WO2017164969A1 - Method and system of joining at least two tubular members - Google Patents
Method and system of joining at least two tubular members Download PDFInfo
- Publication number
- WO2017164969A1 WO2017164969A1 PCT/US2017/014159 US2017014159W WO2017164969A1 WO 2017164969 A1 WO2017164969 A1 WO 2017164969A1 US 2017014159 W US2017014159 W US 2017014159W WO 2017164969 A1 WO2017164969 A1 WO 2017164969A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- tubular members
- transitional film
- coupler
- film
- transitional
- Prior art date
Abstract
A method of joining at least two polyolefin tubular members containing placing the respective ends of the tubular members within a coupler thereby defining a coupler joint, wrapping the respective ends of the tubular members and the coupler joint with a transitional film having a first surface adapted to bond to the tubular members, bonding the transitional film to the respective ends of the tubular members, and applying a reinforcement system over the transitional film. The bonding of the transitional film to the respective ends of the tubular members contains applying heat to the transitional film and the bonding of the transitional film to the respective ends of the tubular members contains wrapping the pipe with heat-activated shrink tape and heating the damaged area to activate a bonding process of the transitional film to the respective ends of the tubular members.
Description
METHOD AND SYSTEM OF JOINING AT LEAST TWO TUBULAR MEMBERS
FIELD OF THE INVENTION [0001 ] The present invention relates generally to polyolefin pipes and other structures, and more particularly relates to a method and apparatus for repairing and/or joining polyolefin pipes and other structures.
BACKGROUND OF THE INVENTION [0002] Polyolefin materials include the following: thermoplastic polyolefins:
polyethylene (PE), polypropylene (PP), polymethylpentene (PMP), polybutene-1 (PB-1 ); Polyolefin elastomers (POE): polyisobutylene (PIB), ethylene propylene rubber (EPR), ethylene propylene diene monomer (M-class) rubber (EPDM rubber). Such materials, especially in a tubular configuration (i.e., pipes), are utilized to deliver or convey an assortment of media that may have corrosive chemical properties. PE and PP pipe is commonly used by gas utility companies, for example. Such pipes themselves may be deployed in environments that also subject the exterior of the pipe to corrosive or otherwise physically or chemically damaging conditions. Polyolefins are also materials from which various other types of structures, such as holding tanks, pressure vessels and the like, which may be deployed in harsh environments.
[0003] When deploying polyolefin pipe in a particular application, it is of course frequently necessary to join two sections of pipe together end-to-end. One method of accomplishing this is by welding the pipe sections together. In a common technique known as butt fusion, the two pipe sections are heated by a welding plate in the form of a heated disk to cause the ends of the pipes to become molten. The welding plate is then removed and the pipe sections are pressed together with some predetermined force for some predetermined duration of time, depending upon wall thickness and pipe diameter. The result is a weld joint that typically has a circumferential bead cap. There are known potential problems with such weld joints, due to stress differentials and the
like that may exist in the heat-affected zone. Weld joints are susceptible to cracking over time, either due to external forces, such as soil movement or physical impact, or due to the material becoming brittle over time.
[0004] There are also various types of field connections that may be made to polyolefin pipe. These include couplings such as tees, elbows, reducers, and so on. Field connections typically employ some form of crimping force to squeeze the joints together. This crimping process is known to introduce micro-cracks in the pipe material. These micro-cracks can grow over time, due to cyclic pressures, exposure to
temperature swings, material embrittlement, and so on, leading to failure or leaks.
[0005] Persons of ordinary skill in the art will appreciate that polyolefins are materials that by their very nature are difficult to bond to, due to their molecular density and low surface energy. This prevents most simple methods of bonding most types of materials to a polyolefin surface from being entirely effective. Consequently, there has heretofore been little that could be done to repair polyolefin structures that have become degraded by mechanisms such as described above. Pipes may exhibit mechanical damage, including the growth of micro-cracks that can be induced from crimp
connections. Of course, this is undesirable where such defects could allow for leaking, posing dangers to individuals or the environment.
