WO2022013634A1

WO2022013634A1 - Rechargeable metal halide battery with intercalation anode

Info

Publication number: WO2022013634A1
Application number: PCT/IB2021/054363
Authority: WO
Inventors: Jangwoo Kim; Andy Theodora Tek
Original assignee: IBM China Investment Co Ltd; IBM Israel Science and Technology Ltd; International Business Machines Corp
Current assignee: IBM China Investment Co Ltd; IBM Israel Science and Technology Ltd; International Business Machines Corp
Priority date: 2020-07-13
Filing date: 2021-05-20
Publication date: 2022-01-20
Anticipated expiration: 2023-01-13
Also published as: US20220013778A1; CN116134641A; KR20230031887A; JP2023534217A; GB2612510B; DE112021003738T5; GB2612510A; US12288877B2; JP7706537B2; KR102944074B1

Abstract

A metal halide battery includes an intercalation anode, a cathode that includes a metal halide incorporated into an electrically conductive material, an oxidizing gas, and an electrolyte in contact with the intercalation anode, the cathode, and the oxidizing gas. The battery has a cycle life reaching 1000 cycles at a current density that enables the battery to charge within 10-15 minutes. Electrolytes that may be used in the metal halide batteries include (i) carbonate ester-based compounds with at least one ethyl group and an ion-conducting salt and/or (ii) at least one cyclic ester compound.

