WO2020223688A1 - Polyethylene-based compositions and films and articles comprising the same - Google Patents

Polyethylene-based compositions and films and articles comprising the same Download PDF

Info

Publication number
WO2020223688A1
WO2020223688A1 PCT/US2020/031151 US2020031151W WO2020223688A1 WO 2020223688 A1 WO2020223688 A1 WO 2020223688A1 US 2020031151 W US2020031151 W US 2020031151W WO 2020223688 A1 WO2020223688 A1 WO 2020223688A1
Authority
WO
WIPO (PCT)
Prior art keywords
polyethylene
composition
weight
film
fraction
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/US2020/031151
Other languages
English (en)
French (fr)
Inventor
Andrew T. Heitsch
Sanjib Biswas
Mridula Babli Kapur
Alexander Williamson
Philip P. Fontaine
Joshua B. GAUBERT
Daniel W. BAUGH III
Jin Wang
Didem Oner-Deliormanli
Hitendra K. SINGH
Shadid Askar
Arnaldo T. LORENZO
Mehmet Demirors
Vivek KALIHARI
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dow Global Technologies LLC
Original Assignee
Dow Global Technologies LLC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dow Global Technologies LLC filed Critical Dow Global Technologies LLC
Priority to EP20727106.5A priority Critical patent/EP3962998B1/en
Priority to MX2021012936A priority patent/MX2021012936A/es
Priority to CN202080026502.5A priority patent/CN113661209B/zh
Priority to JP2021561807A priority patent/JP7601786B2/ja
Priority to US17/432,449 priority patent/US12129363B2/en
Priority to ES20727106T priority patent/ES2953841T3/es
Priority to BR112021019568-8A priority patent/BR112021019568B1/pt
Publication of WO2020223688A1 publication Critical patent/WO2020223688A1/en
Anticipated expiration legal-status Critical
Priority to CONC2021/0015974A priority patent/CO2021015974A2/es
Ceased legal-status Critical Current

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L23/00—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers
    • C08L23/02—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers not modified by chemical after-treatment
    • C08L23/04—Homopolymers or copolymers of ethene
    • C08L23/06—Polyethylene
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J5/00—Manufacture of articles or shaped materials containing macromolecular substances
    • C08J5/18—Manufacture of films or sheets
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K3/00—Use of inorganic substances as compounding ingredients
    • C08K3/34—Silicon-containing compounds
    • C08K3/36—Silica
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K5/00—Use of organic ingredients
    • C08K5/04—Oxygen-containing compounds
    • C08K5/09—Carboxylic acids; Metal salts thereof; Anhydrides thereof
    • C08K5/098—Metal salts of carboxylic acids
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2323/00—Characterised by the use of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Derivatives of such polymers
    • C08J2323/02—Characterised by the use of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Derivatives of such polymers not modified by chemical after treatment
    • C08J2323/04—Homopolymers or copolymers of ethene
    • C08J2323/06—Polyethene
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2423/00—Characterised by the use of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Derivatives of such polymers
    • C08J2423/02—Characterised by the use of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Derivatives of such polymers not modified by chemical after treatment
    • C08J2423/04—Homopolymers or copolymers of ethene
    • C08J2423/06—Polyethene
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L2201/00—Properties
    • C08L2201/14—Gas barrier composition
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L2203/00—Applications
    • C08L2203/16—Applications used for films
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L2205/00—Polymer mixtures characterised by other features
    • C08L2205/02—Polymer mixtures characterised by other features containing two or more polymers of the same C08L -group
    • C08L2205/025—Polymer mixtures characterised by other features containing two or more polymers of the same C08L -group containing two or more polymers of the same hierarchy C08L, and differing only in parameters such as density, comonomer content, molecular weight, structure
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L2205/00—Polymer mixtures characterised by other features
    • C08L2205/24—Crystallisation aids
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L2207/00—Properties characterising the ingredient of the composition
    • C08L2207/06—Properties of polyethylene
    • C08L2207/062—HDPE

