WO2019150005A1 - Procédés de production de micronutriments à partir de piles alcalines usagées - Google Patents

Procédés de production de micronutriments à partir de piles alcalines usagées Download PDF

Info

Publication number
WO2019150005A1
WO2019150005A1 PCT/FI2019/050085 FI2019050085W WO2019150005A1 WO 2019150005 A1 WO2019150005 A1 WO 2019150005A1 FI 2019050085 W FI2019050085 W FI 2019050085W WO 2019150005 A1 WO2019150005 A1 WO 2019150005A1
Authority
WO
WIPO (PCT)
Prior art keywords
cementation
solution
black mass
leach solution
leaching
Prior art date
Application number
PCT/FI2019/050085
Other languages
English (en)
Inventor
Mikko JOENSUU
Joni RAHUNEN
Lasse RAUTIO
Original Assignee
Tracegrow Oy
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from FI20185100A external-priority patent/FI128333B/en
Application filed by Tracegrow Oy filed Critical Tracegrow Oy
Priority to US16/961,542 priority Critical patent/US20200399736A1/en
Priority to BR112020015906-9A priority patent/BR112020015906A2/pt
Priority to CN201980011688.4A priority patent/CN111684634B/zh
Priority to CA3088491A priority patent/CA3088491A1/fr
Priority to EP19746890.3A priority patent/EP3750206A4/fr
Priority to AU2019214459A priority patent/AU2019214459B2/en
Priority to EA202091734A priority patent/EA202091734A1/ru
Publication of WO2019150005A1 publication Critical patent/WO2019150005A1/fr
Priority to ZA2020/05173A priority patent/ZA202005173B/en

Abstract

La présente invention concerne un procédé de traitement d'une solution de lixiviation de masse noire de batteries alcalines usagées, ladite solution de lixiviation (14) comprenant des métaux dissous dans une solution acide. Dans ledit procédé, un ou plusieurs éléments (49) sont éliminés (D) de la solution de lixiviation par une opération de cimentation (48, 104, 207, 309) par application d'au moins un métal non noble (58) sous forme métallique en tant qu'agent de cimentation (47). En plus d'au moins un métal non noble sous forme métallique, un ou plusieurs agents de cimentation supplémentaires (27), qui se trouvent sous une ou plusieurs formes choisies dans le groupe qui comprend un sulfate et un nitrate, sont appliqués dans l'opération de cimentation afin de traiter la solution de lixiviation en un produit (17, 17', 17'') d'au moins une solution de sulfate contenant du manganèse et du zinc qui est appropriée pour des micronutriments dans des engrais ou en tant que telles pour contribuer à la croissance et à la santé de plantes.En outre, l'invention concerne également un procédé de traitement d'une masse noire de batteries alcalines usagées.
PCT/FI2019/050085 2018-02-05 2019-02-05 Procédés de production de micronutriments à partir de piles alcalines usagées WO2019150005A1 (fr)

Priority Applications (8)

Application Number Priority Date Filing Date Title
US16/961,542 US20200399736A1 (en) 2018-02-05 2019-02-05 Processes for production of micronutrients from spent alkaline batteries
BR112020015906-9A BR112020015906A2 (pt) 2018-02-05 2019-02-05 Processos para a produção de micronutrientes a partir de baterias alcalinas usadas
CN201980011688.4A CN111684634B (zh) 2018-02-05 2019-02-05 从废旧碱性电池生产微量营养素的方法
CA3088491A CA3088491A1 (fr) 2018-02-05 2019-02-05 Procedes de production de micronutriments a partir de piles alcalines usagees
EP19746890.3A EP3750206A4 (fr) 2018-02-05 2019-02-05 Procédés de production de micronutriments à partir de piles alcalines usagées
AU2019214459A AU2019214459B2 (en) 2018-02-05 2019-02-05 Processes for production of micronutrients from spent alkaline batteries
EA202091734A EA202091734A1 (ru) 2018-03-06 2019-02-05 Способ получения питательных микроэлементов из отработавших щелочных батарей
ZA2020/05173A ZA202005173B (en) 2018-02-05 2020-08-20 Processes for production of micronutrients from spent alkaline batteries