Description

RECHARGEABLE METAL HALIDE BATTERY WITH INTERCALATION ANODE TECHNICAL FIELD [0001] The present invention relates generally to rechargeable metal halide batteries and, more specifically, to a rechargeable metal halide battery with an intercalation anode, an oxidizing gas, and an electrolyte that includes (i) a carbonate ester-based compound with at least one ethyl group and an ion-conducting salt and/or (ii) at least one cyclic ester compound. BACKGROUND OF THE INVENTION [0002] Rechargeable batteries are in high demand for a wide range of applications, from small batteries for industrial and medical devices, to larger batteries for electric vehicles and grid energy storage systems. There are two types of rechargeable batteries currently in use: (i) batteries that run via electrochemical intercalation/de-intercalation behavior of acting ions and (ii) batteries that run via conversion reaction of active electrode/electrolyte materials. The most well-known and widely used rechargeable batteries are the lithium-ion batteries, which use an intercalated lithium compound as one electrode material and have the lithium ion move back and forth through a liquid electrolyte. Lithium-ion batteries suffer from shortcomings such as slow charging/discharging rates and the high cost of cathode materials that need to be overcome in order to meet the high standard of demand in the market. Cathode materials, such as lithium nickel manganese cobalt oxide (NMC), lithium nickel cobalt aluminum oxide (NCA), lithium cobalt oxide (LCO), and lithium iron phosphate (LFP), prohibit lithium-ion batteries from moving into a wider range of applications. Lithium metal has been widely considered as the preferred active anode material due to its high theoretical energy density; however, issues with lithium metal, such as dendrite growth, which result in the cell short circuiting, has prevented lithium-ion batteries from being widely commercialized. SUMMARY OF THE INVENTION [0003] The present invention overcomes the need in the art with a rechargeable metal halide battery comprising an intercalation anode, an oxidizing gas, and an electrolyte that may include (i) a carbonate ester-based compound with at least one ethyl group and an ion-conducting salt, and/or (ii) at least one cyclic ester compound. [0004] In one embodiment, the present invention relates to a battery comprising: an intercalation anode; a cathode comprising a metal halide incorporated into an electrically conductive material, an oxidizing gas, and an electrolyte in contact with the intercalation anode, the cathode, and the oxidizing gas. [0005] In another embodiment, the present invention relates to a battery, comprising: an intercalation anode; a cathode comprising a metal halide incorporated into an electrically conductive material, an oxidizing gas, and an electrolyte comprising (i) a carbonate ester-based compound with at least one ethyl group; and (ii) an ion-conducting salt comprising a metal cation [M]⁺ and an anion [X]- having a chemical formula of [M]⁺[X]-, wherein the electrolyte is in contact with the intercalation anode, the cathode, and the oxidizing gas. [0006] In a further embodiment, the present invention relates to a battery, comprising: an intercalation anode; a cathode comprising a metal halide incorporated into an electrically conductive material, an oxidizing gas, and an electrolyte comprising at least one cyclic ester compound, wherein the electrolyte is in contact with the intercalation anode, the cathode, and the oxidizing gas. [0007] In one aspect, the present invention relates to a method of forming a battery comprising: forming a battery stack comprising an intercalation anode, a metal halide cathode in an electrically conductive material, a separator positioned between the intercalation anode and the electrically conductive material of the metal halide cathode, and an electrolyte comprising (i) a carbonate ester- based compound with at least one ethyl group and (ii) an ion-conducting salt comprising a metal cation [M]⁺ and an anion [X]- having a chemical formula of [M]⁺[X]-, wherein an oxidizing gas is introduced into the battery stack and the electrolyte is in contact with the intercalation anode, the metal halide cathode, and the oxidizing gas. [0008] In another aspect, the present invention relates to a method of forming a battery comprising: forming a battery stack comprising an intercalation anode, a metal halide cathode in an electrically conductive material, a separator positioned between the intercalation anode and the electrically conductive material of the metal halide cathode, and an electrolyte comprising at least one cyclic ester compound, wherein an oxidizing gas is introduced into the battery stack and the electrolyte is in contact with the intercalation anode, the metal halide cathode, and the oxidizing gas. [0009] In other embodiments and aspects, the carbonate ester-based compound includes at least two ethyl groups. [0010] In further embodiments and aspects, the carbonate ester-based compound is selected from the group consisting of ethylene carbonate (EC), vinylene carbonate (VC), propylene carbonate (PC), diethyl carbonate (DEC), dipropyl carbonate (DPC), dibutyl carbonate (DBC), dimethyl carbonate (DMC), ethyl methyl carbonate (EMC), ethyl propyl carbonate (EPC), ethyl butyl carbonate (EBC), ethyl salicylate carbonate (ESC), fluoroethylene carbonate (FEC), allyl methyl carbonate (AMC), dodecyl ethyl carbonate (DDEC), diethyl decarbonate (DEDC), and combinations thereof. [0011] In other embodiments and aspects, the metal cation [M]⁺ is selected from the group consisting of Li⁺, Mg²⁺, Zn²⁺, Al³⁺, Na⁺, and combinations thereof. [0012] In further embodiments and aspects, the anion [X]- is selected from the group consisting of nitrate (NO₃-), hexafluorophosphate (PF₆-), tetrafluoroborate (BF₄-), bisoxalato borate (BOB-), difluorooxalato borate (DFOB-), trifluoromethanesulfonate (TF-), trifluoromethanesulfonylimide (TFSI-), fluorosulfonylimide (FSI-), and combinations thereof. [0013] In other embodiments and aspects, the at least one cyclic ester compound is an additive to the carbonate ester-based electrolyte. [0014] In further embodiments and aspects, the at least one cyclic ester compound has a weight percent concentration in the electrolyte between 5% and 20%. [0015] In other embodiments and aspects, the at least one cyclic ester compound is selected from the group consisting of beta-propiolactone (BPL), beta-butyrolactone (BBL), alpha-methyl- gamma-butyrolactone (AMGBL), gamma-butyrolactone (GBL), gamma-valerolactone (GVL), delta- valerolactone (DVL), gamma-caprolactone (GCL), epsilon-caprolactone (ECL), gamma- octanolactone (GOL), gamma-nanolactone (GNL), gamma-decanolactone (GDL), delta- decanolactone (DDL), gamma-undecanolactone (GUL), delta-undecanolactone (DUL), delta- dodecanolactone (DDDL), and combinations thereof. [0016] In further embodiments and aspects, the at least one cyclic ester compound is gamma-butyrolactone (GBL) and/or epsilon-caprolactone (ECL). [0017] In other embodiments and aspects, the intercalation anode is selected from the group consisting of graphite, graphene, reduced graphene oxide (RGO), silicon, silicon alloys, silicon- carbon