WO2020127048A1 - Panneau composite à base de plantes - Google Patents
Panneau composite à base de plantes Download PDFInfo
- Publication number
- WO2020127048A1 WO2020127048A1 PCT/EP2019/085349 EP2019085349W WO2020127048A1 WO 2020127048 A1 WO2020127048 A1 WO 2020127048A1 EP 2019085349 W EP2019085349 W EP 2019085349W WO 2020127048 A1 WO2020127048 A1 WO 2020127048A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- plants
- posidonia
- parts
- genus
- composite panel
- Prior art date
Abstract
L'invention concerne un panneau composite à base de plantes, comprenant des parties de plantes du genre Posidonia, en particulier des feuilles de plantes du genre Posidonia, ainsi qu'un matériau polymère. L'invention concerne également un procédé permettant d'obtenir ledit panneau composite, ce procédé consistant : à rincer des parties de plantes du genre Posidonia, à sécher les parties de plantes ainsi rincées, à mélanger les parties de plantes ainsi séchées avec une résine polymère, puis à réaliser une étape de formation.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
IT102018000011152A IT201800011152A1 (it) | 2018-12-17 | 2018-12-17 | Pannello composito a base vegetale |
IT102018000011152 | 2018-12-17 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2020127048A1 true WO2020127048A1 (fr) | 2020-06-25 |
Family
ID=65951897
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/EP2019/085349 WO2020127048A1 (fr) | 2018-12-17 | 2019-12-16 | Panneau composite à base de plantes |
Country Status (2)
Country | Link |
---|---|
IT (1) | IT201800011152A1 (fr) |
WO (1) | WO2020127048A1 (fr) |
Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
FR2556738A1 (fr) * | 1983-12-16 | 1985-06-21 | Ferrazzini Patrick | Materiau agglomere a haut degre d'ininflammabilite |
WO2010000983A1 (fr) | 2008-07-03 | 2010-01-07 | Energia Sarl | Nouveau matériau à base végétale |
WO2018029496A1 (fr) * | 2016-08-09 | 2018-02-15 | Pavlakis Loannis | Panneau respectueux de l'environnement provenant de feuilles d'algues mortes de posidonia oceanica |
-
2018
- 2018-12-17 IT IT102018000011152A patent/IT201800011152A1/it unknown
-
2019
- 2019-12-16 WO PCT/EP2019/085349 patent/WO2020127048A1/fr active Application Filing
Patent Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
FR2556738A1 (fr) * | 1983-12-16 | 1985-06-21 | Ferrazzini Patrick | Materiau agglomere a haut degre d'ininflammabilite |
WO2010000983A1 (fr) | 2008-07-03 | 2010-01-07 | Energia Sarl | Nouveau matériau à base végétale |
WO2018029496A1 (fr) * | 2016-08-09 | 2018-02-15 | Pavlakis Loannis | Panneau respectueux de l'environnement provenant de feuilles d'algues mortes de posidonia oceanica |
Also Published As
Publication number | Publication date |
---|---|
IT201800011152A1 (it) | 2020-06-17 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
Abdulkareem et al. | Development of particleboard from waste styrofoam and sawdust | |
Chanhoun et al. | Study of the implementation of waste wood, plastics and polystyrenes for various applications in the building industry | |
Cook et al. | Coir fibre reinforced cement as a low cost roofing material | |
Babenko et al. | Study of thermal properties of lightweight insulation made of flax straw | |
Yadollahi et al. | Reuse of waste sludge from papermaking process in cement composites | |
Abdulkareem et al. | Development of plastic composite using waste sawdust, rice husk and bamboo in the polystyrene-based resin (PBR) matrix at ambient conditions | |
US20120010332A1 (en) | Materials, Methods and Compositions for a Composite Building Material | |
Ekpenyong et al. | Assessment of Thermophysical and Mechanical Properties of Composite Panels Fabricated from Untreated and Treated Coconut Husk Particles for Structural Application | |
Wuzella et al. | Green composite material made from Typha latifolia fibres bonded with an epoxidized linseed oil/tall oil-based polyamide binder system | |
Kazemi Najafi et al. | Effect of bark flour content on the hygroscopic characteristics of wood–polypropylene composites | |
WO2020127048A1 (fr) | Panneau composite à base de plantes | |
Atoyebi et al. | Strength Evaluation of Cocos nucifera Fibre Reinforced Concrete | |
Tichi et al. | The effect of nano-wollastonite on biological, mechanical, physical, and microstructural properties of the composite made of wood-cement fiber | |
Bui | Study on performance enhancement of coconut fibres reinforced cementitious composites | |
Liu et al. | Effect of inorganic particles gradation on the properties of high‐filled unsaturated polyester resin/CaCO3 composites | |
DİEYE | Thermomechanical characterization of particleboards from powder Typha leaves | |
Findik et al. | Civil engineering materials | |
Mendes et al. | Study of new reinforcing materials for cementitious panel production | |
Rupal et al. | Utilization of polymer composite for development of sustainable construction material | |
Oriyomi et al. | A review of recycled use of post consumer waste paper in construction | |
Kaith et al. | Synthesis, characterization and mechanical evaluation of the phenol-formaldehyde composites | |
RU2368633C2 (ru) | Защитное эпоксидно-древесное покрытие для пенополистирола | |
Umoh et al. | The Recycling of Sawdust Waste into Particleboard Using Starch-Based Modified Adhesive | |
Wicaksono et al. | Mechanical to physical aspects of PP and LDPE plastic waste for potential wood plastic composite | |
Abdullahi et al. | Potentials of unsaturated polyester–groundnut shell composite as material in building industry |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 19820760 Country of ref document: EP Kind code of ref document: A1 |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 19820760 Country of ref document: EP Kind code of ref document: A1 |