WO2020130677A1 - 버링성이 우수한 고강도 냉연강판 및 합금화 용융아연도금강판과 이들의 제조방법 - Google Patents

버링성이 우수한 고강도 냉연강판 및 합금화 용융아연도금강판과 이들의 제조방법 Download PDF

Info

Publication number
WO2020130677A1
WO2020130677A1 PCT/KR2019/018109 KR2019018109W WO2020130677A1 WO 2020130677 A1 WO2020130677 A1 WO 2020130677A1 KR 2019018109 W KR2019018109 W KR 2019018109W WO 2020130677 A1 WO2020130677 A1 WO 2020130677A1
Authority
WO
WIPO (PCT)
Prior art keywords
steel sheet
rolled steel
ferrite
cold rolled
cold
Prior art date
Application number
PCT/KR2019/018109
Other languages
English (en)
French (fr)
Inventor
조항식
곽재현
Original Assignee
주식회사 포스코
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 포스코 filed Critical 주식회사 포스코
Priority to CN201980081736.7A priority Critical patent/CN113195773B/zh
Priority to EP19899805.6A priority patent/EP3901314A4/en
Priority to JP2021534952A priority patent/JP7267428B2/ja
Priority to US17/312,753 priority patent/US20220056563A1/en
Publication of WO2020130677A1 publication Critical patent/WO2020130677A1/ko

Abstract

본 발명의 일 측면에 따른 버링성이 우수한 고강도 냉연강판은, 중량%로, 탄소(C): 0.13~0.25%, 실리콘(Si): 1.0~2.0%, 망간(Mn): 1.5~3.0%, 알루미늄(Al)+크롬(Cr)+몰리브덴(Mo): 0.08~1.5%, 인(P): 0.1% 이하, 황(S): 0.01% 이하, 질소(N): 0.01% 이하, 나머지 Fe 및 불가피한 불순물을 포함하고, 면적분율로, 페라이트: 3~25%, 마르텐사이트: 20~40%, 잔류 오스테나이트: 5~20%를 포함하고, 4/t 지점을 기준으로(여기서, t는 강판 두께를 의미함), 페라이트의 평균 결정립도가 2㎛ 이하이며, 강판 두께방향의 페라이트 길이에 대한 강판 압연방향의 페라이트 길이 비의 평균값이 1.5 이하일 수 있다.

Description

버링성이 우수한 고강도 냉연강판 및 합금화 용융아연도금강판과 이들의 제조방법
본 발명은 냉연강판 및 합금화 용융아연도금강판과 이들의 제조방법에 관한 것이며, 상세하게는 고강도 특성을 가지면서도 버링성을 효과적으로 향상시킨 냉연강판 및 합금화 용융아연도금강판과 이들의 제조방법에 관한 것이다.
자동차용 강판은 지구환경 보존을 위한 연비 규제와 충돌 등 사고 시의 탑승자 안정성을 확보하기 위하여, 고강도 강재의 채용을 늘려가고 있다. 자용차용 강재의 등급은 통상 인장강도와 연신율의 곱(TS×EL)으로 나타내는 경우가 많으며, 반드시 이로 제한되는 것은 아니지만 TS×EL이 25,000MPa·% 미만인 AHSS(Advanced High Strength Steel), 50,000MPa·%를 초과하는 UHSS(Ultra High Strength Steel), 그리고 AHSS와 UHSS 사이의 값을 가지는 X-AHSS(Extra-Advanced High Strength Steel) 등이 대표적인 예로 제시될 수 있다.
강재의 등급이 정해지면, 인장강도와 연신율의 곱이 대략 일정하게 결정되는 것이기 때문에, 강재의 인강강도와 연신율을 동시에 만족시키는 것이 용이하지 않다. 인장강도와 연신율은 서로 반비례하는 것이 일반적인 강재의 특성이기 때문이다.
강재의 강도와 연신율의 곱을 높이기 위하여 새로운 개념을 가지는 강재로서, 강재 내에 잔류 오스테나이트가 존재하여 가공성과 강도 모두를 향상시킬 수 있는 소위 TRIP(TRansformation Induced Plasticity) 현상을 이용한 강재가 개발되었으며, 이와 같은 TRIP 강은 동일한 강도에서도 연신율이 향상되어 고성형성의 고강도 강재를 제조하는데 주로 활용되어 왔다.
그러나 이와 같은 종래의 강재는 인장강도나 연신율은 높은 수준으로 확보 가능하더라도, 버링성에는 취약하다는 문제점이 존재한다.
버링성은 강재의 구멍 확장 가공성을 평가하는 물성으로 널리 이용되었으나, 최근에는 버링성이 반드시 강재의 구멍 확장 가공성을 평가하는 물성만으로 국한되어 해석되는 것은 아니다. 즉, 극심한 가공을 받는 강재에서 버링성이 충분히 확보되지 않으면 강재의 파손을 방지하기 어려우므로, 버링성은 극심한 가공 조건에서 강재의 파손 저항성을 확인할 수 있는 지표로 이용될 수 있다. 즉, 냉간 프레스 가공과 같이 극심한 조건에서 가공되는 자동차용 강재의 경우, 가공에 의한 강재의 파손을 방지하기 위하여 고강도 특성뿐만 아니라 우수한 버링성이 요구된다.
(선행기술문헌)
(특허문헌 1) 일본 공개특허공보 특개2014-019905호 (2014.02.03. 공개)
본 발명의 한 가지 측면에 따르면 버링성이 우수한 고강도 냉연강판 및 합금화 용융아연도금강판과 이들의 제조방법이 제공될 수 있다.
본 발명의 과제는 상술한 내용에 한정되지 않는다. 통상의 기술자라면 본 명세서의 전반적인 내용으로부터 본 발명의 추가적인 과제를 이해하는데 아무런 어려움이 없을 것이다.
본 발명의 일 측면에 따른 버링성이 우수한 고강도 냉연강판은, 중량%로, 탄소(C): 0.13~0.25%, 실리콘(Si): 1.0~2.0%, 망간(Mn): 1.5~3.0%, 알루미늄(Al)+크롬(Cr)+몰리브덴(Mo): 0.08~1.5%, 인(P): 0.1% 이하, 황(S): 0.01% 이하, 질소(N): 0.01% 이하, 나머지 Fe 및 불가피한 불순물을 포함하고, 면적분율로, 페라이트: 3~25%, 마르텐사이트: 20~40%, 잔류 오스테나이트: 5~20%를 포함하고, 4/t 지점을 기준으로(여기서, t는 강판 두께를 의미함), 페라이트의 평균 결정립도가 2㎛ 이하이며, 강판 두께방향의 페라이트 길이에 대한 강판 압연방향의 페라이트 길이 비의 평균값이 1.5 이하일 수 있다.
상기 냉연강판은 면적분율로 15~50%의 베이나이트를 더 포함할 수 있다.
상기 마르텐사이트는 템퍼드 마르텐사이트 및 프레시 마르텐사이트로 이루어지며, 상기 전체 마르텐사이트 중 상기 템퍼드 마르텐사이트가 차지하는 비율은 50면적%를 초과할 수 있다.
상기 냉연강판은 3~15면적%의 페라이트를 포함할 수 있다.
