WO2020145170A1 - 導電性接着剤組成物 - Google Patents

導電性接着剤組成物 Download PDF

Info

Publication number
WO2020145170A1
WO2020145170A1 PCT/JP2019/051028 JP2019051028W WO2020145170A1 WO 2020145170 A1 WO2020145170 A1 WO 2020145170A1 JP 2019051028 W JP2019051028 W JP 2019051028W WO 2020145170 A1 WO2020145170 A1 WO 2020145170A1
Authority
WO
WIPO (PCT)
Prior art keywords
conductive adhesive
particles
adhesive composition
average particle
particle diameter
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2019/051028
Other languages
English (en)
French (fr)
Inventor
真太郎 阿部
近藤　剛史
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tanaka Kikinzoku Kogyo KK
Original Assignee
Tanaka Kikinzoku Kogyo KK
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tanaka Kikinzoku Kogyo KK filed Critical Tanaka Kikinzoku Kogyo KK
Publication of WO2020145170A1 publication Critical patent/WO2020145170A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

本発明は、平均粒子径０．５～１０μｍの金属粒子（ａ１）と平均粒子径１０～２００ｎｍの銀粒子（ａ２）とを含む導電性フィラー（Ａ）と、平均粒子径２～１４μｍの熱可塑性樹脂の粒子（Ｂ）と、を含有し、熱可塑性樹脂の融点が、１３０～２５０℃である導電性接着剤組成物に関する。

Description

導電性接着剤組成物
　本発明は、導電性接着剤組成物に関する。
　電子部品において、半導体素子をリードフレーム等の支持部材に接着・接合するためのダイボンド材として、導電性接着剤組成物が用いられている。導電性接着剤組成物には、高い電気伝導性を有することから銀粉や銅粉等の金属粉が一般的に用いられており、これらを含む接着剤や焼結により接着するペースト状の接着剤に関する報告が多くなされている。
　ここで、近年小型化・高機能化された電子部品、例えば、パワーデバイス又は発光ダイオード（ＬＥＤ）に対する需要が急速に拡大しており、電子部品の小型化が進行するに伴い、半導体素子の発熱量は増大傾向にある。ところが、半導体素子は、高温環境に長時間さらされると、本来の機能を発揮することができなくなり、また、寿命が低下することになる。そのため、ダイボンド材には半導体素子から発生した熱を支持部材に効率よく逃がすために、高い熱伝導率が求められており、その要求水準は上昇を続けている。
　導電性接着剤において、上述の要請から熱伝導性を向上させるために、導電性フィラーとして、従来から用いられていたマイクロメートルオーダーの金属粒子に加え、ナノメートルオーダーの金属粒子を用いる技術が報告されている。
　例えば、特許文献１において、平均粒子径が２～２０μｍ、タップ密度（ＴＤ）が２．０～７．０ｇ／ｃｍ３、かつ、炭素含有化合物の含有割合が０．５質量％以下であるフレーク状銀粉と、平均粒子径が１０～５００ｎｍである銀ナノ粒子と、熱硬化性樹脂と、を含有することを特徴とする導電性ペーストが報告されている。
　また、特許文献２において、銀粉、銀微粒子、脂肪酸銀、及びアミンを含み、前記銀粉は、平均粒子径が０．３μｍ～１００μｍであり、前記銀微粒子は、１次粒子の平均粒子径が５０～１５０ｎｍであり、結晶子径が２０～５０ｎｍであり、かつ、結晶子径に対する平均粒子径の比が１～７．５であり、さらに、銀レジネートを含む、熱伝導性組成物が報告されている。
日本国特開２０１５－１６２３９２号公報 日本国特許第５８７２５４５号公報
　先述のようなマイクロメートルオーダーの金属粒子にナノメートルオーダーの金属粒子を加えた導電性接着剤組成物の硬化物（以下、接着剤層ともいう）は、緻密な焼結構造を形成しているが、それでもなおその硬化物中には空隙が存在する。このような硬化物が上記のような半導体素子の発熱による温度変化を繰り返し受けた場合、ネッキング構造を形成していた金属が空隙に接する面積を減らして表面エネルギーを低下させる方向に移動し、その結果金属が成長する場合がある。
