WO2018062796A1 - 피부 또는 모발 코팅을 위한 피막 형성용 조성물 - Google Patents

피부 또는 모발 코팅을 위한 피막 형성용 조성물 Download PDF

Info

Publication number
WO2018062796A1
WO2018062796A1 PCT/KR2017/010577 KR2017010577W WO2018062796A1 WO 2018062796 A1 WO2018062796 A1 WO 2018062796A1 KR 2017010577 W KR2017010577 W KR 2017010577W WO 2018062796 A1 WO2018062796 A1 WO 2018062796A1
Authority
WO
WIPO (PCT)
Prior art keywords
film
skin
composition
forming
hair
Prior art date
Application number
PCT/KR2017/010577
Other languages
English (en)
French (fr)
Inventor
황윤균
빈성아
안다운
최장원
김종협
박성일
Original Assignee
(주)아모레퍼시픽
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from KR1020170123468A external-priority patent/KR102034537B1/ko
Application filed by (주)아모레퍼시픽 filed Critical (주)아모레퍼시픽
Priority to US16/337,248 priority Critical patent/US20190254947A1/en
Priority to CN201780071752.9A priority patent/CN109963550A/zh
Priority to JP2019537730A priority patent/JP2019529561A/ja
Publication of WO2018062796A1 publication Critical patent/WO2018062796A1/ko

Abstract

본 발명은 피부 또는 모발 코팅을 위한 피막 형성용 조성물에 관한 것이다. 본 발명에 따른 피부 또는 모발 코팅을 위한 피막 형성용 조성물은 피부 또는 모발에 도포시 가벼운 사용감을 나타내고 지속성이 우수하여 피부 또는 모발 자체를 보호할 수 있으며 또는 피부 등에 도포된 화장료를 보호할 수 있다. 또한 도포시에 피막이 형성되도록 실란과 수분을 분리하여 제조함으로써 사용이 편리하다.

Description

피부 또는 모발 코팅을 위한 피막 형성용 조성물
본 출원은 2016년 9월 27일자 한국 특허출원 제10-2016-0123968호 및 2017년 9월 25일자 한국 특허출원 제10-2017-0123468호에 기초한 우선권의 이익을 주장하며, 해당 한국 특허 출원의 문헌에 개시된 모든 내용을 본 명세서의 일부로서 포함한다.
본 발명은 피부 또는 모발 코팅을 위한 피막 형성용 조성물에 관한 것이다.
사람의 피부에 도포된 화장료 등은 도포되고 시간이 지남에 따라 점점 피부로부터 이탈되어 사라져 화장이 옅어지는 현상이 발생한다. 또한 단백질로 이루어진 피부 자체도 외부 요인들에 의해 손상될 수 있다.
또한, 사람의 모발은 동물의 털, 뿔, 발톱, 피부 및 깃털 등과 같이, 케라틴으로 알려진 단백질성 나선형을 포함한다. 이러한 구조의 단백질들은 외력, 햇빛, 거친 화학 약품 및 공기 중의 오염 물질들에 계속 노출됨에 따라 분해되어 모발이 손상될 수 있다.
손상된 피부 또는 모발 등은 건강한 상태의 물성과 달라지게 되며, 이를 보호하기 위해 피부 또는 모발에 화장품을 사용해 보호막(피막)을 형성시키는 경우가 있다. 하지만 피막의 유지력, 유지시간은 필름을 형성하는 물질의 분자량이 일정 수준 이상이어야 형성이 가능하며, 분자량이 클수록 피막의 두께가 두꺼워져 답답하고 사용감이 무거워진다. 하지만 저분자 물질을 이용하여 피막을 형성하면 휘발성이 강하거나 피막 형성 자체가 어려울 수 있다.
따라서 저분자 물질을 이용해 피막을 만드는 기술의 연구가 절실한 실정이다.
[선행기술문헌]
[특허문헌]
(특허문헌 1) 한국공개특허 제2006-0035343호 "폴리에틸렌 글리콜 유도체를 유효성분으로 함유하는 모발코팅용 조성물"
(특허문헌 2) 한국공개특허 제2016-0108126호 "식물성 모발보호제 및 그 제조방법과 코팅방법"
기존의 피부 또는 모발 보호를 위한 피막의 유지력 및 유지시간은 피막을 형성하는 물질의 분자량이 일정 수준 이상이어야 가능하지만, 분자량이 클수록 피막의 두께가 두꺼워져 답답하고 무거운 사용감으로 나타난다. 다만 저분자량의 물질은 피막을 형성하기 어렵고 지속성이 떨어지는 단점이 있다.