composites, carbon nanotubes, fullerenes, titanium dioxide (TiO2), titanium disulfide (TiS2), molybdenum dioxide (MoO2), molybdenum trioxide (MoO3), molybdenum disulfide (MoS2), and combinations thereof. [0018] In further embodiments and aspects, the intercalation anode comprises graphite. [0019] In other embodiments and aspects, the metal halide of the cathode comprises (i) a metal ion selected from the group consisting of Li⁺, Mg⁺, Zn⁺, Al⁺, Na⁺, and combinations thereof; and (ii) a halide ion selected from the group consisting of I-, Br-, Cl-, F-, and combinations thereof. [0020] In further embodiments and aspects, the cathode is a conversion cathode selected from the group consisting of: lithium iodide (LiI), lithium chloride (LiCl), lithium bromide (LiBr), lithium fluoride (LiF), sodium chloride (NaCl), sodium iodide (NaI2), nickel chloride(NiCl2), zinc bromide (ZnBr2), zinc chloride (ZnCl2), and combinations thereof. [0021] In other embodiments and aspects, the electrically conductive material is selected from the group consisting of carbon black, carbon paper, carbon foam, carbon fibers, carbon nanofibers, carbon nanotubes, activated carbon, amorphous carbon, graphite sheets, graphene, reduced graphene oxide, and combinations thereof. [0022] In further embodiments and aspects, the oxidizing gas is selected from the group consisting of oxygen, air, nitric oxide, nitrogen dioxide, and combinations thereof. [0023] Additional embodiments and/or aspects of the invention will be provided, without limitation, in the detailed description of the invention that is set forth below. BRIEF DESCRIPTION OF THE DRAWINGS [0024] FIG.1 is a performance profile graph for the first cycle of a rechargeable metal halide battery cell with a graphite anode, a lithium iodide (LiI) cathode, and an electrolyte solution of 1M lithium hexafluorophosphate (LiPF6) dissolved in ethylene carbonate diethyl carbonate (EC-DEC) (1:1 vol. %) operated under oxygen at a current density of 1 mA/cm² (Example 1). [0025] FIG.2 is a performance profile graph for the first cycle of a rechargeable metal halide battery cell with a graphite anode, an LiI cathode, and 1M LiPF6 dissolved in EC-DEC electrolyte (1:1 vol. %) operated without oxygen under argon at a current density of 1 mA/cm² (Comparative Example 1). [0026] FIG.3 is a performance profile graph for the first cycle of a rechargeable metal halide battery cell with a graphite anode, a LiI cathode, and an electrolyte solution of 1M LiPF6 dissolved in ethylene carbonate dipropyl carbonate (EC-DPC) (1:1 vol. %) operated under oxygen at a current density of 1 mA/cm² (Example 2). [0027] FIG.4 is a performance profile graph for the first cycle of a rechargeable metal halide battery cell with a graphite anode, a LiI cathode, and an electrolyte solution of 1M LiPF6 dissolved in ethylene carbonate ethyl methyl carbonate (EC-EMC) (1:1 vol. %) operated under oxygen at a current density of 1 mA/cm² (Example 3). [0028] FIG.5 is a performance profile graph for the first cycle of a rechargeable metal halide battery cell with a graphite anode, a LiI cathode, and an electrolyte solution of 1M LiPF6 dissolved in ethylene carbonate dimethyl carbonate (EC-DMC) (1:1 vol. %) operated without oxygen under argon at a current density of 1 mA/cm² (Comparative Example 2). [0029] FIG.6 is a performance profile graph for the first cycle (solid line) and the fifth cycle (dotted line) of a rechargeable metal halide battery cell with a graphite anode, a LiI cathode, and an electrolyte solution of 3-methoxypropionitrile (MPN) operated under oxygen at a current density of 1 mA/cm² (Comparative Example 3). [0030] FIG.7 is a performance profile graph for the first cycle of a rechargeable metal halide battery cell with a graphite anode, a LiI cathode, and an electrolyte solution of 1M LiPF6 dissolved in EC-DEC (1:1 vol. %) operated under oxygen at a current density of 5 mA/cm² (Example 4). [0031] FIG.8 is a performance profile graph for the first cycle of a rechargeable metal halide battery cell with a graphite anode, a LiI cathode, and an electrolyte solution of 1M LiPF6 and a gamma-butyrolactone (GBL) additive (10 wt.%) dissolved in EC-DEC (1:1 vol. %) operated under oxygen at a current density of 5 mA/cm² (Example 5). [0032] FIG.9 is a performance profile graph for the first cycle of a rechargeable metal halide battery cell with a graphite anode, a LiI cathode, and an electrolyte solution of 1M LiPF6 and an epsilon-caprolactone (ECL) additive (10 wt.%) dissolved in EC-DEC (1:1 vol. %) operated under oxygen at a current density of 5 mA/cm² (Example 6). [0033] FIG.10 is a cycle life graph for a rechargeable metal halide battery cell with a graphite anode, a LiI cathode, and an electrolyte solution comprising 1M LiPF6 dissolved in EC-DEC electrolyte (1:1 vol. %) without any additive and also with the additive GBL (10 wt.%) and separately ECL (10 wt.%) operated under oxygen at a current density of 5 mA/cm² (Example 7). [0034] FIG.11 is a cycle life graph for a rechargeable metal halide battery cell with a graphite anode, a LiI cathode, and an electrolyte solution comprising 1M LiPF6 dissolved in EC-DEC electrolyte (1:1 vol. %) with different GBL weight fractions operated under oxygen at a current density of 5 mA/cm² (Example 8). [0035] FIG.12 is a cycle life graph for a rechargeable metal halide battery cell with a graphite anode, a LiI cathode, and an electrolyte solution comprising 1M LiPF6 dissolved in EC-DEC electrolyte (1:1 vol. %) with different ECL weight fractions operated under oxygen at a current density of 5 mA/cm² (Example 9). DETAILED DESCRIPTION OF THE INVENTION [0036] Set forth below is a description of what are currently believed to be preferred aspects and/or embodiments of the claimed invention. Any alternates or modifications in function, purpose, or structure are intended to be covered by the appended claims. As used in this specification and the appended claims, the singular forms “a,” “an,” and “the” include plural referents unless the context clearly dictates otherwise. The terms “comprise,” “comprised,” “comprises,” and/or “comprising,” as used in the specification and appended claims, specify the presence of the expressly recited components, elements, features, and/or steps, but do not preclude the presence or addition of one or more other components, elements, features, and/or steps. [0037] As used herein, the term “metal halide” refers to a compound having a metal and a halogen. The metals of metal halides may be any metal in Groups 1 to 16 of the periodic chart but will typically be Group 1 alkali metals. The halides of the metal halides will be any halogen in Group 17 of the periodic chart. [0038] As used herein, the term “cathode” refers to the positive electrode of a battery cell that receives electrons from an external circuit and is reduced during discharging, and transfers them to an external circuit through oxidation during charging. In a metal halide battery, the cathode material comprises a metal halide as defined above. Cathode materials appropriate for the rechargeable metal halide batteries may also be conversion-type cathode materials, which are electrode materials that undergo a conversion reaction according to Formula (1) or Formula (2):

