WO2019208909A1 - 기능성 혼합분말이 함유된 전신 마사지용 조성물의 제조방법과 이에 의해 제조된 기능성 혼합분말이 함유된 전신 마사지용 조성물 및 이를 이용한 전신 마사지 방법 - Google Patents

기능성 혼합분말이 함유된 전신 마사지용 조성물의 제조방법과 이에 의해 제조된 기능성 혼합분말이 함유된 전신 마사지용 조성물 및 이를 이용한 전신 마사지 방법 Download PDF

Info

Publication number
WO2019208909A1
WO2019208909A1 PCT/KR2019/000907 KR2019000907W WO2019208909A1 WO 2019208909 A1 WO2019208909 A1 WO 2019208909A1 KR 2019000907 W KR2019000907 W KR 2019000907W WO 2019208909 A1 WO2019208909 A1 WO 2019208909A1
Authority
WO
WIPO (PCT)
Prior art keywords
powder
composition
weight
body massage
functional
Prior art date
Application number
PCT/KR2019/000907
Other languages
English (en)
French (fr)
Inventor
최용학
이은경
고강호
최승희
장혜원
김진영
Original Assignee
Choi Yong Hak
Lee Eun Kyoung
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Choi Yong Hak, Lee Eun Kyoung filed Critical Choi Yong Hak
Publication of WO2019208909A1 publication Critical patent/WO2019208909A1/ko

Abstract

본 발명은 기능성 혼합분말이 함유된 전신 마사지용 조성물의 제조방법과 이에 의해 제조된 기능성 혼합분말이 함유된 전신 마사지용 조성물 및 이를 이용한 전신 마사지 방법에 관한 것으로서, 본 발명은 전신 마시지용 조성물의 제조방법에 있어서, 900-1100 메시 입자크기 범위에서 동일한 입자크기의 황토분말, 일라이트분말, 토르말린분말 및 CMC분말을 준비하는 단계, 상기 동일한 입자크기의 황토분말, 일라이트분말, 토르말린분말 및 CMC분말을 혼합하여 다수의 공극 형성이 가능한 기능성 혼합분말을 제조하는 단계 및 상기 기능성 혼합분말에 동일 중량의 증류수를 혼합하고 교반하여 전신 마사지용 조성물을 제조하는 단계를 포함하며, 인간의 체온과 유사한 36-40℃ 범위에서 건조되는 과정에서 다수의 공극이 형성되면, 인간의 체온과 유사한 36-40℃ 범위에서 특정 원적외선의 방출이 최대가 되어 인체 내 NO(Nitric Oxide) 농도를 증가시키는 효과와 인간의 체온과 유사한 37℃에서 다량 방출되는 특정 원적외선에 의해 인체 내 NO(Nitric Oxide) 농도를 상승시키고 최적의 혈액 순환 유지, 혈관내피 보호, 강력 항산화제 생성, 순환계, 면역계, 신경계 등의 기능 활성화 촉진, 인체의 항상성을 유지시키는 특유의 효과를 가진다.

Description

기능성 혼합분말이 함유된 전신 마사지용 조성물의 제조방법과 이에 의해 제조된 기능성 혼합분말이 함유된 전신 마사지용 조성물 및 이를 이용한 전신 마사지 방법
본 발명은 기능성 혼합분말이 함유된 전신 마사지용 조성물의 제조방법과 이에 의해 제조된 기능성 혼합분말이 함유된 전신 마사지용 조성물 및 이를 이용한 전신 마사지 방법에 관한 것으로서, 더욱 상세하게는 공극의 형성이 최대로 되는 특정 구성 및 특정 입자크기를 갖는 기능성 혼합분말이 함유된 전신 마사지용 조성물을 이용한 마사지를 통해 인체 내 NO(Nitric Oxide) 농도가 증가되어 인체에 매우 유익한 영향을 주는 전신 마사지용 조성물의 제조방법과 이에 의해 제조된 기능성 혼합분말이 함유된 전신 마사지용 조성물 및 이를 이용한 전신 마사지 방법에 관한 것이다.
피부는 인체의 일차 방어막으로서 온도 및 습도 변화와 자외선, 공해물질 등 외부 환경의 자극으로부터 체내의 제기관을 보호해 주는 고유의 기능을 가지고 있다. 자연의 모든 것과 같이, 피부도 스스로의 균형을 유지하려는 항상성을 지니고 있다. 그러나, 피부는 내적 및 외적 요인에 의해 그 항상성이 무너지게 된다. 구체적으로, 나이가 들어감에 따라 내적으로는 신진대사를 조절하는 각종 호르몬의 분비가 감소하고, 면역 세포의 기능과 세포들의 활성이 저하되어, 생체에 필요한 면역 단백질 및 생체 구성 단백질들의 생합성이 줄어들게 된다. 또한 외적으로는 오존층 파괴로 인하여 태양 광선에 자외선 함량이 증가하게 되고, 환경 오염이 더욱 심화됨에 따라 자유 라디칼 및 활성 유해 산소 등이 증가하게 됨으로써 과도한 물리적, 화학적 자극 및 스트레스 등이 가해지게 되고, 이들은 그 자체만으로도 피부를 불안정하게 만들고, 피부의 항상성을 깨뜨리는 원인이 된다. 항상성을 잃은 피부는 밸런스를 잃게 되고, 자체의 리듬이 흐트러지면서 피부 건조와 탄력 저하, 색소 침착, 트러블, 피지의 불균형적인 분비에 이르기까지 여러 가지 피부 고민을 일으키게 되고, 인체의 항상성이 깨지면 부종도 발생되게 된다.
부종(Ederma)은 체내조직세포 사이에 조직액이 괸 상태를 가리키는 말로서, 간단히는 몸이 붓는 증상이다. 이는 심장병이나 신장병 또는 몸의 어느 한 부분의 혈액 순환 장애로 생길 수 있다. 다리의 경우는 특히 심장에서 거리가 멀고 중력에 의한 영향이 크기 때문에 신장으로 가는 혈류가 줄어들어 부종이 생긴다. 또한 여자의 경우 정상적인 임신 또는 임신중독증일때 부종이 발생하며, 수분이나 소금의 섭취를 많이 한 경우나 피로하거나 숙면을 취하지 못했을 때 일시적으로 부종이 나타날 수 있으나 저절로 가라앉는다. 모세혈관의 투과성이 증가하는 경우, 예를 들면 화상, 외상, 국소적 염증, 알레르기 반응 등의 경우에도 국소부종이 발생한다.
부종이 생기게 되면, 몸이 붓고, 체중이 증가하며, 자고 일어나면 눈이 붓고, 손가락의 반지가 꼭 끼고, 신발이 작아진 것 같다. 종아리 경골부위에 손가락으로 누르면 움푹 들어간 채 우묵부종(함요부종)이 나타내기도 한다.
종래의 마사지 조성물은 피부에 영양분을 제공하는 역할을 하는 성분을 포함하며, 그 중 일반적으로 가장 많이 행해지고 있는 것이 곡물이나, 천연물의 추출물 또는 분말을 액상 물질에 혼합하여 사용하는 것이다. 이러한 종래의 마사지 조성물은 피부에 부착되어 기능성 주성분과 영양분 및 유수분성분을 일시에 공급해주는 역할을 보편적으로 수행한다. 그러나 인체 내 NO(Nitric Oxide) 농도 증가를 통해 부종을 감소시키는 기능성 혼합분말이 함유된 전신 마사지용 조성물에 대한 연구는 전무한 실정이다.
