WO2020124366A1 - Efficient conductive paint - Google Patents
Efficient conductive paint Download PDFInfo
- Publication number
- WO2020124366A1 WO2020124366A1 PCT/CN2018/121762 CN2018121762W WO2020124366A1 WO 2020124366 A1 WO2020124366 A1 WO 2020124366A1 CN 2018121762 W CN2018121762 W CN 2018121762W WO 2020124366 A1 WO2020124366 A1 WO 2020124366A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- parts
- conductive paint
- conductive
- antimony trioxide
- silver
- Prior art date
Abstract
An efficient conductive paint, prepared from the following raw materials in parts by weight: 20-40 parts of silver-nickel powder, 2-5 parts of antimony trioxide, 15-30 parts of acrylic resin, 10-20 parts of alkyd resin, 1-3 parts of tetraethylammonium tetrafluoride borate, 0.5-2 parts of film-forming aid, 2-4 parts of polyvinyl alcohol, 40-50 parts of aromatic hydrocarbons; 20-40 parts of styrene, 20-40 parts of acetaldehyde, 5-10 parts of polyethylene wax powder, 2-3 parts of leveling agent, 1-4 parts of tetrahydrofuran; and 5-8 parts of BYK-101 dispersant. According to the conductive paint, silver-nickel powder is used as a conductive medium, antimony trioxide having a conductive dispersion property is added, and acrylic resin and alkyd resin are adopted as main materials; the product obtained has low price and good conductive performance; coating films of the conductive paint dries quickly, is smooth, and has good covering effect as well as good wear resistance and corrosion resistance.
Description
本发明涉及导电漆领域，尤其涉及一种高效导电漆。The invention relates to the field of conductive paint, in particular to an efficient conductive paint.
导电漆就是能用于喷涂的一种油漆干燥形成漆膜后能起到导电的作用,从而屏蔽电磁波干扰的功能。按照所添加的金属粉末的成分，目前广泛使用的导电漆主要有银导电漆、铜导电漆、镍导电漆几种产品，其中，以铜导电漆使用最为广泛，因为相比银导电漆价格便宜很多，相比镍导电导电性能也相对好很多。因此，人们力求一种导电性能好，价格也相对实惠的导电漆。Conductive paint is a kind of paint that can be used for spraying. After drying to form a paint film, it can play a conductive role, thereby shielding the function of electromagnetic interference. According to the composition of the added metal powder, the currently widely used conductive paints mainly include silver conductive paint, copper conductive paint, and nickel conductive paint. Among them, copper conductive paint is the most widely used because it is cheaper than silver conductive paint. Many, compared to nickel, conductive performance is relatively better. Therefore, people strive for a conductive paint with good conductivity and relatively affordable price.
发明内容Summary of the invention
本发明要解决的技术问题是提供一种导电性能良好且价格低的高效导电漆。The technical problem to be solved by the present invention is to provide a highly efficient conductive paint with good conductivity and low price.
为解决上述技术问题，本发明的技术方案为：一种高效导电漆，其创新点在于：由以下重量份数的原料制备而成：银镍粉20-40份，三氧化二锑2份～5份，丙烯酸树脂15份～30份，醇酸树脂10份～20份，四乙胺四氟化硼酸盐1份～3份，成膜助剂0.5份～2份，聚乙烯醇2份～4份，芳香烃40份～50份，苯乙烯20-40份，乙醛20-40份，聚乙烯蜡粉5-10份，流平剂2-3份，四氢呋喃1-4份；BYK-101分散剂5-8份。In order to solve the above technical problems, the technical solution of the present invention is: a highly efficient conductive paint, the innovation of which is: prepared from the following parts by weight of raw materials: silver nickel powder 20-40 parts, antimony trioxide 2 parts ~ 5 parts, acrylic resin 15 parts to 30 parts, alkyd resin 10 parts to 20 parts, tetraethylamine tetrafluoroborate 1 part to 3 parts, film-forming aid 0.5 part to 2 parts, polyvinyl alcohol 2 parts ～4 parts, aromatic hydrocarbons 40～50 parts, styrene 20-40 parts, acetaldehyde 20-40 parts, polyethylene wax powder 5-10 parts, leveling agent 2-3 parts, tetrahydrofuran 1-4 parts; BYK -101 dispersant 5-8 parts.
本发明的优点在于：The advantages of the present invention are:
1)本发明以银镍粉作为导电介质，添加了具有导电分散性能的三氧化二锑，并以丙烯酸树脂和醇酸树脂作为主材料，所得产品价格低廉，导电性能较好；本发明导电漆涂膜干爽，并具有较好的光洁度和遮盖力，耐磨性以及耐腐蚀性能较好。1) In the present invention, silver nickel powder is used as the conductive medium, antimony trioxide with conductive dispersion properties is added, and acrylic resin and alkyd resin are used as the main materials. The resulting product is cheap and has good conductive properties; The coating film is dry, and has good finish and hiding power, good wear resistance and corrosion resistance.
