WO2021050791A1 - Compositions de polymères conducteurs et leurs procédés de fabrication et d'utilisation - Google Patents
Compositions de polymères conducteurs et leurs procédés de fabrication et d'utilisation Download PDFInfo
- Publication number
- WO2021050791A1 WO2021050791A1 PCT/US2020/050275 US2020050275W WO2021050791A1 WO 2021050791 A1 WO2021050791 A1 WO 2021050791A1 US 2020050275 W US2020050275 W US 2020050275W WO 2021050791 A1 WO2021050791 A1 WO 2021050791A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- pedot
- layer
- polymer
- substrate
- rust
- Prior art date
Abstract
Divers aspects de la présente invention concernent des procédés et des compositions pour fabriquer des particules et des couches polymères conductrices nanostructurées (par exemple, des films, des mats) à l'aide de procédés de polymérisation en phase vapeur, ainsi que des composants électriques et des dispositifs comprenant les particules et les couches polymères conductrices nanostructurées.
Applications Claiming Priority (6)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US201962898195P | 2019-09-10 | 2019-09-10 | |
US62/898,195 | 2019-09-10 | ||
US201962939265P | 2019-11-22 | 2019-11-22 | |
US62/939,265 | 2019-11-22 | ||
US202063000870P | 2020-03-27 | 2020-03-27 | |
US63/000,870 | 2020-03-27 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2021050791A1 true WO2021050791A1 (fr) | 2021-03-18 |
Family
ID=74865610
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/US2020/050275 WO2021050791A1 (fr) | 2019-09-10 | 2020-09-10 | Compositions de polymères conducteurs et leurs procédés de fabrication et d'utilisation |
Country Status (1)
Country | Link |
---|---|
WO (1) | WO2021050791A1 (fr) |
Cited By (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN113690056A (zh) * | 2021-07-30 | 2021-11-23 | 江苏浴普太阳能有限公司 | 一种电能储能砖的加工方法 |
CN113881040A (zh) * | 2021-09-26 | 2022-01-04 | 上海交通大学 | 一种二维MXene/聚多巴胺复合脱盐电极材料的制备方法及应用 |
CN114530335A (zh) * | 2022-02-23 | 2022-05-24 | 苏州固韧纳米材料技术有限公司 | 超级电容器储能砖、其制备方法及超级电容器 |
WO2023055607A1 (fr) * | 2021-09-28 | 2023-04-06 | Kemet Electronics Corporation | Dispersion de polymère avancée et condensateur sur sa base |
CN115975499A (zh) * | 2022-12-16 | 2023-04-18 | 浙江工业大学 | 一种用于太阳能界面蒸发的光热涂层复合材料的制备方法 |
Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US8183082B1 (en) * | 2008-12-03 | 2012-05-22 | University Of South Florida | Fabrication of organic solar array for applications in microelectromechanical systems and others |
US20140322608A1 (en) * | 2011-08-15 | 2014-10-30 | Purdue Research Foundation | Modified graphitic electrodes for electrochemical energy storage enhancement |
WO2015077792A1 (fr) * | 2013-11-25 | 2015-05-28 | Georgetown University | Dispositifs électroniques à nanoparticules organiques |
US9379326B2 (en) * | 2011-10-27 | 2016-06-28 | Merck Patent Gmbh | Selective etching of a matrix comprising silver nano wires |
-
2020
- 2020-09-10 WO PCT/US2020/050275 patent/WO2021050791A1/fr active Application Filing
Patent Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US8183082B1 (en) * | 2008-12-03 | 2012-05-22 | University Of South Florida | Fabrication of organic solar array for applications in microelectromechanical systems and others |
US20140322608A1 (en) * | 2011-08-15 | 2014-10-30 | Purdue Research Foundation | Modified graphitic electrodes for electrochemical energy storage enhancement |
US9379326B2 (en) * | 2011-10-27 | 2016-06-28 | Merck Patent Gmbh | Selective etching of a matrix comprising silver nano wires |
WO2015077792A1 (fr) * | 2013-11-25 | 2015-05-28 | Georgetown University | Dispositifs électroniques à nanoparticules organiques |
Non-Patent Citations (2)
Title |
---|
D’ARCY JULIO M., EL-KADY MAHER F., KHINE PWINT P., ZHANG LINGHONG, LEE SUN HWA, DAVIS NICOLE R., LIU DAVID S., YEUNG MICHAEL T., K: "Vapor-Phase Polymerization of Nanofibrillar Poly(3,4-ethylenedioxythiophene) for Supercapacitors", ACS NANO, vol. 8, no. 2, 3 February 2014 (2014-02-03), pages 1500 - 1510, XP055804773, DOI: 10.1021/nn405595r * |
DIAO YIFAN, CHEN HAOZHE, LU YANG, SANTINO LUCIANO M., WANG HONGMIN, D’ARCY JULIO M.: "Converting Rust to PEDOT Nanofibers for Supercapacitors", ACS APPLIED ENERGY MATERIALS, vol. 2, no. 5, 7 May 2019 (2019-05-07), pages 3435 - 3444, XP055804771, DOI: 10.1021/acsaem.9b00244 * |