본 발명과 관련된 선행문헌을 살펴보면 대한민국 공개특허공보 제10-2018-0009367호에는 천연 추출물을 포함하는 조성물에 관하여 기재되어 있다. 선행문헌의 조성물은 인동, 자초, 율피 및 고삼 추출물을 유효성분으로 포함하여 항염증 효과를 가질 뿐 아니라, 항산화능을 가지므로 산화를 억제하거나 지연시키는 효과와 부종을 억제하거나 완화시키는 효과를 가지는 천연 추출물을 포함하는 조성물에 관한 것이다. 그러나 상기 선행문헌 역시 영양성분 및 유수분성분의 일시적 공급에 의해 효과가 발생하는 것으로서, 본 발명인 인체 내 NO(Nitric Oxide) 농도 증가를 통해 부종을 감소시키는 기능성 혼합분말이 함유된 전신 마사지용 조성물에 대한 연구와는 차이가 있다.
본 발명은 상기와 같은 종래 기술의 문제점을 해결하기 위하여 안출된 것으로서, 본 발명의 목적은 전신 마사지용 조성물이 인간의 체온과 유사한 36-40℃ 범위에서 건조되는 과정에서 다수의 공극이 형성되면, 인간의 체온과 유사한 36-40℃ 범위에서 특정 원적외선의 방출이 최대가 되어 인체 내 NO(Nitric Oxide) 농도를 증가시키는 기능성 혼합분말이 함유된 전신 마사지용 조성물의 제조방법과 이에 의해 제조된 기능성 혼합분말이 함유된 전신 마사지용 조성물 및 이를 이용한 전신 마사지 방법을 제공하는 것이다.
본 발명의 또 다른 목적은 인간의 체온과 유사한 37℃에서 다량 방출되는 원적외선에 의해 인체 내 NO(Nitric Oxide) 농도를 상승시키고 최적의 혈액 순환 유지, 혈관내피 보호, 강력 항산화제 생성, 순환계, 면역계, 신경계 등의 기능 활성화 촉진, 인체의 항상성을 유지시켜주는 기능성 혼합분말이 함유된 전신 마사지용 조성물의 제조방법과 이에 의해 제조된 기능성 혼합분말이 함유된 전신 마사지용 조성물 및 이를 이용한 전신 마사지 방법을 제공하는 것이다.
본 발명의 또 다른 목적은 인체 내 NO(Nitric Oxide) 농도의 증가에 의해 림프 순환이 촉진되고 노폐물이 제거되어 피부의 붓기를 빼주는 기능성 혼합분말이 함유된 전신 마사지용 조성물의 제조방법과 이에 의해 제조된 기능성 혼합분말이 함유된 전신 마사지용 조성물 및 이를 이용한 전신 마사지 방법을 제공하는 것이다.
본 발명의 또 다른 목적은 인체 내 NO(Nitric Oxide) 농도의 증가에 의해 혈액 순환이 촉진되어 영양분과 수분이 공급되고 노폐물이 제거되어 피부탄력을 증가시키고 피로를 회복시키는 기능성 혼합분말이 함유된 전신 마사지용 조성물의 제조방법과 이에 의해 제조된 기능성 혼합분말이 함유된 전신 마사지용 조성물 및 이를 이용한 전신 마사지 방법을 제공하는 것이다.
본 발명은 상기의 목적을 달성하기 위해 전신 마시지용 조성물의 제조방법에 있어서, 900-1100 메시 입자크기 범위에서 동일한 입자크기의 황토분말, 일라이트분말, 토르말린분말 및 CMC분말을 준비하는 단계, 상기 동일한 입자크기의 황토분말, 일라이트분말, 토르말린분말 및 CMC분말을 혼합하여 다수의 공극 형성이 가능한 기능성 혼합분말을 제조하는 단계 및 상기 기능성 혼합분말에 동일 중량의 증류수를 혼합하고 교반하여 전신 마사지용 조성물을 제조하는 단계를 포함하는 기능성 혼합분말이 함유된 전신 마사지용 조성물의 제조방법을 제공한다.
본 발명은 상기 목적을 달성하기 위해 각 기능성 물질 간(間)에 공극 형성이 되는 900-1100 메시 입자크기 범위에서 동일한 입자크기의 황토분말, 일라이트분말, 토르말린분말 및 CMC분말이 혼합된 기능성 혼합분말과 상기 기능성 혼합분말에 증류수가 혼합되어 이루어진 전신 마사지용 조성물을 제공한다.
본 발명은 상기의 목적을 달성하기 위해 900-1100 메시 입자크기 범위에서 동일한 입자크기의 황토분말, 일라이트분말, 토르말린분말 및 CMC분말을 준비하는 단계, 상기 동일한 입자크기의 황토분말, 일라이트분말, 토르말린분말 및 CMC분말을 혼합하여 다수의 공극 형성이 가능한 기능성 혼합분말을 제조하는 단계, 상기 기능성 혼합분말에 동일 중량의 증류수를 혼합하고 교반하여 전신 마사지용 조성물을 제조하는 단계, 상기 전신 마사지용 조성물을 인체의 대상피부표면에 도포하여 제1조성물층을 형성시키는 단계, 상기 제1조성물층 상에 물에 적신 70㎛-90㎛ 두께의 한지를 덮어 한지층을 형성시키는 단계, 상기 한지층 상에 상기 전신 마사지용 조성물을 다시 도포하여 제2조성물층을 형성시키는 단계 및 상기 제2조성물층 상에 은박지를 덮어 은박지층을 형성시키는 단계를 포함하는 기능성 혼합분말이 함유된 전신 마사지용 조성물을 이용한 전신 마사지 방법을 제공한다.
본 발명인 기능성 혼합분말이 함유된 전신 마사지용 조성물 제조방법과 이에 의해 제조된 기능성 혼합분말이 함유된 전신 마사지용 조성물 및 이를 이용한 전신 마사지 방법은 인간의 체온과 유사한 36-40℃ 범위에서 건조되는 과정에서 다수의 공극이 형성되면, 인간의 체온과 유사한 36-40℃ 범위에서 특정 원적외선의 방출이 최대가 되어 인체 내 NO(Nitric Oxide) 농도를 증가시키는 효과를 가진다.
본 발명인 기능성 혼합분말이 함유된 전신 마사지용 조성물 제조방법과 이에 의해 제조된 기능성 혼합분말이 함유된 전신 마사지용 조성물 및 이를 이용한 전신 마사지 방법에서 900-1100 메시(MESH) 입자크기 범위 내에서 동일한 입자크기의 황토분말, 일라이트분말, 토르말린분말 및 CMC분말의 기능성 혼합분말을 이용하여 전신 마사지를 수행하게 되면, 동일한 입자크기로 인해 다수의 특정 크기 공극 형성이 되고, 인간의 체온과 유사한 36-40℃ 범위에서 특정 원적외선의 방출이 풍부하게 이루어져서 인체 내 NO(Nitric Oxide) 농도를 증가시키는 효과를 가진다. 나아가 10㎛-15㎛ 길이범위의 파쇄된 한지가 추가되면, 초기에 황토가 마르지 않은 상태에는 섬유소가 입자 안에서 입자간 결합을 강하게 유지하며 공극을 모두 막아 잡고 있고, 황토가 수분을 잃고 마르는 시간 동안에는 섬유소의 체적이 줄어들어 결합을 유지하면서 미세 공극을 만들어 주는 효과를 가진다. 또한 1000 메시 입자크기의 황토분말, 일라이트분말, 토르말린분말 및 CMC분말에 13㎛ 길이의 파쇄된 한지를 물에 불린 섬유소를 혼합하는 경우에는 1000 메시 입자크기와 13㎛의 길이가 서로 근사한 값이기 때문에 미세공극이 가장 많이 발생되는 결과가 보이고, 인간의 체온과 유사한 36-40℃ 범위에서 특정 원적외선의 방출이 가장 많이 이루어져서 인체 내 NO(Nitric Oxide) 농도를 가장 크게 증가시키는 효과를 가진다.
본 발명인 기능성 혼합분말이 함유된 전신 마사지용 조성물 제조방법과 이에 의해 제조된 기능성 혼합분말이 함유된 전신 마사지용 조성물 및 이를 이용한 전신 마사지 방법은 인간의 체온과 유사한 37℃에서 다량 방출되는 특정 원적외선에 의해 인체 내 NO(Nitric Oxide) 농도를 상승시키고 최적의 혈액 순환 유지, 혈관내피 보호, 강력 항산화제 생성, 순환계, 면역계, 신경계 등의 기능 활성화 촉진, 인체의 항상성을 유지시키는 특유의 효과를 가진다.