　一般に、マイクロメートルオーダーの金属粒子にナノメートルオーダーの金属粒子を加えた導電性接着剤組成物の硬化物は、その緻密な結晶構造に起因して応力緩和性能が低い。そのうえ、上記のような金属の成長が生じると、金属の移動に伴い接着界面付近に大きな空隙が生じること等に起因し、応力緩和性能がさらに低下することとなる。この場合、被接着材料同士の線熱膨張率の差により生じる応力によって、被接着材料の剥離が生じやすくなるという問題がある。
　また、導電性接着剤組成物においては導電性や熱伝導率を向上させるために、導電性接着剤組成物内の金属成分の含有率を高くして充填密度を高めることが行われている。上記特許文献１、及び特許文献２においても、導電性接着剤組成物の全体量に対して、マイクロメートルオーダー、ナノメートルオーダーの金属粒子をあわせて８０％以上含むような導電性接着剤組成物が実施例において開示されている。しかし、このような金属含有率が高い導電性接着剤組成物の硬化物は一般的に応力緩和性能が低く、上述の剥離が特に生じやすい。
　また、接着剤層を薄くすると、応力緩和性能が低くなるため、上述の剥離が生じやすくなる。しかし、近年においては、半導体素子の発熱量の増加により、放熱効率のより一層の向上が求められることから、接着剤層の薄層化への要請が強い。
　したがって、繰り返しの温度変化に起因する被接着材料の剥離の抑制性能が高く、接着剤層を薄層化した場合においても剥離を十分に抑制できるような導電性接着剤組成物が望まれている。
　本発明は、上記課題に鑑みて発明されたものであり、その目的は、熱伝導性に優れ、さらに、繰り返し温度変化を受けた場合にも被接着材料の剥離を十分に抑制できる導電性接着剤組成物を提供することである。
　本発明者らは、鋭意研究した結果、平均粒子径０．５～１０μｍの金属粒子と平均粒子径１０～２００ｎｍの銀粒子とを含む導電性フィラーと、平均粒子径２～１４μｍの、融点が１３０～２５０℃である熱可塑性樹脂の粒子とを含有する導電性接着剤組成物によって、熱伝導性に優れ、かつ繰り返し温度変化を受けた場合にも被接着材料の剥離が生じにくい接着を実現できることを見出し、本発明を完成するに至った。
　すなわち、本発明の導電性接着剤組成物は平均粒子径０．５～１０μｍの金属粒子（ａ１）と平均粒子径１０～２００ｎｍの銀粒子（ａ２）とを含む導電性フィラー（Ａ）と、平均粒子径２～１４μｍの熱可塑性樹脂の粒子（Ｂ）と、を含有し、熱可塑性樹脂の融点が、１３０～２５０℃である。
　本発明の一態様に係る導電性接着剤組成物は、金属粒子（ａ１）の主成分が銀である。
　本発明の一態様に係る導電性接着剤組成物は、導電性接着剤組成物の全体量に対して、金属粒子（ａ１）を３５～８５質量％、銀粒子（ａ２）を５～５０質量％の範囲で含有する。
　本発明の一態様に係る導電性接着剤組成物は、金属粒子（ａ１）と銀粒子（ａ２）との含有比率が、質量比で９５：５～４０：６０の範囲である。
　本発明の一態様に係る導電性接着剤組成物は、導電性接着剤組成物の全体量に対して、熱可塑性樹脂の粒子（Ｂ）を０．１～１０質量％の範囲で含有する。
　また、本発明の導電性接着剤硬化物は、前記いずれか１の導電性接着剤組成物を硬化したものである。
　また、本発明の電子機器は、前記いずれか１の導電性接着剤組成物を部品の接着に使用したものである。
　本発明の導電性接着剤組成物は、平均粒子径０．５～１０μｍの金属粒子（ａ１）と、平均粒子径１０～２００ｎｍの銀粒子（ａ２）とを含む導電性フィラー（Ａ）を含有することにより熱伝導率を向上させている。また、平均粒子径２～１４μｍの、融点が１３０～２５０℃の熱可塑性樹脂の粒子（Ｂ）を含有することにより、ナノメートルオーダーの銀粒子を含有することに起因する、繰り返し温度変化を受けた場合における被接着材料の剥離発生の可能性の上昇を抑制している。このことから、本発明の導電性接着剤は、熱伝導性に優れ、さらに、繰り返し温度変化を受けた場合の被接着材料の剥離が十分に抑制されたものである。
　以下に、本発明を実施するための形態を説明するが、本発明は以下の実施形態に限定されるものではなく、本発明の要旨を逸脱しない範囲において、任意に変形して実施することができる。また、本明細書において数値範囲を示す「～」とは、その前後に記載された数値を下限値、及び上限値として含む意味で使用される。
　また、本明細書において金属粒子（ａ１）および熱可塑性樹脂の粒子（Ｂ）の平均粒子径はレーザー回折・散乱式粒度分析計を用いて測定された粒子径分布の５０％平均粒子径（Ｄ５０）とする。当該平均粒子径は、例えば、日機装株式会社製のレーザー回折・散乱式粒度分析計ＭＴ－３０００を用いて測定することができる。銀粒子（ａ２）の平均粒子径は動的光散乱法を用いて測定された粒子径分布の５０％平均粒子径（Ｄ５０）とする。当該平均粒子径は、例えば、日機装株式会社製のナノトラック粒子分布測定装置を用いて測定することができる。
　［導電性フィラー（Ａ）］
　本発明の実施形態における導電性フィラー（Ａ）は、平均粒子径０．５～１０μｍの金属粒子（ａ１）と、平均粒子径１０～２００ｎｍの銀粒子（ａ２）とを含むものである。
　＜金属粒子（ａ１）＞
　本発明の実施形態における金属粒子（ａ１）の平均粒子径は０．５μｍ以上であり、好ましくは０．６μｍ以上であり、より好ましくは０．７μｍ以上であり、さらに好ましくは０．８μｍ以上である。また、本発明の実施形態における金属粒子（ａ１）の平均粒子径は１０μｍ以下であり、好ましくは８μｍ以下であり、より好ましくは７μｍ以下であり、さらに好ましくは６μｍ以下である。
　また、本発明の実施形態における金属粒子（ａ１）の平均粒子径は０．５～１０μｍであり、好ましくは０．６～８μｍであり、より好ましくは０．７～７μｍ、さらに好ましくは０．８～６μｍである。
　金属粒子（ａ１）の平均粒子径が０．５μｍ未満であると、導電性接着剤組成物の硬化後の収縮が抑制されなくなるため被接着材料との密着性が低下してしまう。金属粒子（ａ１）の平均粒子径が１０μｍを超えると金属粒子（ａ１）の焼結が進みにくく被接着材料との密着性が低下してしまう。
　本発明の実施形態における金属粒子（ａ１）は、導電性接着剤における導電性に寄与する成分であれば特に制限されない。中でも、金属やカーボンナノチューブ等が好ましい。
　金属としては、一般的な導体として扱われる金属の粉末を利用することができる。例えば、銀、銅、金、ニッケル、アルミニウム、クロム、白金、パラジウム、タングステン、モリブデン等の単体、これら２種以上の金属からなる合金、これら金属のコーティング品、これら金属の酸化物、あるいはこれら金属の化合物で良好な導電性を有するもの等が挙げられる。中でも、酸化しづらく熱伝導性が高いことから、銀を主成分とする金属がより好ましい。ここで「主成分」とは、金属粒子を構成する成分の中で、最も含有量の多い成分のことをさす。
　金属粒子（ａ１）のタップ密度は、特に限定されないが、被接着材料への接着強度を確保するために、４ｇ／ｃｍ３以上であることが好ましく、５ｇ／ｃｍ３以上であることがより好ましく、５．５ｇ／ｃｍ３以上であることがさらに好ましい。また、導電性接着剤組成物を長期保管した際に金属粒子（ａ１）が沈降し不安定になることを防ぐために、８ｇ／ｃｍ３以下であることが好ましく、７．５ｇ／ｃｍ３以下であることがより好ましく、７ｇ／ｃｍ３以下であることがさらに好ましい。タップ密度は、例えばＪＩＳ規格Ｚ２５１２：２０１２の金属粉－タップ密度測定方法により測定され算出される。
　金属粒子（ａ１）の比表面積は、特に限定されないが、０．１ｍ２／ｇ以上であることが好ましく、より好ましくは０．２ｍ２／ｇ以上であり、さらに好ましくは０．３ｍ２／ｇ以上である。また、金属粒子（ａ１）の比表面積は、３ｍ２／ｇ以下であることが好ましく、より好ましくは２ｍ２／ｇ以下であり、さらに好ましくは１ｍ２／ｇ以下である。
　また、金属粒子（ａ１）の比表面積は、０．１～３ｍ２／ｇであることが好ましく、より好ましくは０．２～２ｍ２／ｇであり、さらに好ましくは０．３～１ｍ２／ｇである。
　金属粒子（ａ１）の比表面積が０．１ｍ２／ｇ以上であることにより、被接着材料に接する金属粒子（ａ１）の表面積が確保できる。また、金属粒子（ａ１）の比表面積が３ｍ２／ｇ以下であることにより、導電性組成物に添加する溶剤量を少なくできる。
　金属粒子（ａ１）の形状は特に限定されず、例えば、球状、フレーク状、プレート状、箔状および樹枝状等が挙げられる。一般的にはフレーク状または球状が選択される。また、金属粒子（ａ１）には、単一の金属からなる粒子のほか、２種以上の金属からなる表面被覆された金属粒子、またはこれらの混合物を用いることができる。
　＜銀粒子（ａ２）＞
　本発明の実施形態における銀粒子（ａ２）の平均粒子径は１０ｎｍ以上であり、好ましくは２０ｎｍ以上であり、より好ましくは３０ｎｍ以上であり、更に好ましくは４０ｎｍ以上である。また、本発明の実施形態における銀粒子（ａ２）の平均粒子径は２００ｎｍ以下であり、好ましくは１８０ｎｍ以下であり、より好ましくは１７０ｎｍ以下であり、更に好ましくは１６０ｎｍ以下である。
　本発明の実施形態における銀粒子（ａ２）の平均粒子径は１０～２００ｎｍであり、好ましくは２０～１８０ｎｍであり、より好ましくは３０～１７０ｎｍであり、更に好ましくは４０～１６０ｎｍである。
　銀粒子（ａ２）の平均粒子径が１０ｎｍ未満であると、銀粒子を被覆する有機物の除去が難しくなり焼結が進みにくい。銀粒子（ａ２）の平均粒子径が２００ｎｍを超えると比表面積が小さくなり銀粒子の焼結が進みにくい。
　銀粒子（ａ２）のタップ密度は、特に限定されないが、銀粒子の接触点を増やし焼結しやすくするために、４ｇ／ｃｍ３以上であることが好ましく、５ｇ／ｃｍ３以上であることがより好ましく、５．５ｇ／ｃｍ３以上であることがさらに好ましい。また、導電性接着剤組成物を長期保管した際に銀粒子（ａ２）が沈降し不安定になることを防ぐために、８ｇ／ｃｍ３以下であることが好ましく、７．５ｇ／ｃｍ３以下であることがより好ましく、７ｇ／ｃｍ３以下であることがさらに好ましい。タップ密度は、例えばＪＩＳ規格Ｚ２５１２：２０１２の金属粉－タップ密度測定方法により測定され算出される。
