WO2018232817A1 - Surface rustproof treatment process for metal tool - Google Patents

Surface rustproof treatment process for metal tool Download PDF

Info

Publication number
WO2018232817A1
WO2018232817A1 PCT/CN2017/094168 CN2017094168W WO2018232817A1 WO 2018232817 A1 WO2018232817 A1 WO 2018232817A1 CN 2017094168 W CN2017094168 W CN 2017094168W WO 2018232817 A1 WO2018232817 A1 WO 2018232817A1
Authority
WO
WIPO (PCT)
Prior art keywords
metal tool
parts
drying
water
treatment process
Prior art date
Application number
PCT/CN2017/094168
Other languages
French (fr)
Chinese (zh)
Inventor
季威威
Original Assignee
江苏军威电子科技有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 江苏军威电子科技有限公司 filed Critical 江苏军威电子科技有限公司
Publication of WO2018232817A1 publication Critical patent/WO2018232817A1/en

Abstract

The invention discloses a surface rustproof treatment process for a metal tool. The surface rustproof treatment process comprises the following steps: polishing; washing with water; drying; immersing with a rustproof agent; washing with water; drying; and cooling. The rustproof capability of a metal surface can be remarkably improved by adopting treatment steps of polishing, washing with water and immersing with the rustproof agent, so that the service life of the metal tool is effectively prolonged; a whole process has relatively simple and convenient steps, and is suitable for wide popularization and application.