상기 강판 두께방향의 페라이트 길이에 대한 강판 압연방향의 페라이트 길이 비의 평균값이 0.5 이상일 수 있다.
상기 냉연강판은, 중량%로, 보론(B): 0.001~0.005% 및 티타늄(Ti): 0.005~0.04% 중 1종 이상을 더 포함할 수 있다.
상기 알루미늄(Al)은 0.01~0.09중량%의 함량으로 상기 냉연강판에 포함될 수 있다.
상기 크롬(Cr)은 0.01~0.7중량%의 함량으로 상기 냉연강판에 포함될 수 있다.
상기 크롬(Cr)은 0.2~0.6중량%의 함량으로 상기 냉연강판에 포함될 수 있다.
상기 몰리브덴(Mo)은 0.02~0.08중량%의 함량으로 상기 냉연강판에 포함될 수 있다.
상기 냉연강판은, 1180MPa 이상의 인장강도, 14% 이상의 연신율, 25% 이상의 구멍 확장비(Hole Expansion Ratio, HER)를 가질 수 있다.
상기 냉연강판의 구명 확장비(HER)는 30% 이상일 수 있다.
본 발명의 일 측면에 따른 버링성이 우수한 고강도 합금화 용융아연도금강판은, 소지강판 및 상기 소지강판의 표면 상에 형성된 합금화 용융아연도금층을 포함하며, 상기 소지강판은 상기 냉연강판일 수 있다.
본 발명의 일 측면에 따른 버링성이 우수한 고강도 냉연강판은, 중량%로, 탄소(C): 0.13~0.25%, 실리콘(Si): 1.0~2.0%, 망간(Mn): 1.5~3.0%, 알루미늄(Al)+크롬(Cr)+몰리브덴(Mo): 0.08~1.5%, 인(P): 0.1% 이하, 황(S): 0.01% 이하, 질소(N): 0.01% 이하, 나머지 Fe 및 불가피한 불순물을 포함하는 강재를 냉간압연 한 후, 상기 강재가 완전히 오스테나이트로 변태되도록 상기 강재를 가열하고, 상기 가열된 강재를 630~670℃의 서냉 정지온도까지 5~12℃/s의 냉각속도로 서냉한 후 서냉 정지온도에서 10~90초 동안 유지하고, 상기 서냉된 강재를 마르텐사이트 변태종료온도(Mf) 이상, 마르텐사이트 변태개시온도(Ms) 이하의 온도범위까지 7~30℃/s의 냉각속도로 급냉하고, 상기 급냉된 강재를 마르텐사이트 변태개시온도(Ms) 초과, 베이나이트 변태개시온도(Bs) 이하의 온도에서 300~600초 동안 유지하는 분배처리에 의해 제조될 수 있다.
상기 강재는, 중량%로, 보론(B): 0.001~0.005% 및 티타늄(Ti): 0.005~0.04% 중 1종 이상을 더 포함할 수 있다.
상기 알루미늄(Al)은 0.01~0.09중량%의 함량으로 상기 강재에 포함될 수 있다.
상기 크롬(Cr)은 0.01~0.7중량%의 함량으로 상기 강재에 포함될 수 있다.
상기 크롬(Cr)은 0.2%~0.6중량%의 함량으로 상기 강재에 포함될 수 있다.
상기 몰리브덴(Mo)은 0.02~0.08중량%의 함량으로 상기 강재에 포함될 수 있다.
본 발명의 일 측면에 따른 버링성이 우수한 고강도 합금화 용융아연도금강판은, 상기 냉연강판을 소지강판으로 하여 상기 소지강판의 표면에 용융아연도금층을 형성하고 합금화처리하여 제조될 수 있다.
상기 과제의 해결 수단은 본 발명의 특징을 모두 열거한 것은 아니며, 본 발명의 다양한 특징과 그에 따른 장점과 효과는 아래의 구체적인 실시예를 참조하여 보다 상세하게 이해될 수 있을 것이다.
본 발명의 일 측면에 따르면, 고강도 특성을 가지면서도 연신율 특성 및 버링성이 우수하여 자동차용 강판으로 특히 적합한 냉연강판 및 합금화 용융아연도금강판과 이들의 제조방법을 제공할 수 있다.
도 1은 시간에 대한 온도변화를 이용하여 본 발명의 제조공정을 개략적으로 나타낸 그래프이다.
도 2는 발명예 1의 미세조직을 주사전자현미경으로 관찰한 이미지이며, 도 3은 비교예 2의 미세조직을 주사전자현미경으로 관찰한 이미지이다.
본 발명은 버링성이 우수한 냉연강판 및 합금화 용융아연도금강판과 이들의 제조방법에 관한 것으로, 이하에서는 본 발명의 바람직한 실시예들을 설명하고자 한다. 본 발명의 실시예들은 여러 가지 형태로 변형될 수 있으며, 본 발명의 범위가 아래에서 설명되는 실시예들에 한정되는 것으로 해석되어서는 안된다. 본 실시예들은 당해 발명이 속하는 기술분야에서 통상의 지식을 가지는 자에게 본 발명을 더욱 상세하기 위하여 제공되는 것이다.
이하, 본 발명의 강 조성에 대하여 보다 상세히 설명한다. 이하, 특별히 달리 표시하지 않는 한, 이하, 특별히 달리 표시하지 않는 한 각 원소의 함량을 나타내는 %는 중량을 기준으로 한다.
본 발명의 일 측면에 냉연강판은, 중량%로, 탄소(C): 0.13~0.25%, 실리콘(Si): 1.0~2.0%, 망간(Mn): 1.5~3.0%, 알루미늄(Al)+크롬(Cr)+몰리브덴(Mo): 0.08~1.5%, 인(P): 0.1% 이하, 황(S): 0.01% 이하, 질소(N): 0.01% 이하, 나머지 Fe 및 불가피한 불순물을 포함할 수 있다. 또한, 본 발명의 일 측면에 따른 냉연강판은, 중량%로, 보론(B): 0.001~0.005% 및 티타늄(Ti): 0.005~0.04% 중 1종 이상을 더 포함할 수 있다. 상기 알루미늄(Al), 크롬(Cr) 및 몰리브덴(Mo)은 각각 중량%로, 0.01~0.09%, 0.01~0.7%, 0.02~0.08%의 함량으로 포함될 수 있다.
탄소(C) 0.13~0.25%
탄소(C)는 경제적으로 강도를 확보할 수 있는 중요한 원소이므로, 본 발명은 이러한 효과를 달성하기 위하여 탄소(C) 함량의 하한을 0.13%로 제한할 수 있다. 다만, 탄소(C)가 과다하게 첨가되는 경우, 용접성이 열화되는 문제점이 발생할 수 있으므로, 본 발명은 탄소(C) 함량의 상한을 0.25%로 제한할 수 있다. 따라서, 본 발명의 탄소(C) 함량은 0.15~0.25%의 범위일 수 있다. 바람직한 탄소(C) 함량은 0.14~0.25%의 범위일 수 있으며, 보다 바람직한 탄소(C) 함량은 0.14~0.20%의 범위일 수 있다.