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
FI20185100A FI128333B (en) 2018-02-05 2018-02-05 PROCESSES OF ALKALINE BATTERIES USED IN THE MANUFACTURE OF MINERAL NUTRIENTS
FI20185100 2018-02-05
US201862638987P 2018-03-06 2018-03-06
US62/638,987 2018-03-06

Publications (1)

Publication Number Publication Date
WO2019150005A1 true WO2019150005A1 (fr) 2019-08-08

Family

ID=67479661

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/FI2019/050085 WO2019150005A1 (fr) 2018-02-05 2019-02-05 Procédés de production de micronutriments à partir de piles alcalines usagées

Country Status (1)

Country Link
WO (1) WO2019150005A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP3816308A1 (fr) * 2019-11-01 2021-05-05 Battery Reclamation Research Associates LLC Procédé de séparation et de recyclage d'une batterie alcaline usagée
US20210344059A1 (en) * 2020-04-30 2021-11-04 Fortum Oyj Process for recovering components from alkaline batteries

Citations (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CA1133229A (fr) * 1980-10-24 1982-10-12 Cominco Ltd. Epuration des poussieres de zinc des solutions de sulfate de zinc
JPS61261443A (ja) * 1985-05-16 1986-11-19 Nippon Mining Co Ltd 廃乾電池からの有価物の分離回収方法
WO1994011911A1 (fr) 1992-11-18 1994-05-26 Fairtec Delemont S.A. Procede physique et physico-chimique pour le traitement des piles et batteries usagees
EP0620607A1 (fr) 1993-04-16 1994-10-19 Institut National Polytechnique De Grenoble Procédé de traitement de piles usagées par électrolyse
ES2134725A1 (es) * 1997-06-13 1999-10-01 Tecnicas Reunidas S A Procedimiento de tratamiento de pilas electroquimicas secas gastadas de usos domesticos, con recuperacion de elementos componentes.
EP1148571A1 (fr) * 2000-04-17 2001-10-24 Revatech S.A. Procédé de recyclage et de valorisation de piles salines et alcalines
WO2003021708A2 (fr) 2001-07-23 2003-03-13 Recupyl Sa Procede de recyclage des piles electriques usagees par traitement hydrometallurgique
WO2003029148A2 (fr) * 2001-10-01 2003-04-10 Erachem Comilog Procede de preparation d'oxyde mixte de zinc et de manganese
CN1674331A (zh) * 2005-02-28 2005-09-28 张晓东 利用废干电池制备锰锌铁氧体颗粒料和混合碳酸盐的方法
US20110123419A1 (en) * 2009-11-20 2011-05-26 Korea Institute Of Geoscience And Mineral Method for preparing manganese sulfate and zinc sulfate from waste batteries containing manganese and zinc
WO2013124399A1 (fr) 2012-02-24 2013-08-29 Rec Alkaline Oy Récupération d'ions métalliques provenant de déchets de batterie en utilisant de l'ammoniac

Patent Citations (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CA1133229A (fr) * 1980-10-24 1982-10-12 Cominco Ltd. Epuration des poussieres de zinc des solutions de sulfate de zinc
JPS61261443A (ja) * 1985-05-16 1986-11-19 Nippon Mining Co Ltd 廃乾電池からの有価物の分離回収方法
WO1994011911A1 (fr) 1992-11-18 1994-05-26 Fairtec Delemont S.A. Procede physique et physico-chimique pour le traitement des piles et batteries usagees
EP0620607A1 (fr) 1993-04-16 1994-10-19 Institut National Polytechnique De Grenoble Procédé de traitement de piles usagées par électrolyse
ES2134725A1 (es) * 1997-06-13 1999-10-01 Tecnicas Reunidas S A Procedimiento de tratamiento de pilas electroquimicas secas gastadas de usos domesticos, con recuperacion de elementos componentes.
EP1148571A1 (fr) * 2000-04-17 2001-10-24 Revatech S.A. Procédé de recyclage et de valorisation de piles salines et alcalines
EP1148571B1 (fr) 2000-04-17 2009-10-21 Revatech S.A. Procédé de recyclage et de valorisation de piles salines et alcalines
WO2003021708A2 (fr) 2001-07-23 2003-03-13 Recupyl Sa Procede de recyclage des piles electriques usagees par traitement hydrometallurgique
WO2003029148A2 (fr) * 2001-10-01 2003-04-10 Erachem Comilog Procede de preparation d'oxyde mixte de zinc et de manganese
CN1674331A (zh) * 2005-02-28 2005-09-28 张晓东 利用废干电池制备锰锌铁氧体颗粒料和混合碳酸盐的方法
US20110123419A1 (en) * 2009-11-20 2011-05-26 Korea Institute Of Geoscience And Mineral Method for preparing manganese sulfate and zinc sulfate from waste batteries containing manganese and zinc
WO2013124399A1 (fr) 2012-02-24 2013-08-29 Rec Alkaline Oy Récupération d'ions métalliques provenant de déchets de batterie en utilisant de l'ammoniac

