WO2019023789A1 - Procédé et appareil d'extrusion de matériau visqueux pour impression tridimensionnelle indirecte de métal - Google Patents

Procédé et appareil d'extrusion de matériau visqueux pour impression tridimensionnelle indirecte de métal Download PDF

Info

Publication number
WO2019023789A1
WO2019023789A1 PCT/CA2018/050921 CA2018050921W WO2019023789A1 WO 2019023789 A1 WO2019023789 A1 WO 2019023789A1 CA 2018050921 W CA2018050921 W CA 2018050921W WO 2019023789 A1 WO2019023789 A1 WO 2019023789A1
Authority
WO
WIPO (PCT)
Prior art keywords
nozzle
viscous material
curing
build
viscous
Prior art date
Application number
PCT/CA2018/050921
Other languages
English (en)
Inventor
Eric SAMMUT
Original Assignee
Sammut Eric
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sammut Eric filed Critical Sammut Eric
Publication of WO2019023789A1 publication Critical patent/WO2019023789A1/fr

Abstract

L'invention concerne un appareil d'extrusion pour fabriquer un objet tridimensionnel (3D) à partir d'une charge de matériau visqueux, comprenant une buse qui dépose le matériau visqueux pour construire l'objet 3D, un système de distribution de matériau visqueux qui distribue le matériau visqueux à la buse ; et un appareil de durcissement associé à la buse qui produit de l'énergie de durcissement et focalise l'énergie de durcissement au niveau de la pointe de buse pour initier le durcissement du matériau visqueux lorsqu'il sort de la buse. La charge de matière visqueuse comprend le matériau de construction et un liant qui peut être activé (c'est-à-dire durci) par exposition à l'énergie de durcissement telle que la chaleur et/ou la lumière. Des modes de réalisation peuvent être mis en œuvre dans une imprimante 3D et permettent une fabrication rapide de moules de coulée et de composants de moules de coulée qui sont prêts au coulage ou des objets crus en poudre métallique qui sont prêts au déliantage et au frittage.
PCT/CA2018/050921 2017-08-01 2018-07-30 Procédé et appareil d'extrusion de matériau visqueux pour impression tridimensionnelle indirecte de métal WO2019023789A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US201762539700P 2017-08-01 2017-08-01
US62/539,700 2017-08-01

Publications (1)

Publication Number Publication Date
WO2019023789A1 true WO2019023789A1 (fr) 2019-02-07

Family

ID=65232145

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/CA2018/050921 WO2019023789A1 (fr) 2017-08-01 2018-07-30 Procédé et appareil d'extrusion de matériau visqueux pour impression tridimensionnelle indirecte de métal

Country Status (1)

Country Link
WO (1) WO2019023789A1 (fr)

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN109895385A (zh) * 2019-02-25 2019-06-18 泉州市比邻三维科技有限公司 一种3d打印机器人的改进型出料结构及3d打印机器人
CN110435136A (zh) * 2019-08-06 2019-11-12 武汉卫亚汽车零部件有限公司 一种汽车座椅连接杆一体成型的工艺
US11318679B2 (en) * 2019-06-25 2022-05-03 Mighty Buildings, Inc. 3D printer print head system with curing module on rotation platform
CN114749682A (zh) * 2022-04-07 2022-07-15 中国第一汽车股份有限公司 一种隔离材料、金属3d打印零件及其制备方法
US20220314561A1 (en) * 2021-03-31 2022-10-06 Mighty Buildings, Inc. High intensity light curing for three-dimensional printing
US20230271251A1 (en) * 2022-02-28 2023-08-31 Xerox Corporation Metal drop ejecting three-dimensional (3d) object printer and method of operation for building support structures

Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2016125138A2 (fr) * 2015-02-02 2016-08-11 Massivit 3D Printing Technologies Ltd Système de durcissement permettant d'imprimer des objets 3d

Patent Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2016125138A2 (fr) * 2015-02-02 2016-08-11 Massivit 3D Printing Technologies Ltd Système de durcissement permettant d'imprimer des objets 3d

Non-Patent Citations (5)

* Cited by examiner, † Cited by third party
Title
"Potterbot 7 UV PASTE 3D printer", POTTER, 8 July 2017 (2017-07-08), pages 1 - 2, XP055575457, Retrieved from the Internet <URL:https://web.archive.org/web/20170708055622/http://www.deltabots.com:80/products/v-25-uv-uv-paste-printer> *
2 COMPONENT PRINT HEAD FOR LIQUIDS IN 3D PRINTING, 26 June 2017 (2017-06-26), XP055575441, Retrieved from the Internet <URL:https://www.viscotec.de/en/2-component-print-head-liquids-3d-printing> *
FAES ET AL.: "Extrusion-based additive manufacturing of Zr02 using photoinitiated polymerization", CIRP JOURNAL OF MANUFACTURING SCIENCE AND TECHNOLOGY, vol. 14, 1 June 2016 (2016-06-01), pages 28 - 34, XP029655377, Retrieved from the Internet <URL:http://www.sciencedirect.com/ science /article/pii/S 1755581716300232> DOI: doi:10.1016/j.cirpj.2016.05.002 *
HAZAN ET AL.: "Robotic deposition of 3d nanocomposite and ceramic fiber architechtures via UV curable colloidal inks", JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, vol. 32, no. 6, 11 January 2012 (2012-01-11), pages 1187 - 1198, XP055575446 *
SCHEITHAUER ET AL.: "Thermoplastic 3D Printing An Additive Manufacturing Methodfor Producing Dense Ceramics", INT. J. APPL. CERAM. TECHNOL., vol. 12, no. 1, 31 August 2014 (2014-08-31), pages 26 - 31, XP055575451 *