　銀粒子（ａ２）の形状は特に限定されず、例えば、球状、キュービック状、ロッド状等が挙げられる。また、銀粒子（ａ２）には、純銀粒子のほか、銀で表面被覆された金属粒子、またはこれらの混合物を用いることができる。
　銀粒子（ａ２）は、その表面がコーティング剤で被覆されていてもよい。用いるコーティング剤や被覆方法は特に限定されないが、例えば、アミンまたはカルボン酸の官能基を含むコーティング剤が挙げられる。中でも、カルボン酸の官能基を含むコーティング剤を用いることによって、導電性接着剤組成物の放熱性をより一層向上させることができるため好ましい。
　また、不活性ガス雰囲気下での導電性接着剤組成物の硬化を容易にするためには、コーティング剤は加熱時に除去されやすいものが望ましく、官能基はカルボン酸であることが好ましい。カルボン酸の官能基を含むコーティング剤としては、特に限定されず、例えば、モノカルボン酸、ポリカルボン酸およびオキシカルボン酸等が挙げられる。コーティング剤に含まれるカルボン酸は２種以上の混合物であってもよい。また、コーティング剤は炭素数１２～２４の飽和脂肪酸または不飽和脂肪酸である高級脂肪酸が好ましい。
　銀粒子（ａ２）の表面をコーティング剤で被覆する方法としては、例えば、両者をミキサー中で撹拌、混練する方法、銀粒子（ａ２）にカルボン酸の溶液を含浸して溶剤を揮発させる方法等の公知の方法が挙げられる。
　本発明の実施形態の導電性接着剤組成物において、導電性や熱伝導率の向上、及び塗工性の確保のために、金属粒子（ａ１）の含有量は導電性接着剤組成物の全体量に対して３５質量％以上であることが好ましく、４０質量％以上であることがより好ましく、４５質量％以上であることがさらに好ましい。また、金属粒子（ａ１）の含有量は導電性接着剤組成物の全体量に対して８５質量％以下であることが好ましく、７５質量％以下であることがより好ましく、６５質量％以下であることがさらに好ましい。
　本発明の実施形態の導電性接着剤組成物において、金属粒子（ａ１）の含有量は導電性接着剤組成物の全体量に対して３５～８５質量％であることが好ましく、４０～７５質量％であることがより好ましく、４５～６５質量％であることがさらに好ましい。
　また、銀粒子（ａ２）の含有量は、導電性接着剤組成物の全体量に対して５質量％以上であることが好ましく、１０質量％以上であることがより好ましく、１５質量％以上であることがさらに好ましい。また、銀粒子（ａ２）の含有量は、導電性接着剤組成物の全体量に対して５０質量％以下であることが好ましく、４０質量％以下であることがより好ましく、３５質量％以下であることがさらに好ましい。
　また、銀粒子（ａ２）の含有量は、導電性接着剤組成物の全体量に対して５～５０質量％であることが好ましく、１０～４０質量％であることがより好ましく、１５～３５質量％であることがさらに好ましい。
　また、本発明の実施形態の導電性接着剤組成物において、熱伝導率を向上させるために、金属粒子（ａ１）と銀粒子（ａ２）との含有比率は、質量比で９５：５～４０：６０の範囲であることが好ましく、９０：１０～５０：５０の範囲であることがより好ましく、８５：１５～６０：４０の範囲であることがさらに好ましい。
　なお、本発明の実施形態の導電性接着剤組成物においては、本発明の効果を損なわない限りにおいて、他の導電性フィラーを併用することができる。そのような導電性フィラーとしては、導電性を有するものであれば特に限定はされないが、例えばカーボンナノチューブなどが挙げられる。
　［熱可塑性樹脂の粒子（Ｂ）］
　本発明の実施形態の導電性接着剤組成物は、平均粒子径２～１４μｍ、融点が１３０～２５０℃の熱可塑性樹脂の粒子（Ｂ）をさらに含有する。
　通常、本発明のようにナノメートルオーダーの銀粒子を含有する導電性接着剤組成物の硬化物（以下、単に「導電性接着剤硬化物」ともいう）は、緻密な構造を有するため応力緩和性能が低い。さらに、繰り返しの温度変化を受けることにより金属が成長し、このことによって応力緩和性能がさらに低下する。そのため、ナノメートルオーダーの銀粒子を含有する導電性接着剤組成物による接着では、被接着材料同士の線熱膨張率の差により生じる応力によって、被接着材料の剥離が生じやすい。
　しかし、熱可塑性樹脂の粒子（Ｂ）を含有する本発明の実施形態の導電性接着剤組成物では、熱を加えて硬化させる際に、熱可塑性樹脂の粒子（Ｂ）が溶融し、導電性接着剤硬化物内の空隙を充填する。このことにより、導電性接着剤硬化物内での金属の移動が妨げられ、上記のように、金属の成長によって応力による被接着材料の剥離が生じやすくなることを防いでいるものと考えられる。
　他にも、導電性接着剤硬化物内の空隙に充填された熱可塑性樹脂が弾性変形することによって応力を緩和することが可能となり、導電性接着剤硬化物の応力緩和性能が向上すること、また、熱可塑性樹脂が導電性接着剤硬化物と被接着材料の接着界面に存在する空隙を充填することにより、接着強度が向上することも、繰り返しの温度変化による剥離の抑制に寄与していると考えられる。
