WO2019132310A1 - Tôle d'acier résistante à l'usure ayant une excellente uniformité de matériau, et procédé de fabrication associé - Google Patents

Tôle d'acier résistante à l'usure ayant une excellente uniformité de matériau, et procédé de fabrication associé Download PDF

Info

Publication number
WO2019132310A1
WO2019132310A1 PCT/KR2018/015581 KR2018015581W WO2019132310A1 WO 2019132310 A1 WO2019132310 A1 WO 2019132310A1 KR 2018015581 W KR2018015581 W KR 2018015581W WO 2019132310 A1 WO2019132310 A1 WO 2019132310A1
Authority
WO
WIPO (PCT)
Prior art keywords
steel sheet
excluding
less
uniformity
hardness
Prior art date
Application number
PCT/KR2018/015581
Other languages
English (en)
Korean (ko)
Inventor
김용우
정영진
유승호
Original Assignee
주식회사 포스코
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 포스코 filed Critical 주식회사 포스코
Publication of WO2019132310A1 publication Critical patent/WO2019132310A1/fr

Abstract

La présente invention concerne une tôle d'acier ayant un haut degré de dureté, utilisée dans l'industrie, des machines de construction et analogues et, plus particulièrement, une tôle d'acier résistante à l'usure ayant une excellente uniformité de matériau, et un procédé de fabrication associé.
PCT/KR2018/015581 2017-12-26 2018-12-10 Tôle d'acier résistante à l'usure ayant une excellente uniformité de matériau, et procédé de fabrication associé WO2019132310A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
KR10-2017-0179490 2017-12-26
KR1020170179490A KR102045646B1 (ko) 2017-12-26 2017-12-26 재질 균일성이 우수한 내마모 강판 및 그 제조방법

Publications (1)

Publication Number Publication Date
WO2019132310A1 true WO2019132310A1 (fr) 2019-07-04

Family

ID=67067807

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/KR2018/015581 WO2019132310A1 (fr) 2017-12-26 2018-12-10 Tôle d'acier résistante à l'usure ayant une excellente uniformité de matériau, et procédé de fabrication associé

Country Status (2)

Country Link
KR (1) KR102045646B1 (fr)
WO (1) WO2019132310A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN115667562A (zh) * 2020-05-28 2023-01-31 杰富意钢铁株式会社 耐磨损钢板和耐磨损钢板的制造方法
CN115667561A (zh) * 2020-05-28 2023-01-31 杰富意钢铁株式会社 耐磨损钢板和耐磨损钢板的制造方法

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
AU2021280575B2 (en) * 2020-05-28 2023-12-14 Jfe Steel Corporation Abrasion-resistant steel plate and method of producing abrasion-resistant steel plate

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2002020837A (ja) * 2000-07-06 2002-01-23 Nkk Corp 靭性に優れた耐摩耗鋼およびその製造方法
KR20120071614A (ko) * 2010-12-23 2012-07-03 주식회사 포스코 저온인성이 우수한 극후물 내마모용 후강판 및 그 제조방법
KR20150036798A (ko) * 2012-09-19 2015-04-07 제이에프이 스틸 가부시키가이샤 저온 인성 및 내부식 마모성이 우수한 내마모 강판
US20160002759A1 (en) * 2013-03-28 2016-01-07 Baoshan Iron & Steel Co., Ltd. High-toughness low-alloy wear-resistant steel sheet and method of manufacturing the same
KR20160072099A (ko) * 2013-08-30 2016-06-22 라우타루끼 오와이제이 고경도 열간압연된 강 제품 및 이를 제조하는 방법
KR101696094B1 (ko) * 2015-08-21 2017-01-13 주식회사 포스코 고 경도 강판 및 그 제조방법

Family Cites Families (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS61166954A (ja) 1985-01-18 1986-07-28 Sumitomo Metal Ind Ltd 高靭性耐摩耗鋼
JPH0841535A (ja) 1994-07-29 1996-02-13 Nippon Steel Corp 低温靱性に優れた高硬度耐摩耗鋼の製造方法
JP4650013B2 (ja) * 2004-02-12 2011-03-16 Jfeスチール株式会社 低温靱性に優れた耐摩耗鋼板およびその製造方法
MX348365B (es) 2011-03-29 2017-06-08 Jfe Steel Corp Placa de acero o lamina de acero resistente a la abrasion excelente en resistencia al agrietamiento por corrosion y esfuerzo y metodo para la fabricacion de la misma.