따라서 본 발명의 목적은 사용감이 가볍고 지속성이 우수한 저분자 물질을 이용한 피막 형성용 조성물을 제공하는 데 있다.
상기 목적을 달성하기 위하여 본 발명은, 실란 및 수분을 포함하되, 상기 실란이 수분산된 피부 또는 모발 코팅을 위한 피막 형성용 조성물을 제공한다.
이때, 상기 피막 형성용 조성물은 상기 실란이 담지된 마이셀이 수분산된 형태로서, 상기 실란과 수분을 분리하여 포함하며, 도포 시에 상기 실란과 상기 수분이 반응하여 피막을 형성할 수 있다.
이때, 상기 실란은 아미노프로필트리에톡시실란, 헥실트리메톡시실란, 퍼플루오로옥틸트리에톡시실란, 트리에톡시카프릴릴실란, 레티녹시트리메틸실란, 스테아릴트리에톡시실란 및 스테아록시트리메틸실란으로 이루어진 군으로부터 선택된 하나 이상의 실란 화합물일 수 있다.
이때, 상기 실란은 상기 피막 형성 조성물 전체 중량을 기준으로 0.1 내지 5 중량% 포함될 수 있다.
이때, 상기 피막 형성용 조성물은 실리콘계 오일을 추가로 포함할 수 있다.
이때, 상기 실리콘계 오일은 상기 피막 형성 조성물 전체 중량을 기준으로 1 내지 40 중량% 포함될 수 있다.
이때, 상기 실리콘계 오일의 중량평균분자량은 3,000~50,000일 수 있다.
이때, 상기 실리콘계 오일은 디메치콘올, 디메치콘, 사이클로메치콘, 사이클로페닐메치콘, 카프릴디메치콘, 카프릴릴트리메치콘, 카프릴릴메치콘, 세테아릴메치콘, 헥사데실메치콘, 헥실메치콘, 라우릴메치콘, 미리스칠메치콘, 페닐메치콘, 스테아릴메치콘, 스테아릴디메치콘, 트리플루오로프로필메치콘, 세틸디메치콘, 폴리페닐메칠실록산, 디메틸폴리실록산, 메틸페닐폴리실록산, 사이클로펜타실록산, 데카메틸사이클로펜타실록산, 사이클로헥사실록산, 사이클로헵타실록산, 사이클로테트라실록산, 사이클로트리실록산, 메틸크트리메치콘, 디페닐실록시페닐트리메치콘, 카프릴릴메치콘 및 페닐트리메치콘으로 이루어진 군으로부터 선택된 하나 이상일 수 있다.
이때, 상기 피막 형성용 조성물은 계면활성제를 추가로 포함하고, 상기 실란 화합물을 코어(core)에 담지하는 마이셀이 수분산된 에멀젼(emulsion)일 수 있다.
이때, 상기 계면활성제는 스테아트리모늄클로라이드, 세트리모늄클로라이드, 베헤닐트리메틸암모늄클로라이드, 세틸트리메틸암모늄클로라이드, 스테아릴트리메틸암모늄클로라이드, 디스테아릴디메틸암모늄클로라이드, 디세틸디메틸암모늄클로라이드, 코카아미도프로필디메틸아민, 스테아르아미도프로필디메틸아민, 베헤닐아미도프로필디메틸아민, 올레아미도프로필디메틸아민 및 이소스테아르아미도프로필디메틸아민으로 이루어진 군으로부터 선택된 하나 이상인 양이온 계면활성제; 또는 트리데세스-10(Trideceth-10), 트리데세스-12(Trideceth-12), 라우릴 글루코시드, 데실 글루코시드, PEG-20 글리세릴 트리이소스테아레이트, PEG-15 글리세릴 이소스테아레이트, 폴리글리세릴-3 디이소스테아레이트 및 폴리글리세릴-10 디올리에이트로 이루어진 군으로부터 선택된 하나 이상인 비이온 계면활성제;일 수 있다.
이때, 상기 피막 형성용 조성물은 피부 또는 모발에 바를 경우 상기 마이셀이 깨져 상기 실란과 상기 수분이 반응하여 피막을 형성할 수 있다.
