WO2020098288A1 - Plaque épaisse q690d produite par un procédé de refroidissement ultra rapide et procédé de fabrication - Google Patents

Plaque épaisse q690d produite par un procédé de refroidissement ultra rapide et procédé de fabrication Download PDF

Info

Publication number
WO2020098288A1
WO2020098288A1 PCT/CN2019/093665 CN2019093665W WO2020098288A1 WO 2020098288 A1 WO2020098288 A1 WO 2020098288A1 CN 2019093665 W CN2019093665 W CN 2019093665W WO 2020098288 A1 WO2020098288 A1 WO 2020098288A1
Authority
WO
WIPO (PCT)
Prior art keywords
ultra
fast cooling
cooling process
thick plate
rolling
Prior art date
Application number
PCT/CN2019/093665
Other languages
English (en)
Chinese (zh)
Inventor
姜在伟
张清辉
闫强军
侯中华
姜辉
张仪杰
Original Assignee
南京钢铁股份有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 南京钢铁股份有限公司 filed Critical 南京钢铁股份有限公司
Priority to AU2019381076A priority Critical patent/AU2019381076B2/en
Publication of WO2020098288A1 publication Critical patent/WO2020098288A1/fr
Priority to ZA2021/03240A priority patent/ZA202103240B/en

Abstract

La présente invention se rapporte au domaine technique de la métallurgie et concerne une plaque épaisse Q690D produite par un procédé de refroidissement ultra rapide, la plaque épaisse comprenant les composants chimiques et les pourcentages en masse suivants : C : 0,05 % à 0,10 %, Si : 0,20 % à 0,50 %, Mn : 1,40 % à1,80 %, P ≤ 0,020 %, S ≤ 0,003 %, Cr : 0,10 % à 0,50 %, Mo : 0,08 % à 0,30 %, Ti : 0,008 % à 0,030 %, Nb : 0,015 % à 0,050 %, B : 0,0008 % à 0,0025 %, et Ceq ≤ 0,43, le reste étant du Fe et des impuretés inévitables. La présente invention utilise une conception de composant à faible teneur en carbone et en alliage, fournissant une plaque épaisse d'acier Q690D à haute résistance, le procédé de production présentant un écoulement simple, un rythme de production rapide et un faible coût.
PCT/CN2019/093665 2018-11-12 2019-06-28 Plaque épaisse q690d produite par un procédé de refroidissement ultra rapide et procédé de fabrication WO2020098288A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
AU2019381076A AU2019381076B2 (en) 2018-11-12 2019-06-28 Q690D thick plate produced by ultra fast cooling process and manufacturing method
ZA2021/03240A ZA202103240B (en) 2018-11-12 2021-05-13 Q690d thick plate produced by ultra fast cooling process and manufacturing method

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
CN201811342554.4A CN109338225A (zh) 2018-11-12 2018-11-12 一种超快冷工艺生产q690d厚板及制造方法
CN201811342554.4 2018-11-12

Publications (1)

Publication Number Publication Date
WO2020098288A1 true WO2020098288A1 (fr) 2020-05-22

Family

ID=65315226

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/CN2019/093665 WO2020098288A1 (fr) 2018-11-12 2019-06-28 Plaque épaisse q690d produite par un procédé de refroidissement ultra rapide et procédé de fabrication

Country Status (4)

Country Link
CN (1) CN109338225A (fr)
AU (1) AU2019381076B2 (fr)
WO (1) WO2020098288A1 (fr)
ZA (1) ZA202103240B (fr)

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN111876558A (zh) * 2020-07-21 2020-11-03 安阳钢铁股份有限公司 一种基于lf+vd工艺生产包晶高强钢精准控制碳含量的方法
CN113770176A (zh) * 2021-06-29 2021-12-10 张家港宏昌钢板有限公司 在线识别探伤板、代表板的目视化物料跟踪方法及系统
CN114160580A (zh) * 2021-11-22 2022-03-11 南京钢铁股份有限公司 一种改善耐候钢A709Gr50平直度的冷却方法
CN114231718A (zh) * 2021-11-18 2022-03-25 首钢京唐钢铁联合有限责任公司 一种窄强度同板差的管线钢及其生产方法
CN114480969A (zh) * 2022-01-24 2022-05-13 南阳汉冶特钢有限公司 一种压缩比≤4高韧性高z向性能特厚钢q460gj的生产方法
CN113770176B (zh) * 2021-06-29 2024-05-14 张家港宏昌钢板有限公司 在线识别探伤板、代表板的目视化物料跟踪方法及系统

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN109338225A (zh) * 2018-11-12 2019-02-15 南京钢铁股份有限公司 一种超快冷工艺生产q690d厚板及制造方法

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN102851604A (zh) * 2012-09-22 2013-01-02 内蒙古包钢钢联股份有限公司 一种屈服强度690MPa级高强度钢板的生产方法
CN102888565A (zh) * 2012-09-22 2013-01-23 内蒙古包钢钢联股份有限公司 一种屈服强度690MPa级高强度钢板及其制造方法
CN107675097A (zh) * 2017-08-15 2018-02-09 河钢股份有限公司邯郸分公司 具有良好侧弯性能的高强钢q690d钢板及其生产方法
CN109338225A (zh) * 2018-11-12 2019-02-15 南京钢铁股份有限公司 一种超快冷工艺生产q690d厚板及制造方法

Family Cites Families (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN102268607A (zh) * 2010-06-07 2011-12-07 鞍钢股份有限公司 煤矿液压支架专用高强韧钢板及其制造方法
CN102345061B (zh) * 2011-06-28 2013-06-12 南阳汉冶特钢有限公司 一种q690d优质结构钢中厚板及其生产方法
KR102275814B1 (ko) * 2014-12-31 2021-07-09 두산중공업 주식회사 해양 구조물용 초고강도 고인성 극후 강판 및 그 제조방법
CN104947000A (zh) * 2015-06-14 2015-09-30 秦皇岛首秦金属材料有限公司 屈服强度700MPa级高强钢及TMCP制造方法
KR20160149640A (ko) * 2015-06-18 2016-12-28 현대제철 주식회사 초고강도 강재 및 그 제조방법
CN106282774B (zh) * 2016-08-31 2018-04-20 南京钢铁股份有限公司 一种高横纵向冲击比值大厚度q690e高强钢生产方法
CN106756544B (zh) * 2016-12-12 2019-06-04 南京钢铁股份有限公司 一种超低碳当量大厚度q690d高强钢的生产方法
CN107447167A (zh) * 2017-07-30 2017-12-08 湖南华菱湘潭钢铁有限公司 一种低屈强比高强度中厚钢板的生产方法

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN102851604A (zh) * 2012-09-22 2013-01-02 内蒙古包钢钢联股份有限公司 一种屈服强度690MPa级高强度钢板的生产方法
CN102888565A (zh) * 2012-09-22 2013-01-23 内蒙古包钢钢联股份有限公司 一种屈服强度690MPa级高强度钢板及其制造方法
CN107675097A (zh) * 2017-08-15 2018-02-09 河钢股份有限公司邯郸分公司 具有良好侧弯性能的高强钢q690d钢板及其生产方法
CN109338225A (zh) * 2018-11-12 2019-02-15 南京钢铁股份有限公司 一种超快冷工艺生产q690d厚板及制造方法

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN111876558A (zh) * 2020-07-21 2020-11-03 安阳钢铁股份有限公司 一种基于lf+vd工艺生产包晶高强钢精准控制碳含量的方法
CN113770176A (zh) * 2021-06-29 2021-12-10 张家港宏昌钢板有限公司 在线识别探伤板、代表板的目视化物料跟踪方法及系统
CN113770176B (zh) * 2021-06-29 2024-05-14 张家港宏昌钢板有限公司 在线识别探伤板、代表板的目视化物料跟踪方法及系统
CN114231718A (zh) * 2021-11-18 2022-03-25 首钢京唐钢铁联合有限责任公司 一种窄强度同板差的管线钢及其生产方法
CN114231718B (zh) * 2021-11-18 2024-03-19 首钢京唐钢铁联合有限责任公司 一种窄强度同板差的管线钢及其生产方法
CN114160580A (zh) * 2021-11-22 2022-03-11 南京钢铁股份有限公司 一种改善耐候钢A709Gr50平直度的冷却方法
CN114480969A (zh) * 2022-01-24 2022-05-13 南阳汉冶特钢有限公司 一种压缩比≤4高韧性高z向性能特厚钢q460gj的生产方法

Also Published As

Publication number Publication date
ZA202103240B (en) 2023-03-29
AU2019381076B2 (en) 2022-05-12
CN109338225A (zh) 2019-02-15
AU2019381076A1 (en) 2021-05-27

Similar Documents

Publication Publication Date Title
CN109280850B (zh) 一种80mm大厚度高韧性低合金耐磨钢板及其制造方法
JP5928654B2 (ja) 厚肉高靭性高張力鋼板およびその製造方法
WO2022011936A1 (fr) Plaque de cuve hautement solide présentant une excellente résistance au froid et procédé de fabrication
WO2020098288A1 (fr) Plaque épaisse q690d produite par un procédé de refroidissement ultra rapide et procédé de fabrication
JP6466582B2 (ja) 降伏強度８００ＭＰａ級高強度鋼及びその製造方法
US10443110B2 (en) High toughness and high tensile strength thick steel plate and production method therefor
WO2016095721A1 (fr) Acier à haute résistance trempé et revenu ayant une limite d'élasticité de nuance 900 mpa à 1000 mpa, et procédé pour le fabriquer
CN103014554B (zh) 一种低屈强比高韧性钢板及其制造方法
EP2218801B1 (fr) Tôle d'acier à limite d'élasticité de grade 800 mpa et faible sensibilité à la fissuration de soudure, et son procédé de fabrication
JP5979338B1 (ja) 材質均一性に優れた厚肉高靭性高張力鋼板およびその製造方法
WO2016045266A1 (fr) Acier à haute résistance pour laminage à chaud à haute ténacité présentant une limite d'élasticité de 800 mpa et son procédé de préparation
JP6048626B1 (ja) 厚肉高靭性高強度鋼板およびその製造方法
CN105543669B (zh) 一种厚规格和窄硬度区间耐磨钢板及其制备方法
CN109536846B (zh) 屈服强度700MPa级高韧性热轧钢板及其制造方法
CN105112806A (zh) 屈服强度460MPa级高止裂韧性钢板及其生产方法
WO2020062564A1 (fr) Brame à très haute teneur en acier q960e et procédé de fabrication
WO2022067962A1 (fr) Acier à pont q370qe-hps à haute performance et faible coût, et procédé de production
WO2022052335A1 (fr) Plaque en acier résistante à l'usure haute ténacité à faible équivalent en carbone épaisse et son procédé de fabrication
AU2018387506A1 (en) High-grade low-alloy wear-resistant steel plate having brookfield hardness of greater than 550 HB and manufacturing method
CN103882344A (zh) 加钒铬钼钢板及其生产方法
CN103695807A (zh) 止裂性优良的超高强x100管线钢板及其制备方法
CN110846571A (zh) 一种高韧性低合金耐磨钢厚板及其制造方法
CN114107819A (zh) 一种800MPa级抗回火性高强钢板及其制备方法
CN111748737B (zh) 一种冷裂纹敏感系数≤0.25的易焊接超高强钢及生产方法
CN105112810B (zh) 一种抗大线能量焊接用钢及其制备方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 19884327

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 2019381076

Country of ref document: AU

Date of ref document: 20190628

Kind code of ref document: A

122 Ep: pct application non-entry in european phase

Ref document number: 19884327

Country of ref document: EP

Kind code of ref document: A1