WO2022077014A1 - Coated fuel pellets with enhanced water and steam oxidation resistance - Google Patents
Coated fuel pellets with enhanced water and steam oxidation resistance Download PDFInfo
- Publication number
- WO2022077014A1 WO2022077014A1 PCT/US2021/071767 US2021071767W WO2022077014A1 WO 2022077014 A1 WO2022077014 A1 WO 2022077014A1 US 2021071767 W US2021071767 W US 2021071767W WO 2022077014 A1 WO2022077014 A1 WO 2022077014A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- uranium
- coating
- fissile
- method recited
- ceramic material
- Prior art date
Abstract
Description
Claims