WO2022041374A1 - Matériau de modification pour granulat de faible qualité et procédé de traitement - Google Patents

Matériau de modification pour granulat de faible qualité et procédé de traitement Download PDF

Info

Publication number
WO2022041374A1
WO2022041374A1 PCT/CN2020/117739 CN2020117739W WO2022041374A1 WO 2022041374 A1 WO2022041374 A1 WO 2022041374A1 CN 2020117739 W CN2020117739 W CN 2020117739W WO 2022041374 A1 WO2022041374 A1 WO 2022041374A1
Authority
WO
WIPO (PCT)
Prior art keywords
low
quality
aggregate
agent
modified material
Prior art date
Application number
PCT/CN2020/117739
Other languages
English (en)
Chinese (zh)
Inventor
王玲
王振地
姚燕
Original Assignee
中国建筑材料科学研究总院有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 中国建筑材料科学研究总院有限公司 filed Critical 中国建筑材料科学研究总院有限公司
Publication of WO2022041374A1 publication Critical patent/WO2022041374A1/fr

Abstract

La présente invention concerne le domaine technique des matériaux de construction et se rapporte en particulier à un matériau de modification pour un granulat de faible qualité et à un procédé de traitement correspondant. Le matériau de modification pour un granulat de faible qualité selon la présente invention comprend les composants suivants en pourcentage en masse : 46 à 50 % de ciment ; 10 à 15 % d'un mélange minéral ; 2 à 5 % d'une poudre active ; 0,2 à 0,6 % d'un agent réducteur d'eau ; 0,001 à 0,004 % d'un agent d'ajustement de la viscosité ; 0 à 3,2 % d'un agent d'expansion ; 0 à 0,12 % d'un agent entraîneur d'air ; et 0 à 0,0007 % d'un agent antimousse. Le matériau de modification selon la présente invention permet de parvenir à une modification efficace par bouchage des pores et enrobage d'un granulat de faible qualité au moyen des actions combinées des composants et de l'ajustement de leurs quantités et, en particulier, il permet d'ajuster efficacement la tension superficielle et la viscosité du matériau de modification et d'optimiser de manière coordonnée la quantité d'immersion dans les pores et l'épaisseur d'enrobage de coque au moyen des actions combinées du ciment, de la poudre active et de l'agent d'ajustement de la viscosité en quantités spécifiques. L'utilisation combinée des composants inorganiques et organiques permet de favoriser l'hydratation secondaire/la liaison chimique d'une couche de coulis et d'améliorer la résistance de l'interface entre le granulat et la couche de coulis. Après le traitement de modification, la résistance moyenne en compression sur cylindres du granulat est accrue de 40 % ou plus, la valeur de concassage est réduite de 30 % ou plus, et le taux d'absorption d'eau en 24 heures est réduit de 15 % ou plus.
PCT/CN2020/117739 2020-08-27 2020-09-25 Matériau de modification pour granulat de faible qualité et procédé de traitement WO2022041374A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
CN202010879703.1 2020-08-27
CN202010879703.1A CN111978056A (zh) 2020-08-27 2020-08-27 一种低品质骨料的改性材料及处理方法

Publications (1)

Publication Number Publication Date
WO2022041374A1 true WO2022041374A1 (fr) 2022-03-03

Family

ID=73440799

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/CN2020/117739 WO2022041374A1 (fr) 2020-08-27 2020-09-25 Matériau de modification pour granulat de faible qualité et procédé de traitement

Country Status (2)

Country Link
CN (1) CN111978056A (fr)
WO (1) WO2022041374A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN116375387A (zh) * 2023-02-22 2023-07-04 北京市高强混凝土有限责任公司 一种优质骨料及其制备方法
CN118164730A (zh) * 2024-01-31 2024-06-11 菏泽鹏远混凝土有限公司 一种砖瓦再生骨料轻质混凝土的制备方法

Families Citing this family (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN112500062B (zh) * 2020-12-26 2021-12-21 靖江市恒生混凝土制造有限公司 一种再生骨料配制的自密实混凝土及其制备方法
CN112811866A (zh) * 2021-01-15 2021-05-18 深圳市宝金华混凝土有限公司 一种再生骨料混凝土及其制备方法
CN113185169B (zh) * 2021-03-04 2022-06-21 中国地质大学（武汉） 一种基于偏高岭土浆体浸泡的再生骨料及其改性方法
CN113087427A (zh) * 2021-03-12 2021-07-09 中国地质大学（武汉） 一种基于偏高岭土浆体浸泡的再生骨料及其改性方法
CN113780734A (zh) * 2021-08-06 2021-12-10 中国建筑材料科学研究总院有限公司 一种珊瑚骨料改性处理中包覆材料用量的确定方法、改性方法
CN113845351B (zh) * 2021-10-28 2023-03-24 上海靓固生态环境科技股份有限公司 一种有色透水路面材料及其制备工艺
CN114380523A (zh) * 2021-12-27 2022-04-22 常熟市博海新型建材有限公司 一种应用于叠合板再生骨料的制备方法
CN115594446B (zh) * 2022-08-23 2024-04-26 中交特种工程有限公司 一种基于淤泥和废旧混凝土的绿色混凝土的制备方法
CN115477513B (zh) * 2022-09-14 2023-08-04 重庆中吉达环保科技有限公司 一种高强轻骨料混凝土及其制备方法
CN117720297B (zh) * 2023-12-29 2024-06-18 中铁河北投资开发建设有限公司 一种复合激发材料提高废旧混凝土再生粗集料质量的方法