Definitions

  • the presort invention relates to polyethylene-based compositions, to films
  • Some packages such as food packages are designed to protect the contents from the external environment and to facilitate a longer shelf. Such packages are often constructed using barrier films with low oxygen transmission rates (OTR) and water vapor transmission rates (WVTR). However, in balancing the barrier properties, consideration is also given to package integrity to, for example, avoid leakage.
  • OTR oxygen transmission rates
  • WVTR water vapor transmission rates
  • the presort invention provides polyethylene-based compositions suitable for packaging applications, films, and articles.
  • the polyethylene-based compositions when incorporated into a film, provide improved moisture vapor barrio ⁇ .
  • the polyethylene-based compositions when incorporated into film, provide improved moisture vapor barrier performance (reduced amount of water vapor passing through film) while also maintaining desired physical properties.
  • the compositions can be incorporated into multilayer films and articles that are comprised primarily, if not substantially or entirely, of polyolefins in order to provide a film and articles that are more easily recyclable.
  • polyethyelene-based compositions of the present invention can be incorporated into a surface layer of a film and exhibit a relatively low level of dusting.
  • a polyethylene-based composition suitable for packaging applications comprises (a) at least 97% by weight, based on the total weight of the polyethylene-based composition, of a polyethylene composition comprising:
  • the polyethylene composition comprises from 25 to 37 percent by weight of the first polyethylene fraction having a density in the range of 0.940 to 0.947 g/cm 3 and from 63 to 75 percent by weight of the second polyethylene fraction having a density of 0.970 g/cm 3 or greater.
  • the present invention relates to a film comprising any of the polyethylene-based compositions disclosed herein.
  • the present invention relates to an article, such as a food package, comprising any of the polyethylene-based compositions or films disclosed herein.
  • composition refers to a mixture of materials which comprises the composition, as well as reaction products and decomposition products formed from the materials of the composition.
  • Polymer means a polymeric compound prepared by polymerizing monomers, whether of the same or a different type.
  • the generic terrm polymer thus embraces the term homopolymer as defined hereafter, and the term interpolymer as defined hereinafter. Trace amounts of impurities (for example, catalyst residues) may be incorporated into and/or within the polymer.
  • a polymer may be a single polymer, a polymer blend or a polymer mixture, including mixtures of polymers that are formed in situ during polymerization.
  • homopolymer refers to polymers prepared from only one type of monomer with the understanding that trace amounts of impurities can be incorporated into the polymer structure.
  • interpolymer refers to polymers prepared by the polymerization of at least two different types of monomers.
  • the generic term interpolymer thus includes copolymers (employed to refer to polymers prepared from two different types of monomers), and polymers prepared from more than two different types of monomers.
  • olefin-based polymer or“polyolefin”, as used herein, refer to a polymer that comprises, in polymerized form, a majority amount of olefin monomer, for example ethylene or propylene (based on the weight of the polymer), and optionally may comprise one or more comonomers.
  • ethylene/a-olefin interpolymer refers to an interpolymer that comprises, in polymerized form, a majority amount (>50 mol %) of units derived from ethylene monomer, and the remaining units derived from one or more a-olefins.
  • Typical a- olefins used in forming ethylene/a-olefin interpolymers are C 3 -C 10 alkenes.
  • ethylene/a-olefin copolymer refers to a copolymer that comprises, in polymerized form, a majority amount (>50 mol%) of ethylene monomer, and an a-olefin, as the only two monomer types.
  • a-olefin refers to an alkene having a double bond at the primary or alpha (a) position.
  • Polyethylene or“ethylene-based polymer” shall mean polymers comprising a majority amount (>50 mol %) of units which have been derived from ethylene monomer. This includes polyethylene homopolymers or copolymers (meaning units derived from two or more comonomers).
  • LDPE Low Density Polyethylene
  • LLDFE Linear Low Density Polyethylene
  • ULDFE Ultra Low Density Polyethylene
  • VLDFE Very Low Density Polyethylene
  • m-LLDPE linear low density resins
  • POP ethylene-based plastomers
  • POE ethylene-based elastomers
  • MDFE Medium Density Polyethylene
  • HOPE High Density Polyethylene
  • LDFE low density ethylene polymer
  • high pressure ethylene polymer or “highly branched polyethylene” and is defined to mean that the polymer is partly or entirely homo-polymerized or copolymerized in autoclave or tubular reactors at pressures above 14,500 psi (100 MPa) with the use of free-radical initiators, such as peroxides (see for example US 4,599,392, which is hereby incorporated by reference).
  • LDPE resins typically have a density in the range of 0.916 to 0.935 gZcm 3 .
  • LLDPE includes both resin made using the traditional Ziegler-Natta catalyst systems and chromium-based catalyst systems as well as single- site catalysts, including, but not limited to, substituted mono- or bis-cyclopentadienyl catalysts (typically referred to as metallocene), constrained geometry catalysts, phosphinimine catalysts & polyvalent aryloxyether catalysts (typically referred to as bisphenyl phenoxy), and includes linear, substantially linear or heterogeneous polyethylene copolymers or homopolymers.
  • LLDFEs contain less long chain blanching than LDPEs and includes the substantially linear ethylene polymers which are further defined in U.S. Patent 5,272,236, U.S.
  • the LLDFEs can be made via gas-phase, solution-phase or slurry polymerization or any combination thereof, using any type of reactor or reactor configuration known in the ait.
  • “MDFE” refers to polyethylenes having densities from 0.926 to 0.935 g/cm 3 .
  • “MDFE” is typically made using chromium or Ziegler-Natta catalysts or using single-site catalysts including, but not limited to, substituted mono- or bis-cyclopentadienyl catalysts (typically referred to as metallocene), constrained geometry catalysts, phosphinimine catalysts & polyvalent aryloxyether catalysts (typically referred to as bisphenyl phenoxy), and typically have a molecular weight distribution (“MWD”) greater than 2.5.
  • MWD molecular weight distribution
  • HOPE refers to polyethylenes having densities greater than about 0.935 g/cm 3 and up to about 0.980 g/cm 3 , which are generally prepared with Ziegler-Natta catalysts, chrome catalysts or single- site catalysts including, but not limited to, substituted mono- or bis-cyclopentadienyl catalysts (typically referred to as metallocene), constrained geometry catalysts, phosphinimine catalysts & polyvalent aryloxyether catalysts (typically referred to as bisphenyl phenoxy).
  • ULDFE refers to polyethylenes having densities of 0.855 to 0.912 g/cm 3 , which are generally prepared with Ziegler-Natta catalysts, chrome catalysts, or single- site catalysts including, but not limited to, substituted mono- or bis-cyclopentadienyl catalysts (typically referred to as metallocene), constrained geometry catalysts,
  • ULDFEs include, but are not limited to, polyethylene (ethylene-based) plastomers and polyethylene (ethylene-based) elastomers.
  • Polyethylene (ethylene-based) elastomers plastomers generally have densities of 0.855 to 0.912 g/cm 3 .
  • Blend “polymer blend” and like terms mean a composition of two or more polymers. Such a blend may or may not be miscible. Such a blend may or may not be phase separated. Such a blend may or may not contain one or more domain configurations, as determined from transmission electron spectroscopy, light scattering, x-ray scattering, and any other method known in the art Blends are not laminates, but one or more layers of a laminate may contain a blend. Such blends can be prepared as dry blends, formed in situ (e.g., in a reactor), melt blends, or using other techniques known to those of skill in the art
  • compositions claimed through use of the term“comprising” may include any additional additive, adjuvant, or compound, whether polymeric or otherwise, unless stated to the contrary.
  • the term,“consisting essentially of” excludes from the scope of any succeeding recitation any other component, step or procedure, excepting those that are not essential to operability.
  • the torn“consisting of” excludes any component, step or procedure not specifically delineated or listed.
  • the presort invention generally relates to polyethylene-based compositions suitable for packaging applications.
  • the polyethylene-based compositions can provide a reduction in water vapor transmission rates.
  • the combination of a unique design for a polyethylene composition and a specific amount of a nucleator can deliver improved barrier performance.
  • the inventive polyethylene-based compositions can be incorporated into films and articles having improved barrier and in particular, increased barrier to water vapor. Because the inventive compositions are polyethylene-based, in some embodiments, the films and articles can be formed entirely or substantially entirely from polyolefins making the films and articles more readily recyclable.
  • a polyethylene-based composition suitable for packaging applications comprises (a) at least 97% by weight, based on the total weight of the polyethylene-based composition, of a polyethylene composition comprising:
  • the first polyethylene fraction has a density of 0.940 to 0.947 g/cm 3 .
  • the second polyethylene fraction has a density of 0.970 g/cm 3 or more.
  • the polyethylene composition comprises from 25 to 37 percent by weight of the first polyethylene fraction having a density in the range of 0.940 to 0.947 g/cm 3 and from 63 to 75 percent by weight of the second polyethylene fraction having a density of 0.970 g/cm 3 or greater.
  • the polyethylene composition comprises 30 to 37 percent by weight of the first polyethylene fraction.
  • the second polyethylene fraction has a melt index (I 2 ) of at least 100 g/10 minutes. In some embodiments, the second polyethylene fraction has a melt index (I 2 ) of at least 100 g/10 minutes and to 10,000 g/10 minutes or more. The second polyethylene fraction has a melt index (I 2 ) of at least 100 g/10 minutes and up to 10,000 g/10 minutes, in some embodiments. The second polyethylene fraction has a melt index (I 2 ) of at least 100 g/10 minutes and up to 1,000 g/10 minutes, in some embodiments. In some embodiments, the ratio of the melt index (I 2 ) of the second polyethylene fraction to the melt index (I 2 ) of the first polyethylene fraction is at least 1,000.
  • the polyethylene-based composition has an overall melt index (I 2 ) of 2.5 g/10 minutes or less.
  • the polyethylene-based composition has a zero shear viscosity ratio of less than 2.0.
  • the polyethylene composition has less than 0.05 branches per 1,000 carbon atoms when measured using 13 C NMR.
  • the polyethylene composition has less than 0.03 branches per 1,000 carbon atoms when measured using 13 C NMR in some embodiments.
  • the polyethylene-based composition in some anbodiments, has less than 25 non-vinyl unsaturations per 1 million carbons.
  • the polyethylene-based composition in some anbodiments, has less than 20 non-vinyl unsaturations per 1 million carbons.
  • the polyethylene composition has less than 0.05 branches per 1,000 carbon atoms when measured using 13 C NMR and less than 20 non-vinyl unsaturations per 1 million carbons.
  • die polyethylene-based composition further comprises a fatty acid metal salt in the amount of 45 to 360 ppm based on the total weight of the composition.
  • the metal in the fatty add metal salt is preferably zinc or magnesium.
  • the fatty add metal salt is at least one of zinc stearate and zinc palmitate, in some embodiments.
  • the polyethylene-based composition further comprises silica in the amount of 75 to 800 ppm, based on the total weight of the composition.
  • the film when the polyethylene-based composition is incorporated into a monolayer film, the film exhibits a WVTR of 0.1 or less (g-mil)/(100 in 2 ⁇ day) when measured according to ASTM F1249-06 at 38° C and 100% relative humidity.
  • the present invention relates to a film comprising any of the polyethylene-based compositions disclosed herein.
  • the present invention relates to an article, such as a food package, comprising any of the polyethylene-based compositions or films disclosed herein.
  • polyethylene-based compositions of the present invention comprise a polyethylene composition comprising (i) from 25 to 37 percent by wdght of a first polyethylene fraction having a density in the range of 0.935 to 0.947 g/cm 3 and a melt index (I 2 ) of less than 0.1 g/10 minutes; and (ii) from 63 to 75 percent by weight of a second polyethylene fraction, wherein the polyethylene composition has less than 0.10 branches per 1,000 carbon atoms when measured using 13 C NMR, wherein the density of the
  • polyethylene-based composition is at least 0.965 g/cm 3 , and wherein the melt index (I 2 ) of the polyethylene-based composition is 0.5 to 10 g/10 minutes.
  • the polyethylene composition may comprise a combination of two or more embodiments as described herein.
  • the polyethylene composition has a density of at least 0.965 g/cm 3 . In some embodiments, the polyethylene composition has a density of at least 0.968 g/cm 3 .
  • the polyethylene composition in some embodiments, has a density of up to 0.976 g/cm 3 . In some embodiments, the polyethylene composition has a density in the range of 0.965 to 0.976 g/cm 3 , for example from 0.965 to 0.970, or from 0.967 to 0.969, or from 0.965 to 0.970 g/cm 3 .
  • the density can be from a lower limit of 0.965 or 0.967 g/cm 3 , to an upper limit of 0.970, 0.972, 0.975, or 0.976 g/cm 3 .
  • the polyethylene composition has a melt index (I2 or 12; at 190°C / 2.16kg) from 0.5 to 10 g/10 minutes.
  • the melt index (L ⁇ or 12; at 190°C / 2.16 kg) can be from a lower limit of 0.5, 0.7, 0.9, 1.0, 1.1, 1.2, 1.5, 2, 3, 4, or 5 g/10 minutes, to an upper limit of 1.5, 2, 2.5, 3, 4, 5, 6, 7, 8, 9, or 10 g/10 minutes.
  • the polyethylene composition has a melt index (I 2 ) from 0.5 to 5 g/10 minutes, or from 0.5 to 2.5 g/10 minutes, or from 0.7 to 3 g/10 minutes, or from 1.0 to 2.0 g/10 minutes, or from 1.0 to 1.5 g/10 minutes.
  • the polyethylene composition has a melt index ratio (I 10 /I 2 ) of 10 or more.
  • the polyethylene composition has a melt index ratio (I 10 /I 2 ) of up to 17 in some embodiments.
  • the polyethylene composition has a melt index ratio (I 10 /I 2 ) of 10 to 17.
  • the polyethylene composition has a melt index ratio (I 10 /I 2 ) of 12 to 17 in some embodiments.
  • the polyethylene composition has low levels of branching.
  • the polyethylene composition has less than 0.10 branches per 1,000 carbon atoms when measured using 13 C NMR in some embodiments.
  • the polyethylene composition in some embodiments has less than 0.07 branches per 1,000 carbon atoms when measured using 13 C NMR.
  • the polyethylene composition has less than 0.05 branches per 1,000 carbon atoms when measured using 13 C NMR in some embodiments.
  • the polyethylene composition has less than 0.03 branches per 1,000 carbon atoms when measured using 13 C NMR.
  • the polyethylene composition has low levels of non-vinyl unsaturations.
  • the polyethylene composition has less than 25 nonvinyl unsaturations per 1 million carbons when measured using 1 H NMR.
  • the polyethylene composition in some anbodiments, has less than 20 non-vinyl unsaturations per 1 million carbons when measured using 1 H NMR .
  • the combination of low levels of branching and low levels of non-vinyl unsaturation in the polyethylene compositions provide a greater amount of crystallinity in the polyethylene compositions, thereby improving its barrier properties when formed into a film.
  • the polyethylene composition has a ZSVR value of less than 2.0, or from 1.0 to 2.0, or from 1.2 to 1.8, or from 1.3 to 1.7.
  • the polyethylene composition has a molecular weight distribution, expressed as the ratio of the weight average molecular weight to number average molecular weight (MVMn; as determined by conv. GPC) in the range of from 8.0 to 14.0.
  • M w /M n the molecular weight distribution
  • M w /M n the molecular weight distribution
  • the M w /M n is from 10.0 to 12.0.
  • the polyethylene composition has a number average molecular weight (Ma; as determined by conv. GPC) in the range from 8,000 to 20,000 g/mole.
  • Mo number average molecular weight
  • the number average molecular weight can be from a lower limit of 8,000, 9,000,
  • the polyethylene composition has a weight average molecular weight (M w ; as determined by conv. GPC) in the range from 100,000 to 125,000 g/mole.
  • the weight average molecular weight can be from a lower limit of 100,000, 105,000, or 110,000 g/mole, to an upper limit of 115,000, 120,000, or 124,000 g/mole.
  • the polyethylene composition has a z average molecular weight (Mzi as determined by conv. GPC) of at least 350,000 g/mole, such as in the range from 350,000 to 600,000 g/mole.
  • Mzi as determined by conv. GPC
  • the z average molecular weight can be from a Iowa limit of 350,000, 375,000, 400,000, 405,000, or 410,000 g/mole, to an upper limit of 420,000, 425,000, 450,000, 475,000, 500,000, 550,000, or 600,000 g/mole.
  • the polyethylene composition has a M z /M w ratio (each as determined by conv. GPC) of greater than 3.0.
  • the polyethylene composition has a MVM W ratio (each as determined by conv. GPC) of greater than 3.5 in some embodiments.
  • the M z /M w can be from 3.0 to 4.0 in some embodiments, or from 3.5 to 4.5 in some
  • the polyethylene composition has a ZSVR of less than 2.0 and a
  • the polyethylene compositions has a ZSVR of less than 2.0 and a M z M w ratio (each as determined by conv. GPC) of greater than 3.5.
  • the polyethylene composition preferably comprises ethylene-based polymers formed in the absence of comonomers. In some embodiments, the polyethylene composition comprises at least 99% by weight ethylene-based polymers formed in the absence of comonomers. In some embodiments, the polyethylene composition comprises at least 99% by weight polymers comprising a majority amount (>99 mol %) of units which have been derived from ethylene monomer.
  • polyethylene compositions used in polyethylene-based compositions of the present invention comprise two fractions of polyethylenes.
  • the first polyethylene fraction has a density of 0.935 to 0.947 g/cm 3 . In some embodiments, the first polyethylene fraction has a density of 0.940 to 0.947 g/cm 3 .
  • the first polyethylene fraction has a melt index (I 2 ) of less than 0.1 g/10 minutes. In some embodiments, the first polyethylene fraction has a melt index (I 2 ) of 0.01 g/10 minutes or greater.
  • the first polyethylene fraction has a melt index from 0.05 to 0.1 g/10 minutes in some embodiments.
  • the first polyethylene fraction in some embodiments, has less than 0.10 branches per 1,000 carbon atoms when measured using 13 C NMR.
  • the second polyethylene fraction has a density of 0.970 g/cm 3 or more.
