WO2018210436A1 - Optimisation de l'introduction d'énergie dans la couche inférieure - Google Patents

Optimisation de l'introduction d'énergie dans la couche inférieure Download PDF

Info

Publication number
WO2018210436A1
WO2018210436A1 PCT/EP2017/062195 EP2017062195W WO2018210436A1 WO 2018210436 A1 WO2018210436 A1 WO 2018210436A1 EP 2017062195 W EP2017062195 W EP 2017062195W WO 2018210436 A1 WO2018210436 A1 WO 2018210436A1
Authority
WO
WIPO (PCT)
Prior art keywords
layer
building material
section
energy input
energy
Prior art date
Application number
PCT/EP2017/062195
Other languages
German (de)
English (en)
Inventor
Ludger HÜMMELER
Original Assignee
Eos Gmbh Electro Optical Systems
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Eos Gmbh Electro Optical Systems filed Critical Eos Gmbh Electro Optical Systems
Priority to PCT/EP2017/062195 priority Critical patent/WO2018210436A1/fr
Publication of WO2018210436A1 publication Critical patent/WO2018210436A1/fr

Abstract

L'invention concerne un procédé assisté par ordinateur pour la mise à disposition de données de commande pour un dispositif de fabrication additive par couches, présentant : une première étape (S1) d'accès à une multitude de jeux de données de couche, qui présentent à chaque fois un modèle de données d'une couche de matériau de construction à solidifier sélectivement pendant la fabrication, caractérisé en ce que, dans une deuxième étape (S2), une partie d'objet est fixée, qui comprend au moins une partie d'une ou de plusieurs sections transversales d'objet, et la multitude de jeux de données de couche est modifiée de manière telle que des valeurs d'au moins un paramètre d'introduction d'énergie sont attribuées à une multitude de sites correspondant à la partie d'objet dans la multitude de jeux de données de couche, de manière telle que les valeurs sont modifiées en plusieurs étapes, de préférence de manière sensiblement monotone, lors d'une modification de la distance par rapport à une section de bord de la partie d'objet et, dans une troisième étape (S3), la multitude de jeux de données de couche modifiée dans la deuxième étape est mise à disposition pour la génération d'un jeu de données de commande pour le dispositif de fabrication additive par couches.
PCT/EP2017/062195 2017-05-19 2017-05-19 Optimisation de l'introduction d'énergie dans la couche inférieure WO2018210436A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
PCT/EP2017/062195 WO2018210436A1 (fr) 2017-05-19 2017-05-19 Optimisation de l'introduction d'énergie dans la couche inférieure

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/EP2017/062195 WO2018210436A1 (fr) 2017-05-19 2017-05-19 Optimisation de l'introduction d'énergie dans la couche inférieure

Publications (1)

Publication Number Publication Date
WO2018210436A1 true WO2018210436A1 (fr) 2018-11-22

Family

ID=58994895

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2017/062195 WO2018210436A1 (fr) 2017-05-19 2017-05-19 Optimisation de l'introduction d'énergie dans la couche inférieure

Country Status (1)

Country Link
WO (1) WO2018210436A1 (fr)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2019068455A1 (fr) * 2017-10-02 2019-04-11 Siemens Aktiengesellschaft Procédé d'irradiation d'une couche de poudre au cours d'une fabrication additive comprenant des paramètres de fabrication définis en continu
CN113510240A (zh) * 2020-04-09 2021-10-19 中国航发商用航空发动机有限责任公司 管件的增材制造方法
EP3900856A1 (fr) 2020-04-24 2021-10-27 Technische Universität Graz Poudres de fabrication additive pour une utilisation dans des processus de fabrication additive donnant lieu à une stabilité améliorée de voie d'acier fondu
WO2023078762A1 (fr) * 2021-11-05 2023-05-11 Trumpf Laser- Und Systemtechnik Gmbh Procédé, dispositif de planification et produit-programme informatique de planification d'une exposition localement sélective d'une zone de travail au rayonnement d'un faisceau d'énergie, et procédé, dispositif de production et produit-programme informatique pour la fabrication additive de composants à partir d'un matériau en poudre
DE102022201696A1 (de) 2022-02-18 2023-08-24 Siemens Energy Global GmbH & Co. KG Additive Herstellung einer dünnen angeschrägten Bauteilstruktur

Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6085122A (en) * 1997-05-30 2000-07-04 Dtm Corporation End-of-vector laser power control in a selective laser sintering system
US20090206065A1 (en) * 2006-06-20 2009-08-20 Jean-Pierre Kruth Procedure and apparatus for in-situ monitoring and feedback control of selective laser powder processing
DE102008031926A1 (de) 2008-07-08 2010-01-14 Bego Medical Gmbh Verfahren zum schichtweisen Herstellen stark geneigter Flächen
DE102011087374A1 (de) * 2011-11-29 2013-05-29 Matthias Fockele Verfahren zur Herstellung eines Formkörpers durch schichtweises Aufbauen aus Werkstoffpulver
WO2015114035A1 (fr) * 2014-01-31 2015-08-06 Eos Gmbh Electro Optical Systems Procédé et dispositif de commande améliorée de l'apport d'énergie dans un procédé de construction additive par génération de couches
US20160059493A1 (en) * 2014-09-02 2016-03-03 Product Innovation and Engineering L.L.C. Additive layering method using improved build description
DE102014226839A1 (de) * 2014-12-22 2016-06-23 Siemens Aktiengesellschaft Verfahren zur generativen Fertigung eines Werkstücks
EP3263317A1 (fr) * 2016-07-01 2018-01-03 EOS GmbH Electro Optical Systems Dispositif et procédé de commande de rayonnement dans un dispositif de fabrication d'un objet tridimensionnel

Patent Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6085122A (en) * 1997-05-30 2000-07-04 Dtm Corporation End-of-vector laser power control in a selective laser sintering system
US20090206065A1 (en) * 2006-06-20 2009-08-20 Jean-Pierre Kruth Procedure and apparatus for in-situ monitoring and feedback control of selective laser powder processing
DE102008031926A1 (de) 2008-07-08 2010-01-14 Bego Medical Gmbh Verfahren zum schichtweisen Herstellen stark geneigter Flächen
DE102011087374A1 (de) * 2011-11-29 2013-05-29 Matthias Fockele Verfahren zur Herstellung eines Formkörpers durch schichtweises Aufbauen aus Werkstoffpulver
WO2015114035A1 (fr) * 2014-01-31 2015-08-06 Eos Gmbh Electro Optical Systems Procédé et dispositif de commande améliorée de l'apport d'énergie dans un procédé de construction additive par génération de couches
US20160059493A1 (en) * 2014-09-02 2016-03-03 Product Innovation and Engineering L.L.C. Additive layering method using improved build description
DE102014226839A1 (de) * 2014-12-22 2016-06-23 Siemens Aktiengesellschaft Verfahren zur generativen Fertigung eines Werkstücks
EP3263317A1 (fr) * 2016-07-01 2018-01-03 EOS GmbH Electro Optical Systems Dispositif et procédé de commande de rayonnement dans un dispositif de fabrication d'un objet tridimensionnel