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN110981255A (zh) * 2019-12-27 2020-04-10 中国矿业大学 一种多孔珊瑚骨料的增强方法
CN111217571A (zh) * 2020-02-25 2020-06-02 临沂人民公园 一种混凝土用陶粒的处理方法及以所述陶粒作为粗骨料的透水混凝土

Family Cites Families (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN102092993A (zh) * 2010-11-25 2011-06-15 浙江大学 一种再生骨料混凝土的纳米强化方法
KR101706116B1 (ko) * 2016-03-08 2017-02-14 장영수 친환경 황토 레미콘 조성물
CN106477929A (zh) * 2016-09-20 2017-03-08 上海市建筑科学研究院 一种强化再生骨料的制备方法及强化再生骨料混凝土
CN107117842A (zh) * 2017-05-05 2017-09-01 上海百理新材料科技股份有限公司 一种建筑用再生骨料配方及制备工艺
CN108383457B (zh) * 2018-04-28 2021-06-22 武汉源锦商品混凝土有限公司 一种高强度重矿渣透水混凝土及其制备方法
CN109704676B (zh) * 2019-01-19 2021-11-05 江苏盛达飞建筑材料有限公司 一种抗渗再生混凝土及其制备方法
CN110256025A (zh) * 2019-06-25 2019-09-20 绍兴上虞南方普银混凝土有限公司 一种再生混凝土骨料的制备工艺及应用其的再生混凝土

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN110981255A (zh) * 2019-12-27 2020-04-10 中国矿业大学 一种多孔珊瑚骨料的增强方法
CN111217571A (zh) * 2020-02-25 2020-06-02 临沂人民公园 一种混凝土用陶粒的处理方法及以所述陶粒作为粗骨料的透水混凝土

Non-Patent Citations (3)

* Cited by examiner, † Cited by third party
Title
CHENG, HAILI: "Experimental Study on Durability of Sodium Silicate on Recycled Concrete Aggregate", NEW BUILDING MATERIALS, no. 12, 1 January 2004 (2004-01-01), XP055909923 *
LI, GUOQIANG: "Application of Strengthened Recycled Concrete Aggregate", 1 January 2015 (2015-01-01), XP055909942, ISBN: 978-7-5608-5721-3, [retrieved on 20220406] *
YANG, FEIHUA: "Experimental Research on Concrete Strength and Frost Resistance of Modified Sodium Silicate Recycled Concrete Aggregate", JIANGXI BUILDING MATERIALS, vol. 12, no. 165, 1 January 2015 (2015-01-01), XP055909930 *

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN116375387A (zh) * 2023-02-22 2023-07-04 北京市高强混凝土有限责任公司 一种优质骨料及其制备方法
CN116375387B (zh) * 2023-02-22 2023-11-14 北京市高强混凝土有限责任公司 一种优质骨料及其制备方法
CN118164730A (zh) * 2024-01-31 2024-06-11 菏泽鹏远混凝土有限公司 一种砖瓦再生骨料轻质混凝土的制备方法

Also Published As

Publication number Publication date
CN111978056A (zh) 2020-11-24

Similar Documents

Publication Publication Date Title
WO2022041374A1 (fr) Matériau de modification pour granulat de faible qualité et procédé de traitement
CN111205036B (zh) 一种高强轻质混凝土及其制备方法
CN108569859B (zh) 一种具有自修复功能的防水抗渗混凝土添加剂及其制备方法
WO2021012867A1 (fr) Procédé de préparation de béton à base d'agrégat corallien à haute résistance dans des conditions de basse pression d'air
CN113461372B (zh) 一种轻集料混凝土及其制备方法
CN113387646B (zh) 一种轻质膨胀型超高性能混凝土及其制备方法
Tian et al. Damage and Degradation of Concrete under Coupling Action of Freeze‐Thaw Cycle and Sulfate Attack
CN113045285A (zh) 基于磷酸镁水泥基抗硫酸盐涂层快速修补材料及制备方法
CN111333392A (zh) 一种海水拌养珊瑚礁砂c120uhpc及其制备方法
CN115124298B (zh) 一种利用废弃石粉制备的高强再生骨料混凝土及其制备方法
CN116375425A (zh) 一种高耐侵蚀的海工混凝土及其制备方法
CN114772976B (zh) 一种防冻抗裂型混凝土防水剂及其制备方法
CN110590224A (zh) 一种渗透结晶防水剂及其在地下室结构混凝土中的应用
CN115636613A (zh) 一种提升混凝土抗碳化性能的外加剂及其应用
CN115340340A (zh) 一种生物基轻骨料混凝土及其制备方法
CN114735985A (zh) 一种抗裂高强型珊瑚砂浆及其制备方法
CN113896478A (zh) 一种超高强度混凝土及其制备方法
CN111548046A (zh) 一种提高抗氯离子渗透能力的混凝土矿物掺合料及混凝土
CN112479610A (zh) 一种低热耐腐蚀硅酸盐水泥及其制备方法
Xu et al. Effect of Mitigating Strength Retrogradation of Alkali Accelerator by the Synergism of Sodium Sulfate and Waste Glass Powder
CN114560667B (zh) 一种轻质节能泡沫混凝土及其制备方法
CN116143477B (zh) 一种高孔隙率骨料在混凝土中的应用
CN115521121B (zh) 一种耐腐蚀水泥砂浆及其制备方法
CN112830759B (zh) 一种适用于油井固井的孔隙疏水的氯氧镁水泥体系的制备方法
CN117342807B (zh) 一种低热水泥及其生产工艺

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 20951042

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase