WO2020087426A1 - High-strength rubber - Google Patents
High-strength rubber Download PDFInfo
- Publication number
- WO2020087426A1 WO2020087426A1 PCT/CN2018/113247 CN2018113247W WO2020087426A1 WO 2020087426 A1 WO2020087426 A1 WO 2020087426A1 CN 2018113247 W CN2018113247 W CN 2018113247W WO 2020087426 A1 WO2020087426 A1 WO 2020087426A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- parts
- rubber
- strength
- raw materials
- chloride resin
- Prior art date
Abstract
A high-strength rubber, being made of the following raw materials in parts by weight: 30-55 parts of a natural rubber, 25-40 parts of a silicone rubber, 8-15 parts of a polyvinyl chloride resin, 5-8 parts of nano zinc oxide, 1-3 parts of a vulcanizing agent, 1-3 parts of an antiaging agent, 3-8 parts of carbon black, 3-6 parts of a flame retardant, 4-6 parts of clay powder, 2-4 parts of dibutyl phthalate, 8-10 parts of polyethylene oxide, 7-12 parts of a polyvinylsilicone oil, and 2-8 parts of a butadiene-styrene rubber. Said rubber has good properties such as high tensile strength, flame resistance, aging resistance, corrosion resistance, and good stability.
Description
本发明涉及橡胶技术领域,尤其涉及一种高强度橡胶。The invention relates to the technical field of rubber, in particular to a high-strength rubber.
橡胶在现代社会广泛应用,例如最为常见的制造汽车轮胎,而目前橡胶的耐老化、防油等性能、抗拉强度、稳定性均较差,大大影响和制约了橡胶的使用性能。Rubber is widely used in modern society, such as the most common manufacturing of automobile tires, and the current rubber has poor aging resistance, oil resistance and other properties, tensile strength and stability, which greatly affects and restricts the performance of rubber.
发明内容Summary of the invention
本发明的目的在于提供一种高强度橡胶,以解决上述技术问题。The object of the present invention is to provide a high-strength rubber to solve the above technical problems.
为实现上述目的本发明采用以下技术方案:In order to achieve the above object, the present invention adopts the following technical solutions:
一种高强度橡胶,由以下重量份数的原料制备而成:天然胶30-55份、硅橡胶25-40份、聚氯乙烯树脂8-15份、纳米氧化锌5-8份、硫化剂1-3份、防老剂1-3份、炭黑3-8份、阻燃剂3-6份、陶土粉4-6份、邻苯二甲酸二丁酯2-4份、聚环氧乙烷8-10份、多乙烯基硅油7-12份、丁苯胶2-8份。A high-strength rubber, prepared from the following parts by weight of raw materials: natural rubber 30-55 parts, silicone rubber 25-40 parts, polyvinyl chloride resin 8-15 parts, nano zinc oxide 5-8 parts, vulcanizing agent 1-3 parts, anti-aging agent 1-3 parts, carbon black 3-8 parts, flame retardant 3-6 parts, clay powder 4-6 parts, dibutyl phthalate 2-4 parts, polyethylene oxide 8-10 parts of alkane, 7-12 parts of polyvinyl silicone oil, 2-8 parts of styrene butadiene rubber.
本发明的有益效果是:本发明制备的橡胶具有抗拉强度高,耐火、耐老化、耐腐蚀、稳定性好等良好的性能。The beneficial effects of the present invention are: the rubber prepared by the present invention has good properties such as high tensile strength, fire resistance, aging resistance, corrosion resistance, and good stability.
下面对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本发明一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例,都属于本发明保护的范围。The following clearly and completely describes the technical solutions in the embodiments of the present invention. Obviously, the described embodiments are only a part of the embodiments of the present invention, but not all the embodiments. Based on the embodiments of the present invention, all other embodiments obtained by a person of ordinary skill in the art without making creative efforts fall within the protection scope of the present invention.