  • the first polyethylene fraction has a density of 0.940 to 0.947 g/cm 3
  • the second polyethylene fraction has a density of 0.970 g/cm 3 or more.
  • the second polyethylene fraction has a melt index (I 2 ) of at least 100 g/10 minutes.
  • the second polyethylene fraction has a melt index (I 2 ) of at least 100 g/10 minutes and up to 10,000 g/10 minutes or more.
  • the second polyethylene fraction has a melt index (I 2 ) of at least 100 g/10 minutes and up to 10,000 g/10 minutes, in some embodiments-
  • the second polyethylene fraction has a melt index (I 2 ) of at least 100 g/10 minutes and up to 1,000 g/10 minutes, in some embodiments.
  • the ratio of the melt index (I 2 ) of the second polyethylene fraction to the melt index (I 2 ) of the first polyethylene fraction is at least 1,000.
  • the polyethylene composition comprises from 25 to 37 percent by weight of the first polyethylene fraction and from 63 to 75 percent by weight of the second polyethylene fraction, based on the total weight of the polyethylene composition. In some embodiments, the polyethylene composition comprises 30 to 37 percmt by weight of the first polyethylene fraction and 63 to 70 percmt by weight of the second polyethylene fraction, based on the total weight of the polyethylene composition.
  • the polyethylene-based ccxnposition comprises at least 97% by weight of the polyethylene composition, based on the total weight of the polyethylene-based ccxnposition. In some embodiments, the polyethylene-based ccxnposition comprises up to 99% by weight of the polyethylene composition, based on the total weight of the polyethylene-based composition. The polyethylene-based composition, in some embodiments, comprises from 97% to 98% by weight of the polyethylene composition, based on the total weight of the polyethylene-based composition.
  • Any conventional polymerization processes may be employed to produce the polyethylene composition.
  • Such conventional polymerization processes include, but are not limited to, slurry polymerization processes, solution polymerization process, using one or more conventional reactors e.g. loop reactors, isothermal reactors, stirred tank reactors, batch reactors in parallel, series, and/or any combinations thereof.
  • the polyethylene composition may, for example, be produced via solution phase polymerization process using one or more loop reactors, isothermal reactors, and combinations thereof.
  • the solution phase polymerization process occurs in one or more well- mixed reactors such as one or more isothermal loop reactors or one or more adiabatic reactors at a temperature in the range of from 115 to 250°C; for example, from 115 to 200°C, and at pressures in the range of from 300 to 1,000 psi; for example, from 400 to 750 psi.
  • the temperature in the first reactor is in the range of from 115 to 190 °C, for example, from 115 to 175°C
  • the second reactor temperature is in the range of 150 to 250°C, for example, from 130 to 165°C.
  • the temperature in the reactor is in the range of from 115 to 250°C, for example, from 115 to 225°C.
  • the residence time in solution phase polymerization process may be in the range of from 2 to 30 minutes; for example, from 10 to 20 minutes.
  • Ethylene, solvent, hydrogen, one or more catalyst systems, optionally one or more cocatalysts, and optionally one or more comonomers are fed continuously to one or more reactors.
  • Exemplary solvents include, but are not limited to, isoparaffins.
  • such solvents are commercially available under the name ISOPAR E from ExxonMobil Chemical Co., Houston, Texas.
  • solvent recovery unit i.e. heat exchangers and vapor liquid separator drum
  • the polyethylene composition may be produced via solution polymerization in a dual reactor system, for example a dual loop reactor system, wherein ethylene is polymerized in the presence of one or more catalyst systems. In some embodiments, only ethylene is polymerized. Additionally, one or more cocatalysts may be present. In another embodiment, the polyethylene composition may be produced via solution polymerization in a single reactor system, for example a single loop reactor system, wherein ethylene is polymerized in the presence of two catalyst systems. In some embodiments, only ethylene is polymerized.
  • R groups such as, R 1 , R 2 , R 3 , R 4 , and R 5 can be identical or different (e.g., R 1 , R 2 , R 3 , R 4 , and R 5 may all be substituted alkyls or R 1 and R 2 may be a substituted alkyl and R 3 may be an aryl, etc.).
  • Use of the singular includes use of the plural and vice versa (e.g., a hexane solvent, includes hexanes).
  • a named R group will generally have the structure that is recognized in the art as corresponding to R groups having that name.
  • procatalyst refers to a compound that has catalytic activity when combined with an activator.
  • activator refers to a compound that chemically reacts with a procatalyst in a manner that converts the procatalyst to a catalytically active catalyst.
  • terns“co-catalyst” and“activator” are interchangeable terms.
  • a parenthetical expression having the form“(C x -C y )" means that the unsubstituted form of the chemical group has from x carbon atoms to y carbon atoms, inclusive of x and y.
  • a (C 1 -C 40 )alkyl is an alkyl group having from 1 to 40 carbon atoms in its unsubstituted form.
  • certain chemical groups may be substituted by one or more substituents such as R s .
  • R s substituted version of a chemical group defined using the“(C x -C y )" parenthetical may contain more than y carbon atoms depending on the identity of any groups R s .
  • a“(C 1 -C 40 )alkyl substituted with exactly one group R s where R s is phenyl (-C 6 H 5 )" may contain from 7 to 46 carbon atoms.
  • the minimum and maximum total number of carbon atoms of the chemical group is determined by adding to both x and y the combined sum of the number of carbon atoms from all of the carbon atom-containing substituents R s .
  • substitution means that at least one hydrogen atom (-H) bonded to a carbon atom or heteroatom of a corresponding unsubstituted compound or function group is replaced by a substituent (e.g. R 8 ).
  • persubstitution means that every hydrogen atom (H) bonded to a carbon atom or heteroatom of a corresponding unsubstituted compound or functional group is replaced by a substituent (e.g., R s ).
  • “polysubstitution” means that at least two, but fewer than all, hydrogen atoms bonded to carbon atoms or heteroatoms of a corresponding unsubstituted compound or functional group are replaced by a substituent
  • “-H” means a hydrogen or hydrogen radical that is covalently bonded to another atom.“Hydrogen” and“-H” are interchangeable, and unless clearly specified mean the same thing.
  • (C 1 -C 40 )hydrocarbyl means a hydrocarbon radical of from 1 to 40 carbon atoms and the term“(C 1 -C 40 )hydrocarbylene” means a hydrocarbon diradical of from 1 to 40 carbon atoms, in which each hydrocarbon radical and each hydrocarbon diradical is aromatic or non-aromatic, saturated or unsaturated, straight chain or branched chain, cyclic (including mono- and poly-cyclic, fused and non-fused polycyclic, including bicyclic; 3 carbon atoms or more) or acyclic and is unsubstituted or substituted by one or more R s .
  • a (C 1 -C 40 )hydrocarbyl can be an unsubstitnted or substituted (C 1 -C 40 )alkyl, (C 3 -C 40 )cycloalkyl, (C 3 -C 20 )cycloalkyl-(C 1 -C 20 )alkylene, (C 6 -C 40 )aryl, or (C 6 -C 20 )aryl-(C 1 -C 20 )alkylene.
  • (C 1 -C 40 )hydrocaibyl groups has a maximum of 20 carbon atoms (i.e., (C 1 -C 20 hydrocarbyl) and other embodiments, a maximum of 12 carbon atoms.
  • (C 1 -C 40 )alkyl and“(C 1 -C 18 )alkyl” mean a saturated straight or branched hydrocarbon radical of from 1 to 40 carbon atoms or from 1 to 18 carbon atoms, respectively, that is unsubstituted or substituted by one or more RS.
  • Examples of unsubstituted (C 1 -C 40 )alkyl are unsubstituted (C 1 -C 20 )alkyl; unsubstituted (C 1 -C 10 )alkyl; unsubstituted (C 1 -C 5 )alkyl; methyl; ethyl; 1-propyl; 2-propyl; 1-butyl; 2-butyl; 2- methylpropyl; 1,1-dimethylethyl; 1-pentyl; 1-hexyl; 1-heptyl; 1-nonyl; and 1-decyl.
  • substituted (C 1 -C 40 )alkyl are substituted (C 1 -C 20 )alkyl, substituted
  • (C 1 -C 10 )alkyl trifhioromethyl, and [C 45 ] alkyl.
  • the term“[C 45 ]alkyl” (with square brackets) means there is a maximum of 45 carbon atoms in the radical, including substituents, and is, for example, a (C 27 — C 40 )alkyl substituted by one R s , which is a (C 1 -C 5 )alkyl, respectively.
  • Each (C 1 -C 5 )alkyl may be methyl, trifluoromethyl, ethyl, 1-propyl, 1-methylethyl, or 1,1- dimethylethyl.
  • (C 6 -C 40 )aryl means an unsubstituted or substituted (by one or more R s ) mono-, bi- or tricyclic aromatic hydrocarbon radical of from 6 to 40 carbon atoms, of which at least from 6 to 14 of the carbon atoms are aromatic ring carbon atoms, and the mono-, bi- or tricyclic radical comprises 1, 2, or 3 rings, respectively; wherein the 1 ring is aromatic and the 2 or 3 rings independently are fused or non-fused and at least one of the 2 or 3 rings is aromatic.
  • Examples of unsubstituted (C 6 -C 40 )aryl are unsubstituted (C 6 -C 20 )aryl unsubstituted (C 6 -C 18 )aryl; 2-(C 1 -C 5 )alkyl-phenyl; 2,4-bis(C 1 -C 5 )alkyl-phenyl; phenyl; fluorenyl; tetrahydrofluorenyl; indacenyl; hexahydroindacenyl; indenyl; dihydroindenyl; naphthyl; tetrahydronaphthyl; and phenanthrene.
  • Examples of substituted (C 6 -C 40 )aryl are substituted (C 1 -C 20 )aryl; substituted (C 6 -C 18 )aryl; 2,4-bis[(C 20 )alkyl]-phenyl;
  • (C 3 -C 40 )cycloalkyl means a saturated cyclic hydrocarbon radical of from 3 to 40 carbon atoms that is unsubstituted or substituted by one or more R s .
  • Other cycloalkyl groups e.g., (C x -C y )cycloalkyl are defined in an analogous manner as having from x to y carbon atoms and being cither unsubstituted or substituted with one or more R s .
  • Examples of unsubstituted (C 3 -C 40 )cycloalkyl are unsubstituted (C 3 -C 20 )cycloa]kyl, unsubstituted (C 3 -C 10 )cycloalkyl, cyclopropyl, cyclobutyl, cyclopentyl, cyclohexyl, cycloheptyl, cyclooctyl, cyclononyl, and cyclodecyl.
  • (C 3 -C 40 )cycloalkyl are substituted (C 3 -C 20 )cycloalkyl, substituted (C 3 -C 10 )cycloalkyl, cyclopentanon-2-yl, and 1-fluorocyclohexyl.
  • Examples of (C 1 -C 40 )hydrocarbylene include unsubstituted or substituted
  • the diradicals are on the same carbon atom (e.g., -CHr-) or on adjacent carbon atoms (i.e., 1,2- diradicals), or are spaced apart by one, two, or more than two intervening carbon atoms (e.g., respective 1,3-diradicals, 1,4-diradicals, etc.).
  • Some diradicals include a,w-diradical.
  • the a,w-diradical is a diradical that has maximum carbon backbone spacing between the radical carbons.
  • (C 2 -C 20 )alkylene a,w- diradicals include ethan-l,2-diyl (i.e. -CH 2 CH 2 -), propan- 1,3-diyl (i.e. -CH 2 CH 2 CH 2 -), 2- mcthylpropan- 1 ,3-diyl (i.e. -CH 2 CH(CH 3 )CH 2 -) .
  • Some examples of (C 6 -C 50 )arylene a,w- diradicals include phenyl- 1,4-diyl, napthalen-2,6-diyl, or napthalen-3,7-diyl.
  • (C 1 -C 40 )a]kylene means a saturated straight chain or branched chain diradical (i.e., the radicals are not on ring atoms) of from 1 to 40 carbon atoms that is unsubstituted or substituted by one or more R s .
  • unsubstituted (C 1 -C 50 )alkylene examples include unsubstituted (C 1 -C 20 )alkylene, including unsubstituted -CH 2 CH 2 -, -(CH 2 ) 3 -, -(CH 2 ) 4 -,— (CH 2 ) 5 — , -(CH 2 ) 6 -, -(CH 2 )7-, -(CH 2 ) 8 -, -CH 2 C*HCH 3 , and
  • (C 1 -C 50 )alkylene are substituted (C 1 -C 20 )alkylene, -CF 2 -, -C(O)-, and
  • substituted (C 1 -C 50 )alkylene also include l,2-bis(methylene)cyclopentane, 1,2- bis(methylene)cyclohexane, 2,3-bis(methylene)-7,7-dimethyl-bicyclo[2.2.1]heptane, and 2,3- bis (methylene)bicyclo [2.2.2] octane.
  • (C 3 -C 40 )cycloalkylene means a cyclic diradical (i.c., the radicals are on ring atoms) of from 3 to 40 carbon atoms that is unsubstituted or substituted by one or more
  • heteroatom refers to an atom other than hydrogen or carbon.
  • heterohydrocarbon refers to a molecule or molecular framework in which one or more carbon atoms are replaced with a heteroatom.
  • (C 1 -C 40 )heterohydrocarbyl means a heterohydrocarbon radical of from 1 to 40 carbon atoms and the term“(C 1 -C 40 )heterohydrocarbylene” means a heterohydrocarbon diradical of from 1 to 40 carbon atoms, and each heterohydrocarbon has one or more heteroatoms.
  • the radical of the heterohydrocaibyl is on a carbon atom or a heteroatom, and diradicals of the heterohydrocaibyl may be on: (1) one or two carbon atom, (2) one or two heteroatoms, or (3) a carbon atom and a heteroatom.
  • (C 1 -C 50 )heterohy drocarbylene may be unsubstituted or substituted (by one or more R s ), aromatic or non-aromatic, saturated or unsaturated, straight chain or branched chain, cyclic (including mono- and poly-cyclic, fused and non-fused polycyclic), or acyclic.
  • the (C 1 -C 40 )hetcrohydrocarbyl may be unsubstituted or substituted
  • (C 4 -C 40 )heteroaryl means an unsubstituted or substituted (by one or more R s ) mono-, bi- or tricyclic heteroaromatic hydrocarbon radical of from 4 to 40 total carbon atoms and from 1 to 10 heteroatoms, and the mono-, bi- or tricyclic radical comprises 1, 2 or 3 rings, respectively, wherein the 2 or 3 rings independently are fused or non-fused and at least one of the 2 or 3 rings is heteroaromatic.
  • heteroaryl groups c.g., (C x -C y )heteroaryl generally, such as (C 4 -C 12 )heteroaryl
  • the monocyclic heteroaromatic hydrocarbon radical is a 5-membered or 6-membered ring.
  • the 5-membered ring has 5 minus h carbon atoms, wherein h is the number of heteroatoms and may be 1, 2, or 3;and each heteroatom may be O, S, N, or P.
  • Examples of 5-membered ring heteroaromatic hydrocarbon radical are pyrrol- 1-yl; pyrrol-2-yl; furan-3-yl; thiophen-2-yl; pyrazol-l-yl; isoxazol-2-yl; isothiazol-5-yl; inridazol-2-yl; oxazol-4-yl; thiazol-2-yl; 1,2,4-triazol-l-yl; l,3,4-oxadiazol-2-yl; l,3,4-thiadiazol-2-yl ⁇ , tetrazol-l-yl; tetrazol-2-yl; and tetrazol-5-yl.
  • the 6-membered ring has 6 minus h carbon atoms, wherein h is the number of heteroatoms and may be 1 or 2 and the heteroatoms may be N or P.
  • 6-membered ring heteroaromatic hydrocarbon radical are pyridine-2-yl; pyrimidin-2-yl; and pyrazin-2-yl.
  • the bicyclic heteroaromatic hydrocarbon radical can be a fused 5,6- or 6,6-ring system.
  • Examples of the fused 5,6-ring system bicyclic heteroaromatic hydrocarbon radical are indol-l-yl; and benzimidazole-l-yl.
  • Examples of the fused 6,6-ring system bicyclic heteroaromatic hydrocarbon radical are quinolin-2-yl; and isoquinolin-l-yl.
  • the tricyclic heteroaromatic hydrocarbon radical can be a fused 5,6,5-; 5,6,6-; 6,5,6-; or 6,6,6-ring system.
  • An example of the fused 5,6,5-ring system is 1 ,7-dihydropyrrolo[3,2-f]indol- 1 -yl.
  • An example of the fused 5,6,6-ring system is lH-benzo[f] indol-l-yl.
  • An example of the fused 6,5,6-ring system is 9H-carbazol-9-yl.
  • An example of the fused 6,5,6- ring system is 9H-carbazol-9-yl.
  • An example of the fused 6,6,6-ring System is acrydin-9-yl.
  • heteroalkyl may be saturated straight or branched chain radicals containing (C 1 -C 50 ) carbon atoms, or fewer carbon atoms and one or more of the heteroatoms.
  • heteroalkylene may be saturated straight or branched chain diradicals containing from 1 to 50 carbon atoms and one or more than one heteroatoms.
  • the heteroatoms may include Si(R C ) 3 , Ge(R C ) 3 , Si(R C ) 2 , Ge(R C ) 2 , P(R P ) 2 , P(R P ), N(R N ) 2 , N(R N ), N, O, OR C , S, SR C , S(O), and S(O) 2 , wherein each of the heteroalkyl and heteroalkylene groups are unsubstituted or substituted by one or more R s .
  • halogen atom or“halogen” means the radical of a fluorine atom (F), chlorine atom (Cl), bromine atom (Br), or iodine atom (I).
  • halide means anionic form of the halogen atom: fluoride (F-), chloride (Cl-), bromide (Br-), or iodide (I-).
  • saturated means lacking carbon-carbon double bonds, carbon-carbon triple bonds, and (in heteroatom-containing groups) carbon-nitrogen, carbon-phosphorous, and carbon- silicon double bonds. Where a saturated chemical group is substituted by one or more substituents R s , one or more double and/or triple bonds optionally may or may not be present in substituents R s .
  • unsaturated means containing one or more carbon- carbon double bonds, carbon-carbon triple bonds, and (in heteroatom-containing groups) carbon-nitrogen, carbon-phosphorous, and carbon-silicon double bonds, not including any such double bonds that may be present in substituents R s , if any, or in (hetero) aromatic rings, if any.
  • a catalyst system for producing a polyethylene composition includes a metal-ligand complex according to formula (I):
  • M is a metal chosen from titanium, zirconium, or hafnium, the metal being in a formal oxidation state of +2, +3, or +4; n is 0, 1, or 2; when n is 1, X is a monodentate ligand or a bidentate ligand; when n is 2, each X is a monodentate Hgand and is the same or different; the metal-ligand complex is overall charge-neutral; each Z is independently chosen from -0-, -S-, -N(R N )-, or -P(R P )-; L is (C 1 -C 40 )hydrocarbylene or (C 1 -C 40 )heterohydrocarbylene, wherein the (C 1 -C 40 )hydrocarbylene has a portion that comprises a 1 -carbon atom to 10-carbon atom linker backbone linking the two Z groups in Formula (I) (to which L is bonded) or the (C 1 -C 40 ).
  • (C 1 -C 40 )heterohydrocarbylene independently is a carbon atom or heteroatom, wherein each heteroatom independently is O, S, S(O), S(O) 2, Si(R C ) 2 , Ge(R C ) 2 , P(R C ), or N(R C ), wherein independently each R C is (C 1 -C 30 )hydrocaibyl or (C 1 -C 30 )heteohydrocarbyl; R 1 and R 8 are independently selected from the group consisting of -H, (C 1 -C 40 )hydrocarbyl,
  • each of R 2 " 4 , R 5-7 , and R 9-16 is independently selected from
  • the polyethylene composition is formed using a first catalyst according to formula (I) in a first reactor and a different catalyst according to formula (I) in a second reactor.
  • the procatalyst used in the first loop is zirconium, [[2,2”’-[[bis[l- methylethyl)germylene]bis(methyleneoxy-kO)]bis[3’’,5,5” -tris(l , 1 -dimethylethyl)-5’ - octyl[l,l’:3’,l”-terphenyl]-2’-olato-kO]](2-)]dimethyl-, having the chemical formula C 86 H 128 F 2 GeO 4 Zr and the following structure:
  • the procatalyst used in the second loop is zirconium, [[2,2”’-[l,3- propanediyIbis(oxy-KO)]bis [3- [2,7-bis( 1 , 1 -dimethylethyl)-9H-carbazol-9-yl]]-5’ - (dimethyloctylsilyl)-3’ -methyl-5- (1 ,1,3,3- tetramethylbutyl) [ 1 , l]-biphenyl]-2-olato-KO]](2- )] dimethyl, having the chemical formula C 107 H 154 N 2 O 4 Si 2 Zr ⁇ and the following structure:
  • the catalyst system comprising a metal-ligand complex of formula (I) may be rendered catalytically active by any technique known in the art for activating metal-based catalysts of olefin polymerization reactions.
  • the system comprising a metal- ligand complex of formula (I) may be rendered catalytically active by contacting the complex to, or combining the complex with, an activating co-catalyst.
  • Suitable activating co-catalysts for use herein include alkyl aluminums; polymeric or oligomeric alumoxanes (also known as aluminoxanes); neutral Lewis adds; and non-polymeric, non-coordinating, ion-forming compounds (including the use of such compounds under oxidizing conditions).
  • a suitable activating technique is bulk electrolysis. Combinations of one or more of the foregoing activating co-catalysts and techniques are also contemplated.
