packaged in one or more equal or unequal container units: silicone rubber base 30.33; technical pentaerythritol 19.00; ammonium polyphosphate 42.00; heat melting structurant 5.74; catalytic mixture, packaged in one or more container units of equal or unequal volume 2.73; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.05 May. % of the total number of mentioned starting components; and contains an additive in the form of a 10% solution of M(beta-aminoethyl)gamma-aminopropyltrimethoxysilane and gamma-aminopropyltrimethoxysilane or M-(2-aminoethyl)-3-aminopropyltrimethoxysilane in hexane or toluene, taken in an amount of 0.15 wt. % of the total number of mentioned starting components. [0032] Fire Retardant Intumescent Composition for Metalwork and/or Primer Coatings No. 16: base packaged in one or more equal or unequal container units: silicone rubber base 30.33; technical pentaerythritol 19.00; ammonium polyphosphate 42.00; heat melting structurant 5.74; catalytic mixture, packaged in one or more container units of equal or unequal volume 2.68; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.1 May. % of the total number of mentioned starting components; and contains an additive in the form of a 10% solution of M(beta-aminoethyl)gamma-aminopropyltrimethoxysilane and gamma-aminopropyltrimethoxysilane or M-(2-aminoethyl)-3-aminopropyltrimethoxysilane in hexane or toluene, taken in an amount of 0.15 wt. % of the total number of mentioned starting components.
[0033] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 17: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 30,33; пентаэритрит технический 19,00; полифосфат аммония 42,00; структурирующий агент, плавящийся под воздействием тепла 5,74; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 2,68; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,15 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде 10% раствора М(бета- аминоэтил)гамма-аминопропилтриметоксисилана и гамма- аминопропилтриметоксисилана или М-(2-аминоэтил)-3- аминопропилтриметоксисилана в гексане или толуоле, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов.
[0034] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 18: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 40,44; пентаэритрит технический 17,76; полифосфат аммония 35,00; структурирующий агент, плавящийся под воздействием тепла 3,0; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 3,50; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,15 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде 10% раствора М(бета- аминоэтил)гамма-аминопропилтриметоксисилана и гамма- аминопропилтриметоксисилана или М-(2-аминоэтил)-3- аминопропилтриметоксисилана в гексане или толуоле, взятого в количестве 0,15 мае. % от общего количества упомянутых исходных компонентов. [0033] Set of Fire Retardant Intumescent Composition for Metalwork and/or Primer Coatings No. 17: base packaged in one or more equal or unequal container units: silicone rubber base 30.33; technical pentaerythritol 19.00; ammonium polyphosphate 42.00; heat melting structurant 5.74; catalytic mixture, packaged in one or more container units of equal or unequal volume 2.68; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.15 May. % of the total number of mentioned starting components; and contains an additive in the form of a 10% solution of M(beta-aminoethyl)gamma-aminopropyltrimethoxysilane and gamma-aminopropyltrimethoxysilane or M-(2-aminoethyl)-3-aminopropyltrimethoxysilane in hexane or toluene, taken in an amount of 0.1 wt. % of the total number of mentioned starting components. [0034] Fire Retardant Intumescent Composition for Metalwork and/or Undercoats No. 18: base packaged in one or more equal or unequal container units: silicone rubber base 40.44; technical pentaerythritol 17.76; ammonium polyphosphate 35.00; heat melting structuring agent 3.0; catalyst mixture packaged in one or more container units of equal or unequal volume 3.50; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.15 May. % of the total number of mentioned starting components; and contains an additive in the form of a 10% solution of M(beta-aminoethyl)gamma-aminopropyltrimethoxysilane and gamma-aminopropyltrimethoxysilane or M-(2-aminoethyl)-3-aminopropyltrimethoxysilane in hexane or toluene, taken in an amount of 0.15 wt. % of the total number of mentioned starting components.
[0035] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 19: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 40,44; пентаэритрит технический 17,76; полифосфат аммония 35,00; структурирующий агент, плавящийся под воздействием тепла 3,0; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 3,70; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,05 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде 10% раствора М(бета- аминоэтил)гамма-аминопропилтриметоксисилана и гамма- аминопропилтриметоксисилана или М-(2-аминоэтил)-3- аминопропилтриметоксисилана в гексане или толуоле, взятого в количестве 0,05 мае. % от общего количества упомянутых исходных компонентов.
[0036] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 20: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 40,44; пентаэритрит технический 17,76; полифосфат аммония 35,00; структурирующий агент, плавящийся под воздействием тепла 3,0; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 3,60; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,05 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде 10% раствора М(бета- аминоэтил)гамма-аминопропилтриметоксисилана и гамма- аминопропилтриметоксисилана или М-(2-аминоэтил)-3- аминопропилтриметоксисилана в гексане или толуоле, взятого в количестве 0,15 мае. % от общего количества упомянутых исходных компонентов. [0035] Fire Retardant Intumescent Composition for Metalwork and/or Undercoats No. 19: base packaged in one or more equal or unequal container units: silicone rubber base 40.44; technical pentaerythritol 17.76; ammonium polyphosphate 35.00; heat melting structuring agent 3.0; catalytic mixture, packaged in one or more container units of equal or unequal volume 3.70; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.05 May. % of the total number of mentioned starting components; and contains an additive in the form of a 10% solution of M(beta-aminoethyl)gamma-aminopropyltrimethoxysilane and gamma-aminopropyltrimethoxysilane or M-(2-aminoethyl)-3-aminopropyltrimethoxysilane in hexane or toluene, taken in an amount of 0.05 wt. % of the total number of mentioned starting components. [0036] Fire Retardant Intumescent Composition for Metalwork and/or Primer Coatings No. 20: base packaged in one or more equal or unequal container units: silicone rubber base 40.44; technical pentaerythritol 17.76; ammonium polyphosphate 35.00; heat melting structuring agent 3.0; catalytic mixture, packaged in one or more container units of equal or unequal volume 3.60; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.05 May. % of the total number of mentioned starting components; and contains an additive in the form of a 10% solution of M(beta-aminoethyl)gamma-aminopropyltrimethoxysilane and gamma-aminopropyltrimethoxysilane or M-(2-aminoethyl)-3-aminopropyltrimethoxysilane in hexane or toluene, taken in an amount of 0.15 wt. % of the total number of mentioned starting components.