Description

一种金属工具表面防锈处理工艺Anti-rust treatment process for metal tool surface 技术领域Technical field
本发明涉及一种表面处理的技术领域，具体涉及一种金属工具表面防锈处理工艺。The invention relates to the technical field of surface treatment, in particular to a metal tool surface anti-rust treatment process.
背景技术Background technique
金属表面防锈是工业生产中的重要课题，传统的防锈液、防锈油有优点也有缺点。普通防锈水中含大量的亚硝酸钠，有致癌性，不利于环保和人身体健康，而采用保湿剂延长防锈水的寿命，又带来沾手、沾灰尘的弊病，且不能长期防锈；一般硬膜防锈油虽然适合长期防锈，成膜也透明美观，但是无色透明的树脂种类较少，不稳定也易氧化变色，还需要有机溶剂溶解，带来易燃易爆的危险也不利于环保和健康；一般的防锈油使用矿物油，难降解，而且用于短期防锈时也会带来除油难的问题。因此，研究综合性能更加优异，针对不同场合研究更加适合的防锈产品是新的方向和趋势。Metal surface rust prevention is an important issue in industrial production. Traditional rust preventive liquids and rust preventive oils have advantages and disadvantages. Ordinary rust-proof water contains a large amount of sodium nitrite, which is carcinogenic, which is not conducive to environmental protection and human health. The use of moisturizers prolongs the life of rust-proof water, and brings the disadvantages of hand and dust, and can not prevent rust for a long time; Generally, although the hard film rust preventive oil is suitable for long-term rust prevention, the film formation is transparent and beautiful, but the colorless and transparent resin is less in kind, unstable and oxidatively discolored, and requires organic solvent to dissolve, which brings the risk of flammability and explosion. It is not conducive to environmental protection and health; the general anti-rust oil uses mineral oil, which is difficult to degrade, and it is also difficult to remove oil when used for short-term anti-rust. Therefore, the comprehensive performance of research is more excellent, and it is a new direction and trend to study more suitable anti-rust products for different occasions.
发明内容Summary of the invention
发明目的：本发明的目的是为了弥补现有技术的不足，提供一种简洁方便、防锈效果好的金属工具表面防锈处理工艺。OBJECT OF THE INVENTION The purpose of the present invention is to provide a rust-preventing treatment process for a metal tool surface that is simple, convenient, and rust-proof.
本发明采用的技术方案：一种金属工具表面防锈处理工艺，包括如下步骤：The technical solution adopted by the invention: a metal tool surface anti-rust treatment process, comprising the following steps:
步骤一：使用砂纸对金属工具的表面进行精磨，直至表面完全光滑为止；Step 1: Use a sandpaper to finish the surface of the metal tool until the surface is completely smooth;
步骤二：将金属工具放入到水箱内进行水洗，水的温度为40℃-50℃；Step 2: The metal tool is placed in a water tank for water washing, and the temperature of the water is 40 ° C - 50 ° C;
步骤三：将金属工具放置在烘箱内进行烘干，烘干温度为90℃-100℃，烘干时间为5-8分钟；Step 3: The metal tool is placed in an oven for drying, the drying temperature is 90 ° C - 100 ° C, and the drying time is 5-8 minutes;
步骤四：将金属工具放入到防锈剂内浸泡2-3分钟；Step 4: Put the metal tool into the rust inhibitor for 2-3 minutes;
步骤五：将金属工具放入到水箱内进行水洗，水的温度为30℃-40℃；Step 5: Put the metal tool into the water tank for water washing, the temperature of the water is 30 ° C -40 ° C;
步骤六：将金属工具放置在烘箱内进行烘干，烘干温度为90℃-100℃，烘干时间为5-8分钟；Step 6: The metal tool is placed in an oven for drying, the drying temperature is 90 ° C - 100 ° C, and the drying time is 5-8 minutes;
步骤七：自然冷却即可。Step 7: Allow natural cooling.
所述步骤四中的防锈剂由以下重量份配比组成：氟化氢胺3-5份、表面活性剂1-2份、氧化铬20-30份、柠檬酸钠10-20份、海藻酸钠10-15份、助膜剂1-2份。The rust inhibitor in the step 4 is composed of the following parts by weight: 3-5 parts of hydrogen fluoride amine, 1-2 parts of surfactant, 20-30 parts of chromium oxide, 10-20 parts of sodium citrate, sodium alginate 10-15 parts, 1-2 parts of the film aid.
所述步骤二和步骤五的水洗时间为1～3min。The water washing time of the second step and the fifth step is 1 to 3 minutes.
有益效果：本发明所述的一种金属工具表面防锈处理工艺，通过采用打磨、水洗、浸泡入防锈剂的处理，可以显著提高金属表面的防锈能力，从而有效的延长了金属工具的使用寿命，而且整个工艺步骤比较简洁方便，适宜于广泛推广使用。Advantageous Effects: The surface anti-rust treatment process of the metal tool according to the present invention can significantly improve the anti-rust ability of the metal surface by using the treatment of grinding, washing, and immersion into the rust preventive agent, thereby effectively extending the metal tool. The service life, and the whole process steps are relatively simple and convenient, and suitable for widespread use.
具体实施方式Detailed ways
下面结合具体实施例对本发明作进一步说明：The present invention will be further described below in conjunction with specific embodiments:
本发明所揭示的一种金属工具表面防锈处理工艺，包括如下步骤： The metal tool surface anti-rust treatment process disclosed by the invention comprises the following steps:
步骤一：使用砂纸对金属工具的表面进行精磨，直至表面完全光滑为止；Step 1: Use a sandpaper to finish the surface of the metal tool until the surface is completely smooth;
步骤二：将金属工具放入到水箱内进行水洗，水的温度为40℃-50℃；Step 2: The metal tool is placed in a water tank for water washing, and the temperature of the water is 40 ° C - 50 ° C;
步骤三：将金属工具放置在烘箱内进行烘干，烘干温度为90℃-100℃，烘干时间为5-8分钟；Step 3: The metal tool is placed in an oven for drying, the drying temperature is 90 ° C - 100 ° C, and the drying time is 5-8 minutes;
步骤四：将金属工具放入到防锈剂内浸泡2-3分钟；Step 4: Put the metal tool into the rust inhibitor for 2-3 minutes;
步骤五：将金属工具放入到水箱内进行水洗，水的温度为30℃-40℃；Step 5: Put the metal tool into the water tank for water washing, the temperature of the water is 30 ° C -40 ° C;
步骤六：将金属工具放置在烘箱内进行烘干，烘干温度为90℃-100℃，烘干时间为5-8分钟；Step 6: The metal tool is placed in an oven for drying, the drying temperature is 90 ° C - 100 ° C, and the drying time is 5-8 minutes;
步骤七：自然冷却即可。Step 7: Allow natural cooling.
所述步骤四中的防锈剂由以下重量份配比组成：氟化氢胺3-5份、表面活性剂1-2份、氧化铬20-30份、柠檬酸钠10-20份、海藻酸钠10-15份、助膜剂1-2份。The rust inhibitor in the step 4 is composed of the following parts by weight: 3-5 parts of hydrogen fluoride amine, 1-2 parts of surfactant, 20-30 parts of chromium oxide, 10-20 parts of sodium citrate, sodium alginate 10-15 parts, 1-2 parts of the film aid.
所述步骤二和步骤五的水洗时间为1～3min。The water washing time of the second step and the fifth step is 1 to 3 minutes.
以上所述的实施例只是本发明的一种较佳的方案，并非对本发明作任何形式上的限制，在不超出权利要求所记载的技术方案的前提下，还有其它的变体及改型。 The above-mentioned embodiments are only a preferred embodiment of the present invention, and are not intended to limit the present invention in any way. Other variations and modifications may be made without departing from the technical solutions described in the claims. .