　また、熱可塑性樹脂の粒子（Ｂ）には、導電性接着剤硬化物における亀裂の発生や進展を抑制する効果もある。本発明の実施形態の導電性接着剤組成物の硬化物の内部には溶融した熱可塑性樹脂が分散しているが、この樹脂が、亀裂先端の応力を分散する効果、亀裂にぶつかって亀裂の進展を止める効果、変形して亀裂進展のエネルギーを消費させる効果などを奏することにより、亀裂の発生及び進展を抑制することができる。
　上述の剥離抑制の効果を得るには、熱可塑性樹脂の粒子（Ｂ）が導電性接着剤組成物の硬化の際に溶融して、導電性接着剤硬化物内の空隙を充填する必要がある。導電性接着剤組成物の硬化の際の適切な加熱温度は、例えば導電性フィラー（Ａ）の種類等、様々な条件により変化するが、通常１３０～２５０℃である。したがって本発明の実施形態においては、導電性接着剤組成物の硬化の際に熱硬化性樹脂の粒子（Ｂ）が十分に溶融するように、熱可塑性樹脂の粒子（Ｂ）の融点は２５０℃以下とする。また、熱可塑性樹脂の粒子（Ｂ）の融点は、２３０℃以下が好ましく、２００℃以下がより好ましい。
　一方、導電性接着剤組成物の硬化の際に導電性フィラー（Ａ）の焼結より先に熱可塑性樹脂の粒子（Ｂ）が溶融すると、導電性フィラー（Ａ）の焼結を妨げる恐れがある。導電性フィラー（Ａ）の焼結温度はその種類等によっても異なるが、通常は１３０℃以下である。したがって本発明の実施形態においては、導電性フィラー（Ａ）の焼結より先に熱可塑性樹脂の粒子（Ｂ）が溶融しないように、熱可塑性樹脂の粒子（Ｂ）の融点は１３０℃以上とする。また、熱可塑性樹脂の粒子（Ｂ）の融点は、１４０℃以上が好ましく、１５０℃以上がより好ましく、１６０℃以上がさらに好ましい。
　また、上述の剥離抑制の効果を得るには、熱可塑性樹脂の粒子（Ｂ）の平均粒子径も重要となる。
　熱可塑性樹脂の粒子（Ｂ）の平均粒子径が大きいと、同じ量での個数が少なくなり、応力を分散する効果が乏しくなる。また、熱可塑性樹脂の粒子（Ｂ）の平均粒子径が大きいと接着剤層の厚み方向に対しての樹脂粒子の存在比率が非常に高い箇所ができるが、このような箇所は接着剤層内の脆弱点になりえる。
　また、熱可塑性樹脂の粒子（Ｂ）の平均粒子径が大きすぎると、接着剤層を薄くできなくなり、半導体素子等の被着体から発生した熱を効率よく逃がせなくなるため、この観点からも熱可塑性樹脂の粒子（Ｂ）の平均粒子径が大きすぎることは好ましくない。
　上記より、熱可塑性樹脂の粒子（Ｂ）の平均粒子径は、１４μｍ以下とする。また、熱可塑性樹脂の粒子（Ｂ）の平均粒子径は、１３μｍ以下が好ましい。
　一方、平均粒子径が小さすぎると応力緩和の能力および亀裂進展抑制効果が乏しくなる。
　上記より、熱可塑性樹脂の粒子（Ｂ）の平均粒子径は、２μｍ以上とする。また、熱可塑性樹脂の粒子（Ｂ）の平均粒子径は、３μｍ以上が好ましい。
　本発明の実施形態における熱可塑性樹脂の粒子（Ｂ）としては、上記の融点及び平均粒子径の条件をみたす公知の樹脂の粒子であってよい。例えば、ナイロン１１、ナイロン１２、ナイロン６等の公知のポリアミド、ＡＳ樹脂、ＡＢＳ樹脂、ＡＥＳ樹脂、酢酸ビニル樹脂、ポリスチレン、ポリエチレン、ポリプロピレン、ポリ塩化ビニル、アクリル樹脂、メタクリル樹脂、ポリビニルアルコール樹脂、ポリビニルエーテル、ポリアセタール、ポリカーボネート、ポリエチレンテレフタレート、ポリブチレンテレフタレート、ポリビニルブチラール、ポリビニルホルマール、ポリスルホン、ポリエーテルスルホン、ポリイミド、フェノキシ樹脂ポリエーテルイミド、エチルセルロース、酢酸セルロース、各種のフッ素樹脂、ポリオレフィンエラストマー、シリコーン樹脂等の粒子が挙げられ、これらの混合物や共重合体（コポリマー）であっても良い。
　本発明の実施形態における熱可塑性樹脂の粒子（Ｂ）の形状は特に限定されず、例えば、略球状、立方体状、円柱状、角柱状、円錐状、角錐状、フレーク状、箔状および樹枝状等が挙げられるが、略球状、立方体状が好ましい。
　本発明の実施形態の導電性接着剤組成物において、繰り返し温度変化を受けた場合の被接着材料の剥離を高い水準で防止するために、熱可塑性樹脂の粒子（Ｂ）の含有量は導電性接着剤組成物の全体量に対して０．１質量％以上であることが好ましく、０．５質量％以上であることがより好ましく、１質量％以上であることがさらに好ましく、２質量％以上であることが特に好ましい。
　また、熱可塑性樹脂の粒子（Ｂ）を過剰に含有することによって導電性接着剤硬化物の熱伝導率が低下することを防止するため、熱可塑性樹脂の粒子（Ｂ）の含有量は導電性接着剤組成物の全体量に対して１０質量％以下であることが好ましく、７質量％以下であることがより好ましく、５質量％以下であることがさらに好ましい。
　［その他の成分］
　＜バインダ樹脂＞