본 발명인 기능성 혼합분말이 함유된 전신 마사지용 조성물 제조방법과 이에 의해 제조된 기능성 혼합분말이 함유된 전신 마사지용 조성물 및 이를 이용한 전신 마사지 방법은 인체 내 NO(Nitric Oxide) 농도의 증가에 의해 림프 순환이 촉진되고 노폐물이 제거되어 피부의 부기를 빼주는효과를 가진다.
본 발명인 기능성 혼합분말이 함유된 전신 마사지용 조성물 제조방법과 이에 의해 제조된 기능성 혼합분말이 함유된 전신 마사지용 조성물 및 이를 이용한 전신 마사지 방법은 인체 내 NO(Nitric Oxide) 농도의 증가에 의해 혈액 순환이 촉진되어 영양분과 수분이 공급되고 노폐물이 제거되어 피부탄력을 증가시키고 피로를 회복시키는 효과를 가진다.
도 1은 본 발명인 기능성 혼합분말이 함유된 전신 마사지용 조성물 제조방법의 순서도이다.
도 2는 기능성 혼합분말이 함유된 전신 마사지용 조성물을 이용한 전신 마사지 방법의 순서도이다.
도 3a는 기능성 혼합분말이 함유된 전신 마사지용 조성물을 이용한 전신 마사지 방법에 따라 마사지를 수행하는 모습과 공극의 형성을 보여주는 사진이다.
도 3b는 황토분말 30 중량부, 일라이트분말 170 중량부, 토르말린분말 6 중량부, CMC분말 5 중량부와 섬유소 5 중량부가 혼합되어 이루어진 기능성 혼합분말에서 황토분말, 일라이트분말, 토르말린분말 및 CMC분말은 모두 1000 메시의 동일한 입자크기를 가지고 섬유소는 13㎛ 길이를 가질 때 다수의 공극이 형성되는 것을 보여주는 사진이다.
도 4는 Neogenis Test Strips의 인체 내 NO(Nitric Oxide) 농도에 따른 색상 변화를 보여주는 기준 사진이다.
도 5는 기능성 혼합분말이 함유된 전신 마사지용 조성물을 이용한 전신 마사지 방법이 시술되기 전과 전신 마사지 방법이 시술된 후 실험대상자의 타액(침)을 묻힌 Neogenis Test Strips의 색상을 비교한 사진이다.
도 6은 상이한 입자크기의 황토분말, 일라이트분말, 토르말린분말 및 CMC분말을 혼합한 분말을 이용하여 전신 마사지를 수행한 후 실험대상자의 타액(침)을 묻힌 Neogenis Test Strips의 색상과 동일한 입자크기의 황토분말, 일라이트분말, 토르말린분말 및 CMC분말을 혼합하여 다수의 공극 형성이 가능한 기능성 혼합분말을 이용하여 전신 마사지를 수행한 후의 실험대상자의 타액(침)을 묻힌 Neogenis Test Strips의 색상을 비교한 사진이다.
본 발명의 실시를 위한 최선의 형태로서, 본 발명의 실시를 위한 전신 마사지용 조성물을 이용한 전신 마사지 방법의 순서도에 따라 최선의 실시예를 설명하면 이하와 같다(도 2 참조).
본 발명인 기능성 혼합분말이 함유된 전신 마사지용 조성물을 이용한 전신 마사지 방법은 900-1100 메시 입자크기 범위에서 동일한 입자크기의 황토분말, 일라이트분말, 토르말린분말 및 CMC분말을 준비하는 단계, 상기 동일한 입자크기의 황토분말, 일라이트분말, 토르말린분말 및 CMC분말을 혼합하여 다수의 공극 형성이 가능한 기능성 혼합분말을 제조하는 단계, 상기 기능성 혼합분말에 동일 중량의 증류수를 혼합하고 교반하여 전신 마사지용 조성물을 제조하는 단계, 상기 전신 마사지용 조성물을 인체의 대상피부표면에 도포하여 제1조성물층을 형성시키는 단계, 상기 제1조성물층 상에 물에 적신 70㎛-90㎛ 두께의 한지를 덮어 한지층을 형성시키는 단계, 상기 한지층 상에 상기 전신 마사지용 조성물을 다시 도포하여 제2조성물층을 형성시키는 단계 및 상기 제2조성물층 상에 은박지를 덮어 은박지층을 형성시키는 단계를 포함한다.
상기 900-1100 메시 입자크기 범위에서 동일한 입자크기의 황토분말, 일라이트분말, 토르말린분말 및 CMC분말에 동일 중량의 증류수가 혼합된 전신 마사지용 조성물을 인체의 대상피부표면에 도포하여 제1조성물층을 형성시키고, 상기 제1조성물층은 0.5-2cm 두께를 가지는 것이 바람직하다. 상기 제1조성물층이 0.5cm 미만이면 인간의 체온과 유사한 36-40℃ 범위에서의 특정 원적외선 방출의 양이 상대적으로 적어 인체 내 NO(Nitric Oxide) 농도를 증가시키는 효과가 미흡한 측면이 있고, 제1조성물층이 2cm를 초과하면 특정 크기의 미세 공극의 형성에 어려움이 있고, 피시술자가 답답함을 호소하며 시술과정에서 소요되는 시간이 과다해지는 문제가 발생할 수 있다.
추가하여 상기 제1조성물층 상에 물에 적신 70㎛-90㎛ 두께의 한지를 덮어 한지층이 형성시키는데, 상기 한지층이 형성됨으로써 피부 보습이 향상되는 효과를 가지고 한지층이 70㎛ 미만이면 한지층이 쉽게 찢어지는 문제가 있고 다수의 특정 크기 미세 공극이 형성되지 아니하여 인간의 체온과 유사한 36-40℃ 범위에서의 특정 원적외선 방출이 상대적으로 감소되어 인체 내 NO(Nitric Oxide) 농도를 증가시키는 효과가 발생되지 않는 문제가 발생할 수 있다. 그리고 상기 한지층이 90㎛를 초과하면 한지층이 너무 두꺼워 피시술자가 답답함을 호소하는 문제가 있고 다수의 특정 크기 미세 공극이 형성되지 아니하여 인간의 체온과 유사한 36-40℃ 범위에서의 특정 원적외선 방출이 상대적으로 감소되어 인체 내 NO(Nitric Oxide) 농도를 증가시키는 효과가 발생되지 않는 문제가 발생할 수 있다.
그리고, 상기 한지층 상에 900-1100 메시 입자크기 범위에서 동일한 입자크기의 황토분말, 일라이트분말, 토르말린분말 및 CMC분말에 동일 중량의 증류수가 혼합된 전신 마사지용 조성물을 도포하여 제2조성물층을 형성시킨다. 상기 제2조성물층은 0.5-2cm 두께를 가지는 것이 바람직하다. 제2조성물층이 0.5cm 미만이면 인간의 체온과 유사한 36-40℃ 범위에서의 특정 원적외선 방출의 양이 상대적으로 적어 인체 내 NO(Nitric Oxide) 농도를 증가시키는 효과가 미흡한 측면이 있고, 제2조성물층이 2cm를 초과하면 미세 공극의 형성에 어려움이 있고, 피시술자가 답답함을 호소하며 시술과정에서 소요되는 시간이 과다해지는 문제가 발생할 수 있다.
추가하여 상기 제2조성물층 상에 은박지를 덮어 은박지층을 더 형성시킨다. 상기 은박지층이 형성됨으로써, 다수의 특정 크기 미세 공극에 의해 인간의 체온과 유사한 36-40℃ 범위에서 방출되는 특정 원적외선이 외부로 발산되지 아니하고, 은박지층에 의해 반사되어 인체의 대상피부표면에 조사됨으로써, 대상피부표면에 조사되는 특정 원적외선양이 상대적으로 증가되고 인체 내 NO(Nitric Oxide) 농도의 증가가 증폭된다.
