WO2019145860A1 - Polariseur réfléchissant multicouche ayant des couches à faible indice cristallin - Google Patents
Polariseur réfléchissant multicouche ayant des couches à faible indice cristallin Download PDFInfo
- Publication number
- WO2019145860A1 WO2019145860A1 PCT/IB2019/050541 IB2019050541W WO2019145860A1 WO 2019145860 A1 WO2019145860 A1 WO 2019145860A1 IB 2019050541 W IB2019050541 W IB 2019050541W WO 2019145860 A1 WO2019145860 A1 WO 2019145860A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polymer layers
- reflective polarizer
- multilayer reflective
- layers
- polymer
- Prior art date
Abstract
L'invention concerne des polariseurs réfléchissants multicouche. En particulier, l'invention concerne des polariseurs réfléchissants multicouche qui comprennent à la fois des couches à haut indice cristallin et des couches à faible indice cristallin. Ces polariseurs réfléchissants peuvent être particulièrement appropriés pour des applications de combineur, y compris des applications d'affichage tête haute d'automobile dans des environnements ambiants exigeants.
Priority Applications (4)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
EP19708891.7A EP3743751A1 (fr) | 2018-01-26 | 2019-01-22 | Polariseur réfléchissant multicouche ayant des couches à faible indice cristallin |
JP2020560631A JP2021510856A (ja) | 2018-01-26 | 2019-01-22 | 結晶性低屈折率層を有する多層反射偏光子 |
US16/964,722 US20200355859A1 (en) | 2018-01-26 | 2019-01-22 | Multilayer Reflective Polarizer with Crystalline Low Index Layers |
KR1020207020849A KR20200115495A (ko) | 2018-01-26 | 2019-01-22 | 결정질 저 굴절률 층을 갖는 다층 반사 편광기 |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US201862622526P | 2018-01-26 | 2018-01-26 | |
US62/622,526 | 2018-01-26 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2019145860A1 true WO2019145860A1 (fr) | 2019-08-01 |
Family
ID=65657495
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/IB2019/050541 WO2019145860A1 (fr) | 2018-01-26 | 2019-01-22 | Polariseur réfléchissant multicouche ayant des couches à faible indice cristallin |
Country Status (5)
Country | Link |
---|---|
US (1) | US20200355859A1 (fr) |
EP (1) | EP3743751A1 (fr) |
JP (1) | JP2021510856A (fr) |
KR (1) | KR20200115495A (fr) |
WO (1) | WO2019145860A1 (fr) |
Cited By (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2020222117A1 (fr) | 2019-04-30 | 2020-11-05 | 3M Innovative Properties Company | Empilement optique |
EP4100274A4 (fr) * | 2020-02-07 | 2024-03-27 | 3M Innovative Properties Company | Systèmes optiques pour systèmes ath |
US12019258B2 (en) | 2018-09-06 | 2024-06-25 | 3M Innovative Properties Company | Multilayer reflective polarizer with crystalline low index layers |
Citations (17)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3610729A (en) | 1969-06-18 | 1971-10-05 | Polaroid Corp | Multilayered light polarizer |
US4446305A (en) | 1981-03-02 | 1984-05-01 | Polaroid Corporation | Optical device including birefringent polymer |
US4540623A (en) | 1983-10-14 | 1985-09-10 | The Dow Chemical Company | Coextruded multi-layered articles |
US5061042A (en) * | 1987-02-02 | 1991-10-29 | Sumitomo Chemical Co., Ltd. | Phase retarder and liquid crystal display using the same |
US5103337A (en) | 1990-07-24 | 1992-04-07 | The Dow Chemical Company | Infrared reflective optical interference film |
US5360659A (en) | 1993-05-24 | 1994-11-01 | The Dow Chemical Company | Two component infrared reflecting film |
WO1995017303A1 (fr) | 1993-12-21 | 1995-06-29 | Minnesota Mining And Manufacturing Company | Film optique multicouche |
US5448404A (en) | 1992-10-29 | 1995-09-05 | The Dow Chemical Company | Formable reflective multilayer body |
US5882774A (en) | 1993-12-21 | 1999-03-16 | Minnesota Mining And Manufacturing Company | Optical film |
WO1999036810A1 (fr) * | 1998-01-13 | 1999-07-22 | Minnesota Mining And Manufacturing Company | Corps optique multicomposant |
WO1999039224A1 (fr) | 1998-01-28 | 1999-08-05 | Minnesota Mining And Manufacturing Company | Filtre interferentiel infrarouge |
US6157490A (en) | 1998-01-13 | 2000-12-05 | 3M Innovative Properties Company | Optical film with sharpened bandedge |
US6368699B1 (en) | 1995-06-26 | 2002-04-09 | 3M Innovative Properties Company | Multilayer polymer film with additional coatings or layers |