　本発明の実施形態の導電性接着剤組成物において、導電性フィラー（Ａ）、及び熱可塑性樹脂の粒子（Ｂ）は、バインダ樹脂中に分散されてもよい。バインダ樹脂は特に限定されないが、例えば、エポキシ樹脂、フェノール樹脂、ウレタン樹脂、アクリル樹脂、シリコーン樹脂又はポリイミド樹脂等を用いることができ、これらを単独で用いても、複数種類組み合わせて用いてもよい。作業性の観点から本発明の実施形態におけるバインダ樹脂は熱硬化性樹脂であることが好ましく、エポキシ樹脂であることが特に好ましい。
　バインダ樹脂の含有量は、導電性接着剤組成物の全体量に対して１０質量％以下であることが好ましく、８質量％以下であることがより好ましく、６質量％以下であることがさらに好ましい。バインダ樹脂の含有量が１０質量％以下であると、導電性フィラーのネッキングによるネットワークが形成され易く、安定した導電性および熱伝導性が得られる。またバインダ樹脂を含有させる場合は、０．５質量％以上用いることが好ましい。
　＜硬化剤＞
　また、本発明の実施形態の導電性接着剤組成物は、上記成分のほかにも、例えば、硬化剤を含有していてもよい。硬化剤としては、例えば、三級アミン、アルキル尿素、イミダゾール等のアミン系硬化剤や、フェノール系硬化剤等が挙げられる。
　硬化剤の含有量は導電性接着剤組成物の全体量に対して２質量％以下であることが好ましい。そうすることで未硬化の硬化剤が残りにくくなり、被接着材料との密着性が良好となる為である。
　＜硬化促進剤＞
　本発明の実施形態の導電性接着剤組成物には硬化促進剤を配合することもできる。硬化促進剤としては、例えば、２－フェニル－４，５－ジヒドロキシメチルイミダゾール、２－フェニル－４―メチル－５－ヒドロキシメチルイミダゾール、２―メチル－４－メチルイミダゾール、１－シアノ－２－エチル－４－メチルイミダゾール等のイミダゾール類、第３級アミン類、トリフェニルフォスフィン類、尿素系化合物、フェノール類、アルコール類、カルボン酸類等が例示される。硬化促進剤は１種類だけ使用しても２種類以上を併用してもよい。
　硬化促進剤の配合量は限定されるものではなく適宜決定すればよいが、使用する場合は一般には、本発明の実施形態の導電性接着剤組成物の全体量に対して０．５質量％以下である。
　＜溶剤＞
　本発明の実施形態の導電性接着剤組成物には、さらに導電性接着剤組成物をペースト状にするために溶剤を含んでいてもよい。溶剤を含む場合は、ペースト中において熱可塑性樹脂の粒子（Ｂ）の形状を維持するために、これを溶解しない性質の溶剤を用いる。その他は特に限定されないが、導電性接着剤組成物の硬化の際に溶剤が揮発しやすいことから沸点３５０℃以下のものが好ましく、沸点３００℃以下のものがより好ましい。具体的にはアセテート、エーテル、炭化水素等が挙げられ、より具体的には、ジブチルカルビトール、ブチルカルビトールアセテート等が好ましく用いられる。
　溶剤の含有率は、導電性接着剤組成物に対して通常１５質量％以下であり、作業性の観点から好ましくは１０質量％以下である。
　本発明の実施形態の導電性接着剤組成物には、上記成分の他にも、酸化防止剤、紫外線吸収剤、粘着付与剤、粘性調整剤、分散剤、カップリング剤、強靭性付与剤、エラストマー等を、本発明の実施形態の効果を損なわない範囲で適宜配合することができる。
　本発明の実施形態の導電性接着剤組成物は、上記の（Ａ）及び（Ｂ）並びにその他の成分を任意の順序で混合、撹拌することにより得ることができる。分散方法としては、例えば、二本ロール、三本ロール、サンドミル、ロールミル、ボールミル、コロイドミル、ジェットミル、ビーズミル、ニーダー、ホモジナイザー、及びプロペラレスミキサー等の方式を採用することができる。
　本発明の実施形態の導電性接着剤硬化物は、上記導電性接着剤組成物を熱処理して硬化させることにより得られる。
　本発明の実施形態の導電性接着剤組成物を硬化させる際の加熱の温度は特に限定はされないが、導電性フィラー（Ａ）同士、及び、被接着材料と導電性フィラー（Ａ）との間に、互いに点接触した近接状態を形成させ、接着部としての形状を安定させるために１５０℃以上であることが好ましく、１８０℃以上であることがより好ましく、２００℃以上であることがさらに好ましい。
　また、導電性フィラー（Ａ）同士の結合が過度に進行し導電性フィラー（Ａ）間のネッキングが生じて強固に結合し、硬すぎる状態となることを避けるために３００℃以下であることが好ましく、２７５℃以下であることがより好ましく、２５０℃以下であることがさらに好ましい。
　また、上記加熱の時間は、導電性フィラー（Ａ）の焼結が十分に進行するような時間であれば特に限定はされないが、通常は０．５～３時間である。
　上記加熱は、空気中でおこなってもよく、Ｎ２などの不活性ガス中でおこなってもよい。空気中で加熱すると、導電性フィラー（Ａ）の表面のコーティング剤の除去が進みやすいため、焼結を行いやすいが、導電性フィラー（Ａ）が酸化されやすいため、得られる導電性接着剤硬化物の導電性や熱伝導率が損なわれるおそれがある。また、空気中で加熱すると、酸化しやすい被着体（例えばＣｕ基板など）を用いた場合に被着体が酸化して接合が阻害されたり、他にも酸化されやすい周辺部材が酸化されて劣化したりするおそれもある。