[0037] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 21 : основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 40,44; пентаэритрит технический 17,76; полифосфат аммония 35,00; структурирующий агент, плавящийся под воздействием тепла 3,0; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 3,60; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,15 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде 10% раствора М(бета- аминоэтил)гамма-аминопропилтриметоксисилана и гамма- аминопропилтриметоксисилана или М-(2-аминоэтил)-3- аминопропилтриметоксисилана в гексане или толуоле, взятого в количестве 0,05 мае. % от общего количества упомянутых исходных компонентов.
[0038] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 22: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 40,44; пентаэритрит технический 17,76; полифосфат аммония 35,00; структурирующий агент, плавящийся под воздействием тепла 3,0; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 3,65; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде 10% раствора М(бета- аминоэтил)гамма-аминопропилтриметоксисилана и гамма- аминопропилтриметоксисилана или М-(2-аминоэтил)-3- аминопропилтриметоксисилана в гексане или толуоле, взятого в количестве 0,05 мае. % от общего количества упомянутых исходных компонентов. [0037] Set of Fire Retardant Intumescent Composition for Metalwork and/or Primer Coatings No. 21: base packaged in one or more equal or unequal container units: silicone rubber base 40.44; technical pentaerythritol 17.76; ammonium polyphosphate 35.00; heat melting structuring agent 3.0; catalytic mixture, packaged in one or more container units of equal or unequal volume 3.60; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.15 May. % of the total number of mentioned starting components; and contains an additive in the form of a 10% solution of M(beta-aminoethyl)gamma-aminopropyltrimethoxysilane and gamma-aminopropyltrimethoxysilane or M-(2-aminoethyl)-3-aminopropyltrimethoxysilane in hexane or toluene, taken in an amount of 0.05 wt. % of the total number of mentioned starting components. [0038] Fire Retardant Intumescent Composition for Metalwork and/or Undercoats No. 22: base packaged in one or more equal or unequal container units: silicone rubber base 40.44; technical pentaerythritol 17.76; ammonium polyphosphate 35.00; heat melting structuring agent 3.0; catalytic mixture, packaged in one or more container units of equal or unequal volume 3.65; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.1 May. % of the total number of mentioned starting components; and contains an additive in the form of a 10% solution of M(beta-aminoethyl)gamma-aminopropyltrimethoxysilane and gamma-aminopropyltrimethoxysilane or M-(2-aminoethyl)-3-aminopropyltrimethoxysilane in hexane or toluene, taken in an amount of 0.05 wt. % of the total number of mentioned starting components.
[0039] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 23: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 40,44; пентаэритрит технический 17,76; полифосфат аммония 35,00; структурирующий агент, плавящийся под воздействием тепла 3,0; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 3,65; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,05 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде 10% раствора М(бета- аминоэтил)гамма-аминопропилтриметоксисилана и гамма- аминопропилтриметоксисилана или М-(2-аминоэтил)-3- аминопропилтриметоксисилана в гексане или толуоле, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов.
[0040] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 24: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 23,60; пентаэритрит технический 21 ,66; полифосфат аммония 46,10; структурирующий агент, плавящийся под воздействием тепла 6,06; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 2,53; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,05 мае. % от общего количества упомянутых исходных компонентов. [0039] Fire Retardant Intumescent Composition for Metalwork and/or Undercoats No. 23: base packaged in one or more equal or unequal container units: silicone rubber base 40.44; technical pentaerythritol 17.76; ammonium polyphosphate 35.00; heat melting structuring agent 3.0; catalytic mixture, packaged in one or more container units of equal or unequal volume 3.65; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.05 May. % of the total number of mentioned starting components; and contains an additive in the form of a 10% solution of M(beta-aminoethyl)gamma-aminopropyltrimethoxysilane and gamma-aminopropyltrimethoxysilane or M-(2-aminoethyl)-3-aminopropyltrimethoxysilane in hexane or toluene, taken in an amount of 0.1 wt. % of the total number of mentioned starting components. [0040] Fire Retardant Intumescent Composition for Metalwork and/or Primer Coatings No. 24: base packaged in one or more equal or unequal container units: silicone rubber base 23.60; technical pentaerythritol 21.66; ammonium polyphosphate 46.10; heat melting structurant 6.06; catalytic mixture, packaged in one or more container units of equal or unequal volume 2.53; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.05 May. % of the total number of mentioned starting components.
[0041] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 25: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 23,60; пентаэритрит технический 21 ,66; полифосфат аммония 46,10; структурирующий агент, плавящийся под воздействием тепла 6,06; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 2,43; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,15 мае. % от общего количества упомянутых исходных компонентов. [0041] Set of Fire Retardant Intumescent Composition for Metalwork and/or Primer Coatings No. 25: base packaged in one or more equal or unequal container units: silicone rubber base 23.60; technical pentaerythritol 21.66; ammonium polyphosphate 46.10; heat melting structurant 6.06; catalytic mixture, packaged in one or more container units of equal or unequal volume 2.43; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.15 May. % of the total number of mentioned starting components.
[0042] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 26: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 30,34; пентаэритрит технический 18,57; полифосфат аммония 42,10; структурирующий агент, плавящийся под воздействием тепла 5,73;
катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 3,21 ; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,05 мае. % от общего количества упомянутых исходных компонентов. [0042] Fire Retardant Intumescent Composition for Metalwork and/or Undercoats No. 26: base packaged in one or more equal or unequal container units: silicone rubber base 30.34; technical pentaerythritol 18.57; ammonium polyphosphate 42.10; heat melting structurant 5.73; catalytic mixture, packaged in one or more tare units of equal or unequal volume 3.21 ; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.05 May. % of the total number of mentioned starting components.