  • the term“alkyl aluminum” means a monoalkyl aluminum dihydride or monoalkylauminum dihalide, a dialkyl aluminum hydride or dialkyl aluminum halide, or a trialkylaluminum.
  • Examples of polymeric or oligomeric alumoxanes include methylalumoxane, triisobutylaluminum- modified methylalumoxane, and isobutylalumoxane.
  • Lewis add activates include Group 13 metal compounds containing from 1 to 3 (C 1 -C 20 )hydrocarbyl substituents as described herein.
  • Group 13 metal compounds are tri((C 1 -C 20 )hydrocarbyl)-substituted-alummum or tri((C 1 -C 20 )hydrocarbyl)-boron confounds,
  • Group 13 metal compounds are tri(hydrocaibyl)-substituted-aluminum, tri((C i-C2o)hydrocarbyl)-boron compounds, tri((C 1 -C 10 )alkyl)aluminum, tri((C 6 -C 18 )aryl)boron compounds, and halogenated (including perhalogenated) derivatives thereof.
  • Group 13 metal compounds are tris(fluoro- substituted phenyl)boranes,
  • the activating co-catalyst is a tris((C 1 -C 20 )hydrocarbyl borate (e.g. trityl tetrafluoroborate) or a
  • ammonium means a nitrogen cation that is a ((C 1 -C 20 )hydrocarbyl).iN + a
  • each (Ci-Cao)hydrocarbyl when two or more are present, may be the same or different
  • Combinations of neutral Lewis add activators include mixtures comprising a combination of a tri((C 1 -C 4 )alkyl)aluminum and a halogenated
  • tri((C 6 -C 18 )aiyl)boron compound especially a tris(pentafluorophenyl)borane.
  • Other embodiments are combinations of such neutral Lewis acid mixtures with a polymeric or oligomeric alumoxane, and combinations of a single neutral Lewis arid, especially tris(pentafluorophenyl)borane with a polymeric or oligomeric alumoxane.
  • Ratios of numbers of moles of (metal-ligand complex) (tris(pentafhioro-phenylborane):
  • (alumoxane) [e.g., (Group 4 metal-ligand complex) :(tris(pentafluoro- phenylborane) : (alumoxane)] are from 1:1:1 to 1:10:30, in other embodiments, from 1:1:1.5 to 1:5:10.
  • the catalyst system comprising the metal-ligand complex of formula (I) may be activated to form an active catalyst composition by combination with one or more co- catalysts, for example, a cation forming co-catalyst, a strong Lewis add, or combinations thereof.
  • Suitable activating co-catalysts include polymeric or oligomeric aluminoxanes, especially methyl aluminoxane, as well as inert, compatible, noncoordinating, ion forming compounds.
  • Exemplary suitable co-catalysts include, but are not limited to: modified methyl aluminoxane (MMAO), bis(hydrogenatcd tallow alkyl)methyl,
  • one or more of the foregoing activating co-catalysts are used in combination with each other.
  • An especially preferred combination is a mixture of a tri((C 1 -C 4 )hydrocarbyl)alummum, tri((C 1 -C 4 )hydrocarbyl)borane, or an ammonium borate with an oligomeric or polymeric alumoxane compound.
  • the ratio of total number of moles of one or more metal-ligand complexes of formula (I) to total number of moles of one or more of the activating co-catalysts is from 1:10,000 to 100:1.
  • the ratio is at least 1:5000, in some other embodiments, at least 1:1000; and 10:1 or less, and in some other embodiments, 1:1 or less.
  • the number of moles of the alumoxane that are employed is at least
  • the number of moles of the tris(pentafluorophenyl)borane that are employed to the total number of moles of one or more metal-ligand complexes of formula (I) from 0.5: 1 to 10:1, from 1:1 to 6:1, or from 1:1 to 5:1.
  • the remaining activating co-catalysts are generally employed in approximately mole quantities equal to the total mole quantities of one or more metal-ligand complexes of formula (I).
  • the polyethylene-based compositions of the presort invention further comprise a calcium salt of 1,2-cyclohexanedicarboxylic acid.
  • the calcium salt of 1,2- cyclohexanedicarboxylic acid is a type of nucleator that, when used in the appropriate amount and in combination with the polyethylene compositions described herein, has bear found to provide a significant improvement in moisture barrier for films formed from the polyethylene-based compositions (i.e., a reduction in the amount of moisture transmitted through the film).
  • the amount of calcium salt of 1,2-cyclohexanedicarboxylic add used in the polyethylene-based composition is important in providing the desired moisture barrier performance (i.e., a reduction in the amount of moisture transmitted through the film).
  • the polycthylene-based composition comprises 90 to 540 ppm of calcium salt of 1,2- cyclohexanedicaiboxylic add, based on the total weight of the polyethylene-based composition.
  • the polyethylene-based composition comprises 150 to 525 ppm of calrium salt of 1 ,2-cyclohexanedicaiboxylic add, based on the total weight of the polyethylene-based composition.
  • the polyethylene-based composition comprises 165 to 495 ppm of calrium salt of 1 , 2-cyclohexanedicaiboxylic arid, based on the total weight of the polyethylene-based composition.
  • the calrium salt of 1 ,2-cyclohexanedicaiboxyHc arid may be provided with a fatty arid metal salt such as zinc stearate, zinc palmitate, and mixtures thereof. Based on how zinc stearate is prepared commercially, some zinc palmitate may also be present as commercial stearic arid often contains a substantial amount of palmitic arid.
  • the polyethylene-based composition comprises 45 to 360 ppm of at least one of zinc stearate and zinc palmitate, based on the total weight of the polyethylene-based composition. In some embodiments, the polyethylene-based composition comprises 50 to 275 ppm of zinc stearate and/or zinc palmitate, based on the total weight of the polyethylene-based composition. In some embodiments, the
  • polyethylene-based composition comprises 85 to 255 ppm of zinc stearate and/or zinc palmitate, based on the total weight of the polyethylene-based composition.
  • calrium salt of 1 ,2-cyclohexanedicaiboxylic arid that can be used in embodiments of the present invention is Hyperform HPN-2QE from Milliken
  • Hyperform HPN-20E comprises 60-70 weight percent of calrium salt of 1, 2-cyclohexanedicaiboxylic arid and 30-40 weight percent of zinc stearate/zinc palmitate
  • the polyethylene-based composition comprises 150 to 800 ppm of Hyperform HPN-20E based on the total weight of the polyethylene-based composition.
  • the polyethylene-based composition in some embodiments, comprises 250 to 750 ppm of Hyperform HFN-20E based on the total weight of the polyethylene-based composition.
  • the calrium salt of 1 ,2-cyclohexanedicaiboxyHc arid (and the fatty arid metal salt (e.g., zinc stearate and/or zinc palmitate) when also included) can be provided as a masteibatch by blending it with a carrier resin before combining with the polyethylene compositions described herein.
  • the carrier resin is a polyethylene having a melt index (I 2 ) of 4 to 12 g/10 minutes.
  • the masterbatch comprises 2 to 4 weight percent of the calcium salt of 1 ,2-cyclohexanedicarboxylic acid and zinc stearate/zinc palmitate, based on the total weight of the masterbatch.
  • the carrier resin is a narrow molecular weight distribution high density polyethylore homopolyma having a density of 0.965 and a melt index (I 2 ) of 8 to 9 g/10 minutes.
  • the mastobatch can include other additives as well. Depending on the total amount of additives included, the mastobatch can comprise 85 to 98 weight pocort of the carrio resin, based on the total weight of the masterbatch.
  • the polyethylene composition furtho comprises silica.
  • Silica when used in the appropriate amount and in combination with the polyethylene compositions described herein, has beat found to provide a reduced level of dusting in films formed from the polyethylene-based compositions.
  • the amount of silica used in the polyethylene-based composition can be important in reducing the level of dusting when the polyethylene-based composition is incorporated into a surface layer of a film.
  • the polyethylene-based composition comprises 75 to 800 ppm silica, based on the total weight of the polyethylene-based composition. In some embodiments, the polyethylene-based composition comprises 100 to 500 ppm of silica, based on the total weight of the polyethylene-based composition.
  • silica that can be used in embodiments of the presort invention is Sylobloc 45 commercially available from Grace Davison Company.
  • talc can be used in addition to, or as an alternative to, silica.
  • the siHca can be provided as a mastobatch by blending it with a carrier resin, the calcium salt of 1 ,2-cyclohexanedicarboxylic acid, and zinc stearate/zinc palmitate before combining with the polyethylene compositions described herein.
  • the masterbatch can be as described above in connection with the calcium salt of 1 ,2-cyclohexanedicarboxylic acid and zinc stearate/zinc palmitate.
  • the amount of silica in the mastobatch can be based on the target silica for the overall polyethylene-based composition.
  • the presort invartion relates to a film formed from any of the inventive polyethylene-based compositions as described herein.
  • the polyethylene-based compositions when incorporated into a film, provide improved moisture vapor barrier.
  • the film when the polyethylene-based composition is incorporated into a monolayer film, the film exhibits a WVTR of 0.15 or less (g-mil)/( 1 OOin 2 ⁇ day) when measured according to ASTM F1249-06 at 38° C and 100% relative humidity.
  • the film when the polyethylene-based composition is incorporated into a monolayer film, the film exhibits a WVTR of 0.10 or less (g- mil)/(l OOin 2 ⁇ day) when measured according to ASTM F1249-06 at 38° C and 100% relative humidity.
  • the film when incorporated into a monolayer film or a surface layer of a multilayer film, the film can exhibit a desirable (i.e., low) level of dusting.
  • a low level of dusting is advantageous during the film fabrication as well as film conversion to other articles.
  • lower dusting also helps in better print retention on the article.
  • a multilayer film can include a polyethylene-based composition of the present invention in a surface layer and also in an inner laya.
  • the multilayer film may be significantly simplified in terms of the number of different polymers incorporated in the multilayer film.
  • the film is a blown film.
  • die film is a monolaya film.
  • the film in some anbodiments, is a mnltilaya film. Films can be formed from the inventive polyethylene-based compositions using methods and equipment well- known to those of skill in the art
  • the amount of the polyethylene-based composition to use in films of the present invention can depend on a number of factors including, for example, whetha the film is a monolaya or multilayer film, the other layers in the film if it is a multilayer film, the desired barria properties of the film, the aid use application of the film, and others.
  • the inventive polyethylene-based composition can be provided in a single layer to provide a barria property.
  • Films of the present invention can have a variety of thicknesses.
  • the thickness of the blown film can depend on a number of factors including, for example, whether the film is a monolayer or multilayer film, the other layers in the film if it is a multilayer film, the desired properties of the film, the end use application of the film, the equipment available to manufacture the film, and others.
  • a film of the present invention has a thickness of up to 10 mils.
  • the blown film can have a thickness from a lower limit of 0.25 mils, 0.5 mils, 0.7 mils, 1.0 mil, 1.75 mils, or 2.0 mils to an upper limit of 4.0 mils, 6.0 mils, 8.0 mils, or 10 mils.
  • the number of layers in the film can depend on a number of factors including, for example, the desired properties of the film, the desired thickness of the film, the content of the other layers of the film, the end use application of the film, the equipment available to manufacture the film, and others.
  • a multilayer blown film can comprise up to 2, 3, 4, 5, 6, 7, 8, 9, 10, or 11 layers in various embodiments.
  • the inventive polyethylene-based composition in some embodiments, can be used in more than one layer of the film.
  • Other layers within a multilayer film of the present invention can comprise, in various embodiments, a polymer selected from the following: the inventive composition, a LLDPE, a VLDPE (a very low density polyethylene), a MORE, a LDFE, a HOPE, a HMWHDFE (a high molecular weight HOPE), a propylene- based polymer, a polyolefin plastomer (POP), a polyolefin elastomer (POE), an olefin block copolymer (OBC), an ethylene vinyl acetate, an ethylene acrylic acid, an ethylene methacrylic acid, an ethylene methyl acrylate, an ethylene ethyl acrylate, an ethylene butyl acrylate, an isobutylene, a maleic anhydride-grafted polyolefin, an ionomer of any of
  • any of the foregoing layers can further comprise one or more additives as known to those of skill in the art such as, for example, antioxidants, ultraviolet light stabilizers, thermal stabilizers, slip agents, antiblock, pigments or colorants, processing aids, crosslinking catalysts, flame retardants, fillers and foaming agents,
  • the polyethylene-based composition comprises up to 3 weight percent of such additional additives. All individual values and subranges from 0 to 3 wt% are included and disclosed herein; for example, the total amount of additives in the polymer blend can be from a lower limit of 0.5, 1, 1.5, 2, 2.5, 3, 3.5, 4, or 4.5 wt% to an upper limit of 1, 2, 3, 4, or 5 wt%.
  • the inventive polyethylene-based compositions can be incorporated into multilayer films and articles that are comprised primarily, if not substantially or entirely, of polyolefins in order to provide a film and articles that is more easily recyclable.
  • the polyethylene-based compositions of the present invention are particularly advantageous in proving films wherein the film is formed primarily from polyolefins such as polyethylene and/or polypropylene.
  • a coated film wherein the film comprises primarily polyethylene or polypropylene has an improved recyclability profile in addition to other advantages that the usage of such polymers may provide.
  • the film comprises 95 weight percent or more polyethylene based on the total weight of the film.
  • the film comprises 96 weight percent or more, 97 weight percent or more, 98 weight percent or more, or 99 weight percent or more polyethylene based on the total weight of the film.
  • the film comprising a layer formed from the inventive polyethylene-based composition can be laminated to another film.
  • Films of the present invention can be corona treated and/or printed (e.g., reverse or surface printed) using techniques known to those of skill in the art.
  • films of the present invention can be oriented, uniaxially (e.g., in the machine direction) or biaxially using techniques known to those of skill in the art
  • Embodiments of the present invention also relate to articles, such as packages, formed from or incorporating polyethylene-based compositions of the present invention (or films incorporating polyethylene-based compositions of the present invention).
  • packages can be formed from any of the polyethylene-based compositions of the present invention (or films incorporating polyethylene-based compositions of the present invention) described herein.
  • Polyethylene-based compositions of the present invention are particularly useful in articles where a Mgh water vapor barrier is desired.
  • Examples of such articles can include flexible packages, pouches, stand-up pouches, and pre-made packages or pouches.
  • multilayer films or laminates of the present invention can be used for food packages.
  • Examples of food that can be included in such packages include meats, cheeses, cereal, nuts, juices, sauces, and others.
  • Such packages can be formed using techniques known to those of skill in the art based on the teachings herein and based on the particular use for the package (e.g., type of food, amount of food, etc.).
  • the WVTR of a film is measured with a Mocon W3/33 according to ASTM F1249- 06 at 38° C, 100% relative humidity, and a thickness of -50 microns.
  • a GPC-IR high temperature chromatographic system from PolymerChar (Valencia, Spain), is equipped with a Precision Detectors (Amherst, MA), 2-angle laser light scattering detector Model 2040, an IRS infra-red detector and a 4-capillary viscometer, both from PolymeiChar. Data collection is performed using PolymeiChar Instrument Control software and data collection interface.
  • the system is equipped with an on-line, solvent degas device and pumping system from Agilent Technologies (Santa Gara, CA).
  • Injection temperature is controlled at ISO degrees Celsius.
  • the columns used are three, 10-micron“Mixed-B” columns from Polymer Laboratories (Shropshire, UK).
  • the solvent used is 1,2,4-trichlorobenzene.
  • the samples are prepared at a concentration of“0.1 grams of polymer in 50 milliliters of solvent”
  • the chromatographic solvent and the sample preparation solvent each contained“200 ppm of butylated hydroxytoluene (BHT).” Both solvent sources are nitrogen sparged. Ethylene-based polymer samples are stirred gently at 160 degrees Celsius for three hours.
  • the injection volume is“200 microliters,’ and the flow rate is“1 nrilHliters/mmute.”
  • the GPC column set is calibrated by running 21“narrow molecular weight distribution” polystyrene standards.
  • the molecular weight (MW) of the standards ranges from 580 to 8,400,000 g/mole, and the standards are contained in six “cocktail” mixtures. Each standard mixture has at least a decade of separation between individual molecular weights.
  • the standard mixtures are purchased from Polymer Laboratories.
  • the polystyrene standards are prepared at“0.025 g in 50 mL of solvent” for molecular weights equal to, or greater than, 1 ,000,000 g/mole, and at“0.050 g in 50 mL of solvent” for molecular weights less than 1,000,000 g/mole.
  • the polystyrene standards are dissolved at 80°C, with gentle agitation, for 30 minutes.
  • the narrow standards mixtures are run first, and in onto of decreasing“highest molecular weight component," to minimize degradation.
  • the polystyrene standard peak molecular weights are converted to polyethylene molecular weight using Equation 1 (as described in Williams and Ward, J. Polym. Sci, Polym. Letters, 6, 621 (1968)):
  • M is the molecular weight
  • A is equal to 0.4316 and B is equal to 1.0.
  • Number-average molecular weight (Mn(conv gpc)), weight average molecular weight (Mw-conv gpc), and z-average molecular weight (Mz(conv gpc)) are calculated according to Equations 2-4 below.
  • RV column retention volume (lineariy-spaced), collected at “1 point per second”
  • IR the baseline- subtracted IR detector signal, in Volts, from the IRS measurement channel of the GPC instrument
  • MPE polyethylene-equivalent MW detennined from Equation 1. Data calculation are performed using“GPC One software (version 2.013H)” from PolymerChar.
  • Zero-shear viscosities are obtained via creep tests, which are conducted on an AR G2 stress controlled rheometer (TA Instruments; New Castle, Del), using“25-mm- diameter” parallel plates, at 190°C.
  • the rheometer oven is set to test temperature for at least 30 minutes, prior to zeroing the fixtures.
  • a compression molded sample disk is inserted between the plates, and allowed to come to equilibrium for five minutes.
  • the upper plate is then lowered down to 50 pm (instrument setting) above the desired testing gap (1.5 mm). Any superfluous material is trimmed off, and the upper plate is lowered to the desired gap. Measurements are done under nitrogen purging, at a flow rate of 5 L/min.