실리콘(Si): 1.0~2.0%
실리콘(Si)은 강재의 강도 및 연신율을 효과적으로 향상시킬 수 있는 원소이므로, 본 발명은 이러한 효과를 달성하기 위하여 실리콘(Si) 함량의 하한을 1.0%로 제한할 수 있다. 실리콘(Si)은 표면 스케일 결함을 유발할 뿐만 아니라 도금강판의 표면특성을 저하시키고, 화성처리성을 떨어뜨리기 때문에 통상 실리콘(Si)의 함량은 1.0% 이하의 범위로 제한되는 경우가 많았으나, 최근 도금기술의 발전 등에 의해 강중 함량 2.0% 정도까지는 큰 문제없이 제조할 수 있게 되었으므로, 본 발명은 실리콘(Si) 함량의 상한을 2.0%로 제한할 수 있다. 따라서, 본 발명의 실리콘(Si) 함량은 1.0~2.0%의 범위일 수 있다. 바람직한 실리콘(Si) 함량은 1.2~2.0%의 범위일 수 있으며, 보다 바람직한 실리콘(Si) 함량은 1.2~1.8%의 범위일 수 있다.
망간(Mn): 1.5~3.0%
망간(Mn)은 강재 내에 존재할 경우 고용강화에 큰 역할을 할 수 있는 원소이며, 변태강화강에서 경화능 향상에 기여하는 원소이므로, 본 발명은 망간(Mn) 함량의 하한을 1.5%로 제한할 수 있다. 다만, 망간(Mn)이 과다하게 첨가되는 경우, 용접성과 냉갑압연 부하 등의 문제가 발생할 가능성이 높으며, 소둔 농화물 형성에 의해 덴트(dent)와 같은 표면결함을 유발할 수 있으므로, 본 발명은 망간(Mn) 함량의 상한을 3.0%로 제한할 수 있다. 따라서, 본 발명의 망간(Mn) 함량은 1.5~3.0%의 범위일 수 있다. 바람직한 망간(Mn) 함량은 2.0~3.0%의 범위일 수 있으며, 보다 바람직한 방간(Mn) 함량은 2.2~2.9%의 범위일 수 있다.
알루미늄(Al), 크롬(Cr) 및 몰리브덴(Mo)의 합: 0.08~1.5%
알루미늄(Al), 크롬(Cr) 및 몰리브덴(Mo)은 강도 증가 및 페라이트역 확장 원소로서 페라이트 분율을 확보하는데 유용한 원소이므로, 본 발명은 알루미늄(Al), 크롬(Cr) 및 몰리브덴(Mo) 함량의 합을 0.08% 이상으로 제한할 수 있다. 다만, 알루미늄(Al), 크롬(Cr) 및 몰리브덴(Mo)이 과다하게 첨가되는 경우, 슬라브의 표면 품질 저하 및 제조비용의 증가가 문제되므로, 본 발명은 알루미늄(Al), 크롬(Cr) 및 몰리브덴(Mo) 함량의 합을 1.5% 이하로 제한할 수 있다. 따라서, 본 발명의 알루미늄(Al), 크롬(Cr) 및 몰리브덴(Mo) 함량의 합은 0.08~1.5%의 범위일 수 있다.
알루미늄(Al): 0.01~0.09%
알루미늄(Al)은 강 중 산소(O)와 결합하여 탈산 작용을 하고, 실리콘(Si)과 같이 페라이트 내 탄소(C)를 오스테나이트로 분배하여 마르텐사이트 경화능을 향상시키는데 중요한 원소이므로, 본 발명은 이와 같은 효과 달성을 위해 알루미늄(Al) 함량의 하한을 0.01%로 제한할 수 있다. 다만, 알루미늄(Al)이 과다하게 첨가되는 경우, 연주 시 노즐막힘이 발생할 가능성이 있으며, 강도 증가에 따른 버링성 저하가 문제될 수 있으므로, 본 발명은 알루미늄(Al) 함량의 상한을 0.09%로 제한할 수 있다. 따라서, 본 발명의 알루미늄(Al) 함량은 0.01~0.09%의 범위일 수 있다. 바람직한 알루미늄(Al) 함량은 0.02~0.09%의 범위일 수 있으며, 보다 바람직한 알루미늄(Al) 함량은 0.02~0.08%의 범위일 수 있다. 본 발명에서 알루미늄(Al)이라 함은 산 가용성 Al(sol.Al)을 의미한다.
크롬(Cr): 0.01~0.7%
크롬(Cr)은 효과적인 경화능 향상 원소이므로, 본 발명은 강도 향상의 효과를 달성하기 위하여 크롬(Cr) 함량의 하한을 0.01%로 제한할 수 있다. 다만, 크롬(Cr)이 과다하게 첨가되는 경우 실리콘(Si)의 산화를 촉진시켜 열연재 표면의 적스케일 결함을 증가시키고, 최종 강재의 표면 품질을 저하를 유발하므로, 본 발명은 크롬(Cr) 함량의 상한을 0.7%로 제한할 수 있다. 따라서, 본 발명의 크롬(Cr) 함량은 0.2~0.7%의 범위일 수 있다. 바람직한 크롬(Cr) 함량은 0.1~0.7%의 범위일 수 있으며, 보다 바람직한 크롬(Cr) 함량은 0.2~0.6%의 범위일 수 있다.
몰리브덴(Mo): 0.02~0.08%
몰리브덴(Mo) 역시 경화능 향상에 효과적으로 기여하는 원소이므로, 본 발명은 강도 향상의 효과를 달성하기 위해 몰리브덴(Mo) 함량의 하한을 0.02%로 제한할 수 있다. 다만, 몰리브덴(Mo)은 고가의 원소로서 과다 첨가는 경제성 측면에서 바람직하지 않으며, 몰리브덴(Mo)이 과다하게 첨가되는 경우 강도가 과도하게 증가하여 버링성이 저하되는 문제가 발생하므로, 본 발명은 몰리브덴(Mo) 함량의 상한을 0.08%로 제한할 수 있다. 바람직한 몰리브덴(Mo) 함량은 0.03~0.08%의 범위일 수 있으며, 보다 바람직한 몰리브덴(Mo) 함량은 0.03~0.07%의 범위일 수 있다.
인(P): 0.1% 이하
인(P)은 강의 성형성을 해지지 않으면서도 강도 확보에 유리한 원소이나, 과다하게 첨가되는 경우 취성 파괴가 발생할 가능성이 크게 높아져 열간압연 도중 슬라브의 판파단이 발생할 가능성이 증가되며, 도금표면 특성을 저해하는 원소로도 작용할 수 있다. 따라서, 본 발명은 인(P) 함량의 상한을 0.1%로 제한할 수 있으며, 보다 바람직한 인(P) 함량의 상한은 0.05%일 수 있다. 다만, 불가피하게 첨가되는 수준을 고려하여 0%는 제외될 수 있다.
황(S): 0.01% 이하
황(S)은 강 중 불순물 원소로서 불가피하게 첨가되는 원소이므로, 그 함량을 가급적 낮게 관리하는 것이 바람직하다. 특히, 황(S)은 강의 연성 및 용접성을 저해하는 원소로서 본 발명에서는 그 함량을 최대한 억제하는 것이 바람직하다. 따라서, 본 발명은 황(S) 함량의 상한을 0.01%로 제한할 수 있으며, 보다 바람직한 황(S) 함량의 상한은 0.005%일 수 있다. 다만, 불가피하게 첨가되는 수준을 고려하여 0%는 제외될 수 있다.