SUMMARY OF THE INVENTION
In view of the foregoing and other considerations, the present invention is directed to a method and apparatus for repairing polyolefin structures, particularly (but not exclusively) PE or PP pipe. In one embodiment of the invention, a damaged area of a polyolefin pipe has filler material applied thereto as necessary to fill cracks, voids, or other degradation of the pipe. Following application of a filler material, a transitional film is applied over the area being repaired. The transitional film has a first side that is adapted to bond to polyolefins. The bonding process may involve application of heat and/or compressive force. After the transitional film is applied and bonded, a
reinforcement system, such as a fiber-reinforced polyurethane application, is applied over the repair area to complete the repair process.
In another embodiment of the invention, a butt weld joint is repaired or reinforced. In some cases, it may be necessary to prepare the joint by smoothing or eliminating the bead cap formed during the welding process. In this embodiment, no filler material may be necessary. The transitional film as described above is applied over the joint and bonded to the joined segments of pipe. Thereafter, a reinforcement system is applied over the transitional film to complete the repair or preventative reinforcement of the weld joint.
In another embodiment of the invention, a crimped area, such as at a field connection, is repaired or reinforced, in a manner similar to that described above for repairing or reinforcing a butt weld.
BRIEF DESCRIPTION OF THE DRAWINGS
The present invention is best understood with reference to the following detailed description of embodiments of the invention when read in conjunction with the attached drawings, in which like numerals refer to like elements, and in which:
Figure 1 is a side, longitudinal cross-sectional view of a length of pipe to be repaired in accordance with one embodiment of the invention;
Figure 2 is a side, longitudinal cross-sectional view of the pipe from Figure 1 having a filler material applied in a damaged area thereof; Figure 3 is a side, longitudinal cross-sectional view of the pipe from Figure 2 having a transitional film applied thereover;
Figure 4 is a side, longitudinal, cross-sectional view of the pipe from Figure 3 having a reinforcement system applied over the repair area including the transitional film;
Figure 5 is a side, longitudinal, cross-sectional view of two sections of pipe aligned end-to-end in preparation for a joining operation in accordance with one embodiment of the invention;
Figure 6 is a side, longitudinal, cross-sectional view of the two sections of pipe from Figure 5 with a transitional film applied over the joint area;
Figure 7 is a side, longitudinal, cross-sectional view of the two sections of pipe from Figure 5 with a reinforcement system applied over the transitional film;
Figure 8 is a side, longitudinal, cross-sectional view of two sections of pipe having been welded together using a conventional butt fusion technique;
Figure 9 is a side, longitudinal, cross-sectional view of the two welded sections of pipe from Figure 8 with the joint reinforced in accordance with one embodiment of the invention;
Figure 10 is a flow diagram illustrating the steps of repairing a tubular member in accordance with one embodiment of the invention; and
Figure 1 1 is a flow diagram illustrating the steps of repairing a non-tubular member in accordance with another embodiment of the invention.
DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS OF THE INVENTION
[0006] In the disclosure that follows, in the interest of clarity, not all features of actual implementations are described. It will of course be appreciated that in the development of any such actual implementation, as in any such project, numerous engineering and technical decisions must be made to achieve the developers' specific goals and subgoals (e.g., compliance with system and technical constraints), which will vary from one implementation to another. Moreover, attention will necessarily be paid to proper engineering practices for the environment in question. It will be appreciated that such development efforts might be complex and time-consuming, outside the knowledge base of typical laymen, but would nevertheless be a routine undertaking for those of ordinary skill in the relevant fields.
