WO2019002563A2 - Solidification refinement and general phase transformation control through application of in situ gas jet impingement in metal additive manufacturing - Google Patents
Solidification refinement and general phase transformation control through application of in situ gas jet impingement in metal additive manufacturing Download PDFInfo
- Publication number
- WO2019002563A2 WO2019002563A2 PCT/EP2018/067608 EP2018067608W WO2019002563A2 WO 2019002563 A2 WO2019002563 A2 WO 2019002563A2 EP 2018067608 W EP2018067608 W EP 2018067608W WO 2019002563 A2 WO2019002563 A2 WO 2019002563A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- cooling gas
- jet device
- nozzle
- cooling
- conduit
- Prior art date
Abstract
Description
Claims