  • the default creep time is set for two hours.
  • Each sample is compression- molded into a“2 mm thick x 25 mm diameter'’ circular plaque, at 177°C, for five minutes, under 10 MPa pressure, in air. The sample is then taken out of the press and placed on a counter top to cool.
  • a constant low shear stress of 20 Pa is applied for all of the samples, to ensure that the steady state shear rate was low enough to be in the Newtonian region.
  • the resulting steady state shear rates are in the range from 10- 3 to 10 -4 s- 1 for the samples in this study.
  • Steady state is determined by taking a linear regression for all the data, in the last 10% time window of the plot of“log (J(t)) vs. log(t),” where J(t) is creep compliance and t is creep time. If the slope of the linear regression is greater than 0.97, steady state is considered to be reached, then the creep test is stopped. In all cases in this study, the slope meets the criterion within one hour.
  • the steady state shear rate is determined from the slope of the linear regression of all of the data points, in the last 10% time window of the plot of“e vs. t,” where e is strain.
  • the creep zero shear viscosity is determined from the ratio of the applied stress to the steady state shear rate.
  • a small amplitude oscillatory shear test is conducted before, and after, the creep test, on the same specimen from 0.1 to 100 rad/s.
  • the complex viscosity values of the two tests are compared. If the difference of the viscosity values, at 0.1 rad/s, is greater than 5%, the sample was considered to have degraded during the creep test, and the result is discarded.
  • Zero-Shear Viscosity Ratio ZSVR
  • ZSVR zero- shear viscosity ratio
  • the ZSV value is obtained from a creep test at 190 °C, via the method described above.
  • the Mwt is determined using conventional gel permeation chromatography, as described above.
  • the correlation between the ZSV of linear polyethylene and its molecular weight was established based on a series of linear polyethylene reference materials.
  • Lower ZSVR indicates lower level of long chain branching. Branching Measurements using 13 C NMR
  • the samples are prepared by adding approximately 2.7 g of a 50/50 mixture of tetrachloroethane-d2/orthodichlorobenzene containing 0.025 M CT(ACAC)3 as a relaxation agent to a 0.20 to 0.30g sample in a Norell 1001-7 10 mm NMR tube. Oxygen is removed by purging the tube with N2 for 1 minute. The samples are dissolved and homogenized by healing the tube and its contents to 120-140°C using a heating block and vortex mixer.
  • the data are collected using a Broker 600 MHz spectrometer equipped with a Broker 10mm mnltinudear high-temperature CryoProbe.
  • the data are acquired using 1280 transients pa data file, a 7.8 sec pulse repetition delay, 90 degree flip angles, and inverse gated decoupling with a sample temperature of 120 °C. All measurements are made on non-spinning samples in locked mode. Samples are allowed to thermally equilibrate prior to data acquisition. The 13 C NMR chemical shifts are internally referenced to the F.F.F. triad at 30.0 ppm.
  • the data is processed into a spectrum, appropriate peaks are integrated (quantitating the branches), and then one or more peak integral values are used or averaged for the total branches/1000C. In the event that no branching is detected, die integrals and signal-to-noise ratio of peaks such as those due to chain ends are used to calculate the limit of detection of the spectrum.
  • a stock solution (3.26 g) is added to 0.10 to 0.13 g of the polymer sample in a 10 mm NMR tube.
  • the stock solution is either a mixture of tetrachloroethane-cb (TCE) and perchloroethylene (50:50, w:w) with 0.001M Cr 3+ or 100% TCE with 0.001M Cr 3+ .
  • TCE tetrachloroethane-cb
  • perchloroethylene 50:50, w:w
  • the solution in the tube is sparged with N2 for 5 minutes to reduce the amount of oxygen.
  • the sample is dissolved at 120 to 140°C with periodic vortex mixing.
  • Each 1 H NM anRalysis is run with a 10 mm cryoprobe, at 120°C, on a Broker AVANCE 600 MHz spectrometer.
  • the data are processed with an exponential window function with 0.7 Hz line broadening, and the baseline is corrected from about 7 to 4 ppm.
  • the signal from residual 1 H of TCE is set to 100, and the corresponding integrals for unsaturations are integrated. It is well known to
  • the unsaturation units per 1,000 total carbons, i.e., all polymer carbons including backbone and branches, are calculated as:
  • the chemical shift reference is set at 6.0 ppm for the 1 H signal from residual proton from TCE-d2.
  • Polyethylene Composition 1 is prepared according to the following process and based on the reaction conditions reported in Table 1. All raw materials (ethylene monomer) and the process solvent (a narrow boiling range high-purity isoparaffinic solvent, Isopar-E) are purified with molecular sieves before introduction into the reaction environment Hydrogen is supplied pressurized as a high purity grade and is not further purified.
  • the reactor monomer feed stream is pressurized via a mechanical compressor to above reaction pressure.
  • the solvent feed is pressurized via a pump to above reaction pressure.
  • the individual catalyst components are manually batch diluted to specified component concentrations with purified solvent and pressured to above reaction pressure. All reaction feed flows are measured with mass flow meters and independently controlled with computer automated valve control systems.
  • the continuous solution polymerization reactors consist of two liquid full, non- adiabatic, isothermal, circulating, loop reactors which mimic continuously stirred tank reactors (CSTRs) with heat removal. Independent control of all fresh solvent, monomer, hydrogen, and catalyst component feeds to each reactor is possible.
  • the total flesh feed streams to each reactor are temperature controlled by passing the feed stream through a heat exchanger.
  • the total flesh feed to each polymerization reactor is injected into the reactor at two locations per reactor roughly with equal reactor volumes between each injection location.
  • the fresh feed to the first reactor is controlled typically with each injector receiving half of the total fresh feed mass flow.
  • the fresh feed to the second reactor in series is controlled typically to maintain half of the total ethylene mass flow near each injector, and since the non-reacted ethylene from the first reactor enters the second reactor adjacent to the lower pressure fresh feed this injector usually has less than half of the total fresh feed mass flow to the second reactor.
  • the catalyst/cocatalyst components for each reactor are injected into the polymerization reactor through specially designed injection stingos. Each catalyst/cocatalyst component is separately injected into the same relative location in the reactor with no contact time prior to the reactor.
  • the primary catalyst component is computer controlled to maintain the individual reactor monomer conversion at the specified target
  • the cocatalyst components are fed based on calculated specified molar ratios to the primary catalyst component.
  • the catalyst used in the first reactor is zirconium, [[2,2”’-[[bis[l- methylethyl)germylene]bis(methyleneoxy- kO)]bis[3” ,5,5” -tris( 1 , 1 -dimethylethyl)-5’ - octyl[l,l’:3’,l”-terphenyl]-2’-olato- kO]](2-)]dimethyl-, having the chemical formula C 86 H 128 F 2 Ge0 4 Zr and the following structure (“Catalyst 1”):
  • the catalyst used in the second reactor is zirconium, [[2,2”’-[l,3-propanediyIbis(oxy- kO)]bis [3- [2,7-bis( 1 , 1 - ⁇ timethylethyl)-9H-carbazol-9-yl]]-5’ -(dimethyloctylsilyl)-3’ - methyl-5-(l, 1,3,3- tetramethylbutyl) [ 1 , 1 ]-biphenyl] -2-olato- kO] ] (2-)] dimethyl, having the chemical formula C 107 H 154 N 2 O 4 Si 2 Zr and the following structure (“Catalyst 2”):
  • each reactor feed injection location the feed streams are mixed with the circulating polymerization reactor contents with static mixing elements.
  • the contents of each reactor are continuously circulated through heat exchangers responsible for removing much of the heat of reaction and with the temperature of the coolant side responsible for maintaining an isothermal reaction environment at the specified reactor temperature. Circulation around each reactor loop is provided by a pump.
  • the effluent from the first polymerization reactor exits the first reactor loop and passes through a control valve (responsible for controlling the pressure of the first reactor at a specified target) and is injected into the second polymerization reactor of similar design.
  • the final effluent from the second polymerization reactor enters a zone where it is deactivated with the addition of and reaction with a suitable reagent (water). At this same reactor exit location other additives are added for polymer stabilization.
  • This final effluent stream passes through another set of static mixing elements to facilitate the deactivation of the catalyst and dispersion of the additives.
  • the reactor effluent enters a devolatization system where the polymer is removed from the non-polymer stream.
  • the isolated polymer melt is pelletized and collected.
  • the non-polymer stream passes through various pieces of equipment which separate most of the ethylene which is removed from the system. Most of the solvent is recycled back to the reactor after passing through a purification system. A small amount of solvent is purged from the process.
  • Polyethylene Composition 1 was stabilized with minor (ppm) amounts of stabilizers.
  • tetrakis(paitafluorophenyl)borate( 1 -) amine); and Cocat. 2 modified methyl ahuninoxane (MMAO) are each used as a cocatalyst for Catalyst 1 and Catalyst 2.
  • MMAO modified methyl ahuninoxane
  • Polyethylene Composition 2 is prepared using the same catalyst system as
  • Polyethylene Composition 1 and Polyethylene Composition 2 are measured using the Test Methods described above, and are reported in Table 2.
  • the First Polyethylene Fraction refers to the polycthylmc component from the first reactor
  • the Second Polyethylene Fraction refers to the polycthylmc fraction from the second reactor.
  • the densities of the first polyethylene fraction for Polyethylene Composition 1, the overall Polyethylme Composition 1, and the overall Polyethylene Composition 2 are measured as described above in the Test Methods section.
  • the density of the first polyethylme fraction for Polyethylene Composition 2 is the target value.
  • the density of the second polyethylene fraction is calculated using the following blend rule:
  • Comparative Composition A is ELITETM 5960G, a high density enhanced polyethylene resin commercially available from The Dow Chemical Company that does not include Hyperform HPN-20E. Comparative Composition A has a density of 0.962 g/cm 3 and a melt index (I 2 ) of 0.85 g/10 minutes. Comparative Composition B is a commercially available high density polyethylene resin that has a density of 0.967 g/cm 3 and a melt index (b) of 1.2 g/10 minutes, and that contains -1200 ppm of Hyperform HPN-
  • Table 3 illustrates some of the differences in the polymer design of these resins.
  • Polyethylene Composition 1 and Comparative Compositions A and B are evaluated on a blown film line.
  • the resins are dry blended with an Hyperform HPN-20E nucleating agent (Milliken Chemical) provided in a mastebatch to target different final loadings of the HPN-20E nucleating agent (“HFN-20E”) (targets: 0, 250, 750, 1250, 2500, and 5000 ppm HPN-20E loading) and furthermore to evaluate moisture vapor barrier properties (MVTR or WVTR).
  • the mastebatch with HPN-20E includes 3 weight percent of HPN-20E, 1.5 weight percent silica, 0.5 weight percent hydrotalcite, 5 weight percent antioxidant, and 90 weight percent of a carrier resin.
  • the carrier resin is a narrow molecular weight distribution high density polyethylene homopolymer having a density of 0.965g/cm 3 and a melt index (b) of 8.0 g/10 minutes.
  • the Hyperform HPN-20E comprises -66 weight percent of calcium salt of 1 ,2-cyclohexanedicaiboxylic acid and -34 weight percent of zinc stearate/zinc palmitale.
  • the blown film line utilizes a twin screw extruder in which the specified resin and nucleating agent are dry blended and melted prior to being sent to a two inch diameter extrusion ring at a nominal rate of 15 lbs/hr.
  • the extruder die temperature is set between 215 and 235 * C.
  • the blown film structure is a monolayer film with a target thickness of 2 mils.
  • the blow-up ratio is targeted to be 2.5, the frost line height ranged from - 9 to 11 inches, and the lay flat was -7.9 inches. Approximately 100 feet of bubble film is produced and split into two films.
  • the water vapor transmission rates (WVTR) of the films are measured, with a WVTR of 0.10 (g-miiy(100h ⁇ -day) being particularly desirable.
  • the results are shown in Table 4 in units of (g-miiy( lOOin 2 ⁇ day).
  • compositions that are blends of Polyethylene Composition 1 and HPN-20E, particularly at 250-1250 ppm represent polyethylene-based compositions according to some embodiments of the present invention.
  • the compositions that are blends with Comparative Composition A or Comparative Composition B are comparative examples. Note that data for Comparative Composition B are not available at 0-750 ppm because it is commercially available with -1200 ppm of HPN-20E.
  • the inventive polyethylene-based composition with HPN-20E at 250 ppm provides the best WVTR performance.
  • Additional film samples are made using a Dr. Collin 3-layer coextrusion blown film line.
  • this blown film line has a single screw extruder that feeds a 2.36 inch diameter extrusion ring.
  • the nominal run rate is 30 lbs/hr with the extruder die temperature was set at -215 * C.
  • the blown film structure is a monolayer film with a target thickness of 2 mils.
  • the blow-up ratio is targeted to be 2.5, the frost line height is -5.5 inches, and the lay flat was -10 inches. Approximately 100 feet of bubble film is produced and split into two films.
  • Three polyethylene-based compositions are made with Polyethylene Composition 1 by: (1) dry blending Polyethylene Composition 1 with an HPN-20E masterbatch (as described in Example 1) in the single screw extruder at the blown film line (“Dry”)
  • compositions utilizing 250-750 ppm of HPN-20E represent polyethylene- based compositions according to some embodiments of the present invention,
  • melt blending of Polyethylene Composition 1 with 250 HPN-20E provided particularly desirable WVTR values, nearly 20% lower than Comparative Composition B.
  • a number of multilayer films are made using a 7-layer Alpine blown film line.
  • the multilayer films are produced with five distinct layers that have a total nominal thickness of 2.2 mils and are formed at a blow-up ratio of 2.5.
  • the film structure is: Layer A (15%)/Layer B (20%)/Layer C (30%)/Layer D (20%)/Layer E (15%).
  • Layer A is formed from ELITETM 5960G1 (The Dow Chemical Company).
  • Layers B and D are each formed with INNATETM TH 60 (The Dow Chemical Company).
  • Layer E is a sealant layer and is formed with SEALUTIONTM 220 (The Dow Chemical Company).
  • Layer C is a barrio layo and is described further in Table 6 below.
  • Blends of Polyethylene Composition 1 and a masterbatch HFN-20E are eitho dry bloided in the extrudo feeding the Alpine blown film line (“Dry Blended”), or melt bloided with a ZSK40 twin screw extrudo before being provided to the extrudo feeding the Alpine blown film Hne (“Melt Blended”).
  • Comparative Composition B is evaluated in Layo C as commercially available. The WVTR of the samples are measured and the results are shown in Table 6.
  • the blends of Polyethylene Compositions 1 and 250-750 ppm HFN-20E represent polyethylene-based compositions according to some embodiments Q f the present invention. Providing polyethylene-based compositions with 750 ppm of HPN-20E results in particularly desirable WVTR results. In particular, the melt blending of Polyethylene Composition 1 with 750 ppm of HFN-20E provides an improvement in WVTR of -15% over Comparative Composition B.
  • Polyethylene Composition 2 is melt blended with an Hyperform HFN-20E nucleating agent (MilHken Chemical) (“HFN-20E”) provided in a mastobatch, along with silica, hydrotalcite, antioxidant, and a HOPE carrier resin.
  • the mastobatch includes 3 weight percent of HFN-20E, 1.5 weight percent silica, 0.5 weight percent hydrotalcite, 5 weight percent antioxidant, and 90 weight percent of a carrier resin.
  • the carrio resin is a narrow molecular weight distribution high density polyethylene homopolymo having a density of 0.965g/cm 3 and a melt index (L ⁇ ) of 8.0 g/10 minutes.
  • the Hyperform HFN-20E comprises -66 weight percent of calcium salt of 1,2-cyclohexanedicarboxylic acid and -34 weight percent of zinc stearate/zinc palmitate.
  • the inventive polyethylene-based composition formed from Polyethylene Composition 2 and the masterbatch (“Polyethylene- based Composition 2”) includes 750 ppm of HFN-20E, 375 ppm of silica, 125 ppm of hydrotalcite, and 1,250 ppm of antioxidants, based on the total weight of the polyethylene- based composition.
  • Comparative Composition B contains -1200 ppm of HPN-20E and is not believed to include any silica.
  • Monolayer films having a target thickness of 2 mils are produced from
  • Polyethylene-based Composition 2 and Comparative Composition B on a blown film line is equipped with a screw single screw extruder using a 8 inch DSB P screw design capable of an output rate near 600 Ibs/hr of polyethylene.
  • a target temperature profile during extrusion is 177 ° C, 218 ° C, 193 ° C, 163 ° C, 163 ° C, 221 ° C, and 227 * C through bands 1- 5, the screen block, and lower-upper die respectively.
  • the Compositions are sent to an 8 inch blown film die with a 70 mil die gap and an output rate of 10.4 lb/hr/in of die circumference.
  • a target melt temperature is 227° C, and the blow-up ratio is maintained at 2.5 to 1.
  • the air temperature in the air ring and air cooling unit is 7.2 °C.
  • the frost line height is an average of 34 inches.
  • Rim thickness is controlled within ⁇ 10% at 2 mils by adjusting the nip roller speed.
  • the layflat of the bubble is 31 inches wide. The films are wound up into a roll before slitting.
  • the films are evaluated for dusting. Dust from the films is collected on 8.5 inch x 11 inch black felt sheets adhered to a stationary roller on a slitter/rewinder machine. The films slid over the stationary felt sheets as they were wound through the machine. Dust is collected from 800 feet of each sample at a 200 feet/min run rate. The black felt samples are then carefully removed and visually inspected. The film samples formed from
  • Polyethylene-based Composition 2 exhibited less dusting than the film samples formed from Comparative Composition B.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Health & Medical Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Medicinal Chemistry (AREA)
  • Polymers & Plastics (AREA)
  • Organic Chemistry (AREA)
  • Engineering & Computer Science (AREA)
  • Manufacturing & Machinery (AREA)
  • Materials Engineering (AREA)
  • Compositions Of Macromolecular Compounds (AREA)
  • Manufacture Of Macromolecular Shaped Articles (AREA)
  • Laminated Bodies (AREA)
  • Wrappers (AREA)
PCT/US2020/031151 2019-05-02 2020-05-01 Polyethylene-based compositions and films and articles comprising the same Ceased WO2020223688A1 (en)