[0007] Referring to Figure 1 , there is shown a longitudinal, cross-sectional view of a section of polyolefin pipe (e.g., PE or PP pipe) identified with reference numeral 10. As shown in Figure 1 , pipe 10 has a damaged area 12 at which pipe 10 has been degraded. Although the embodiment of Figure 1 comprises a pipe, those of ordinary
skill in the art having the benefit of the present disclosure will appreciate that the invention may be practiced in connection with other types of PE structures.
[0008] Figure 2 illustrates a first step in a repair method in accordance with an exemplary embodiment of the invention, wherein a filler material 14 is applied over the damaged area 12 as necessary to fill the damaged area 12. In one embodiment, the filler material 14 may be a polyester, epoxy, vinyl ester, polyurethane, thermoplastic material, rubber compound, or acrylic, such as a methylacrylate or thermoplastic material.
[0009] Once the filler material has been applied and cured or otherwise hardened, a next step in accordance with the disclosed embodiment of the invention is to overlay a transitional film 16 over the section of pipe being repaired. This is shown in Figure 3. In a presently preferred embodiment of the invention, the transitional film 16 comprises Nolax S22.2202, a co-extruded multi-layer adhesive film commercially available from Nolax AG, a member of the Colla no Group headquartered in Sempach Station, Switzerland. See www.nolax.com.
[00010] A preferred attribute of the transitional film 16 is that it is adapted on one side thereof to bond effectively with polyolefinic materials, such as PE, EVA, EPOM, and PP and adapted on the opposite side thereof to bond to PVC, polyurethane, ABS, PC, PA, etc.
[0001 1 ] In an exemplary embodiment, the transitional film is wrapped around the length of pipe 10 being repaired. Those of ordinary skill in the art will recognize that the bonding of film 16 to pipe 10 must be activated. Typically, this is accomplished by means of application of heat and compressive force. One method of accomplishing this is through the use of heat-activated shrink tape (not shown in the Figures), such as 220R 4" 20% shrink release coated roll commercially available from Dunston Inc., headquartered in Charlotte, North Carolina, United States. See www.shrinktape.com .
[00012] Once film 16 has been bonded to pipe 10 over the area being repaired, an outer reinforcement system 18 is applied over the repair area, as shown in Figure 4. Note that the heat shrink tape or other means for activating the bond of the film 14 to pipe 10 is preferably removed prior to application of the outer reinforcement system 18 and hence is not shown in Figure 4. In one preferred embodiment of the invention, the
outer reinforcement system 18 comprises A+ Wrap™, a high-strength wrap comprised of a fiberglass reinforced substrate factory impregnated with moisture-cured
polyurethane. A+ Wrap™ is commercially available from Pipe Wrap, Inc., Houston, Texas. See http:Uwww.piperepair.net/products/structural-repair/a-wrap/, hereby incorporated by reference herein in its entirety. In another embodiment, the outer reinforcement system 18 comprises a fiber-reinforced epoxy system, such as
FormaShield™, which is also commercially available from Pipe Wrap, Inc. See http://www.piperepair.net/products/structural/repair/formashield/, hereby incorporated by reference herein in its entirety.
[00013] In addition to providing a means of effectuating structural repair of polyolefin structures such as PE pipes, as described above with reference to Figures 1 - 4, it is contemplated that the present invention may be employed to create a joint between two sections of pipe, circumventing the need for a conventional butt fusion operation. This is shown in Figures 5-7.
[00014] In particular, in Figure 5, there is shown a longitudinal, cross-sectional view of two sections of pipe designated with reference numerals 20 and 22. Pipe sections 20 and 22 are oriented end-to-end in preparation of the creation of a joint therebetween.
[00015] Figure 6 shows the respective pipe sections 20 and 22 from Figure 5 with a transitional film layer 24 bonded over the joint area. As in the previously described embodiment, transitional film layer 24 is adapted on one side to bond to polyol.efins, and the bond may be activated by applying heat and compressive force.