Cited By (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN113690056A (zh) * | 2021-07-30 | 2021-11-23 | 江苏浴普太阳能有限公司 | 一种电能储能砖的加工方法 |
CN113881040A (zh) * | 2021-09-26 | 2022-01-04 | 上海交通大学 | 一种二维MXene/聚多巴胺复合脱盐电极材料的制备方法及应用 |
CN113881040B (zh) * | 2021-09-26 | 2022-05-31 | 上海交通大学 | 一种二维MXene/聚多巴胺复合脱盐电极材料的制备方法及应用 |
WO2023055607A1 (fr) * | 2021-09-28 | 2023-04-06 | Kemet Electronics Corporation | Dispersion de polymère avancée et condensateur sur sa base |
CN114530335A (zh) * | 2022-02-23 | 2022-05-24 | 苏州固韧纳米材料技术有限公司 | 超级电容器储能砖、其制备方法及超级电容器 |
CN114530335B (zh) * | 2022-02-23 | 2023-09-29 | 苏州固韧纳米材料技术有限公司 | 超级电容器储能砖、其制备方法及超级电容器 |
CN115975499A (zh) * | 2022-12-16 | 2023-04-18 | 浙江工业大学 | 一种用于太阳能界面蒸发的光热涂层复合材料的制备方法 |
CN115975499B (zh) * | 2022-12-16 | 2023-11-17 | 浙江工业大学 | 一种用于太阳能界面蒸发的光热涂层复合材料的制备方法 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
WO2021050791A1 (fr) | Compositions de polymères conducteurs et leurs procédés de fabrication et d'utilisation | |
Zhang et al. | Recent progress on nanostructured conducting polymers and composites: synthesis, application and future aspects | |
Browne et al. | 3D printing for electrochemical energy applications | |
Sekhar et al. | Conductive silver nanowires-fenced carbon cloth fibers-supported layered double hydroxide nanosheets as a flexible and binder-free electrode for high-performance asymmetric supercapacitors | |
Tan et al. | Graphene as a flexible electrode: review of fabrication approaches | |
Han et al. | Hierarchical Co3O4@ PPy@ MnO2 core–shell–shell nanowire arrays for enhanced electrochemical energy storage | |
Ellis et al. | Three‐dimensional self‐supported metal oxides for advanced energy storage | |
Liang et al. | Inorganic porous films for renewable energy storage | |
Li et al. | Electrochemical synthesis of nanostructured materials for electrochemical energy conversion and storage | |
Santhanagopalan et al. | Scalable high-power redox capacitors with aligned nanoforests of crystalline MnO2 nanorods by high voltage electrophoretic deposition | |
Patil et al. | An ion exchange mediated shape-preserving strategy for constructing 1-D arrays of porous CoS 1.0365 nanorods for electrocatalytic reduction of triiodide | |
Xu et al. | Understanding the effect of polypyrrole and poly (3, 4-ethylenedioxythiophene) on enhancing the supercapacitor performance of NiCo 2 O 4 electrodes | |
Feng et al. | Template synthesis of a heterostructured MnO2@ SnO2 hollow sphere composite for high asymmetric supercapacitor performance | |
Das et al. | Binder-free CuS@ PEDOT and Co–V–Se electrodes for flexible quasi-solid-state asymmetric supercapacitor | |
Diao et al. | Converting rust to PEDOT nanofibers for supercapacitors | |
CN104813425A (zh) | 高比电容和高功率密度印刷柔性微型超级电容器 | |
Deshmukh et al. | Inexpensive synthesis route of porous polyaniline–ruthenium oxide composite for supercapacitor application | |
CN103403922A (zh) | 表面介导的锂离子交换能量存储装置 | |
Shinde et al. | Chemical synthesis of flower-like hybrid Cu (OH) 2/CuO electrode: application of polyvinyl alcohol and triton X-100 to enhance supercapacitor performance | |
Huang et al. | Amorphous NiWO4 nanospheres with high-conductivity and-capacitive performance for supercapacitors | |
Singh et al. | Nanoporous gold–copper oxide based all-solid-state micro-supercapacitors | |
Shen et al. | Polypyrrole embedded in nickel-cobalt sulfide nanosheets grown on nickel particles passivated silicon nanowire arrays for high-performance supercapacitors | |
US20230053249A1 (en) | Dendritic materials with hierarchical porosity | |
Zhang et al. | MOF-derived hollow and porous Co3O4 nanocages for superior hybrid supercapacitor electrodes | |
Khani et al. | Modifying current collectors to produce high volumetric energy density and power density storage devices |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 20862139 Country of ref document: EP Kind code of ref document: A1 |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 20862139 Country of ref document: EP Kind code of ref document: A1 |