[0043] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 27: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 30,34; пентаэритрит технический 18,57; полифосфат аммония 42,10; структурирующий агент, плавящийся под воздействием тепла 5,73; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 3,11 ; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,15 мае. % от общего количества упомянутых исходных компонентов. [0043] Set of Fire Retardant Intumescent Composition for Metalwork and/or Primer Coatings No. 27: base packaged in one or more equal or unequal container units: silicone rubber base 30.34; technical pentaerythritol 18.57; ammonium polyphosphate 42.10; heat melting structurant 5.73; catalytic mixture packaged in one or more tare units of equal or unequal volume 3.11 ; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.15 May. % of the total number of mentioned starting components.
[0044] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 28: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 40,44; пентаэритрит технический 17,18; полифосфат аммония 35,10; структурирующий агент, плавящийся под воздействием тепла 3,0; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 4,23; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,05 мае. % от общего количества упомянутых исходных компонентов. [0044] Fire Retardant Intumescent Composition for Metalwork and/or Undercoats No. 28: base packaged in one or more equal or unequal container units: silicone rubber base 40.44; technical pentaerythritol 17.18; ammonium polyphosphate 35.10; heat melting structuring agent 3.0; catalytic mixture, packaged in one or more container units of equal or unequal volume 4.23; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.05 May. % of the total number of mentioned starting components.
[0045] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 29: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма:
силиконовая каучуковая основа 40,44; пентаэритрит технический 17,18; полифосфат аммония 35,10; структурирующий агент, плавящийся под воздействием тепла 3,0; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 4,13; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,15 мае. % от общего количества упомянутых исходных компонентов. [0045] Set of Fire Retardant Intumescent Composition for Metalwork and/or Undercoats No. 29: base packaged in one or more equal or unequal container units: silicone rubber base 40.44; technical pentaerythritol 17.18; ammonium polyphosphate 35.10; heat melting structuring agent 3.0; catalytic mixture, packaged in one or more container units of equal or unequal volume 4.13; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.15 May. % of the total number of mentioned starting components.
[0046] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 30: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 23,59; пентаэритрит технический 22,0; полифосфат аммония 46,0; структурирующий агент, плавящийся под воздействием тепла 6,07; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 2,09; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде 10% раствора М(бета- аминоэтил)гамма-аминопропилтриметоксисилана и гамма- аминопропилтриметоксисилана или М-(2-аминоэтил)-3- аминопропилтриметоксисилана в гексане или толуоле, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде ускорителя полимеризации, взятого в количестве 0,05 мае. % от общего количества упомянутых исходных компонентов. [0046] Fire Retardant Intumescent Composition for Metalwork and/or Primer Coatings No. 30: base packaged in one or more equal or unequal container units: silicone rubber base 23.59; technical pentaerythritol 22.0; ammonium polyphosphate 46.0; heat melting structurant 6.07; catalytic mixture, packaged in one or more container units of equal or unequal volume 2.09; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.1 May. % of the total number of mentioned starting components; and contains an additive in the form of a 10% solution of M(beta-aminoethyl)gamma-aminopropyltrimethoxysilane and gamma-aminopropyltrimethoxysilane or M-(2-aminoethyl)-3-aminopropyltrimethoxysilane in hexane or toluene, taken in an amount of 0.1 wt. % of the total number of mentioned starting components; and contains an additive in the form of a polymerization accelerator, taken in the amount of 0.05 May. % of the total number of mentioned starting components.
[0047] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 31 : основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 23,59; пентаэритрит технический 22,0; полифосфат аммония 46,0;
структурирующий агент, плавящийся под воздействием тепла 6,07; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 2,04; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде 10% раствора М(бета- аминоэтил)гамма-аминопропилтриметоксисилана и гамма- аминопропилтриметоксисилана или М-(2-аминоэтил)-3- аминопропилтриметоксисилана в гексане или толуоле, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде ускорителя полимеризации, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов. [0047] Set of Fire Retardant Intumescent Composition for Metalwork and/or Primer Coatings No. 31: base packaged in one or more equal or unequal container units: silicone rubber base 23.59; technical pentaerythritol 22.0; ammonium polyphosphate 46.0; heat melting structurant 6.07; catalytic mixture, packaged in one or more container units of equal or unequal volume 2.04; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.1 May. % of the total number of mentioned starting components; and contains an additive in the form of a 10% solution of M(beta-aminoethyl)gamma-aminopropyltrimethoxysilane and gamma-aminopropyltrimethoxysilane or M-(2-aminoethyl)-3-aminopropyltrimethoxysilane in hexane or toluene, taken in an amount of 0.1 wt. % of the total number of mentioned starting components; and contains an additive in the form of a polymerization accelerator, taken in an amount of 0.1 May. % of the total number of mentioned starting components.
[0048] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 32: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 23,59; пентаэритрит технический 22,0; полифосфат аммония 46,0; структурирующий агент, плавящийся под воздействием тепла 6,07; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 1 ,99; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде 10% раствора М(бета- аминоэтил)гамма-аминопропилтриметоксисилана и гамма- аминопропилтриметоксисилана или М-(2-аминоэтил)-3- аминопропилтриметоксисилана в гексане или толуоле, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде ускорителя полимеризации, взятого в количестве 0,15 мае. % от общего количества упомянутых исходных компонентов. [0048] Fire Retardant Intumescent Composition for Metalwork and/or Undercoats No. 32: base packaged in one or more equal or unequal container units: silicone rubber base 23.59; technical pentaerythritol 22.0; ammonium polyphosphate 46.0; heat melting structurant 6.07; catalytic mixture, packaged in one or more container units of equal or unequal volume 1.99; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.1 May. % of the total number of mentioned starting components; and contains an additive in the form of a 10% solution of M(beta-aminoethyl)gamma-aminopropyltrimethoxysilane and gamma-aminopropyltrimethoxysilane or M-(2-aminoethyl)-3-aminopropyltrimethoxysilane in hexane or toluene, taken in an amount of 0.1 wt. % of the total number of mentioned starting components; and contains an additive in the form of a polymerization accelerator, taken in the amount of 0.15 May. % of the total number of mentioned starting components.