where Y is an alkali earth metal (1) or an alkaline earth metal (2) and Z is a halogen, such as F, Cl, Br, and I. In the charging reaction of Formulas (1) and (2) (the forward reaction →), the conversion- type cathode materials having the chemical formulas YZ or YZ₂ release electrons to an external circuit to form Z2. The excess metal ions, Y⁺ or Y²⁺, are released from the cathode, move toward the anode, and are reduced on the anode surface by receiving the electrons transferred through the external circuit during the charging process. In the discharging reaction of Formulas (1) and (2) (the reverse reaction ←), Z2 receives electrons formed during the anode oxidation and transfers the electrons through an external circuit, forming Z-. The reduced species, Z-, ionically binds with Y⁺ or Y²⁺, which are diffused from the anode to the cathode to form the conversion-type cathode materials, YZ or YZ2. [0039] Unlike lithium-ion and nickel metal hydride (NiMH) batteries, metal halide batteries do not require heavy metal cathode materials (such as cobalt or nickel, respectively); thus, rechargeable metal halide batteries have potentially lower manufacturing costs than traditional lithium-ion or NiMH batteries. Further, because the rechargeable metal halide batteries do not require a lithium metal, the batteries also have a reduced risk of fire and are thus safer to run than rechargeable batteries used in the art that require lithium metal for operation. [0040] As used herein, the term “anode” refers to the negative electrode of a battery cell that transfers electrons to an external circuit through oxidation during discharging, and receives them from an external circuit and is reduced during charging. Anode materials appropriate for the rechargeable metal halide batteries may be intercalation-type anode materials, which have a reaction mechanism between the metal ions of a metal halide cathode material (including the lithium of conversion-type cathode materials) and the anode material in an intercalation/de-intercalation process, wherein the metal ions are inserted into (during charging), and subsequently released from (during discharging), stable sites within or on the surface of the anode material. Exemplary intercalation-type anode materials will typically be lattice-type structures. Materials that may form such lattice-type structures include carbon allotropes, silicon compounds, titanium compounds, and molybdenum compounds. [0041] As used herein, the term “electrolyte” refers to a material that provides for ion transport between the anode and cathode of a battery cell. An electrolyte acts as a conduit for ion transport through its interaction with the anode and the cathode. Upon battery charging, an electrolyte facilitates the movement of ions from the cathode to the anode, whereas upon discharge, the electrolyte facilitates the movement of ions from the anode to the cathode. In rechargeable batteries, the electrolyte promotes ion cycling between the anode and the cathode. [0042] As used herein, the term “oxidizing gas” refers to a gas that induces a reduction- oxidation (redox) reaction in a battery cell. Examples of oxidizing gases include, without limitation, oxygen, air, nitric oxide, nitrogen dioxide, and combinations thereof. As is known to those of skill in the art, a redox reaction is a reaction that transfers electrons between (i) a reducing agent that undergoes oxidation through the loss of electrons and (ii) an oxidizing agent that undergoes reduction through the gain of electrons. Within the context of the present invention, the oxidizing gas works in concert with the electrolyte to form a stable SEI (solid-electrolyte interphase) layer on the surface of electrodes of a rechargeable metal halide battery, and promote the redox reaction of active cathode materials. [0043] The rechargeable metal halide batteries described herein comprise an anode, a metal halide cathode, an oxidizing gas, and an electrolyte in contact with the anode, the cathode, and the oxidizing gas. The batteries are high powered, fast-charging, and electrically stable. The combination of battery components is capable of prolonging the cycle life of a metal halide battery by up to 1000 cycles at a current density that enables the battery to charge within 10-15 minutes (e.g., FIGS.10-12, Examples 7-9). [0044] In one embodiment, the metal halide cathode of the rechargeable metal halide battery may comprise (i) a metal ion selected from the group consisting of Li⁺, Mg²⁺, Zn²⁺, Al³⁺, Na⁺, and combinations thereof; and (ii) a halogen ion selected from the group consisting of I-, Br-, Cl-, F-, and combinations thereof. Where the metal halide cathode is a conversion cathode, the conversion cathode material may include, without limitation, lithium iodide (LiI), lithium chloride (LiCl), lithium bromide (LiBr), lithium fluoride (LiF), sodium chloride (NaCl), sodium iodide (NaI2), nickel chloride(NiCl2), zinc bromide (ZnBr2), zinc chloride (ZnCl2), and combinations thereof. [0045] In another embodiment, the anode of the rechargeable metal halide battery is an intercalation anode. Intercalation anode materials that may be used in the rechargeable metal halide battery include, without limitation, graphite, graphene, reduced graphene oxide (RGO), silicon, silicon alloys, silicon-carbon composites, carbon nanotubes, fullerenes, titanium dioxide (TiO2), titanium disulfide (TiS2), molybdenum dioxide (MoO2), molybdenum trioxide (MoO3), molybdenum disulfide (MoS₂), and combinations thereof. [0046] In a further embodiment, the metal halide cathode may be incorporated into an electrically conductive material, such as a carbon current collector and/or porous carbon. Examples of electrically conductive materials that may be used to incorporate the cathode material include, without limitation, carbon black, carbon paper, carbon foam, carbon fibers, carbon nanofibers, carbon nanotubes, activated carbon, amorphous carbon, graphite sheets, graphene, reduced graphene oxide, and combinations thereof. Depending on the electrically conductive material used, the metal halide may be interspersed within the electrically conductive material or adsorbed onto the electrically conductive material. Where the electrically conductive material is a porous material, the metal halide may be incorporated into a plurality of pores of the porous material. [0047] In another embodiment, the electrolyte for the rechargeable metal halide battery comprises a carbonate ester-based compound with at least one ethyl group. In a further embodiment, the electrolyte comprises a carbonate ester-based compound with at least two ethyl groups. Examples of such carbonate ester-based compounds that may be used for the battery electrolyte include, without limitation, ethylene carbonate (EC), vinylene carbonate (VC), propylene carbonate (PC), diethyl carbonate (DEC), dipropyl carbonate (DPC), dibutyl carbonate (DBC), dimethyl carbonate (DMC), ethyl methyl carbonate (EMC), ethyl propyl carbonate (EPC), ethyl butyl