[00016] Figure 7 shows the respective pipe sections 20 and 22 with a
reinforcement system 26 applied over and bonded pipes 20 and 22 in the area of transitional film 24. The aforementioned A+ Wrap™ or Formashield™ products are contemplated to be suitable reinforcement systems 26 for the purposes of the present invention.
[00017] It is further contemplated that the present invention may be employed as a preventative measure to strengthen the integrity of a conventional butt fusion joint between two sections of pipe. Figure 8 shows two sections of polyolefin pipe 28 and 30 having been welded together using a conventional butt fusion technique. As previously
noted such a technique commonly results in the formation of a bead cap 32 around the circumference of the weld joint.
[00018] Figure 9 shows the sections of pipe 28 and 30 with the weld joint therebetween 5 reinforced in accordance with one embodiment of the invention. From Figure 9, it is evident that the bead cap 32 is preferably removed prior to application and bonding of a transitional film 32 and a reinforcement system 34.
[00019] Turning to Figure 10, there is shown a flow diagram illustrating a repair methodology in accordance with one embodiment of the invention. In particular, the process depicted in Figure 10 is believed to be the preferable means of repairing tubular members, such as pipes.
[00020] As shown in Figure 10, the first step 40 is to clean the repair area, for example, with an appropriate solvent, to assure optimal bonding during the repair process.
[00021 ] As described above, the next step 42 is to apply filler material as necessary to provide a relatively smooth repair surface. This step 42 may or may not be necessary depending upon the nature of the damage being repaired. As noted above, suitable filler materials may be a polyester, epoxy, vinyl ester, polyurethane,
thermoplastic material, rubber compound, or acrylic, such as a methylacrylate or thermoplastic material.
[00022] The next step 44 is to apply the bi-material coextruded transitional film to the repair area. In one embodiment, bonding of the transitional film to the repair area is accomplished by applying heat, such as with a heat gun or the like, as represented by block 46.
[00023] Next, in block 48, a reinforcement system is applied over the repair area. The aforementioned A+ Wrap™ or FormaShield™ systems are candidates for the reinforcement system.
[00024] Next, in block 50, compressive force is applied to the repair area. As noted above, one manner of accomplishing this is through the use of heat-shrinking tape that is wrapped around the tubular member being repaired and then applying heat, such as with a heat gun, to cause the tape wrap to constrict or compress around the tubular member and the repair area.
[00025] As noted in block 52, the reinforcement system is allowed to cure, at which time the means of applying compressive force (e.g., the heat-shrink tape) may be removed.
[00026] Turning now to Figure 1 1 , there is shown an embodiment of the invention which may be advantageously employed for the repair of non-tubular polyolefin members. The process begins with block 56, wherein the repair surface is prepared by cleaning, with appropriate solvent(s). As in the previous embodiments, a filler material may or may not be applied, as represented by block 58 in Figure 1 1 .
[00027] In block 60, the hi-material, co-extruded transitional film is applied, as hereinbefore described. Heat is the preferred method of bonding the transitional film to the repair area, as reflected by block 52. Thereafter, a reinforcement system as described above is applied.
[00028] In the embodiment of Figure 1 1 , a next step, in block 66, is to apply a release film over the reinforcement system. In a preferred embodiment, the release film is a silicone-treated PE sheet that is perforated. Following application of the release film, a bleeder cloth material is applied over the repair area, as represented by block 68. In one embodiment, the bleeder cloth material is a non-woven polyester material adapted to absorb excess resin out of the reinforcement system during the cure process.
[00029] A vacuum bag pressure system is employed to exert compression force on the repair area as the reinforcement system is curing. In block 70 of Figure 1 1 , a vacuum bag is sealed around the repair area. In one embodiment, a zinc-oxide based double-sided tape is used to create the seal of the vacuum bag, which may be a high- density PE film, for example.
[00030] In block 72, vacuum pressure is applied to compress the vacuum bag against the repair area. This compression force is maintained for as long as it takes for the reinforcement system to cure, typically two to four hours.
