WO2021096445A1 - Nouveau procédé pour ciments à haute performance - Google Patents

Nouveau procédé pour ciments à haute performance Download PDF

Info

Publication number
WO2021096445A1
WO2021096445A1 PCT/TR2019/050945 TR2019050945W WO2021096445A1 WO 2021096445 A1 WO2021096445 A1 WO 2021096445A1 TR 2019050945 W TR2019050945 W TR 2019050945W WO 2021096445 A1 WO2021096445 A1 WO 2021096445A1
Authority
WO
WIPO (PCT)
Prior art keywords
additive
cement
aqueous composition
glycol
composition
Prior art date
Application number
PCT/TR2019/050945
Other languages
English (en)
Inventor
Ozlem AKALIN
Original Assignee
Plustechno Danismanlik Ve Yapi Kimyasallari Tic. Ltd. Sti
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Plustechno Danismanlik Ve Yapi Kimyasallari Tic. Ltd. Sti filed Critical Plustechno Danismanlik Ve Yapi Kimyasallari Tic. Ltd. Sti
Priority to PCT/TR2019/050945 priority Critical patent/WO2021096445A1/fr
Priority to KR1020227019951A priority patent/KR20220104191A/ko
Priority to EP19952883.7A priority patent/EP4073013A4/fr
Publication of WO2021096445A1 publication Critical patent/WO2021096445A1/fr

Abstract

La présente invention concerne un nouveau procédé de fabrication de ciments à haute performance, une nouvelle composition d'aide au broyage comprenant un polycarboxylate ester et/ou éther, un procédé de production d'une telle composition et l'utilisation de ladite composition dans la production de ciment avec ou sans autres additifs. La présente invention concerne une nouvelle composition aqueuse destinée à être utilisée en tant qu'auxiliaire de broyage dans la production de ciment à haute performance, la composition comprenant au moins un polymère de polycarboxylate et au moins un tensioactif.
PCT/TR2019/050945 2019-11-13 2019-11-13 Nouveau procédé pour ciments à haute performance WO2021096445A1 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
PCT/TR2019/050945 WO2021096445A1 (fr) 2019-11-13 2019-11-13 Nouveau procédé pour ciments à haute performance
KR1020227019951A KR20220104191A (ko) 2019-11-13 2019-11-13 고성능 시멘트를 위한 신규한 공정
EP19952883.7A EP4073013A4 (fr) 2019-11-13 2019-11-13 Nouveau procédé pour ciments à haute performance

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/TR2019/050945 WO2021096445A1 (fr) 2019-11-13 2019-11-13 Nouveau procédé pour ciments à haute performance

Publications (1)

Publication Number Publication Date
WO2021096445A1 true WO2021096445A1 (fr) 2021-05-20

Family

ID=75913165

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/TR2019/050945 WO2021096445A1 (fr) 2019-11-13 2019-11-13 Nouveau procédé pour ciments à haute performance

Country Status (3)

Country Link
EP (1) EP4073013A4 (fr)
KR (1) KR20220104191A (fr)
WO (1) WO2021096445A1 (fr)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN113880490A (zh) * 2021-10-26 2022-01-04 宁波海螺新材料科技有限公司 一种立磨粉磨水泥专用助磨剂及其应用
CN114634322A (zh) * 2022-04-11 2022-06-17 安徽海螺新材料科技有限公司 一种水泥强度抗衰减剂及其制备方法和应用
CN114907030A (zh) * 2022-05-26 2022-08-16 昌德新材科技股份有限公司 一种水泥生料添加剂及其应用和水泥生产工艺
CN116375395A (zh) * 2023-03-03 2023-07-04 湖北工业大学 一种利用碳化钙基硅酸盐固废制备绿色硅酸钙板的方法

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2013049094A1 (fr) * 2011-09-29 2013-04-04 Dow Global Technologies Llc Composition de cémentation comprenant des éthers de cellulose modifiés anioniquement et hydrophobiquement et son utilisation
WO2014093157A1 (fr) * 2012-12-11 2014-06-19 Dow Global Technologies Llc Composition de cimentation comprenant des éthers de cellulose non anionique modifiés hydrophobiquement et son utilisation
WO2017192507A1 (fr) * 2016-05-03 2017-11-09 Gcp Applied Technologies Inc. Polymère réducteur d'eau de haut à moyen pouvoir de réduction avec chaînes latérales polyoxyalkylène mixtes
US20190233332A1 (en) * 2018-01-29 2019-08-01 Lawrence L Kuo Method for Low-to-Mid-Range Water Reduction of Cementitious Compositions

