WO2021032493A1 - Temperable coatings having diamond-like carbon and deposition by means of high-power impulse magnetron sputtering - Google Patents
Temperable coatings having diamond-like carbon and deposition by means of high-power impulse magnetron sputtering Download PDFInfo
- Publication number
- WO2021032493A1 WO2021032493A1 PCT/EP2020/072116 EP2020072116W WO2021032493A1 WO 2021032493 A1 WO2021032493 A1 WO 2021032493A1 EP 2020072116 W EP2020072116 W EP 2020072116W WO 2021032493 A1 WO2021032493 A1 WO 2021032493A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- dlc
- layers
- release layer
- carbon
- Prior art date
Abstract
Description
Claims