질소(N): 0.01% 이하
질소(N)는 불순물 원소로서 불가피하게 첨가되는 원소이다. 질소(N)는 가능한 낮게 관리하는 것이 중요하나, 이를 위해서는 강의 정련 비용이 급격히 상승하는 문제가 있다. 따라서, 본 발명은 조업조건상 가능한 범위를 고려하여 질소(N) 함량의 상한을 0.01%로 제어할 수 있으며, 보다 바람직한 질소(N) 함량의 상한은 0.005%일 수 있다. 다만, 불가피하게 첨가되는 수준을 고려하여 0%는 제외될 수 있다.
보론(B): 0.001~0.005%
보론(B)은 고용에 의한 강도 향상에 효과적으로 기여하는 원소이며, 소량 첨가에 의하더라도 이와 같은 효과를 확보할 수 있는 유효한 원소이다. 따라서, 보 발명은 이와 같은 효과 달성을 위해 보론(B) 함량의 하한을 0.001%로 제한할 수 있다. 다만, 보론(B)이 과다하게 첨가되는 경우, 강도 향상 효과는 포화되는 반면, 표면에 과다한 보론(B) 농화층을 형성하여 도금 밀착성의 열화를 초래할 수 있으므로, 본 발명은 보론(B) 함량의 상한을 0.005%로 제한할 수 있다. 따라서, 본 발명의 보론(B) 함량은 0.001~0.005%의 범위일 수 있다. 바람직한 보론(B) 함량은 0.001~0.004%의 범위일 수 있으며, 보다 바람직한 보론 함량은 0.0013~0.0035%의 범위일 수 있다.
티타늄(Ti): 0.005~0.04%
티타늄(Ti)은 강의 강도 상승 및 입도 미세화에 유효한 원소이다. 또한, 티타늄(Ti)은 질소(N)와 결합하여 TiN 석출물을 형성하므로, 보론(B)이 질소(N)와 결합되어 보론(B)의 첨가 효과가 소실되는 것을 효과적으로 방지할 수 있는 원소이다. 따라서, 본 발명은 티타늄(Ti) 함량의 하한을 0.005%로 제한할 수 있다. 다만, 티타늄(Ti)이 과도하게 첨가되는 경우, 연주 시 노즐 막힘을 유발하거나, 과도한 석출물 생성에 의해 강의 연성이 열화될 수 있으므로, 본 발명은 티타늄(Ti) 함량의 상한을 0.04%로 제한할 수 있다. 따라서, 본 발명의 티타늄(Ti) 함량은 0.005~0.04%의 범위일 수 있다. 바람직한 티타늄(Ti) 함량은 0.01~0.04%의 범위일 수 있으며, 보다 바람직한 티타늄(Ti) 함량은 0.01~0.03%의 범위일 수 있다.
본 발명의 냉연강판은, 상술한 강 조성 이외 나머지는 Fe 및 불가피한 불순물을 포함할 수 있다. 불가피한 불순물은 통상의 철강 제조공정에서 의도되지 않게 혼입될 수 있는 것으로, 이를 전면 배제할 수는 없으며, 통상의 철강제조 분야의 기술자라면 그 의미를 쉽게 이해할 수 있다. 또한, 본 발명은, 앞서 언급한 강 조성 이외의 다른 조성의 첨가를 전면적으로 배제하는 것은 아니다.
이하, 본 발명의 미세조직에 대해 보다 상세히 설명한다. 이하, 달리 특별히 표시하지 않는 한, 미세조직의 비율을 나타내는 %는 면적을 기준으로 한다.
본 발명의 발명자들은 강판의 강도와 연신율을 동시에 확보하는 동시에, 버링성도 겸비시키기 위한 조건을 검토한 결과, 강재의 조성과 조직의 종류 및 분율을 적절히 제어하여 강도와 연신율을 적정범위로 제어하더라도, 강재에 존재하는 조직의 형태를 적절하게 제어하지 않으면 높은 버링성을 얻을 수 없다는 사실을 확인하고 본 발명에 이르게 되었다.
본 발명은 강재의 강도와 연신율을 확보하기 위하여, 강재 내에 페라이트의 조성을 적절한 범위 내로 제어하고, 그 외에 잔류 오스테나이트와 마르텐사이트를 포함하는 TRIP 강재를 그 대상으로 한다.
일반적으로, TRIP 강재에서 마르텐사이트는 높은 강도 확보를 위하여 강재 내에 소정의 범위로 포함되게 되며, 페라이트는 강재의 연신율을 확보하기 위하여 소정의 범위로 포함되게 된다. 잔류 오스테나이트는 가공 과정 중 마르텐사이트로 변태되며, 이러한 변태 과정을 통해 강재의 가공성 향상에 기여할 수 있다.
이러한 측면에서 본 발명의 페라이트는 3~25면적%의 비율로 포함될 수 있다. 즉, 충분한 연신율을 부여하기 위하여 페라이트 비율을 3면적% 이상으로 제어할 필요가 있으며, 연질조직인 페라이트가 과도하게 형성됨에 따라 강도가 저하되는 것을 방지하기 위하여 페라이트의 비율을 25면적% 이하로 제어할 수 있다. 바람직한 페라이트의 분율은 20면적% 이하일 수 있으며, 보다 바람직한 페라이트의 분율은 15면적% 이하, 또는 15 면적% 미만일 수 있다.
또한, 충분한 강도 확보를 위하여 마르텐사이트는 20면적% 이상의 비율로 포함되는 것이 바람직하며, 경질조직인 마르텐사이트가 과도하게 형성됨에 따라 연신율 감소가 일어날 수 있으므로, 마르텐사이트의 비율을 40면적% 이하로 제어할 수 있다.
본 발명의 마르텐사이트는 템퍼드 마르텐사이트(tempered martensite) 및 프레시 마르텐사이트(fresh martensite)로 이루어지며, 전체 마르텐사이트 중 템퍼드 마르텐사이트가 차지하는 비율은 50면적%를 초과할 수 있다. 바람직한 템퍼드 마르텐사이트의 비율은 전체 마르텐사이트 대비 60면적% 이상일 수 있다. 프레시 마르텐사이트는 강도 확보에 유효하지만, 강도 및 연신율의 양립 측면에서는 템퍼드 마르텐사이트가 보다 바람직하기 때문이다.
더불어, 잔류 오스테나이트를 포함하는 경우 강재의 TS×EL이 높아지므로, 전체적으로 강도와 연신율의 밸런스가 향상될 수 있다. 따라서, 잔류 오스테나이트는 5면적% 이상으로 포함되는 것이 바람직하다. 다만, 잔류 오스테나이트가 과도하게 형성되는 경우 수소취성의 민감도가 늘어나는 문제가 있으므로, 잔류 오스테나이트의 분율은 20면적% 이하로 제어하는 것이 바람직하다.
이와는 별도로, 본 발명에서는 면적분율로 15~50%의 베이나이트를 더 포함할 수 있다. 베이나이트는 조직 간의 강도 차를 줄여서 버링성을 향상시킬 수 있으므로, 베이나이트 분율을 15면적% 이상으로 제어하는 것이 바람직하다. 다만, 베이나이트가 과도하게 형성되는 경우 오히려 버링성이 저하될 수 있는바, 베이나이트의 분율은 50면적% 이하로 제어하는 것이 바람직하다.