[0049] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 33: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма:
силиконовая каучуковая основа 30,33; пентаэритрит технический 19,00; полифосфат аммония 42,00; структурирующий агент, плавящийся под воздействием тепла 5,74; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 2,68; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде 10% раствора М(бета- аминоэтил)гамма-аминопропилтриметоксисилана и гамма- аминопропилтриметоксисилана или М-(2-аминоэтил)-3- аминопропилтриметоксисилана в гексане или толуоле, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде ускорителя полимеризации, взятого в количестве 0,05 мае. % от общего количества упомянутых исходных компонентов. [0049] Set of Fire Retardant Intumescent Composition for Metalwork and/or Primers No. 33: base packaged in one or more container units of equal or unequal volume: silicone rubber base 30.33; technical pentaerythritol 19.00; ammonium polyphosphate 42.00; heat melting structurant 5.74; catalytic mixture, packaged in one or more container units of equal or unequal volume 2.68; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.1 May. % of the total number of mentioned starting components; and contains an additive in the form of a 10% solution of M(beta-aminoethyl)gamma-aminopropyltrimethoxysilane and gamma-aminopropyltrimethoxysilane or M-(2-aminoethyl)-3-aminopropyltrimethoxysilane in hexane or toluene, taken in an amount of 0.1 wt. % of the total number of mentioned starting components; and contains an additive in the form of a polymerization accelerator, taken in the amount of 0.05 May. % of the total number of mentioned starting components.
[0050] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 34: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 30,33; пентаэритрит технический 19,00; полифосфат аммония 42,00; структурирующий агент, плавящийся под воздействием тепла 5,74; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 2,63; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде 10% раствора М(бета- аминоэтил)гамма-аминопропилтриметоксисилана и гамма- аминопропилтриметоксисилана или М-(2-аминоэтил)-3- аминопропилтриметоксисилана в гексане или толуоле, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде ускорителя полимеризации, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов.
[0051 ] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 35: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 30,33; пентаэритрит технический 19,00; полифосфат аммония 42,00; структурирующий агент, плавящийся под воздействием тепла 5,74; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 2,58; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде 10% раствора М(бета- аминоэтил)гамма-аминопропилтриметоксисилана и гамма- аминопропилтриметоксисилана или М-(2-аминоэтил)-3- аминопропилтриметоксисилана в гексане или толуоле, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде ускорителя полимеризации, взятого в количестве 0,15 мае. % от общего количества упомянутых исходных компонентов. [0050] Set of Fire Retardant Intumescent Composition for Metalwork and/or Primer Coatings No. 34: base packaged in one or more equal or unequal container units: silicone rubber base 30.33; technical pentaerythritol 19.00; ammonium polyphosphate 42.00; heat melting structurant 5.74; catalytic mixture, packaged in one or more container units of equal or unequal volume 2.63; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.1 May. % of the total number of mentioned starting components; and contains an additive in the form of a 10% solution of M(beta-aminoethyl)gamma-aminopropyltrimethoxysilane and gamma-aminopropyltrimethoxysilane or M-(2-aminoethyl)-3-aminopropyltrimethoxysilane in hexane or toluene, taken in an amount of 0.1 wt. % of the total number of mentioned starting components; and contains an additive in the form of a polymerization accelerator, taken in an amount of 0.1 May. % of the total number of mentioned starting components. [0051] Fire Retardant Intumescent Composition for Metalwork and/or Undercoats No. 35: base packaged in one or more equal or unequal container units: silicone rubber base 30.33; technical pentaerythritol 19.00; ammonium polyphosphate 42.00; heat melting structurant 5.74; catalytic mixture packaged in one or more container units of equal or unequal volume 2.58; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.1 May. % of the total number of mentioned starting components; and contains an additive in the form of a 10% solution of M(beta-aminoethyl)gamma-aminopropyltrimethoxysilane and gamma-aminopropyltrimethoxysilane or M-(2-aminoethyl)-3-aminopropyltrimethoxysilane in hexane or toluene, taken in an amount of 0.1 wt. % of the total number of mentioned starting components; and contains an additive in the form of a polymerization accelerator, taken in the amount of 0.15 May. % of the total number of mentioned starting components.
[0052] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 36: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 40,44; пентаэритрит технический 17,76; полифосфат аммония 35,00; структурирующий агент, плавящийся под воздействием тепла 3,0; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 3,55; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде 10% раствора М(бета- аминоэтил)гамма-аминопропилтриметоксисилана и гамма- аминопропилтриметоксисилана или М-(2-аминоэтил)-3- аминопропилтриметоксисилана в гексане или толуоле, взятого в количестве 0,1 мае.
% от общего количества упомянутых исходных компонентов; и содержит добавку в виде ускорителя полимеризации, взятого в количестве 0,05 мае. % от общего количества упомянутых исходных компонентов. [0052] Fire Retardant Intumescent Composition for Metalwork and/or Undercoats No. 36: base packaged in one or more equal or unequal container units: silicone rubber base 40.44; technical pentaerythritol 17.76; ammonium polyphosphate 35.00; heat melting structuring agent 3.0; catalytic mixture, packaged in one or more container units of equal or unequal volume 3.55; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.1 May. % of the total number of mentioned starting components; and contains an additive in the form of a 10% solution of M(beta-aminoethyl)gamma-aminopropyltrimethoxysilane and gamma-aminopropyltrimethoxysilane or M-(2-aminoethyl)-3-aminopropyltrimethoxysilane in hexane or toluene, taken in an amount of 0.1 wt. % of the total number of mentioned starting components; and contains an additive in the form of a polymerization accelerator, taken in the amount of 0.05 May. % of the total number of mentioned starting components.
