WO2021002440A1 - Plaque polarisante à base de colorant hautement durable contenant un colorant absorbant le proche infrarouge - Google Patents

Plaque polarisante à base de colorant hautement durable contenant un colorant absorbant le proche infrarouge Download PDF

Info

Publication number
WO2021002440A1
WO2021002440A1 PCT/JP2020/026065 JP2020026065W WO2021002440A1 WO 2021002440 A1 WO2021002440 A1 WO 2021002440A1 JP 2020026065 W JP2020026065 W JP 2020026065W WO 2021002440 A1 WO2021002440 A1 WO 2021002440A1
Authority
WO
WIPO (PCT)
Prior art keywords
group
polarizing plate
substituted
carbon atoms
plate according
Prior art date
Application number
PCT/JP2020/026065
Other languages
English (en)
Japanese (ja)
Inventor
典明 望月
陵太郎 森田
由侑 服部
Original Assignee
日本化薬株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日本化薬株式会社 filed Critical 日本化薬株式会社
Priority to JP2021529191A priority Critical patent/JPWO2021002440A1/ja
Publication of WO2021002440A1 publication Critical patent/WO2021002440A1/fr

Abstract

Plaque de polarisation qui comprend un film polymère hydrophile contenant un colorant absorbant le proche infrarouge et un substrat qui est disposé sur une surface ou sur les deux surfaces du film, le substrat ayant au moins l'une des caractéristiques (a) et (b) décrites ci-dessous.　(a) Si le film polymère hydrophile contient un composé de bore, la masse du composé de bore (en termes d'acide borique) contenu dans le film polymère hydrophile, après exposition de la plaque polarisante à un environnement à une humidité relative de 90 % RH à 80°C pendant 1 000 heures, est maintenue à 20 ou plus si sa masse avant l'exposition est prise en tant que 100. (b) La perméabilité à l'humidité du substrat dans un environnement à une humidité relative de 90 % RH à 40°C, telle que déterminée par un test de perméabilité à la vapeur d'eau conformément à la norme JIS Z 0208, est de 0 à 1 500 g/2 en 24 heures.
PCT/JP2020/026065 2019-07-03 2020-07-02 Plaque polarisante à base de colorant hautement durable contenant un colorant absorbant le proche infrarouge WO2021002440A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2021529191A JPWO2021002440A1 (fr) 2019-07-03 2020-07-02

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2019124226 2019-07-03
JP2019-124226 2019-07-03

Publications (1)

Publication Number Publication Date
WO2021002440A1 true WO2021002440A1 (fr) 2021-01-07

Family

ID=74100387

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2020/026065 WO2021002440A1 (fr) 2019-07-03 2020-07-02 Plaque polarisante à base de colorant hautement durable contenant un colorant absorbant le proche infrarouge

Country Status (3)

Country Link
JP (1) JPWO2021002440A1 (fr)
TW (1) TW202112979A (fr)
WO (1) WO2021002440A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2022215757A1 (fr) * 2021-04-09 2022-10-13 富士フイルム株式会社 Couche anisotrope d'absorption optique, stratifié et système de capteur de lumière infrarouge

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2016171126A1 (fr) * 2015-04-20 2016-10-27 日本化薬株式会社 Composition contenant un colorant dichroïque, film colorant produit en l'utilisant, et élément polarisant comprenant ledit film colorant
WO2018088558A1 (fr) * 2016-11-14 2018-05-17 日本化薬株式会社 Plaque polarisante à base de colorant pour plage de longueur d'onde infrarouge

Family Cites Families (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR102200551B1 (ko) * 2017-10-31 2021-01-07 주식회사 엘지화학 배터리 팩

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2016171126A1 (fr) * 2015-04-20 2016-10-27 日本化薬株式会社 Composition contenant un colorant dichroïque, film colorant produit en l'utilisant, et élément polarisant comprenant ledit film colorant
WO2018088558A1 (fr) * 2016-11-14 2018-05-17 日本化薬株式会社 Plaque polarisante à base de colorant pour plage de longueur d'onde infrarouge

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2022215757A1 (fr) * 2021-04-09 2022-10-13 富士フイルム株式会社 Couche anisotrope d'absorption optique, stratifié et système de capteur de lumière infrarouge

Also Published As

Publication number Publication date
JPWO2021002440A1 (fr) 2021-01-07
TW202112979A (zh) 2021-04-01

Similar Documents

Publication Publication Date Title
TWI643908B (zh) 具有高透過率之無彩色之染料系偏光元件及偏光板
JP7230079B2 (ja) アゾ化合物又はその塩及びこれを含有する偏光膜
TWI600719B (zh) Dye-based polarizing element, polarizing plate using the dye-based polarizing element and liquid crystal display device
US20140085721A1 (en) Dye-Based Polarizing Element And Polarizing Plate
JP7010850B2 (ja) アゾ化合物又はその塩、並びにこれを含有する染料系偏光膜及び染料系偏光板
JP7507695B2 (ja) アゾ化合物又はその塩、並びにこれを含有する染料系偏光膜及び染料系偏光板
WO2021002440A1 (fr) Plaque polarisante à base de colorant hautement durable contenant un colorant absorbant le proche infrarouge
JP6609260B2 (ja) 偏光素子および該偏光素子を有する偏光板、並びに該偏光素子又は該偏光板を有する液晶表示装置
TWI774864B (zh) 抬頭顯示器裝置
TWI762601B (zh) 偏光板
US20140126054A1 (en) Dye-Based Polarizing Element And Polarizing Plate
JP7507694B2 (ja) アゾ化合物又はその塩、並びにこれを含有する染料系偏光膜及び染料系偏光板
WO2013129170A1 (fr) Élément polarisant à base de colorant et plaque polarisante
WO2013129171A1 (fr) Élément polarisant à base de colorant et plaque polarisante
WO2020230647A1 (fr) Polariseur achromatique, plaque polarisante achromatique l'utilisant, et dispositif d'affichage
WO2021246437A1 (fr) Élément polarisant et plaque polarisante destinés à être utilisés dans la plage visible et la plage infrarouge, et dispositif d'affichage à cristaux liquides équipé de celui-ci

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 20834677

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2021529191

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 20834677

Country of ref document: EP

Kind code of ref document: A1