下面的实施例可以使本专业的技术人员更全面地理解本发明，但并不因此将本发明限制在所述的实施例范围之中。The following embodiments can enable those skilled in the art to more fully understand the present invention, but do not limit the present invention to the scope of the described embodiments.
实施例1：Example 1:
一种高效导电漆，由以下重量份数的原料制备而成：银镍粉20份，三氧化二锑2份，丙烯酸树脂15份，醇酸树脂10份，四乙胺四氟化硼酸盐1份，成膜助剂0.5份，聚乙烯醇2份，芳香烃40份，苯乙烯20-40份，乙醛20份，聚乙烯蜡粉5份，流平剂2份，四氢呋喃1份；BYK-101分散剂5份。An efficient conductive paint, prepared from the following parts by weight of raw materials: 20 parts of silver nickel powder, 2 parts of antimony trioxide, 15 parts of acrylic resin, 10 parts of alkyd resin, tetraethylamine tetrafluoroborate 1 part, film forming aid 0.5 parts, polyvinyl alcohol 2 parts, aromatic hydrocarbon 40 parts, styrene 20-40 parts, acetaldehyde 20 parts, polyethylene wax powder 5 parts, leveling agent 2 parts, tetrahydrofuran 1 part; 5 parts of BYK-101 dispersant.
实施例2：Example 2:
一种高效导电漆，由以下重量份数的原料制备而成：银镍粉30份，三氧化二锑3.5份，丙烯酸树脂23份，醇酸树脂15份，四乙胺四氟化硼酸盐2份，成膜助剂1.25份，聚乙烯醇3份，芳香烃45份，苯乙烯30份，乙醛30份，聚乙烯蜡粉8份，流平剂2.5份，四氢呋喃2.5份；BYK-101分散剂6.5份。An efficient conductive paint, prepared from the following parts by weight of raw materials: silver nickel powder 30 parts, antimony trioxide 3.5 parts, acrylic resin 23 parts, alkyd resin 15 parts, tetraethylamine tetrafluoroborate 2 parts, 1.25 parts film-forming aid, 3 parts polyvinyl alcohol, 45 parts aromatic hydrocarbon, 30 parts styrene, 30 parts acetaldehyde, 8 parts polyethylene wax powder, 2.5 parts leveling agent, 2.5 parts tetrahydrofuran; BYK- 101 6.5 parts of dispersant.
实施例3：Example 3:
一种高效导电漆，由以下重量份数的原料制备而成：银镍粉40份，三氧化二锑5份，丙烯酸树脂30份，醇酸树脂20份，四乙胺四 氟化硼酸盐3份，成膜助剂2份，聚乙烯醇4份，芳香烃50份，苯乙烯40份，乙醛40份，聚乙烯蜡粉10份，流平剂3份，四氢呋喃4份；BYK-101分散剂8份。An efficient conductive paint, prepared from the following parts by weight of raw materials: silver nickel powder 40 parts, antimony trioxide 5 parts, acrylic resin 30 parts, alkyd resin 20 parts, tetraethylamine tetrafluoroborate 3 parts, film-forming aid 2 parts, polyvinyl alcohol 4 parts, aromatic hydrocarbon 50 parts, styrene 40 parts, acetaldehyde 40 parts, polyethylene wax powder 10 parts, leveling agent 3 parts, tetrahydrofuran 4 parts; BYK- 8 parts of 101 dispersant.
本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。Those skilled in the art should understand that the present invention is not limited by the above embodiments. The above embodiments and the description only describe the principles of the present invention. Without departing from the spirit and scope of the present invention, the present invention will have Various changes and improvements that fall within the scope of the claimed invention. The claimed protection scope of the present invention is defined by the appended claims and their equivalents.
Claims (1)
- 一种高效导电漆，其特征在于：由以下重量份数的原料制备而成：银镍粉20-40份，三氧化二锑2份～5份，丙烯酸树脂15份～30份，醇酸树脂10份～20份，四乙胺四氟化硼酸盐1份～3份，成膜助剂0.5份～2份，聚乙烯醇2份～4份，芳香烃40份～50份，苯乙烯20-40份，乙醛20-40份，聚乙烯蜡粉5-10份，流平剂2-3份，四氢呋喃1-4份；BYK-101分散剂5-8份。A high-efficiency conductive paint, characterized by being prepared from the following parts by weight of raw materials: silver nickel powder 20-40 parts, antimony trioxide 2-5 parts, acrylic resin 15-30 parts, alkyd resin 10 to 20 parts, 1 to 3 parts of tetraethylammonium tetrafluoride borate, 0.5 to 2 parts of film-forming aid, 2 to 4 parts of polyvinyl alcohol, 40 to 50 parts of aromatic hydrocarbon, styrene 20-40 parts, acetaldehyde 20-40 parts, polyethylene wax powder 5-10 parts, leveling agent 2-3 parts, tetrahydrofuran 1-4 parts; BYK-101 dispersant 5-8 parts.