[00031 ] Referring now to Figure 12, there is shown a system of at least two polyolefin tubular members 20, 22 joined end-to-end. The two tubular members 20, 22 are arranged in a coupler 1 10 such that their respective ends are within the coupler 1 10. A transitional film 24 is applied and bonded to the coupler 1 10 and at least a portion of
the at least two tubular members 20, 22. The transitional film has a first side and a second side, the first side adapted to bond to polyolefins and the transitional film is oriented such that the first side is facing the tubular members 20, 22. A reinforcement system 26 is applied over the transitional film 24. Preferably, the reinforcement system comprises a fiber-reinforced polyurethane or a fiber-reinforced epoxy system. The reinforcement system 26 is bonded to the second side of the transitional film.
[00032] The transitional film 24 and the reinforcement system 26 can be any of the transitional films 24 and the reinforcement systems 26 described in relation to any of the other embodiments.
[00033] When the respective ends of the tubular members 20, 22 are placed within the couple 1 10, which defines the coupler joint (the couple joint contains the coupler and the portion of the tubular members within the coupler). Preferably, when the transitional film 24 is applied and bonded to the coupler 1 10 and at least a portion of the at least two tubular members 20, 22 it is wrapped around the coupler 1 10 and the tubular members 20, 22. The wrapping of the transitional film 24 preferably completely covers the coupler 1 10. The wrapping of the transitional film 24 preferably extends onto the tubular members 20, 22 at least about 0.5 inch more preferably 1 inch past the end of the coupler.
[00034] In one embodiment, the bonding of the transitional film to the respective ends of the tubular members comprises applying heat to the transitional film. In one embodiment, the bonding of the transitional film to the respective ends of the tubular members comprises wrapping the pipe with heat-activated shrink tape and heating the damaged area to activate a bonding process of the transitional film to the respective ends of the tubular members.
[00035] In one embodiment, applying a reinforcement system over the transitional film comprises wrapping the reinforcement system over the transitional film. In one embodiment, less than 100% or less than 90% of the surface area of the transitional film is covered by the reinforcement system. In another embodiment, essentially all of the surface area of the transitional film is covered by the reinforcement system. "Essentially all" in this application is defined to be at least 95%. In another embodiment, the
reinforcement system covers essentially all of the surface area of the transitional film and at least a portion of the tubular members outside of the transitional film area.
[00036] The coupler may be made of any suitable material such as metal, or a polymer. It may be made of the same or different materials than the tubular members.
[00037] The coupler may contain more than two tubular members. Figure 13 illustrates a coupler 1 10 having three tubular members 20, 22, 124. Figure 14 illustrates a coupler 1 10 having four tubular members 20, 22, 124, 126. The coupler may contain more than 4 tubular members. For each of the embodiments shown in Figures 13 and 14, the transitional film and reinforcement system would be applied over the coupler and a portion of the tubular members in a similar manner as shown in Figure 12.
[00038] The ends of the tubular members to be joined together must reside within the coupler, but they do not have to be physically touching. In one embodiment, the ends of the tubular members are in physical contact touching with nothing else between them. In another embodiment, the ends are close to each other, being separated by less than about 5 millimeters, more preferably less than 3 millimeters. In another embodiment, the ends are separated by a more substantial distance, between about 0.5 and 2 inches. In another embodiment, there is a material located between the ends of the tubular members, such as formed during butt fusion, adhesives, gaskets, or any other suitable material.
[00039] From the foregoing detailed description, it will be apparent to those of ordinary skill in the art that a method and apparatus (system) for repair polyolefin structures such as PE or PP pipes as well as non-tubular structures, such as holding tanks and the like, has been disclosed. Although specific implementation details have been provided herein, this has been done solely for the purposes of illustrating generally the scope of the invention, which is defined in the claims which follow. It is to be understood that various substitutions, alterations, and/or modifications may be made to the disclosed embodiment without departing from the actual scope of the invention.