본 발명의 강재에서는 경질조직인 마르텐사이트와 연질조직인 페라이트가 포함되므로, 버링 가공 또는 이와 유사한 프레스 가공 시 연질조직과 경질조직의 경계에서 크랙이 개시되어 전파되는 현상이 발생할 수 있다. 페라이트 조직은 연신율 향상에는 크게 기여할 수 있으나, 버링 가공 등에서 페라이트와 마르텐사이트 조직간의 경도 차이로 인한 크랙 발생을 조장하는 단점이 있다.
이와 같은 형태의 파손을 방지하기 위하여, 본 발명의 한가지 측면에서는 페라이트를 미세화함과 동시에 페라이트의 길이 비(강판 압연방향 길이/강판 두께방향 길이)를 일정 범위로 제한할 수 있다. 본 발명의 발명자는 TRIP 강에 존재하는 페라이트의 형상과 가공 시 크랙 발생 및 전파 특성에 대해 심도 있게 연구하였으며, 페라이트의 입도뿐만 아니라 페라이트의 길이 비(강판 압연방향 길이/강판 두께방향 길이)가 가공 시 크랙 발생 및 전파 특성에 영향을 미치는 것을 확인할 수 있었다.
즉, 통상의 TRIP 강에서 연질조직인 페라이트는 압연방향을 따라 연신된 형태로 존재하므로, 페라이트 결정립의 미세화에 의하더라도 가공 시 발생한 크랙이 압연방향을 따라 쉽게 진행하는 것을 효과적으로 억제할 수 없다. 따라서, 본 발명은 최종 강재에 존재하는 페라이트를 미세화하되, 페라이트 형상 제어를 통해 크랙의 발생 및 전파를 최대한 억제하고자 한다.
본 발명의 바람직한 한가지 측면에서, 페라이트의 평균 결정립도를 2㎛ 이하로 제어하여 페라이트를 미세화함과 동시에 평균 페라이트의 길이 비(강판 압연방향 길이/강판 두께방향 길이)를 1.5 이하로 제어할 수 있다. 즉, 본 발명은 페라이트의 결정립을 일정 수준 이하로 미세화하되, 평균 페라이트 결정립 길이 비(강판 압연방향 길이/강판 두께방향 길이)를 일정 수준 이하로 제어하므로, 크랙의 발생 및 진행을 효과적으로 저지하여 강재의 버링성을 효과적으로 확보할 수 있다. 다만, 평균 페라이트의 길이 비(강판 압연방향 길이/강판 두께방향 길이)를 일정 수준 미만으로 제어하는 데에는 공정상 한계점이 존재하므로, 본 발명은 평균 페라이트의 길이 비(강판 압연방향 길이/강판 두께방향 길이)의 하한을 0.5로 제한할 수 있다.
본 발명의 페라이트 평균 결정립도 및 평균 페라이트 길이 비는 t/4 지점을 기준으로 하며, 여기서 t는 강판의 두께(mm)를 의미한다.
본 발명은 페라이트를 미세화함과 동시에 페라이트의 길이 비를 최적의 수준으로 제어하므로, 강재의 가공 시 크랙의 발생 및 진행을 효과적으로 억제할 수 있으며, 그에 따라 강재의 파손을 효과적으로 방지할 수 있다.
또한, 본 발명은 전술한 냉연강판 상에 용융아연도금층이 형성된 용융아연도금강판을 포함할 수 있으며, 이를 합금화 처리한 합금화 용융아연도금강판을 포함할 수 있다. 용융아연도금층은 내식성 확보를 위해 통상적으로 이용되는 조성으로 구비될 수 있으며, 아연(Zn) 외에 알루미늄(Al), 마그네슘(Mg) 등의 추가 원소를 포함할 수 있다.
이와 같은 조건을 충족하는 본 발명의 냉연강판 및 합금화 용융아연도금강판은, 인장강도: 1180MPa 이상, 연신율: 14% 이상 및 구멍확장비(Hole Expansion Ratio, HER): 25% 이상을 만족할 수 있다. 버링성 확보 측면에서 보다 바람직한 구멍확장비(HER)는 30% 이상일 수 있다.
이하, 본 발명의 제조방법에 대해 보다 상세히 설명한다.
상술한 조성의 강재를 냉간압연 한 후, 상기 강재가 완전히 오스테나이트로 변태되도록 상기 냉간압연된 강재를 가열하고, 상기 가열된 강재를 630~670℃의 서냉 정지온도까지 5~12℃/s의 냉각속도로 서냉한 후 서냉 정지온도에서 30~90초 동안 유지하고, 상기 서냉 및 유지된 강재를 마르텐사이트 변태종료온도(Mf) 이상, 마르텐사이트 변태개시온도(Ms) 이하의 온도범위까지 7~30℃/s의 냉각속도로 급냉하고, 상기 급냉된 강재를 마르텐사이트 변태개시온도(Ms) 초과, 베이나이트 변태개시온도(Bs) 이하의 온도에서 300~600초 동안 유지하여 분배처리할 수 있다. 시간에 대한 온도 변화를 이용하여 냉간압연 이후의 본 발명의 공정조건을 도 1에 묘사하였다.
본 발명의 냉간압연에 제공되는 강재는 열연재일 수 있으며, 이와 같은 열연재는 통상의 TRIP 강 제조에 이용되는 열연재일 수 있다. 본 발명의 냉간압연에 제공되는 열연재의 제조방법은 특별히 제한되는 것은 아니나, 상술한 조성으로 구비되는 슬라브를 1000~1300℃의 온도범위에서 재가열하고, 800~950℃의 마무리 압연 온도범위에서 열간압연하고, 750℃ 이하의 온도범위에서 권취하여 제조될 수 있다. 본 발명의 냉간압연 역시 통상의 TRIP 강 제조에 있어서 실시되는 공정 조건으로 실시될 수 있다. 고객사의 요구 두께를 확보하기 위하여 적절한 압하율로 냉간압연을 실시할 수 있으나, 후속의 소둔 공정에서의 조대 페라이트 생성을 억제하기 위하여 30% 이상의 냉간 압하율로 냉간압연을 실시하는 것이 바람직하다.
이하, 본 발명의 공정 조건에 대하여 보다 상세히 설명한다.
냉간압연 후 오스테나이트 영역으로 강재를 가열
냉간압연된 강재의 조직을 모두 오스테나이트로 변태시키기 위하여 강재를 오스테나이트 온도 영역(full austenite 영역)으로 가열한다. 통상 페라이트를 일정 수준으로 포함하는 TRIP 강의 경우 오스테나이트와 페라이트가 공전하는 소위 이상역 온도 구간으로 강재를 가열하는 경우가 많으나, 이와 같이 가열할 경우 본 발명에서 의도하는 입도 및 분포도를 가지는 페라이트를 얻기가 매우 곤란할 뿐만 아니라, 열간압연 과정에서 생성된 밴드 조직이 그대로 잔존하여 버링성 개선에 불리하다. 따라서, 본 발명에서는 냉간압연된 강재를 840℃ 이상의 오스테나이트 영역으로 가열할 수 있다.