본 발명에 따른 피부 또는 모발 코팅을 위한 피막 형성용 조성물은 피부 또는 모발에 도포시 가벼운 사용감을 나타내고 지속성이 우수하여 피부 또는 모발 자체를 보호할 수 있으며 또는 피부 등에 도포된 화장료를 보호할 수 있다.
또한, 상기 피막 형성용 조성물은 실란을 포함하는 마이셀이 수분산된 형태를 가지므로, 피부 또는 모발에 도포 전에는 실란과 물이 분리되어 있다가, 피부 또는 모발에 도포 시에 마이셀이 깨지면서 실란과 물의 반응에 의해 피막이 형성되므로, 사용이 편리하고 코팅 효과가 우수하다.
도 1은 실험예 1의 접촉각 측정 과정을 도시한 것이다.
도 2는 실험예 1의 접촉각 측정을 통한 모발 표면의 발수력을 측정한 결과를 나타낸 것이다.
도 3은 실험예 2의 피막 형성용 조성물의 지속력 평가 결과를 나타낸 것이다.
이하, 본 발명을 보다 구체적으로 설명하기 위하여 본 발명에 따른 바람직한 실시예를 설명한다. 그러나 본 발명은 여기서 설명되는 실시예에 한정되지 않고 다른 형태로 구체화될 수도 있다.
본 발명은 실란 및 수분을 포함하는 것을 특징으로 하는 피부 또는 모발 코팅을 위한 피막 형성용 조성물에 관한 것으로, 피부나 모발에 도포시 얇은 두께의 피막을 형성하여 사용감이 무겁지 않도록 하기 위하여 저분자의 원료를 사용하면서도 피부나 모발에 대한 코팅효과가 우수한 피막 형성용 조성물에 관한 것이다.
또한, 상기 피막 형성용 조성물은 상기 실란 및 상기 수분을 분리하여 포함하며, 피부 또는 모발에 도포 시에 상기 실란과 상기 수분이 반응하여 피막을 형성할 수 있다.
본 발명에서 사용된 용어 "피부 또는 모발 코팅을 위한 피막 형성용 조성물"은 피부 또는 모발 각각에 코팅을 위한 피막 형성용 조성물을 의미하는 것일 수도 있고, 피부 및 모발 모두에 코팅을 위한 피막 형성용 조성물을 의미하는 것일 수도 있다.
이하 본 발명의 제조에 사용되는 각 핵심 성분에 대하여 보다 상세히 설명한다.
실란
실란은 물과 반응하면 실란 내의 알콕시기가 가수분해되어 실란올기를 형성한다. 실란올기는 다른 실란올기와 축합반응을 하여 실록산 고분자쇄를 형성함으로써 피막을 형성할 수 있다. 상기 실란과 물에 의해 형성된 피막이 피부 또는 모발에 형성되면 저분자량의 보호용 피막으로 작용하여 피부와 모발을 보호할 수 있다. 또한 상기 피부에 화장품을 바르거나 상기 모발에 염료 등을 바른 후, 그 위에 상기 피막을 형성하면 화장 또는 염색 지속성 등을 향상시킬 수 있다. 또한 실란을 이용하여 피막을 형성하면 저분자 피막을 형성할 수 있어서, 가벼운 사용감을 제공할 수 있다.
상기 실란은 단분자 물질로서, 아미노프로필트리에톡시실란, 헥실트리메톡시실란, 퍼플루오로옥틸트리에톡시실란, 트리에톡시카프릴릴실란, 레티녹시트리메틸실란, 스테아릴트리에톡시실란 및 스테아록시트리메틸실란으로 이루어진 군으로부터 선택된 하나 이상일 수 있다.
본 발명에 있어서, 상기 실란은 상기 피막 형성용 조성물 전체 중량을 기준으로, 0.1 내지 5 중량% 포함될 수 있고, 상기 실란의 함량이 상기 범위 미만이면 피막을 형성하기가 어려워 피부나 모발에 대한 코팅 효과가 저하되고, 상기 범위 초과이면 사용감이 무거워 선호도가 저하될 수 있다.
실리콘계 오일
본 발명에 있어서, 상기 피막 형성용 조성물은 실리콘계 오일을 추가로 포함할 수 있다. 실리콘계 오일은 본 피막 형성용 조성물에 첨가되어 부드러움을 부여하며 피부 또는 모발을 보호하는 역할을 한다.