이하, 본 발명의 구체적인 내용을 당업자가 용이하게 실시할 수 있도록 도면을 참조하여 구체적으로 설명한다.
도 1은 본 발명인 기능성 혼합분말이 함유된 전신 마사지용 조성물 제조방법의 순서도이다. 도 1에 의하면 본 발명인 기능성 혼합분말이 함유된 전신 마사지용 조성물의 제조방법은 900-1100 메시 입자크기 범위에서 동일한 입자크기의 황토분말, 일라이트분말, 토르말린분말 및 CMC분말을 준비하는 단계, 상기 동일한 입자크기의 황토분말, 일라이트분말, 토르말린분말 및 CMC분말을 혼합하여 다수의 공극 형성이 가능한 기능성 혼합분말을 제조하는 단계 및 상기 기능성 혼합분말에 동일 중량의 증류수를 혼합하고 교반하여 전신 마사지용 조성물을 제조하는 단계를 포함한다.
인간의 체온과 유사한 36-40℃ 범위에서 본 발명인 기능성 혼합분말이 함유된 전신 마사지용 조성물이 건조되는 과정에서 다수의 공극이 형성되면, 인간의 체온과 유사한 36-40℃ 범위에서 특정 원적외선이 대량으로 방출되고, 인체 내 내피세포(Endothelial cell)에서 특정 원적외선의 자극에 의해 NADPH가 NADP+로 산화되면, L-아르지닌(L-Arginine)이 산소(O2)와 결합하여 L-시트룰린(L-Citrulline)으로 변화하고, 인체 내에서 일산화질소(NO)가 생성된다. 본 발명인 기능성 혼합분말이 함유된 전신 마사지용 조성물에 의해 첫번째로 혈관 내피세포에서 일산화질소(NO)가 많이 발생하며, 혈관 내피세포에서 발생된 일산화질소(NO)는 혈관을 확장하고 노폐물을 없애는 역할을 수행하여 노화를 방지하는 효과를 가진다. 본 발명인 기능성 혼합분말이 함유된 전신 마사지용 조성물에 의해 두번째로 뇌의 신경세포에서도 일산화질소(NO)가 많이 발생하며, 뇌의 신경세포에서 발생된 일산화질소(NO)는 뇌혈류를 강화하여 치매나 알츠하이머를 예방하는 효과를 가진다. 본 발명인 기능성 혼합분말이 함유된 전신 마사지용 조성물에 의해 세번째로 폐에서도 일산화질소(NO)가 많이 발생하며, 폐에서 발생된 일산화질소(NO)는 기도를 확장하여 편안한 호흡을 가능하게 하는 효과를 가진다. 본 발명인 기능성 혼합분말이 함유된 전신 마사지용 조성물에 의해 네번째로 백혈구에서도 일산화질소(NO)가 많이 발생하며, 백혈구에서 발생된 일산화질소(NO)는 식균작용을 강화하여 항암 효과를 증폭시키는 효과를 가진다. 본 발명인 기능성 혼합분말이 함유된 전신 마사지용 조성물에 의해 다섯째로 생식기에서도 일산화질소(NO)가 많이 발생하며, 생식기에서 발생된 일산화질소(NO)는 혈관을 확장하여 발기능력을 강화하는 효과를 가진다,
황토는 황토에서 파장되는 특유의 원적외선이 있으며, 이러한 원적외선은 인체의 건강에 매우 유익한 도움을 주는 것으로 알려져 있다. 또한 이러한 황토는 세포를 활성화시키는 소생력을 동서고금으로부터 인정받아 왔으며 피부노화를 지연시키고 항균성을 지녀 세균을 제거함과 동시에 흡착성을 가지고 있어 마사지용으로 사용하는 경우 피부에 축적된 노폐물을 제거하는 효과가 뛰어나다. 본 발명에서 황토분말은 900-1100 메시 입자크기를 사용한다. 황토분말의 입자크기가 900 메시 미만이면 전신 마사지 방법이 시술되는 실험대상자의 피부에 전신 마사지용 조성물의 부착에 어려움이 발생할 수 있고, 실험대상자의 피부에 상처가 발생될 가능성이 있다. 또한 황토분말의 입자크기가 1100 메시를 초과하면 제조비용이 상승하여 경제성에 문제가 발생할 가능성이 있다. 나아가 황토분말이 900-1100 메시 입자크기 범위를 벗어나면 인간의 체온과 유사한 36-40℃ 범위에서 건조되는 과정에서 다수의 공극이 형성되지 아니할 수 있으며, 인간의 체온과 유사한 36-40℃ 범위에서 특정 원적외선의 방출이 감소될 수 있어 인체 내 NO(Nitric Oxide) 농도를 증가시키는 효과가 발생되지 않을 수 있다.
일라이트(화학조성 : (K,H3O)Al2(Si,Al)4O10(H2O,OH)2)는 단사정계에 속하는 운모족 광물이다. 굳기는 1~2, 비중은 2.6~2.9이고 조흔색은 백색이다. 이러한 화학성분과 결정구조를 가지는 일라이트는 부드러운 원적외선을 방출하는 광물로서 피부에 안전하며, 세포에 대한 생리효과 외에도 보습효과, 탄력효과, 미백효과 및 청정효과 등의 우수한 화장효과를 준다. 일라이트분말은 900-1100 메시 입자크기를 사용한다. 일라이트분말의 입자크기가 900 메시 미만이면 전신 마사지 방법이 시술되는 실험대상자의 피부에 전신 마사지용 조성물의 부착에 어려움이 발생할 수 있고, 실험대상자의 피부에 상처가 발생될 가능성이 있다. 또한 일라이트분말의 입자크기가 1100 메시를 초과하면 제조비용이 상승하여 경제성에 문제가 발생할 가능성이 있다. 나아가 일라이트분말이 900-1100 메시 입자크기 범위를 벗어나면 인간의 체온과 유사한 36-40℃ 범위에서 건조되는 과정에서 다수의 공극이 형성되지 아니할 수 있으며, 인간의 체온과 유사한 36-40℃ 범위에서 특정 원적외선의 방출이 감소될 수 있어 인체 내 NO(Nitric Oxide) 농도를 증가시키는 효과가 발생되지 않을 수 있다.
토르말린(tourmaline, 電氣石)의 화학성분은 철, 마그네슘, 알칼리금속 등과 알루미늄의 복잡한 붕규산염이다. 대개는 6각 또는 9각 때로는 3각 주상을 이루며, 수정과 같은 결정구조를 가지는 육방정계에 속하는 광물로 되어 있다. 토르말린은 피부 순환을 촉진해주는 기능을 한다. 토르말린의 음이온과 미약한 전류가 피부에 닿아 상승효과를 내므로 피부 미용에 매우 효과적이다. 또한, 원적외선을 방출해 피부를 활성화시켜 주므로, 미용과 피부 건강 유지에 우수하다. 토르말린분말은 900-1100 메시 입자크기를 사용한다. 토르말린분말의 입자크기가 900 메시 미만이면 전신 마사지 방법이 시술되는 실험대상자의 피부에 전신 마사지용 조성물의 부착에 어려움이 발생할 수 있고, 실험대상자의 피부에 상처가 발생될 가능성이 있다. 또한 토르말린분말의 입자크기가 1100 메시를 초과하면 제조비용이 상승하여 경제성에 문제가 발생할 가능성이 있다. 나아가 토르말린분말이 900-1100 메시 입자크기 범위를 벗어나면 인간의 체온과 유사한 36-40℃ 범위에서 건조되는 과정에서 다수의 공극이 형성되지 아니할 수 있으며, 인간의 체온과 유사한 36-40℃ 범위에서 특정 원적외선의 방출이 감소될 수 있어 인체 내 NO(Nitric Oxide) 농도를 증가시키는 효과가 발생되지 않을 수 있다.