Priority Applications (8)

Application Number Priority Date Filing Date Title
EP20727106.5A EP3962998B1 (en) 2019-05-02 2020-05-01 Polyethylene-based compositions and films and articles comprising the same
MX2021012936A MX2021012936A (es) 2019-05-02 2020-05-01 Composiciones a base de polietileno y peliculas y articulos que las comprenden.
CN202080026502.5A CN113661209B (zh) 2019-05-02 2020-05-01 基于聚乙烯的组合物和包含它们的薄膜和制品
JP2021561807A JP7601786B2 (ja) 2019-05-02 2020-05-01 ポリエチレン系組成物、ならびにそれらを含むフィルムおよび物品
US17/432,449 US12129363B2 (en) 2019-05-02 2020-05-01 Polyethylene-based compositions and films and articles comprising the same
ES20727106T ES2953841T3 (es) 2019-05-02 2020-05-01 Composiciones y películas a base de polietileno y artículos que comprenden las mismas
BR112021019568-8A BR112021019568B1 (pt) 2019-05-02 2020-05-01 Composição à base de polietileno adequada para aplicações de embalagem, filme e artigo
CONC2021/0015974A CO2021015974A2 (es) 2019-05-02 2021-11-26 Composiciones a base de polietileno y películas y artículos que las comprenden