　したがって、上記のような問題の発生を回避するためには、Ｎ２などの不活性ガス中で加熱を行うことが好ましい。また、不活性ガス中で加熱を行う場合は、金属粒子（ａ１）及び銀粒子（ａ２）のコーティング剤として先述の適切なものを採用することが好ましい。
　半導体素子等の被着体から発生した熱を効率よく逃がすためには、導電性接着剤硬化物は薄いことが好ましい。具体的には、導電性接着剤硬化物の厚みは５０μｍ以下が好ましく、４０μｍ以下がより好ましく、３０μｍ以下が更に好ましい。
　一方、基板等の被着体の熱膨張差から発生する内部応力を接着剤層厚み方向で担うため導電性接着剤硬化物は厚い方が望ましい。具体的には、導電性接着剤硬化物の厚みは５μｍ以上が好ましく、１０μｍ以上がより好ましく、２０μｍ以上が更に好ましい。
　本発明の実施形態の導電性接着剤硬化物の熱伝導率は、被接着材料の放熱性を確保するために、２０Ｗ／ｍ・Ｋ以上であることが好ましく、３５Ｗ／ｍ・Ｋ以上であることがより好ましく、５０Ｗ／ｍ・Ｋ以上であることがさらに好ましい。なお、導電性接着剤硬化物の熱伝導率は、実施例の欄において後述する方法を用いて算出することができる。
　本発明の実施形態の導電性接着剤組成物を用いて被接着材料を接着した場合に、繰り返し温度変化を受けた場合にも被接着材料の剥離が生じにくくなっていることを評価する方法としては、種々の方法が挙げられるが、例えば、実施例の欄において後述する方法で冷熱サイクル試験を行い、試験後の剥離面積の割合を実施例の欄において後述する方法で測定する方法が挙げられる。当該方法で測定した剥離面積の割合は１５％以下であることが好ましく、１０％以下であることがより好ましく、５％以下であることがさらに好ましい。
　本発明の実施形態の導電性接着剤組成物は、電子機器における部品の接着に用いることができる。
　以下、実施例により本発明をさらに具体的に説明するが、本発明はこれらの実施例により何ら限定されるものではない。
　Ａ．導電性接着剤組成物の調製
　表１～３に記載された各材料を三本ロールにて混練し、表１～３に示す組成の導電性接着剤組成物を調製した（各材料の数値は導電性接着剤組成物の総質量に対する質量％を表す）。使用した材料は下記の通りである。なお、混練の順番は、金属粒子（ａ１）、銀粒子（ａ２）、熱可塑性樹脂の粒子（Ｂ）、バインダ樹脂、硬化剤、硬化促進剤、溶剤の順である。
　［導電性フィラー（Ａ）］
　＜金属粒子（ａ１）＞
・銀粒子（１）：フレーク状、平均粒子径ｄ５０：５．５μｍ、タップ密度：７．０ｇ／ｃｍ３、田中貴金属工業社製
・銀粒子（２）：フレーク状、平均粒子径ｄ５０：４μｍ、タップ密度：６．７ｇ／ｃｍ３、田中貴金属工業社製
・銀粒子（３）：球状、平均粒子径ｄ５０：０．８μｍ、タップ密度：５．５ｇ／ｃｍ３、田中貴金属工業社製
・銅粒子：球状、平均粒子径ｄ５０：５μｍ、タップ密度：５．０ｇ／ｃｍ３、三井金属鉱業社製
　＜銀粒子（ａ２）＞
・銀粒子（４）：球状、平均粒子径ｄ５０：０．０９μｍ、田中貴金属工業社製、コーティング剤としてカルボキシル基を有する高分子分散剤（ビッグケミー製、「ディスパービック１９０」、親水性ユニットであるポリエチレンオキサイド鎖と疎水性ユニットであるアルキル基とを有する両親媒性分散剤、溶媒：水、不揮発成分４０％、酸価１０ｍｇＫＯＨ／ｇ、アミン価０）
・銀粒子（５）：球状、平均粒子径ｄ５０：０．１６μｍ、田中貴金属工業社製、コーティング剤としてオレイン酸
・銀粒子（６）：球状、平均粒子径ｄ５０：０．１０μｍ、田中貴金属工業社製、コーティング剤としてドデシルアミン
　［熱可塑性樹脂の粒子（Ｂ）］
・熱可塑性樹脂粒子（１）：「ＳＰ－５００」（商品名）、東レ社製、ナイロン１２製、平均粒子径ｄ５０：５μｍ、球状、融点：１６５～１７１℃
・熱可塑性樹脂粒子（２）：「ＳＰ－１０」（商品名）、東レ社製、ナイロン１２製、平均粒子径ｄ５０：１０μｍ、球状、融点：１６５～１７１℃
・熱可塑性樹脂粒子（３）：「ＰＭ－２００」（商品名）、三井化学社製、ポリエチレン製、平均粒子径ｄ５０：１０μｍ、球状、融点：１３６℃
・熱可塑性樹脂粒子（４）：東レ社製「ＳＰ－５００」（商品名）を分級して得られた粒子、ナイロン１２製、分級後の平均粒子径ｄ５０：３μｍ（分級前のｄ５０は５μｍ）、球状、融点：１６５～１７１℃
・熱可塑性樹脂粒子（５）：東レ社製「ＳＰ－１０」（商品名）を分級して得られた粒子、ナイロン１２製、分級後の平均粒子径ｄ５０：１５μｍ（分級前のｄ５０は１０μｍ）、球状、融点：１６５～１７１℃
・熱可塑性樹脂粒子（６）：「Ｏｒａｇａｓｏｌ３５０１ＥＸＤ」（商品名）、アルケマ社製、ナイロン１２およびナイロン６の共重合体製、平均粒子径ｄ５０：１０μｍ、球状、融点：１４２℃
・熱可塑性樹脂粒子（７）：「ＴＲ-１」（商品名）、東レ社製、ナイロン６製、平均粒子径ｄ５０：１３μｍ、球状、融点：２１５℃
　［バインダ樹脂・硬化剤・硬化促進剤・溶剤］