[0053] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 37: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 40,44; пентаэритрит технический 17,76; полифосфат аммония 35,00; структурирующий агент, плавящийся под воздействием тепла 3,0; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 3,50; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде 10% раствора М(бета- аминоэтил)гамма-аминопропилтриметоксисилана и гамма- аминопропилтриметоксисилана или М-(2-аминоэтил)-3- аминопропилтриметоксисилана в гексане или толуоле, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде ускорителя полимеризации, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов. [0053] Fire Retardant Intumescent Composition for Metalwork and/or Primer Coatings No. 37: base packaged in one or more equal or unequal container units: silicone rubber base 40.44; technical pentaerythritol 17.76; ammonium polyphosphate 35.00; heat melting structuring agent 3.0; catalyst mixture packaged in one or more container units of equal or unequal volume 3.50; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.1 May. % of the total number of mentioned starting components; and contains an additive in the form of a 10% solution of M(beta-aminoethyl)gamma-aminopropyltrimethoxysilane and gamma-aminopropyltrimethoxysilane or M-(2-aminoethyl)-3-aminopropyltrimethoxysilane in hexane or toluene, taken in an amount of 0.1 wt. % of the total number of mentioned starting components; and contains an additive in the form of a polymerization accelerator, taken in an amount of 0.1 May. % of the total number of mentioned starting components.
[0054] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 38: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 40,44; пентаэритрит технический 17,76; полифосфат аммония 35,00; структурирующий агент, плавящийся под воздействием тепла 3,0; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 3,45; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде 10% раствора М(бета-
аминоэтил)гамма-аминопропилтриметоксисилана и гамма- аминопропилтриметоксисилана или 1\1-(2-аминоэтил)-3- аминопропилтриметоксисилана в гексане или толуоле, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде ускорителя полимеризации, взятого в количестве 0,15 мае. % от общего количества упомянутых исходных компонентов. [0054] Fire Retardant Intumescent Composition for Metalwork and/or Undercoats No. 38: base packaged in one or more equal or unequal container units: silicone rubber base 40.44; technical pentaerythritol 17.76; ammonium polyphosphate 35.00; heat melting structuring agent 3.0; catalytic mixture, packaged in one or more container units of equal or unequal volume 3.45; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.1 May. % of the total number of mentioned starting components; and contains an additive in the form of a 10% solution of M(beta- aminoethyl)gamma-aminopropyltrimethoxysilane and gamma-aminopropyltrimethoxysilane or 1\1-(2-aminoethyl)-3-aminopropyltrimethoxysilane in hexane or toluene, taken in an amount of 0.1 May. % of the total number of mentioned starting components; and contains an additive in the form of a polymerization accelerator, taken in the amount of 0.15 May. % of the total number of mentioned starting components.
[0055] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 39: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 23,60; пентаэритрит технический 21 ,66; полифосфат аммония 46,10; структурирующий агент, плавящийся под воздействием тепла 6,06; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 2,43; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде ускорителя полимеризации, взятого в количестве 0,05 мае. % от общего количества упомянутых исходных компонентов. [0055] Fire Retardant Intumescent Composition for Metalwork and/or Undercoats No. 39: base packaged in one or more equal or unequal container units: silicone rubber base 23.60; technical pentaerythritol 21.66; ammonium polyphosphate 46.10; heat melting structurant 6.06; catalytic mixture, packaged in one or more container units of equal or unequal volume 2.43; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.1 May. % of the total number of mentioned starting components; and contains an additive in the form of a polymerization accelerator, taken in the amount of 0.05 May. % of the total number of mentioned starting components.
[0056] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 40: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 23,60; пентаэритрит технический 21 ,66; полифосфат аммония 46,10; структурирующий агент, плавящийся под воздействием тепла 6,06; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 2,38; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде ускорителя полимеризации,
взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов. [0056] Fire Retardant Intumescent Composition for Metalwork and/or Undercoats No. 40: base packaged in one or more equal or unequal container units: silicone rubber base 23.60; technical pentaerythritol 21.66; ammonium polyphosphate 46.10; heat melting structurant 6.06; catalytic mixture, packaged in one or more container units of equal or unequal volume 2.38; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.1 May. % of the total number of mentioned starting components; and contains an additive in the form of a polymerization accelerator, taken in the amount of 0.1 May. % of the total number of mentioned starting components.
[0057] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 41 : основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 23,60; пентаэритрит технический 21 ,66; полифосфат аммония 46,10; структурирующий агент, плавящийся под воздействием тепла 6,06; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 2,33; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде ускорителя полимеризации, взятого в количестве 0,15 мае. % от общего количества упомянутых исходных компонентов. [0057] Fire Retardant Intumescent Composition for Metalwork and/or Primer Coatings No. 41: base packaged in one or more equal or unequal container units: silicone rubber base 23.60; technical pentaerythritol 21.66; ammonium polyphosphate 46.10; heat melting structurant 6.06; catalytic mixture, packaged in one or more container units of equal or unequal volume 2.33; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.1 May. % of the total number of mentioned starting components; and contains an additive in the form of a polymerization accelerator, taken in the amount of 0.15 May. % of the total number of mentioned starting components.
[0058] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 42: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 30,34; пентаэритрит технический 18,57; полифосфат аммония 42,10; структурирующий агент, плавящийся под воздействием тепла 5,73; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 3,09; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде ускорителя полимеризации, взятого в количестве 0,05 мае. % от общего количества упомянутых исходных компонентов. [0058] Fire Retardant Intumescent Composition for Metalwork and/or Primer Coatings No. 42: base packaged in one or more equal or unequal container units: silicone rubber base 30.34; technical pentaerythritol 18.57; ammonium polyphosphate 42.10; heat melting structurant 5.73; catalytic mixture, packaged in one or more container units of equal or unequal volume 3.09; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.1 May. % of the total number of mentioned starting components; and contains an additive in the form of a polymerization accelerator, taken in the amount of 0.05 May. % of the total number of mentioned starting components.