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US201962842253P 2019-05-02 2019-05-02
US62/842,253 2019-05-02

Publications (1)

Publication Number Publication Date
WO2020223688A1 true WO2020223688A1 (en) 2020-11-05

Family

ID=70775587

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2020/031151 Ceased WO2020223688A1 (en) 2019-05-02 2020-05-01 Polyethylene-based compositions and films and articles comprising the same

Country Status (9)

Country Link
US (1) US12129363B2 (https=)
EP (1) EP3962998B1 (https=)
JP (1) JP7601786B2 (https=)
CN (1) CN113661209B (https=)
AR (1) AR118858A1 (https=)
CO (1) CO2021015974A2 (https=)
ES (1) ES2953841T3 (https=)
MX (1) MX2021012936A (https=)
WO (1) WO2020223688A1 (https=)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2021118739A1 (en) * 2019-12-10 2021-06-17 Dow Global Technologies Llc Oriented polyethylene films and articles comprising the same
WO2021242384A1 (en) * 2020-05-29 2021-12-02 Dow Global Technologies Llc Oriented polyethylene films and articles comprising the same
EP4242262A4 (en) * 2021-10-25 2024-06-26 Lg Chem, Ltd. POLYETHYLENE RESIN COMPOSITION AND FILM
US12263628B2 (en) 2020-10-30 2025-04-01 Dow Global Technologies Llc Multilayer films and articles comprising the same