Claims
1 . A method of joining at least two polyolefin tubular members, comprising:
(a) placing the respective ends of the tubular members within a coupler, thereby defining a coupler joint;
(b) wrapping the respective ends of the tubular members and the coupler joint with a transitional film having a first surface adapted to bond to the tubular members;
(c) bonding the transitional film to the respective ends of the tubular members, wherein the bonding of the transitional film to the respective ends of the tubular members comprises applying heat to the transitional film, and wherein the bonding of the transitional film to the respective ends of the tubular members comprises wrapping the pipe with heat-activated shrink tape and heating the damaged area to activate a bonding process of the transitional film to the respective ends of the tubular members; and
(d) applying a reinforcement system over the transitional film.
2. The method of claim 1 , wherein the coupler is metal.
3. The method of claim 1 , wherein the method comprises joining 2 tubular members.
4. The method of claim 1 , wherein the method comprises joining 3 tubular members.
5. A method of claim 1 , wherein the step (d) of applying a reinforcement system over the transitional film comprises applying a fiber-reinforced polyurethane system which bonds to a second side of the transitional film.
6. A method of claim 1 , wherein the step (d) of applying a reinforcement system over the transitional film comprises applying a fiber-reinforced epoxy system which bonds to a second side of the transitional film.
7. The method of claim 1 , wherein the distance between the ends of the tubular
members within the coupler is less than about 5 millimeters.
8. The method of claim 1 , wherein the reinforcement system covers essentially all of the transitional film.
9. A method of joining at least two polyolefin tubular members, comprising:
(a) placing the respective ends of the tubular members within a coupler, thereby defining a coupler joint;
(b) wrapping the respective ends of the tubular members and the coupler joint with a transitional film having a first surface adapted to bond to the tubular members;
(c) bonding the transitional film to the respective ends of the tubular members; and
(d) applying a reinforcement system over the transitional film comprising applying a fiber-reinforced polyurethane system which bonds to a second side of the transitional film.
10. The method of claim 9, wherein the coupler is metal.
1 1 . The method of claim 9, wherein in step (c) of bonding the transitional film to the structure comprises applying heat to the transitional film.
12. The method of claim 9, wherein the distance between the ends of the tubular
members within the coupler is less than about 5 millimeters.
13. A method of joining at least two polyolefin tubular members, comprising:
(a) placing the respective ends of the tubular members within a coupler, thereby defining a coupler joint;
(b) wrapping the respective ends of the tubular members and the coupler joint with a transitional film having a first surface adapted to bond to the tubular members;
(c) bonding the transitional film to the respective ends of the tubular members; and
(d) applying a reinforcement system over the transitional film comprising applying a fiber-reinforced epoxy system which bonds to a second side of the transitional film.
14. The method of claim 13, wherein the distance between the ends of the tubular members within the coupler is less than about 5 millimeters.
15. The method of claim 13, wherein the coupler is metal.
16. The method of claim 13, wherein in step (c) of bonding the transitional film to the structure comprises applying heat to the transitional film.
17. A system at least two polyolefin tubular members joined end-to-end, comprising: the at least two tubular members arranged in a coupler such that their respective ends are within the coupler;
a transitional film applied and bonded to the coupler and at least a portion of the at least two tubular members, the transitional film having a first side and a second side, the first side adapted to bond to polyolefins; and
a reinforcement system, applied over the transitional film, wherein the
reinforcement system comprises a fiber-reinforced polyurethane or a fiber-reinforced epoxy system bonded to the second side of the transitional film.
18. The system of claim 17, wherein the transitional film comprises a bi-material co- extruded film.
19. The system of claim 17, wherein the distance between the ends of the tubular members within the coupler is less than about 5 millimeters.
20. The system of claim 17, wherein the reinforcement system covers essentially all of the transitional film.