US6531230B1 (en) | 1998-01-13 | 2003-03-11 | 3M Innovative Properties Company | Color shifting film |
US6783349B2 (en) | 1998-01-13 | 2004-08-31 | 3M Innovative Properties Company | Apparatus for making multilayer optical films |
WO2011146288A1 (fr) * | 2010-05-21 | 2011-11-24 | 3M Innovative Properties Company | Films optiques multicouches partiellement réfléchissants à couleur réduite |
US20140313572A1 (en) * | 2013-04-19 | 2014-10-23 | 3M Innovative Properties Company | Multilayer Stack with Overlapping Harmonics for Wide Visible-Infrared Coverage |
Family Cites Families (24)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4310584A (en) * | 1979-12-26 | 1982-01-12 | The Mearl Corporation | Multilayer light-reflecting film |
US5278694A (en) * | 1990-01-11 | 1994-01-11 | The Dow Chemical Company | Optically dissimilar composition for polymeric reflective bodies |
WO1997001778A1 (fr) * | 1995-06-26 | 1997-01-16 | Minnesota Mining And Manufacturing Company | Dispositif multicouche transparent |
US6049419A (en) * | 1998-01-13 | 2000-04-11 | 3M Innovative Properties Co | Multilayer infrared reflecting optical body |
JP4274696B2 (ja) * | 1998-01-13 | 2009-06-10 | スリーエム カンパニー | 変性コポリエステルおよび改善された多層反射フィルム |
US7064897B2 (en) * | 2002-12-31 | 2006-06-20 | 3M Innovative Properties Company | Optical polarizing films with designed color shifts |
US7345137B2 (en) * | 2004-10-18 | 2008-03-18 | 3M Innovative Properties Company | Modified copolyesters and optical films including modified copolyesters |
JP2008537797A (ja) * | 2005-04-06 | 2008-09-25 | スリーエム イノベイティブ プロパティズ カンパニー | 特定の機能層を有する光学フィルムを備えた光学体 |
US20070047080A1 (en) * | 2005-08-31 | 2007-03-01 | 3M Innovative Properties Company | Methods of producing multilayer reflective polarizer |
US20080274293A1 (en) * | 2006-03-31 | 2008-11-06 | 3M Innovative Properties Company | Spiral Multilayer Fibers |
KR101073845B1 (ko) * | 2009-12-22 | 2011-10-17 | 에스케이씨 주식회사 | 2파장 반사 다층필름 |
US9477011B2 (en) * | 2010-06-30 | 2016-10-25 | Yufeng Liu | Multilayer optical film |
JP2012030563A (ja) * | 2010-08-03 | 2012-02-16 | Toray Ind Inc | 積層フィルムおよびそれを用いた自動車用窓ガラス |
KR20140005222A (ko) * | 2010-12-30 | 2014-01-14 | 쓰리엠 이노베이티브 프로퍼티즈 컴파니 | 금 대향 층을 갖는 지지 부재를 사용하여 레이저 절단하기 위한 장치 및 방법 |
EP2769247B1 (fr) * | 2011-10-20 | 2021-12-01 | 3M Innovative Properties Company | Réflecteurs partiels large bande apodisés |
US9551818B2 (en) * | 2011-10-20 | 2017-01-24 | 3M Innovative Properties Company | Apodized broadband partial reflectors having differing optical packets |
KR101417250B1 (ko) * | 2012-02-20 | 2014-07-08 | (주)엘지하우시스 | 고내열성 다층 광학필름 및 그의 제조방법 |
WO2015034910A1 (fr) * | 2013-09-05 | 2015-03-12 | 3M Innovative Properties Company | Marque dessinée de film optique multicouche par conduction thermique |
US10185068B2 (en) * | 2013-09-06 | 2019-01-22 | 3M Innovative Properties Company | Multilayer reflective polarizer |
KR20180027590A (ko) * | 2015-08-14 | 2018-03-14 | 젠텍스 코포레이션 | 헤드업 디스플레이 시스템 |
EP3463875A1 (fr) * | 2016-05-25 | 2019-04-10 | 3M Innovative Properties Company | Substrat destiné à un capteur tactile |
CN109154693B (zh) * | 2016-05-26 | 2021-05-04 | 3M创新有限公司 | 偏振器叠堆 |
US10948644B2 (en) * | 2016-07-13 | 2021-03-16 | 3M Innovative Properties Company | Optical film having third or higher order visible reflection bands |
US20230168421A1 (en) * | 2021-11-29 | 2023-06-01 | 3M Innovative Properties Company | Optical film, reflective polarizer, optical stack, and optical construction |
-
2019
- 2019-01-22 WO PCT/IB2019/050541 patent/WO2019145860A1/fr unknown
- 2019-01-22 US US16/964,722 patent/US20200355859A1/en active Pending
- 2019-01-22 KR KR1020207020849A patent/KR20200115495A/ko unknown
- 2019-01-22 JP JP2020560631A patent/JP2021510856A/ja active Pending
- 2019-01-22 EP EP19708891.7A patent/EP3743751A1/fr active Pending
Patent Citations (17)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3610729A (en) | 1969-06-18 | 1971-10-05 | Polaroid Corp | Multilayered light polarizer |
US4446305A (en) | 1981-03-02 | 1984-05-01 | Polaroid Corporation | Optical device including birefringent polymer |
US4540623A (en) | 1983-10-14 | 1985-09-10 | The Dow Chemical Company | Coextruded multi-layered articles |
