WO2019077050A1 - Set control composition for cementitious systems - Google Patents
Set control composition for cementitious systems Download PDFInfo
- Publication number
- WO2019077050A1 WO2019077050A1 PCT/EP2018/078576 EP2018078576W WO2019077050A1 WO 2019077050 A1 WO2019077050 A1 WO 2019077050A1 EP 2018078576 W EP2018078576 W EP 2018078576W WO 2019077050 A1 WO2019077050 A1 WO 2019077050A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- carbonate
- composition according
- acid
- groups
- cement
- Prior art date
Abstract
Description
Claims