CMC(Carboxymethylcellulose, 카르복시메틸셀룰로오스)분말은 천연의 결합제로서 전신 마사지용 조성물을 이용하는 마사지 과정에서 다수의 공극을 형성시켜 특정 원적외선의 방출을 최대로 하는 효과를 가지며 독성이 없고 인체에 무해하다. CMC분말은 900-1100 메시 입자크기를 사용한다. CMC분말의 입자크기가 900 메시 미만이면 전신 마사지 방법이 시술되는 실험대상자의 피부에 전신 마사지용 조성물의 부착에 어려움이 발생할 수 있다. 또한 CMC분말의 입자크기가 1100 메시를 초과하면 제조비용이 상승하여 경제성에 문제가 발생할 가능성이 있다. 나아가 CMC분말이 900-1100 메시 입자크기 범위를 벗어나면 인간의 체온과 유사한 36-40℃ 범위에서 건조되는 과정에서 다수의 공극이 형성되지 아니할 수 있으며, 인간의 체온과 유사한 36-40℃ 범위에서 특정 원적외선의 방출이 감소될 수 있어 인체 내 NO(Nitric Oxide) 농도를 증가시키는 효과가 발생되지 않을 수 있다.
황토분말, 일라이트분말, 토르말린분말 및 CMC분말을 혼합하여 제조된 기능성 혼합분말을 이용하여 전신 마사지를 수행할 때 다수의 특정 크기 공극 형성이 가능하기 위해서는 900-1100 메시 입자크기 범위내에서 동일한 입자크기를 가져야한다. 동일한 입자크기가 아닌 상이한 입자크기의 황토분말, 일라이트분말, 토르말린분말 및 CMC분말을 혼합하여 제조된 혼합분말을 이용하여 전신 마사지를 수행하는 경우에는 다수의 특정 크기 공극 형성이 어렵고 인간의 체온과 유사한 36-40℃ 범위에서 특정 원적외선의 방출이 감소되어 인체 내 NO(Nitric Oxide) 농도를 증가시키는 효과가 발생하지 않는다.
상기 기능성 혼합분말을 제조하는 단계에는 10㎛-15㎛ 길이의 파쇄된 한지를 물에 불린 섬유소가 추가로 혼합될 수 있다. 파쇄된 한지를 물에 불린 섬유소를 기능성 혼합분말에 추가함으로써 부드러운 촉감으로 피부와의 접촉성이 향상되고, 10㎛-15㎛ 길이의 파쇄된 한지를 물에 불린 섬유소의 자연성분으로 인하여 마사지 과정 중에 피부 기공을 살아 숨쉬게 되고 피부에 좋은 유효성분의 흡수가 빠르고 보습 효과가 있다. 파쇄된 한지를 물에 불린 섬유소는 10㎛-15㎛ 길이를 가져야 한다. 파쇄된 한지를 물에 불린 섬유소의 길이범위가 10㎛-15㎛를 벗어나게 되면 인간의 체온과 유사한 36-40℃ 범위에서 건조되는 과정에서 다수의 공극이 형성되지 아니하며, 인간의 체온과 유사한 36-40℃ 범위에서 특정 원적외선의 방출이 감소되어 인체 내 NO(Nitric Oxide) 농도를 증가시키는 효과가 발생되지 않는다. 파쇄된 한지를 물에 불린 섬유소는 초기 기능성 혼합분말이 마르지 않은 경우에는 입자 안에서 입자간 결합을 강하게 유지하며 공극을 모두 막아 잡고 있으나, 황토가 수분을 잃고 마르는 시간 동안 파쇄된 한지를 물에 불린 섬유소의 체적이 줄어들어 결합을 유지하면서 미세 공극을 만들어 주게된다. 이러한 미세 공극은 파쇄된 한지를 물에 불린 섬유소가 줄어들어 생기는 공극에 해당한다. 미세공극이 가장 많이 발생되는 길이는 1000 메시 입자크기의 황토분말, 일라이트분말, 토르말린분말 및 CMC분말에 13㎛ 길이의 파쇄된 한지를 물에 불린 섬유소를 혼합하는 경우이다. 1000 메시 입자크기와 13㎛의 길이는 서로 근사한 값이기 때문에 미세공극이 가장 많이 발생되는 결과가 발생되게 된다.
기능성 혼합분말은 상기 황토분말 20-40 중량부, 상기 일라이트분말 150-190 중량부, 상기 토르말린분말 5-7 중량부, 상기 CMC분말 4-6 중량부 및 상기 섬유소 4-6 중량부가 혼합되어 제조될 수 있다.
황토분말은 바람직하게는 20-40 중량부가 혼합된다. 황토분말이 20 중량부 미만이면 마사지 과정 중에서 접착성에 문제가 있고 건조과정에서 부스러짐이 발생할 가능성이 있다. 황토분말이 40 중량부를 초과하면 공극의 수가 감소하고 인간의 체온과 유사한 36-40℃ 범위에서 원적외선 방출이 감소하여 인체 내 NO(Nitric Oxide) 농도를 증가시키는 효과가 발생되지 않는 문제가 발생하여 할 수 있다. 더욱더 바람직하게는 황토분말은 30 중량부가 혼합될 수 있다.
일라이트분말은 바람직하게는 150-190 중량부가 혼합된다. 일라이트분말이 150 중량부 미만이면 공극의 수가 감소하고 인간의 체온과 유사한 36-40℃ 범위에서는 원적외선 방출이 감소하는 문제가 발생할 수 있다. 일라이트분말이 190 중량부를 초과하면 접착성에 문제가 있고 마사지 과정 중에 깨짐이나 부스러짐이 발생할 가능성이 있다. 나아가 일라이트분말이 상기의 범위를 벗어나면 인간의 체온과 유사한 36-40℃ 범위에서의 특정 원적외선 방출이 상대적으로 감소되어 인체 내 NO(Nitric Oxide) 농도를 증가시키는 효과가 발생되지 않는 문제가 발생하여 할 수 있다. 더욱더 바람직하게는 일라이트분말은 170 중량부가 혼합될 수 있다.
토르말린분말은 바람직하게는 5-7 중량부가 혼합된다. 토르말린분말이 상기의 범위를 벗어나면 인간의 체온과 유사한 36-40℃ 범위에서의 특정 원적외선 방출이 상대적으로 감소되어 인체 내 NO(Nitric Oxide) 농도를 증가시키는 효과가 발생되지 않는 문제가 발생하여 할 수 있다. 더욱더 바람직하게는 토르말린분말은 6 중량부가 혼합될 수 있다.
CMC(Carboxymethylcellulose, 카르복시메틸셀룰로오스)분말은 바람직하게는 4-6 중량부가 포함되는 구성을 갖는다. CMC분말이 4 중량부 미만이면 구성요소 간의 결합력이 약해져 마사지 과정 중에 부스러짐이나 갈라짐이 발생하는 문제가 발생할 수 있다. CMC분말이 6 중량부를 초과하면 구성요소 간의 결합력이 너무 강해져 끈적임이 과다하고 마사지를 위해 도포하는 과정에 어려움이 발생할 수 있다. 또한 CMC분말이 상기 범위를 벗어나면 인간의 체온과 유사한 36-40℃ 범위에서의 특정 원적외선 방출이 상대적으로 감소하여 인체 내 NO(Nitric Oxide) 농도를 증가시키는 효과가 발생되지 않는 문제가 발생할 수 있다. CMC분말은 초기 기능성 혼합분말이 마르지 않은 경우에는 입자 안에서 입자간 결합을 강하게 유지하며 공극을 모두 막아 잡고 있으나, 기능성 혼합분말이 수분을 잃고 마르는 시간 동안 그 체적이 줄어들어 결합을 유지하면서 미세 공극을 만들어 주게 된다. 이러한 미세 공극은 CMC의 체적이 줄어들어 생기는 공극에 해당한다. 더욱더 바람직하게는 CMC분말은 5 중량부가 혼합될 수 있다.