・エポキシ樹脂（１）：「ＥＰＩＣＬＯＮ　８３０－Ｓ」（商品名）、大日本インキ化学工業社製、室温で液状、エポキシ当量：１６９ｇ／ｅｑ
・エポキシ樹脂（２）：「ＥＲＩＳＹＳ　ＧＥ－２１」（商品名）、ＣＶＣ社製、室温で液状、エポキシ当量：１２５ｇ／ｅｑ
・硬化剤：フェノール系硬化剤（ＭＥＨ８０００Ｈ、明和化成社製）
・硬化剤促進：２－フェニル－４，５－ジヒドロキシメチルイミダゾール（２ＰＨＺ、四国化成社製）
・溶剤（１）：ジブチルカルビトール（東京化成工業社製）
・溶剤（２）：ブチルカルビトールアセテート（東京化成工業社製）
　Ｂ．物性評価
　得られた導電性接着剤組成物を１０ｍｍ×１０ｍｍの銀メッキした銅リードフレームに塗布し、塗布面に５ｍｍ×５ｍｍの銀スパッタリングシリコンチップを戴置後、窒素雰囲気下、２５０℃で６０分加熱し、銀メッキした銅リードフレームと銀スパッタリングしたシリコンチップが導電性接着剤硬化物により接合された金属接合体（以下、単に「金属接合体」ともいう）を作製した。得られた金属接合体について、以下に示す方法で物性評価を行った。
　＜熱伝導率＞
　得られた金属接合体の熱伝導率を表１～３に示す。
　熱伝導率λ（Ｗ／ｍ・Ｋ）は、レーザーフラッシュ法熱定数測定装置　（「ＴＣ－７０００」（商品名）、ＵＬＶＡＣ－ＲＩＫＯ社製）を用いてＡＳＴＭ－Ｅ１４６１に準拠して熱拡散ａを測定し、ピクノメーター法により室温での比重ｄを算出し、また、示差走査熱量測定装置（「ＤＳＣ７０２０」（商品名）、セイコー電子工業社製）を用いてＪＩＳ－Ｋ７１２３　２０１２に準拠して室温での比熱Ｃｐを測定して、関係式λ＝ａ×ｄ×Ｃｐにより算出した。
　＜剥離試験１＞
　また、得られた金属接合体を用いて冷熱サイクル試験を行い、剥離面積を測定した。この試験では、基板を－５０℃に３０分間保持した後に１５０℃に３０分間保持する操作を１サイクルとして２０００サイクル繰返し、試験後のシリコンチップの剥離面積の割合を測定した。結果を表１～３に示す。
　なお、剥離面積の割合は、２０００サイクル後の超音波映像・検査装置「Ｆｉｎｅ　ＳＡＴ」（商品名）で得られた剥離状態の画像を二値化ソフト「ｉｍａｇｅ　Ｊ」で濃淡を白と黒の二階調に画像変換し、以下の関係式で求めた。
　剥離面積の割合（％）＝剥離面積（黒色画素数）÷チップ面積（黒色画素数＋白色画素数）×１００
　＜剥離試験２＞
　冷却及び加熱のサイクル数を３０００サイクルとした点以外は剥離試験１と同様にして、剥離試験２を行った。結果を表１～３に示す。なお、表１～３の剥離試験２の欄の「‐」は、剥離試験２を行っていないことを意味する。
Figure JPOXMLDOC01-appb-T000001
Figure JPOXMLDOC01-appb-T000002
Figure JPOXMLDOC01-appb-T000003
　表１～３に示すように、実施例の導電性接着剤組成物で得られた金属接合体は、比較例の導電性接着剤組成物で得られた金属接合体と比べて冷熱サイクル試験後の剥離面積が少なかった。また、熱伝導率も良好な値であった。
　この結果から、本発明の実施形態の導電性接着剤組成物によれば、熱伝導性に優れ、さらに繰り返し温度変化を受けた場合にも被接着材料の剥離が生じにくい接着を達成できることが確認された。
　本発明を特定の態様を用いて詳細に説明したが、本発明の意図と範囲を離れることなく様々な変更及び変形が可能であることは、当業者にとって明らかである。なお本出願は、２０１９年１月１０日付で出願された日本特許出願（特願２０１９－００２８２２）に基づいており、その全体が引用により援用される。

Claims (7)

  1. 　平均粒子径０．５～１０μｍの金属粒子（ａ１）と平均粒子径１０～２００ｎｍの銀粒子（ａ２）とを含む導電性フィラー（Ａ）と、
    　平均粒子径２～１４μｍの熱可塑性樹脂の粒子（Ｂ）と、を含有し、
    　前記熱可塑性樹脂の融点が、１３０～２５０℃である導電性接着剤組成物。
  2. 　前記金属粒子（ａ１）の主成分が銀である請求項１に記載の導電性接着剤組成物。
  3. 　前記導電性接着剤組成物の全体量に対して、前記金属粒子（ａ１）を３５～８５質量％、前記銀粒子（ａ２）を５～５０質量％の範囲で含有する請求項１または２に記載の導電性接着剤組成物。
  4. 　前記金属粒子（ａ１）と前記銀粒子（ａ２）との含有比率が、質量比で９５：５～４０：６０の範囲である請求項１～３のいずれか１項に記載の導電性接着剤組成物。
  5. 　前記導電性接着剤組成物の全体量に対して、前記熱可塑性樹脂の粒子（Ｂ）を０．１～１０質量％の範囲で含有する請求項１～４のいずれか１項に記載の導電性接着剤組成物。
  6. 　請求項１～５のいずれか１項に記載の導電性接着剤組成物を硬化した、導電性接着剤硬化物。
  7. 　請求項１～５のいずれか１項に記載の導電性接着剤組成物を部品の接着に使用した電子機器。
PCT/JP2019/051028 2019-01-10 2019-12-25 導電性接着剤組成物 Ceased WO2020145170A1 (ja)