[0059] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 43:
основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 30,34; пентаэритрит технический 18,57; полифосфат аммония 42,10; структурирующий агент, плавящийся под воздействием тепла 5,73; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 3,04; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде ускорителя полимеризации, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов. [0059] Fire Retardant Intumescent Composition for Structural Steel and/or Primers No. 43: base packaged in one or more tare units of equal or unequal volume: silicone rubber base 30.34; technical pentaerythritol 18.57; ammonium polyphosphate 42.10; heat melting structurant 5.73; catalytic mixture, packaged in one or more container units of equal or unequal volume 3.04; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.1 May. % of the total number of mentioned starting components; and contains an additive in the form of a polymerization accelerator, taken in an amount of 0.1 May. % of the total number of mentioned starting components.
[0060] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 44: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 30,34; пентаэритрит технический 18,57; полифосфат аммония 42,10; структурирующий агент, плавящийся под воздействием тепла 5,73; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 2,99; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде ускорителя полимеризации, взятого в количестве 0,15 мае. % от общего количества упомянутых исходных компонентов. [0060] Fire Retardant Intumescent Composition for Metalwork and/or Undercoats No. 44: base packaged in one or more equal or unequal container units: silicone rubber base 30.34; technical pentaerythritol 18.57; ammonium polyphosphate 42.10; heat melting structurant 5.73; catalytic mixture, packaged in one or more tare units of equal or unequal volume 2.99; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.1 May. % of the total number of mentioned starting components; and contains an additive in the form of a polymerization accelerator, taken in the amount of 0.15 May. % of the total number of mentioned starting components.
[0061] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 45: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 40,44; пентаэритрит технический 17,18; полифосфат аммония 35,10;
структурирующий агент, плавящийся под воздействием тепла 3,0; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 4,13; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде ускорителя полимеризации, взятого в количестве 0,05 мае. % от общего количества упомянутых исходных компонентов. [0061] Fire Retardant Intumescent Composition for Metalwork and/or Undercoats No. 45: base packaged in one or more equal or unequal container units: silicone rubber base 40.44; technical pentaerythritol 17.18; ammonium polyphosphate 35.10; heat melting structuring agent 3.0; catalytic mixture, packaged in one or more container units of equal or unequal volume 4.13; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.1 May. % of the total number of mentioned starting components; and contains an additive in the form of a polymerization accelerator, taken in the amount of 0.05 May. % of the total number of mentioned starting components.
[0062] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 46: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 40,44; пентаэритрит технический 17,18; полифосфат аммония 35,10; структурирующий агент, плавящийся под воздействием тепла 3,0; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 4,08; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде ускорителя полимеризации, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов. [0062] Fire Retardant Intumescent Composition for Metalwork and/or Undercoats No. 46: base packaged in one or more equal or unequal container units: silicone rubber base 40.44; technical pentaerythritol 17.18; ammonium polyphosphate 35.10; heat melting structuring agent 3.0; catalytic mixture, packaged in one or more container units of equal or unequal volume 4.08; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.1 May. % of the total number of mentioned starting components; and contains an additive in the form of a polymerization accelerator, taken in an amount of 0.1 May. % of the total number of mentioned starting components.
[0063] Набор огнезащитной вспучивающейся композиции для металлоконструкций и/или грунтовочных покрытий № 47: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа 40,44; пентаэритрит технический 17,18; полифосфат аммония 35,10; структурирующий агент, плавящийся под воздействием тепла 3,0; катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объёма 4,03; при этом катализирующая смесь содержит добавку в виде модификатора вязкости, взятого в количестве 0,1 мае. % от общего количества упомянутых
исходных компонентов; и содержит добавку в виде ускорителя полимеризации, взятого в количестве 0,15 мае. % от общего количества упомянутых исходных компонентов. [0063] Fire Retardant Intumescent Composition for Metalwork and/or Undercoats No. 47: base packaged in one or more equal or unequal container units: silicone rubber base 40.44; technical pentaerythritol 17.18; ammonium polyphosphate 35.10; heat melting structuring agent 3.0; catalytic mixture, packaged in one or more container units of equal or unequal volume 4.03; while the catalytic mixture contains an additive in the form of a viscosity modifier, taken in the amount of 0.1 May. % of the total number mentioned initial components; and contains an additive in the form of a polymerization accelerator, taken in the amount of 0.15 May. % of the total number of mentioned starting components.