파쇄된 한지를 물에 불린 섬유소는 바람직하게는 4-6 중량부가 포함되는 구성을 갖는다. 파쇄된 한지를 물에 불린 섬유소가 4 중량부 미만이면 구성요소 간의 결합력이 약해져 마사지 과정 중에 부스러짐이나 갈라짐이 발생하는 문제가 발생할 수 있다. 파쇄된 한지를 물에 불린 섬유소가 6 중량부를 초과하면 인간의 체온과 유사한 36-40℃ 범위에서의 특정 원적외선 방출이 상대적으로 감소되어 인체 내 NO(Nitric Oxide) 농도를 증가시키는 효과가 발생되지 않는 문제가 발생할 수 있다. 더욱더 바람직하게는 파쇄된 한지를 물에 불린 섬유소는 5 중량부가 혼합될 수 있다.
상기 기능성 혼합분말에는 동일 중량의 증류수가 혼합되고 교반되어 전신 마사지용 조성물이 제조된다. 동일 중량보다 작은 중량의 증류수가 혼합되는 경우에는 점도가 너무 높아 끈적임이 과다하고 마사지를 위해 도포하는 과정에 어려움이 발생할 수 있다. 동일 중량보다 큰 중량의 증류수가 혼합되는 경우에는 점도가 너무 낮아 흘러내림이 발생하는 등 마사지를 위해 도포하는 과정에 어려움이 발생할 수 있다. 나아가 기능성 혼합분말에는 동일 중량의 증류수가 혼합되지 아니하면 인간의 체온과 유사한 36-40℃ 범위에서의 특정 원적외선 방출이 상대적으로 감소되어 인체 내 NO(Nitric Oxide) 농도를 증가시키는 효과가 발생되지 않는 문제가 발생할 수 있다.
전체적으로 상기 구성요소들의 입자크기나 중량이 지정된 범위를 벗어나면 다수의 특정 크기 미세 공극이 형성되지 아니하여 인간의 체온과 유사한 36-40℃ 범위에서의 특정 원적외선 방출이 상대적으로 감소되고 인체 내 NO(Nitric Oxide) 농도가 증가되는 효과에 문제가 발생할 수 있다.
도 3a는 기능성 혼합분말이 함유된 전신 마사지용 조성물을 이용한 전신 마사지 방법에 따라 마사지를 수행하는 모습과 공극의 형성을 보여주는 사진이다.
도 3a에 의하면 제1조성물층, 한지층 및 제2조성물층이 형성된 이후에 10-20분의 건조시간이 적용된다. 즉, 제2조성물층을 형성시키는 단계와 은박지층을 형성시키는 단계 사이에는 10-20분의 시간 간격이 존재하게 된다. 10-20분의 시간 간격 동안 증류수가 증발하면서 다수의 특정 크기 미세 공극이 형성되고, 인간의 체온과 유사한 36-40℃ 범위에서의 특정 원적외선 방출이 상대적으로 많이 발생되어 인체 내 NO(Nitric Oxide) 농도를 증가시키는 효과가 발생되게 된다. 도 3a에 의하면 건조에 의해 공극이 형성되고, 시간이 경과될수록 다수의 공극이 형성되는 것을 볼 수 있다. 은박지층을 형성시키는 단계 이후에는 10-20분의 유지시간이 존재하게 된다. 10-20분의 유지시간 동안 다수의 특정 크기 미세 공극에 의해 발생되는 인간의 체온과 유사한 36-40℃ 범위에서의 특정 원적외선이 인체의 대상피부표면에 조사되고, 인체 내 NO(Nitric Oxide) 농도의 증가가 발생되게 된다.
도 3b는 황토분말 30 중량부, 일라이트분말 170 중량부, 토르말린분말 6 중량부, CMC분말 5 중량부와 섬유소 5 중량부가 혼합되어 이루어진 기능성 혼합분말에서 황토분말, 일라이트분말, 토르말린분말 및 CMC분말은 모두 1000 메시의 동일한 입자크기를 가지고 섬유소는 13㎛ 길이를 가질때 다수의 공극이 형성되는 것을 보여주는 사진으로서, 도 3b에 의하면 파쇄된 한지를 물에 불린 13㎛ 길이의 섬유소를 첨가한 기능성 혼합분말을 이용하여 제2조성물층을 형성한 직후, 1분 경과 후, 3분 경과 후, 5분 경과 후, 10분 경과 후의 사진을 비교해보면 파쇄된 한지를 물에 불린 13㎛ 길이의 섬유소에 의해 다수의 공극이 형성되는 것을 확인할 수 있었다. 즉, 파쇄된 한지를 물에 불린 13㎛ 길이의 섬유소가 첨가되면, 초기 기능성 혼합분말이 마르지 않은 경우에는 입자 안에서 입자간 결합을 강하게 유지하며 공극을 모두 막아 잡고 있게 되고, 기능성 혼합분말이 수분을 잃고 마르는 시간 동안 파쇄된 한지를 물에 불린 섬유소의 체적이 줄어들어 결합을 유지하면서 다수의 미세 공극을 만들어 주는 결과를 확인할 수 있었다. 나아가 도 3a와 도 3b를 비교하면 파쇄된 한지를 물에 불린 13㎛ 길이의 섬유소가 첨가에 의해 생성되는 미세 공극의 수가 더 많아진다는 사실을 알 수 있었다.
도 4는 Neogenis Test Strips의 인체 내 NO(Nitric Oxide) 농도에 따른 색상 변화를 보여주는 기준 사진이다.
도 5는 기능성 혼합분말이 함유된 전신 마사지용 조성물을 이용한 전신 마사지 방법이 시술되기 전과 전신 마사지 방법이 시술된 후 실험대상자의 타액(침)을 묻힌 Neogenis Test Strips의 색상을 비교한 사진이다. 도 5에 의하면 23세의 여성을 대상으로 공복상태에서 실험을 진행한 결과, 전신 마사지 방법이 시술된 전, 후에 인체 내 NO(Nitric Oxide) 농도에 차이가 나타났다. 도 5에 의하면 23세의 여성 실험대상자는 공복상태에서 본 발명인 기능성 혼합분말이 함유된 전신 마사지용 조성물을 이용하여 전신 마시지 방법이 시술되기 전에는 인체 내 NO(Nitric Oxide) 농도가 25-100(Ч㏖/L) 범위 내에 있어 Low(부족)상태에 있었다. 하지만 기능성 혼합분말이 함유된 전신 마사지용 조성물을 이용한 전신 마사지 방법이 시술되고, 10분의 시간이 경과된 후에는 인체 내 NO(Nitric Oxide) 농도가 100-300(Ч㏖/L) 범위 내에 있어 Normal(정상)상태로 상승하였다.
도 6은 상이한 입자크기의 황토분말, 일라이트분말, 토르말린분말 및 CMC분말을 혼합한 분말을 이용하여 전신 마사지를 수행한 후 실험대상자의 타액(침)을 묻힌 Neogenis Test Strips의 색상과 동일한 입자크기의 황토분말, 일라이트분말, 토르말린분말 및 CMC분말을 혼합하여 다수의 공극 형성이 가능한 기능성 혼합분말을 이용하여 전신 마사지를 수행한 후의 실험대상자의 타액(침)을 묻힌 Neogenis Test Strips의 색상을 비교한 사진이다. 도 6에 의하면 동일한 입자크기의 황토분말, 일라이트분말, 토르말린분말 및 CMC분말을 혼합한 기능성 혼합분말을 이용하여 전신 마사지를 수행하고 20분의 시간이 경과된 경우, 다수의 공극 형성되어 인간의 체온과 유사한 36-40℃ 범위에서 특정 원적외선의 방출이 최대가 되고 인체 내 NO(Nitric Oxide) 농도를 증가시키는 효과가 발생되는데 반해, 상이한 입자크기의 황토분말, 일라이트분말, 토르말린분말 및 CMC분말을 혼합한 혼합분말을 이용하여 전신 마사지를 수행하고 20분의 시간이 경과된 경우, 다수의 공극 형성되지 아니하여 인간의 체온과 유사한 36-40℃ 범위에서 특정 원적외선의 방출이 감소되고 인체 내 NO(Nitric Oxide) 농도를 증가시키는 효과가 발생되지 않는다.