Family Cites Families (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8460457B2 (en) * 2009-08-20 2013-06-11 W. R. Grace & Co.-Conn. Robust air-detraining for cement milling
EP2788299A1 (fr) * 2011-12-06 2014-10-15 Sika Technology AG Stabilisation de polyols bruts obtenus à partir de biomasse
JP6166274B2 (ja) * 2011-12-22 2017-07-19 シーカ テクノロジー アクチェンゲゼルシャフト 粒径に応じて固体粒子を分離する装置の効率向上
EP2660218A1 (fr) * 2012-05-04 2013-11-06 Construction Research & Technology GmbH Procédé de fabrication d'un liant hydraulique, additif correspondant et son utilisation.
US10336652B2 (en) * 2017-11-10 2019-07-02 Gcp Applied Technologies Inc. Enhancing calcined clay use with inorganic binders

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2013049094A1 (fr) * 2011-09-29 2013-04-04 Dow Global Technologies Llc Composition de cémentation comprenant des éthers de cellulose modifiés anioniquement et hydrophobiquement et son utilisation
WO2014093157A1 (fr) * 2012-12-11 2014-06-19 Dow Global Technologies Llc Composition de cimentation comprenant des éthers de cellulose non anionique modifiés hydrophobiquement et son utilisation
WO2017192507A1 (fr) * 2016-05-03 2017-11-09 Gcp Applied Technologies Inc. Polymère réducteur d'eau de haut à moyen pouvoir de réduction avec chaînes latérales polyoxyalkylène mixtes
US20190233332A1 (en) * 2018-01-29 2019-08-01 Lawrence L Kuo Method for Low-to-Mid-Range Water Reduction of Cementitious Compositions

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN113880490A (zh) * 2021-10-26 2022-01-04 宁波海螺新材料科技有限公司 一种立磨粉磨水泥专用助磨剂及其应用
CN114634322A (zh) * 2022-04-11 2022-06-17 安徽海螺新材料科技有限公司 一种水泥强度抗衰减剂及其制备方法和应用
CN114634322B (zh) * 2022-04-11 2023-03-14 安徽海螺材料科技股份有限公司 一种水泥强度抗衰减剂及其制备方法和应用
CN114907030A (zh) * 2022-05-26 2022-08-16 昌德新材科技股份有限公司 一种水泥生料添加剂及其应用和水泥生产工艺
CN116375395A (zh) * 2023-03-03 2023-07-04 湖北工业大学 一种利用碳化钙基硅酸盐固废制备绿色硅酸钙板的方法
CN116375395B (zh) * 2023-03-03 2024-05-03 湖北工业大学 一种利用碳化钙基硅酸盐固废制备绿色硅酸钙板的方法

Also Published As

Publication number Publication date
KR20220104191A (ko) 2022-07-26
EP4073013A4 (fr) 2023-10-11
EP4073013A1 (fr) 2022-10-19

Similar Documents

Publication Publication Date Title
US8460457B2 (en) Robust air-detraining for cement milling
US7160384B2 (en) Amine-containing cement processing additives
WO2021096445A1 (fr) Nouveau procédé pour ciments à haute performance
AU745142B2 (en) Strength enhanced portland cement compositions
EP2842925B1 (fr) Liants composites de sulfoaluminate de calcium
DK2582643T3 (en) Grinding Aids
AU2014317429A2 (en) Calcium sulfoaluminate composite binders
WO2018150753A1 (fr) Composition de géopolymère, et mortier et béton l'utilisant
EP2842924A1 (fr) Liant composite comprenant du ciment de sulfoaluminate de calcium et du nitrate de calcium ou du nitrite de calcium
EP3615491B1 (fr) Agents d'amélioration de la résistance du ciment
JP5737710B2 (ja) 石炭灰混合セメント組成物
WO2022201818A1 (fr) Composition de ciment et son procédé de production
JP2004284865A (ja) 水硬性組成物及びポンプ圧送性に優れたコンクリートまたはモルタル
CN115872707B (zh) 一种自生长纳米钙矾石纤维增韧混凝土及其制备方法
TR2021019185A2 (tr) Öğütme yardimcisi
WO2023104349A1 (fr) Auxiliaire de broyage
WO2023036229A1 (fr) Adjuvant pour ciment
CN115872707A (zh) 一种自生长纳米钙矾石纤维增韧混凝土及其制备方法
JP2022155004A (ja) 混合セメント組成物およびその製造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 19952883

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 20227019951

Country of ref document: KR

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 2019952883

Country of ref document: EP

Effective date: 20220613