实施例1Example 1
一种高强度橡胶,由以下重量份数的原料制备而成:天然胶55份、硅橡胶40份、聚氯乙烯树脂15份、纳米氧化锌8份、硫化剂3份、防老剂3份、炭黑8份、阻燃剂6份、陶土粉6份、邻苯二甲酸二丁酯4份、聚环氧乙烷10份、多乙烯基硅油12份、丁苯胶8份。A high-strength rubber, prepared from the following parts by weight of raw materials: natural rubber 55 parts, silicone rubber 40 parts, polyvinyl chloride resin 15 parts, nano zinc oxide 8 parts, vulcanizing agent 3 parts, anti-aging agent 3 parts, 8 parts of carbon black, 6 parts of flame retardant, 6 parts of clay powder, 4 parts of dibutyl phthalate, 10 parts of polyethylene oxide, 12 parts of polyvinyl silicone oil, and 8 parts of styrene butadiene rubber.
实施例2Example 2
一种高强度橡胶,由以下重量份数的原料制备而成:天然胶50份、硅橡胶30份、聚氯乙烯树脂10份、纳米氧化锌6份、硫化剂2份、防老2份、炭黑5份、 阻燃剂5份、陶土粉5份、邻苯二甲酸二丁酯3份、聚环氧乙烷8份、多乙烯基硅油10份、丁苯胶5份。A high-strength rubber prepared from the following parts by weight of raw materials: 50 parts of natural rubber, 30 parts of silicone rubber, 10 parts of polyvinyl chloride resin, 6 parts of nano zinc oxide, 2 parts of vulcanizing agent, 2 parts of anti-aging, carbon 5 parts black, 5 parts flame retardant, 5 parts clay powder, 3 parts dibutyl phthalate, 8 parts polyethylene oxide, 10 parts polyvinyl silicone oil, and 5 parts styrene butadiene rubber.
本发明原料易得,制备出的橡胶具有抗拉强度高,耐火、耐老化、耐腐蚀、稳定性好等良好的性能。The raw materials of the invention are easily available, and the prepared rubber has good properties such as high tensile strength, fire resistance, aging resistance, corrosion resistance, and good stability.
尽管已经示出和描述了本发明的实施例,对于本领域的普通技术人员而言,可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型,本发明的范围由所附权利要求及其等同物限定。Although the embodiments of the present invention have been shown and described, those of ordinary skill in the art can understand that various changes, modifications, and substitutions can be made to these embodiments without departing from the principles and spirit of the present invention And variations, the scope of the invention is defined by the appended claims and their equivalents.
Claims (2)
- 一种高强度橡胶,其特征在于,由以下重量份数的原料制备而成:天然胶30-55份、硅橡胶25-40份、聚氯乙烯树脂8-15份、纳米氧化锌5-8份、硫化剂1-3份、防老剂1-3份、炭黑3-8份、阻燃剂3-6份、陶土粉4-6份、邻苯二甲酸二丁酯2-4份、聚环氧乙烷8-10份、多乙烯基硅油7-12份、丁苯胶2-8份。A high-strength rubber, characterized by being prepared from the following parts by weight of raw materials: natural rubber 30-55 parts, silicone rubber 25-40 parts, polyvinyl chloride resin 8-15 parts, nano zinc oxide 5-8 Parts, 1-3 parts of vulcanizing agent, 1-3 parts of anti-aging agent, 3-8 parts of carbon black, 3-6 parts of flame retardant, 4-6 parts of clay powder, 2-4 parts of dibutyl phthalate, 8-10 parts of polyethylene oxide, 7-12 parts of polyvinyl silicone oil, and 2-8 parts of styrene butadiene rubber.
- 如权利要求1所述的一种高强度橡胶,其特征在于,由以下重量份数的原料制备而成:天然胶50份、硅橡胶30份、聚氯乙烯树脂10份、纳米氧化锌6份、硫化剂2份、防老2份、炭黑5份、阻燃剂5份、陶土粉5份、邻苯二甲酸二丁酯3份、聚环氧乙烷8份、多乙烯基硅油10份、丁苯胶5份。The high-strength rubber according to claim 1, characterized by being prepared from the following parts by weight of raw materials: 50 parts of natural rubber, 30 parts of silicone rubber, 10 parts of polyvinyl chloride resin, and 6 parts of nano zinc oxide , 2 parts of vulcanizing agent, 2 parts of anti-aging, 5 parts of carbon black, 5 parts of flame retardant, 5 parts of clay powder, 3 parts of dibutyl phthalate, 8 parts of polyethylene oxide, 10 parts of poly vinyl silicone oil 5 pieces of styrene butadiene rubber.