가열된 강재를 630~670℃의 영역까지 서냉 및 유지
본 발명은 페라이트의 미세화 및 길이비 조절을 위해, 가열된 강재를 5~12℃/s의 냉각속도로 서냉한 후 해당 온도범위에서 일정 시간 유지할 수 있다. 가열된 강재를 서냉하는 동안 강재 내부에서는 다발적인 핵생성 작용에 의하여 미세한 결정립을 가지는 페라이트가 형성될 수 있기 때문이다. 따라서, 본 발명은 페라이트의 핵생성 사이트 증가 및 페라이트의 길이 비 조절을 위해, 가열된 강재를 일정 온도범위까지 서냉할 수 있다. 서냉 정지온도를 초과하여 서냉을 중지하고 바로 급냉을 실시하는 경우, 충분한 페라이트 분율을 확보할 수 없어 연신율 확보 측면에서 불리하며, 서냉 정지온도 미만의 온도까지 서냉을 실시하는 경우, 페라이트 이외의 기타 조직의 비율이 충분하지 않아 강도 확보 측면에서 불리하기 때문에, 본 발명은 서냉 정지온도를 630~670℃의 범위로 제한할 수 있다. 또한, 본 발명의 서냉은 일반적인 서냉 조건에 비해 다소 빠른 냉각속도를 적용하므로, 페라이트의 핵생성 사이트를 효과적으로 증가시킬 수 있다. 따라서, 본 발명의 서냉에서의 냉각속도는 5~12℃/s의 범위일 수 있으나, 페라이트 핵생성 사이트 증가 측면에서 보다 바람직한 냉각속도는 7~12℃/s의 범위일 수 있다.
630~670℃의 온도범위까지 강재를 냉각한 후 해당 온도범위에서 서냉된 강재를 10~90초 동안 유지할 수 있다. 본 발명은 가열된 강재에 대해 서냉 후 유지를 적용하므로, 서냉에 의해 생성된 페라이트가 조대하게 성장하는 것을 효과적으로 방지할 수 있다. 즉, 본 발명은 서냉 및 유지에 의해 페라이트가 압연방향을 따라 성장하는 것을 효과적으로 방지하므로, 페라이트의 길이 비(강판 압연방향 길이/강판 두께방향 길이)를 효과적으로 제어할 수 있다.
서냉 및 유지된 강재를 Mf~Ms의 온도로 급냉
본 발명에서 의도하는 비율의 마르텐사이트를 얻기 위해서는 서냉 및 유지된 강재를 바로 Mf~Ms의 온도범위까지 급냉하는 절차가 후속될 수 있다. 여기서, Mf는 마르텐사이트 변태종료온도를 의미하며, Ms는 마르텐사이트 변태개시온도를 의미한다. 서냉 및 유지된 강재를 Mf~Ms의 온도범위까지 급냉하므로, 급냉 후 강재에는 마르텐사이트 및 잔류 오스테나이트가 도입될 수 있다. 즉, 급냉 정지온도를 Ms 이하로 제어하므로 급냉 후 강재 내에 마르텐사이트가 도입될 수 있으며, 급냉 정지온도를 Mf 이상으로 제어하므로 오스테나이트가 전부 마르텐사이트로 변태되는 것을 방지하여 급냉 후 강재 내에 잔류 오스테나이트가 도입될 수 있다. 급냉 시 바람직한 냉각속도는 7~30℃/s의 범위일 수 있으며, 바람직한 하나의 수단은 켄칭(Quenching)일 수 있다.
급냉된 강재를 분배(Partitioning) 처리
급냉된 조직 중 마르텐사이트는 탄소를 다량 함유하고 있던 오스테나이트가 부확산 변태한 것이기 때문에, 마르텐사이트 내에는 다량의 탄소가 함유되어 있다. 이러한 경우, 조직의 경도가 높을 수 있으나, 반대로 인성이 급격히 열화되는 문제가 발생할 수 있다. 통상의 경우, 높은 온도에서 강재를 템퍼링 처리하여 마르텐사이트 내에서 탄소가 탄화물로 석출하도록 하는 방법을 사용한다. 하지만, 본 발명에서는 특유의 방직으로 조직을 제어하기 위하여 템퍼링이 아닌 다른 방법을 사용할 수 있다.
즉, 본 발명에서는 급냉된 강재를 Ms 초과, Bs 이하의 온도범위에서 일정 시간 유지되도록 함으로써 마르텐사이트 내에 존재하던 탄소가 고용량의 차이로 인하여 잔류 오스테나이트로 분배(Pratitioning)되고, 소정량의 베이나이트가 생성되도록 유도한다. 여기서, Ms는 마르텐사이트 변태개시온도를 의미하며, Bs는 베이나이트 변태개시온도를 의미한다. 잔류 오스테나이트의 탄소 고용량이 증가할 경우 잔류 오스테나이트의 안정성이 증대되므로, 본 발명이 목적하는 잔류 오스테나이트 분율을 효과적으로 확보할 수 있다.
또한, 이와 같이 강재를 유지함으로써 본 발명의 강재는 베이나이트를 면적비율로 15~50%로 포함할 수 있다. 즉, 본 발명에서는 급냉 후 1차 냉각단계와 2차 유지단계에서 마르텐사이트와 잔류 오스테나이트 사이에 탄소의 분배가 일어나며, 마르텐사이트의 일부가 베이나이트로 변태되어 본 발명의 일 측면에서 의도하는 조직 구성을 얻을 수 있다.
충분한 분배 효과를 얻기 위해서는 상술한 유지시간은 300초 이상일 수 있다. 다만, 유지시간이 600초를 초과하는 경우, 더 이상 효과의 상승을 기대하기 어려울 뿐 아니라, 생산성이 저하될 수도 있으므로, 본 발명의 일 측면에서는 상술한 유지시간의 상한을 600초로 제한할 수 있다.
전술한 처리를 거진 냉연강판은 이후 공지된 방법에 의하여 용융아연도금 처리될 수 있다. 또한, 용융아연도금 처리된 강판은 공지된 방법에 의해 합금화 처리될 수 있다.
이상의 제조방법에 의해 제조된 냉연강판은, 면적분율로, 페라이트: 3~25%, 마르텐사이트: 20~40%, 잔류 오스테나이트 5~20%를 포함하고, 4/t 지점을 기준으로(여기서, t는 강판 두께를 의미함), 페라이트의 평균 결정립도가 2㎛ 이하이며, 강판 두께방향의 페라이트 길이에 대한 강판 압연방향의 페라이트 길이 비의 평균값이 1.5 이하일 수 있다.
또한, 이상의 제조방법에 의해 제조된 냉연강판 및 합금화 용융아연도금강판은, 1180MPa 이상의 인장강도, 14% 이상의 연신율, 25% 이상의 구멍 확장비(Hole Expansion Ratio, HER)를 만족할 수 있다.
이하, 실시예를 통하여 본 발명을 보다 구체적으로 설명한다. 다만, 아래의 실시예는 본 발명을 예시하여 구체화하기 위한 것일 뿐, 본 발명의 권리범위를 제한하기 위한 것이 아니라는 점에 유의할 필요가 있다.