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2025006343A1 (en) * 2023-06-29 2025-01-02 Dow Global Technologies Llc Cap with barrier composition
WO2025149673A1 (en) 2024-01-11 2025-07-17 Totalenergies Onetech Pfas-free polymer composition

Citations (17)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3645992A (en) 1967-03-02 1972-02-29 Du Pont Canada Process for preparation of homogenous random partly crystalline copolymers of ethylene with other alpha-olefins
US3914342A (en) 1971-07-13 1975-10-21 Dow Chemical Co Ethylene polymer blend and polymerization process for preparation thereof
US4076698A (en) 1956-03-01 1978-02-28 E. I. Du Pont De Nemours And Company Hydrocarbon interpolymer compositions
US4599392A (en) 1983-06-13 1986-07-08 The Dow Chemical Company Interpolymers of ethylene and unsaturated carboxylic acids
US5272236A (en) 1991-10-15 1993-12-21 The Dow Chemical Company Elastic substantially linear olefin polymers
US5278272A (en) 1991-10-15 1994-01-11 The Dow Chemical Company Elastic substantialy linear olefin polymers
US5562905A (en) 1988-04-26 1996-10-08 E. I. Du Pont De Nemours And Company Human immunodeficiency virus (hiv) env-coded peptide capable of eliciting hiv-inhibiting antibodies in mammals
US5582923A (en) 1991-10-15 1996-12-10 The Dow Chemical Company Extrusion compositions having high drawdown and substantially reduced neck-in
US5733155A (en) 1995-07-28 1998-03-31 The Whitaker Corporation Female contact
US5854045A (en) 1994-05-12 1998-12-29 The Rockefeller University Transmembrane tyrosine phosphatase and methods of use thereof
US6127484A (en) 1999-04-29 2000-10-03 Equistar Chemicals, Lp Olefin polymerization process
WO2001070827A1 (en) 2000-03-20 2001-09-27 Chevron Phillips Chemical Company Lp Process for making mvtr resin
EP0799274B1 (en) 1994-12-22 2003-04-02 ExxonMobil Chemical Patents Inc. Polyethylene articles with improved resistance to water vapor transmission
WO2004000933A1 (en) 2002-06-20 2003-12-31 Borealis Technology Oy Breathable films
WO2005090464A1 (en) 2004-03-19 2005-09-29 Dow Global Technologies Inc. Film layers made from polymer formulations
WO2016135590A1 (en) * 2015-02-24 2016-09-01 Nova Chemicals (International) S.A. Bottle cap
US20170130040A1 (en) * 2006-11-17 2017-05-11 Nova Chemicals (International) S.A. Barrier film for food packaging

Family Cites Families (23)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6599971B2 (en) 2001-03-29 2003-07-29 Milliken & Company Metals salts of hexahydrophthalic acid as nucleating additives for crystalline thermoplastics
CA2479704C (en) 2004-08-31 2013-08-13 Nova Chemicals Corporation High density homopolymer blends
US7625982B2 (en) 2005-08-22 2009-12-01 Chevron Phillips Chemical Company Lp Multimodal polyethylene compositions and pipe made from same
US7659336B2 (en) 2006-03-08 2010-02-09 Milliken & Company Nucleating agent additive compositions and methods
EP1834986A1 (en) 2006-03-13 2007-09-19 Borealis Technology Oy High density polyethylene
US8436085B2 (en) 2007-03-14 2013-05-07 Equistar Chemicals, Lp Barrier properties of substantially linear HDPE film with nucleating agents
CA2594472A1 (en) 2007-07-23 2009-01-23 Nova Chemicals Corporation Multilayer barrier film
US8026305B2 (en) 2008-10-01 2011-09-27 Fina Technology Inc Articles formed from nucleated polyethylene
US9187627B2 (en) 2008-10-23 2015-11-17 Equistar Chemicals, Lp Polyethylene having faster crystallization rate and improved environmental stress cracking resistance
US20100159173A1 (en) 2008-12-18 2010-06-24 Fina Technology, Inc. Polyethylene Polymerization Processes
SG177446A1 (en) * 2009-07-01 2012-02-28 Dow Global Technologies Llc Ethylenic polymer and its use
US8829115B2 (en) 2009-07-01 2014-09-09 Dow Global Technologies Llc Ethylene-based polymer composition
US20110003940A1 (en) 2009-07-01 2011-01-06 Dow Global Technologies Inc. Ethylene-based polymer compositions for use as a blend component in shrinkage film applications
US20120107542A1 (en) 2009-11-03 2012-05-03 Kevin Philip Nelson High Density Polyethylene Blend Films
CA2688092C (en) 2009-12-10 2016-07-12 Nova Chemicals Corporation Multilayer film structure
US8476394B2 (en) 2010-09-03 2013-07-02 Chevron Philips Chemical Company Lp Polymer resins having improved barrier properties and methods of making same
US8580893B2 (en) 2011-12-22 2013-11-12 Fina Technology, Inc. Methods for improving multimodal polyethylene and films produced therefrom
US9783663B2 (en) 2012-12-14 2017-10-10 Nova Chemicals (International) S.A. Polyethylene compositions having high dimensional stability and excellent processability for caps and closures
CA2798854C (en) 2012-12-14 2020-02-18 Nova Chemicals Corporation Polyethylene compositions having high dimensional stability and excellent processability for caps and closures
SG11201503581PA (en) * 2012-12-27 2015-06-29 Dow Global Technologies Llc Catalyst systems for olefin polymerization
CA2914354C (en) * 2015-12-10 2022-11-08 Nova Chemicals Corp. Hot fill process with closures made frm bimodal polyethylene compositions
MX2018007482A (es) 2015-12-21 2018-08-01 Dow Global Technologies Llc Formulaciones de polietileno con barrera y resistencia al agrietamiento por estres ambiental mejoradas.
CA2942493C (en) * 2016-09-20 2023-08-01 Nova Chemicals Corporation Nucleated polyethylene blends and their use in molded articles

Patent Citations (18)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4076698A (en) 1956-03-01 1978-02-28 E. I. Du Pont De Nemours And Company Hydrocarbon interpolymer compositions
US4076698B1 (https=) 1956-03-01 1993-04-27 Du Pont
US3645992A (en) 1967-03-02 1972-02-29 Du Pont Canada Process for preparation of homogenous random partly crystalline copolymers of ethylene with other alpha-olefins
US3914342A (en) 1971-07-13 1975-10-21 Dow Chemical Co Ethylene polymer blend and polymerization process for preparation thereof
US4599392A (en) 1983-06-13 1986-07-08 The Dow Chemical Company Interpolymers of ethylene and unsaturated carboxylic acids
US5562905A (en) 1988-04-26 1996-10-08 E. I. Du Pont De Nemours And Company Human immunodeficiency virus (hiv) env-coded peptide capable of eliciting hiv-inhibiting antibodies in mammals
US5582923A (en) 1991-10-15 1996-12-10 The Dow Chemical Company Extrusion compositions having high drawdown and substantially reduced neck-in
US5278272A (en) 1991-10-15 1994-01-11 The Dow Chemical Company Elastic substantialy linear olefin polymers
US5272236A (en) 1991-10-15 1993-12-21 The Dow Chemical Company Elastic substantially linear olefin polymers
US5854045A (en) 1994-05-12 1998-12-29 The Rockefeller University Transmembrane tyrosine phosphatase and methods of use thereof
EP0799274B1 (en) 1994-12-22 2003-04-02 ExxonMobil Chemical Patents Inc. Polyethylene articles with improved resistance to water vapor transmission
US5733155A (en) 1995-07-28 1998-03-31 The Whitaker Corporation Female contact
US6127484A (en) 1999-04-29 2000-10-03 Equistar Chemicals, Lp Olefin polymerization process
WO2001070827A1 (en) 2000-03-20 2001-09-27 Chevron Phillips Chemical Company Lp Process for making mvtr resin
WO2004000933A1 (en) 2002-06-20 2003-12-31 Borealis Technology Oy Breathable films
WO2005090464A1 (en) 2004-03-19 2005-09-29 Dow Global Technologies Inc. Film layers made from polymer formulations
US20170130040A1 (en) * 2006-11-17 2017-05-11 Nova Chemicals (International) S.A. Barrier film for food packaging
WO2016135590A1 (en) * 2015-02-24 2016-09-01 Nova Chemicals (International) S.A. Bottle cap

Non-Patent Citations (2)

* Cited by examiner, † Cited by third party
Title
BUSICO, V. ET AL., MACROMOLECULES, vol. 38, 2005, pages 6988
WILLIAMSWARD, J. POLYM. SCI., POLYM. LETTERS, vol. 6, 1968, pages 621

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2021118739A1 (en) * 2019-12-10 2021-06-17 Dow Global Technologies Llc Oriented polyethylene films and articles comprising the same
US12145344B2 (en) 2019-12-10 2024-11-19 Dow Global Technologies Llc Oriented polyethylene films and articles comprising the same
WO2021242384A1 (en) * 2020-05-29 2021-12-02 Dow Global Technologies Llc Oriented polyethylene films and articles comprising the same
US12263628B2 (en) 2020-10-30 2025-04-01 Dow Global Technologies Llc Multilayer films and articles comprising the same
EP4242262A4 (en) * 2021-10-25 2024-06-26 Lg Chem, Ltd. POLYETHYLENE RESIN COMPOSITION AND FILM

Also Published As

Publication number Publication date
CN113661209A (zh) 2021-11-16
EP3962998A1 (en) 2022-03-09
JP2022531089A (ja) 2022-07-06
CO2021015974A2 (es) 2022-04-08
EP3962998B1 (en) 2023-06-21
BR112021019568A2 (pt) 2021-12-07
AR118858A1 (es) 2021-11-03
ES2953841T3 (es) 2023-11-16
US20220056250A1 (en) 2022-02-24
US12129363B2 (en) 2024-10-29
MX2021012936A (es) 2021-11-25
CN113661209B (zh) 2023-10-13
JP7601786B2 (ja) 2024-12-17

Similar Documents

Publication Publication Date Title
CN115697700B (zh) 定向聚乙烯膜和包括其的制品
EP3962998B1 (en) Polyethylene-based compositions and films and articles comprising the same
US12145344B2 (en) Oriented polyethylene films and articles comprising the same
US20210331845A1 (en) Polyethylene laminates for use in flexible packaging materials
US20210040295A1 (en) Polyethylene compositions
EP4010192A1 (en) Polyethylene compositions
US12600115B2 (en) Oriented polyethylene films and articles comprising the same
CN116670224B (zh) 聚乙烯组合物、膜和制品
WO2022093488A1 (en) Multilayer films and articles comprising the same
JP7825047B2 (ja) 二軸配向ポリオレフィンフィルム
US12263628B2 (en) Multilayer films and articles comprising the same

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 20727106

Country of ref document: EP

Kind code of ref document: A1

REG Reference to national code

Ref country code: BR

Ref legal event code: B01A

Ref document number: 112021019568

Country of ref document: BR

ENP Entry into the national phase

Ref document number: 2021561807

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

WWE Wipo information: entry into national phase

Ref document number: NC2021/0015974

Country of ref document: CO

ENP Entry into the national phase

Ref document number: 2020727106

Country of ref document: EP

Effective date: 20211202

ENP Entry into the national phase

Ref document number: 112021019568

Country of ref document: BR

Kind code of ref document: A2

Effective date: 20210929

WWP Wipo information: published in national office

Ref document number: NC2021/0015974

Country of ref document: CO

WWG Wipo information: grant in national office

Ref document number: MX/A/2021/012936

Country of ref document: MX