carbonate (EBC), ethyl salicylate carbonate (ESC), fluoroethylene carbonate (FEC), allyl methyl carbonate (AMC), dodecyl ethyl carbonate (DDEC), diethyl decarbonate (DEDC), and combinations thereof. [0048] In another embodiment, the electrolyte comprises an ion-conducting salt comprising a metal cation [M]⁺ and an anion [X]- having a chemical formula of [M]⁺[X]-. Examples of metal cations that may comprise the ion-conducting salt of the electrolyte solution include, without limitation, Li⁺, Mg²⁺, Zn²⁺, Al³⁺, Na⁺, and combinations thereof. Examples of anions that may comprise the ion-conducting salt include, without limitation, nitrate (NO3-), hexafluorophosphate (PF6-), tetrafluoroborate (BF4-), bisoxalato borate (BOB-), difluorooxalato borate (DFOB-), trifluoromethanesulfonate (TF-), trifluoromethanesulfonylimide (TFSI-), fluorosulfonylimide (FSI-), and combinations thereof. [0049] In a further embodiment, the electrolyte comprises at least one cyclic ester and/or lactone (cyclic carboxylic ester). The at least one cyclic ester and/or lactone is collectively referred to herein as “cyclic ester(s).” The cyclic ester may be used as an additive to the carbonate ester- based electrolyte. Examples of such cyclic esters include, without limitation, beta-propiolactone (BPL), beta-butyrolactone (BBL), alpha-methyl-gamma-butyrolactone (AMGBL), gamma- butyrolactone (GBL), gamma-valerolactone (GVL), delta-valerolactone (DVL), gamma-caprolactone (GCL), epsilon-caprolactone (ECL), gamma-octanolactone (GOL), gamma-nanolactone (GNL), gamma-decanolactone (GDL), delta-decanolactone (DDL), gamma-undecanolactone (GUL), delta- undecanolactone (DUL), delta-dodecanolactone (DDDL), and combinations thereof. [0050] Rechargeable metal halide batteries manufactured with the components described herein may further include a separator between the anode and the cathode. In one embodiment, a battery stack is formed by placing a separator between the intercalation anode and the metal halide cathode. In a further embodiment, the battery stack is formed by placing the separator between the intercalation anode and the electrically conductive material, the latter of which incorporates the metal halide cathode. In another embodiment, an electrolyte solution as described herein is used to soak the separator prior to incorporation into the battery stack. In a further embodiment, the electrolyte solution is introduced into the battery stack either during or after formation of the stack. In another embodiment, an oxidizing gas is introduced into the battery stack. In operation, the metal halide battery is charged after introduction of the oxidizing gas to the battery stack. To return the battery to an idle state, the oxidizing gas may be removed by purging the battery with an inert gas. Examples of inert gases include, without limitation, argon (Ar), nitrogen (N), helium (He), neon (Ne), xenon (Xe), krypton (Kr), and combinations thereof. [0051] The following discussion provides data derived from batteries operated with a graphite anode, a lithium iodide (LiI) cathode, electrolyte solutions comprising 1M lithium hexafluorophosphate (LiPF6) as an ion-conducting salt dissolved in various different carbonate ester solutions (with and without cyclic ester additives), and oxygen as an oxidizing gas. It is to be understood that the graphite anode, the LiI cathode, the electrolyte solutions, and the oxygen are used as exemplary materials and are not meant to be limiting to the various different battery combinations as disclosed herein. [0052] FIG.1 is a cycle performance graph showing the first charge/discharge cycle of a rechargeable metal halide battery comprising graphite as an anode material, LiI as an active cathode material, an electrolyte solution of 1M LiPF6 dissolved in an organic solution of EC-DEC (1:1 vol.%), and oxygen as a catalyst (Example 1), run at a current density of 1 mA/cm². FIG.7 shows the same battery from FIG.1, but run at a current density of 5 mA/cm² (Example 4). In FIG.1, the first cycle voltaic and coulombic efficiencies are both in excess of 95%, and the first cycle specific capacity for the battery is greater than 100 mAh/g, normalized by the amount of lithium iodide. FIG.7 shows similar first cycle results as FIG.1, with voltaic and coulombic efficiency both in excess of 85% and the specific capacity of the battery also greater than 100 mAh/g, normalized by the amount of lithium iodide. [0053] FIG.2 is a cycle performance graph showing the first charge/discharge cycle of a rechargeable metal halide battery comprising graphite as an anode material, LiI as an active cathode material, and an electrolyte solution of 1M LiPF6 dissolved in EC-DEC (1:1 vol.%), run at a current density of 1 mA/cm², without oxygen as a catalyst (Comparative Example 1). The first cycle results of FIG.2 show voltaic efficiency below 70%, coulombic efficiency below 10%, and specific capacity less than 10 mAh/g, normalized by the amount of lithium iodide. The omission of oxygen from the battery of FIG.1 results in significantly reduced battery rechargeability and life span. [0054] FIG.3 is a cycle performance graph showing the first charge/discharge cycle of a rechargeable metal halide battery comprising graphite as an anode material, LiI as an active cathode material, an electrolyte solution of 1M LiPF6 dissolved in EC-DPC (1:1 vol.%), and oxygen as a catalyst, run at a current density of 1 mA/cm² (Example 2). The first cycle results of FIG.3 show voltaic efficiency and coulombic efficiency both in excess of 95% and specific capacity greater than 125 mAh/g, normalized by the amount of lithium iodide. [0055] FIG.4 is a cycle performance graph showing the first charge/discharge cycle of a rechargeable metal halide battery comprising graphite as an anode material, LiI as an active cathode material, an electrolyte solution of 1M LiPF₆ dissolved in EC-EMC (1:1 vol.%), and oxygen as a catalyst, run at a current density of 1 mA/cm² (Example 3). The first cycle results of FIG.4 show voltaic efficiency was in excess of 80%, coulombic efficiency was excess of 60%, and specific capacity greater than 100 mAh/g, normalized by the amount of lithium iodide. [0056] FIG.5 is a cycle performance graph showing the first charge/discharge cycle of a rechargeable metal halide battery comprising graphite as an anode material, LiI as an active cathode material, and an electrolyte solution of 1M LiPF6 dissolved in EC-DMC (1:1 vol.