WO2022015097A1 - 통신기기용 절연 세척제 조성물 - Google Patents
통신기기용 절연 세척제 조성물 Download PDFInfo
- Publication number
- WO2022015097A1 WO2022015097A1 PCT/KR2021/009165 KR2021009165W WO2022015097A1 WO 2022015097 A1 WO2022015097 A1 WO 2022015097A1 KR 2021009165 W KR2021009165 W KR 2021009165W WO 2022015097 A1 WO2022015097 A1 WO 2022015097A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- communication devices
- diglycerol
- insulating
- cleaning agent
- weight
- Prior art date
Abstract
본 발명은 통신기기용 절연 세척제 조성물에 관한 것으로, 그 구성은 인화점이 300℃ 이상인 디글리세롤 에스테르화물 70 내지 85 중량%, 1,1-디클로로에탄 10 내지 18 중량%, 1,1,1,2-테트라플루오에테인 3 내지 15 중량%가 혼합되어 이루어지는 것을 특징으로 하는 것으로서, 높은 인화점과 함께 우수한 절연특성을 갖는 디글리세롤 에스테르화물의 사용으로 인해 배전반환경에 적합할 뿐만 아니라, 다양한 전기 계통의 기기의 안전한 세척을 유도할 수 있어 세척제의 사용범용성을 강화할 수 있는 효과가 있다.
Description
본 발명은 통신기기용 절연 세척제 조성물에 관한 것으로, 더욱 상세하게는 높은 인화점과 함께 우수한 절연특성을 갖는 디글리세롤 에스테르화물의 사용으로 인해 배전반환경에 적합할 뿐만 아니라, 다양한 전기 계통의 기기의 안전한 세척을 유도할 수 있어 세척제의 사용범용성을 강화할 수 있는 통신기기용 절연 세척제 조성물에 관한 것이다.
종래의 무정전 통전기기용 절연세척제 조성물은 무기염류와 계면활성제를 혼합하여 제조되었으나, 한정된 세척 기능에 의해 사용범위가 극히 제한되어 왔으며, 반고형 오물세척용 세척제의 경우에 있어서는 대부분이 세척 능력을 갖는 성분에 마찰성 물질을 첨가하여 사용시 경도가 큰 마찰성 물질을 배합한 세척제는 그 사용 빈도가 높을 경우 피세척물의 표면이 마모되어 손상을 입게 되고 기계류의 경우에는 정확도를 상실하게 되는 문제점이 있었다.
한편, 통전기기용 장치 중 배전반이 가장 대표적인데, 배전반은 전기의 사용량이 많은 빌딩 또는 변전소 등의 옥내나 옥외에 설치되어 사용되는 장비로서 각종 스위치, 계기 및 릴레이(계전기) 등을 일정하게 배열하여 관리하는 전기 장치이다.
상기 배전반에는 고압 주회로의 차단기를 개폐하는 조작레버, 저압 주회로의 기중 개폐기, 전압계, 전류계, 전력계, 적산전력계, 전류계전기 등이 설치되고, 내부에는 고압의 전류가 흐른다.
한국특허등록 제10-1286798호에는 1,1-디클로로에탄(1,1-DICHLOROETHANE), 미네랄 스피릿 66/3(MINERALSPIRITS 66/3) 및 1,1,1,2-테트라플루오로에테인(1,1,1,2-TETRAFLUOROETHANE)을 각각 1:1:3의 중량비가 되도록 혼합하는 것을 특징으로 하는 통전기기 절연 세척제용 조성물이 기재되어 있는데, 상기의 조성물은 절연파괴전압은 우수하지만, 인화점이 낮아 전원을 차단하지 않은 무정전 상태에서 전기 배전반을 세척하는데 적합하지 못한 문제점이 있었다.
또한, 최근에는 기업체에서 생산라인이나 관리라인을 24시간 가동하여 효율성의 향상을 꾀하기 위해 절연성이 향상된 세척제를 이용하여 무정전 상태에서 세척과정이 진행되는 것을 선호하고, 상기의 선행기술은 최근에 기업체가 요구하는 부분을 만족시키지 못하는 문제점이 있다.