[0064] Способ приготовления каждого набора огнезащитной вспучивающейся композиции холодного отверждения для металлоконструкций и/или грунтовочных покрытий, например, не ограничиваясь, включает следующие основные этапы. На первом этапе каучуковую основу требуемой вязкости загружают в мешалку. На втором этапе при перемешивании добавляют к основе пентаэритрит технический и полифосфат аммония. На третьем этапе при перемешивании к смеси добавляют структурирующий агент, плавящийся под воздействием тепла. При этом готовность основы для розлива в тарные единицы контролируют посредством вискозиметра, например, не ограничиваясь, вискозиметра Брукфилда, при этом основа считается готовой, когда изменение вязкости основы вышло на плато. Наряду с указанными этапами готовят катализирующую смесь путем смешивания компонентов с модификатором вязкости (при необходимости и с ускорителем полимеризации) и 10% раствором М(бета-аминоэтил)гамма-аминопропилтриметоксисилана и гамма- минопропилтриметоксисилана или М-(2-аминоэтил)-3- аминопропилтриметоксисилана в гексане или толуоле или путем смешивания модификатора вязкости (при необходимости и ускорителя полимеризации) и 10% раствора М(бета-аминоэтил)гамма-аминопропилтриметоксисилана и гамма- минопропилтриметоксисилана или М-(2-аминоэтил)-3- аминопропилтриметоксисилана в гексане или толуоле с катализирующей смесью в виде готового продукта в указанных количествах, после чего разливают в тарные единицы в количестве, обеспечивающем указанное содержание компонентов в наборе; при этом ускоритель полимеризации может быть также использован в собственной тарной единице и добавлен в состав катализирующей смеси с добавками непосредственно перед приготовлением огнезащитной композиции. [0064] The method of preparing each set of cold set fire retardant intumescent composition for metal structures and/or primers, for example, without limitation, includes the following main steps. At the first stage, the rubber base of the required viscosity is loaded into the mixer. At the second stage, with stirring, technical pentaerythritol and ammonium polyphosphate are added to the base. In the third step, a heat-melting structuring agent is added to the mixture while stirring. At the same time, the readiness of the base for filling into tare units is controlled by means of a viscometer, for example, without limitation, a Brookfield viscometer, and the base is considered ready when the change in the viscosity of the base has reached a plateau. Along with the above steps, a catalytic mixture is prepared by mixing the components with a viscosity modifier (if necessary, with a polymerization accelerator) and a 10% solution of M (beta-aminoethyl) gamma-aminopropyltrimethoxysilane and gamma-minopropyltrimethoxysilane or M- (2-aminoethyl) -3- aminopropyltrimethoxysilane in hexane or toluene, or by mixing a viscosity modifier (if necessary, and a polymerization accelerator) and a 10% solution of N (beta-aminoethyl) gamma-aminopropyltrimethoxysilane and gamma-aminopropyltrimethoxysilane or M-(2-aminoethyl)-3-aminopropyltrimethoxysilane in hexane or toluene with catalyzing mixture in the form of a finished product in the specified quantities, and then poured into containers in an amount that provides the specified content of the components in the set; in this case, the polymerization accelerator can also be used in its own container unit and added to the composition of the catalytic mixture with additives immediately before the preparation of the flame retardant composition.
[0065] Настоящее описание осуществления заявленного изобретения демонстрирует лишь частные варианты осуществления и не ограничивает иные варианты реализации заявленного изобретения, поскольку возможные иные альтернативные варианты осуществления заявленного изобретения, не выходящие за пределы объёма информации, изложенной в настоящей заявке, должны быть очевидными для специалиста в данной области техники, имеющим обычную квалификацию, на которого рассчитано заявленное изобретение.
[0065] The present description of the implementation of the claimed invention demonstrates only private embodiments and does not limit other embodiments of the claimed invention, since possible other alternative embodiments of the claimed invention that do not go beyond the scope of the information set forth in this application should be obvious to a person skilled in this field of technology, having the usual qualifications, for which the claimed invention is intended.
Claims
1. Набор для приготовления огнезащитной вспучивающейся композиции холодного отверждения для металлоконструкций и/или грунтовочных покрытий, включающий одну или несколько тарных единиц равного или неравного объёма с основой и одну или несколько тарных единиц равного или неравного объёма с катализатором или катализирующей смесью, причём в сумме тарные единицы содержат следующие исходные компоненты при следующем соотношении исходных компонентов, мае. %: основа, фасованная в одну или несколько тарных единиц равного или неравного объёма: силиконовая каучуковая основа, представляющая собой каучук синтетический термостойкий низкомолекулярный марки СКТН-А, или СКТН-Б, или СКТН-В, или СКТН-Г вязкостью от 100 до 20 000 сП или каучук синтетический термостойкий низкомолекулярный марки СКТН-А, или СКТН-Б, или СКТН-В, или СКТН-Г, разбавленной до вязкости от 100 до 20 000 сП низковязким неорганическим полимером с гидроксильной группой, в том числе, силанольной жидкостью, вязкостью от 50 до 120 сП 23,59-40,44; пентаэритрит технический 17,18-22,00; полифосфат аммония 35,10-46,10; структурирующий агент, плавящийся под воздействием тепла, представляющий собой одно из или комбинацию из: кварц, микросфера стеклянная, микросфера алюмосиликатная 3,10-6,17; и или катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объема, представляющая собой смесь гамма- аминопропилтриэтоксилана, трис-бутаноноксим-метилсилана и добавки в виде модификатора вязкости, являющегося пенорегулятором «ПЕНТА®-483», взятых при следующем соотношении компонентов от общего количества компонентов композиции, мае. %: гамма-аминопропилтриэтоксилан 0,49-0,84; трис-бутаноноксим-метилсилан 1 ,89-3,24; пенорегулятор «ПЕНТА®-483» 0,05-0,15; или катализирующая смесь, фасованная в одну или несколько тарных единиц равного или неравного объема, представляющая собой смесь гамма- аминопропилтриэтоксилана и трис-бутаноноксим-метилсилана, взятых при следующем соотношении компонентов от общего количества компонентов композиции, мае. %: гамма-аминопропилтриэтоксилан 0,49-0,84; трис-бутаноноксим-метилсилан 1 ,89-3,24; 1. A set for the preparation of a fire-retardant intumescent composition of cold curing for metal structures and / or primer coatings, including one or more container units of equal or unequal volume with the base and one or more container units of equal or unequal volume with a catalyst or catalytic mixture, and in total container units contain the following initial components at the following ratio of initial components, May. %: base packaged in one or more tare units of equal or unequal volume: silicone rubber base, which is synthetic heat-resistant low molecular weight rubber grade SKTN-A, or SKTN-B, or SKTN-V, or SKTN-G with a viscosity of 100 to 20 000 cP or synthetic heat-resistant low molecular weight rubber grade SKTN-A, or SKTN-B, or SKTN-V, or SKTN-G, diluted to a viscosity of 100 to 20,000 cP with a low-viscosity inorganic polymer with a hydroxyl group, including silanol liquid, viscosity from 50 to 120 cP 23.59-40.44; technical pentaerythritol 17.18-22.00; ammonium polyphosphate 35.10-46.10; structuring agent, melting under the influence of heat, which is one of or a combination of: quartz, glass microsphere, aluminosilicate microsphere 3.10-6.17; and or a catalyst mixture packaged in one or more container units of equal or unequal volume, which is a mixture of gamma-aminopropyltriethoxylan, tris-butanonoxime-methylsilane and an additive in the form of a viscosity modifier, which is a foam regulator "PENTA®-483", taken in the following ratio of components from the total number of components of the composition, May. %: gamma-aminopropyltriethoxylan 0.49-0.84; tris-butanonoxime-methylsilane 1.89-3.24; foam regulator "PENTA®-483" 0.05-0.15; or a catalytic mixture packaged in one or more container units of equal or unequal volume, which is a mixture of gamma-aminopropyltriethoxylan and tris-butanonoxime-methylsilane, taken in the following ratio of components from the total number of components of the composition, May. %: gamma-aminopropyltriethoxylan 0.49-0.84; tris-butanonoxime-methylsilane 1.89-3.24;
32
и добавка для катализирующей смеси в виде модификатора вязкости, являющегося пенорегулятором «ПЕНТА®-483», фасованная в отдельную тарную единицу в количестве 0,05-0,15 мае. % от общего количества компонентов композиции. 32 and an additive for the catalytic mixture in the form of a viscosity modifier, which is a foam regulator "PENTA®-483", packaged in a separate container unit in the amount of 0.05-0.15 May. % of the total number of components of the composition.