(실시예)
아래의 표 1에 기재된 조성의 강재를 표 2에 기재된 조건으로 처리하여 냉연강판을 제조하였다. 표 2에서 급냉은 냉연강판의 표면에 미스트를 분사하거나 질소가스 또는 질소-수소 혼합가스를 분사하는 방법으로 실시하였다. 비교예 1은 본 발명의 분배 시간보다 짧은 시간 동안 분배처리를 한 경우이고, 비교예 2 및 비교예 4는 본 발명의 가열 온도보다 낮은 온도범위에서 가열을 실시한 경우이다. 비교예 5는 본 발명의 서냉 냉각속도에 비해 느린 냉각속도로 서냉하여 본 발명의 서냉 냉각 정지온도범위보다 더 낮은 온도범위에서 서냉을 종료하고, 서냉 후 유지하지 않고 바로 급냉을 실시한 경우이다. 급냉 후 유지 온도는 모든 발명예와 비교예에서 Ms 초과 Bs 미만의 관계를 충족한다.
구분 강 조성(wt%)
C Si Mn P S Al N Cr Mo Ti B
발명예1 0.24 1.5 2.4 0.007 0.002 0.034 0.004 0.4 0 0.02 0.002
발명예2 0.18 1.3 2.7 0.013 0.004 0.055 0.006 0.5 0 0.02 0.002
발명예3 0.2 1.4 2.5 0.01 0.006 0.062 0.005 0.12 0.01 0.02 0.002
발명예4 0.19 1.6 2.4 0.015 0.005 0.04 0.006 0.2 0.05 0.02 0.002
발명예5 0.2 1.7 2.6 0.006 0.005 0.21 0.004 0.01 0.03 0.02 0.002
발명예6 0.16 1.1 2.8 0.011 0.006 0.047 0.005 0.03 0.02 0.02 0.002
비교예1 0.22 1.2 2.5 0.008 0.005 0.39 0.006 0.05 0.05 0.02 0.002
비교예2 0.15 2.3 1.2 0.013 0.01 0.05 0.004 0.001 0.05 0.02 0.002
비교예3 0.27 0.1 1.1 0.015 0.008 0.043 0.005 0.002 0.01 0.02 0.002
비교예4 0.16 1.4 2.2 0.01 0.005 0.03 0.006 0.008 0 0.02 0.002
비교예5 0.2 1.7 2.6 0.006 0.005 0.21 0.004 0.01 0.03 0.02 0.002
구분 가열온도(℃) 가열시간(초) 서냉정지온도(℃) 서냉속도(℃/s) 서냉 후유지시간(초) 급냉정지온도(℃) 급냉 후유지온도(℃) 급냉 후유지시간(초) 도금실시여부
발명예1 860 60 650 25 60 300 400 500 미실시
발명예2 870 60 650 25 60 300 400 500 미실시
발명예3 860 60 650 25 60 300 400 500 실시
발명예4 870 60 650 25 60 300 400 500 실시
발명예5 870 60 650 25 60 300 400 500 실시
발명예6 850 60 650 25 60 300 400 500 실시
비교예1 870 60 650 25 60 300 400 100 실시
비교예2 830 60 650 25 60 300 400 500 실시
비교예3 870 60 650 25 60 300 400 500 미실시
비교예4 810 60 650 25 60 300 400 500 실시
비교예5 870 60 600 3.5 0 300 400 500 실시
상술한 과정에 의해 제조된 냉연강판의 내부조직과 물성을 평가한 결과를 아래의 표 3에 나타내었다. 주사전자현미경을 이용하여 각 냉연강판의 미세조직을 관찰 및 평가하였으며, JIS 5호 인장시험편을 제작하여 항복강도(YS), 인장강도(TS), 연신율(T-El) 및 구멍 확장성(HER)을 측정 및 평가하였다. 도금성 평가는 도금강재에 한하여 실시하였으며, 표면에 미도금된 영역이 존재하는지(X), 그렇지 않은지(O) 여부를 기준으로 판단하였다.
구분 페라이트평균입도(㎛) 페라이트길이 비(압연방향/두께방향) 페라이트분율(면적%) 마르텐사이트분율(면적%) 잔류오스테나이트분율(면적%) 베이나이트분율(면적%) 항복강도(MPa) 인장강도(MPa) 연신율(%) HER(%) 도금성
발명예1 1.1 0.98 14 27 15 44 783 1195 18 32 -
발명예2 1 1.06 11 32 12 45 984 1210 18 40 -
발명예3 0.9 1.2 21 30 13 36 910 1249 17 28 O
발명예4 1 1.26 20 29 12 39 898 1235 16 27 O
발명예5 0.8 1.1 8 34 11 47 1021 1278 16 38 O
발명예6 0.9 1.12 9 30 12 49 968 1202 15 35 O
비교예1 0.9 0.99 10 41 4 45 873 1351 9 17 O
비교예2 3.4 1.6 12 20 20 48 763 1100 15 23 X
비교예3 0.8 1.1 5 55 3 37 1120 1398 8 31 -
비교예4 4.4 1.8 16 25 10 49 628 1153 17 11 O
비교예5 2.2 1.1 8 30 12 50 958 1242 16 24 O
상기 표 3에서 확인할 수 있듯이, 본 발명의 조성을 충족하고 본 발명의 제조조건을 만족하는 발명예 1 내지 발명예 6은 페라이트의 평균 결정립도가 2㎛ 이하이며, 상기 페라이트의 두께 방향 길이에 대한 상기 페라이트의 압연 방향 길이의 비가 평균 1.5 이하이므로, 항복강도와 인장강도가 높으면서도 높은 연신율 및 구멍확장성(HER)을 나타내는 것을 확인할 수 있다.
반면, 본 발명의 강 조성 및/또는 본 발명의 제조조건을 만족하지 않는 비교예 1 내지 비교예 5는 본 발명이 목적하는 연신율 및/또는 구멍확장성(HER)을 확보하지 못함을 알 수 있다.
비교예 1은 본 발명이 제한하는 분배 시간보다 짧은 시간 분배처리를 실시하여 잔류 오스테나이트가 충분히 형성되지 않았는바, 연신율이 열위한 것을 확인할 수 있다.
비교예 2 및 4는 본 발명이 제한하는 가열 온도보다 낮은 온도범위에서 가열을 실시하여 조대한 페라이트가 형성되었으며, 구멍 확장성(HER)이 열위하고, 도금성이 열위한 것을 확인할 수 있다.
비교예 3은 C 함량이 본 발명의 범위를 초과하고, Si 및 Mn이 본 발명의 범위에 미치지 못하므로, 페라이트가 충분히 형성되지 않아 연신율이 열위한 것을 확인할 수 있다.
비교예 5는 가열 후 서냉 조건이 본 발명의 범위를 벗어나므로, 페라이트가 조대하게 형성되어 목적하는 구멍 확장성(HER)을 확보하지 못함을 확인할 수 있다.
도 2는 발명예 1의 미세조직을 주사전자현미경으로 관찰한 이미지이며, 도 3은 비교예 2의 미세조직을 주사전자현미경으로 관찰한 이미지이다. 도 2 및 도 3에 나타난 바와 같이, 발명예 1의 페라이트(F)는 미세하게 형성된 반면 비교예 2의 페라이트(F)는 조대하게 형성되어 압연 방향을 따라 연신된 형상으로 존재하는 것을 확인할 수 있다.