상기 실리콘계 오일의 중량평균분자량은 3,000 ~ 50,000일 수 있으며, 상기 실리콘계 오일의 중량평균분자량이 3,000 미만이면 피부나 모발에 피막 형성시 피막의 강도가 저하되고, 조성물의 부드러움을 향상시키는 효과가 미미하며, 50,000 초과이면 역시 조성물의 부드러움을 향상시키는 효과가 미미하고 피부와 모발 보호 기능이 저하될 수 있다.
이때, 상기 실리콘계 오일은 디메치콘올, 디메치콘, 사이클로메치콘, 사이클로페닐메치콘, 카프릴디메치콘, 카프릴릴트리메치콘, 카프릴릴메치콘, 세테아릴메치콘, 헥사데실메치콘, 헥실메치콘, 라우릴메치콘, 미리스칠메치콘, 페닐메치콘, 스테아릴메치콘, 스테아릴디메치콘, 트리플루오로프로필메치콘, 세틸디메치콘, 폴리페닐메칠실록산, 디메틸폴리실록산, 메틸페닐폴리실록산, 사이클로펜타실록산, 데카메틸사이클로펜타실록산, 사이클로헥사실록산, 사이클로헵타실록산, 사이클로테트라실록산, 사이클로트리실록산, 메틸크트리메치콘, 디페닐실록시페닐트리메치콘, 카프릴릴메치콘 및 페닐트리메치콘으로 이루어진 군으로부터 선택된 하나 이상일 수 있으며, 바람직하게는 디메치콘올일 수 있다.
또한, 상기 실리콘계 오일은 상기 피막 형성용 조성물 전체 중량을 기준으로, 1 내지 40 중량% 포함될 수 있고, 상기 실리콘계 오일의 함량이 상기 범위 미만이면 피부 도포감이 저하되고, 조성물의 부드러움을 향상시키는 효과가 미미하며, 상기 범위 초과이면 피부와 모발 보호 기능이 저하될 수 있다.
계면활성제
상기 피막 형성용 조성물은 계면활성제를 추가로 포함하고, 상기 실란 화합물을 코어에 담지하는 마이셀이 수분산된 에멀젼일 수 있다.
계면활성제는 보통 수용액 내에서 분자 형태로 존재하지만, 용액 내 계면활성제의 농도가 증가함에 따라 표면 장력의상기 피막 형성용 조성물은 계면활성제를 추가로 포함하고, 상기 실란 화합물을 코어에 담지하는 마이셀이 수분산된 에멀젼일 수 있다.
계면활성제는 보통 수용액 내에서 분자 형태로 존재하지만, 용액 내 계면활성제의 농도가 증가함에 따라 표면 장력의 저하가 이루어지고, 더이상 표면장력의 저하가 일어나기 어려워지면 계면활성제의 소수성기 상호간의 회합이 발생하여 소수성기는 내부로, 그리고 친수성기는 물과 닿을 수 있도록 외부로 향하는 구조를 가지는 응집체인 마이셀이 형성된다. 이와 같이, 마이셀을 형성하게 되는 계면활성제 용액의 농도를 임계 마이셀 농도(critical micelle concentration, CMC)라고 한다. 이러한 임계마이셀농도를 전후로 하여 계면활성제 용액의 계면장력, 표면장력, 전기전도도, 세정 능력, 점도 등의 물리적 성질이 급격히 변화한다. 예를 들면, 계면활성제 용액 내에서 용해되지 않는 제3의 물질을 임계 마이셀 농도 이상에서는 마이셀 내부에 용해시킬 수 있는 성질을 갖게 되며 이를 용해화(solubilization)라고 한다.
상기 마이셀의 코어에 실란 또는 실란과 실리콘 오일의 혼합물을 담지하고 수중에 분산되는 에멀젼 상태의 피막 형성용 조성물을 제조하면 상기 실란과 수분이 반응하지 않은 상태로 존재할 수 있다.