Non-Patent Citations (5)

* Cited by examiner, † Cited by third party
Title
BOYANOV, B. S.: "Purification of zinc sulfate solutions from cobalt and nickel through activated cementation", HYDROMETALLURGY, vol. 73, September 2003 (2003-09-01), pages 163 - 168, XP004494953 *
FERELLA ET AL., JOURNAL OF POWER SOURCES, vol. 183, 2008, pages 805 - 811
HASANI M ET AL.: "Effects of zinc and manganese as foliar spray on pomegranate yield, fruit quality and leaf minerals", JOURNAL OF SOIL SCIENCE AND PLANT NUTRITION, vol. 12, no. 3, 31 December 2012 (2012-12-31)
SAYILGAN ET AL.: "A review of technologies for the recovery of metals from spent alkaline and zinc-carbon batteries", HYDROMETALLURGY, vol. 97, 2009, pages 158 - 166
SAYILGAN, E. ET AL.: "A review of technologies for the recovery of metals from spent alkaline and zinc–carbon batteries", HYDROMETALLURGY, vol. 97, March 2009 (2009-03-01), pages 158 - 166, XP026116549 *

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP3816308A1 (fr) * 2019-11-01 2021-05-05 Battery Reclamation Research Associates LLC Procédé de séparation et de recyclage d'une batterie alcaline usagée
US11430997B2 (en) 2019-11-01 2022-08-30 Battery Reclamation Research Associates Llc Process for separating and recycling a spent alkaline battery
US20210344059A1 (en) * 2020-04-30 2021-11-04 Fortum Oyj Process for recovering components from alkaline batteries

Similar Documents

Publication Publication Date Title
US11273453B2 (en) Process, apparatus, and system for recovering materials from batteries
US20160308261A1 (en) Zero lead pollution process for recycling used lead acid batteries
WO2019150005A1 (fr) Procédés de production de micronutriments à partir de piles alcalines usagées
EP3750206A1 (fr) Procédés de production de micronutriments à partir de piles alcalines usagées
AU2019214459B2 (en) Processes for production of micronutrients from spent alkaline batteries
CN116706302A (zh) 一种锂电池回收方法
FI127830B (en) Procedure for processing the black mass in used alkaline batteries
EA040536B1 (ru) Способ получения питательных микроэлементов из отработавших щелочных батарей
WO2023140198A1 (fr) Procédé de récupération de substance précieuse

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 19746890

Country of ref document: EP

Kind code of ref document: A1

DPE1 Request for preliminary examination filed after expiration of 19th month from priority date (pct application filed from 20040101)
ENP Entry into the national phase

Ref document number: 3088491

Country of ref document: CA

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 2019746890

Country of ref document: EP

Effective date: 20200907

ENP Entry into the national phase

Ref document number: 2019214459

Country of ref document: AU

Date of ref document: 20190205

Kind code of ref document: A

REG Reference to national code

Ref country code: BR

Ref legal event code: B01A

Ref document number: 112020015906

Country of ref document: BR

ENP Entry into the national phase

Ref document number: 112020015906

Country of ref document: BR

Kind code of ref document: A2

Effective date: 20200804