US5061042A (en) * | 1987-02-02 | 1991-10-29 | Sumitomo Chemical Co., Ltd. | Phase retarder and liquid crystal display using the same |
US5103337A (en) | 1990-07-24 | 1992-04-07 | The Dow Chemical Company | Infrared reflective optical interference film |
US5448404A (en) | 1992-10-29 | 1995-09-05 | The Dow Chemical Company | Formable reflective multilayer body |
US5360659A (en) | 1993-05-24 | 1994-11-01 | The Dow Chemical Company | Two component infrared reflecting film |
US5882774A (en) | 1993-12-21 | 1999-03-16 | Minnesota Mining And Manufacturing Company | Optical film |
WO1995017303A1 (fr) | 1993-12-21 | 1995-06-29 | Minnesota Mining And Manufacturing Company | Film optique multicouche |
US6368699B1 (en) | 1995-06-26 | 2002-04-09 | 3M Innovative Properties Company | Multilayer polymer film with additional coatings or layers |
WO1999036810A1 (fr) * | 1998-01-13 | 1999-07-22 | Minnesota Mining And Manufacturing Company | Corps optique multicomposant |
US6157490A (en) | 1998-01-13 | 2000-12-05 | 3M Innovative Properties Company | Optical film with sharpened bandedge |
US6531230B1 (en) | 1998-01-13 | 2003-03-11 | 3M Innovative Properties Company | Color shifting film |
US6783349B2 (en) | 1998-01-13 | 2004-08-31 | 3M Innovative Properties Company | Apparatus for making multilayer optical films |
WO1999039224A1 (fr) | 1998-01-28 | 1999-08-05 | Minnesota Mining And Manufacturing Company | Filtre interferentiel infrarouge |
WO2011146288A1 (fr) * | 2010-05-21 | 2011-11-24 | 3M Innovative Properties Company | Films optiques multicouches partiellement réfléchissants à couleur réduite |
US20140313572A1 (en) * | 2013-04-19 | 2014-10-23 | 3M Innovative Properties Company | Multilayer Stack with Overlapping Harmonics for Wide Visible-Infrared Coverage |
Non-Patent Citations (4)
Title |
---|
A. THELAN: "Design of Optical Interference Filters", 1989, MCGRAW-HILL, INC. |
FARAHATY ET AL.: "Study of Optical and Structure Properties of Polyester (PET) and Copolyester (PETG) Fibers by Interferometry", INTERNATIONAL JOURNAL OF POLYMERIC MATERIALS, vol. 56, 2007, pages 715 - 728, XP002791057 * |
H. A. MACLEOD: "Thin-Film Optical Filters", 1986, MACMILLAN PUBLISHING CO. |
WEBER: "Giant Birefringent Optics in Multilayer Polymer Mirrors", SCIENCE, vol. 287, March 2000 (2000-03-01), XP000990141, DOI: doi:10.1126/science.287.5462.2451 |
Cited By (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US12019258B2 (en) | 2018-09-06 | 2024-06-25 | 3M Innovative Properties Company | Multilayer reflective polarizer with crystalline low index layers |
WO2020222117A1 (fr) | 2019-04-30 | 2020-11-05 | 3M Innovative Properties Company | Empilement optique |
EP4100274A4 (fr) * | 2020-02-07 | 2024-03-27 | 3M Innovative Properties Company | Systèmes optiques pour systèmes ath |
Also Published As
Publication number | Publication date |
---|---|
JP2021510856A (ja) | 2021-04-30 |
EP3743751A1 (fr) | 2020-12-02 |
US20200355859A1 (en) | 2020-11-12 |
KR20200115495A (ko) | 2020-10-07 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
EP0736187B1 (fr) | Polariseur optique | |
US6565982B1 (en) | Transparent multilayer device | |
US6926952B1 (en) | Anti-reflective polymer constructions and method for producing same | |
KR102227059B1 (ko) | 다층 반사 편광기 | |
US20240302583A1 (en) | Multilayer optical film with crystalline low index layers | |
EP3593194B1 (fr) | Ensemble de projection pour véhicule | |
US20200355859A1 (en) | Multilayer Reflective Polarizer with Crystalline Low Index Layers | |
US20220146728A1 (en) | Optical film and glass laminate | |
US20210302637A1 (en) | Optical film including infrared reflector and multilayer reflective polarizer with crystalline low index layers | |
EP3899610B1 (fr) | Empilement optique |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 19708891 Country of ref document: EP Kind code of ref document: A1 |
|
ENP | Entry into the national phase |
Ref document number: 2020560631 Country of ref document: JP Kind code of ref document: A |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
ENP | Entry into the national phase |
Ref document number: 2019708891 Country of ref document: EP Effective date: 20200826 |