WO2017162954A1 - Procede de fabrication de verre peint ou laque - Google Patents
Procede de fabrication de verre peint ou laque Download PDFInfo
- Publication number
- WO2017162954A1 WO2017162954A1 PCT/FR2017/050571 FR2017050571W WO2017162954A1 WO 2017162954 A1 WO2017162954 A1 WO 2017162954A1 FR 2017050571 W FR2017050571 W FR 2017050571W WO 2017162954 A1 WO2017162954 A1 WO 2017162954A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- glass sheet
- liquid composition
- layer
- speed
- organic binder
- Prior art date
Abstract
Description
Claims