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2019068455A1 (fr) * 2017-10-02 2019-04-11 Siemens Aktiengesellschaft Procédé d'irradiation d'une couche de poudre au cours d'une fabrication additive comprenant des paramètres de fabrication définis en continu
US11846928B2 (en) 2017-10-02 2023-12-19 Siemens Energy Global GmbH & Co. KG Method for irradiating a powder layer in additive production using continuously defined production parameters
CN113510240A (zh) * 2020-04-09 2021-10-19 中国航发商用航空发动机有限责任公司 管件的增材制造方法
EP3900856A1 (fr) 2020-04-24 2021-10-27 Technische Universität Graz Poudres de fabrication additive pour une utilisation dans des processus de fabrication additive donnant lieu à une stabilité améliorée de voie d'acier fondu
WO2021214106A1 (fr) 2020-04-24 2021-10-28 Technische Universität Graz Poudres de fabrication additive destinées à être utilisées dans des processus de fabrication additive résultant en une stabilité améliorée de canal de coulée d'acier
WO2023078762A1 (fr) * 2021-11-05 2023-05-11 Trumpf Laser- Und Systemtechnik Gmbh Procédé, dispositif de planification et produit-programme informatique de planification d'une exposition localement sélective d'une zone de travail au rayonnement d'un faisceau d'énergie, et procédé, dispositif de production et produit-programme informatique pour la fabrication additive de composants à partir d'un matériau en poudre
DE102022201696A1 (de) 2022-02-18 2023-08-24 Siemens Energy Global GmbH & Co. KG Additive Herstellung einer dünnen angeschrägten Bauteilstruktur

Similar Documents

Publication Publication Date Title
EP3648955B1 (fr) Procédé optimisé de segmentation
WO2016166337A1 (fr) Procédé et unité de génération d'instructions de commande servant à générer automatiquement des instructions de commande d'un dispositif de construction stratifiée génératif
EP3585592B1 (fr) Homogénéisation de l'apport énergétique
DE60115136T2 (de) Herstellung von dreidimensionalen Gegenständen durch kontrollierte Photohärtung
WO2018210436A1 (fr) Optimisation de l'introduction d'énergie dans la couche inférieure
EP3579996A1 (fr) Stratégie d'exposition dans des systèmes de fabrication additive (am) à faisceaux multiples
EP3579998B1 (fr) Augmentation de la qualité de surface
EP3362263B1 (fr) Procédé et dispositif de détermination des besoins en matière de construction
DE102018202506A1 (de) Additives Herstellverfahren mit kontrollierter Verfestigung und zugehörige Vorrichtung
EP3375607A1 (fr) Procédé de détermination des valeurs de paramètre de processus d'impression, procédé de commande d'une imprimante 3d, mémoire lisible par ordinateur et imprimante 3d
WO2018172079A1 (fr) Optimisation de chevauchement
WO2017153187A1 (fr) Procédé de construction par couches génératif présentant une résolution améliorée des détails et dispositif pour sa réalisation
WO2018206581A1 (fr) Entrée d'énergie spécifique à la position
WO2018019567A1 (fr) Procédé et dispositif de détermination de la qualité d'un composant
EP3566856A1 (fr) Procédé et dispositif d'amélioration de l'homogénéité de composant d'objets fabriqués selon un procédé de fabrication additive
DE102018205688A1 (de) Verfahren und Vorrichtung zur Verbesserung der Bauteilqualität von durch ein additives Herstellverfahren hergestellten Objekten
EP3416813B1 (fr) Outil d'usinage et son procédé de fabrication au moyen d'un processus de fabrication par couches génératif
WO2019201498A1 (fr) Post-exposition sélective
EP4412784A1 (fr) Procédé pour déterminer automatiquement des motifs d'exposition
WO2023213690A1 (fr) Procédé et dispositif de génération de données de commande d'irradiation pour un dispositif de fabrication additive d'un composant
WO2023208470A1 (fr) Attribution dynamique d'objets à fabriquer à des dispositifs de fabrication additive
WO2023078762A1 (fr) Procédé, dispositif de planification et produit-programme informatique de planification d'une exposition localement sélective d'une zone de travail au rayonnement d'un faisceau d'énergie, et procédé, dispositif de production et produit-programme informatique pour la fabrication additive de composants à partir d'un matériau en poudre
DE102018131540A1 (de) Erstellen von Steuerungsdaten für eine Schichtaufbauvorrichtung
DE102015225022A1 (de) Verfahren und Vorrichtung zur Prüfung eines Eingangsdatensatzes einer generativen Schichtbauvorrichtung

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 17727512

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 17727512

Country of ref document: EP

Kind code of ref document: A1