따라서, 본 발명의 일 측면에 따르면, 인장강도가 980MPa 이상, 연신율이 14%, HER(Hole Expansion Ratio, 구멍 확장비)이 25% 이상으로 자용차용 소재로 특히 적합한 냉연강판을 제공할 수 있음을 확인할 수 있다.
이상에서 실시예를 통하여 본 발명을 상세하게 설명하였으나, 이와 다른 형태의 실시예들도 가능하다. 그러므로, 이하에 기재된 청구항들의 기술적 사상과 범위는 실시예들에 한정되지 않는다.

Claims (20)

  1. 중량%로, 탄소(C): 0.13~0.25%, 실리콘(Si): 1.0~2.0%, 망간(Mn): 1.5~3.0%, 알루미늄(Al)+크롬(Cr)+몰리브덴(Mo): 0.08~1.5%, 인(P): 0.1% 이하, 황(S): 0.01% 이하, 질소(N): 0.01% 이하, 나머지 Fe 및 불가피한 불순물을 포함하고,
    면적분율로, 페라이트: 3~25%, 마르텐사이트: 20~40%, 잔류 오스테나이트: 5~20%를 포함하고,
    4/t 지점을 기준으로(여기서, t는 강판 두께를 의미함), 페라이트의 평균 결정립도가 2㎛ 이하이며, 강판 두께방향의 페라이트 길이에 대한 강판 압연방향의 페라이트 길이 비의 평균값이 1.5 이하인, 버링성이 우수한 고강도 냉연강판.\
  2. 제1항에 있어서,
    상기 냉연강판은 면적분율로 15~50%의 베이나이트를 더 포함하는, 버링성이 우수한 고강도 냉연강판.
  3. 제1항에 있어서,
    상기 마르텐사이트는 템퍼드 마르텐사이트 및 프레시 마르텐사이트로 이루어지며,
    상기 전체 마르텐사이트 중 상기 템퍼드 마르텐사이트가 차지하는 비율은 50면적%를 초과하는, 버링성이 우수한 고강도 냉연강판.
  4. 제1항에 있어서,
    상기 냉연강판은 3~15면적%의 페라이트를 포함하는, 버링성이 우수한 고강도 냉연강판.
  5. 제1항에 있어서,
    상기 강판 두께방향의 페라이트 길이에 대한 강판 압연방향의 페라이트 길이 비의 평균값이 0.5 이상인, 버링성이 우수한 고강도 냉연강판.
  6. 제1항에 있어서,
    상기 냉연강판은, 중량%로, 보론(B): 0.001~0.005% 및 티타늄(Ti): 0.005~0.04% 중 1종 이상을 더 포함하는, 버링성이 우수한 고강도 냉연강판.
  7. 제1항에 있어서,
    상기 알루미늄(Al)은 0.01~0.09중량%의 함량으로 상기 냉연강판에 포함되는, 버링성이 우수한 고강도 냉연강판.
  8. 제1항에 있어서,
    상기 크롬(Cr)은 0.01~0.7중량%의 함량으로 상기 냉연강판에 포함되는, 버링성이 우수한 고강도 냉연강판.
  9. 제8항에 있어서,
    상기 크롬(Cr)은 0.2~0.6중량%의 함량으로 상기 냉연강판에 포함되는, 버링성이 우수한 고강도 냉연강판.
  10. 제1항에 있어서,
    상기 몰리브덴(Mo)은 0.02~0.08중량%의 함량으로 상기 냉연강판에 포함되는, 버링성이 우수한 고강도 냉연강판.
  11. 제1항에 있어서,
    상기 냉연강판은, 1180MPa 이상의 인장강도, 14% 이상의 연신율, 25% 이상의 구멍 확장비(Hole Expansion Ratio, HER)를 가지는, 버링성이 우수한 고강도 냉연강판.
  12. 제11항에 있어서,
    상기 냉연강판의 구명 확장비(HER)는 30% 이상인, 버링성이 우수한 고강도 냉연강판.
  13. 소지강판 및 상기 소지강판의 표면 상에 형성된 합금화 용융아연도금층을 포함하며,
    상기 소지강판은 제1항 내지 제12항 중 어느 한 항의 냉연강판인, 버링성이 우수한 고강도 합금화 용융아연도금강판.
  14. 중량%로, 탄소(C): 0.13~0.25%, 실리콘(Si): 1.0~2.0%, 망간(Mn): 1.5~3.0%, 알루미늄(Al)+크롬(Cr)+몰리브덴(Mo): 0.08~1.5%, 인(P): 0.1% 이하, 황(S): 0.01% 이하, 질소(N): 0.01% 이하, 나머지 Fe 및 불가피한 불순물을 포함하는 강재를 냉간압연 한 후, 상기 강재가 완전히 오스테나이트로 변태되도록 상기 강재를 가열하고,
    상기 가열된 강재를 630~670℃의 서냉 정지온도까지 5~12℃/s의 냉각속도로 서냉한 후 서냉 정지온도에서 10~90초 동안 유지하고,
    상기 서냉된 강재를 마르텐사이트 변태종료온도(Mf) 이상, 마르텐사이트 변태개시온도(Ms) 이하의 온도범위까지 7~30℃/s의 냉각속도로 급냉하고,
    상기 급냉된 강재를 마르텐사이트 변태개시온도(Ms) 초과, 베이나이트 변태개시온도(Bs) 이하의 온도에서 300~600초 동안 유지하여 분배처리하는, 버링성이 우수한 고강도 냉연강판의 제조방법.
  15. 제14항에 있어서,
    상기 강재는, 중량%로, 보론(B): 0.001~0.005% 및 티타늄(Ti): 0.005~0.04% 중 1종 이상을 더 포함하는, 버링성이 우수한 고강도 냉연강판의 제조방법.
  16. 제14항에 있어서,
    상기 알루미늄(Al)은 0.01~0.09중량%의 함량으로 상기 강재에 포함되는, 버링성이 우수한 고강도 냉연강판의 제조방법.
  17. 제14항에 있어서,
    상기 크롬(Cr)은 0.01~0.7중량%의 함량으로 상기 강재에 포함되는, 버링성이 우수한 고강도 냉연강판의 제조방법.
  18. 제14항에 있어서,
    상기 크롬(Cr)은 0.2%~0.6중량%의 함량으로 상기 강재에 포함되는, 버링성이 우수한 고강도 냉연강판.
  19. 제14항에 있어서,
    상기 몰리브덴(Mo)은 0.02~0.08중량%의 함량으로 상기 강재에 포함되는, 버링성이 우수한 고강도 냉연강판의 제조방법.
  20. 소지강판의 표면에 용융아연도금층을 형성하고 합금화처리하되,
    상기 소지강판은 제14항 내지 제19항 중 어느 하나의 제조방법에 의해 제조된 냉연강판인, 버링성이 우수한 고강도 합금화 용융아연도금강판의 제조방법.
PCT/KR2019/018109 2018-12-19 2019-12-19 버링성이 우수한 고강도 냉연강판 및 합금화 용융아연도금강판과 이들의 제조방법 WO2020130677A1 (ko)