도 6을 자세히 살펴보면, 동일한 입자크기의 황토분말, 일라이트분말, 토르말린분말 및 CMC분말을 혼합한 기능성 혼합분말을 이용하여 23세와 38세의 여성을 대상으로 공복상태에서 마사지를 수행하고 실험을 진행한 결과, 전신 마사지 방법이 시술되고 20분의 시간이 경과된 경우 인체 내 NO(Nitric Oxide) 농도의 상승이 나타났다. 도 6에 의하면 23세와 38세의 여성 실험대상자는 모두 공복상태에서 본 발명인 기능성 혼합분말이 함유된 전신 마사지용 조성물을 이용하여 전신 마시지 방법이 시술되기 전에는 인체 내 NO(Nitric Oxide) 농도가 25-100(Ч㏖/L) 범위 내에 있어 Low(부족)상태에 있었다. 그러나 기능성 혼합분말이 함유된 전신 마사지용 조성물을 이용한 전신 마사지 방법이 시술되고, 20분의 시간이 경과된 후에는 23세와 38세의 여성 실험대상자 모두는 인체 내 NO(Nitric Oxide) 농도가 300(Ч㏖/L)을 초과하는 범위로 상승하여 Optimal(최적)상태가 되었다.
공극률이란 고체의 전체 부피에 대한 공극의 비율로서, 일반적으로 입자의 크기가 작고 고를수록 공극률이 큰 값을 갖는다. 본 발명에서 900-1100 메시 입자크기 범위에서 동일한 입자크기의 황토분말, 일라이트분말, 토르말린분말 및 CMC분말의 기능성 혼합분말에 증류수를 혼합하고 교반하여 건조할때 다수의 공극이 형성되고, 이러한 다수의 공극이 형성되는 경우에만 인간의 체온과 유사한 36-40℃ 범위에서 원적외선 방출이 최대가 되어, 전신 마사지를 수행한 후의 실험대상자의 타액(침)을 묻힌 Neogenis Test Strips의 색상에 의하면 인체 내 NO(Nitric Oxide) 농도가 증가됨을 알 수 있었다. 이에 반해 상이한 입자크기의 황토분말, 일라이트분말, 토르말린분말 및 CMC분말의 혼합분말에 증류수를 혼합하고 교반하여 건조할때에는 다수의 공극이 형성되지 않고, 인간의 체온과 유사한 36-40℃ 범위에서 원적외선 방출이 감소되어, 전신 마사지를 수행한 후의 실험대상자의 타액(침)을 묻힌 Neogenis Test Strips의 색상에 의하면 인체 내 NO(Nitric Oxide) 농도가 증가하지 않음을 알 수 있었다
이상에서 살펴본 바와 같이 본 발명인 동일한 입자크기의 황토분말, 일라이트분말, 토르말린분말 및 CMC분말을 혼합한 기능성 혼합분말이 함유된 전신 마사지용 조성물을 이용하여 전신 마사지 방법을 수행하면, 인간의 체온과 유사한 37℃-40℃에서 특정 원적외선이 다량 방출되어, 인체 내 NO(Nitric Oxide) 농도를 상승시키게 되고, 그에 따라 최적의 혈액 순환 유지, 혈관내피 보호, 강력 항산화제 생성, 순환계, 면역계, 신경계 등의 기능 활성화 촉진, 인체의 항상성을 유지라는 특유의 효과를 가지게 된다. 나아가 본 발명인 동일한 입자크기의 황토분말, 일라이트분말, 토르말린분말 및 CMC분말을 혼합한 기능성 혼합분말에 근사한 길이의 파쇄된 한지를 물에 불린 섬유소를 추가한 기능성 혼합분말이 함유된 전신 마사지용 조성물을 이용하여 전신 마사지 방법을 수행하면, 인간의 체온과 유사한 37℃-40℃에서 특정 원적외선이 더욱더 많이 방출되어, 인체 내 NO(Nitric Oxide) 농도의 상승이 더욱더 커지고, 그에 따라 최적의 혈액 순환 유지, 혈관내피 보호, 강력 항산화제 생성, 순환계, 면역계, 신경계 등의 기능 활성화 촉진, 인체의 항상성을 유지라는 특유의 효과가 더욱더 강화되는 효과를 가지게 된다.
[실시예 1]
1000 메시의 황토분말 30g, 일라이트분말 170g, 토르말린분말 6g 및 CMC분말 5g과 13㎛ 길이의 섬유소 5g을 혼합하여 기능성 혼합분말을 제조하였다. 기능성 혼합분말 216g에 216g의 증류수를 혼합하고 교반하여 전신 마사지용 조성물을 제조하였다. 전신 마사지용 조성물을 인체의 대상피부표면에 도포하여 제1조성물층을 형성시키고, 그 위에 물에 적신 70㎛-90㎛ 두께의 한지를 덮어 한지층을 형성시켰다. 그 후에 한지층 전신 마사지용 조성물을 다시 도포하여 제2조성물층을 형성시키고, 20분의 시간 간격을 두고 제2조성물층 상에 은박지를 덮어 은박지층을 형성시켰다. 그 후 20분의 유지시간을 두었다.
[실험예 1]
상기에서 제조된 실시예 1에 의한 부종감소 효과를 알아보기 위해, 20-30대 여성 8명을 대상으로 상기 실시예 1의 기능성 혼합분말이 함유된 전신 마사지용 조성물을 이용한 전신 마사지 방법이 시행되기 전, 후의 종아리 두께를 비교하였다. 상기 실시예 1의 기능성 혼합분말이 함유된 전신 마사지용 조성물을 이용한 전신 마사지 방법이 시행되기 전의 피시험자의 종아리 두께를 측정하고, 상기 실시예 1의 기능성 혼합분말이 함유된 전신 마사지용 조성물을 이용한 전신 마사지 방법이 시행된 후 20분의 유지시간 후의 종아리 둘레 길이를 측정하였다.
표 1은 실시예 1의 기능성 혼합분말이 함유된 전신 마사지용 조성물을 이용한 전신 마사지 방법이 시행되기 전, 후의 종아리 둘레 길이와 본 발명인 기능성 혼합분말이 함유된 전신 마사지용 조성물을 이용한 전신 마사지 방법이 시행된 후의 종아리 둘레 길이 감소율을 나타낸 것이다.
피시험자(20-30대 여성) 전신 마사지 방법 시행 전 종아리 둘레 길이(cm) 전신 마사지 방법 시행 후 종아리 둘레 길이(cm) 감소율(%)
1 34.50 32.80 4.93
2 32.45 31.25 3.70
3 35.30 32.45 8.07
4 37.25 34.50 7.38
5 31.85 29.90 6.12
6 29.90 28.75 3.85
7 32.10 31.35 2.34
8 30.85 28.95 6.16
평균 32.88 31.24 5.39
표 1에 의하면 실시예 1의 기능성 혼합분말이 함유된 전신 마사지용 조성물을 이용한 전신 마사지 방법이 시행되기 전과 후에 평균 5.39%의 종아리 둘레 길이 감소를 보였다. 따라서 본 발명인 기능성 혼합분말이 함유된 전신 마사지용 조성물을 이용한 전신 마사지 방법이 부종 감소 효과가 있음을 확인할 수 있었다.이상과 같이 본 발명은 비록 한정된 실시예들에 의해 설명되었으나, 본 발명은 상기의 실시예들에 한정되는 것은 아니며, 이는 본 발명이 속하는 분야에서 통상의 지식을 가진 자라면 이러한 기재로부터 다양한 수정 및 변형이 가능하다. 따라서, 본 발명의 사상은 아래에 기재된 특허청구범위에 의해서만 파악되어야 하고, 이의 균등 또는 등가적 변형 모두는 본 발명 사상의 범주에 속한다고 할 것이다.