또한 상기 계면활성제는 스테아트리모늄클로라이드, 세트리모늄클로라이드, 베헤닐트리메틸암모늄클로라이드, 세틸트리메틸암모늄클로라이드, 스테아릴트리메틸암모늄클로라이드, 디스테아릴디메틸암모늄클로라이드, 디세틸디메틸암모늄클로라이드, 코카아미도프로필디메틸아민, 스테아르아미도프로필디메틸아민, 베헤닐아미도프로필디메틸아민, 올레아미도프로필디메틸아민 및 이소스테아르아미도프로필디메틸아민으로 이루어진 군으로부터 선택된 하나 이상인 양이온 계면활성제; 또는 트리데세스-10(Trideceth-10), 트리데세스-12(Trideceth-12), 라우릴 글루코시드, 데실 글루코시드, PEG(Poly Ethylene Glycol)-20 글리세릴 트리이소스테아레이트, PEG-15 글리세릴 이소스테아레이트, 폴리글리세릴-3 디이소스테아레이트 및 폴리글리세릴-10 디올리에이트로 이루어진 군으로부터 선택된 하나 이상인 비이온 계면활성제;일 수 있다.
본 발명의 피막 형성용 조성물 계면활성제의 농도는 임계 마이셀 농도보다 높을 수 있으며, 상기 마이셀의 직경은 100~300nm일 수 있다. 마이셀의 직경이 상기 범위 이하이면 피막의 두께가 얇아 지속력 향상이 어려울 수 있으며, 상기 범위 이상이면 피막의 두께가 두꺼워져 얇은 피막을 통해 가벼운 사용감으로 지속력을 높이고자 하는 목적에서 벗어날 수 있다.
상기 피막 형성용 조성물은 피부 또는 모발에 바를 경우 상기 마이셀이 깨져 상기 실란과 상기 수분이 반응하여 피막을 형성할 수 있다. 구체적으로, 상기 피막 형성용 조성물을 피부나 모발에 도포시 수분 증발과 재유화 과정에서 마이셀이 깨지면서 마이셀 내에 담지된 실란과 마이셀 외부의 수분이 만나면서 반응하여 피막을 형성할 수 있다. 따라서 사용, 즉 바르기 전에는 실란과 수분이 분리되어 있어서 보관이 용이하고 사용이 편리하다.
또한 상기 피막 형성 조성물을 피부 또는 모발에 도포한 후에는 효과적인 피막 형성을 위하여 추가로 열처리를 할 수 있다. 피부의 경우에는 화상을 입지 않는 범위의 온도에서 피부에 온풍을 가하거나 스팀 타월 등을 피부에 접하여 피막 형성을 도울 수 있으며, 모발의 경우에는 열 스타일러(고데기, straightener) 또는 살롱에서 사용하는 열처리 기계 등을 이용하여 모발에 열을 가할 수 있으며 80~150℃의 범위의 열을 가하는 것이 바람직하다.
이하, 본 발명의 효과에 대한 이해를 돕기 위하여 실시예, 비교예 및 실험예를 기재한다. 다만, 하기 기재는 본 발명의 내용 및 효과에 관한 일 예에 해당할 뿐, 본 발명의 권리 범위 및 효과가 이에 한정되는 것은 아니다.
< 실시예 1> 실란 및 실리콘을 담지하는 마이셀이 수분산된 에멀젼을 포함하는 피막 형성용 조성물의 제조
비이온성 계면활성제 트리데세스-12(Trideceth-12)를 5g, 실리콘계 오일로서 중량평균분자량이 5000인 디메치콘올 10g 및 실란으로서 트리에톡시카프릴릴실란 2g을 50℃에서 균일하게 혼합한 후, 탈이온수 10g를 가하고 상전이 시점(W/O상에서 O/W상으로 상전이 되는 시점)을 관측하며 고속(3600 rpm)으로 10분간 교반 하였다. 이후 상온으로 온도를 낮추고 탈이온수 73g를 투입하고, 고속으로 1시간 동안 교반하여, 실란 및 실리콘을 담지하는 마이셀이 수분산된 에멀젼 형태의 피막 형성용 조성물을 제조하였다.
< 비교예 1> 실리콘을 담지하는 마이셀이 수분산된 에멀젼을 포함하는 피막 형성용 조성물의 제조
상기 실시예 1과 동일한 방법으로 실시하되, 다만, 상기 실란으로서 트리에톡시카프릴릴실란을 사용하지 않고 피막 형성용 조성물을 제조하였다.