%), run at a current density of 1 mA/cm², without oxygen as a catalyst (Comparative Example 2). The first cycle results of FIG.5 show voltaic efficiency was below 70%, coulombic efficiency was below 60%, and specific capacity was less than 100 mAh/g, normalized by the amount of lithium iodide. The omission of oxygen again results in a battery with a reduced battery rechargeability and life span. [0057] FIG.6 is a cycle performance graph showing the first and fifth charge/discharge cycles of a rechargeable metal halide battery comprising graphite as an anode material, LiI as an active cathode material, 3-methoxypropionitrile (MPN) as an electrolyte solution, and oxygen as a catalyst, run at a current density of 1 mA/cm² (Comparative Example 3). The MPN represents an electrolyte solution that does not contain a carbonate ester with at least one ethyl group. The first cycle results of FIG.6 show voltaic and coulombic efficiency both below 80% and specific capacity greater than 100 mAh/g, normalized by the amount of lithium iodide. At the fifth cycle, the specific capacity was reduced to less than 80 mAh/g, representing less than 80% of the battery’s original capacity. The results of FIG. 6 demonstrate that the carbonate ester electrolytes run under oxygen as described herein have superior rechargeability and efficiency in comparison to a nitrile ester electrolyte, such as MPN [0058] FIG.8 is a cycle performance graph showing the first charge/discharge cycle for a rechargeable metal halide battery comprising graphite as an anode material, LiI as an active cathode material, an electrolyte solution of 1M LiPF₆ plus the electrolyte additive GBL (10 wt.%) dissolved in EC-DEC (1:1 vol. %), and oxygen as a catalyst, run at a current density of 5 mA/cm² (Example 5). The first cycle results of FIG.8 show voltaic and coulombic efficiency both in excess of 85%, and specific capacity greater than 100 mAh/g, normalized by the amount of lithium iodide. [0059] FIG.9 is a cycle performance graph showing the first charge/discharge cycle for a rechargeable metal halide battery comprising graphite as an anode material, LiI as an active cathode material, an electrolyte solution of 1M LiPF6 plus the electrolyte additive ECL (10 wt.%) dissolved in EC-DEC (1:1 vol. %), and oxygen as a catalyst, run at a current density of 5 mA/cm² (Example 6). The first cycle results of FIG.9 show voltaic and coulombic efficiency both in excess of 80%, and specific capacity greater than 100 mAh/g, normalized by the amount of lithium iodide. [0060] FIG.10 is a cycle life graph that compares different electrolyte solutions in rechargeable metal halide battery cells comprising graphite as an anode material and LiI as an active cathode material, with the batteries operated under oxygen at a current density of 5 mA/cm². The electrolyte solutions subject to comparison are (1) 1M LiPF6 EC-DEC (1:1 vol. %) (without an additive); (2) 1M LiPF6 EC-DEC (1:1 vol. %) with GBL additive (10 wt.%); and (3) 1M LiPF6 EC-DEC (1:1 vol. %) with ECL additive (10 wt.%) (Example 7). As shown in FIG.10, the battery cells with the GBL and ECL electrolyte additives demonstrate prolonged life cycle (> 500) in comparison to the battery without an electrolyte additive. The battery with the GBL additives achieves near 1000 cycles at 80% of its initial capacity and maintains above 100 mAh/g of discharge capacity at the 1000^th cycle. [0061] FIG.11 is a cycle life graph that compares different weight percentages of the electrolyte additive GBL in rechargeable metal halide battery cells comprising graphite as an anode material and LiI as an active cathode material, the batteries being operated under oxygen at a current density 5 mA/cm². The electrolyte solution is 1 M LiPF6 dissolved in EC-DEC (1:1 vol.%) with GBL added to the electrolyte solution in the following weight percentages: 0%, 10%, 20%, 30%, 50%, and 100% (Example 8). As shown in FIG.11, the electrolyte solution with 10 wt% of GBL shows the longest cycle life of 912 charge/discharge cycles at 80% of its best cycle capacity and above 1000 at 80% of its first cycle capacity (c.f., FIG.10). The battery cells with greater than 10 wt% of GBL in the electrolyte solution show decreases in cycle life. At 100 wt% of GBL, the battery runs less than 20 charge/discharge cycles. [0062] FIG.12 is a cycle life graph that compares different weight percentages of the electrolyte additive ECL in rechargeable metal halide battery cells comprising graphite as an anode material and LiI as an active cathode material, with the batteries operated under oxygen at a current density 5 mA/cm². The electrolyte solution is 1 M LiPF6 dissolved in EC-DEC (1:1 vol.%) with ECL added to the electrolyte solution in the following weight percentages: 0%, 10%, 20%, 30%, 50%, and 100% (Example 9). As shown in FIG.12, the electrolyte solution with 10 wt% of ECL shows the longest cycle life of 689 charge/discharge cycles at 80% of its best cycle capacity and above 900 at 80% of its first cycle capacity (c.f., FIG.10). The battery cells with greater than 10 wt% of ECL in the electrolyte solution shows decreases in cycle life. At 100 wt% of ECL, the battery runs less than 10 charge/discharge cycles. [0063] The figures and Examples provided herein show that the combination of an intercalation anode (such as graphite), a metal halide cathode, a carbonate ester-based electrolyte, at least one cyclic ester additive, and an oxidizing gas is able to improve the life cycle of a rechargeable battery by more than 900%, achieving near 100 cycles at 80% of the original capacity (e.g., FIGS.10-12, Examples 7-9). [0064] The descriptions of the various aspects and/or embodiments of the present invention have been presented for purposes of illustration, but are not intended to be exhaustive or limited to the embodiments disclosed. Many modifications and variations will be apparent to those of ordinary skill in the art without departing from the scope of the described embodiments. The terminology used herein was chosen to best explain the principles of the aspects and/or embodiments, the practical application or technical improvement over technologies found in the marketplace, or to enable others of ordinary skill in the art to understand the aspects and/or embodiments disclosed herein. EXPERIMENTAL [0065] The following examples are set forth to provide those of ordinary skill in the art with a complete disclosure of how to make and use the aspects and/or embodiments of the invention as set forth herein. While efforts have been made to ensure accuracy with respect to variables such as amounts, temperature, etc., experimental error and deviations should be taken into account. Unless indicated otherwise, parts are parts by weight, temperature is degrees centigrade, and pressure is at or near atmospheric. All components were obtained commercially unless otherwise indicated. [0066] The same materials and cell fabrication techniques were used for each of the Examples. The following materials were purchased from Sigma Aldrich (St. Louis, MO, USA): 1M lithium hexafluorophosphate (LiPF6), ethylene carbonate (EC) diethyl carbonate (DEC) (1:1 vol.