본 발명은 본 발명은 기능성 혼합분말이 함유된 전신 마사지용 조성물의 제조방법과 이에 의해 제조된 기능성 혼합분말이 함유된 전신 마사지용 조성물 및 이를 이용한 전신 마사지 방법에 관한 것으로서, 전신 마사지를 이용하여 피로회복을 시키는 산업분야에 이용 가능하다.

Claims (11)

  1. 각 기능성 물질 간(間)에 공극 형성이 되는 900-1100 메시 입자크기 범위에서 동일한 입자크기의 황토분말, 일라이트분말, 토르말린분말 및 CMC분말이 혼합된 기능성 혼합분말과 상기 기능성 혼합분말에 증류수가 혼합되어 이루어진 전신 마사지용 조성물.
  2. 제1항에 있어서,
    상기 기능성 혼합분말에 10㎛-15㎛ 길이의 파쇄된 한지를 물에 불린 섬유소가 추가로 혼합되어 이루어진 전신 마사지용 조성물.
  3. 제2항에 있어서,
    상기 기능성 혼합분말은 상기 황토분말 20-40 중량부, 상기 일라이트분말 150-190 중량부, 상기 토르말린분말 5-7 중량부, 상기 CMC분말 4-6 중량부 및 상기 섬유소 4-6 중량부가 혼합되어 이루어진 전신 마사지용 조성물.
  4. 전신 마시지용 조성물의 제조방법에 있어서,
    900-1100 메시 입자크기 범위에서 동일한 입자크기의 황토분말, 일라이트분말, 토르말린분말 및 CMC분말을 준비하는 단계;
    상기 동일한 입자크기의 황토분말, 일라이트분말, 토르말린분말 및 CMC분말을 혼합하여 다수의 공극 형성이 가능한 기능성 혼합분말을 제조하는 단계; 및
    상기 기능성 혼합분말에 동일 중량의 증류수를 혼합하고 교반하여 전신 마사지용 조성물을 제조하는 단계;
    를 포함하는 기능성 혼합분말이 함유된 전신 마사지용 조성물의 제조방법.
  5. 제4항에 있어서,
    상기 기능성 혼합분말을 제조하는 단계에는 10㎛-15㎛ 길이의 파쇄된 한지를 물에 불린 섬유소가 추가로 혼합되는 것을 특징으로 하는 기능성 혼합분말이 함유된 전신 마사지용 조성물의 제조방법.
  6. 제5항에 있어서,
    상기 기능성 혼합분말은 상기 황토분말 20-40 중량부, 상기 일라이트분말 150-190 중량부, 상기 토르말린분말 5-7 중량부, 상기 CMC분말 4-6 중량부 및 상기 섬유소 4-6 중량부가 혼합되어 이루어지는 것을 특징으로 하는 기능성 혼합분말이 함유된 전신 마사지용 조성물의 제조방법.
  7. 제6항에 있어서,
    상기 기능성 혼합분말은 상기 황토분말 30 중량부, 상기 일라이트분말 170 중량부, 상기 토르말린분말 6 중량부, 상기 CMC분말 5 중량부와 상기 섬유소 5 중량부가 혼합되어 이루어지며, 상기 황토분말, 상기 일라이트분말, 상기 토르말린분말 및 상기 CMC분말은 모두 1000 메시의 동일한 입자크기를 가지고 상기 섬유소는 13㎛ 길이를 가지는 것을 특징으로 하는 기능성 혼합분말이 함유된 전신 마사지용 조성물의 제조방법.
  8. 900-1100 메시 입자크기 범위에서 동일한 입자크기의 황토분말, 일라이트분말, 토르말린분말 및 CMC분말을 준비하는 단계;
    상기 동일한 입자크기의 황토분말, 일라이트분말, 토르말린분말 및 CMC분말을 혼합하여 다수의 공극 형성이 가능한 기능성 혼합분말을 제조하는 단계;
    상기 기능성 혼합분말에 동일 중량의 증류수를 혼합하고 교반하여 전신 마사지용 조성물을 제조하는 단계;
    상기 전신 마사지용 조성물을 인체의 대상피부표면에 도포하여 제1조성물층을 형성시키는 단계;
    상기 제1조성물층 상에 물에 적신 70㎛-90㎛ 두께의 한지를 덮어 한지층을 형성시키는 단계;
    상기 한지층 상에 상기 전신 마사지용 조성물을 다시 도포하여 제2조성물층을 형성시키는 단계; 및
    상기 제2조성물층 상에 은박지를 덮어 은박지층을 형성시키는 단계;
    를 포함하는 기능성 혼합분말이 함유된 전신 마사지용 조성물을 이용한 전신 마사지 방법.
    900-1100 메시 입자크기 범위에서 동일한 입자크기의 황토분말, 일라이트분말, 토르말린분말 및 CMC분말을 준비하는 단계;
    상기 동일한 입자크기의 황토분말, 일라이트분말, 토르말린분말 및 CMC분말을 혼합하여 다수의 공극 형성이 가능한 기능성 혼합분말을 제조하는 단계;
    상기 기능성 혼합분말에 동일 중량의 증류수를 혼합하고 교반하여 전신 마사지용 조성물을 제조하는 단계;
    상기 전신 마사지용 조성물을 인체의 대상피부표면에 도포하여 제1조성물층을 형성시키는 단계;
    상기 제1조성물층 상에 물에 적신 70㎛-90㎛ 두께의 한지를 덮어 한지층을 형성시키는 단계;
    상기 한지층 상에 상기 전신 마사지용 조성물을 다시 도포하여 제2조성물층을 형성시키는 단계; 및
    상기 제2조성물층 상에 은박지를 덮어 은박지층을 형성시키는 단계;
    를 포함하는 기능성 혼합분말이 함유된 전신 마사지용 조성물을 이용한 전신 마사지 방법.
  9. 제8항에 있어서,
    상기 기능성 혼합분말을 제조하는 단계에는 10㎛-15㎛ 길이의 파쇄된 한지를 물에 불린 섬유소가 추가로 혼합되는 것을 특징으로 하는 기능성 혼합분말이 함유된 전신 마사지용 조성물을 이용한 전신 마사지 방법.
  10. 제9항에 있어서,
    상기 기능성 혼합분말은 상기 황토분말 20-40 중량부, 상기 일라이트분말 150-190 중량부, 상기 토르말린분말 5-7 중량부, 상기 CMC분말 4-6 중량부 및 상기 섬유소 4-6 중량부가 혼합되어 이루어지는 것을 특징으로 하는 기능성 혼합분말이 함유된 전신 마사지용 조성물을 이용한 전신 마사지 방법.
  11. 제10항에 있어서,
    상기 기능성 혼합분말은 상기 황토분말은 30 중량부, 상기 일라이트분말은 170 중량부, 상기 토르말린분말은 6 중량부, 상기 CMC분말은 5 중량부와 상기 섬유소 5 중량부가 혼합되어 이루어지며, 상기 황토분말, 상기 일라이트분말, 상기 토르말린분말 및 상기 CMC분말은 모두 1000 메시 입자크기를 가지고 상기 섬유소는 13㎛ 길이를 가지는 것을 특징으로 하는 기능성 혼합분말이 함유된 전신 마사지용 조성물을 이용한 전신 마사지 방법.
PCT/KR2019/000907 2018-04-27 2019-01-22 기능성 혼합분말이 함유된 전신 마사지용 조성물의 제조방법과 이에 의해 제조된 기능성 혼합분말이 함유된 전신 마사지용 조성물 및 이를 이용한 전신 마사지 방법 WO2019208909A1 (ko)