2. Набор по п. 1, характеризующийся тем, что катализирующая смесь дополнительно содержит добавку в виде 10% раствора М(бета-аминоэтил)гамма- аминопропилтриметоксисилана и гамма-аминопропилтриметоксисилана или N-(2- аминоэтил)-3-аминопропилтриметоксисилана в гексане или толуоле, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов. 2. The kit according to claim 1, characterized in that the catalyst mixture additionally contains an additive in the form of a 10% solution of M (beta-aminoethyl) gamma-aminopropyltrimethoxysilane and gamma-aminopropyltrimethoxysilane or N- (2-aminoethyl) -3-aminopropyltrimethoxysilane in hexane or toluene, taken in an amount of 0.1 May. % of the total number of mentioned starting components.
3. Набор по п. 2, характеризующийся тем, что упомянутая добавка в виде виде 10% раствора М(бета-аминоэтил)гамма-аминопропилтриметоксисилана и гамма- аминопропилтриметоксисилана или М-(2-аминоэтил)-3-аминопропилтриметоксисилана в гексане или толуоле использована в качестве внутреннего промоутера адгезии. 3. The kit according to claim 2, characterized in that the said additive in the form of a 10% solution of M(beta-aminoethyl)gamma-aminopropyltrimethoxysilane and gamma-aminopropyltrimethoxysilane or M-(2-aminoethyl)-3-aminopropyltrimethoxysilane in hexane or toluene is used as an internal adhesion promoter.
4. Набор по п. 1, характеризующийся тем, что катализирующая смесь содержит добавку в виде ускорителя полимеризации, взятого в количестве 0,05-0,15 мае. % от общего количества упомянутых исходных компонентов. 4. The kit according to claim 1, characterized in that the catalytic mixture contains an additive in the form of a polymerization accelerator, taken in an amount of 0.05-0.15 wt. % of the total number of mentioned starting components.
5. Набор по п. 4, характеризующийся тем, что ускоритель полимеризации представляет собой дибутилдиацетат олова или дибутилдилаурат олова. 5. The kit according to claim 4, characterized in that the polymerization accelerator is tin dibutyl diacetate or tin dibutyl dilaurate.
6. Набор по п. 1, характеризующийся тем, что катализирующая смесь содержит добавку в виде 10% раствора М(бета-аминоэтил)гамма-аминопропилтриметоксисилана и гамма-аминопропилтриметоксисилана или М-(2-аминоэтил)-3- аминопропилтриметоксисилана в гексане или толуоле, взятого в количестве 0,1 мае. % от общего количества упомянутых исходных компонентов; и содержит добавку в виде ускорителя полимеризации, взятого в количестве 0,05-0,15 мае. % от общего количества упомянутых исходных компонентов. 6. The set according to claim 1, characterized in that the catalyst mixture contains an additive in the form of a 10% solution of M (beta-aminoethyl) gamma-aminopropyltrimethoxysilane and gamma-aminopropyltrimethoxysilane or M- (2-aminoethyl) -3- aminopropyltrimethoxysilane in hexane or toluene taken in the amount of 0.1 May. % of the total number of mentioned starting components; and contains an additive in the form of a polymerization accelerator, taken in an amount of 0.05-0.15 May. % of the total number of mentioned starting components.
7. Набор по п. 6, характеризующийся тем, что упомянутая добавка в виде виде 10% раствора М(бета-аминоэтил)гамма-аминопропилтриметоксисилана и гамма- аминопропилтриметоксисилана или М-(2-аминоэтил)-3-аминопропилтриметоксисилана в гексане или толуоле использована в качестве внутреннего промоутера адгезии. 7. The kit according to claim 6, characterized in that the said additive in the form of a 10% solution of M(beta-aminoethyl)gamma-aminopropyltrimethoxysilane and gamma-aminopropyltrimethoxysilane or M-(2-aminoethyl)-3-aminopropyltrimethoxysilane in hexane or toluene is used as an internal adhesion promoter.
8. Набор по п. 6, характеризующийся тем, что ускоритель полимеризации представляет собой дибутилдиацетат олова или дибутилдилаурат олова. 8. The kit according to claim 6, characterized in that the polymerization accelerator is tin dibutyl diacetate or tin dibutyl dilaurate.
9. Огнезащитная вспучивающаяся композиция холодного отверждения для металлоконструкций и/или грунтовочных покрытий, полученная с использованием набора по любому из п.п. 1-8. 9. Fire retardant intumescent composition of cold curing for metal structures and/or primer coatings, obtained using a set according to any one of paragraphs. 1-8.
33
33