%) electrolyte solution; gamma-butyrolactone (GBL); epsilon-caprolactone (ECL); and lithium iodide (LiI). The foregoing materials were dried and stored in an argon filled glovebox (< 0.1 ppm H2O, O2). The LiI cathode was prepared by incorporating LiI onto a carbon cloth current collector with a mass loading of 3 oz/yd² (102 g/m²) (ZOLTEK® PX30, Zoltek Corporation, St. Louis, MO, USA). GBL or ECL were used as electrolyte additives and evaluated at different weight ratios in the presence of an oxidizing gas. A CELGARD® (Celgard, LLC, Charlotte, NC, USA) separator was placed in between the graphite anode and the LiI cathode. The electrolyte solution was used to wet the separator. All cell assembly was done in the argon filled glovebox. All cell components were placed in a cell equipped with inlet and outlet SWAGELOK® (Swagelok Company, Solon, OH, USA) tubing for oxygen flow. After oxygen was introduced from the inlet tubing outside of the argon filled glovebox, the cell was completely sealed by closing the valves of both the inlet and the outlet tubing. EXAMPLE 1 RECHARGEABLE LITHIUM IODIDE GRAPHITE CELL PERFORMANCE 1M LIPF6 EC-DEC ELECTROLYTE (1:1 vol.%) UNDER OXYGEN (at 1 mA/cm²) [0067] A rechargeable lithium iodide battery with a graphite anode, 1M LiPF₆ as an active cathode material, and an electrolyte solution of EC-DEC (1:1 vol. %) was operated under oxygen at a current density of 1 mA/cm². FIG.1 shows the voltaic efficiency, coulombic efficiency, and specific capacity (normalized by the amount of lithium iodide) at the first charge/discharge cycle. COMPARATIVE EXAMPLE 1 RECHARGEABLE LITHIUM IODIDE GRAPHITE CELL PERFORMANCE 1M LIPF6 EC-DEC ELECTROLYTE (1:1 vol.%) UNDER ARGON (at 1 mA/cm²) [0068] A rechargeable lithium iodide battery with a graphite anode, 1M LiPF₆ as an active cathode material, and an electrolyte solution of 1M LiPF6 EC-DEC (1:1 vol. %) was operated under argon at a current density of 1 mA/cm². FIG.2 shows the voltaic efficiency, coulombic efficiency, and specific capacity (normalized by the amount of lithium iodide) at the first charge/discharge cycle. EXAMPLE 2 RECHARGEABLE LITHIUM IODIDE GRAPHITE CELL PERFORMANCE 1M LIPF6 EC-DPC ELECTROLYTE (1:1 VOL.%) UNDER OXYGEN (at 1 mA/cm²) [0069] A rechargeable lithium iodide battery with a graphite anode, 1M LiPF6 as an active cathode material, and an electrolyte solution of 1M LiPF₆ EC-DPC (1:1 vol. %) was operated under oxygen at a current density of 1 mA/cm². FIG.3 shows the voltaic efficiency, coulombic efficiency, and specific capacity (normalized by the amount of lithium iodide) at the first charge/discharge cycle. EXAMPLE 3 RECHARGEABLE LITHIUM IODIDE GRAPHITE CELL PERFORMANCE 1M LIPF6 EC-EMC ELECTROLYTE (1:1 VOL.%) UNDER OXYGEN (at 1 mA/cm²) [0070] A rechargeable lithium iodide battery with a graphite anode and an electrolyte solution of 1M LiPF6 EC-EMC (1:1 vol. %) was operated under oxygen at a current density of 1 mA/cm². FIG.4 shows the voltaic efficiency, coulombic efficiency, and specific capacity (normalized by the amount of lithium iodide) at the first charge/discharge cycle. COMPARATIVE EXAMPLE 2 RECHARGEABLE LITHIUM IODIDE GRAPHITE CELL PERFORMANCE 1M LIPF6 EC-DMC ELECTROLYTE (1:1 VOL.%) UNDER ARGON (at 1 mA/cm²) [0071] A rechargeable lithium iodide battery with a graphite anode and an electrolyte solution of 1M LiPF6 EC-DMC (1:1 vol. %) was operated under argon at a current density of 1 mA/cm². FIG. 5 shows voltaic efficiency, coulombic efficiency, and specific capacity (normalized by the amount of lithium iodide) at the first charge/discharge cycle. COMPARATIVE EXAMPLE 3 RECHARGEABLE LITHIUM IODIDE GRAPHITE CELL PERFORMANCE MPN ELECTROLYTE UNDER OXYGEN [0072] A rechargeable lithium iodide battery with a graphite anode and an electrolyte solution of MPN was operated under oxygen at a current density of 1 mA/cm². FIG.6 shows voltaic efficiency, coulombic efficiency, and specific capacity (normalized by the amount of lithium iodide) at the first and fifth charge/discharge cycles. EXAMPLE 4 RECHARGEABLE LITHIUM IODIDE GRAPHITE CELL PERFORMANCE 1M LIPF6 EC-DEC ELECTROLYTE (1:1 vol.%) UNDER OXYGEN (at 5 mA/cm²) [0073] A rechargeable lithium iodide battery with a graphite anode and an electrolyte solution of 1M LiPF6 EC-DEC (1:1 vol. %) was operated under oxygen at a current density of 5 mA/cm². FIG. 7 shows voltaic efficiency, coulombic efficiency, and specific capacity (normalized by the amount of lithium iodide) at the first charge/discharge cycle. EXAMPLE 5 RECHARGEABLE LITHIUM IODIDE GRAPHITE CELL PERFORMANCE 1M LIPF6 EC-DEC ELECTROLYTE (1:1 vol.%) WITH GBL ADDITIVE (10 wt.%) UNDER OXYGEN (at 5 mA/cm²) [0074] A rechargeable lithium iodide battery with a graphite anode and an electrolyte solution of 1M LiPF6 EC-DEC (1:1 vol. %) with the electrolyte additive, GBL (10 wt.%), was operated under oxygen at a current density of 5 mA/cm². FIG.8 shows voltaic efficiency, coulombic efficiency, and specific capacity (normalized by the amount of lithium iodide) at the first charge/discharge cycle. EXAMPLE 6 RECHARGEABLE LITHIUM IODIDE GRAPHITE CELL PERFORMANCE 1M LIPF₆ EC-DEC ELECTROLYTE (1:1 vol.%) WITH ECL ADDITIVE (10 wt.%) UNDER OXYGEN (at 5 mA/cm²) [0075] A rechargeable lithium iodide battery with a graphite anode and an electrolyte solution of 1M LiPF6 EC-DEC (1:1 vol. %) with the electrolyte additive, ECL (10 wt.%), was operated under oxygen at a current density of 5 mA/cm². FIG.9 shows voltaic efficiency, coulombic efficiency, and specific capacity (normalized by the amount of lithium iodide) at the first charge/discharge cycle. EXAMPLE 7 RECHARGEABLE LITHIUM IODIDE GRAPHITE CELL PERFORMANCE 1M LIPF6 EC-DEC ELECTROLYTE (1:1 vol.%) WITH AND WITHOUT ADDITIVES UNDER OXYGEN (at 5 mA/cm²) [0076] Rechargeable lithium iodide batteries with graphite anodes and the following electrolyte solutions operated under oxygen at a current density of 5 mA/cm² were compared: (1) 1M LiPF6 EC-DEC (1:1 vol. %) (without an additive); (2) 1M LiPF6 EC-DEC (1:1 vol. %) with GBL additive (10 wt.%); and (3) 1M LiPF6 EC-DEC (1:1 vol. %) with ECL additive (10 wt.%). FIG. 10 shows the cycle life for the lithium iodide batteries as a function of specific capacity (mAh/g) for the battery with no additive, the battery with the GBL additive, and the battery with the ECL additive. EXAMPLE 8 RECHARGEABLE LITHIUM IODIDE GRAPHITE CELL PERFORMANCE 1M LIPF6 EC-DEC ELECTROLYTE (1:1 vol.%) WITH GBL ADDITIVE AT DIFFERENT WEIGHT FRACTIONS UNDER OXYGEN (at 5 mA/cm²) [0077] Rechargeable lithium iodide batteries with graphite anodes, 1M LiPF6 EC-DEC (1:1 vol. %) electrolyte solution, and GBL additive at the following weight percentages, relative to the electrolyte, were operated under oxygen at a current density of 5 mA/cm²: 0%, 10%, 20%, 30%, 50%, and 100%. FIG.11 shows cycle life at 80% of original capacity (from Example 7) per GBL weight percentage. EXAMPLE 9 RECHARGEABLE LITHIUM IODIDE GRAPHITE CELL PERFORMANCE 1M LIPF6 EC-DEC ELECTROLYTE (1:1 vol.%) WITH ECL ADDITIVE AT DIFFERENT WEIGHT FRACTIONS UNDER OXYGEN (at 5 mA/cm²) [0078] Rechargeable lithium iodide batteries with graphite anodes, 1M LiPF6 EC-DEC (1:1 vol. %) electrolyte solution, and ECL additive at the following weight percentages, relative to the electrolyte, were operated under oxygen at a current density of 5 mA/cm²: 0%, 10%, 20%, 30%, 50%, and 100%. FIG.12 shows cycle life at 80% of original capacity (from Example 7) per ECL weight percentage.