<실험예 1> 모발의 접촉각(contact angle) 측정을 통한 발수력 측정
상기 실시예 1의 피막 형성용 조성물을 도포한 모발 및 상기 비교예 1의 피막 형성용 조성물을 도포한 모발을 총 3회 샴푸로 세정하여, 세정횟수(0회, 1회, 2회 및 3회)에 따른 모발의 접촉각을 측정기기(Process Tensiometer K100)를 이용하여 측정하였으며, 접촉각 측정 과정을 도 1에 도시하였다. 도 1을 참고하면 상기 두 가지 모발을 각각 파이버 홀더(fiber holder)에 수직으로 설치한 후, 상기 모발이 물에 잠기도록 파이버 홀더를 일정한 속도로 아래로 이동시키며, 모발에 접촉되는 액체의 무게변화를 감지하여 모발의 접촉각을 구하였다. 상기 모발의 접촉각 측정을 통해 모발 표면의 발수력을 측정한 결과를 도 2에 나타내었다.
도 2에 나타난 바와 같이, 3회의 세정 후에도 실시예 1의 피막 형성용 조성물을 도포한 모발의 접촉각은 70.96°를 나타내었는 바, 51.25°의 접촉각을 나타낸 비교예 1의 피막 형성용 조성물을 도포한 모발에 비하여 모발 표면의 발수력 및 코팅 효과가 우수한 것을 확인할 수 있다.
<실험예 2> 피막 형성용 조성물의 흡착량 및 지속력 평가(wool swatch test)
5cm X 5cm 크기의 양모천(wool swatch)에 삼푸 1g을 올려놓고 37.5℃ 수돗물을 10g 가하고 1분간 고르게 도포하면서 작은 힘으로 가볍게 러빙(rubbing)하였다. 러빙 후 상기 양모천을 37.5℃의 수돗물에 100g/s의 유속으로 30초 이상 충분히 헹구었다. 상기 과정을 3회 반복하였다. 이후, 상기 양모천을 0.5% 형광 다이(nile red (Mw: 318)) 용액을 포함하여 제조한 5%의 실시예 1의 피막 형성용 조성물 또는 0.5% 형광 다이(nile red (Mw: 318)) 용액을 포함하여 제조한 5%의 비교예 1의 피막 형성용 조성물에 각각 3분간 담지시켰다. 3분 후 양모천을 건져낸 후 90℃로 5분간 열처리한 뒤, 37.5℃의 수돗물에 100g/s 유속으로 30초 이상 충분히 헹군 후 자연건조시켰다. 그 다음 색차계(CHROMA METER CR-100, MINOLTA CAMERA CO., LTD. 일본)로 착색된 색상의 정도를 측정하였으며, 이로부터 세정 횟수에 따라서 양모천에 남아 있는 조성물의 잔여량을 평가하였다. 측정 결과는 도 3에 나타내었다.
도 3에 나타난 바와 같이, 본 발명에 따른 실란이 포함된 조성물(실시예 1)을 적용한 경우에는 물세정 및 샴푸 3회 세정에도 흡착량의 변화가 크지 않고 지속력이 우수함을 알 수 있다. 그러나 실란이 포함되지 않은 조성물(비교예 1)을 적용한 경우에는 대부분의 성분이 제거되고 조성물의 흡착량이 거의 없음을 알 수 있다. 이로부터 본 발명에 따른 조성물은 실란 피막이 형성됨으로써 기재에 용이하게 흡착하면서 흡착된 성분이 보다 오래 유지되어 모발 부드러움의 지속력을 증대시킬 수 있음을 알 수 있다.
<실험예 3> 관능 평가
상기 실시예 1 및 비교예 1에 대해 20-30세 여성 20명을 시험대상으로 하여 윤기, 지속력 및 가벼운 사용감 평가를 실시하였다. 5점 척도법으로 관능 평가를 실시하여 결과를 평균하여 하기 표 1에 나타내었다.
[평가기준]
5: 매우 우수, 4: 우수, 3: 보통, 2: 나쁨, 1: 매우 나쁨
구분 윤기 지속력 가벼운 사용감
실시예 1 4.5 4.7 4.1
비교예 1 3.0 2.2 4.0
상기 표 1에 나타난 바와 같이, 실시예 1의 피막 형성용 조성물이 비교예 1의 피막 형성용 조성물에 비하여 윤기 및 지속력이 우수한 것으로 나타났다.

Claims (10)

  1. 실란 및 수분을 포함하되 상기 실란이 수분산된, 피부 또는 모발 코팅을 위한 피막 형성용 조성물.