[선행기술문헌]
[특허문헌]
[문헌 0001] 대한민국 등록특허공보 제10-1286798호 (2013.07.10)
본 발명은 상기한 바와 같은 제반 문제점을 해결하기 위하여 제안된 것으로, 그 목적은 높은 인화점과 함께 우수한 절연특성을 갖는 디글리세롤 에스테르화물의 사용으로 인해 배전반환경에 적합할 뿐만 아니라, 다양한 전기 계통의 기기의 안전한 세척을 유도할 수 있어 세척제의 사용범용성을 강화할 수 있는 통신기기용 절연 세척제 조성물을 제공함에 있다.
또한, 식물성 혼합지방산을 기반을 기반으로 조성 제작되는 특성상, 세척제가 매우 친환경적이라는 장점이 있는 통신기기용 절연 세척제 조성물을 제공함에 있다.
본 발명에 따른 통신기기용 절연 세척제 조성물은 인화점이 300℃ 이상인 디글리세롤 에스테르화물 70 내지 85 중량%, 1,1-디클로로에탄 10 내지 18 중량%, 1,1,1,2-테트라플루오에테인 3 내지 15 중량%가 혼합되어 이루어지는 것을 특징으로 한다.
또한, 상기 디글리세롤 에스테르화물은 식물성 혼합지방산을 디글리세롤과 에스테르화 반응을 통해 형성되는 것을 특징으로 한다.
또한, 상기 식물성 혼합지방산은 카프릴산과 올레산이 1 : 0.3 내지 3의 몰비로 혼합된 것을 특징으로 한다.
본 발명에 따른 통신기기용 절연 세척제 조성물에 의하면, 높은 인화점과 함께 우수한 절연특성을 갖는 디글리세롤 에스테르화물의 사용으로 인해 배전반환경에 적합할 뿐만 아니라, 다양한 전기 계통의 기기의 안전한 세척을 유도할 수 있어 세척제의 사용범용성을 강화할 수 있는 효과가 있다.
또한, 식물성 혼합지방산을 기반을 기반으로 조성 제작되는 특성상, 세척제가 매우 친환경적이라는 장점이 있는 효과가 있다.
도 1은 실시예 1을 통해 제조된 통신기기용 절연 세척제 조성물에 대한 시험 데이터를 나타낸 도면.
본 발명은 통신기기용 절연 세척제 조성물에 있어서, 인화점이 300℃ 이상인 디글리세롤 에스테르화물 70 내지 85 중량%, 1,1-디클로로에탄 10 내지 18 중량%, 1,1,1,2-테트라플루오에테인 3 내지 15 중량%가 혼합되어 이루어지는 것을 특징으로 하는 통신기기용 절연 세척제 조성물에 관한 것이다.
본 발명의 바람직한 실시예에 따른 통신기기용 절연 세척제 조성물을 상세히 설명한다. 본 발명의 요지를 불필요하게 흐릴 수 있다고 판단되는 공지 기능 및 구성에 대한 상세한 기술은 생략한다.
본 발명의 실시예에 따른 통신기기용 절연 세척제 조성물은 인화점이 300℃ 이상인 디글리세롤 에스테르화물 70 내지 85 중량%, 1,1-디클로로에탄 10 내지 18 중량%, 1,1,1,2-테트라플루오에테인 3 내지 15 중량%가 혼합되어 이루어지도록 한다.
상기 디글리세롤 에스테르화물은 인화점이 300℃이 이상인 것이며, 상기 디글리세롤 에스테르화물은 식물성 지방산을 디글리세롤과 에스테르화 반응시켜 얻도록 한다.
여기서, 상기 식물성 지방산은 탄소수 7 내지 10인 직쇄 또는 분기의 지방산 및 탄소수 12 내지 20인 직쇄 또는 분기의 지방산을 포함하도록 하여 지방산의 에스테르화 반응시 사슬의 길이가 다른 지방산으로 인해 입체적인 구조를 가지게 하여 절연내력과 함께 인화점을 300℃ 이상으로 향상시켜 세척제의 우수한 사용 안전성이 확보되도록 한다.
본 발명의 일 실시예에서 디글리세롤 에스테르화물은 이중결합이 없고 8개의 탄소를 가지는 카프릴산(Caprylic acid, CA)와, 이중결합을 가지며 18개의 탄소를 가지는 올레산(Oleic acid, OA)을 황산화 금속산화물 촉매의 존재 하에서 디글리세롤과 반응시켜 합성하였다.