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2002020837A (ja) * 2000-07-06 2002-01-23 Nkk Corp 靭性に優れた耐摩耗鋼およびその製造方法
KR20120071614A (ko) * 2010-12-23 2012-07-03 주식회사 포스코 저온인성이 우수한 극후물 내마모용 후강판 및 그 제조방법
KR20150036798A (ko) * 2012-09-19 2015-04-07 제이에프이 스틸 가부시키가이샤 저온 인성 및 내부식 마모성이 우수한 내마모 강판
US20160002759A1 (en) * 2013-03-28 2016-01-07 Baoshan Iron & Steel Co., Ltd. High-toughness low-alloy wear-resistant steel sheet and method of manufacturing the same
KR20160072099A (ko) * 2013-08-30 2016-06-22 라우타루끼 오와이제이 고경도 열간압연된 강 제품 및 이를 제조하는 방법
KR101696094B1 (ko) * 2015-08-21 2017-01-13 주식회사 포스코 고 경도 강판 및 그 제조방법

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN115667562A (zh) * 2020-05-28 2023-01-31 杰富意钢铁株式会社 耐磨损钢板和耐磨损钢板的制造方法
CN115667561A (zh) * 2020-05-28 2023-01-31 杰富意钢铁株式会社 耐磨损钢板和耐磨损钢板的制造方法

Also Published As

Publication number Publication date
KR102045646B1 (ko) 2019-11-15
KR20190077916A (ko) 2019-07-04

Similar Documents

Publication Publication Date Title
WO2018117481A1 (fr) Acier résistant à l'usure à dureté élevée et son procédé de fabrication
WO2016104975A1 (fr) Matériau d'acier haute résistance pour récipient sous pression ayant une ténacité remarquable après traitement thermique post-soudure (pwht), et son procédé de production
WO2019125083A1 (fr) Acier résistant à l'usure possédant une excellente dureté et une excellente ténacité aux chocs, et son procédé de production
WO2018117482A1 (fr) Acier résistant à l'usure à dureté élevée et son procédé de fabrication
WO2020067685A1 (fr) Acier résistant à l'usure ayant d'excellentes dureté et ténacité au choc et procédé de fabrication de celui-ci
WO2021125621A1 (fr) Acier résistant à l'usure à dureté élevée ayant une excellente ténacité à l'impact à basse température, et son procédé de fabrication
WO2018074887A1 (fr) Armature de béton armé à haute résistance et procédé de fabrication de ladite armature de béton armé à haute résistance
WO2021091138A1 (fr) Plaque d'acier présentant une résistance élevée et une excellente ténacité à basse température, et son procédé de fabrication
WO2018117497A1 (fr) Matériau d'acier pour tuyau en acier soudé, présentant un excellent allongement uniforme longitudinal, son procédé de fabrication, et tuyau en acier l'utilisant
WO2019132310A1 (fr) Tôle d'acier résistante à l'usure ayant une excellente uniformité de matériau, et procédé de fabrication associé
WO2017034216A1 (fr) Tôle d'acier à dureté élevée et son procédé de fabrication
WO2018117676A1 (fr) Matériau d'acier austénitique présentant une résistance à l'abrasion et une ténacité excellentes, et procédé pour le produire
WO2020067686A1 (fr) Acier résistant à l'abrasion présentant une excellente dureté et une excellente solidité au choc, et son procédé de fabrication
WO2018088761A1 (fr) Acier de résevoir sous pression doté d'une excellente résistance à la fissuration induite par l'hydrogène et procédé de fabrication associé
WO2018117507A1 (fr) Tôle d'acier à faible rapport d'élasticité présentant une excellente ténacité à basse température et son procédé de fabrication
WO2018117470A1 (fr) Tôle d'acier haute résistance ayant une excellente aptitude au soyage à basse température et son procédé de fabrication
WO2018117496A1 (fr) Acier pour récipients sous pression ayant une excellente résistance aux traitements thermiques de trempe à haute température et aux traitements thermiques après soudage et son procédé de fabrication
WO2017111345A1 (fr) Acier à haute résistance de type à faible rapport d'élasticité et son procédé de fabrication
WO2022139191A1 (fr) Matériau d'acier hautement épais ayant une excellente résistance aux chocs à basse température et son procédé de fabrication
WO2020226301A1 (fr) Feuille d'acier très haute résistance offrant une excellente ouvrabilité de cisaillement et son procédé de fabrication
WO2018117606A1 (fr) Acier revêtu par immersion à chaud présentant une excellente aptitude au traitement, et son procédé de fabrication
WO2021010599A2 (fr) Acier inoxydable austénitique ayant une résistance améliorée et procédé de fabrication associé
WO2013154254A1 (fr) Tôle d'acier laminée à chaud à teneur élevée en carbone présentant une excellente uniformité et son procédé de fabrication
WO2019125076A1 (fr) Acier résistant à l'usure ayant d'excellentes dureté et ténacité au choc et procédé pour la production de celui-ci
WO2022139214A1 (fr) Acier inoxydable martensitique ayant une résistance et une résistance à la corrosion améliorées, et son procédé de fabrication

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 18894002

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 18894002

Country of ref document: EP

Kind code of ref document: A1