  2. 제1항에 있어서,
    상기 피막 형성용 조성물은 상기 실란이 담지된 마이셀이 수분산된 형태이며,
    도포 시에 상기 실란과 상기 수분이 반응하여 피막을 형성하는, 피부 또는 모발 코팅을 위한 피막 형성용 조성물.
  3. 제1항에 있어서,
    상기 실란은 아미노프로필트리에톡시실란, 헥실트리메톡시실란, 퍼플루오로옥틸트리에톡시실란, 트리에톡시카프릴릴실란, 레티녹시트리메틸실란, 스테아릴트리에톡시실란 및 스테아록시트리메틸실란으로 이루어진 군으로부터 선택된 하나 이상인, 피부 또는 모발 코팅을 위한 피막 형성용 조성물.
  4. 제1항에 있어서,
    상기 실란은 상기 피막 형성 조성물 전체 중량을 기준으로 0.1 내지 5 중량% 포함되는, 피부 또는 모발 코팅을 위한 피막 형성용 조성물.
  5. 제1항에 있어서,
    상기 피막 형성용 조성물은 실리콘계 오일을 추가로 포함하는 것을 특징으로 하는, 피부 또는 모발 코팅을 위한 피막 형성용 조성물.
  6. 제5항에 있어서,
    상기 실리콘계 오일은 상기 피막 형성 조성물 전체 중량을 기준으로 1 내지 40 중량% 포함되는, 피부 또는 모발 코팅을 위한 피막 형성용 조성물.
  7. 제5항에 있어서,
    상기 실리콘계 오일의 중량평균분자량은 3,000 ~ 50,000인 것을 특징으로 하는, 피부 또는 모발 코팅을 위한 피막 형성용 조성물.
  8. 제5항에 있어서,
    상기 실리콘계 오일은 디메치콘올, 디메치콘, 사이클로메치콘, 사이클로페닐메치콘, 카프릴디메치콘, 카프릴릴트리메치콘, 카프릴릴메치콘, 세테아릴메치콘, 헥사데실메치콘, 헥실메치콘, 라우릴메치콘, 미리스칠메치콘, 페닐메치콘, 스테아릴메치콘, 스테아릴디메치콘, 트리플루오로프로필메치콘, 세틸디메치콘, 폴리페닐메칠실록산, 디메틸폴리실록산, 메틸페닐폴리실록산, 사이클로펜타실록산, 데카메틸사이클로펜타실록산, 사이클로헥사실록산, 사이클로헵타실록산, 사이클로테트라실록산, 사이클로트리실록산, 메틸크트리메치콘, 디페닐실록시페닐트리메치콘, 카프릴릴메치콘 및 페닐트리메치콘으로 이루어진 군으로부터 선택된 하나 이상인 것을 특징으로 하는, 피부 또는 모발 코팅을 위한 피막 형성용 조성물.
  9. 제1항에 있어서,
    상기 피막 형성용 조성물은 계면활성제를 추가로 포함하고, 상기 실란이 담지된 마이셀이 수분산된 에멀젼인 것을 특징으로 하는, 피부 또는 모발 코팅을 위한 피막 형성용 조성물.
  10. 제9항에 있어서,
    상기 계면활성제는 스테아트리모늄클로라이드, 세트리모늄클로라이드, 베헤닐트리메틸암모늄클로라이드, 세틸트리메틸암모늄클로라이드, 스테아릴트리메틸암모늄클로라이드, 디스테아릴디메틸암모늄클로라이드, 디세틸디메틸암모늄클로라이드, 코카아미도프로필디메틸아민, 스테아르아미도프로필디메틸아민, 베헤닐아미도프로필디메틸아민, 올레아미도프로필디메틸아민 및 이소스테아르아미도프로필디메틸아민으로 이루어진 군으로부터 선택된 하나 이상인 양이온 계면활성제; 또는 트리데세스-10, 트리데세스-12, 라우릴 글루코시드, 데실 글루코시드, PEG-20 글리세릴 트리이소스테아레이트, PEG-15 글리세릴 이소스테아레이트, 폴리글리세릴-3 디이소스테아레이트 및 폴리글리세릴-10 디올리에이트로 이루어진 군으로부터 선택된 하나 이상인 비이온 계면활성제;인 것을 특징으로 하는, 피부 또는 모발 코팅을 위한 피막 형성용 조성물.
PCT/KR2017/010577 2016-09-27 2017-09-26 피부 또는 모발 코팅을 위한 피막 형성용 조성물 WO2018062796A1 (ko)