Claims (3)

  1. 一种金属工具表面防锈处理工艺，其特征在于：包括如下步骤：A metal tool surface anti-rust treatment process, characterized in that the method comprises the following steps:
    步骤一：使用砂纸对金属工具的表面进行精磨，直至表面完全光滑为止；Step 1: Use a sandpaper to finish the surface of the metal tool until the surface is completely smooth;
    步骤二：将金属工具放入到水箱内进行水洗，水的温度为40℃-50℃；Step 2: The metal tool is placed in a water tank for water washing, and the temperature of the water is 40 ° C - 50 ° C;
    步骤三：将金属工具放置在烘箱内进行烘干，烘干温度为90℃-100℃，烘干时间为5-8分钟；Step 3: The metal tool is placed in an oven for drying, the drying temperature is 90 ° C - 100 ° C, and the drying time is 5-8 minutes;
    步骤四：将金属工具放入到防锈剂内浸泡2-3分钟；Step 4: Put the metal tool into the rust inhibitor for 2-3 minutes;
    步骤五：将金属工具放入到水箱内进行水洗，水的温度为30℃-40℃；Step 5: Put the metal tool into the water tank for water washing, the temperature of the water is 30 ° C -40 ° C;
    步骤六：将金属工具放置在烘箱内进行烘干，烘干温度为90℃-100℃，烘干时间为5-8分钟；Step 6: The metal tool is placed in an oven for drying, the drying temperature is 90 ° C - 100 ° C, and the drying time is 5-8 minutes;
    步骤七：自然冷却即可。Step 7: Allow natural cooling.
  2. 根据权利要求1所述的一种金属工具表面防锈处理工艺，其特征在于：所述步骤四中的防锈剂由以下重量份配比组成：氟化氢胺3-5份、表面活性剂1-2份、氧化铬20-30份、柠檬酸钠10-20份、海藻酸钠10-15份、助膜剂1-2份。The surface anti-rust treatment process for a metal tool according to claim 1, wherein the rust inhibitor in the fourth step is composed of the following parts by weight: 3-5 parts of hydrogen fluoride amine, surfactant 1- 2 parts, 20-30 parts of chromium oxide, 10-20 parts of sodium citrate, 10-15 parts of sodium alginate, and 1-2 parts of a film aid.
  3. 根据权利要求1所述的一种金属工具表面防锈处理工艺，其特征在于：所述步骤二和步骤五的水洗时间为1～3min。 The metal tool surface anti-rust treatment process according to claim 1, wherein the water washing time of the second step and the fifth step is 1 to 3 minutes.
PCT/CN2017/094168 2017-06-20 2017-07-24 Surface rustproof treatment process for metal tool WO2018232817A1 (en)