Claims

WE CLAIM: 1. A battery, comprising: an intercalation anode; a cathode comprising a metal halide incorporated into an electrically conductive material; an oxidizing gas; and an electrolyte in contact with the intercalation anode, the cathode, and the oxidizing gas.

2. The battery of claim 1, wherein the intercalation anode is selected from the group consisting of graphite, graphene, reduced graphene oxide (RGO), silicon, silicon alloys, silicon- carbon composites, carbon nanotubes, fullerenes, titanium dioxide (TiO2), titanium disulfide (TiS2), molybdenum dioxide (MoO2), molybdenum trioxide (MoO3), molybdenum disulfide (MoS2), and combinations thereof.

3. The battery of claim 1, wherein the intercalation anode comprises graphite.

4. The battery of claim 1, wherein the metal halide of the cathode comprises (i) a metal ion selected from the group consisting of Li⁺, Mg⁺, Zn⁺, Al⁺, Na⁺, and combinations thereof; and (ii) a halide ion selected from the group consisting of I-, Br-, Cl-, F-, and combinations thereof.

5. The battery of claim 1, wherein the cathode is a conversion cathode selected from the group consisting of: lithium iodide (LiI), lithium chloride (LiCl), lithium bromide (LiBr), lithium fluoride (LiF), sodium chloride (NaCl), sodium iodide (NaI2), nickel chloride(NiCl2), zinc bromide (ZnBr2), zinc chloride (ZnCl2), and combinations thereof.

6. The battery of claim 1, wherein the electrically conductive material is selected from the group consisting of carbon black, carbon paper, carbon foam, carbon fibers, carbon nanofibers, carbon nanotubes, activated carbon, amorphous carbon, graphite sheets, graphene, reduced graphene oxide, and combinations thereof.

7. The battery of claim 1, wherein the oxidizing gas is selected from the group consisting of oxygen, air, nitric oxide, nitrogen dioxide, and combinations thereof.

8. The battery of claim 1, wherein the electrolyte comprises: (i) a carbonate ester-based compound with at least one ethyl group; and (ii) an ion-conducting salt comprising a metal cation [M]⁺ and an anion [X]- having a chemical formula of [M]⁺[X]-, wherein the metal cation [M]⁺ is selected from the group consisting of Li⁺, Mg²⁺, Zn²⁺, Al³⁺, Na⁺, and combinations thereof.

9. The battery of claim 8, wherein the carbonate ester-based compound includes at least two ethyl groups.

10. The battery of claim 8, wherein the carbonate ester-based compound is selected from the group consisting of ethylene carbonate (EC), vinylene carbonate (VC), propylene carbonate (PC), diethyl carbonate (DEC), dipropyl carbonate (DPC), dibutyl carbonate (DBC), dimethyl carbonate (DMC), ethyl methyl carbonate (EMC), ethyl propyl carbonate (EPC), ethyl butyl carbonate (EBC), ethyl salicylate carbonate (ESC), fluoroethylene carbonate (FEC), allyl methyl carbonate (AMC), dodecyl ethyl carbonate (DDEC), diethyl decarbonate (DEDC), and combinations thereof.

11. The battery of claim 8, wherein the metal cation [M]⁺ is Li⁺.

12. The battery of claim 8, wherein the anion [X]- is selected from the group consisting of nitrate (NO₃-), hexafluorophosphate (PF₆-), tetrafluoroborate (BF₄-), bisoxalato borate (BOB-), difluorooxalato borate (DFOB-), trifluoromethanesulfonate (TF-), trifluoromethanesulfonylimide (TFSI-), fluorosulfonylimide (FSI-), and combinations thereof.

13. The battery of claim 1, wherein the electrolyte comprises at least one cyclic ester compound.

14. The battery of claim 13, wherein the at least one cyclic ester compound has a weight percent concentration in the electrolyte between 5% and 20%.

15. The battery of claim 13, wherein the at least one cyclic ester compound is selected from the group consisting of beta-propiolactone (BPL), beta-butyrolactone (BBL), alpha-methyl-gamma- butyrolactone (AMGBL), gamma-butyrolactone (GBL), gamma-valerolactone (GVL), delta- valerolactone (DVL), gamma-caprolactone (GCL), epsilon-caprolactone (ECL), gamma- octanolactone (GOL), gamma-nanolactone (GNL), gamma-decanolactone (GDL), delta- decanolactone (DDL), gamma-undecanolactone (GUL), delta-undecanolactone (DUL), delta- dodecanolactone (DDDL), and combinations thereof.

16. The battery of claim 13, wherein the at least one cyclic ester compound is gamma-butyrolactone (GBL) and/or epsilon-caprolactone (ECL).

17. A method of forming a battery comprising: forming a battery stack comprising an intercalation anode, a metal halide cathode in an electrically conductive material, a separator positioned between the intercalation anode and the electrically conductive material of the metal halide cathode, and an electrolyte comprising (i) a carbonate ester-based compound with at least one ethyl group and (ii) an ion-conducting salt comprising a metal cation [M]⁺ and an anion [X]- having a chemical formula of [M]⁺[X]-, wherein an oxidizing gas is introduced into the battery stack and the electrolyte is in contact with the intercalation anode, the metal halide cathode, and the oxidizing gas.

18. The method of claim 17, wherein the metal cation [M]⁺ of the electrolyte ion-conducting salt is selected from the group consisting of Li⁺ _, Mg²⁺, Zn²⁺, Al³⁺, Na⁺, and combinations thereof.

19. The method of claim 17, wherein the electrolyte solution comprises at least one cyclic ester compound with a weight percent concentration in the electrolyte solution between 5% and 20%.

20. The method of claim 17, wherein the at least one cyclic ester compound is gamma-butyrolactone (GBL) and/or epsilon-caprolactone (ECL).