이때, 상기 카프릴산과 올레산이 1 : 0.3 내지 3의 몰비로 혼합될 수 있는데, 바람직하게는 지방산의 몰비가 카프릴산 : 올레산이 1 : 0.4일 때 인화점이 306℃로 가장 높게 나타남을 확인할 수 있었다.
본 발명의 통신기기용 절연 세척제 조성물에서 상기와 같은 디글리세롤 에스테르화물 함량이 70 중량% 미만이면 높은 인화점으로 인한 세척제의 세척 안정성에 대한 효과를 기대하기 곤란하고, 상기 디글리세롤 에스테르화물 함량이 85 중량%를 초과하면 상대적으로 상기 1,1-디클로로에탄과 1,1,1,2-테트라플루오에테인의 함량이 절감되어 세척제의 세척력이 저하될 수 있다.
따라서 본 발명의 통신기기용 절연 세척제 조성물에서는 디글리세롤 에스테르화물 함량이 70 내지 85 중량%가 첨가되도록 함이 바람직하다.
상기의 1,1-디클로로에탄은 본 발명에 따른 통신기기용 절연 세척제 조성물에 세정력을 향상시키고, 조성물을 제조하는 과정에서 압력을 낮춰주는 역할을 하기 때문에, 혼합 및 보관 용기를 두텁게 형성할 필요가 없기 때문에 제조비용을 절감시키는 역할도 한다.
상기의 1,1,1,2-테트라플루오로에테인은 본 발명에 따른 통신기기용 절연 세척제 조성물에 세척력을 부여하는 역할을 수행한다.
상기 조성 성분에 있어서, 첨가되는 1,1-디클로로에탄과 1,1,1,2-테트라플루오로에테인이 상기 한정치 미만으로 첨가되는 경우에는 세척력이 저하되는 반면, 초과하여 첨가되는 경우에는 상대적으로 상기 디글리세롤 에스테르화물의 첨가량이 절감되어 인화점 및 자연증발 성능이 저하될 수 있다.
따라서 본 발명의 통신기기용 절연 세척제 조성물에서는 1,1-디클로로에탄 10 내지 18 중량%, 1,1,1,2-테트라플루오에테인 3 내지 15 중량%가 첨가되도록 함이 바람직하다.
[실시예 1]
인화점이 300℃ 이상인 디글리세롤 에스테르화물 80 중량%, 1,1-디클로로에탄 12 중량%, 1,1,1,2-테트라플루오에테인 8 중량%가 혼합하고, 실온에서 교반기를 이용하여 5분 동안 교반하여 통신기기용 절연 세척제 조성물을 제조하였다.
상기 실시예 1를 통해 제조된 통신기기용 절연 세척제 조성물에 대한 시험 데이터는 도 1과 같다.
따라서 본 발명의 통신기기용 절연 세척제 조성물은 매우 우수한 인화점 및 절연파괴전압이 나타나는 것을 알 수 있다.
본 발명은 실시예를 참고로 설명되었으나 이는 예시적인 것으로 상술한 실시예에 한정되지 않으며, 당해 분야에서 통상의 지식을 가진 자라면 이로부터 다양한 변형 및 균등한 실시예가 가능하다는 점을 이해할 수 있을 것이다. 또위 내로 정해지는 것이 아니라 후술되는 청구범위와 이의 기술적 사상에 의해 한정될 것이다.
Claims (3)
- 통신기기용 절연 세척제 조성물에 있어서,인화점이 300℃ 이상인 디글리세롤 에스테르화물 70 내지 85 중량%, 1,1-디클로로에탄 10 내지 18 중량%, 1,1,1,2-테트라플루오에테인 3 내지 15 중량%가 혼합되어 이루어지는 것을 특징으로 하는 통신기기용 절연 세척제 조성물.
- 제 1 항에 있어서,상기 디글리세롤 에스테르화물은,식물성 혼합지방산을 디글리세롤과 에스테르화 반응을 통해 형성되는 것을 특징으로 하는 통신기기용 절연 세척제 조성물.
- 제 2 항에 있어서,상기 식물성 혼합지방산은 카프릴산과 올레산이 1 : 0.3 내지 3의 몰비로 혼합된 것을 특징으로 하는 통신기기용 절연 세척제 조성물.