Cited By (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN109895385A (zh) * 2019-02-25 2019-06-18 泉州市比邻三维科技有限公司 一种3d打印机器人的改进型出料结构及3d打印机器人
CN109895385B (zh) * 2019-02-25 2021-08-27 泉州市比邻三维科技有限公司 一种3d打印机器人的改进型出料结构及3d打印机器人
US11318679B2 (en) * 2019-06-25 2022-05-03 Mighty Buildings, Inc. 3D printer print head system with curing module on rotation platform
JP2022538165A (ja) * 2019-06-25 2022-08-31 マイティ ビルディングス インコーポレーテッド 回転プラットフォーム上にキュアリングモジュールを有する３ｄプリンタ印刷ヘッドシステム
JP7324879B2 (ja) 2019-06-25 2023-08-10 マイティ ビルディングス インコーポレーテッド 回転プラットフォーム上にキュアリングモジュールを有する３ｄプリンタ印刷ヘッドシステム
CN110435136A (zh) * 2019-08-06 2019-11-12 武汉卫亚汽车零部件有限公司 一种汽车座椅连接杆一体成型的工艺
US20220314561A1 (en) * 2021-03-31 2022-10-06 Mighty Buildings, Inc. High intensity light curing for three-dimensional printing
US20230271251A1 (en) * 2022-02-28 2023-08-31 Xerox Corporation Metal drop ejecting three-dimensional (3d) object printer and method of operation for building support structures
CN114749682A (zh) * 2022-04-07 2022-07-15 中国第一汽车股份有限公司 一种隔离材料、金属3d打印零件及其制备方法
CN114749682B (zh) * 2022-04-07 2024-03-15 中国第一汽车股份有限公司 一种隔离材料、金属3d打印零件及其制备方法

Similar Documents

Publication Publication Date Title
WO2019023789A1 (fr) Procédé et appareil d&#39;extrusion de matériau visqueux pour impression tridimensionnelle indirecte de métal
US11420254B2 (en) Method of forming an object using 3D printing
Pelz et al. Additive manufacturing of structural ceramics: a historical perspective
EP3117982B1 (fr) Procede et système d&#39;impression 3d
JP6983792B2 (ja) Ｉｎ−ｓｉｔｕ注入を適用する中実造形方法及び装置
JP6030185B2 (ja) ３ｄプリンティング装置及び方法、これを利用した鉄骨コンクリート構造物の施工方法
Tay et al. Solid freeform fabrication of ceramics
US5738817A (en) Solid freeform fabrication methods
JP6390108B2 (ja) 焼結造形材料、焼結造形方法、焼結造形物および焼結造形装置
US11541593B2 (en) Extruder for a system for the additive manufacture of metal parts using the composite extrusion modeling (CEM) method
JP2020512943A (ja) ゲル支持環境における付加製造
US20160151833A1 (en) Flexible 3D Freeform Techniques
EP3615245A1 (fr) Impression tridimensionnelle (3d) utilisant des effets de traitement mesurés avec rétroaction pour des paramètres de traitement
CN110756805B (zh) 一种激光选区固化金属的3d打印装置及其使用方法
EP3595830A1 (fr) Plaque de base utilisée dans la fabrication additive
EP3717208B1 (fr) Appareil de fabrication additive et procédé associé
US20200156290A1 (en) Centrifugal additive manufacturing apparatus and method
Oropeza et al. A laboratory-scale binder jet additive manufacturing testbed for process exploration and material development
US11292056B2 (en) Cold-spray nozzle
Özden et al. Additive manufacturing of ceramics from thermoplastic feedstocks
Maqsood et al. A review on development and manufacturing of polymer matrix composites using 3D printing technologies
WO2018195306A1 (fr) Support structural pour portique d&#39;imprimante 3d
US20230321723A1 (en) Method for producing a 3d shaped article, and device using a sieve plate
Weerasekera et al. Issues in resolution and build size scaling of additive manufacturing technologies
Zhao et al. 6 Metal Additive Manufacturing

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 18840153

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 18840153

Country of ref document: EP

Kind code of ref document: A1